Improved Hybrid Smelting System

Abstract

The present invention relates to improving induction smelting processes. The present invention relates to a hybrid combination of plasma on induction for a super-efficient continuous smelting process and real-time monitoring and regulation of the smelting process. Disclosed is a hybrid smelting system including a real-time controller and a reduction zone, where plasma on induction heating continuously smelts the feed material fed into the reduction zone. Slag and reduced metal (alloy) are released under the supervision of the real-time controller.

Description

[Technical field]

[0001] This invention relates to improvements in induction smelting processes, and in particular to improved means for controlling a hybrid combination of induction and plasma for an ultra-high efficiency continuous smelting process, as well as real-time monitoring and regulation of the smelting process.

[0002] Benefits include removal of residual metals from ores, concentrates, and slag waste; increased metal unit yields; the ability to smelt fine materials; real-time analysis of feed materials for precise addition of fluxes and reductants; real-time control of the smelting process with a backscattered X-ray unit; and continuous throughput smelting.

[0003] A particular advantage of the present invention is that the system allows for a significant reduction in power consumption, for example at least 50% over current smelting processes. [Background technology]

[0004] In smelting, metal oxides, reducing agents, and fluxes are mixed in a furnace where heat-induced chemical reactions produce molten metal. The metal oxides, reducing agents, and fluxes are fed to the furnace as solid feed materials. The metal oxide feed material may be crushed ore. The reducing agent feed material may be a carbonaceous material such as coking coal. In the chemical reaction, the reducing agent reduces the metal oxides and separates oxygen from the molten metal. The flux feed material (e.g., lime or dolomite) is used to catalyze the chemical reaction and chemically combine with undesired impurities or reaction products.

[0005] The molten by-product of the chemical reaction, known as slag, floats on top of the molten metal in the furnace. Above the slag is a space in the furnace where gases from the chemical reaction collect. Air or oxygen-enriched air is blown into this space by a lance to combust the reaction gases. This generates heat, which helps keep the slag and metal in the furnace molten. An exhaust gas duct leads out of the space to remove the burnt reaction gases.

[0006] The mining and mineral processing industry uses AC / DC electric arc furnace technology to smelt lump, fine, and concentrate ores into a variety of base metal products. AC / DC electric arc furnaces can consume up to 4,500 kW of electrical energy per tonne of smelted metal for chromite ores and up to 6500 KW of energy per tonne for other ores due to the high levels of alumina and / or silica oxides present in the smelting concentrate.

[0007] The smelted metal in an AC / DC electric arc furnace is kept molten by forming a thick head of insulating, slush-like slag above the molten metal. A solid feed material of quartz stone (silica) may be fed into the furnace to increase the thickness of the slag. The slag must be kept molten, which also requires a significant amount of energy.

[0008] AC / DC electric arc furnaces require large amounts of electricity and produce significant carbon dioxide emissions.

[0009] Blast furnaces also produce significant carbon dioxide emissions. Blast furnaces are heated by certain grades of steam coal (i.e., low in sulfur, phosphorus, and volatiles) and coking coal for reducing metal oxides to metals. Some or all of the coal may be crushed or powdered into chunks or pellets of certain size and gravity fed into the furnace from the top. Some or all of the coal may be pulverized and injected into the bottom of the blast furnace.

[0010] The feed must remain gas permeable, allowing exhaust gases and air to flow upwardly through the feed and out the top of the furnace.

[0011] If the feed material is too fine, or if clumps of material break up in the furnace, gas and air flow can be restricted, impeding the combustion process and potentially solidifying the molten contents in the furnace bottom, halting the smelting process. If this occurs, the furnace must be shut down and cooled, which can take a week or more. After cooling, all solidification must be removed and the furnace lining repaired before the furnace can be operated again. This process takes a significant amount of time and money.

[0012] Induction furnaces achieve greater energy efficiency than blast furnaces and electric arc furnaces. Induction furnaces produce electromagnetic fields that couple with conductive materials such as metals and carbon. These electromagnetic fields are contained within the furnace body by shunt bars placed around the induction coil, focusing the electromagnetic fields on the material being smelted in the center of the furnace. Electromagnetic coupling with the conductive material allows the induction furnace to transfer energy directly into the material being smelted, producing rapid melting rates.

[0013] However, certain limiting factors restrict induction furnaces from widespread use, such as: the magnetic field in an induction furnace can only couple with conductive materials such as metals and carbon, thereby limiting potential smelting applications; for example, the electromagnetic field from an induction furnace will not couple with non-conductive metal oxides (silica, alumina, magnesium, etc.); the slag content must be less than 6%, thereby limiting the use of induction furnaces as primary smelting furnaces; and, further, the slag material may need to be frequently removed or scraped off from the top of the molten metal as it cools and forms a hard crust that interferes with the smelting or melting process (the crust creates a seal that traps gas-generating molten metal underneath, which can overheat and melt through the refractory lining into the water-cooled induction coil, or cause a gas pressure spike that can also lead to a furnace explosion).

[0014] To prevent the formation of a hard crust, fluxes are added to the smelt to reduce the melting temperature of the slag to that of the metal being processed, and the slag is removed or scraped out of the furnace. However, melting the slag and keeping it molten relies on radiant heat from the molten metal in the furnace. This reliance on radiant heat transfer from the molten metal limits the amount of slag that an induction furnace can safely handle. Therefore, smelting is done in small batches on pre-melted metal in the induction furnace (known as heal smelting), and the slag must be continually removed, making the process inefficient.

[0015] A further constraint relates to the fact that in industrial-scale induction furnaces (capacity of 5 tonnes per hour or more), the electrical frequency of the power supply unit is limited to 2-20 Hz. Moreover, such low-frequency magnetic fields require bulk feed material of 40 mm or more for bonding and therefore cannot bond with fine metal concentrates produced from metal recovery and / or concentrating processes.

[0016] This limiting factor can be overcome by starting the furnace with a "starter" ingot, previously produced by other means, of the required metal. This ingot melts to form a molten pool of metal in the furnace, which radiates heat to the fine concentrate, eventually melting it. However, because it is the radiant heat from the molten metal that heats the slag, and only at the slag-metal interface, and not by an electromagnetic field, there remains a high risk of furnace freeze-out, and thus the possibility of furnace freeze-out is a significant trigger point condition.

[0017] Thus, while conventional induction furnaces are efficient tools for remelting relatively clean metals for the foundry industry, they are less suitable as primary smelting furnaces for fine metal concentrates, lump ores, and ore concentrates. This is due, among other things, to their inability to electromagnetically couple to fine materials and to directly heat slag or non-conductive materials. In addition, conventional induction furnaces do not have a means to continuously discharge the slag and metal produced to maintain continuous operation.

