Display materials containing patterned areas of encapsulated electrophoretic medium

Abstract

A method for forming a patterned display comprising isolated portions of an encapsulated electrophoretic medium disposed between continuous light-transmitting electrodes. The resulting patterned electrophoretic display allows a viewer to see through the gaps between the portions of the encapsulated electrophoretic medium, thereby allowing the viewer to visualize a surface or object behind the electrophoretic display. The invention provides displays comprising patterned areas of electro-optic material. The electro-optic material is typically an encapsulated electrophoretic material, i.e., an electrophoretic medium encapsulated in a capsule, an array of sealed microcells, or dispersed in a polymer that is not miscible with the electrophoretic medium.

Description

[Technical Field]

[0001] (Related Applications) This application claims priority to U.S. Provisional Application No. 63 / 330,751, filed April 13, 2022. All patents and patent applications disclosed herein are incorporated by reference in their entirety.

[0002] The present invention relates to the field of electrophoretic displays and color-changing materials made using electrophoretic media. [Background technology]

[0003] Historically, the electrophoretic display medium in electro-optic displays has been continuous, sandwiched between control electrodes. For example, if the control electrodes were also continuous, the resulting (optionally flexible) sheet material could result in complex designs that could be cut and electronically switched between optical states (e.g., E INK PRISM). TM Alternatively, the continuous electrophoretic medium may span multiple electrodes, as in the case of active matrix electrophoretic display modules, in which a continuous encapsulating layer of electrophoretic medium is coated over an active matrix of pixel electrodes. Such assemblies are commonly incorporated into e-readers such as the Amazon KINDLE®. Alternatively, the continuous encapsulating layer of electrophoretic medium may span multiple electrodes, as in the case of active matrix electrophoretic display modules, in which a continuous encapsulating layer of electrophoretic medium is coated over an active matrix of pixel electrodes. Such assemblies are commonly incorporated into e-readers such as the Amazon KINDLE®. TM As in a display line module, it may be encapsulated in a sealed microcell and laminated to an active matrix backplane. Previously, it has not been disclosed to create segments that are intentionally isolated from each other by intentionally cutting portions of the electrophoretic medium and placing multiple electrophoretic segments that do not contact each other between the same continuous top and bottom electrodes, which are then formed into a display.

[0004] The present invention relates to electro-optical and related devices and methods for producing such devices. The invention is particularly, but not exclusively, intended for displays comprising an electrophoretic medium. The term "electro-optical," as applied to a material or display or device, is used herein in its conventional sense in the imaging arts to refer to a material having first and second display states in which at least one optical property differs, and which is changed from its first display state to its second display state by application of an electric field to the material. The optical property is typically color perceptible to the human eye, but it can also be another optical property, such as optical transmittance, reflectance, luminescence, or, in the case of displays intended for machine reading, pseudocolor in the sense of a change in reflectance of electromagnetic wavelengths outside the visible range.

[0005] The term “gray state” is used herein in its conventional sense in the imaging arts to refer to a state intermediate between two extreme pixel optical states and does not necessarily imply a black-to-white transition between these two extreme states. For example, some of the E Ink patents and published applications referenced below describe electrophoretic displays in which the extreme states are white and dark blue, so that an intermediate “gray state” would actually be light blue. In fact, as already mentioned, a change in optical state may not be a change in color at all. The terms “black” and “white” may be used hereinafter to refer to the two extreme optical states of a display and should generally be understood to include extreme optical states that are not strictly black and white, such as the aforementioned white and dark blue states. The term “monochrome” may be used hereinafter to refer to a drive scheme that drives pixels to only their two extreme optical states, without any intervening gray states.

[0006] The terms "bistable" and "bistable" are used herein in their conventional sense in the art to refer to displays having display elements with first and second display states that differ in at least one optical property, such that after any given element is driven with a finite-duration addressing pulse to assume either its first or second display state, that state persists after the addressing pulse is terminated for at least several times, e.g., at least four times, the minimum duration of the addressing pulse required to change the state of the display element. U.S. Pat. No. 7,170,670 indicates that some grayscale-capable particle-based electrophoretic displays are stable not only in their extreme black and white states but also in their intermediate gray states, and the same is true for several other types of electro-optic displays. Displays of this type are properly referred to as "multistable" rather than bistable, but for convenience, the term "bistable" may be used herein to encompass both bistable and multistable displays.

[0007] Several types of electro-optic displays are known. One type of electro-optic display is the rotating dichroic member type, as described, for example, in U.S. Patent Nos. 5,808,783, 5,777,782, 5,760,761, 6,054,071, 6,055,091, 6,097,531, 6,128,124, 6,137,467, and 6,147,791 (displays of this type are often referred to as "rotating dichroic ball" displays, although in some of the above-mentioned patents the rotating member is not spherical and the term "rotating dichroic member" is more accurate and preferred). Such displays use a number of small bodies (typically spherical or cylindrical) having two or more sections with different optical properties and an internal dipole. These bodies are suspended within liquid-filled vesicles within a matrix, and the vesicles are filled with liquid so that the bodies are free to rotate. The appearance of the display is changed by applying an electric field to it, thus rotating the bodies to various positions and varying the section of the body that is seen through the viewing surface. This type of electro-optic medium is typically bistable.

[0008] Another type of electro-optic display that has been the subject of intensive research and development for many years is the particle-based electrophoretic display, in which a plurality of charged particles move through a fluid under the influence of an electric field. Electrophoretic displays can have attributes of good brightness and contrast, wide viewing angles, state bistability, and low power consumption when compared to liquid crystal displays. Nevertheless, problems with the long-term image quality of these displays have prevented their widespread use. For example, the particles that make up electrophoretic displays tend to settle, resulting in an inadequate usable lifespan for these displays.

[0009] As described above, electrophoretic media require the presence of a fluid. In most prior art electrophoretic media, this fluid is liquid, but electrophoretic media can also be produced using gaseous fluids. See, for example, Kitamura, T., et al., "Electrical toner movement for electronic paper-like display," IDW Japan, 2001, Paper HCS1-1, and Yamaguchi, Y., et al., "Toner display using insulative particles charged triboelectrically," IDW Japan, 2001, Paper AMD4-4. See also U.S. Patent Publication No. 2005 / 0001810, European Patent Applications Nos. 1,462,847, 1,482,354, 1,484,635, 1,500,971, 1,501,194, 1,536,271, 1,542,067, 1,577,702, 1,577,703, and 1,598,694, and International Applications Nos. WO 2004 / 090626, WO 2004 / 079442, and WO 2004 / 001498. Such gas-based electrophoretic media are believed to be susceptible to the same types of problems as liquid-based electrophoretic media due to particle settling when the media is used in an orientation that allows for such settling, for example, in a sign where the media is positioned in a vertical plane. Indeed, particle settling is believed to be a more severe problem in gas-based electrophoretic media than in liquid-based electrophoretic media due to the lower viscosity of the gaseous suspending fluid compared to the viscosity of a liquid, which allows for faster settling of the electrophoretic particles.

