Surface finishing molding materials

Abstract

A molding material comprising: (a) a structural reinforcement layer comprising a fibrous reinforcing material, optionally combined with a second resin composition; and (b) a surface reinforcement layer for contacting a mold or tool surface, comprising a first nonwoven fibrous carrier combined with a first resin composition containing a rheology modifier and a curing agent, the first resin composition providing the outer mold or tool contact surface of the molding material. The molding material can be cured to form a molded article having a high-quality surface finish that requires minimal preparation before painting and / or application for its intended use. The molded article may be provided with a sacrificial discontinuity indicator means to aid in the uniform removal of a portion of the surface reinforcement layer of the molded article for a particular application.

Description

[Technical Field]

[0001] The present invention relates to a molding material that provides an enhanced surface finish, as well as a method for preparing the molding material, a method for preparing a molded article by curing such a molding material, and a molded article obtained by such a method. In particular, the present invention relates to a fiber-reinforced composite molding material that can be cured at low temperatures and includes a surface finish layer for providing a molded article having a high-quality surface finish that requires only minimal preparation after curing, although it is not limited to use in the wind turbine and automotive industries in particular. [Background technology]

[0002] Composite materials offer well-supported advantages over conventional building materials, particularly in their ability to provide superior mechanical properties at very low material densities. As a result, the use of such composite materials is widespread in many industries, including aerospace, automotive, marine, and wind turbine industries.

[0003] Prepregs containing fiber arrays impregnated with thermosetting resins such as epoxy resins are widely used in the production of such composite materials. Typically, several layers of such prepregs are “layup” as desired, and the resulting assembly or laminate is placed in a mold and cured by exposure, usually to high temperatures and sometimes under pressure, to produce a cured composite laminate. However, if such composite materials are not surface-treated, they often cure with an inadequate surface finish, which can manifest as a rough, wavy, or pinhole surface, or as narrow grooves on the surface of the molded structure where adjacent prepreg layers overlap to ensure a continuous layer. This tendency to form an uneven surface seems to be closely related to the roughness of the underlying reinforcing material, and the problem becomes more pronounced the rougher the reinforcing material. This can be particularly problematic when rough reinforcing material is used for structural rigidity, such as in the manufacture of automotive body panels requiring a Class A finish, or wind turbine blades, where a smooth surface finish is desired.

[0004] There are several different techniques for improving the surface finish of fiber-reinforced composite molded materials and molded articles manufactured from such materials. For example, manufacturers of large composite structures such as wind turbine blades typically use an in-mold gel coat or process coat that acts as a surface finish layer that can be finished after demolding by filling defects, sanding to remove release agents and minor imperfections, and "keying in" to the surface, and then applying (coating) a topcoat layer of paint to protect the structure from environmental conditions. Essentially, such a gel coat process involves adhering a fluid composition to the inner surface of a mold, then partially curing it to form a gel layer, and placing the prepreg assembly on the gel layer before curing. During curing, the prepreg and gel coat fuse to each other, which generally results in a smooth surface on the formed composite. However, this process is very labor-intensive in that it requires an initial curing step and tends to result in a gel layer of uneven thickness. Furthermore, the layer needs to be relatively thick (e.g., 0.3 mm on average) to cover defects, which can lead to an undesirable weight increase.

[0005] Other methods typically involve surface finishing films incorporated into the mold engagement surface of a composite molding material, which typically includes a thermosetting resin supported on a nonwoven mat carrier. International Publication No. 2008 / 007094(A2) discloses, for example, a composite material assembly comprising a surface reinforcing layer including at least one layer of fibers having a length-to-width aspect ratio greater than 5:1, and b) a structural layer including at least one reinforcing fiber and at least one polymer matrix. This document discloses that the fibers used in the surface reinforcing layer may be prepared by segmenting the fibers longitudinally and then forming a film or veil from the segmented fibers, resulting in a much denser veil structure and increased fiber density for the same weight. This document discloses that a denser veil structure provides an improved surface finish in terms of both appearance and smoothness.

[0006] Furthermore, manufacturers of large composite components such as wind turbine blades desire that all traces of release agents, used to coat molds to facilitate the removal of cured composite components and subsequently transferred onto the surface of the cured component, be reliably removed to ensure good adhesion of the final topcoat layer of paint to the composite surface. Such traces of release agents are typically removed using a sanding process. However, one problem found when surface finishing films are incorporated into the mold engagement surfaces of composite molding materials is that end users sand the laminate containing the surface finishing film to such an extent that it damages the structure and creates the very same pinholes on the surface that the finishing film was supposed to prevent. During sanding, end users typically look for a change in the level of surface gloss as an indicator of sufficient sanding. Surfaces produced by the use of such finishing films appear to be more resistant to sanding than before, and as a result, end users tend to use more aggressive sanding methods, which seems to lead to damage.

[0007] One approach to overcome this problem was to improve the sandability of the surface reinforcement layer so that any traces of the release agent could be easily and reliably removed under typical sanding conditions. For example, International Publication No. 2010 / 046682(A1) discloses a prepreg assembly comprising resin and fibers, including an upper curable resin surface layer, wherein upon curing of the assembly, the upper surface layer has a sandability of at least 0.30 mg / cycle over 200 cycles, as measured according to ASTM D4060 using a Taber 5151 abrasion tester fitted with an H18 wheel and a 1.0 kg weight. In a preferred embodiment, the upper curable resin surface layer comprises at least 10.0% by weight of fine particle material in the form of glass spheres having a particle size of 5 to 50 μm, providing the required sandability.

[0008] Other approaches have addressed the slippage problem of fiber-reinforced composite molding materials when laid up in a mold, which can result in surface irregularities on the molded part after curing. This problem can be particularly applicable when adjacent layers of the reinforcement or prepreg overlap within the mold, depleting the resin in the overlapping area and potentially forming narrow depressions along the overlap seam during curing. For example, International Publication No. 2017 / 021147 (A1) discloses a molding material comprising a layer of fibrous material in a curable resin matrix provided on at least one surface with a surface finishing film containing an adhesive resin, where a veil is provided on the surface of the finishing film separated from the molding material and perforations are formed in the veil such that the adhesive resin of the surface finishing film can pass through the veil during the molding operation. This document discloses that the presence of such perforations in the veil provides a slight adhesiveness between the molding material and the mold surface with a small amount of the adhesive resin, thereby enabling the molding material to be held in place.

[0009] All of the various approaches for improving the surface finish of fiber-reinforced composite molding materials and molded articles made from such materials as described above have some drawback, such as the need to cure an additional gel coat layer within the mold, or the need to use a surface finish layer containing longitudinally segmented fibers, or the need to include additional glass spheres to improve the ease of sanding of the surface finish layer, or the need to perforate any fiber veils within the surface finish layer, which can affect the resin flow and surface finish. SUMMARY OF THE INVENTION PROBLEMS TO BE SOLVED BY THE INVENTION

[0010] The present invention aims to overcome at least some of the aforementioned problems and / or generally provide an improvement. MEANS FOR SOLVING THE PROBLEMS

[0011] According to the present invention, there are provided a molding material, a method for preparing the same, a method for preparing a molded article by curing such a molding material, and a molded article obtained by a method as described below or as defined in any one of the appended claims.

[0012] Thus, in a first aspect of the present invention, there is provided a surface strengthening layer for contacting the surface of a mold or tool, comprising: (a) a structural reinforcing layer containing a fibrous reinforcing material; and (b) a first non-woven fiber carrier combined with a first resin composition containing a rheology modifier and a curing agent, wherein the first resin composition provides an external mold or tool contact surface of the molding material.

[0013] The first resin composition is at least partially impregnated into the first non-woven layer, and in a preferred embodiment, is completely impregnated into the first non-woven layer. However, the essential feature of the present invention is that a sufficient amount of the first resin composition is present on the surface of the first non-woven layer away from the structural reinforcing layer to form a continuous layer on the external mold or tool contact surface of the molding material.

