MOLD FOR THE PRODUCTION OF VOLUME-SHAPED CASTING BODY

Description

[0001] The invention lies in the field of foundry technology and can be used with particular advantage in the production of spirals, springs or coils made of a metal, in particular copper.

[0002] Wound coils are used in electrical machines. These coils do not ideally fill the available installation space. This results in a lower power or torque density of the electrical machines relative to their weight or installation space. Cast copper coils can compensate for this disadvantage, but to date, no series-production processes for the production of cast copper coils or cast coils made of copper alloys in permanent molds with sufficient service life are known.

[0003] To increase the power density or torque density of electrical machines, complex, often manually manufactured coils are wound to slightly improve the fill ratio compared to series production processes. Wire of the same cross-section is used across the winding height. Furthermore, in conventional electrical machines, the coil turns, which are arranged one on top of the other from the inside out, impair heat dissipation and lead to greater heating of the coils, thus necessitating a limitation of the maximum current density relative to the winding cross-section.

[0004] Cast Cu coils or cast coils made of Cu alloys are generally known, but are not yet manufactured in permanent molds, but in lost form such as in investment casting or in the lost foam process.

[0005] EP 3 208 013 A1 relates to a method for casting a component of complex geometry, in which a casting mold is used, at least one molded part of which is designed as a lost mold. The at least one molded part designed as a lost mold is produced from a salt or a salt mixture. At least one outer or inner part of the casting mold, which determines the outer or inner geometry of the component, is composed of more than two mold segments, which are preferably stacked one above the other.

[0006] The document DE 10 2014 106851 A1 discloses a coil package for an electrical machine, comprising a coil carrier made of an electrically non-conductive material and a coil made of an electrically conductive material accommodated by the coil carrier, wherein the coil carrier is made of a ceramic material, and wherein the coil is designed as a cast coil.

[0007] Against the background of the prior art, the invention is based on the object of creating a possibility for the production of cast metal coils with multi-purpose tools.

[0008] The object is achieved by a casting mold according to claim 1. Advantageous embodiments emerge from the dependent claims and from the description.

[0009] The invention relates to a casting mold for producing helical castings, according to claim 1.

[0010] The inner shape of the die, i.e. its hollow interior which determines the outer shape of the coil, can be conical or truncated pyramid-shaped, so that the casting has a conical or truncated pyramid-shaped outer contour. The contour of the mold core can be essentially cylindrical, i.e. apart from a draft angle, for example, or else conical or truncated pyramid-shaped. If the coil is placed on a tooth of a motor sheet, this can have straight contours, so that an inner contour of the coil that is cylindrical or cuboid-shaped is also expedient. Accordingly, in this case the outer contour of the mold core can also have a cylindrical or cuboid shape, or the shape of a cone or a four-sided pyramid, or a truncated cone or pyramid.

[0011] With a conical or pyramidal outer contour, the wall thickness of the coil body can increase toward the radially outer end of the coil in an electrical machine. Accordingly, the height of the individual turns, measured longitudinally along the coil, can decrease toward the thicker end of the coil, i.e., toward the end with a larger outer diameter, especially while maintaining the same overall cross-section of each individual turn.

[0012] Advantageously, it can be provided that the core pull has one or more webs that define the helix and separate different, adjacent turns of the helix of the cast body from each other.

[0013] The geometry of the webs on the core puller and / or on the die can be designed in such a way that the pitch and / or the winding strength of the helical body is constant or variable over its length, i.e., for example, increases or decreases towards one end.

[0014] A continuous helical web can be provided on the surface of the core pull, which defines the negative shape of the helix as well as the facing interfaces of the individual helix turns. The web is arranged between the individual helix turns of the casting during the casting process.

[0015] Furthermore, it can advantageously be provided that the core pull falls in at least one or two directions during demoulding.

[0016] For this purpose, it can be provided that the core pull consists of two or three or more than three partial bodies which are, for example, prism-shaped or wedge-shaped, of which at least two, three or more than three each form a part of the surface of the core pull which borders on the helical body.

[0017] The partial bodies can, for example, each have a circular ring segment shape in cross section.

[0018] Several partial bodies can together form a hollow, in particular hollow-cylindrical, body, wherein at least one of the partial bodies can be displaced radially inward or collapsed. It can also be provided that at least one of the partial bodies of the core pull consists of a soluble material, such as a water-soluble salt body or a crushable sand mold body. This soluble partial body can support the remaining, at least partially non-soluble and reusable partial bodies during the casting process.

[0019] According to the invention, the core has at least one dissolvable or destructible partial body and at least one non-dissolvable partial body usable as a permanent mold, wherein only the partial bodies usable as a permanent mold come into contact with the casting material or the melt.

[0020] Furthermore, it can advantageously be provided that the core puller rotates during demoulding and thus supports demoulding from the coil.