[0010] Numerous patents and applications assigned to or in the name of Massachusetts Institute of Technology (MIT), E Ink Corporation, E Ink California, LLC, and related companies describe various techniques used for encapsulation and microcell electrophoresis and other electro-optic media. Encapsulated electrophoretic media include a number of microcapsules, each of which includes an internal phase containing electrophoretically movable particles in a fluid medium and a capsule wall surrounding the internal phase. Typically, the microcapsules themselves are held in a polymeric binder to form a coherent layer positioned between two electrodes. In microcell electrophoretic displays, the charged particles and fluid are not encapsulated within microcapsules, but instead are held within multiple cavities formed in a carrier medium, typically a polymeric film. Techniques described in these patents and applications include the following: (a) Electrophoretic particles, fluids, and fluid additives (see, e.g., U.S. Pat. Nos. 7,002,728 and 7,679,814) (b) Microcapsules, Binders, and Encapsulation Processes (see, e.g., U.S. Patent Nos. 6,922,276 and 7,411,719) (c) Microcell structures, wall materials, and methods of forming the microcells (see, e.g., U.S. Patent Nos. 7,072,095 and 9,279,906) (d) Methods for filling and sealing microcells (see, e.g., U.S. Patent Nos. 7,144,942 and 7,715,088) (e) Films and subassemblies containing electro-optical materials (see, e.g., U.S. Patent Nos. 6,982,178 and 7,839,564) (f) backplanes, adhesive layers, and other auxiliary layers and methods used in displays (see, e.g., U.S. Patent Nos. 7,075,703, 7,116,318, 7,535,624, 7,554,712, 7,561,324, 7,649,674, 7,733,554, 8,034,209, 8,610,988, and 9,835,925). (g) Color formation and color control (see, e.g., U.S. Patent Nos. 7,075,502 and 7,839,564) (h) Methods for driving displays (see, e.g., U.S. Patent Nos. 7,012,600 and 7,453,445) (i) Display applications (see, e.g., U.S. Patent Nos. 7,312,784 and 8,009,348) (j) Non-electrophoretic display and non-display applications of encapsulation and microcell technology, such as those described in U.S. Pat. No. 6,241,921 and U.S. Patent Application Publication No. 2015 / 0277160 (see, e.g., U.S. Pat. No. 7,615,325 and U.S. Patent Application Publication Nos. 2015 / 0005720 and 2016 / 0012710).

[0011] Many of the aforementioned patents and applications recognize that the walls surrounding discrete microcapsules in an encapsulated electrophoretic medium may be replaced by a continuous phase, thus producing a so-called polymer-dispersed electrophoretic display, in which the electrophoretic medium comprises a plurality of discrete droplets of electrophoretic fluid and a continuous phase of polymer material, and that the discrete droplets of electrophoretic fluid in such a polymer-dispersed electrophoretic display may be considered capsules or microcapsules even though no discrete capsule membrane is associated with each individual droplet. See, for example, the aforementioned U.S. Patent No. 6,866,760. Therefore, for purposes of this application, such polymer-dispersed electrophoretic media are considered a subspecies of encapsulated electrophoretic media.

[0012] A related type of electrophoretic display is the so-called "microcell electrophoretic display." In a microcell electrophoretic display, the charged particles and fluid are not encapsulated in microcapsules, but instead are held within a plurality of cavities formed in a carrier medium, typically a polymeric film. See, for example, U.S. Patent Nos. 6,672,921 and 6,788,449, both assigned to SiPix Imaging, Inc.

[0013] Encapsulated or microcell electrophoretic displays typically do not suffer from the clustering and settling failure modes of conventional electrophoretic devices and offer additional advantages, such as the ability to print or coat displays on a wide variety of flexible and rigid substrates. The use of the word "printing" is intended to include all forms of printing and coating, including, but not limited to, patch die coating, slot or extrusion coating, slide or cascade coating, pre-metered coating such as curtain coating, roll coating such as knife-over-roll coating, forward and reverse roll coating, gravure coating, dip coating, spray coating, meniscus coating, spin coating, brush coating, air knife coating, silk screen printing processes, electrostatic printing processes, thermal printing processes, inkjet printing processes, electrophoretic deposition, and other similar techniques. Thus, the resulting display can be flexible. Furthermore, because the display medium can be printed (using a variety of methods), the display itself can be inexpensively produced.

[0014] An electro-optic display typically comprises a layer of electro-optic material and at least two other layers (one of these two layers is an electrode layer) disposed on opposite sides of the electro-optic material layer. In most such displays, both layers are electrode layers, and one or both of the electrode layers are patterned to define the pixels of the display. For example, one electrode layer may be patterned into elongated row electrodes and the other into elongated column electrodes extending perpendicular to the row electrodes, with pixels defined by the intersections of the row and column electrodes. Alternatively, and more commonly, one electrode layer has the form of a single continuous electrode, and the other electrode layer is patterned into a matrix of pixel electrodes, each of which defines one pixel of the display. In another type of electro-optic display, where the display is intended for use with a separate stylus, print head, or similar movable electrode, only one of the layers adjacent to the electro-optic material layer comprises an electrode, and the layer on the opposite side of the electro-optic material layer is typically a protective layer intended to prevent the movable electrode from damaging the electro-optic material layer. Summary of the Invention [Means for solving the problem]

[0015] The present invention provides displays comprising patterned areas of electro-optic material. The electro-optic material is typically an encapsulated electrophoretic material, i.e., an electrophoretic medium encapsulated in capsules, an array of sealed microcells, or dispersed in a polymer that is not miscible with the electrophoretic medium. Alternatively, the encapsulated electro-optic material may comprise rotating particles, liquid crystals, or electrochromic materials. Nevertheless, the patterned material can be made to change optical states using the application of an electric field, typically created between a top transparent electrode and a bottom electrode, which may comprise a single electrode, or may comprise several (e.g., segmented) electrodes, or may comprise an array of individually addressable pixel electrodes, e.g., using an array of thin film transistors (TFTs).