Brief Description of the Drawings

[0014] [Figure 1] FIG. 1 shows a partially sanded molding material according to a preferred embodiment of the present invention.

Embodiments for Carrying Out the Invention

[0015] In the context of the present invention, the term "molding material" refers to a fiber-reinforced composite material that can be laid up with other such materials within a mold or tool and cured to form a composite part that takes the shape of the mold or tool. Using such molding materials, many various components can be prepared, including but not limited to components of a wind turbine, including nacelles, propellers, and rotor blades.

[0016] The structural reinforcement layer can take many forms. Typically, the molding material according to the present invention includes several structural reinforcement layers, but in some applications, a single layer may suffice.

[0017] The fibrous reinforcing material may be in the form of a sheet, a continuous mat, or a continuous filament. In other embodiments, the fibrous reinforcing material includes short fibers, such as a chopped strand mat. The fibrous reinforcing material may be in the form of multiple fiber tows, each tow containing multiple fiber filaments forming a tow. The tows can be sewn or woven to form a fabric. The fibers may consist of natural materials such as cotton, flax, hemp, wool, or silk; or semi-synthetic materials such as rayon, viscose, or modal; or synthetic materials such as carbon, polyester, minerals, nylon, acrylic, glass, or aramid (aromatic polyamide). In preferred embodiments, the fibrous reinforcing material includes carbon fibers or glass fibers.

[0018] In some embodiments, the fibrous reinforcing material is in the form of a woven fabric. In other embodiments, the fibrous reinforcing material includes a unidirectional (UD) woven fabric in which the majority of the fibers, rovings, or tows present in the fabric extend in only one direction, although a small number of fibers, rovings, or tows may extend in a different direction from the majority, for example, as cross-stitching to maintain the majority unidirectional alignment. The fibers, rovings, or tows of a unidirectional woven fabric can be held in a straight line by several different methods, including weaving, sewing, and bonding. Thus, such a unidirectional woven fabric may be woven or nonwoven. In further embodiments, the fibrous reinforcing material includes a unidirectional woven fabric combined with a biaxial or multiaxial woven fabric or mat in which either component may be woven or nonwoven.

[0019] Woven and nonwoven fabrics suitable for use in composite materials are commercially available from specialized manufacturers, including, but are not limited to, Chomarat Textiles Industries (Esher, Surrey, UK), Hexcel Reinforcements UK Limited (Narborough, Leicestershire, UK), and Zhenshi Group Hengshi Fibreglass Fabrics Co., Ltd. (Tongxiang Economic Development Zone, Jiaxing, Zhejiang, 314500, China). In one embodiment, the woven or nonwoven fabric is a carbon fiber or glass fiber fabric such as BB200, BB600, or BB1200, where BB1200 is, for example, 1200 g / m². 2 This refers to a biaxial glass fabric having a basis weight (grammage).

[0020] Hybrid or mixed fiber systems may also be considered. The use of cracked (i.e., tear-cut) or selectively discontinuous fibers may be advantageous in facilitating the layup of the molding material according to the present invention and improving its molding ability.

[0021] The basis weight of fibrous reinforcing materials is typically 40-4,000 g / m². 2 In a preferred embodiment, the basis weight of the fibers is preferably 100 to 2,500 g / m². 2 more comfortably 150~2,000g / m² 2 It is within the range of [the specified range].

[0022] In structural reinforcement layers, or structural reinforcement layers with two or more layers, the fibrous reinforcing material is typically a heavy, non-crimped fabric such as glass fiber. Fibers with a density of 68 to 2400 tex (grams per kilogram of yarn) are particularly suitable for glass reinforcing materials.

[0023] The surface strengthening layer of the molding material according to the present invention includes a first non-woven fiber carrier. In the context of the present invention, the non-woven fiber carrier means any non-woven fabric material that is air-permeable and resin-permeable. A suitable non-woven fiber carrier is lightweight, preferably less than 100 g / m 2 2, but preferably supports a layer of resin and has sufficient robustness to withstand processing in the method of the present invention. The non-woven fiber carrier may include continuous fibers or discontinuous fibers. In one embodiment, the first non-woven fiber carrier includes a veil (sometimes known as fleece). In the context of the present invention, the term "veil" refers to a thin and lightweight (i.e., 100 g / m 2 or less in basis weight) porous non-woven fibrous reinforcing material. In a preferred embodiment, the first non-woven fiber carrier is composed of fibers of a thermoplastic material, and preferably, the fibers are bonded to each other using an organic binder to impart structural integrity to the material. In a particular embodiment, the thermoplastic material includes polyester, or an aliphatic or semi-aromatic polyamide such as nylon or polyester fibers. In another embodiment, the non-woven fiber carrier includes a veil formed from a blend of thermoplastic fibers such as a mixture of polyester fibers and nylon fibers. The organic binder is typically present in an amount of 1 to 10% by weight based on the total weight of the first non-woven fiber carrier. The purpose of the first non-woven fiber carrier is to act as a support or carrier for the first resin composition and to control the way in which the first resin composition interacts with the surface of the mold or tool in order to provide a good surface finish. In one embodiment, the first non-woven fiber carrier has an openness of 1 to 10%, preferably 2 to 9%, and / or an average opening area of 75 to 350 μm 2 . In a preferred embodiment, the first non-woven fiber carrier has a basis weight in the range of 1 to 80 g / m 2 , preferably 5 to 50 g / m 2 , more preferably 10 to 40 g / m 2 . In one embodiment, the first non-woven fiber carrier has an air permeability of about 2,300 L / m at an applied pressure of 200 Pa 2It has an air permeability of 1 / second. The air permeability of the nonwoven fiber carrier can be measured by ASTM D737-18: Standard Test Method for Air Permeability of Textile Fabrics. A suitable thermoplastic fiber bale is the one commercially available from Technical Fibre Products Limited (Burnside Mills, Kendal, Cumbria, UK) under the trade name Optiveil® T2761-00.

[0024] The surface reinforcement layer comprises a first resin composition in addition to the first nonwoven fiber carrier. The first resin composition generally includes thermosetting resins such as polyester resins, polyurethane resins, polyurethane / polyurea resins, phenol-formaldehyde resins, urea-formaldehyde resins, vinyl ester resins, cyanate ester resins, polyimide resins, or epoxy resins. In one embodiment, the first resin composition is a thermosetting resin composition, preferably an epoxy resin composition comprising an epoxy resin or a blend of epoxy resins. Suitable epoxy resins include the M9 and M79 series epoxy resins available from Hexcel Composites Limited (Duxford, Cambridgeshire, UK).

[0025] In one embodiment, the first resin composition comprises an epoxy resin having an epoxy equivalent weight (EEW) in the range of 150 to 1,500, preferably 150 to 1,250, preferably 150 to 1,000, preferably 150 to 750, preferably 150 to 500, preferably 200 to 500, preferably 200 to 450, preferably 250 to 350, or any combination thereof.

[0026] The first resin composition includes at least one curing agent to facilitate the crosslinking of the resin and the curing of the molded material, particularly at temperatures below 100°C. In the context of the present invention, the term “curing agent” is understood to include any curing agent and / or accelerator that can achieve or increase the crosslinking rate of the first resin composition. Such curing agents and / or accelerators used in the present invention are well known in the art. In one embodiment, the first resin composition includes a latent curing agent which is a substituted urea. Suitable substituted urea curing agents include a series of materials available from AlzChem Group AG (Trostberg, Germany) under the trade name Dyhard®, including UR200, UR300, UR400, UR500, UR600, and UR700, and a series of materials available from Emerald Performance Materials (Moorefield, New Jersey, USA) under the trade name Omicure®, including U-24M, U-35M, U-52, U-52M, U-210, U-210M, U-405, U-405M, U-410M, and U-415M. In further embodiments, the curing agent may include a dicyandiamide curing agent in combination with the substituted urea. The curing agent may be present in any amount suitable for curing the resin under selective conditions. In some embodiments, the curing agent is present in amounts of 1% to 25% by weight, 1% to 20% by weight, 1% to 15% by weight, 1% to 10% by weight, or 2% to 8% by weight, or any combination thereof, relative to the total weight of the resin composition.

