Magnetoresistive element for detecting a magnetic field on a Z-axis

Description

Technical domain

[0001] The present invention concerns a magnetoresistive element comprising a sense layer, for measuring an external magnetic field along an axis substantially perpendicular to the plane of the sense layer. The present invention further concerns a method for operating the magnetoresistive element.Related art

[0002] Currently, magnetic sensors are widely used in cell phones and other mobile devices as electronic compass. For a two-dimensional magnetic field in an X-Y plane, measurement of the X and Y components of the magnetic field within the plane may be implemented by using two orthogonal sensors, but for the measurement on the magnetic field in a Z-axis direction there are many difficulties. The following solutions are typically utilized.

[0003] One solution includes a separate single-axis planar magnetoresistive sensor installed perpendicular to a two-axis planar sensor. This solution requires assembling two different sensors, the X-Y two-axis magnetoresistive sensor and the Z-axis magnetoresistive sensor.

[0004] Another solution includes a flux guide to convert a magnetic field from the Z-axis direction into magnetic field components in the X- and Y-axis directions. For example, document US2012206137 discloses a single-chip three-axis AMR sensor, which implements measurement of a magnetic field in the Z-axis direction by placing a flux guide above in-plane sensors. In such solution, the magnetic field in the Z-axis direction is not fully converted into the X- and Y-axis directions. In addition, such sensor design needs to use a specific algorithm for calculating the magnetic field in the Z-axis direction, which makes the sensor design more complicated.

[0005] Yet another solution includes micro-machining a substrate to form an inclined plane, onto which a sensor that partially senses the magnetic field in the Z-axis direction is deposited. Such a process is very complicated, has a low spatial efficiency, and may cause some shadowing effects in the deposition of the sensor, which may degrade the performance of the sensor.

[0006] Yet another solution includes using magnetic materials with perpendicular magnetic anisotropy for measuring the magnetic field in the Z-axis direction. For example, document US20130168787 discloses a magnetic sensor which measures a Z-axis component of an external magnetic field by using a perpendicular magnetic anisotropy material. The perpendicular magnetic anisotropy material has a high coercivity, and low magnetoresistance.

[0007] Reference: RAHMAN N ET AL: "Thickness dependence of magnetization dynamics of an in-plane anisotropy ferromagnet under a crossed spin torque polarizer", JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, ELSEVIER, AMSTERDAM, NL, vol. 439, 8 May 2017 (2017-05-08), pages 95-100, discusses magnetization dynamics of a soft layer with in-plane anisotropy and under a spin transfer torque from a perpendicularly magnetized reference layer.

[0008] Document EP3726237 discloses a sensor including first and second magnetoresistive sensor elements configured to produce respective first and second output signals in response to an external magnetic field. The first and second magnetoresistive sensor elements form a gradient unit, each of the magnetoresistive sensor elements includes a sense layer having a vortex magnetization pattern.Summary

[0009] The present invention according to appended claim 1 concerns a magnetoresistive element comprising a reference layer having a fixed reference magnetization, a sense layer having a free sense magnetization and a tunnel barrier layer between the reference and sense layers. The magnetoresistive element is configured to measure an external magnetic field oriented substantially perpendicular to the plane of the layers. The reference magnetization is oriented substantially perpendicular to the plane of the reference layer. The sense magnetization comprising a vortex configuration in the absence of an external magnetic field. The vortex configuration is substantially parallel to the plane of the sense layer and has a vortex core magnetization direction along an out-of-plane axis substantially perpendicular to the plane of the sense layer. The magnetoresistive element has a lateral dimension being smaller than 300 nm, the sense layer has a thickness being greater than 100 nm and a sense magnetization below 850 kA / m at room temperature.

[0010] The present invention according to appended claim 9 further concerns a method for operating the magnetoresistive element, comprising: selecting the direction of the a vortex core by applying an initialization magnetic field until the vortex expulsion field is reached and reducing the initialization magnetic field below a nucleation field at which vortex re-forms; wherein the vortex core magnetization direction is determined by the polarity of the vortex expulsion field and the nucleation field; and measuring an external magnetic field.

[0011] The magnetoresistive element disclosed herein can measure an external magnetic field along an out-of-plane axis substantially perpendicular to the plane of the sense layer. The vortex configuration of the magnetoresistive element can have an expulsion field greater than 200 mT or 250 mT.