[0016] A method for making such a display using a double peel laminated electro-optic medium as well as stainless steel is also described.

[0017] In a first aspect, an electrophoretic display comprises a first continuous light-transmitting electrode disposed on a first light-transmitting substrate, a second continuous light-transmitting electrode disposed on a second light-transmitting substrate, a first portion of an encapsulated electrophoretic medium disposed between the first continuous light-transmitting electrode and the second continuous light-transmitting electrode, and a second portion of the encapsulated electrophoretic medium disposed between the first continuous light-transmitting electrode and the second continuous light-transmitting electrode. In the display, the first portion of the encapsulated electrophoretic medium does not contact the second portion of the encapsulated electrophoretic medium, and application of an electric field between the first continuous light-transmitting electrode and the second continuous light-transmitting electrode causes a change in the optical state of both the first portion of the encapsulated electrophoretic medium and the second portion of the encapsulated electrophoretic medium. In some embodiments, the first portion of the encapsulated electrophoretic medium comprises a first type of electrophoretic particles, and the second portion of the encapsulated electrophoretic medium comprises a second type of electrophoretic particles. In some embodiments, a first portion of the encapsulated electrophoretic medium comprises a first type of electrophoretic particles and a second portion of the encapsulated electrophoretic medium comprises a second type of electrophoretic particles, the first and second types of electrophoretic particles having different optical properties. In some embodiments, both the first portion of the encapsulated electrophoretic medium and the second portion of the encapsulated electrophoretic medium comprise more than one type of electrophoretic particles. In some embodiments, the first portion of the encapsulated electrophoretic medium is encapsulated in microcapsules, and the microcapsules are held together using a polymeric binder. In some embodiments, the microcapsules comprise gelatin or polyvinyl alcohol. In some embodiments, the polymeric binder comprises polyurethane or acrylate. In some embodiments, the first portion of the encapsulated electrophoretic medium is encapsulated in microcells and sealed using a polymeric sealing layer. In some embodiments, the microcells comprise an acrylic polymer or a (meth)acrylic polymer. In some embodiments, the display further comprises a light-transmitting semiconductive adhesive disposed between the first continuous light-transmitting electrode and the second continuous light-transmitting electrode.In some embodiments, the optically transparent semiconductive adhesive comprises a polyurethane doped with an inorganic salt. In some embodiments, the optically transparent semiconductive adhesive comprises a polyurethane doped with an inorganic salt at a concentration of 2% (wt:wt) to 0.05% (wt:wt). In some embodiments, the optically transparent semiconductive adhesive separates a first portion of the encapsulated electrophoretic medium and a second portion of the encapsulated electrophoretic medium. In some embodiments, the first portion of the encapsulated electrophoretic medium and the second portion of the encapsulated electrophoretic medium are separated by a distance of at least 5 mm when measured parallel to the first continuous optically transparent electrode and the second continuous optically transparent electrode.