[0018] Scanning systems such as backscatter scanning are known methods for monitoring feed, for example as described in WO-A1-2008 / 142704 and WO-A1-2016 / 124823. Other known monitoring methods include performing batch analysis or real-time continuous analysis.

[0019] US-A1-2005 / 0120754 describes a hybrid smelting system including a furnace with an induction coil, a feed opening, and twin vertically movable plasma electrodes spaced apart within the furnace roof. In WO-A1-96 / 17093, an induction smelting furnace includes a coil and plasma torch assembly with two angled and adjustable electrodes positioned directly beneath the entrance and spaced apart to create a plasma field therebetween.

[0020] WO-A1-2008 / 142704 describes a feed preparation system in which the feeds (ore, reductant, and flux feed) undergo a mixing and pelletizing step.

[0021] However, while these publications address certain inherent inefficiencies in the smelting process, they do not achieve the efficiency required by modern, rapidly increasing economic and environmental standards, namely, each smelting process is still discontinuous and consumes significant amounts of energy.

[0022] The present invention provides a highly energy efficient system for continuous smelting that consumes at least 50-70% less power than conventional furnace systems. In an exemplary embodiment, the present invention consumes 58% less power. Summary of the Invention [Means for solving the problem]

[0023] According to a first aspect, there is a hybrid smelting system including a hybrid combination of plasma on induction. The hybrid smelting system may include a real-time controller and a reduction zone, where plasma on induction heating continuously smelts a feed material fed into the reduction zone and releases slag and reduced metal (alloy) under the supervision of the real-time controller.

[0024] The hybrid smelting system delivers an ultra-efficient continuous smelting process that significantly reduces power consumption.

[0025] According to another aspect, a hybrid smelting system includes a hybrid combination of plasma on induction including real-time monitoring of the hybrid smelting system and means for adjusting operational parameters. The operational parameters may include reduction zone, raw feed material, amount and blend of concentrate vs. reductant vs. flux. To adjust the operational parameters, the hybrid smelting system may include an imaging device for inspecting the material being processed in the furnace, a tap configured to continuously tap the material, and a grinder configured to granulate the final product.

[0026] According to another aspect, there is a hybrid smelting system that includes a hybrid combination of plasma on induction with a residual metal recovery device that can enable a re-smelting step whereby substantially all of the residual metals are recovered from the slag waste.

[0027] The hybrid smelting system may incorporate means for detecting and monitoring the level of the contents and / or indicating a predetermined level, means for triggering the discharge of molten slag at one or more discharges when the contents in the furnace reach a predetermined level, and means for receiving and continuously analyzing information from sensors and / or scanning systems (e.g., for controlled batch analysis of the ore concentrate, temperature, discharge rate, height of at least one agitator, and temperature of a heating element integral with the agitator). The hybrid smelting system may incorporate means for configuring one or more blades / susceptors for agitation.

[0028] The hybrid smelting system enables an ultra-efficient continuous smelting process using a hybrid combination of plasma on induction, using a variable feed size from ultra-fine powder to chunks over 40mm, capable of continuous smelting of any type of material (conductive or non-conductive).

[0029] In a hybrid smelting system, induction coils and plasma fields can work together. The plasma field can heat the contents from above, while the induction field heats the contents from below and from the surroundings. In this way, various energy sources can heat different materials in the furnace (i.e., the plasma field heats the non-conductive materials and the induction field heats the conductive materials). Both non-conductive and conductive materials can be heated together. They can also be heated simultaneously. The hybrid smelting system thus overcomes the inefficiency of electric arc furnaces and blast furnaces, which are limited to non-conductive materials. The hybrid smelting system overcomes the inefficiency of induction furnaces, which require a carbon crucible to provide the magnetic coupling and allow the melting of non-conductive materials. Carbon crucibles are expensive and require frequent replacement as they oxidize or deteriorate. Deterioration of the carbon crucible results in carbon contamination of the molten metal produced, which is a major disadvantage compared to the hybrid smelting system.

[0030] The efficiency of the hybrid smelting system can extend to re-smelting where nearly all the residual metals are recovered from the slag waste, significantly reducing both energy requirements and carbon dioxide emissions.

[0031] The hybrid smelting system can provide real-time monitoring and adjustment of operating parameters. The hybrid smelting system can include sensors, can include electronics for analysis, and can include measurements and sensor feedback to provide real-time end-to-end supervisory control over the operating functions and smelting process. Such data can enable calculation of optimal reduction zones and analysis of the raw feed material. The feed material can be directed through the plasma field.

[0032] The hybrid smelting system may include mechanical manipulators for steering the feed material and / or the reduction zone. The hybrid smelting system may be configured to steer the feed material and / or the reduction zone by controlling an induction coil or plasma generator. The magnetic or plasma fields may be controlled to provide magnetic and / or electric fields that position the feed material and / or the reduction zone.

[0033] An image of material being processed in a furnace where the hybrid smelting system can measure and blend the concentrate with reducing agents and fluxes. The hybrid smelting system can measure and control the smelting feed into the furnace, the height of the melt level in the furnace, the height of the plasma electrodes above the reduction zone, and the power input into the plasma field and induction coils. These measurements, blends, and controls can maintain a set temperature in the furnace and allow for the continuous tapping of material and granulation of the final product.

[0034] The hybrid smelting system can be configured to receive and continuously analyze information from sensors and / or scanning systems (e.g., for controlled batch analysis of ore concentrate, temperature, discharge rate, height of at least one agitator, and temperature of a heating element integral with the agitator, configuration of one or more blades / susceptors for agitation) to detect and monitor the level of contents and / or to indicate a predetermined level, and to trigger the discharge of molten slag at one or more discharge sections when the contents in the furnace reach a predetermined level.

[0035] Further disclosure of the hybrid smelting system, method, and furnace is set forth in the claims.

[0036] The invention will now be described, by way of example only, with reference to the accompanying drawings, in which: [Brief description of the drawings]

[0037] [Figure 1] 1 shows a flow diagram illustrating the operation of a hybrid smelting system. [Diagram 2] FIG. 1 shows a schematic cross-sectional side view of an induction smelting furnace for producing reduced metal and slag from a feed material under the supervision of a hybrid smelting system. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0038] FIG 1 shows a hybrid smelting process flow diagram for a hybrid smelting system 200. FIG 2 shows a hybrid blast furnace 100 that is part of the hybrid smelting system 200.

[0039] The flow diagram in FIG. 1 illustrates how the actuators in a hybrid smelting system work together under the supervision of a real-time controller 202 to transform feed materials including ore 204, graphite / refractory 206, initiator metals 208, and / or fluxes 210 to produce slag 228, reduced metals 230, and syngas 232.