[0012] The magnetoresistive element has low hysteresis, less than 300 µV / V for external magnetic field magnitudes up to the expulsion field, and high linearity, i.e., less than 2% or 1% error.Short description of the drawings

[0013] Exemplar embodiments of the invention are disclosed in the description and illustrated by the drawings in which: Fig. 1 illustrates a magnetoresistive element, according to an embodiment; Fig. 2 shows a magnetization curve of the magnetoresistive element; Fig. 3 shows an enlarged view of a portion of the reversible linear portion of the magnetization curve of Fig. 2; Fig. 4 report magnetization curves for several thickness of the sense layer and for the magnetoresistive element having a lateral dimension of 250 nm; Fig. 5 report magnetization curves for several thickness of the sense layer and for the magnetoresistive element having a lateral dimension of 450 nm; Fig. 6 reports the sensitivity of the magnetoresistive element as a function of the thickness of the sense layer; Fig. 7 shows the magnetization curve for the magnetoresistive element having a lateral dimension of 250 nm, a sense layer having a thickness of 110 nm and a magnetic moment of 600 kA / m; Fig. 8 shows the magnetization curve for the magnetoresistive element having a lateral dimension of 250 nm, a sense layer having a thickness of 46 nm and a magnetic moment of 400 kA / m; and Fig. 9 illustrates a reference layer of the magnetoresistive element, according to an embodiment. Examples of embodiments

[0014] Fig. 1 illustrates a magnetoresistive element 2, according to an embodiment. The magnetoresistive element comprises a reference layer 21 having a fixed reference magnetization 210, a sense layer 23 having a free sense magnetization 230 and a tunnel barrier layer 22 between the reference layer 21 and the sense layer 23. The sense magnetization 230 comprises a vortex configuration substantially parallel to the plane of the sense layer 23 in the absence of an external magnetic field 60. The reference layer 21 can have perpendicular magnetic anisotropy (PMA) such that the reference magnetization 210 is oriented substantially perpendicular to the plane of the reference layer 21.

[0015] The magnetoresistive element 2 can measure an external magnetic field 60 being oriented substantially perpendicular to the plane of the reference and sense layers 21, 23.

[0016] The sense layer 23 has a sense magnetization 230 direction distribution with a vortex configuration, whereby the vortex magnetization curls in a circular path along the edge of the sense layer 23 and around a vortex core 231. The vortex magnetization direction may be arranged in a clockwise direction and may also be arranged in a counterclockwise direction. During normal sensor operation, the magnetization of the vortex core 231 can vary in accordance with the external magnetic field 60 in a direction substantially perpendicular to the plane of the sense layer 23 (or direction ±z). Referring to Fig. 1, the magnetization of the vortex core 231 can be oriented in an upward direction (i.e., toward the direction +z) or in a downward direction (i.e., toward an opposite direction -z). The size of the vortex core increases or decreases in the direction +z or -z when the magnitude of the external magnetic field 60 increases or decreases, respectively. However, during normal sensor operation the vortex core magnetization direction ±z, or vortex core magnetization polarity, is fixed.

[0017] The vortex configuration provides a linear and non-hysteretic behavior in a large magnitude range of the external magnetic field 60, for practical size of the magnetoresistive element 2 and thickness of the sense layer 23. The linear and non-hysteretic portion of the magnetization curve facilitates the measurement of small variations of the external magnetic field 60. The vortex configuration is thus advantageous for magnetic sensor applications.

[0018] Fig. 2 shows a magnetization curve (or hysteresis response) of the magnetoresistive element 2 as a function of the external magnetic field 60 (indicated by the symbol B extz ). Here, "mz" corresponds to the averaged component along direction ±z of the sense magnetization (<Mz> or z-component of the sense magnetization Ms), normalized to the sense magnetization Ms (mz=<Mz> / Ms). In the case of a vortex configuration, the magnetization curve is characterized by a linear increase of the vortex core magnetization with the external magnetic field B extz until the vortex expulsion field is reached at the H expl point. At this point the sense magnetization 230 becomes magnetically saturated (represented by the arrow pointing upwards (the direction +z). The vortex state in the sensing layer 23 is recovered when the external magnetic field B extz is reduced below a nucleation field H nucl . When the external magnetic field B extz is decreased until the vortex expulsion field is reached at the H expl point (negative external magnetic field B ext ) the sense magnetization 230 becomes magnetically saturated (represented by the arrow pointing downwards (the direction -z). The nucleation field H nucl is the field at which vortex re-forms after vortex expulsion. As long as the magnitude of the external magnetic field B extz is below the absolute value corresponding to the expulsion field (+ / -H expl ), the magnetization curve comprises a reversible linear portion corresponding to the variation of the vortex core 231 magnetization with the external magnetic field 60. The vortex core magnetization polarity can be reversed (between direction z and -z) when the expulsion field H expl is exceeded.