[0027] It is important that the first resin composition contains a rheology modifier. In the context of the present invention, the term "rheology modifier" is used to refer to a compound or substance that can impart non-Newtonian rheological properties to a material such as the first resin composition. In the present invention, the rheology modifier should increase the minimum viscosity of the resin under shear compared to an un-viscosity-modified resin, and should increase the viscosity of the resin under non-shear compared to an un-rheology-modified resin by a greater amount. This can be measured using the shear sweep viscosity method. Suitable conditions for the shear sweep viscosity method are 0.1 to 100 s. -1 A 25 mm parallel plate with a 1 mm gap is set to provide a shear rate and a temperature of 60°C. In the present invention, the rheology modifier is preferably a first resin composition that, when measured as described above, has a shear rate of 60° and a temperature of 0.1 s -1 Viscosity of 200-1000 Pa.s, and 0.1s -1 Viscosity of 25% or less at 60°C and 100s -1 It has viscosity at 60°C and 100s. -1 The viscosity is selected to be 25 Pa.s or higher.

[0028] The shear sweep viscometer can be performed using any viscometer suitable for providing the above conditions, for example, using the TA HR-2 Discovery Hybrid Rheometer manufactured by TA Instruments (Newcastle, Delaware, USA).

[0029] Suitable rheological modifiers include treated and untreated grades of fumed silica, such as hydrophobic silica. Hydrophilic silica can also be used, but thixotropic silica is preferred. Pee booth Ta andThey can be used in combination. Organic affinity phyllosilates can also be used. Suitable silicas include Aerosil® R202, available from Evonik Resource Efficiency GmbH (Germany), and Cab-O-Sil® TS720, available from Cabot Corporation (Alpharetta, Georgia, USA). A suitable organic affinity phyllosilate is Garamite-7305, available from BYK (Altana Group). A suitable thixotropy booster is available from BYK-Chemie GmbH (Wesel, Germany) under the trade name Rheobyk®. In one embodiment, the rheology modifier is a hydrophobic fumed silica such as Aerosil® R202.

[0030] The rheology modifier may optionally be present in combination with a thixotropy booster in an amount of 1 to 20% by weight relative to the total weight of the first resin composition. In preferred embodiments, the rheology modifier may be present in an amount of 1 to 15% by weight, 1 to 12% by weight, 1 to 10% by weight, 2 to 10% by weight, 3 to 9% by weight, 4 to 8% by weight, or any combination thereof, relative to the total weight of the first resin composition.

[0031] The inventors have found that using a lightweight, highly-closed microfiber veil in combination with a rheology-modified epoxy resin composition having the viscosity characteristics described above provides a surface-reinforced layer with good gap-filling properties, significantly reduces pinhole formation, and reduces or completely eliminates narrow grooves that occur when layering molding materials during layup.

[0032] The first resin composition may also contain other components such as reinforcing agents, particulate fillers (e.g., microballoons, glass spheres, talc, etc.), dyes, defoamers, or pigments.

[0033] The first resin composition is provided on the external mold or tool contact surface of the molding material, i.e., on the surface of the molding material that will come into contact with the surface of the mold or tool when the molding material is laid up and ready to cure. For example, in its simplest form, the molding material includes a layer of the first resin composition on which a nonwoven fiber carrier, such as a lightweight surface veil, is placed, together forming a surface reinforcing layer, and on the surface reinforcing layer is a layer of fibrous reinforcing material, such as a heavy glass fiber mat, which forms a structural reinforcing layer. In this case, the layer of the first resin composition is generally a thick layer with a high basis weight. This is because the amount of the first resin composition needs to be sufficient to impregnate not only the surface veil but also the fibrous reinforcing layer once the layer has been consolidated.

[0034] In another embodiment, the structural reinforcing layer exists in combination with a second resin composition. In this case, the molding material may include a layer of the first resin composition on which a lightweight surface veil is placed, a layer of heavy fibrous reinforcing material on which the surface reinforcing layer is placed, and finally a layer of the second resin composition, the last two layers of which form the structural reinforcing layer. In a further embodiment, the layer of the second resin composition may be between the fibrous reinforcing material and the nonwoven fiber carrier layer. In any case, the second resin composition may be partially or completely impregnated into the structural reinforcing layer after compaction of the layer to form, for example, a semipreg or prepreg structure.

[0035] Any of the resin compositions discussed with respect to the first resin composition are suitable for use as the second resin composition. However, since the purpose of the second resin composition is primarily structural rather than providing gap-filling properties, it is not essential that the second resin composition contain a rheology modifier. However, the second resin composition may contain a rheology modifier as needed. In one preferred embodiment, the second resin composition is the same as the first resin composition but does not contain a rheology modifier, and in another preferred embodiment, the second resin composition is the same as the first resin composition but contains a rheology modifier.

[0036] In one embodiment, the molding material according to the present invention further includes a second nonwoven fiber carrier between the structural reinforcing layer and the surface reinforcing layer. The second nonwoven fiber carrier may be the same as the first nonwoven fiber carrier, but the second nonwoven fiber carrier preferably has a larger basis weight than the first nonwoven fiber carrier.

[0037] The second nonwoven fiber carrier may include continuous or discontinuous fibers. In one embodiment, the second nonwoven fiber carrier includes a bale (sometimes known as fleece). The second nonwoven fiber carrier typically consists of nonwoven fibers of glass, carbon, polyester, polyamide, aramid (aromatic polyamide), or a combination thereof, which are bonded together using an organic binder to impart structural integrity to the material. Preferably, the second nonwoven fiber carrier includes glass fleece. The organic binder is typically present in an amount of 1 to 10% by weight relative to the total weight of the second nonwoven fiber carrier. Generally, the second nonwoven fiber carrier has a slightly higher basis weight or surface density than the first nonwoven fiber carrier. In a preferred embodiment, the second nonwoven fiber carrier has a density of 20 to 100 g / m². 2 Preferably 20-90 g / m² 2 More preferably 30-80 g / m² 2 Furthermore, a more comfortable 30-60 g / m 2 This is a nonwoven bale having a basis weight of . Suitable nonwoven glass mats or fleeces include, but are not limited to, Evalith® ST-3022, S4030 and S5030, which are commercially available from Johns Manville (Denver, Colorado, USA) under the trade name Evalith®, and, but are not limited to, Changhai® S-SM30, S-SM50, S-HM30 and S-HM50, which are commercially available from Taishan Fiberglass Inc. (Economic Development Zone, Tai'an, Shandong, China) under the trade name Changhai®.

[0038] The presence of a second nonwoven fiber material helps prevent "print-through" from the fiber reinforcing material within the structural reinforcing layer from appearing on the surface of the molded material after curing, and ensures that sufficient amounts of the second resin composition are retained within the surface reinforcing layer during curing, thereby avoiding the formation of narrow grooves or other surface irregularities due to resin deficiency. The second nonwoven fiber material, like the first nonwoven fiber material, may also help prevent bubble formation or assist in the dissipation of bubbles by the first, second, or third resin composition.

[0039] A second nonwoven fiber carrier may exist in combination with a third resin composition. The third resin composition may be placed on both sides of the second nonwoven fiber carrier to assist in the adhesion of the second nonwoven fiber carrier to the first nonwoven fiber carrier and / or structural reinforcing layer. After compaction, the third resin composition may partially or completely impregnate the second nonwoven fiber carrier.

