Low-temperature CO oxidation catalyst

Abstract

The present disclosure is directed to a low-temperature carbon monoxide (LT-CO) oxidation catalyst composition for mitigating exhaust gas emissions from lean-burn engines. The LT-CO oxidation catalyst composition includes an oxygen storage component (OSC), a first platinum group metal (PGM) component, and a promoter metal, wherein the OSC is impregnated with the first PGM component and the promoter metal. The LT-CO oxidation catalyst composition is effective for oxidizing carbon monoxide (CO) and hydrocarbons (HC) under cold-start conditions. Additionally, a catalyst article (resulting in an LT-CO / DOC article) is provided that includes the LT-CO oxidation catalyst composition, which may optionally further include a diesel oxidation catalyst (DOC) composition. Additionally, an exhaust gas treatment system including such a catalyst article and a method for reducing HC or CO levels in an exhaust gas stream using such a catalyst article are provided.

Description

[Technical field]

[0001] The present invention is directed to catalyst compositions, articles, systems, and methods suitable for treating exhaust gas streams of lean-burn internal combustion engines to reduce carbon monoxide (CO) emissions. [Background technology]

[0002] Environmental regulations regarding emissions from internal combustion engines are becoming increasingly stringent around the world. The operation of lean-burn engines, such as diesel engines, offers users superior fuel economy by operating at high air-fuel ratios under lean fuel conditions. However, diesel engines also produce high levels of particulate matter (PM), unburned hydrocarbons (HC), carbon monoxide (CO), and nitrogen oxides (NO x ), and also releases exhaust gas emissions containing NO x refers to various chemical species of nitrogen oxides, including nitric oxide and nitrogen dioxide, among others. The two main components of exhaust particulate matter are the soluble organic fraction (SOF) and the insoluble carbonaceous soot fraction. SOF condenses in a layer on top of the soot and generally originates from unburned diesel fuel and lubricating oil. SOF can exist in diesel exhaust as a vapor or an aerosol (i.e., fine droplets of liquid condensate), depending on the temperature of the exhaust gases. Soot is composed primarily of particles of carbon.

[0003] Oxidation catalysts containing one or more precious metals, such as platinum group metals (PGMs), dispersed on a refractory metal oxide support, such as alumina, are known to be used in treating diesel engine exhaust to convert hydrocarbon and carbon monoxide gaseous pollutants to carbon dioxide and water by catalyzing the oxidation of these pollutants. Such catalysts are generally contained in units called diesel oxidation catalysts (DOCs), which are placed in the exhaust flow path from a diesel engine to treat the exhaust before it is released into the atmosphere. Typically, diesel oxidation catalysts are formed on a ceramic or metal substrate on which one or more catalytic coating compositions are deposited. In addition to converting gaseous HC and CO emissions and particulate matter (SOF fraction), oxidation catalysts containing one or more PGMs also convert NO to NO 2 The catalyst typically has a light-off temperature, i.e., the temperature at which 50% conversion is achieved (T 50 (also called the

[0004] A major problem encountered in the treatment of automotive exhaust gas streams is the so-called "cold start" period, which is the period at the beginning of the treatment process when the exhaust gas stream and exhaust gas treatment system are cold (i.e., below 150°C). At these low temperatures, exhaust gas treatment systems generally produce a high concentration of hydrocarbons (HC), nitrogen oxides (NO x ), and / or carbon monoxide (CO) emissions. As automakers strive to meet long-term global fuel economy standards, engine exhaust temperatures are expected to drop significantly, so catalysts must operate at lower temperatures to efficiently oxidize CO, HC, and NO. x Therefore, there is a need for oxidation catalysts with lower light-off temperatures for CO and HC. Therefore, there is a need for catalysts with lower light-off temperatures to improve cold start performance. Summary of the Invention

[0005] The present disclosure generally provides low temperature carbon monoxide (LT-CO) oxidation catalyst compositions, catalyst articles, and catalyst systems including such catalyst articles that exhibit enhanced HC and CO oxidation under low temperature conditions, such as those encountered during cold start. In particular, such LT-CO oxidation catalyst compositions, articles, and systems include an oxygen storage component (OSC), a platinum group metal (PGM) component, and a promoter metal, where the OSC is impregnated with the PGM component and the promoter metal. Surprisingly, it has been discovered that impregnating the OSC with both the PGM and the promoter metal provides a catalyst composition with improved cold start performance, as described in further detail herein.

[0006] Accordingly, in one aspect, there is provided a LT-CO oxidation catalyst composition for mitigating exhaust gas emissions from a lean-burn engine, the LT-CO oxidation catalyst composition comprising an oxygen storage component (OSC), a first platinum group metal (PGM) component, and a first promoter metal, wherein the OSC is impregnated with the first PGM component and the first promoter metal, and the LT-CO oxidation catalyst composition is effective for oxidizing carbon monoxide and hydrocarbons under cold start conditions.