[0018] In another aspect, a method of making an electrophoretic display includes providing a layer of encapsulated electrophoretic medium disposed between a first release sheet and first adhesive layer and a second release sheet and second adhesive layer; patterning the layer of encapsulated electrophoretic medium by cutting through the first release sheet, the first adhesive layer, and the layer of encapsulated electrophoretic medium to create a first portion of the encapsulated electrophoretic medium and a second portion of the encapsulated electrophoretic medium; and disposing the first portion of the encapsulated electrophoretic medium and the second portion of the encapsulated electrophoretic medium between a first continuous light-transmitting electrode disposed on a first light-transmitting substrate and a second continuous light-transmitting electrode disposed on a second light-transmitting substrate such that the first portion of the encapsulated electrophoretic medium does not contact the second portion of the encapsulated electrophoretic medium. In some embodiments, an optically transparent semiconductive adhesive is disposed between the first continuous optically transparent electrode and the second continuous optically transparent electrode, separating a first portion of the encapsulated electrophoretic medium from a second portion of the encapsulated electrophoretic medium. In some embodiments, the first portion of the encapsulated electrophoretic medium and the second portion of the encapsulated electrophoretic medium are separated by a distance of at least 5 mm when measured parallel to the first continuous optically transparent electrode and the second continuous optically transparent electrode. In some embodiments, the patterning includes cutting through the second release sheet and the second adhesive layer. In some embodiments, the patterning is performed using a laser, scissors, a knife, or a die. In some embodiments, the patterning step further includes creating a remaining portion of the encapsulated electrophoretic medium, and the method further includes removing the remaining portion of the encapsulated electrophoretic medium from the layer of encapsulated electrophoretic medium. The present specification also provides, for example, the following: (Item 1) 1. An electrophoretic display comprising: a first continuous light-transmitting electrode (340) disposed on a first light-transmitting substrate (350); a second continuous light-transmitting electrode (310) disposed on a second light-transmitting substrate (320); a first portion (220) of an encapsulated electrophoretic medium disposed between the first continuous optically transmissive electrode (350) and the second continuous optically transmissive electrode (310); a second portion (240) of encapsulated electrophoretic medium disposed between the first continuous light-transmitting electrode and the second continuous light-transmitting electrode; Equipped with the first portion (220) of the encapsulated electrophoretic medium does not contact the second portion (240) of the encapsulated electrophoretic medium; an electrophoretic display, wherein application of an electric field between the first continuous light-transmitting electrode and the second continuous light-transmitting electrode (310) causes a change in the optical state of both the first portion (220) of the encapsulated electrophoretic medium and the second portion (240) of the encapsulated electrophoretic medium. (Item 2) Item 1. An electrophoretic display as described in item 1, wherein a first portion (220) of the encapsulated electrophoretic medium contains a first type of electrophoretic particles (142), and a second portion (240) of the encapsulated electrophoretic medium contains the first type of electrophoretic particles (142). (Item 3) Item 1. An electrophoretic display as described in item 1, wherein a first portion (220) of the encapsulated electrophoretic medium contains a first type of electrophoretic particles (142) and a second portion (240) of the encapsulated electrophoretic medium contains a second type of electrophoretic particles (145), and the first and second types of electrophoretic particles (142, 145) have different optical properties. (Item 4) 4. An electrophoretic display according to any of items 1-3, wherein the first portion of encapsulated electrophoretic medium (220) and the second portion of encapsulated electrophoretic medium (240) both contain more than one type of electrophoretic particles (142, 145). (Item 5) 2. The electrophoretic display of claim 1, wherein the first portion (220) of the encapsulated electrophoretic medium is encapsulated in microcapsules, the microcapsules being held together using a polymeric binder. (Item 6) 6. The electrophoretic display of claim 5, wherein the microcapsules comprise gelatin or polyvinyl alcohol. (Item 7) 7. The electrophoretic display of claim 6, wherein the polymeric binder comprises a polyurethane or an acrylate. (Item 8) Item 10. The electrophoretic display of item 1, wherein the first portion (220) of the encapsulated electrophoretic medium is encapsulated in a microcell and sealed using a polymeric sealing layer. (Item 9) Item 9. The electrophoretic display of item 8, wherein the microcells comprise an acrylic polymer or a (meth)acrylic polymer. (Item 10) Item 10. The electrophoretic display of item 1, further comprising a light-transmitting semiconductive adhesive (360) disposed between the first continuous light-transmitting electrode and the second continuous light-transmitting electrode. (Item 11) Item 11. An electrophoretic display according to item 10, wherein the light-transmitting semiconductive adhesive (360) comprises polyurethane doped with an inorganic salt. (Item 12) Item 12. An electrophoretic display according to item 11, wherein the light-transmitting semiconductive adhesive (360) comprises polyurethane doped with an inorganic salt at a concentration of 2% (wt:wt) to 0.05% (wt:wt). (Item 13) 13. The electrophoretic display of claim 10, wherein the optically transparent semiconductive adhesive (360) separates the first portion (220) of the encapsulated electrophoretic medium and the second portion (240) of the encapsulated electrophoretic medium. (Item 14) Item 10. The electrophoretic display of item 1, wherein the first portion (220) of the encapsulated electrophoretic medium and the second portion (240) of the encapsulated electrophoretic medium are separated by a distance of at least 5 mm when measured parallel to the first continuous light-transmitting electrode and the second continuous light-transmitting electrode. (Item 15) 1. A method of making an electrophoretic display, comprising: providing a layer (130) of encapsulated electrophoretic medium disposed between a first release sheet (110) and a first adhesive layer (115) and a second release sheet (120) and a second adhesive layer (125); patterning the layer of encapsulated electrophoretic medium (130) by cutting through the first release sheet (110), the first adhesive layer (115), and the layer of encapsulated electrophoretic medium (130) to create a first portion of encapsulated electrophoretic medium (220) and a second portion of encapsulated electrophoretic medium (240); disposing the first portion (220) of the encapsulated electrophoretic medium and the second portion (240) of the encapsulated electrophoretic medium between a first continuous optically transparent electrode (340) disposed on a first optically transparent substrate (350) and a second continuous optically transparent electrode (310) disposed on a second optically transparent substrate (320) (320) such that the first portion (220) of the encapsulated electrophoretic medium does not contact the second portion (240) of the encapsulated electrophoretic medium; A method comprising: (Item 16) Item 16. The method of item 15, wherein an optically transparent semiconductive adhesive (360) is disposed between the first continuous optically transparent electrode (340) and the second continuous optically transparent electrode (310), separating the first portion (220) of the encapsulated electrophoretic medium from the second portion (240) of the encapsulated electrophoretic medium. (Item 17) 17. The method of claim 15 or 16, wherein the first portion of encapsulated electrophoretic medium (220) and the second portion of encapsulated electrophoretic medium (240) are separated by a distance of at least 5 mm when measured parallel to the first continuous optically transparent electrode (340) and the second continuous optically transparent electrode (310). (Item 18) Item 16. The method of item 15, wherein patterning comprises cutting through the second release sheet (120) and the second adhesive layer (125). (Item 19) 19. The method according to item 15 or 18, wherein the patterning is performed using a laser, scissors, a knife, or a die. (Item 20) Item 16. The method of item 15, wherein the patterning step further comprises creating a remaining portion (250) of the encapsulated electrophoretic medium, and the method further comprises removing the remaining portion (250) of the encapsulated electrophoretic medium from the layer (130) of the encapsulated electrophoretic medium. [Brief explanation of the drawings]

[0019] [Figure 1] FIG. 1 shows a side view of a double peel stack of encapsulated electrophoretic media.

[0020] [Figure 2] FIG. 2 illustrates the creation of patterned features of an encapsulated electrophoretic medium by cutting completely through the double peel stack of FIG.

[0021] [Figure 3] 3 is a top view showing various shapes that can be cut from a single sheet of dual release laminate. In practice, the shapes can be cut very close to each other so that little of the dual release laminate is wasted.

[0022] [Figure 4] Figure 4 shows the cut shapes after they have been removed from the double peel laminate.

[0023] [Figure 5] Figure 5 shows the cut shape affixed to the back conductor, in this case PET-ITO, after one of the two release layers has been removed from the patterned shape and an adhesive layer has been used to laminate the patterned shape to the back conductor.

[0024] [Figure 6] FIG. 6 shows a side view of a cutting shape affixed to a back conductor as in FIG.

[0025] [Figure 7]FIG. 7 shows a side view of FIG. 6 after the second release layer has been removed from the patterned features laminated to the back conductor.

[0026] [Figure 8] FIG. 8 illustrates a top transparent conductor coated with a doped transparent adhesive laminated to the structure of FIG.

[0027] [Figure 9] Figure 9 shows a side view of the completed patterned display containing the encapsulated electrophoretic medium. Importantly, the doped transparent adhesive is not sufficiently conductive to provide an electrical path between the top and bottom conductors. The doped transparent adhesive provides a smooth surface despite the gaps between the patterned encapsulated electrophoretic medium.

[0028] [Figure 10] Figure 10 shows a top view of a completed patterned display including an encapsulated electrophoretic medium. In embodiments in which the top and bottom conductors are light-transmitting, e.g., PET-ITO, the intervening spaces between the patterned encapsulated electrophoretic material are transparent. If the electrophoretic medium includes, for example, colored particles, the patterned areas can switch between colors. If the electrophoretic medium is of the shuttering type, the patterned display including the encapsulated electrophoretic medium can switch between a darkened state and a light-transmitting state.

[0029] [Figure 11] 11 shows an alternative embodiment of a patterned display containing an encapsulated electrophoretic medium in which the bottom electrode is interrupted with a laser cut that goes only through the bottom electrode, thereby creating two independently addressable segments, each containing multiple patterned electro-optic portions. Notably, each bottom electrode requires a separate lead for control, while only a single connection is required for the top electrode, which covers both segments.