[0040] A second nonwoven fiber carrier, if present, may optionally be provided attached to the fibrous reinforcing material of a structural reinforcing layer, for example, these layers may be pre-attached by resin material or stitching.

[0041] Any of the resin compositions discussed with respect to the first or second resin compositions are suitable for use as the third resin composition. However, it is not essential that the third resin composition contains a rheology modifier, but it may contain one if necessary. In one preferred embodiment, the third resin composition is the same as the first and / or second resin compositions but does not contain a rheology modifier, and in another preferred embodiment, the second resin composition is the same as the first and / or second resin compositions but contains a rheology modifier. Using the same resin composition as the first, second and (if any) third resin compositions is particularly advantageous because it simplifies the process and prevents problems arising from incompatibility that may occur between different resin compositions.

[0042] In one embodiment, the molding material further includes at least one additional structural reinforcing layer on the surface of the molding material, away from the surface reinforcing layer. The additional one or more structural reinforcing layers may be the same as or different from the first structural reinforcing layer. In one embodiment, the one or more additional structural reinforcing layers may be different from the first structural reinforcing layer, and the additional reinforcing layers may be associated with the same resin composition as the first structural reinforcing layer or a different epoxy resin composition. In this embodiment, the one or more additional structural reinforcing layers may be conventional prepregs, including, but are not limited to, the HexPly® M79 and M9 series prepregs, which are commercially available from Hexcel Composites GmbH & Co KG (Neumarkt, Austria) under the trade name Heexply®.

[0043] The total amount of resin provided in the molding material of the present invention varies depending on the intended use of the material. For example, if the molding material is to be laid up and cured together with other impregnating or partially impregnating materials, the resin content may be relatively high. Alternatively, if the molding material of the present invention is to be used in combination with an unimpregnated (dry) fiber layer in an intermediate structure into which resin is subsequently injected before curing, the resin content may be relatively low. However, in all cases, there should be enough resin to form an outer layer of the surface reinforcement layer, i.e., a layer that contacts the surface of the mold or tool during the layup of the molding material. However, generally, the total amount of resin present in the molding material of the present invention is 10 to 60% by weight of the molding material. More preferably, in molding materials to be used together with impregnating or partially impregnating materials, the total resin content is 20 to 60% by weight of the molding material, and even more preferably 30 to 50% by weight, and in molding materials to be used in an injection system, the total resin content is preferably 10 to 50% by weight of the molding material.

[0044] Therefore, the basis weight of one or more layers of (single or multiple) resins in the molding material of the present invention can vary significantly depending on the number of (single or multiple) resin layers, the presence of one or two structural reinforcing layers, particularly the weight of the fibrous reinforcing material forming the structural reinforcing layers, and the presence of any additional structural reinforcing layers. As described herein, the total resin may consist of several different resin compositions, but in a preferred embodiment, the same resin composition is used throughout the molding material.

[0045] When different resin compositions are associated with different layers of a molding material, the various resins are initially provided in contact with their associated layers when the molding material is assembled before compaction. When the same resin composition is present throughout the molding material, it may initially be provided as various layers throughout the molding material, or as a single layer. However, after compaction, at least a portion of the resin composition should be present on the surface of a first nonwoven fiber carrier, away from the structural reinforcing layer, thereby providing an external mold or tool contact surface for the molding material.

[0046] In one embodiment, the molding material according to the present invention further includes a discontinuity indicator means attached to the mold or tool contact surface of the molding material that has not fully penetrated the surface reinforcing layer.

[0047] In the context of the present invention, the term "attached" means that the discontinuous indicator means is associated with the mold or tool contact surface of the molding material and therefore cannot be accidentally or easily removed during transport to the end user or in the course of subsequent processing steps.

[0048] In the context of the present invention, “discontinuous” means that the indicator means provides a separate location for the indicator within the surface strengthening layer, providing an indication of which areas of the surface have been treated, for example, by sanding during the post-curing treatment of the molded material.

[0049] The discontinuity indicator means may be applied to the first resin composition on the outer mold or tool contact surface of the molding material during the assembly of various layers and before compaction, but the discontinuity indicator means is preferably applied after compaction but before curing of the structural reinforcing layer and surface reinforcing layer (and any additional layers). At this stage, i.e., before curing, the indicator means is loosely attached to the mold or tool contact surface of the molding material due to the tackiness of the resin layers present on the mold or tool contact surface.

[0050] During the curing of the molding material, the discontinuity indicator means is permanently fixed or embedded in the upper region of the surface reinforcement layer and is therefore sufficiently attached to the mold or tool contact surface of the cured molding material so as not to be removed by handling of the material.

[0051] The indicator means may be bonded only to the surface of the mold or tool contact surface of the molding material, or may penetrate the surface. When the discontinuous indicator means penetrates the surface finishing layer, it may penetrate to any depth as long as it does not penetrate sufficiently into the layer, i.e., the indicator means does not come into contact with the structural reinforcing layer (or the second nonwoven fiber carrier, if present), so that if the surface reinforcing layer is removed to a depth (e.g. by sanding) such that all of the discontinuous indicator means is removed, the underlying layer will not be damaged. Therefore, the indicator means may penetrate the surface reinforcing layer to any depth, from 0% of the layer's depth (i.e., bonded only to the surface) to nearly 100% of the depth, but not completely. In a preferred embodiment, the indicator means penetrates the surface reinforcing layer to 0.1% to 95%, more preferably 1% to 50%, of its depth.

[0052] The molding material of the present invention is particularly suitable for incorporating indicator means on the mold or tool contact surface of the molding material due to the rheological properties of the surface-reinforced layer provided by the rheology modifier of the first resin composition. In particular, the increase in viscosity of the first resin composition means that a clear pattern is maintained because the indicator means is attached to or embedded in the surface layer, remains in a distinct shape, and does not diffuse significantly outward or inward.

[0053] When demolding the cured product, the discontinuity indicator means remain on the surface of the cured product, thereby allowing the cured product to be easily sanded without the risk of completely removing the surface finish layer. In practice, the operator can determine whether the surface or the entire cured product has been sufficiently sanded by evaluating whether all of the discontinuity indicator means have been removed.

[0054] The discontinuous indicator means may include any regular or irregular shapes, and the shapes may be arranged in any regular or irregular arrangement, as long as they function as indicators of sufficient surface treatment. Preferred shapes include regularly or irregularly arranged lines (straight or curved), dots (including circular, square or irregular dots), or a combination thereof. Preferably, the distance between individual shapes is generally shorter than the distance covered by a single sanding pass during manual sanding of the surface. Preferably, the indicator means includes a regular arrangement of regular dots, which makes it easy to assess where the surface has been treated, for example, where the indicator means has been removed by sanding and where the treatment was insufficient.

[0055] The discontinuity indicator means may include any suitable material that remains visible on the surface of the molded material after curing. In one embodiment, the indicator means includes a refractive compound, such as a refractive metal oxide like titanium dioxide. The use of a refractive compound may be useful when sanding of the cured product is automated, and may facilitate the use of optical scanning technology to evaluate progress rather than visual inspection. In other embodiments, the indicator means may be formed from a dye or pigment, such as carbon black, or other similar substances. A preferred form of carbon black for use in the present invention, but not limited to, is the product sold under the trade name Printex® V by Orion Engineered Carbons LLC (4501 Magnolia Cove Drive, Suite 106, Houston, Texas, 77345, USA). In such embodiments, it may be desirable to use a dye insoluble in the first resin composition to prevent “bleeding” of the dye to other parts of the second resin composition. However, it will be readily apparent that the discontinuity means according to the present invention are not limited to the exemplary examples described above.