[0007] In some embodiments, the first PGM component (impregnated into the OSC) is present in an amount of about 1 to about 10 weight percent of the OSC alone (i.e., the OSC before the first PGM component and promoter metal are impregnated). In some embodiments, the first PGM component is present in an amount of about 1 to about 4 weight percent of the OSC alone. In some embodiments, the first PGM component comprises palladium (Pd), e.g., the first PGM component can be Pd. In some embodiments, the first PGM component comprises platinum (Pt), e.g., the first PGM component can be Pt. In some embodiments, the OSC comprises a rare earth metal oxide in an amount ranging from about 0.1 to about 100 weight percent, based on the total weight of the OSC alone. In some embodiments, the rare earth metal oxide is ceria.

[0008] In some embodiments, the LT-CO oxidation catalyst composition further comprises a first refractory metal oxide selected from the group consisting of alumina, silica, zirconia, titania, yttria, and combinations thereof.

[0009] In some embodiments, the LT-CO oxidation catalyst composition further comprises a zeolite. In some embodiments, the first zeolite comprises one or more small pore zeolites having a 6-8 membered ring structure. In some embodiments, the one or more small pore zeolites are selected from the group consisting of chabazite (CHA), zeolite A (LTA), and combinations thereof. In some embodiments, the first zeolite comprises one or more medium pore or large pore zeolites having a 10-12 membered ring structure. In some embodiments, the one or more medium pore or large pore zeolites are selected from the group consisting of ferrierite (FER), ZSM-5 (MFI), beta zeolite (BEA), Y zeolite (FAU), and combinations thereof.

[0010] In some embodiments, the LT-CO oxidation catalyst composition further comprises an alkaline earth metal component, hi some embodiments, the alkaline earth metal component is an oxide of magnesium, calcium, strontium, barium, or a combination thereof.

[0011] In some embodiments, the first promoter metal (impregnated into the OSC) is present in an amount of about 0.1 to about 10% by weight of the OSC alone, calculated on a metal oxide basis. In some embodiments, the first promoter metal is present in an amount of about 0.5 to about 4% by weight of the OSC alone, calculated on a metal oxide basis. In some embodiments, the first promoter metal is present in an amount of about 2 to about 4% by weight of the OSC alone, calculated on a metal oxide basis. In some embodiments, the first promoter metal is tin (Sn). In some embodiments, the OSC comprises ceria (e.g., can consist essentially of ceria), the first PGM component is Pd, Pt, or a combination thereof, and the first promoter metal is Sn. In certain embodiments, the first PGM component is present at about 2% by weight and Sn is present at about 1% by weight, based on the total weight of the OSC alone.

[0012] In some embodiments, a catalyst article is provided that includes a substrate having an inlet end and an outlet end defining an overall length, and a first washcoat including the LT-CO oxidation catalyst composition of the present disclosure disposed on at least a portion thereof. In some embodiments, the catalyst article further includes a diesel oxidation catalyst (DOC) composition, the DOC composition including a second washcoat including a second zeolite, the second zeolite being impregnated with a second PGM component, and a third washcoat including a third zeolite and a second refractory metal oxide, the third PGM component being impregnated with the third zeolite or the second refractory metal oxide, or both.

[0013] In some embodiments, the second refractory metal oxide is impregnated with a promoter metal.

[0014] In some embodiments, the second PGM component comprises Pt, Pd, or a combination thereof. In some embodiments, the second PGM component comprises Pt. In some embodiments, the second PGM component comprises Pt and Pd. In some embodiments, the Pt and Pd are present in a weight ratio of Pt:Pd of about 1:10 to about 10:1. In some embodiments, the third PGM component comprises Pt, Pd, or a combination thereof.

[0015] In some embodiments, the second zeolite and the third zeolite each comprise a hydrothermally stable zeolite in the form of a 6-12 membered ring structure. In some embodiments, the second zeolite and the third zeolite each are independently selected from the group consisting of ZSM-5, beta, mordenite, Y zeolite, chabazite, ferrierite, and combinations thereof. In some embodiments, the second zeolite comprises more than one zeolite. In some embodiments, the third zeolite comprises more than one zeolite. In some embodiments, both the second and third zeolite comprise more than one zeolite.

[0016] In some embodiments where the catalyst article comprises three (or more) layers, the first, second, and third washcoats of the catalyst article are layered or zoned. In some embodiments, the first washcoat is coated on the substrate, the second washcoat is coated on the first washcoat, and the third washcoat is coated on the second washcoat. In some embodiments, the third washcoat is coated on the substrate, the second washcoat is coated on the third washcoat, and the first washcoat is coated on the second washcoat. In some embodiments, the first washcoat is coated on the substrate, the third washcoat is coated on the first washcoat, and the second washcoat is coated on the third washcoat. In some embodiments, a second washcoat is coated on an inlet end of the substrate, a third washcoat is coated on an outlet end of the substrate, and a first washcoat is coated over the second and third washcoats.