[0019] Fig. 3 shows an enlarged view of a portion of the reversible linear portion of the magnetization curve of Fig. 2. The magnetization curve to the external magnetic field B extz is shifted towards higher magnetization values when the external magnetic field B extz is decreased from the nucleation field H nucl , compared to when the external magnetic field B extz is increased from the nucleation field H nucl . In other words, the reversible linear portion of the magnetization curve exhibits a hysteresis due to the different vortex core magnetization polarity, that is the direction of the vortex core 231 magnetization.

[0020] The vortex core magnetization polarity depends on the nucleation field + / -H nucl at which the vortex re-forms after vortex expulsion. It is then possible to operate the magnetoresistive element 2 in only one of the branch of the magnetization curve, for example the branch A (see Fig. 3) when the field is swept back to negative from the positive nucleation field +H nucl (and the positive vortex expulsion field +H expl ) or the branch B when the field is swept back to positive from the negative nucleation field - H nucl (and the negative vortex expulsion field -H expl ).

[0021] A method for operating the magnetoresistive element 2 can comprise the steps of selecting the direction z or -z of the vortex core magnetization (vortex core magnetization polarity) by applying an initialization magnetic field to the magnetoresistive element 2 until the vortex expulsion field H expl is reached and then, reducing the initialization magnetic field below the nucleation field H nucl at which the vortex re-forms. The vortex core magnetization polarity is determined by the polarity of the vortex expulsion field H expl and the nucleation field H nucl . The method further comprises the step of measuring an external magnetic field 60.

[0022] After applying an initialization magnetic field, the method can further comprise a step of programming the magnetoresistive element 2 to program the orientation of the reference magnetization 210. The programming step can be performed by applying a programming magnetic field adapted to orient the reference magnetization 210. The programming step can further comprise heating the magnetoresistive element 2 to a temperature where the orientation of the reference magnetization 210 is facilitated, for example at a temperature where the reference magnetization 210 is unpinned. Heating the magnetoresistive element 2 can be performed by using resistive heating or laser heating. During the programming step, the vortex core magnetization polarity can be considered fixed.

[0023] It should be noted that the operation of the magnetoresistive element 2 is not limited to any specific portion of the branches A or B shown in Fig. 3. Indeed, the magnetoresistive element 2 can be operated anywhere in the linear region of branch A or branch B (the latter with a vortex magnetization polarity reversed relative to the one in branch A).

[0024] In any case, the magnetoresistive element 2 should measure the external magnetic field 60 below the vortex expulsion field + / -H expl . The vortex magnetization polarity is fixed during sensor operation and is independent of vortex chirality (clockwise or counterclockwise).

[0025] The obtention of a vortex configuration in the sense layer 23 depends on a number of factors, including materials properties of the sense layer 23. Generally, the vortex configuration is favored at zero applied field by increasing the aspect ratio of the thickness on the diameter of the sense layer 23. The aspect ratio is still typically much less than 1 (for example 0.01 to 0.5). Moreover, the values and the slope of the linear part of the magnetization curve of Fig. 2 are strongly dependent on the size of the sense layer 23.

[0026] In particular, the vortex configuration can be characterized by its susceptibility χ, which corresponds to the slope of the linear region of the magnetization curve: χ = ∂ M / ∂ H ext

[0027] The sensitivity S of the magnetoresistive element 2 is then proportional to the product between the susceptibility χ and the tunnel magnetoresistance (TMR) of the magnetoresistive sensor element 2: S = χ ∗ TMR

[0028] Fig. 4 reports magnetization curves to the z-aligned external magnetic field B extz on the magnetization of the sense layer 23, for several thickness of the sense layer 23, namely for thicknesses of the sense layer 23 between 10 nm and 60 nm. The magnetoresistive element 2 has a lateral dimension D of about 250 nm. Fig. 4 shows an increase in the slope of the magnetization curve, and thus the susceptibility χ, with increasing thickness of the sense layer 23. For a given TMR value, increasing the thicknesses of the sense layer 23 results in an increase of the sensitivity S of the magnetoresistive element 2. This is in contrast to the case of a vortex configuration in the the plane of the sense layer 23 and having a vortex core magnetization that is reversibly movable substantially parallel to the plane of the sense layer 23.

[0029] Fig. 5 reports magnetization curves to the z-aligned external magnetic field B extz of the sense layer 23 for several thickness of the sense layer 23, namely for thicknesses of the sense layer 23 between 10 nm and 60 nm. The magnetoresistive element 2 has a lateral dimension of about 450 nm. Figs. 4 and 5 show that the susceptibility χ increases, and for a given TMR value the sensitivity S of the magnetoresistive element 2 increases, with decreasing smaller lateral dimension D of the magnetoresistive element 2. For given thicknesses of the layers 21, 23, the value the sensitivity S increases with increasing the aspect ratio t / D of the thickness t to the diameter (lateral dimension) D of the magnetoresistive element 2.