[0056] The indicator means can be applied to the mold or tool engagement surface of the molding material in any suitable manner, for example, by applying a perforation stencil to the surface, spraying a suitable solution or dispersion or solid particles of a metal oxide, dye or pigment onto the surface, and then applying light pressure, such as by using a hand roller. Alternatively, the indicator means can be applied by spraying or printing.

[0057] In a second aspect of the present invention, a method for preparing a molding material, (a) A step of providing a structural reinforcing layer containing a fibrous reinforcing material; (b) A step of providing a surface reinforcing layer for contact with the surface of a mold or tool, comprising a first nonwoven fiber carrier in combination with a first resin composition containing a rheology modifier and a curing agent, wherein the first resin composition is provided on the outer mold or tool contact surface of the molding material, away from the structural reinforcing layer; and (c) a step of compacting these layers so as to impregnate at least the first nonwoven fiber carrier with the first resin composition without curing the resin composition; A method including this is provided.

[0058] In the method of the present invention, densification is performed after the assembly of the structural reinforcing layer and the surface reinforcing layer and any other layers that may be included. Densification can be performed by any conventional method for forming the composite material, preferably by heating the molded material under pressure. For example, densification can be performed by passing the bonded layers through a densification roller (e.g., one or more S-wrap rollers) and heating them to, for example, 80°C.

[0059] In the method of the present invention, the fibrous reinforcing material may optionally be present in combination with a second resin composition.

[0060] In one embodiment, a method according to a second aspect of the present invention further includes, prior to the compaction step, providing a second nonwoven fiber carrier, optionally combined with a third resin composition, between a structural reinforcing layer and a surface reinforcing layer.

[0061] In one embodiment, a method according to a second aspect of the present invention further includes the step of providing at least one additional structural reinforcing layer on the surface of the molded material, away from the surface reinforcing layer, prior to the compaction step.

[0062] If the structural reinforcing layer is provided in combination with a second resin composition, and / or the second nonwoven fiber carrier is provided in combination with a third resin composition, the material may be provided with a structural material in which the resin has already been at least partially impregnated. Alternatively, in a preferred embodiment, the structural layer and the resin layer are provided as separate layers during the assembly of the molded material, and the resin layer is at least partially impregnated into each layer during the compaction step.

[0063] In the method of the present invention, the first resin composition, the first nonwoven carrier, and, if present, the second resin composition, the second nonwoven fiber carrier, the third resin composition, and / or additional (one or more) structural reinforcing layers may each be optionally defined as for similar materials in the molding material of the present invention.

[0064] In one embodiment, a method according to a second aspect of the present invention further includes the steps of applying a discontinuous indicator means to a mold or tool contact surface of a molding material and applying pressure and optionally heat in order to attach the discontinuous indicator means to a first resin composition without completely penetrating the surface reinforcement layer. In the context of the present invention, the term “attach” means that the discontinuous indicator means is associated with the mold or tool contact surface of the molding material and therefore cannot be accidentally or easily removed during transport to the end user or in the course of subsequent processing steps. After curing, the discontinuous indicator means remains visible on the mold or tool contact surface of the cured molded article and may partially penetrate the surface reinforcement layer.

[0065] Discontinuity indicator means can be applied to the mold or tool contact surface of the molding material during the layup and before curing, for example, at any stage before the compaction step. However, preferably, the discontinuity indicator means is added after the compaction step but before curing. The discontinuity indicator means can be applied to the surface in any suitable way. For example, the indicator means can be applied to the mold or tool engagement surface of the molding material by applying a perforation stencil to the surface, spraying a suitable solution or dispersion or solid particles of a metal oxide, dye or pigment onto the surface, and then applying light pressure, such as by using a hand roller. Alternatively, the indicator means can be applied by spraying or printing.

[0066] In a third aspect of the present invention, a molding material obtained by a method according to a second aspect of the present invention is provided.

[0067] A fourth aspect of the present invention provides a method for preparing a molded article, comprising curing a molding material according to a first or third aspect of the present invention, wherein optionally, the molding material is laid up on the surface of the molding material, away from the surface reinforcing layer, along with at least one additional structural reinforcing layer, prior to the curing step.

[0068] The molding material of the present invention can be cured by any conventional method to form a molded article, taking into account the resins (single or multiple types) and curing agents (single or multiple types) present in various layers. Therefore, the appropriate conditions required for curing articles prepared from the molding material according to the present invention can be determined empirically by following standard procedures used in the prepreg industry.

[0069] In a fifth embodiment of the present invention, a molded article obtained by a method according to a fourth embodiment of the present invention is provided.

[0070] In one embodiment, the molded article has an average pinhole area of ​​less than 1%, preferably less than 0.1%, and / or 0.5 mm². 2 Less than 0.05 mm, preferably 0.05 mm 2The molded surface has an average pinhole size of less than 5%, and / or less than 10%, preferably less than 5%, of overlapping defects.

[0071] A sixth aspect of the present invention relates to a method for preparing a finished molded product, (a) A step of preparing a molding material by the method of the present invention, comprising applying a discontinuous indicator means to a mold or tool contact surface of the molding material and applying pressure and optionally heat in order to attach the discontinuous indicator means to a first resin composition without completely penetrating the surface strengthening layer; (b) A step of curing a molding material in a mold or tool by bringing a discontinuous indicator means into contact with the mold or tool, wherein optionally, the molding material is laid up on the surface of the molding material, away from the surface reinforcing layer, along with at least one additional structural reinforcing layer, prior to the curing step; (c) Removing the molded part from the mold or tool and finishing the molded part from step (b) by wearing down the mold or tool contact surface of the molded part to a depth sufficient to remove the discontinuous indicator means without completely removing the surface strengthening layer. A method including this is provided.

[0072] In this embodiment of the present invention, the discontinuity indicator provides the operator with a sign that the outermost surface reinforcement layer of the molded article, into which release agents may be mixed after demolding, has been uniformly removed without the risk of removing the entire surface reinforcement layer.

[0073] In another embodiment of the present invention, a finished product obtained by the method according to the present invention in its sixth aspect is provided. [Examples]

[0074] Example 1 Resin composition 1 is Araldite® LY1589 (semi-solid bisphenol A diglycidyl ether epoxy resin manufactured by Huntsman Advanced Materials GmbH (Basel, Switzerland)) 72.3g; Araldite® LY1556 (Liquid bisphenol A diglycidyl ether epoxy resin manufactured by Huntsman Advanced Materials GmbH (Basel, Switzerland)) 18.17g; Araldite (registered trademark) DW0135 (blue pigment paste manufactured by Huntsman Advanced Materials GmbH (Basel, Switzerland)) 0.10g; BYK-A530 (defoaming agent manufactured by BYK-Chemie GmbH (Wesel, Germany)) 0.18g; Aerosil® R202 (hydrophobic fumed silica rheology modifier manufactured by Evonik Resource Efficiency GmbH (Hanau-Wolfgang, Germany)) 6.00g; and Dyhard® UR500 (a bifunctional latent uron enhancer in powder form, manufactured by Alzchem Group AG (Trostberg, Germany)) 2.82g It was formulated from this.

[0075] The components were thoroughly mixed at a temperature of 50-60°C until the color and consistency of the mixture were uniform. The same resin composition 1 was used for each resin layer of the molding material.

[0076] A molding material 1 having the following structure was constructed. (1) 400g / m 2 A layer of resin composition 1; (2) Layers of LBB1200 fabric (1250g / m² made by Hexcel Reinforcements UK Limited (Narborough, Leicestershire, UK)) 2 Triaxial non-crimped glass fabric); (3) Layers of Evalith® S5030 (50g / m² basis weight, manufactured by Johns Manville, Denver, Colorado, USA) 2 Glass fiber fleece); (4) 200g / m 2 A layer of resin composition 1; (5) 15g / m 2 A layer of lightweight, fully synthetic nonwoven fiber bale containing a blend of polyester and nylon fibers having a basis weight (manufactured by Technical Fibre Products Limited (Burnside Mills, Kendal, Cumbria, UK)); and (6) 200g / m 2 A layer of resin composition 1.