[0040] A feeder 212 under the supervision of the real time controller 202 feeds the feed material into the reduction zone 226. A steering device 216 under the supervision of the real time controller 202 steers the feeder 212 to feed the feed material directly through the high temperature plasma in the reduction zone 226.

[0041] The high temperature plasma is provided by a plasma torch 220, which is regulated by a plasma torch regulator 218 under the supervision of the real time controller 202. Heat is also provided by an induction coil 224, which provides a time-varying magnetic flux in the reduction zone and below the plasma. An induction current regulator 222 regulates the time-varying current of the induction coil 224 under the supervision of the real time controller 202.

[0042] The temperature profile generator 233 communicates with thermometers, IR temperature sensors, and possibly other types of temperature sensors. The temperature profile generator 233 reads the temperatures of the reduced metal 230 below the slag 238, the slag 238 below the plasma 226, and the syngas 232 that is produced within the plasma but is not necessarily temperature sensed therein. In this manner, the real-time controller 202 provides closed-loop control to monitor and / or operate at least one device including, for example, the feeder 212, the dryer 214, the steering gear 216, the plasma torch regulator 218, the plasma torch 220, the induction current regulator 222, the induction coil 224, the reduction zone 226, the weight sensor, and / or the temperature profile regulator 234. These devices are monitored and / or controlled under the supervision of the real-time controller.

[0043] One or more weight sensors monitor the weight of the feed materials 204, 206, 208, 210, as well as the slag 228, reduced metals 230, and syngas 232 flowing in and out of the conduits of the reduction zone 226. The weight sensors communicate in real time with a real time controller 202 to enable adjustment of flow regulators in the feeder 212 and in the conduits outside the reduction zone 226. Inflow / outflow mass balances are thereby controlled by the real time controller 202 to enable operation of the hybrid smelting system.

[0044] Objectives of the hybrid smelting process illustrated by FIG. 1, and in particular the use of a real-time controller, may include maintaining the temperatures of the molten metal and alloy, the slag floating above the molten metal and alloy, and any gases contained above, within preselected ranges of weight, concentration, and / or temperature.

[0045] FIG. 2 illustrates a hybrid blast furnace 100 operating under the supervision of a real-time controller 202 in a hybrid smelting system 200 .

[0046] The hybrid blast furnace 100 includes three zones. Zone 1 25 is the lowest and contains primarily molten metal and alloy during use. Zone 1 25 may also contain small amounts of slag and gases that rise to Zone 2 35. Zone 1 25 is lower and is below Zone 2 35 where lighter slag floats on top of the molten metal and alloy. Molten metal and alloys produced in Zone 2 35 sink into Zone 1 25. Gases generated in Zone 2 35 rise through the slag into Zone 3, the covered space above the slag.

[0047] Zone 3 is primarily a reduction zone. Zone 3 is primarily a reduction zone 226, where reduction occurs under the supervision of real time controller 202. Some reduction and other chemical reactions also occur within zone 1 25 and zone 2 35.

[0048] A feature of the hybrid smelting process 200 is that chemical reactions, such as reduction of feed materials, such as ore 204, graphite refractory 206, and flux 210, occur in Zone 3 above the slag in Zone 2 35. This is because as the feed materials are fed into the covered space of Zone 3, the plasma torches quickly heat the feed materials to a temperature range that sustains the reaction and reduction. Slag and molten metals and alloys are thus produced in Zone 3 and sink into the zones below.

[0049] As shown in Figure 2, there is a container 99 for Zone 1 25 located in the lower portion of the blast furnace 100. The container 99 includes side walls 11, 12 and a bottom floor 13 that form a first wall of the Zone 1 25 reservoir. Molten metals and alloys are held within the Zone 1 25 reservoir.

[0050] Adjacent to the bottom bed 13 is a discharge opening 51. The discharge opening 51 is primarily for discharging molten metal from the bottom of Zone 1 25. The discharge is under the supervision of a real time controller 202 which regulates a valve or elevator 52 which raises a discharge outlet 54.

[0051] Above the side walls 11, 12 of Zone 1 25 is a ledge 17. Resting on the ledge 17 is a second wall 21 of Zone 2 35. Second wall 21 has an inner surface 39. The shape of second wall 21 forms a funnel or step into Zone 1 25. Zone 2 35 has a funnel or stepped cross-section formed by the sloping and / or stepped inner surface 39.

[0052] An inner surface 39 of second wall 21 slopes or steps down to a relatively narrow opening where second wall 21 rests on ledge 17. The width or diameter of the relatively narrow opening is indicated by dimension D1 in Figure 2. Zone 2 35 opens into Zone 1 25 at the relatively narrow opening.

[0053] As shown in Figure 2, there is a slag decant spout inlet 40 into Zone 2 35 and a slag decant spout outlet 41 of the hybrid furnace 100. The slag decant spout is a conduit through the second wall 21 for removing slag from Zone 2 35. The slag decant spout, a teapot spout, rises from the spout inlet 40 at the bottom to the spout outlet 41 at the top.

[0054] The molten slag is decanted through from at or near the bottom of Zone 2 35 where the spout inlet 40 is located within the inner surface 39. Because the spout inlet is near the bottom of Zone 2 35, the conduit prevents the incoming smelting concentrate floating on the surface of the molten slag in Zone 2 35 from being discharged out the side of the furnace. This is a control feature that allows for continuous operation of the hybrid blast furnace and hybrid smelting systems, unlike traditional batching methods. Higher throughput and greater energy efficiency are achieved.

[0055] 2, the thickness of the side walls 11, 12 and bottom floor 13 of zone 1 25 can be compared to the thickness of the second wall 21 around zone 2 35. The second wall 21 around zone 2 35 has a greater thickness relative to the side walls 11, 12.

[0056] The electric coil 42 surrounds and / or is in close proximity to the first walls 11, 12 to generate a time-varying magnetic field within the first zone 25. The first walls 11, 12 must be thin enough to be substantially transparent to the magnetic field generated by the electric coil. The first walls 11, 12 must further be constructed of a non-magnetic and non-conductive material such that the time-varying magnetic field passes efficiently from the coil 42 through the first walls and into zone 1 25.

[0057] Similarly, there is a second electric coil 43 beneath the floor 13 in zone 1 25. The second electric coil 43 also generates a varying magnetic field within the first zone 25 for inductively heating the reduced metal 230 and / or initiator metal 208 within zone 1 25.

[0058] The first walls 11, 12 and floor 13 may include channels or pipes adjacent to or on the exterior surface 15 of the container 99 that carry non-conductive water, oil, or dissolved salts. This liquid may be circulated to cool the first walls 11, 12 and floor 13.

[0059] The second wall 21 of Zone 2 25 does not need to be transparent to the time-varying magnetic field because the slag in Zone 2 35 is non-conductive and is not inductively heated. The second wall 21 may comprise a material different from the material of the first walls 11, 12, 13. The second wall material 21 may be selected primarily for high temperature structural strength and thermal insulation.