[0030] [Figure 12] 12 shows an alternative method for creating a patterned display containing an encapsulated electrophoretic medium. In this method, a stencil (mask) is cut to correspond to the desired pattern of encapsulated electro-optic medium. The stencil is then placed over the bottom electrode, and a slurry of capsules containing electrophoretic particles in a non-polar fluid, for example, is slot or bar coated over the stencil, and the stencil can be removed after coating is completed.

[0031] [Figure 13] FIG. 13 is a top view of a back conductor patterned with an encapsulated electrophoretic medium after the stencil has been removed.

[0032] [Figure 14] FIG. 14 is a side view of FIG. 13 showing that an alternative method allows for the creation of patterned capsules without the need for a second adhesive layer.

[0033] [Figure 15] Figure 15 shows the addition of a top light-transmitting electrode and substrate such as PET-ITO to the patterned assembly of Figure 13. The light-transmitting electrode layer is affixed using a doped transparent adhesive that maintains the relative positions of the patterned electro-optic medium and the top light-transmitting electrode layer.

[0034] [Figure 16] FIG. 16 shows a side view of a completed patterned display containing an encapsulated electrophoretic medium using an alternative method of fabrication.

[0035] [Figure 17]FIG. 17 illustrates the addition of one or more barrier layers that may be used to reduce water vapor transport into a patterned display containing an encapsulated electrophoretic medium, or to reduce damage caused by UV light, or to provide mechanical protection, or some combination thereof. DETAILED DESCRIPTION OF THE INVENTION

[0036] Detailed Description The present invention describes a method for forming a patterned display comprising isolated portions of an encapsulated electrophoretic medium, and a patterned display comprising the resulting encapsulated electrophoretic medium portions. See, for example, FIG. 5. When the resulting encapsulated electrophoretic medium portions are placed between two continuous light-transmitting electrodes, a display is created that allows a viewer to look through a portion of the display while receiving information from the encapsulated electrophoretic medium portion of the display. See, for example, FIGS. 9 and 10. Additionally, when the display is placed against a secondary surface or used to conceal an object, areas of the display are transparent (and optionally flexible), so that the transparent areas of the display will take on the appearance of the surface or object behind the display. (For confirmation, a "continuous optically transparent electrode" spans both the first and second portions of the encapsulated electrophoretic medium, with a gap between the first and second portions (see Figure 9).) In some embodiments, portions of the encapsulated electrophoretic medium may transition between light reflecting and light transmitting (i.e., variable transmission), while in other embodiments, portions of the encapsulated electrophoretic medium may transition between light absorbing and light transmitting. The encapsulated electrophoretic medium may include one, two, three, four, or more different types of electrophoretic particles.

[0037] In one embodiment, a patterned display including an encapsulated electrophoretic medium is formed from a double release laminate 100 of the type described in U.S. Patent No. 7,561,324 (incorporated by reference in its entirety). Such a structure is depicted in FIG. 1 , which shows a first release sheet 110, a first adhesive layer 115, a second release sheet 120, and a second adhesive layer 125. Disposed between first release sheet 110 and first adhesive layer 115 and second release sheet 120 and second adhesive layer 125 is a layer 130 of encapsulated electrophoretic medium. Layer 130 of encapsulated electrophoretic medium may be any of the types discussed above and may include a first type of electrophoretic particles 142 and a second type of electrophoretic particles 145 disposed in a non-polar solvent 147. Additionally, it should be understood that the electrophoretic medium may include one, two, three, four, five, or six charged particles that migrate toward or away from the electrodes in the presence of an applied electric field. In some embodiments, the electrophoretic medium is shuttering-type in that it has a first mode in which pigments are distributed throughout the container (e.g., microcapsules or microcells) to create a darkened state, and a second mode in which the pigments are collected in a smaller volume, reducing the amount of transmitted light absorbed and thereby providing a light-transmitting medium. Using the techniques described herein, it is also possible to include a mixture of patterned electro-optical materials, such as a black and white switching medium in a first portion of the encapsulated electrophoretic medium and a blue and white switching medium in a second portion of the encapsulated electrophoretic medium. It is also possible to mix different types of electrophoretic media, such as a black and white switching patterned portion and a shuttering switching portion. In some embodiments, the patterned capsules or partitioned microprocesses may additionally be colored, for example, using inkjet printing, before an additional conductive layer is adhered to the capsules. In some embodiments, different portions of the encapsulated electrophoretic medium contain the same type of electrophoretic particles. In some embodiments, different portions of the encapsulated electrophoretic medium contain different types of electrophoretic particles.

[0038] To create the encapsulated electrophoretic display of the present invention, the dual release laminate 100 can be patterned to create a first portion 220 of encapsulated electrophoretic medium and a second portion 240 of encapsulated electrophoretic medium, as shown in FIG. 2 . Patterning can be done, for example, using a laser, scissors, a knife, or a die, represented by a narrow wedge in FIG. 2 . The patterning may penetrate completely through the dual release laminate 100, as shown in FIG. 2 , or the patterning may only partially penetrate the dual release laminate 100, allowing the second release sheet 120 and second adhesive layer 125 to remain intact. Such precision cuts are best achieved with a laser cutting assembly that uses a wavelength absorbed by the pigments in the electrophoretic medium. Because the pigments are very dense, when the correct laser wavelength is selected, the pigments in the electrophoretic medium layer essentially stop the laser from progressing beyond the layer 130 of encapsulated electrophoretic medium. Such laser cutting systems may include, for example, Nd:YAG lasers operating at fundamental wavelengths in the near IR. Such laser cutting systems are available from Trotec Laser, Inc. (Plymouth, Michigan).

[0039] As shown in FIG. 3, various portions of the encapsulated electrophoretic medium can be cut from a single sheet of dual release laminate 100. One or more portions of remainder 250 may be removed from dual release laminate 100 to isolate first portion 220 of the encapsulated electrophoretic medium and second portion 240 of the encapsulated electrophoretic medium (and others, as appropriate), as shown in FIG. 4. When dual release laminate 100 is cut completely through both release layers, the resulting portion of encapsulated electrophoretic medium is essentially a double-sided sticker. In a subsequent step, second release sheet 120 of each isolated portion can be removed, and that portion of the encapsulated electrophoretic medium can be affixed to a sheet of PET-ITO, for example, using second adhesive layer 125. The PET-ITO base thus becomes second continuous light-transmitting electrode 310 and second light-transmitting substrate 320 of the claimed display, as shown in FIGS. 5 and 6. According to the present invention, first portion 220 of the encapsulated electrophoretic medium and second portion 240 of the encapsulated electrophoretic medium are separated by a gap, i.e., do not contact, as shown in Figure 6. The gap between first portion 220 of the encapsulated electrophoretic medium and second portion 240 of the encapsulated electrophoretic medium is typically at least 5 mm as measured parallel to the first continuous optically transmissive electrode and the second continuous optically transmissive electrode. In some cases, the gap is larger, e.g., at least 1 cm, e.g., at least 5 cm, e.g., between 1 cm and 10 cm.