[0077] The assembled layers were compacted by passing them through an S-wrap roller system heated to 80°C to form molding material 1.

[0078] After compaction, a layer of P34Tygavac® RF260 (a staggered 12.7 mm center-perforated style FEP fluoropolymer release film with a nominal pore size of 1.143 mm, manufactured by Tygavac Advanced Materials Limited, The Causeway, Broadway Business Park, Chadderton, Oldham OL9 9XD, UK) was placed on top of the resin composition layer at the bottom of the prepreg (i.e., layer (6) - the surface adjacent to the mold surface which becomes the part surface at demolding). After sprinkling Tioxide TR-81 (powdered titanium dioxide manufactured by Huntsman Advanced Materials GmbH (Basel, Switzerland)) onto the surface of the film, the film was lightly pressed with a rubber roller to remove excess titanium dioxide and release film. Approximately 1.7 g / m² of this material was applied to the resin layer on the mold or tool contact surface of molding material 1. 2A regular arrangement of titanium dioxide dots with a basis weight was left.

[0079] A composite part was manufactured by placing molding material 1 in a composite tool treated with Zyvax® Watershield® (a silicone-free water-soluble release agent manufactured by Freeman Manufacturing and Supply Company (Avon, Ohio, USA)) and curing the assembly under vacuum at 80°C and a pressure of 1 bar for 6 hours. Upon cooling, when the cured molded part was removed from the tool, a separate array of colored titanium dioxide dots appeared against the blue background of the cured resin. The dots allowed for the uniform removal of a portion of the surface reinforcement layer of the composite part by sanding (see Figure 1).

[0080] Figure 1 shows the cured molding material 1 manufactured as described above. The left half of material 3 has been sanded to remove all mold release agent remaining on the surface after curing, but the right side of material 5 has not been sanded. The arrangement of titanium dots 7 applied to molding material 1 before curing is still present on the right side of material 5, but the absence of a regular arrangement of dots 7 on the left side 3 indicates at least partial removal of the top layer. The presence of individual dots 9 scattered on the left side 3 of molding material 1 indicates areas where sufficient sanding to completely remove the top layer has not been performed and where further sanding should be completed.

[0081] A sample of the uncured molding material prepared by the method described above was cut and overlapped in the X and Y directions across the surface of the mold with an overlapping area of ​​approximately 2-3 cm. Further molding material was placed on top without any overlap, and the resulting assembly was cured by the method described above. During cooling and demolding, the overlapping area of ​​the cured product showed only minimal defects compared to a standard part manufactured from non-overlapping molding material.

[0082] Example 2 Resin composition 2 is Kukdo KFR136SL (semi-solid bisphenol A diglycidyl ether epoxy resin) 72.9g, manufactured by Kukdo Chemical Company Limited (Seoul, South Korea); Epikote® 828 (Liquid bisphenol A diglycidyl ether epoxy resin manufactured by Hexion Inc. (Columbus, Ohio, USA)) 18.2g; Aerosil® R202 (hydrophobic fumed silica rheology modifier manufactured by Evonik Resource Efficiency GmbH (Hanau-Wolfgang, Germany)) 6g; and Dyhard® UR500 (a bifunctional latent uron enhancer in powder form, manufactured by Alzchem Group AG (Trostberg, Germany)) 2.9g It was formulated from [the following ingredients].

[0083] The components were thoroughly mixed at a temperature of 50-60°C until the color and consistency of the mixture were uniform. The same resin composition 2 was used for each resin layer of the molding material.

[0084] A molding material 2 having the following structure was constructed. (1) 400g / m 2 The layer of resin composition 2; (2) Layers of LBB1200 fabric (1250g / m² made by Hexcel Reinforcements UK Limited (Narborough, Leicestershire, UK)) 2 Triaxial non-crimped glass fabric); (3) Layers of Evalith® S5030 (50g / m² basis weight, manufactured by Johns Manville, Denver, Colorado, USA) 2 Glass fiber fleece); (4) 15g / m 2A layer of lightweight, fully synthetic nonwoven fiber bale containing a blend of polyester and nylon fibers having a basis weight (manufactured by Technical Fibre Products Limited (Burnside Mills, Kendal, Cumbria, UK)); and (5) 400g / m 2 A layer of resin composition 2.

[0085] The assembled layers were compacted by passing them through an S-wrap roller system heated to 80°C to form molding material 2.

[0086] A resin composition layer (5) was placed adjacent to the mold surface within a composite tool treated with Zyvax® Watershield (a silicone-free water-soluble release agent manufactured by Freeman Manufacturing and Supply Company (Avon, Ohio, USA)) using molding material 2. Two layers of HexPly® 79 (a prepreg manufactured by Hexcel GmbH (Neumarkt, Germany)) were placed on top of the molding material in the mold, i.e., next to the resin layer (1). The assembly was cured under vacuum at 80°C and a pressure of 1 bar for 6 hours. After cooling, the cured molded part was removed and inspected and further tested.

[0087] In an alternative embodiment, a layer of individual indicator means containing a regular arrangement of titanium dioxide dots can be applied to the molded material 2 after compaction and before curing.

[0088] Test apparatus and method Matrix Rheology Rheological measurements of resin compositions were performed using a TA HR-2 Discovery Hybrid Rheometer manufactured by TA Instruments (Newcastle, Delaware, USA), with a 25mm parallel plate and a 1mm gap, over a period of 0.1 to 100 seconds. -1The experiment was conducted at the specified shear rate and temperature of 60°C.

[0089] Characterization of Veil The measurement of fiber diameter and bale aperture can be performed using a Keyence VHX-6000 series digital microscope manufactured by Keyence (UK) Limited (Milton Keynes, Buckinghamshire, UK). The bale used as the first nonwoven fiber carrier (i.e., the surface bale used for the surface reinforcement layer) may be provided to the microscope mounted on a blue plastic card to aid in the emphasis of the aperture area when viewed on a computer monitor. The microscope is set to 175x magnification, the light output is set to maximum, and the gain dial setting is adjusted so that the aperture area can be clearly identified. The saved computer image is 2951002 μm. 2 This represents the total area.

[0090] The air permeability of nonwoven fiber carriers can be measured by ASTM D737-18: Standard Test Method for Air Permeability of Textile Fabrics.

[0091] Next, Keyence software is used to measure the thickness (diameter), average "aperture area" (i.e., the space between fibers), and aperture percentage of each individual fiber. The image is also manipulated by adjusting sliders on a histogram to create a two-color image where one color represents the bale fibers and the other represents the aperture spaces. Then, the software is used to measure the area of ​​all individual aperture spaces. This data can be stored in a spreadsheet and used to calculate the total area occupied by the apertures, along with the average size of the apertures (to calculate the aperture percentage).

[0092] Characterization of hardened surfaces The hardened surface of the demolded composite component was characterized by wiping the surface with a carbon black slurry in acetone. After washing away excess slurry, measurements were performed using a Keyence VHX-6000 series digital microscope at 25x magnification and gain settings adjusted to clearly identify surface defects. Keyence software was used to measure 132.63 mm² with the histogram slider set between 000 and 065, the brightness tolerance set to 20, and the noise filter set to 10. 2 The observed images were manipulated. Using software, the average area of ​​the observed pinholes and the percentage of the total observed area identified as pinholes were measured.

[0093] Overlap defects were measured by first highlighting the defects along the overlap using a carbon black slurry in acetone. After washing away excess slurry, the length of the defects was measured using a ruler. The amount of overlap defects was expressed as a percentage of the sum of the measured defects relative to the length of the overlap.