[0060] Considering Figure 1 in conjunction with Figure 2, an initiator metal 208 may be fed into a container and melted by electric coils before the other feed materials ore 204, graphite / refractory 206, and flux 210 to prime the furnace 100. An advantage of the hybrid smelting system 200 is that an initiator metal / alloy 208 is not required since the plasma provides the reduced metal immediately after the other feed metals are fed into the plasma. Thus, a conductive metal is available for the time-varying magnetic field to heat.

[0061] A cover 31 rests on the second ledge 34 of the second wall 21. Cover 31 for closing the container 99. A feeder 212, not shown in FIG. 2, has an access port through the cover 31 for feeding materials including ore 204, graphite / refractory 206, initiator metal 208, and / or flux 210 into zone 3 above zone 2 35.

[0062] There is a torch 61 in Zone 3 beneath cover 31. Torch 61 includes an electrode 63 for striking an arc to generate plasma in Zone 3. The plasma torch 61 is positionable and displaceable above the level of slag discharge opening 41 because the level of slag in Zone 2 35 is at or below the level of slag discharge opening 41.

[0063] 1 in conjunction with FIG. 2, within vessel 99, torch 61 is movable from below slag discharge opening 41 to above slag discharge opening 41 and vice versa. There is also a steering device 216 for directing the feed material to torch 61. Steering device 216 may be supported by cover 31. The feed materials ore 204, graphite refractory 205, and flux 210 are heated by the plasma in zone 3 where they undergo chemical reactions and reduction to produce slag that sinks in zone 2 35 and molten metal and alloy that sinks in zone 1 25.

[0064] The induced current keeps the molten metal in Zone 1 25 above its melting temperature.

[0065] Initially, the initiator metal / alloy 208 can be loaded and inductively heated in Zone 1 25, although an initiator metal / alloy 208 is not required due to the high temperature plasma torch in Zone 3 that brings about the molten metal and alloy from the feed material.

[0066] In one embodiment, the hybrid smelting system 200 shown in FIG. 1 controls an induction hybrid smelting system that includes induction furnace technology known as an induction smelting reduction furnace (IRF), as shown in Zone 1 25 and Zone 2 35 in FIG.

[0067] The IRF is configured to accept feed material (which term includes lump ore, blended fines, smelted concentrate, and pelletized concentrate). However, in a hybrid smelting system 200, there is a hybrid furnace as shown in FIG. 2. The hybrid furnace includes a feed system for introducing the feed material into Zone 3 of the furnace through a furnace inlet. In the hybrid smelting system, below Zone 3 is an upper slag zone, Zone 2 35. Below Zone 2 35 is a lower molten metal zone, Zone 1 25.

[0068] The hybrid smelting system includes an induction coil for heating the molten metal, which transfers energy to the molten metal in Zone 1 25, to keep the slag at the same or similar temperature as the molten metal, avoiding "freezing out" the furnace. Thus, the feed materials 204, 206, 210 can be first heated and reduced, followed by the plasma torch 61. There is also radiative heat transfer from the molten metal in Zone 1 25 to the slag in Zone 2 35, keeping the slag in a safe, molten, low viscosity liquid state.

[0069] The hybrid smelting system 200 includes a plasma energy source that delivers energy to the slag via a plasma torch electrode 63 .

[0070] The hybrid smelting system 200 combines heating of ore 204, graphite / refractory 206, initiator metal 208, and flux 210 feed materials in a furnace where the feed materials are directly heated by electromagnetic induction from coils 41, 43 adjacent to Zone 1 25. There is also subsequent Joule heating (e.g., for conductive contents) and radiative heat transfer (e.g., for non-conductive contents) from both the molten metal pool and the plasma energy source.

[0071] In an exemplary embodiment, the hybrid smelting system shown in combination by FIGS. 1 and 2 includes sensors and electrical systems configured to monitor and adjust IRF operating parameters, including:

[0072] 1i / Monitoring the drying of the raw concentrate by the dryer 214 as it passes through the rotary drying kiln. The raw material may include refractory metals and ores of refractory metals selected from titanium, vanadium, chromium, niobium, molybdenum, zirconium, ruthenium, rhodium, tantalum, tungsten, rhenium, osmium, iridium, and alloys containing these refractory metals, reactive metals selected from zirconium, titanium, and beryllium, and alloys containing these metals. The raw material may also include recovered fine chromium units in the form of chromite, chromium-rich spinel, and ferrochrome metal. The raw material may include components including graphite or graphite infiltrated or contaminated with refractory metals.

[0073] 1ii / The temperature and speed of the rotary kiln are adjusted to dry the raw concentrate to a moisture content of, for example, less than 1%.

[0074] 2 / Analyze the feed concentrate of ore 204, graphite / refractory 206, and initiator metals 208. The analysis is performed, for example, as the dried raw concentrate is conveyed into the batching mixer. The feed concentrate passes through an elemental analysis system on a belt. The hybrid smelting system receives an analysis of the feed concentrate (e.g., by techniques such as prompt gamma neutron activation analysis (PGNAA)) that indicates the percentage of major elements in the concentrate, including oxygen, carbon, and sulfur content. The hybrid smelting system accurately calculates the amount of flux 210 and reductant to be added into the mixing vessel with the feed concentrate of ore 204, graphite refractory 206, and / or initiator metals 208 before being fed into the hybrid furnace as shown in FIG. 2.

[0075] 3 / Receive weight measurements from the mixing vessel to determine the amount of ore 204, graphite / refractory 206, and / or initiator metal 208 concentrate, determine the amount of flux 210 and reducing agent to be released into the mixing vessel, and control the screw feeds that introduce the flux and reducing agent.

[0076] 4 / Simultaneously monitor and control the rate at which a feed system 214, such as a screw feed injection system (SFIS), injects smelter concentrate into the IRF unit and other factors including:

[0077] 4 / (i) Operation of the Hybrid Furnace's Internal Thermal Processes and Mechanical Operations - A Backscatter Scanning System (BSS) located along the side of the Hybrid Furnace unit scans the Zone 1 25 and Zone 2 35 systems from top to bottom, providing a detailed real-time "X-ray" picture of the IRF's internal thermal processes and mechanical operations. The Hybrid Smelting System 200, specifically the real-time controller 202, uses this information to calculate the molten metal and slag levels within the IRF unit, specifically within Zone 1 25 and Zone 2 35. This information is also used to control the plasma field height and power level, the smelting concentrate injection rate, and the molten metal discharge rate. The Hybrid Smelting System also displays a real-time "X-ray" picture on the control screen for the operator to observe and oversee the management and movement of material through the IRF unit.