[0040] After first portion 220 of encapsulated electrophoretic medium and second portion 240 of encapsulated electrophoretic medium are positioned on second continuous light-transmitting electrode 310, first release sheet 110 can then be removed from all of the portions of encapsulated electrophoretic medium, as shown in Figure 7. First continuous light-transmitting electrode 340 and first light-transmitting substrate 350 (e.g., a second sheet of PET-ITO) are coated with light-transmitting semi-conductive adhesive 360, and the assembly of first continuous light-transmitting electrode 340, first light-transmitting substrate 350, and light-transmitting semi-conductive adhesive 360 ​​is applied to the collection of first portion 220 of encapsulated electrophoretic medium, second portion 240 of encapsulated electrophoretic medium, second continuous light-transmitting electrode 310, and second light-transmitting substrate 320, as shown in Figure 8. The resulting electrophoretic display is shown in side profile in FIG. 9 and from above in FIG.

[0041] The optically transparent semiconductive adhesive 360 ​​can be made from several different optically transparent adhesives, such as acrylic and polyurethane, however, polyurethane is typically preferred. It is important that the optically transparent semiconductive adhesive 360 ​​be sufficiently conductive so as not to create a dielectric layer between the first continuous optically transparent electrode 340 and the layer of electrophoretic medium, but it must not be sufficiently conductive so as to create a short circuit path between the first continuous optically transparent electrode 340 and the second continuous optically transparent electrode 310, particularly in the gap between the first portion 220 of the encapsulated electrophoretic medium and the second portion 240 of the encapsulated electrophoretic medium. Therefore, the optically transparent semiconductive adhesive 360 ​​is typically doped with a salt or a charged polymer. The salt may be, for example, an inorganic salt, an organic salt, or a combination thereof. In one embodiment, the salt includes potassium acetate. In alternative embodiments, the salt may comprise a quaternary ammonium salt, for example, a tetraalkylammonium salt such as tetrabutylammonium chloride or hexafluorophosphate. Suitable optically transparent semiconductive adhesives 360 are available from Merck KGaA. Volume Resistivity of Optically Transparent Semiconductive Adhesives 360 rateis typically 1 x 10 5 ~1×10 12 It is ohm cm.

[0042] The present invention is not limited to the embodiment shown in Figures 9 and 10. Several variations are useful, and alternative methods can be used to fabricate such displays, as described below. In one embodiment, the final assembly of first portion 220 of encapsulated electrophoretic medium and second portion 240 of encapsulated electrophoretic medium, disposed between first continuous light-transmitting electrode 340 and second continuous light-transmitting electrode 310, can be made to switch optical states independently, as shown in Figure 11. It is possible to use different types of lasers or knives to cut through only one of the two continuous light-transmitting electrodes, thereby dividing the display into zones that can be controlled independently with different power connections. Using this method, for example, an assembly with eight different switching zones, each with multiple portions of encapsulated electrophoretic medium, can be created.

[0043] An alternative method of fabricating a display of the present invention involves using a mask, template, or stencil 410, as shown in FIG. 12. In this embodiment, the starting substrate is a second continuous light-transmitting electrode 310 on a second light-transmitting substrate 320; however, a stencil 410 is placed over the light-transmitting electrode 310, and a layer of encapsulated electrophoretic medium 130 is applied over the stencil, for example, using a bar coating method or spray coating of the electrophoretic medium. Once the stencil is removed, the first portion 220 of the encapsulated electrophoretic medium and the second portion 240 of the encapsulated electrophoretic medium remain on the second continuous light-transmitting electrode 310 on the second light-transmitting substrate 320, much like the structure shown in FIG. 5; however, the structure of FIG. 13 lacks the first release sheet 110 and first adhesive layer 115. Compare FIGS. 5 and 6 with FIGS. 13 and 14. Note that this alternative method of making an electrophoretic display only works with encapsulated electrophoretic media encapsulated in microcapsules, which can be coated as a slurry over a stencil or sprayed on using a spray gun (see U.S. Pat. No. 9,835,925, incorporated by reference in its entirety). Like the first method, the alternative method is completed with the addition of a first continuous optically transparent electrode 340 and a first optically transparent substrate 350 coated with an optically transparent semiconductive adhesive 360, a first portion 220 of encapsulated electrophoretic media, a second portion 240 of encapsulated electrophoretic media, a second continuous optically transparent electrode 310, and a second optically transparent substrate 320. Compare FIGS. 8 and 15. The final structure of FIG. 14 is very similar to the final structure using the first method; however, first adhesive layer 115 is missing from FIG. 16. Compare FIGS. 9 and 16. In some cases, removing the adhesive layer is optically beneficial because every layer of differential material presents a new scattering interface. In particular, the design of Figure 16 may have lower haze and better transmission when the electrophoretic medium is of the shuttering type.

[0044] The electrophoretic material layer of the present invention may comprise an electrophoretic medium. The electrophoretic medium may be compartmentalized in microcapsules or microcells. The electrophoretic material layer has an upper surface, a lower surface, and a perimeter. The upper and lower surfaces are on opposite sides of the electrophoretic material layer. The upper surface of the electrophoretic material layer is defined by a perimeter. The perimeter has a length and a width.

[0045] The electro-optical device of the present invention may include a first adhesive layer and / or a second adhesive layer. The first adhesive layer has an upper surface, a lower surface, and a peripheral surface. The adhesive can be made from a variety of materials, such as acrylic and polyurethane, however, polyurethane is typically preferred. The upper and lower surfaces are on opposite sides of the first adhesive layer. The term "length and width of the first adhesive layer" refers to the length and width dimensions of the upper surface of the first adhesive layer. The second adhesive layer has an upper surface, a lower surface, and a peripheral surface. The upper and lower surfaces are on opposite sides of the second adhesive layer. The term "length and width of the second adhesive layer" refers to the length and width dimensions of the upper surface of the second adhesive layer.