[0094] result The viscosity of the M79® resin (a commercially available non-rheology-modified epoxy resin matrix manufactured by Hexcel Composites GmbH and Co., KG (Neumarkt, Austria)) and the rheology-modified resin composition 1 used in the molding material 1 of Example 1 (according to the present invention) was tested as described above.

[0095] For M79, the temperature and time are 60°C and 0.1s. -1 The viscosity at 60°C and 100°C is 40 Pa·s. -1 The viscosity was 29 Pa.s.

[0096] For resin composition 1, 60° and 0.1s -1 The viscosity at 60°C and 100s is 470 Pa·s. -1 The viscosity was 66 Pa.s.

[0097] As discussed in Example 1, the material according to the present invention was prepared, cut, and overlapped in the X and Y directions across the surface of the mold with an overlapping area of ​​approximately 2-3 cm, and the material was cured. Three comparative laminates not within the scope of the present invention were also prepared and processed as described above.

[0098] Comparative laminate 1 had a biaxial portion adjacent to the mold surface, lacked a surface-reinforced nonwoven fiber carrier, lacked an intermediate nonwoven fiber carrier, and consisted of a standard prepreg having a non-rheology-modified resin (M79), such as M79 / 40% / LBB1200.

[0099] Comparative laminate 2 had a biaxial portion closest to the mold surface, lacked a surface-reinforced nonwoven fiber carrier, had an S5030 nonwoven fiber carrier between the reinforcing layer and the mold, and consisted of a standard prepreg, such as M79 / 40% / LBB1200, which contained a non-rheology-modified resin (M79).

[0100] Comparative laminate 3 had a biaxial portion closest to the mold surface, but had a surface-reinforced nonwoven fiber carrier in the outer layer adjacent to the mold, and consisted of a standard prepreg, such as M79 / 40% / LBB1200, with an S5030 nonwoven fiber carrier between the reinforcing layer and the surface-reinforced nonwoven fiber carrier. However, the resin of the comparative laminate was a non-rheology-modified resin (M79).

[0101] The surface characterization of pinholes and overlapping defects in composite components prepared by curing control laminates 1, 2, and 3, as well as the surface finishing molding material according to the present invention, typically yielded the following results. [Table 1]

[0102] The molding material according to the present invention can be cured at low temperatures (typically 100°C) to reduce pinholes and overlapping defects and provide molded articles with a good surface finish requiring minimal surface processing. Such materials may be equipped with sacrificial discontinuity indicator means on the molded surface to facilitate uniform surface processing. The various aspects or embodiments that may be included in the present invention can be summarized as follows: [1]. A molding material comprising a surface reinforcing layer for contact with the surface of a mold or tool, the surface reinforcing layer comprising (a) a structural reinforcing layer comprising a fibrous reinforcing material; and (b) a first nonwoven fiber carrier combined with a first resin composition comprising a rheology modifier and a curing agent, wherein the first resin composition provides the external mold or tool contact surface of the molding material. [2]. The first resin composition has a viscosity of 200-1000 Pa.s at 60°C and 0.1s (measured by shear sweep viscosity method). -1 Viscosity at 60°C and 0.1s -1 Viscosity of 25% or less at 60°C and 100s, but 25 Pa.s or more. -1 A molding material according to item 1 above, having viscosity in the given range. [3]. The molding material according to item 1 or 2, wherein the first resin composition is a thermosetting resin composition, preferably an epoxy resin composition. [4]. The first nonwoven fiber carrier is preferably 1 to 80 g / m² 2 A molding material according to any one of the above items 1 to 3, which is a thermoplastic fiber bale having a basis weight in the range of . [5]. The first nonwoven fiber carrier has an opening degree of 1-10% and / or approximately 75-350 μm 2 A molding material according to any one of the above items 1 to 4, having an average opening area. [6]. The molding material according to any one of items 1 to 5, wherein the structural reinforcing layer is present in combination with a second resin composition, and optionally the second resin composition is the same as the first resin composition. [7]. The molding material according to any one of items 1 to 6, further comprising a second nonwoven fiber carrier between the structural reinforcing layer and the surface reinforcing layer, preferably the second nonwoven fiber carrier having a basis weight greater than that of the first nonwoven carrier. [8]. The molding material according to item 7, wherein the second nonwoven fiber carrier is combined with a third resin composition, and preferably the third resin composition is the same as the first and / or second resin composition. [9]. The molding material according to any one of items 1 to 8, further comprising at least one additional structural reinforcing layer on the surface of the molding material, away from the surface reinforcing layer.

[10] . The molding material according to any one of items 1 to 9, further comprising discontinuity indicator means attached to the mold or tool contact surface of the molding material that has not sufficiently penetrated the surface reinforcing layer.

[11] . The molding material according to item 10, wherein the discontinuous indicator means includes a regular or irregular arrangement of shapes, preferably the shapes being selected from lines, dots, or a mixture thereof.

[12] . The molding material according to item 10 or 11, wherein the discontinuity indicator means includes a refractive metal oxide or a dye or pigment such as carbon black.

[13] . A method for preparing a molding material, (a) A step of providing a structural reinforcing layer containing a fibrous reinforcing material; (b) Providing a surface reinforcing layer for contact with the surface of a mold or tool, comprising a first nonwoven fiber carrier in combination with a first resin composition containing a rheology modifier and a curing agent, wherein the first resin composition is provided on the outer mold or tool contact surface of the molding material, away from the structural reinforcing layer; and (c) a step of compacting the layer so as to impregnate at least the first nonwoven fiber carrier with the first resin composition without curing the resin composition; A method comprising, preferably, the compaction being carried out by heating the molding material under pressure.

[14] . The first resin composition has a viscosity of 200-1000 Pa.s at 60°C and 0.1s (measured by shear sweep viscosity method). -1 Viscosity at 60°C and 0.1s -1 Viscosity is less than 25% of the viscosity at 60°C and 100s, but is 25 Pa.s or higher. -1 The method according to item 13 above, having viscosity in the given range.

[15] . The method according to item 13 or 14, wherein the first resin composition is a thermosetting resin composition, preferably an epoxy resin composition.

[16] . The first nonwoven fiber carrier is preferably 1 to 80 g / m² 2 The method according to any one of items 13 to 15 above, which is a thermoplastic fiber bale having a basis weight in the range of .

[17] . The first nonwoven fiber carrier has an opening degree of 1-10% and / or approximately 75-350 μm 2 The method according to any one of items 13 to 16 above, having an average opening area.

[18] . The method according to any one of items 13 to 17, wherein the structural reinforcing layer is provided in combination with a second resin composition, wherein optionally the second resin composition is the same as the first resin composition.

[19] . The method according to any one of items 13 to 18, further comprising the step of providing a second nonwoven fiber carrier between the structural reinforcing layer and the surface reinforcing layer prior to the densification step, preferably the second nonwoven fiber carrier having a basis weight greater than that of the first nonwoven carrier.

[20] . The method according to item 19, wherein the second nonwoven fiber carrier is combined with a third resin composition, and preferably the third resin composition is the same as the first and / or second resin composition.

[21] . The method according to any one of items 13 to 20, further comprising providing at least one additional structural reinforcing layer on the surface of the molding material, away from the surface reinforcing layer, prior to the compaction step.

[22] . The method according to any one of items 13 to 21, further comprising the steps of applying the discontinuous indicator means to the mold or tool contact surface of the molding material and applying pressure and optionally heat in order to attach the discontinuous indicator means to the first resin composition without completely penetrating the surface strengthening layer.

[23] . A molding material obtained by the method described in any one of the above items 13 to 22.

[24] . A method for preparing a molded article, comprising curing a molding material described in any one of items 1 to 12 or 23 above, wherein optionally, the molding material is laid up on the surface of the molding material, away from the surface reinforcing layer, along with at least one additional structural reinforcing layer, prior to the curing step.