[0078] 4 / (ii) Verification of the amount of smelting concentrate injected - The IRF unit including Zone 1 25 and Zone 2 35 is mounted on a load cell which verifies the amount of smelting concentrate being injected by the screw feed injection system and reports that information to the hybrid smelting system 200, specifically the real time controller 202.

[0079] 4 / (iii) Temperature Profile Generation - Thermocouples embedded in the furnace lining provide temperature measurements from the liquid metal at the bottom of the IRF in Zone 1 25, the reaction zone in the middle of the IRF in Zone 1 25, and the slag zone in Zone 2 35 at the top of the IRF below Zone 3. The hybrid smelting system 200, and specifically the real time controller 202, uses this information to generate one or more temperature profiles to adjust the rpm of the screw feed injection system which controls the feed rate of the smelting concentrate.

[0080] 5 / Monitoring and control of the power input into the plasma field generation by the plasma electrode 63 in zone 3 and into the multiple induction coil zones of coils 41, 43. This is done by temperature feedback to the real-time controller 202, for example from thermocouples embedded in the furnace lining side walls 11, 12, floor 13 and second wall 21. The temperature of the discharged molten metal and slag is also monitored by thermocouples in the second wall adjacent to the decant spout inlet 41 and outlet 41 and the molten metal discharge conduit 53. The hybrid smelting system 200 references the process temperature of the material being smelted and uses this information as a baseline control parameter, so as to accurately control the temperatures in zones 1 25, 2 35 and 3. When the smelting feedstock is injected into the furnace, over- or under-powering of the plasma fields and induction coils is avoided.

[0081] 6 / Control the molten metal levels in Zone 1 25 and Slag Zone 2 35. Molten metal may temporarily sink in Zone 1 25 as it is removed from the molten metal conduit 53. Molten metal may temporarily rise into Zone 2 35 if not enough molten metal is withdrawn from Zone 1 25 by the molten metal discharge conduit 53 to prevent molten metal overflow. Feedback from the IRF backscatter scanning system (BSS) and load cells to the real time controller 202 ensures that the feed rate and slag and molten metal discharge rates are adequate to maintain molten metal in Zone 1 25 and slag in Zone 2 35. The hybrid smelting system 200 monitors the concentrate injection rate, slag and metal discharge rates, and the level of molten metal in the IRF. When the molten metal level reaches a predetermined set point, e.g., a maximum set point, the hybrid smelting system opens the molten metal release valve 52 at the bottom of the IRF unit in Zone 1 25 and releases molten metal at a controlled rate to maintain an optimal molten metal level in the IRF unit.

[0082] 7 / The rate of molten metal discharge into the water granulation system is monitored so that the water granulation system can control the temperature and flow rate of the granulation water in the system. The water granulation system freezes the spray droplets, molten metal discharged from outlet 54 molten metal discharge conduit 53. Within the water granulation system there is a pool of water that instantly quenches the droplets into granules.

[0083] 8i / Monitor the rate at which molten slag is discharged from outlet 41 in the second wall.

[0084] 8ii / To produce, for example, spinel prills, the air pressure and the water injection rate are controlled into the slug of molten slag pouring out of the molten slag outlet 41 and flowing into the granulation nozzle.

[0085] A further advantage of the hybrid smelting system 200 is that in monitoring the operating parameters of the sensors and equipment within the hybrid smelting system 200, the hybrid smelting system 200 ensures safe operation within the design parameters of the system. The real time controller 202 triggers communicators to alert an operator and / or automatically initiate a controlled shutdown procedure if any of the set control parameters are violated.

[0086] In one embodiment, slag zone 2 35 is kept at the same or similar temperature as the molten metal in zone 1 25 to avoid "freezing out" the furnace by having induction coils transfer energy into the molten metal and by radiative heat transfer to the slag, keeping the slag in a safe, molten, low viscosity liquid state.

[0087] The plasma energy source 61 delivers energy to the slag in Zone 2 35 below the plasma electrode 63. The surface level of the slag is maintained within certain limits by feedback from the real time controller 202 to the slag outlet 41 valve or tipper of the furnace and by feedback from the real time controller 202 to the molten metal discharge valve or tipper 52.

[0088] The hybrid smelting system 200 combines heating of the feed material in the furnace 100, where the feed material is directly heated by electromagnetic induction from the coils 41, 43, with subsequent Joule heating (e.g., for conductive contents) and radiative heat transfer (e.g., for non-conductive contents) from both the molten metal pool and the plasma energy source.

[0089] In a preferred embodiment, the thermal energy transfer system allows the high efficiency of induction furnace technology to be used for the primary smelting of non-conductive materials by adding a plasma field at the top of the furnace to heat and maintain in molten form the slag generated during smelting. The slag head is maintained at the same temperature as the molten metal, eliminating dangerous furnace "freezing" conditions by heating the non-conductive slag with the plasma field and the conductive metal with the induction field.

[0090] The hybrid smelting system addresses the shortcomings of traditional induction smelting by providing an ultra-efficient primary furnace capable of smelting non-conductive materials while still providing heat to the slag head. Induction heating creates an electromagnetic stirring action, thereby optimizing the smelting environment for the reduction of metal oxides to metals.

[0091] Some non-conductive materials are generally difficult to inductively heat, and for such materials processes may rely on low efficiency electric arc furnaces or blast furnaces, or conventional induction furnaces with carbon crucibles.

[0092] In a further embodiment, the IRF hybrid smelting system is effective to smelt recovered fine chromium units in the form of chromite, chromium-rich spinel, and ferrochrome metal from the raw materials.

[0093] For each desired product, the hybrid smelting system determines and adjusts the reductants, fluxes, blend ratios, and reactions for each feedstock and / or output metal. The feedstock is dried to a concentrate before being sent to be mixed with the reductants and fluxes. The concentrate is analyzed to determine its specific composition or makeup (i.e., the ratios and composition of the feed materials). The properties of that composition or makeup are then used to determine the amount of reductants and fluxes to add to the concentrate.

[0094] The molten metal produced may be a pure (or substantially pure) single metal or an alloy containing two or more metals, depending on the composition of the blend / feed material.

[0095] In one embodiment, the IRF hybrid smelting system 200 includes an electrode plasma torch assembly 61, 62, 63 including two / twin electrodes 63 spaced apart such that a plasma field is formed between the electrodes when the torch is activated. The plasma field is formed at or towards the lower ends of the electrodes, and the lower ends of the twin electrodes are arranged in a V-shape towards each other to form a plasma field between the lower ends of the electrodes.

[0096] In one embodiment, twin electrodes 63 (extending through the lid to the bottom of the furnace) generate a moving plasma field via an electric arc that ionizes the working gas into a plasma, e.g., nitrogen gas is supplied to the tips 62 of the electrodes to ionize the electric arc passing between the electrodes that generates the super-hot plasma field. The nitrogen gas also provides an inert atmosphere within the furnace (to prevent oxidation of the resulting molten metal within the furnace).