[0046] The electro-optical device of the present invention includes a backplane, which may be used interchangeably with the second electrode layer. The backplane has a top surface, a bottom surface, and a peripheral surface. The top surface and the bottom surface are on opposite sides of the backplane. The term "length and width of the backplane" refers to the length and width of the top surface of the backplane.

[0047] The term "active display area" refers to the area of ​​the viewing surface of an electrophoretic display on which a variable image can be displayed. A variable image of an electrophoretic display is an image that can be created as a result of application of an electric field across the electrophoretic material layer of the electrophoretic display.

[0048] In some embodiments, the electro-optic material is an electrophoretic medium that is compartmentalized in microcapsules. Alternatively, the electrophoretic medium may be compartmentalized in microcells. The electrophoretic medium may include electrophoretic particles in a non-polar liquid.

[0049] For example, some of the aforementioned E Ink patents and applications describe processes for manufacturing encapsulated electrophoretic displays, in which an encapsulated electrophoretic medium comprising microcapsules in a binder is coated onto a flexible substrate with an indium tin oxide (ITO) or similar conductive coating or adhesive bonded to a release sheet, i.e., as described above. In some embodiments, the conductive coating is the first light-transmitting electrode layer. Drying or curing of the microcapsule / binder coating forms an electro-optic material layer firmly adhered to the first light-transmitting layer. Microcapsules suitable for use with the present invention may include gelatin-acacia microcapsules as described in U.S. Patent Nos. 7,230,750 and 10,983,410 (both of which are incorporated by reference in their entireties). Alternative microcapsule materials include non-ionic polymers such as polyvinyl alcohol, as described in U.S. Patent Publication No. 2021 / 0191226 (incorporated by reference in their entireties). The binder is typically cured using heat or UV light and may be crosslinked as needed for the application. Suitable binders for use with encapsulated electrophoretic media include polyurethanes sold by companies such as Merck KGaA and acrylics sold by companies such as Sartomer (a division of Arkema). Further examples of suitable binders can be found in U.S. Pat. No. 9,777,201 (incorporated by reference in its entirety).

[0050] In an alternative embodiment, the encapsulated electrophoretic medium is encapsulated within a plurality of microcells. The microcells may be square, round, or polygonal, such as a honeycomb structure. The microcells are typically fabricated by micro-embossing a sheet of acrylic or methacrylic sheet material, as described in U.S. Pat. No. 6,930,818 (incorporated by reference in its entirety). Each microcell includes an opening spanned by a polymeric sealing layer. The polymeric sealing layer may be constructed from a variety of materials, such as acrylate, methacrylate, polycarbonate, polyvinyl alcohol, cellulose, poly(N-isopropylacrylamide) (PNIPAAm), poly(lactic-co-glycolic acid) (PLGA), polyethylene, polypropylene, or polystyrene. The encapsulated electrophoretic medium within the microcells may be prepared as a double peel-apart laminate, or the microcells may be bonded to a light-transmitting electrode layer on a light-transmitting substrate, such as PET-ITO.

[0051] The light-transmitting top (or bottom) conductive layer (electrode) may be carried on a light-transmitting substrate, preferably flexible, in the sense that the substrate can be manually wound around a 25 mm diameter drum without permanent deformation. The substrate is typically a polymeric film, usually having a thickness within the range of about 1 to about 25 mils (25 to 634 μm), preferably about 2 to about 10 mils (51 to 254 μm). The light-transmitting electrode may conveniently be a thin metal layer, e.g., aluminum or indium tin oxide (ITO), or a conductive polymer. Polyethylene terephthalate (PET) films coated with aluminum or ITO are commercially available, e.g., as "Aluminized Mylar" ("Mylar" is a registered trademark) from EI du Pont de Nemours & Company (Wilmington Del.), and such commercial materials may be used with good results in front plane lamination. However, the optically transparent substrate need not be flexible: it may be, for example, glass or a transparent rigid polymer such as cross-linked acrylic or another rigid optically transparent polymer.

[0052] Assembly of an electro-optical device using such a front plane laminate may be achieved by removing the release sheet from the front plane laminate and contacting the backplane with the first adhesive layer under conditions effective to adhere the first adhesive layer to the backplane, thereby affixing the first adhesive layer, electrophoretic medium, and conductive layer to the backplane. This process is well suited to mass production, as the front plane laminate is typically produced in large quantities using roll-to-roll coating techniques and can then be cut into pieces of any size required for use with a specific backplane. An edge seal composition is then dispensed around the pieces to create a conductive edge seal after the edge seal composition dries or cures. The device is typically exposed to a humidity conditioning step at a temperature and relative humidity prior to edge sealing.

[0053] A patterned display containing an encapsulated electrophoretic medium may additionally include an edge seal. The edge seal composition may include a polymer or a combination of polymers. Drying or curing the edge seal composition forms the edge seal of the device. Non-limiting examples of polymers include polyurethane, epoxy, dimethylpolysiloxane, polyacrylate, polymethacrylic acid, polycarbonate, polyvinyl chloride, polystyrene-alkylene copolymer, polyamide, polyester, polystyrene, polyethylene, polypropylene, polyisobutylene, poly(ethylene terephthalate), poly(ethylene naphthalate), ethylene-vinyl alcohol copolymer, poly(ethylene-co-norbornene), styrene-isobutylene-styrene block copolymer, and mixtures thereof. The edge seal composition may also include conductive fillers such as metal particles, metal nanoparticles, metal wires, metal nanowires, metal nanofibers, conductive carbon black particles, carbon nanotubes, graphite, and combinations thereof. The edge seal composition may also include a conductive polymer. Non-limiting examples of conductive polymers are poly(3,4-ethylenedioxythiophene) polystyrene sulfonate (PEDOT-PSS), polyacetylene, polyphenylene sulfide, polyphenylene vinylene, and combinations thereof. The display of the present invention may additionally include a barrier layer 510, as shown in FIG. 17, which is typically a light-transmitting sheet that is impermeable to water (i.e., has a very low WVTR). The barrier layer may also protect against physical damage, for example, resulting from contact with a sharp object. Suitable barrier materials include polyethylene, polyimide, glass, and vapor-deposited ceramics such as indium tin oxide and silicon nitride. An additional layer of optically clear adhesive (OCA) may be used to adhere the barrier layer 510 to the first light-transmitting substrate 350.