[25] . A molded article obtained by the method described in item 24 above.

[26] . An average pinhole area of ​​less than 1%, preferably less than 0.1%, and / or 0.5 mm². 2 Less than 0.05 mm, preferably 0.05 mm 2 The molded article according to item 25, having a molded surface with an average pinhole size of less than 5%, and / or less than 10%, preferably less than 5%, of overlapping defects.

[27] . A method for preparing a finished molded product, (a) the step of preparing a molding material by the method described in item 22 above, and subsequently; (b) A step of curing the molding material in the mold or tool by bringing the discontinuous indicator means into contact with the mold or tool, wherein optionally the molding material is laid up with at least one additional structural reinforcing layer on the surface of the molding material, away from the surface reinforcing layer, prior to the curing step; (c) the step of removing the molded product from the mold or tool; and (d) A step of finishing the molded product of step (b) by wearing down the mold or tool contact surface of the molded product to a depth sufficient to remove the discontinuous indicator means without completely removing the surface strengthening layer. A method that includes this.

[28] . A finished product obtained by the method described in item 27 above.

Claims

1. A molding material for forming composite parts by being laid up and cured together with other molding materials in a mold or tool, A surface reinforcing layer for contact with the surface of a mold or tool used to form the composite part, comprising: (a) a structural reinforcing layer containing a fibrous reinforcing material; and (b) a first nonwoven fiber carrier impregnated with a first resin composition containing a rheology modifier and a curing agent containing fumed silica, wherein the first resin composition provides an external mold or tool contact surface for the molding material, and the first resin composition does not contain particulate material of glass spheres, and the first nonwoven fiber carrier has an opening degree of 1 to 10% and / or 75 to 350 μm ２ It has an average opening area, The present invention further includes discontinuity indicator means attached to the mold or tool contact surface of the molding material that has not sufficiently penetrated the surface reinforcing layer, wherein the discontinuity indicator means comprises a regular or irregular arrangement of shapes, the shapes being selected from lines, dots or a mixture thereof. Molding material.

2. The first resin composition has a viscosity of 200 to 1000 Pa.s at 60°C and 0.1 s (measured by the shear sweep viscosity method). －１ Viscosity at 60°C and 0.1 s －１ The viscosity is 25% or less of the viscosity at 60°C and 100°C, but is 25 Pa·s or higher. －１ The molding material according to claim 1, having viscosity in the given range.

3. The molding material according to claim 1 or 2, wherein the first resin composition is a thermosetting resin composition.

4. The molding material according to claim 3, wherein the first resin composition is an epoxy resin composition.

5. The molding material according to any one of claims 1 to 4, wherein the first nonwoven fiber carrier is a thermoplastic fiber veil.

6. The molding material according to any one of claims 1 to 5, wherein the structural reinforcing layer is present in combination with a second resin composition, and optionally the second resin composition is the same as the first resin composition.

7. The molding material according to any one of claims 1 to 6, further comprising a second nonwoven fiber carrier between the structural reinforcing layer and the surface reinforcing layer.

8. The molding material according to claim 7, wherein the second nonwoven fiber carrier has a basis weight greater than that of the first nonwoven fiber carrier.

9. The molding material according to claim 7 or 8, wherein the second nonwoven fiber carrier is combined with a third resin composition.

10. The molding material according to claim 9, wherein, when the structural reinforcing layer is present in combination with the second resin composition, the third resin composition is the same as the first resin composition and / or the second resin composition.

11. The molding material according to any one of claims 1 to 10, further comprising at least one additional structural reinforcing layer on the surface of the molding material, away from the surface reinforcing layer.

12. The molding material according to claim 1, wherein the discontinuity indicator means includes a refractive metal oxide, or a dye or pigment.

13. The molding material according to claim 12, wherein the discontinuity indicator means includes carbon black.

14. A method for preparing a molding material for forming a composite part by laying up and curing it together with other molding materials in a mold or tool, (a) A step of providing a structural reinforcing layer containing a fibrous reinforcing material; (b) Providing a surface reinforcing layer for contact with the surface of a mold or tool used to form the composite part, comprising a first nonwoven fiber carrier in combination with a first resin composition containing a rheology modifier and a curing agent containing fumed silica, wherein the first resin composition is provided to the outer mold or tool contact surface of the molding material, away from the structural reinforcing layer, wherein the first resin composition does not contain particulate material of glass spheres, and the first nonwoven fiber carrier has an opening degree of 1 to 10% and / or 75 to 350 μm ２ A step having an average opening area; (c) a step of compacting the structural reinforcing layer and the surface reinforcing layer so as to impregnate at least the first nonwoven fiber carrier with the first resin composition without curing the resin composition; and (d) The step of applying the discontinuous indicator means to the mold or tool contact surface of the molding material and applying pressure and optionally heat in order to attach the discontinuous indicator means to the first resin composition without completely penetrating the surface strengthening layer, This discontinuous indicator means includes a regular or irregular arrangement of shapes, the shape being selected from lines, dots, or a mixture thereof. method.

15. The first resin composition has a viscosity of 200 to 1000 Pa.s at 60°C and 0.1 s (measured by the shear sweep viscosity method). －１ Viscosity at 60°C and 0.1 s －１ The viscosity is less than 25% of the viscosity at 60°C and 100°C, but is 25 Pa·s or higher. －１ The method according to claim 14, having a viscosity in [location].

16. The method according to claim 14 or 15, wherein the first resin composition is a thermosetting resin composition.

17. The method according to claim 16, wherein the first resin composition is an epoxy resin composition.

18. The method according to any one of claims 14 to 17, wherein the first nonwoven fiber carrier is a thermoplastic fiber veil.

19. The method according to any one of claims 14 to 18, wherein the structural reinforcing layer is provided in combination with a second resin composition, and optionally the second resin composition is the same as the first resin composition.

20. The method according to any one of claims 14 to 19, further comprising the step of providing a second nonwoven fiber carrier between the structural reinforcing layer and the surface reinforcing layer before the aforementioned compaction step.

21. The method according to claim 20, wherein the second nonwoven fiber carrier has a basis weight greater than that of the first nonwoven fiber carrier.

22. The method according to claim 20 or 21, wherein the second nonwoven fiber carrier is combined with a third resin composition.

23. The method according to claim 22, wherein, when the structural reinforcing layer is present in combination with the second resin composition, the third resin composition is the same as the first resin composition and / or the second resin composition.

24. The method according to any one of claims 14 to 23, further comprising providing at least one additional structural reinforcing layer on the surface of the molding material, away from the surface reinforcing layer, prior to the densification step.

25. A method for preparing a molded article, comprising the step of curing a molding material according to any one of claims 1 to 13, wherein optionally, the molding material is laid up on the surface of the molding material, away from the surface reinforcing layer, with at least one additional structural reinforcing layer prior to the curing step.

26. The forming material has an average pinhole area of less than 1%, and / or an average pinhole size of less than 0.5 mm, and / or less than 10% overlapping defects, and comprises a formed surface, the method according to claim 25. ２ The method according to claim 25, comprising a formed surface having an average pinhole area of less than 1%, and / or an average pinhole size of less than 0.5 mm, and / or less than 10% overlapping defects.

27. A method for preparing a finished molded product, (a) the step of preparing a molding material by the method of claim 14, and subsequently; (b) A step of curing the molding material in the mold or tool by bringing the discontinuous indicator means into contact with the mold or tool, wherein optionally the molding material is laid up on the surface of the molding material, away from the surface reinforcing layer, along with at least one additional structural reinforcing layer, prior to the curing step; (c) the step of removing the molded product from the mold or tool; and (d) A step of finishing the molded product of step (b) by wearing down the mold or tool contact surface of the molded product to a depth sufficient to remove the discontinuity indicator means without completely removing the surface strengthening layer. A method that includes this.

Images