[0021] Furthermore, it can advantageously be provided that the core pull consists of a ceramic material, in particular a molding sand material, which can be dissolved after a casting process.

[0022] The die, which can have a conical or square-pyramidal inner contour, can have a consistent wall thickness along the length of the coil being cast. In this case, the outer contour runs parallel to the inner contour. This, i.e., the constant wall thickness of the die as a tool insert, prevents uneven heating or cooling of the die during rapid temperature changes.

[0023] The die is advantageously used as a tool insert in a steel mold.

[0024] This can have a conical or pyramid-shaped tapered inner contour so that several parts of a potentially multi-part die are reliably positioned and compressed when inserted into the steel mold, even under thermal loads.

[0025] The die completely absorbs the casting material, such as copper, so that the casting material does not come into contact with the steel mold, but rather exclusively with the ceramic surfaces of the die and mold core. This prevents thermal damage to the steel mold when casting copper coils.

[0026] Furthermore, it can advantageously be provided that the die has one or more webs which define the helix and separate different, adjacent turns of the helix of the cast body from each other.

[0027] A continuous helical web can be provided on the surface of the die, defining the negative shape of the helix as well as the facing interfaces of the individual helix turns. The web is arranged between the individual helix turns of the casting during the casting process.

[0028] The helix can also be defined as a whole by a web on the die and a web on the core pull, which lie against each other during the casting process.

[0029] Furthermore, it can advantageously be provided that the die is designed in several parts and is configured so that after each casting process, several parts of the die are removed from each other for demoulding.

[0030] Furthermore, it can advantageously be provided that the matrix and / or a mold core consist entirely or partially of titanium nitride, titanium carbonitride, silicon carbide, silicon nitride or aluminum oxide.

[0031] In general, low-pressure casting and die casting are conceivable as suitable casting processes for series production, especially for the casting mold described above. However, the embodiments of the invention also apply to all other casting processes that use permanent molds.

[0032] In particular, the following aspects can be advantageous; they can apply individually or in groups: a) Forming by casting, in which the main contour of the coil is created in a permanent mold that is closed, filled, and opened during the production cycle to remove the solidified coil or casting cluster with coils. b) The shaping contour in the permanent mold can be designed as a ceramic mold insert within a supporting steel tool. c) The Cu melt comes into contact exclusively with the ceramic inserts or ceramic surfaces in the tool. d) The ceramic inserts consist entirely or partially of titanium nitride, titanium carbonitride, silicon carbide, silicon nitride, aluminum oxide, or similar ceramic materials. e) The inner contour of the coil is formed by a permanent core of the tool as a core pull, which dips in one or two directions for demolding in order to be able to demold the undercuts on the inner contour of the coil. The materials of the permanent core can be the materials listed under d).The avoidance of lost cores is advantageous in order to optimize cycle times and manufacturing costs. f) As an alternative to e), a lost core made of salt or water-soluble plastic or other materials can be used to form the internal coil geometry, so that the core can be rinsed out / dissolved / destroyed after the casting process. g) In conjunction with a simplified method of manufacturing molds by introducing helical cavities into a machinable mold body using a rotating and simultaneously translationally moved cutting tool, the geometry of the ceramic inserts is significantly simplified, so that the use of lost cores can generally be dispensed with. h) The ceramic mold inserts can also be manufactured, for example, by freeze-gelling (according to EP1651404 B1).i) Once the maximum service life has been reached or if the mold inserts are damaged, they are replaced using a quick-change system in the tool. Appropriate mold inserts must be manufactured and kept in sufficient quantities and can be replaced as quickly as possible. j) Alternatively, the mold inserts are produced layer by layer from a ceramic powder bed using additive manufacturing. Contour-fitting cooling channels can be integrated into the mold inserts to shorten cycle times and improve the microstructure of the copper coils. k) The ceramic inserts are further developed based on common structural ceramics such as titanium nitride, titanium carbonitride, silicon carbide, silicon nitride, or aluminum oxide and are adapted and optimized with regard to the thermal cycling stresses encountered during casting.I) The optimization factor in material development for the ceramic mold insert is the lowest possible thermal expansion coefficient and good demoldability of the cast coils. m) As an alternative to d), the shaping contour can also be designed as a ceramic coating or as a ceramic-coated mold insert within a supporting steel tool of the permanent mold.

[0033] The invention makes it possible to produce cast coils made of copper or copper alloys in permanent molds, thus significantly increasing productivity in series production. At the same time, the manufacturing costs of the process are reduced and the technological advantages of cast coils can be utilized for electrical machines.

[0034] The invention is illustrated by way of example in the figures of a drawing and explained below. Fig. 1 shows a cross section of a coil on a tooth / pole of a sheet of an electric motor and Fig. 2 shows a cross section of the die and the steel mold, Fig. 3 shows a cross section of the die and a core pull, Fig. 4 shows a partial body of the core pull, and Fig. 5 shows a perspective view of a core pull.

