Coloring composition for colorful filter and colorful filter

A color filter and coloring composition technology, applied in the direction of optical filters, optics, optical components, etc., can solve the problems of insufficient adaptability, increased viscosity of the coloring composition, and deterioration of filter wettability, etc. Achieve excellent color reproducibility, high contrast, and excellent fluidity

CN101008687AActive Publication Date: 2007-08-01TOYO INK SC HOLD CO LTD
2 Cites 12 Cited by

Patent Information

Authority / Receiving Office
CN · China
Current Assignee / Owner
Publication Date
2007-08-01

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention provides a colored composition for color filter, capable of forming color filter with high contrast, good dispensability, fluidity and dispersion stability, when forming filter with little foreign matter thereinto. The composition contains pigment carriers composed of transparent resin, forebody and their mixtures, pigments, phthalocyanine derivatives D1 having substituents shown in one general formula (1) and phthalocyanine derivatives D2 having substituents shown in two general formulas (1) relative to the phthalocyanine residue, the weight ratio D1:D2 is 85:15 to 56:44, in the general formula (1), X denotes 2+ linking group selected from CO, SO2, CH2 and CH2NHCOCH2, Y denotes direct connection or NH(CH2)n, R1, R2 each independently denotes hydrogen atom, alkyl having substituents with C1-6, R1 and R2 can also combine with each other to form heterocycle which can further contain nitrogen atom or oxygen atom, n denotes 1-6 integer.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The present invention relates to a coloring composition for a color filter and a color filter using the composition. Background technique

[0002] A color filter is to arrange two or more fine band-shaped filter segments of different hues in parallel or crosswise on the surface of a transparent substrate such as glass, or to arrange fine filter segments in a certain arrangement. And constituted. The filter segments are several μm to several hundreds of μm, and each hue is neatly arranged on the substrate in a predetermined arrangement.

[0003] Generally, in a color liquid crystal display device, a transparent electrode for driving liquid crystal is formed on a color filter by vapor deposition or sputtering, and an alignment film for aligning the liquid crystal in a certain direction is formed thereon. In order to give full play to the performance of these transparent electrodes and alignment films, the transparent electrodes and alignment films are ...

Examples

Embodiment 1

[0107] Stir and mix the mixture of the following composition evenly, use zirconia beads with a diameter of 0.5 mm, disperse it with a sand mill for 10 hours, and filter it with a filter of 1.0 μm to prepare a copper phthalocyanine system for blue resist materials. Pigment dispersions.

[0108] ε-type copper phthalocyanine blue pigment (C.I. Pigment Blue 15:6) 10.0 parts

[0109] (BASF "Heliogen Buruichi L-6700F")

[0110] Copper phthalocyanine derivative composition 1.0 parts

[0111] (The weight ratio of phthalocyanine derivative (D1):phthalocyanine derivative (D2)=85:15)

[0112] Phosphate-based pigment dispersant 2.0 parts

[0113] ("BYK111" manufactured by Bitsukuchemi Co., Ltd.)

[0114] Acrylic resin solution 47.0 parts

[0115] Methoxypropyl acetate 40.0 parts

[0116] Next, after stirring and mixing the mixture of the following composition uniformly, the alkali-developing type blue resist material was obtained.

[0117] Copper phthalocyanine pigment dispersion f...

Embodiment 2

[0126] Except that the copper phthalocyanine derivative composition was changed to the weight ratio of phthalocyanine derivative (D1): phthalocyanine derivative (D2) = 65: 35, the same operation was carried out as in Example 1 to obtain an alkali-developable blue resist. etch material.

Embodiment 3

[0128] Except that the copper phthalocyanine derivative composition was changed to the weight ratio of phthalocyanine derivative (D1):phthalocyanine derivative (D2) = 60:45, the same operation was carried out as in Example 1 to obtain an alkali-developable blue resist. etch material.