[0097] The nitrogen consumption of the hybrid smelting system 200 in a preferred configuration can be 90% less than a typical plasma torch (which requires a pressurized flow of working gas to operate).

[0098] The hybrid smelting system increases or decreases the power of the plasma torch 61 to increase or decrease the physical magnitude and amount of heat energy radiated from the plasma field to the surrounding environment.

[0099] As the feed material passes through the plasma field, the material is transformed into its molten form. The ultra-high temperature reducing environment pyrolyzes the ore matrix (e.g. silica / alumina) encapsulating the targeted ores / metal oxides, thereby exposing them to the reducing agents in the feed and optimizing metal yields from the smelting concentrate.

[0100] The very high temperature plasma field in the preferred configuration enables rapid smelting of the feed material contents in two ways. First, as the feed material passes through the plasma field, it is heated and becomes molten. The molten contents accumulate in a reduction zone located on the surface of the molten slag and directly below the plasma field. Second, the plasma field located directly above the surface of the slag provides direct thermal energy to the slag creating a high temperature reduction zone that keeps the slag liquid.

[0101] The molten metal, being denser than the molten slag, sinks towards the bottom of the furnace where it forms a pool of molten metal which electromagnetically couples with the induction field (formed by induction coils 41, 43). The induction field (located below and / or around the molten contents) keeps the molten metal hot and induces a vertical stirring action within the molten metal.

[0102] The stirring action generated by the induction field circulates the microscopic reducing agents and metal oxides through the metal bath, enhancing the reduction of the smelter contents by providing physical contact between the particles.

[0103] The heating provided by the plasma torch assemblies 61, 62, 63 can result in a uniform temperature profile in the hybrid furnace 100, specifically in Zone 1 25 and / or Zone 2 35. The agitation helps homogenize the material being smelted (or melted). The uniform temperature profile helps improve metal yields. The extreme temperatures and extended reduction zone of the IRF system allow for complete (or at least improved) reduction of metal oxides to valuable metals. Moreover, such benefits promote homogenous metal alloys when dealing with compound alloys such as ferrochrome, ferromanganese, etc.

[0104] The dual heat sources from the induction coils 41, 43 and the plasma field around the electrode 63 work synergistically to efficiently smelt both conductive and non-conductive materials. In one embodiment, there is a twin electrode including a first electrode 63 and a twin second electrode. The second electrode is not shown in FIG. 2. There, a plasma arc is generated between the twin electrodes, which is moved (either vertically and / or angularly relative to the furnace) upon command from the real-time controller 202. The magnitude and / or position of the plasma field can be controlled to further enhance the efficiency and / or effective heating of the melt contents.

[0105] In a preferred configuration, plasma torch assemblies 61, 62, 63, which may include twin electrodes, generate a plasma ball having a diameter of 50 mm (eg, during low power start-up) to 400 mm (eg, at high power full production).

[0106] The hybrid smelting system 200 controls the current supplied to the electrodes, thereby controlling the size and strength of the plasma field between the two electrodes. For example, a starting current of about 20 kW creates a minimum plasma field of about 50 mm, 500 kW creates a plasma field of about 300 mm diameter, and increasing the power to 700 kW results in a plasma field of about 420 mm diameter.

[0107] The hybrid smelting system controls 200 the distance of the plasma torch assemblies 61, 62, 63, specifically the electrode 63, from the surface of the molten slag in zone wo35, in order to keep the molten slag beneath the plasma field in the reduction zone and the surrounding slag zone in a safe, low viscosity state.

[0108] When starting smelting in the hybrid smelting system 200, the electrode 63 is extended down into the induction furnace to an initial distance from the bottom bed 13 (e.g. 200 mm) and is thus electromagnetically coupled with the induction furnace so that smelting can commence without the use of a conductive ingot of starter metal to create a starting pool of conductive molten metal and slag.

[0109] As the pool of molten slag and metal rises within the furnace, the electrode 63 is raised and the plasma field is raised to a designed operating level to facilitate continuous production.

[0110] The hybrid smelting system 200 further monitors the erosion rate of the electrode 63 and extends the electrode 63 into the furnace to maintain a distance between the plasma field and the surface of the slag in Zone 2 35 during operation.

[0111] The supply injector system can be vertically or horizontally aligned, movable, and adjustable for start-up purposes.

[0112] The screw feed injection system may be further configured to condense / compress the feed material to regulate the thermochemical reduction rate by limiting the total surface area, and then feed the condensed feed material into the furnace chamber. Condensing the feed material by the screw feed injection system may reduce the need to agglomerate fine concentrates, reductants, and fluxes, for example, prior to entering the screw feed injection system.

[0113] In a preferred configuration, the hybrid smelting system provides pelletized feed material, i.e., binderless pellets of homogenized smelt concentrate, which are reduced 30% faster in the hybrid smelting system compared to smelt concentrate powder. The accelerated reduction is caused by the close proximity and / or direct contact of the metal oxides with the reducing agent and flux. The use of homogenized smelt pellets in the furnace of the hybrid smelting system reduces the external input power by approximately 30%.

[0114] Pelletizing the smelting concentrate into hard pellets also provides the ability to feed the pellets by dropping them directly into an extremely high temperature plasma field which subjects the smelting pellets to approximately 10,000°C for a few milliseconds.

[0115] Pelletizing the smelting concentrate further avoids a problem that, if the smelting concentrate was not pelletized, it would not pass through the plasma field, but rather would be deflected by the field and could accumulate along the edges of the chamber and on the surfaces of the slag zone within the furnace.

[0116] The hybrid smelting system 200 adjusts one or more molten content outlets, e.g., molten metal discharge conduit 54, by operating an actuator 52 which operates a flow control valve by raising and lowering an outlet 54 between elevated and lowered discharge positions to adjust the discharge rate of the molten content. The hybrid smelting system tracks the level of molten metal (referred to as Contents 1) in the furnace and adjusts the height of the Contents 1 outlet to speed up or slow down the discharge rate of the content from the furnace. This feature gives the system 200 the flexibility to allow smelting of most ores and customized concentrates with various amounts of slag, while still maintaining the required balance between the reduction zone, specifically in Zone 3, the slag zone, specifically in Zone 2 35, and the molten metal zone, specifically in Zone 1 25, to ensure safe and continuous operation of the hybrid smelting system 200.

[0117] In one embodiment, the hybrid smelting system 200 can control the contents within the furnace by opening and closing a high temperature release valve located in the bottom region of the furnace.