[0030] The sensitivity S of the magnetoresistive element 2 is plotted as a function of the thickness of the sense layer 23 in Fig. 6. The sensitivity S was simulated for lateral dimensions D of the magnetoresistive element 2 of 150 nm, 200 nm and 250 nm, and for magnetizations of the sense layer 23 of 400 and 600 kA / m. The TMR value of the magnetoresistive element 2 was assumed to be 100%. Fig. 6 shows that the higher values of sensitivity S are obtained for a lateral dimension of 150 nm and a magnetization of 400 kA / m. For a given TMR value, decreasing the sense magnetization 230 of the sense layer 23 results in an increase of the sensitivity S of the magnetoresistive element 2. In the whole text of this application, the expression "sense magnetization" is used indifferently for "saturation sense magnetization" or "spontaneous sense magnetization", where saturation magnetization has its usual meaning of the maximum induced magnetic moment.

[0031] In term of design rules for the magnetoresistive element 2 that can measure an external magnetic field along an out-of-plane axis substantially perpendicular to the plane of the sense layer and having high working field range, low hysteresis, high linearity and sufficient sensitivity, the results shown above suggest providing the magnetoresistive element 2 where the reference layer 21 has a reference magnetization 210 oriented substantially perpendicular to the plane of the reference layer 21, and where the sense layer 23 has a sense magnetization 230 comprising a vortex configuration in the absence of an external magnetic field 60. The vortex configuration should be substantially parallel to the plane of the sense layer 23 and have a vortex core 231 magnetization along an out-of-plane axis 50 substantially perpendicular to the plane of the sense layer 23.

[0032] Moreover, in term of design rules for the magnetoresistive element 2 having high working field range (such as 60 mT or more), low hysteresis (such as less than 300 µV / V) for external magnetic field magnitudes up to the expulsion field, high linearity (such as less than 2% or 1% error) and sufficient sensitivity, the magnetoresistive element 2 should have small lateral dimension D (or high aspect ratio). According to the present invention, the magnetoresistive element has a lateral dimension D below 300 nm, preferably below 250 nm, or preferably below 150 nm, and a small sense magnetization 230 of the sense layer 23, which is below 850 kA / m, possibly below 600 kA / m or possibly below 400 kA / M. Furthermore, the sense layer 23 has a thickness greater than 100 nm.

[0033] In one aspect, the thickness of the sense layer 23 can be thick (more than 100 nm) and the sense magnetization 230 of the sense layer 23 can have a value that corresponds to typical saturation magnetization values found in conventional magnetoresistive elements (for example 600 kA / m or larger, but less than 850 kA / m). In a first example (Fig. 7), the magnetoresistive element 2 has a lateral dimension D of 250 nm and the sense layer 23 has a thickness of 110 nm. The ferromagnetic material forming the sense layer 23 can comprise a ferromagnetic alloy having a sense magnetization of 600 kA / m or larger (here 600 kA / m).

[0034] In an alternative configuration, not covered by the scope of the present invention, the low sense magnetization of the sense layer 23 can be obtained by decreasing the thickness (for example below 50 nm) and / or by a proper selection of the ferromagnetic material forming the sense layer 23 such as to obtain a low sense magnetization (for example lower than 600 kA / m). In a second example (Fig. 8), the magnetoresistive element 2 has a lateral dimension D of 250 nm, the sense layer 23 has a thickness of 46 nm and has a sense magnetization of 400 kA / m. The sense layer 23 can be formed a ferromagnetic alloy having a low magnetization.

[0035] Figs. 7 and 8 show that a substantially identical magnetization curve is obtained for the magnetoresistive element 2 of the first and second examples. In both examples, the expulsion field H expl can be about 300 mT and the nucleation field H nucl can be about 200 mT.

[0036] The magnetoresistive element 2 can have a sensitivity S of 1 mV / V or higher, for TMR = 100%. The sensitivity S can be further increased by increasing TMR.

[0037] Referring again to Fig. 1, the reference layer 21 can comprise a synthetic antiferromagnetic (SAF) structure including a first reference sublayer 211 in contact with the tunnel barrier layer 22 and a second reference sublayer 212 separated from the first reference sublayer 211 by a coupling layer 213, wherein the coupling layer 213 antiferromagnetically couple the first reference sublayer 211 to the second reference sublayer 212. Each of the first and second reference sublayer 211, 212 has PMA such that a reference magnetization 210 is oriented substantially perpendicular to the plane of the first and second reference sublayer 211, 212 and in opposite directions.