[0035] Figure 1 shows a longitudinal section through a cast body to be produced by casting in the form of an electrical coil 1 made of copper, the longitudinal axis of which is designated by 2. The outer diameter D of the coil 1 increases linearly from the first end 1a, which is closest to a rotational axis when installed in an electrical machine, to the second end 1b. The height H of the individual windings 3, 4, 5 decreases towards the second end 1b. The inner diameter of the coil 1 is constant over its length. The coil is in Figure 1shown in its position surrounding a tooth / pole 6 of a laminated core of an electrical machine. Another pole is designated 7.

[0036] In Figure 2 A steel mold 8 is shown, the inner contour 9 of which precisely accommodates a die 10 in the form of a two-part conical ceramic insert. The die is divided along line 11 into the two parts 10a and 10b. The gating system is not shown for clarity.

[0037] Within the die 10, a mold core 12 is shown, which in this example is cylindrically designed as a core pull. On the inside of the die 10, exemplary webs 10c, 10d are shown, which create or represent the spaces between individual turns, either completely or partially, during casting. When inserted into the supporting tool in the form of the steel mold 8, the die is radially compressed in the direction of arrow 13 and seals along the joint 11. The metal casting material, for example, copper, then comes into contact exclusively with the die 10 and the mold core 12, both of which can be made of ceramic or coated with a ceramic material.

[0038] In the Figure 3Shown in cross-section is the die 10 and a core pull 12 with partial bodies 12a, 12b, 12c, which are movable relative to one another and together form the circumferential surface 12d of the core pull 12. Each of the partial bodies 12a, 12b, 12c forms a prismatic body with a partially cylindrical, curved surface. In possible designs, the partial bodies 12a, 12b, 12c can also be wedge-shaped. In the areas where the partial bodies abut one another, their wall thickness is less than in the remaining areas, so that free wedges are formed between the partial bodies 12a, 12b, 12c, which enable the core pull 12 to collapse radially.

[0039] During the casting process, the partial bodies 12a, 12b, 12c can be supported in the central cavity 12e formed between them by a support body 12f, which is designed to be either axially withdrawable or destructible as a dissolvable body for the core puller 12 to collapse. After removal of the partial body designed as a support body 12f, at least one of the remaining partial bodies 12a, 12b, 12c can collapse in the radial direction.

[0040] The core puller 12 can, for example, also have helical webs running around its cylindrical circumference, which separate individual turns of the coil to be cast from one another.

[0041] Figure 5 shows a perspective view of a multi-part core pull without the support body.

Claims

1. A casting mold for producing helical cast bodies (1), in particular coils, springs or spirals, comprising a die (10) in the form of a permanent mold, which establishes the outer contour of the helical bodies and is made of a ceramic material, or is coated with a ceramic material, comprising a supporting tool (8), which supports the die (10) from the outside, and comprising a mold core, which defines the continuous opening inside the helical body (1),wherein mold core is designed as a core puller (12), wherein the mold core has at least one dissolvable or destructible sub-body as a support body (12f) and a plurality of non-dissolvable sub-bodies (12a, 12b, 12c) which can be used as a permanent mold, wherein the sub-bodies (12a, 12b, 12c) which can be used as a permanent mold consist of a ceramic material or are coated with a ceramic material, wherein during the casting process, the sub-bodies (12a, 12b, 12c) can be supported in a central cavity (12e) formed between them by the support body (12f), wherein the support body (12f)is designed as a dissolvable body so as to be destructible, for the core puller (12) to be moved, wherein the mold core is designed in such a way that only the parts of it that can be used as a permanent mold come into contact with a casting material or a melt.

2. The casting mold according to claim 1, characterized in that the core puller (12) comprises one or more projections, which define the helix and separate different, mutually adjoining windings of the helix of the cast body from one another.

3. The casting mold according to claim 1 or 2, characterized in that the core puller moves in at least one or two directions during demolding.

4. The casting mold according to claim 1 or 2, characterized in that the core puller rotates during demolding.

5. The casting mold according to claim 1 or 2, characterized in that the core puller is made of a ceramic material, in particular a foundry sand material, which can be dissolved after a casting process.

6. A casting mold according to any one of claims 1 to 5, characterized in that the die (10) comprises one or more projections (10c, 10d), which define the helix and separate different, mutually adjoining windings (3, 4, 5) of the helix of the cast body (1) from one another.

7. The casting mold according to claim 6, characterized in that the die (10) has a multi-piece design and is configured such that multiple parts of the die are removed from one another after each casting process for demolding.

8. A casting mold according to any one of claims 1 to 7, characterized in that the die (10) and / or a mold core (12) are entirely or partially made of titanium nitride, titanium carbonitride, silicon carbide, silicon nitride or aluminum oxide.