[0118] In one embodiment, the hybrid smelting system controls the feed rate through the furnace mass balance. As material leaves the furnace body, the screw feeder increases speed to inject more into the furnace, specifically into Zone 3. The hybrid smelting system continuously produces a real-time mass balance of the system, including CO and CO2 tail gases generated from the reductant, as it measures the input rate (by load cells mounted on the furnace body) and the output rate (by load cells attached to the molten metal granulator and slag granulator).

[0119] The hybrid smelting system 200 further calculates how the concentrate, reductant, and flux are reacting and flowing within the system, as well as the density differences of the molten metal, interface, and molten slag zones within the furnace from a backscatter scanning system (BSS), thereby keeping the interface centered in the feed injection zone.

[0120] To compensate for different metal to slag ratios, the angle of the outlets, e.g., molten metal discharge conduit 53, can be adjusted in real time by real time controller 202. To enable the molten slag discharge from slag zone 2 35 to be discharged at a predetermined level, a second molten content outlet having an outlet 41 is positioned, e.g., above first molten content outlet 53. In this way, the molten slag and metal are discharged into two separate induction heating trowels which transport the molten material to the granulation system.

[0121] In one embodiment, the functionality of the hybrid smelting system includes one or more of the following: Dryer temperature and / or speed Adding concentrate, reductant, and / or flux into the mixing system Feeding System Speed Twin Electrode Plasma Torch Assembly Input Power Two electrode movements Induction Coil Input Power Movement of the dissolving contents delivery part Feed material injection rate One or more heights of the delivery section Water cooling in screw feed injection systems Water cooling for the induction coil, and Air pressure and water injection rate in slug granulation nozzles to produce spinel prills.

[0122] The hybrid smelting system 200 receives information to adjust the control from one or more of the following: Concentrate or chemical analysis of dried raw concentrate Temperature sensors (e.g. thermocouples, infrared sensors) Weight Sensor Level system for determining the level of slag and / or molten metal Backscatter X-ray unit provides real-time images of slag, metal, and plasma torch height Release rate of molten slag

[0123] Preferably, the hybrid smelting system regulates the smelting rate of the system by controlling one or more of the velocity of the feed material entering the furnace, the discharge rate of the molten slag, and the induction or plasma heating.

[0124] The dried raw concentrate is conveyed into the mixing vessel. As the concentrate is conveyed to the mixer, it passes through a prompt gamma neutron activation analysis (PGNAA) machine. The PGNAA analyzes the concentrate in real time to provide the hybrid smelting system with analytical data of the reactive materials and other materials that make up the concentrate. This data is then used by the hybrid smelting system to determine the proportions (weight, volume, and / or ratio) of the major elements that make up the concentrate, including one or more of the oxygen, carbon, phosphorus, and sulfur content. This analytical data is used by the hybrid smelting system to determine the appropriate amounts of fluxes and reductants to add to the concentrate in the mixing vessel. The appropriate amounts of fluxes and reductants result in ideal smelting conditions for the concentrate's characteristics.

[0125] Various particle sizes of raw materials, reductants, and fluxes are suitable for use in the improved hybrid smelting system 200. It will be appreciated that the particle sizes of the various ingredients of the blend may affect the melting and / or reaction rates. Suitable size ranges may be determined.

[0126] By continuously analyzing the concentrate as it travels to or enters the mixer, the hybrid smelting system 200 quantifies the amount of each reactive material entering the mixer. The prompt gamma neutron activation analysis (PGNAA) system includes a microwave moisture analyzer to determine the moisture percentage. The conveyor passing through the PGNAA includes a weight cell to determine the mass flow rate of the material being conveyed. The PGNAA unit transmits this information to the hybrid smelting system.

[0127] Thus, the hybrid smelting system 200 includes means for one or more of the following in achieving a highly efficient continuous smelting process: Accurate estimation and continuous reading of feed / concentrate composition Formation of Feed Material The injection rate of the feed material into the furnace 100 Control of the power input into the plasma field provided by the plasma torch 61 and metal zone induction coils 41, 43 Control of dissolution level of contents Control of the release rate of molten slag into the slag granulation nozzle, air pressure, and water volume Automatic adjustment and / or shutdown procedures and generation of warnings to operators if parameters are violated Control of the mixer configuration, and / or Management of heatable materials

[0128] The accurate estimation and continuous reading of the feed / concentrate composition can include real-time analysis of the concentrate. This allows the hybrid smelting system 200 to accurately determine the chemical composition and weight of the concentrate being delivered to the furnace feed hopper. This is compared to other methods such as taking samples of the concentrate from time to time and estimating the approximate composition of the entire concentrate batch. This batch mixing to form a blended concentrate (feed material) that can be fed into the furnace feed hopper. The furnace feed hopper can even out the flow rate of the batch mixing process. Therefore, the hybrid smelting furnace 100 can operate continuously.

[0129] The flux, reductant, and concentrate are mixed to form a feedstock, which is stored in a feed hopper of the furnace.

[0130] Controlling the power input into the plasma field and metal zone induction coils also allows the hybrid smelting system 200 to maintain a constant temperature profile across the surface of the refractory lining, for example, in the floor 13 and side walls 11, 12 and second wall 21 of zone 1 25 in the furnace 100. Maintaining a constant temperature profile prevents the refractory lining from cracking due to temperature differences in different areas of the furnace. Controlling the power input is accomplished by temperature feedback from thermocouples and back-up infrared sensors into the real-time controller 202, which in turn controls the feeder 212, molten metal discharge valve 52, slag outlet 41 or tipper, coil 41, 43 current and frequency, plasma torch power, and other devices.

[0131] As the contents are smelted, they form molten metal and slag. Depending on the level of the molten metal, the hybrid smelting system 200 adjusts the height of the molten contents delivery. The hybrid smelting system 200 also monitors the rate of feed material injection and the rate of slag discharge from the slag delivery to control the level (i.e., volume) of molten metal within the furnace.

[0132] The hybrid smelting system 200 allows for increased metal yields of 35% or more depending on the ore and concentrate.

[0133] The hybrid smelting system 200 allows for a minimum 58% reduction in the energy demand of primary ore smelting due to the extremely high temperatures of the plasma field and the extended exposure to the reduction zone.

[0134] The hybrid smelting system 200 allows for increased smelting rates and separation of slag from the metal units being produced. To do this, the hybrid smelting system monitors and maintains the slag in a low viscosity state and continuously decants it from the side of the IRF system while the molten metal units collect in the inductively heated bottom of the IRF system.

[0135] The hybrid smelting system 200 is capable of handling high slag loads without impeding the efficient production of metals.

[0136] The hybrid smelting system 200 allows for the smelting of ultra-fine concentrates, agglomerated materials, and chunky materials (up to 40 mm or larger). The hybrid smelting system provides operational flexibility that allows the IRF hybrid smelting system to effectively transition between processing raw material feed or blending various size pieces, and utilizes fine ore concentrates by blending them into reducing agents and fluxes to provide a homogenized mixture that enhances the efficiency of the smelting process.