[0038] In an embodiment represented in Fig. 9, each of the first and second reference sublayer 211, 212 includes a multilayer structure. In particular, each of the first and second reference sublayer 211, 212 can include a plurality of alternating first metallic layers 201 and second metallic layers 202. For example, the first metallic layer 201 can comprise an ultrathin Co layer and the second metallic layer 202 can comprise an ultrathin Pt layer. Although the second metallic layer 202 preferably comprises Pt, other metals that provide PMA can also be used.

[0039] In one aspect, the ultrathin Co layer 201 can have a thickness between 0.4 nm and 0.6 nm. The ultrathin Pt layer 202 can have a thickness between 0.2 nm and 0.4 nm. The coupling layer 213 can be a Ru layer. Although the coupling layer 213 preferably comprises Ru, other metals that generate RKKY coupling can also be used.

[0040] The reference layer 21 comprising the SAF structure according to the configuration of Fig. 9 can achieve a field stability of greater than 300 mT to 400 mT.Reference numbers and symbols

[0041] 2magnetoresistive element 21reference layer 201first metallic layer 202second metallic layer 210reference magnetization 211first reference sublayer 212second reference sublayer 213coupling layer 22tunnel barrier layer 23sense layer 230sense magnetization 231vortex core 50out-of-plane axis 60external magnetic field A, Bbranch of the magnetization curve B extz external magnetic field along direction z Dlateral dimension, diameter H expl expulsion field H nucl nucleation field mzmagnetization tthickness

Claims

1. Magnetoresistive element (2) comprising a reference layer (21) having a fixed reference magnetization (210), a sense layer (23) having a free sense magnetization (230) and a tunnel barrier layer (22) between the reference layer (21) and the sense layer (23); the magnetoresistive element (2) being configured to measure an external magnetic field (60) oriented substantially perpendicular to the plane of the layers (21, 23); wherein the reference magnetization (210) is oriented substantially perpendicular to the plane of the reference layer (21); and wherein the sense magnetization (230) comprises a vortex configuration in the absence of an external magnetic field (60), the vortex configuration being substantially parallel to the plane of the sense layer (23) and having a vortex core (231) magnetization along an out-of-plane axis (50) substantially perpendicular to the plane of the sense layer (23); characterized in that the magnetoresistive element (2) has a lateral dimension being smaller than 300 nm, the sense layer (23) has a thickness being greater than 100 nm and a sense magnetization (230) below 850 kA / m at room temperature.

2. Magnetoresistive element according to claim 1, having a lateral dimension being smaller than 250 nm or 150 nm.

3. Manetoresistive element according to any one of claims 1 and 2, wherein the sense magnetization (230) is between 400 kA / m and 600 kA / m at room temperature.

4. Magnetoresistive element according to any one of claims 1 to 3, wherein the reference layer (21) comprises a synthetic antiferromagnetic (SAF) structure including a first reference sublayer (211) in contact with the tunnel barrier layer (22) and a second reference sublayer (212) separated from the first reference sublayer (211) by a coupling layer (213) antiferromagnetically coupling the first reference sublayer (211) to the second reference sublayer (212).

5. Magnetoresistive element according to claim 4, wherein each of the first and second reference sublayer (211, 212) comprises a plurality of alternating first metallic layers (201) and second metallic layers (202).

6. Magnetoresistive element according to claim 5, wherein the first metallic layers (201) have a thickness between 0.4 nm and 0.6 nm and the second metallic layers (202) have a thickness between 0.2 nm and 0.4 nm and the second metallic layer (202).

7. Magnetoresistive element according to any one of claims 1 to 6 configured such that the vortex configuration has an expulsion field greater than 200 mT or 250 mT.

8. Magnetoresistive element according to any one of claims 1 to 7, having a linearity error less than 2%.

9. Method for operating the magnetoresistive element (2) according any one of claims 1 to 8, comprising: selecting the direction (z, -z) of the vortex core magnetization by applying an initialization magnetic field until a vortex expulsion field (Hexpl) is reached and reducing the initialization magnetic field below a nucleation field (Hnucl) at which the vortex re-forms; wherein the vortex core direction (z, -z) is determined by the polarity of the vortex expulsion field (Hexpl) and the nucleation field (Hnucl); and measuring an external magnetic field (60).

10. Method according to claim 9, wherein said measuring an external magnetic field (60) is performed for an external magnetic field (60) below the vortex expulsion field (Hexpl).