[0054] It will be apparent to those skilled in the art that numerous changes and modifications can be made in the specific embodiments of the invention described above without departing from the scope of the invention. Accordingly, the whole of the foregoing description is to be interpreted in an illustrative sense, and not in a restrictive sense.

Claims

1. 1. An electrophoretic display, comprising: a first continuous light-transmitting electrode (340) disposed on a first light-transmitting substrate (350); a second continuous light-transmitting electrode (310) disposed on a second light-transmitting substrate (320); a first portion (220) of an encapsulated electrophoretic medium disposed between the first continuous light-transmitting electrode (350) and the second continuous light-transmitting electrode (310); a second portion (240) of encapsulated electrophoretic medium disposed between the first continuous light-transmitting electrode and the second continuous light-transmitting electrode; Equipped with the first portion (220) of the encapsulated electrophoretic medium does not contact the second portion (240) of the encapsulated electrophoretic medium; application of an electric field between the first continuous light-transmitting electrode and the second continuous light-transmitting electrode (310) causes a change in the optical state of both the first portion (220) of the encapsulated electrophoretic medium and the second portion (240) of the encapsulated electrophoretic medium; The electrophoretic display further comprises a light-transmitting semi-electrically conductive adhesive (360) having a volume resistivity of 1×10 5 to 1×10 12 ohm-cm disposed between the first continuous light-transmitting electrode and the second continuous light-transmitting electrode.

2. 2. The electrophoretic display of claim 1, wherein the first portion of the encapsulated electrophoretic medium includes electrophoretic particles and the second portion of the encapsulated electrophoretic medium includes electrophoretic particles, and the electrophoretic particles included in the first portion of the encapsulated electrophoretic medium and the electrophoretic particles included in the second portion of the encapsulated electrophoretic medium have identical optical properties.

3. 10. The electrophoretic display of claim 1, wherein a first portion (220) of the encapsulated electrophoretic medium includes a first type of electrophoretic particles (142) and a second portion (240) of the encapsulated electrophoretic medium includes a second type of electrophoretic particles (145), the first and second types of electrophoretic particles (142, 145) having different optical properties.

4. 4. An electrophoretic display as described in any one of claims 1 to 3, wherein the first portion (220) of the encapsulated electrophoretic medium and the second portion (240) of the encapsulated electrophoretic medium both contain more than one type of electrophoretic particles (142, 145) having different optical properties.

5. 10. The electrophoretic display of claim 1, wherein the first portion of the encapsulated electrophoretic medium is encapsulated in microcapsules, the microcapsules being held together with a polymeric binder.

6. 6. The electrophoretic display of claim 5, wherein the microcapsules comprise gelatin or polyvinyl alcohol.

7. 7. The electrophoretic display of claim 6, wherein the polymeric binder comprises a polyurethane or an acrylate.

8. 10. The electrophoretic display of claim 1, wherein the first portion of the encapsulated electrophoretic medium is encapsulated within a microcell and sealed with a polymeric sealing layer.

9. 9. The electrophoretic display of claim 8, wherein the microcells comprise an acrylic or (meth)acrylic polymer.

10. The electrophoretic display of claim 1, wherein the optically transparent semi-electrically conductive adhesive (360) having a volume resistivity of 1×10 5 to 1×10 12 ohm-cm comprises polyurethane doped with an inorganic salt.

11. An electrophoretic display as described in claim 10, wherein the optically transparent semi-electrically conductive adhesive (360) having a volume resistivity of 1x105 to 1x1012 ohm-cm comprises polyurethane doped with an inorganic salt at a concentration of 2% (wt:wt) to 0.05% (wt:wt).

12. An electrophoretic display as described in claim 1, 10 or 11, wherein the optically transparent semi-electrically conductive adhesive (360) having a volume resistivity of 1x105 to 1x1012 ohm-cm separates the first portion (220) of the encapsulated electrophoretic medium and the second portion (240) of the encapsulated electrophoretic medium.

13. 2. The electrophoretic display of claim 1, wherein the first portion (220) of the encapsulated electrophoretic medium and the second portion (240) of the encapsulated electrophoretic medium are separated by a distance of at least 5 mm when measured parallel to the first continuous light-transmitting electrode and the second continuous light-transmitting electrode.

14. 1. A method of making an electrophoretic display, comprising: providing a layer (130) of encapsulated electrophoretic medium disposed between a first release sheet (110) and first adhesive layer (115) and a second release sheet (120) and second adhesive layer (125), wherein the first release sheet (110) is on the first adhesive layer (115) and the second adhesive layer (125) is on the second release sheet (120); patterning the layer of encapsulated electrophoretic medium (130) by cutting through the first release sheet (110), the first adhesive layer (115), and the layer of encapsulated electrophoretic medium (130) to create a first portion of encapsulated electrophoretic medium (220) and a second portion of encapsulated electrophoretic medium (240); disposing the first portion (220) of the encapsulated electrophoretic medium and the second portion (240) of the encapsulated electrophoretic medium between a first continuous optically transparent electrode (340) disposed on a first optically transparent substrate (350) and a second continuous optically transparent electrode (310) disposed on a second optically transparent substrate (320) (320) such that the first portion (220) of the encapsulated electrophoretic medium does not contact the second portion (240) of the encapsulated electrophoretic medium; A method comprising:

15. The method of claim 14, wherein an optically transparent semi-electrically conductive adhesive (360) having a volume resistivity of 1x105 to 1x1012 ohm-cm is disposed between the first continuous optically transparent electrode (340) and the second continuous optically transparent electrode (310), separating the first portion (220) of the encapsulated electrophoretic medium from the second portion (240) of the encapsulated electrophoretic medium.

16. 16. The method of claim 14 or 15, wherein the first portion (220) of the encapsulated electrophoretic medium and the second portion (240) of the encapsulated electrophoretic medium are separated by a distance of at least 5 mm when measured parallel to the first continuous optically transparent electrode (340) and the second continuous optically transparent electrode (310).

17. 15. The method of claim 14, wherein patterning comprises cutting through the second release sheet (120) and the second adhesive layer (125).

18. 18. The method of claim 14 or 17, wherein the patterning is performed using a laser, scissors, a knife, or a die.

19. 15. The method of claim 14, wherein the patterning step further comprises creating a remaining portion (250) of the encapsulated electrophoretic medium, and the method further comprises removing the remaining portion (250) of the encapsulated electrophoretic medium from the layer (130) of the encapsulated electrophoretic medium.