[0137] Because continuous tapping eliminates the time normally spent on furnace tilting or tapping procedures, the hybrid smelting system 200 allows for approximately 30% time savings. Such time savings translates into savings of up to 300 kWh per hour or up to 7200 kWh per 24-hour operation.

[0138] Using the hybrid smelting system 200, up to 30% of the waste heat energy typically lost in conventional furnace technology is recovered. The recovered heat energy is reused to preheat the feed material in preparation for smelting. Such reuse of heat energy further reduces energy demand, carbon dioxide emissions, and significantly improves the operating efficiency of the smelting process.

[0139] The present invention has been described by way of example only. Accordingly, the foregoing is to be considered as merely illustrative of the principles of the invention. Further, since numerous modifications and changes will readily occur to those skilled in the art, it is not sought to limit the invention to the exact construction and operation as shown and described, and therefore, all suitable modifications and equivalents falling within the scope of the appended claims may be resorted to.

Claims

1. A hybrid smelting system (200) comprising a real-time controller (202) and a hybrid smelting furnace (100) including a container (99) in a reduction zone (226), wherein a plasma on induction heating is supplied into the reduction zone (226) and the feed materials (204, 206, 208, 210) and slag and reduced metal and / or alloy discharged under the supervision of the real-time controller (202) are continuously smelted, The container (99) includes a first wall (11, 12) having electric field permeability for holding and induction heating metal and / or alloy above a molten metal / alloy discharge opening (51) despite the container (99), a second wall (21) having a greater thickness relative to the first wall (11, 12) for holding slag on the first wall up to a slag discharge opening (41) penetrating the container (99), and a plasma torch (61) that can be arranged above the level of the slag discharge opening (41) for heating and reducing the feed materials to produce the metal or alloy and the slag, The torch 61 includes a gas nozzle (62) for guiding gas onto an electric arc electrode (63). Hybrid smelting system (200).

2. The hybrid smelting system (200) according to claim 1, including a feeder (212) operating under the supervision of the real-time controller (202) for supplying the feed materials (204, 206, 208, 210) in the form of debris, detritus, or dross ranging from ultrafine powder or sand to lumps of 40 mm or more into the reduction zone (226).

3. The hybrid smelting system (200) according to claim 1 or 2, including a steering device (216) operating under the supervision of the real-time controller (202) for controlling at least one feeder (212) to supply the feed materials so as to directly pass the plasma into the reduction zone.

4. A reduction metal release regulator (52) and a slag release regulator (33, 41), both operating under the supervision of the real-time controller (202) together with the feeder, to keep the first level of the reduction metal / alloy within a first preselected range in zone 1 (25) and / or to keep the second level of the slag within a second preselected range in zone 2 (35), the hybrid smelting system (200) according to claim 2 or 3.

5. A material dryer (214) operating under the supervision of the real-time controller (202) for drying the feed material to a range of water content from 5 percent to 1 percent or less by weight, the hybrid smelting system (200) according to any one of claims 1 to 4.

6. A plasma torch displacement actuator operating under the supervision of the real-time controller (202) for positioning a plasma torch (61) that generates the plasma in the reduction zone (226) above the slag to keep the viscosity of the slag within a preselected range, the hybrid smelting system (200) according to any one of claims 1 to 5.

7. An imaging device operating under the supervision of the real-time controller (202) for providing observation of the material being processed, the hybrid smelting system (200) according to any one of claims 1 to 6.

8. A plasma current regulator operating under the supervision of the real-time controller (202) for controlling the size, temperature, particle density, and / or light intensity of the plasma, the hybrid smelting system (200) according to any one of claims 1 to 7.

9. The plasma current regulator is operable to provide about 20 kW of power to the plasma and a starting current for forming a plasma field with a diameter from 45 mm to 55 mm, the hybrid smelting system (200) according to claim 8.

10. The plasma current regulator is operable to provide about 500 kW of power to the plasma and a second current for forming a plasma field with a diameter from 270 mm to 330 mm, and / or to provide about 700 kW of power to the plasma and a third current for forming a plasma field with a diameter from 380 mm to 460 mm, the hybrid smelting system (200) according to claim 8 or 9.

11. The hybrid smelting system (200) according to any one of claims 1 to 10, comprising an induction current regulator operating under the supervision of the real-time controller (202) for controlling a fourth current in the induction coils (41, 43).

12. The hybrid smelting system (200) comprising at least one device as disclosed in claims 1 to 11 for maintaining the temperature in the reduction zone (226), slag, and / or reduced metal to enable continuous tapping of the molten material and granulation of the final product.

13. The hybrid smelting system (200) according to claim 12, operable to maintain the slag and the reduced metal / alloy at substantially the same temperature, or within a preselected temperature range, or within preselected temperature ranges for the reduced metal / alloy and the slag respectively.

14. The hybrid smelting system (200) according to claim 12 or 13, comprising a temperature profile generator (234) for reading the temperatures of the reduced metal in zone 1 (25) under the slag, the slag in zone 2 (35) under the plasma and / or the reduction zone (226), and the plasma, and operating the at least one device under the supervision of the real-time controller (202) to maintain the temperatures within a preselected range.

15. The hybrid smelting system (200) according to any one of claims 12, 13, or 14, wherein the temperature is extended in the reduction zone (228) to reduce metal oxides including recovered fine chromium units, chromite, chromium-rich spinel, and / or ferrochrome in the feed material to a homogeneous metal alloy containing iron, chromium, and / or manganese.

16. The hybrid smelting system (200) according to any one of claims 12, 13, 14, or 15, comprising thermocouples embedded in the furnace lining of side walls 11, 12, floor 13, second wall 21, and / or cover 31 for monitoring the temperature of the reduced metal and / or slag and providing temperature feedback to the real-time controller (202) to maintain the temperature.

17. The hybrid smelting system (200) according to any one of claims 1 to 16, configured to maintain the average temperature of the plasma within the range of 3500°C to 12000°C to change organic solid compounds in the feed material into syngas.

18. The hybrid smelting system (200) according to any one of claims 1 to 17, configured to maintain the reducing metal and the slag within a temperature range between 1700 °C and 2800 °C.

19. The hybrid smelting system (200) according to any one of claims 1 to 18, configured to smelt a feed material including an alloy and / or an ore containing titanium, vanadium, chromium, niobium, molybdenum, zirconium, ruthenium, rhodium, tantalum, tungsten, rhenium, osmium, and / or iridium, and / or these refractory metals.

20. The hybrid smelting system (200) according to any one of claims 1 to 19, configured to smelt a feedstock including an alloy and / or an ore containing zirconium, titanium, and / or beryllium, and / or these metals.