[0017] In some embodiments, the catalyst article has a zoned configuration, where a first washcoat is disposed on the substrate from about 10% to about 90% of the total length from either the inlet end or the outlet end, a second washcoat is disposed on the catalyst substrate from about 90% to about 10% of the total length from either the inlet end or the outlet end, and a third washcoat is coated on the first and second washcoats. In some embodiments, the first washcoat has a viscosity of at least about 0.5 g / in. 3 In some embodiments, the substrate is a honeycomb substrate in the form of a wall-flow filter or a flow-through monolith.

[0018] In another aspect, a catalyst article for mitigating exhaust gas emissions from a lean-burn engine, the catalyst article comprising a substrate having an inlet end and an outlet end defining an overall length, a first washcoat comprising an oxygen storage component (OSC), a first platinum group metal (PGM) component, and a first promoter metal, and optionally a first refractory metal oxide, wherein the OSC is impregnated with the first PGM component and the first promoter metal, and a second washcoat comprising a first zeolite, wherein the first zeolite is impregnated with the second PGM component. and a third washcoat comprising a second zeolite and a second refractory metal oxide, wherein the second zeolite, the second refractory metal oxide, or both are impregnated with a third PGM component and optionally a second promoter metal, wherein the first, second, and third washcoats are each disposed on at least a portion of the substrate in a layered or zoned configuration, and the catalyst article is effective for oxidizing carbon monoxide and hydrocarbons under cold start conditions.

[0019] In some embodiments, the first washcoat further comprises a small pore zeolite, a large pore zeolite, an alkaline earth metal component, or a combination thereof.

[0020] In some embodiments, the cold start condition comprises an exhaust gas temperature of less than about 150°C.

[0021] In some embodiments, the LT-CO oxidation catalyst article further comprises an HC trapping composition. In some embodiments, the LT-CO oxidation catalyst article comprises a low temperature NO x In some embodiments, the LT-CO oxidation catalyst article further comprises a sorbent (LT-NA) composition. x It further comprises a capture (LNT) composition.

[0022] In some embodiments, an exhaust gas treatment system for treating a lean-burn engine exhaust gas stream containing hydrocarbons, carbon monoxide, nitrogen oxides, and particulate matter is provided, the exhaust gas treatment system comprising a lean-burn engine generating an exhaust gas stream, an exhaust conduit in fluid communication with the lean-burn engine via an exhaust manifold, and a catalytic article of the present disclosure positioned downstream of the lean-burn engine and in fluid communication with the exhaust gas stream. In some embodiments, the exhaust gas treatment system includes a soot filter, a selective catalytic reduction (SCR) catalyst, a urea injection component, an ammonia oxidation catalyst (AMOX), a low temperature NOx catalyst, a catalytic article of the present disclosure ... x Adsorbent (LT-NA) catalyst, and lean NO x (LNT) hi some embodiments, the lean burn engine is a diesel engine.

[0023] In some embodiments, a method for treating a lean-burn engine exhaust gas stream is provided comprising contacting the exhaust gas stream with a catalytic article of the present disclosure or an exhaust gas treatment system of the present disclosure.

[0024] In some embodiments, methods are provided for reducing CO and HC levels in an exhaust gas stream comprising contacting the gas stream with a catalytic article of the present disclosure or an exhaust gas treatment system of the present disclosure for a time and at a temperature sufficient to reduce the CO and HC levels in the gas stream, in some embodiments, the CO and HC levels in the gas stream are reduced by at least 30% compared to the CO and HC levels in the gas stream before contact with the catalytic article.

[0025] The present disclosure includes, but is not limited to, the following embodiments.

[0026] Embodiment 1: A low temperature carbon monoxide (LT-CO) oxidation catalyst composition for mitigating exhaust gas emissions from a lean-burn engine, the LT-CO oxidation catalyst composition comprising an oxygen storage component (OSC), a first platinum group metal (PGM) component, and a first promoter metal, wherein the OSC is impregnated with the first PGM component and the first promoter metal, and the LT-CO oxidation catalyst composition is effective for oxidizing carbon monoxide and hydrocarbons under cold start conditions.

[0027] Embodiment 2: The LT-CO oxidation catalyst composition of embodiment 1, wherein the first PGM component is present in an amount of about 1 to about 10% by weight of the OSC alone.

[0028] Embodiment 3: The LT-CO oxidation catalyst composition of embodiment 1 or 2, wherein the first PGM component is present in an amount of about 1 to about 4 weight percent of the OSC alone.

[0029] Embodiment 4: The LT-CO oxidation catalyst composition of any one of embodiments 1 to 3, wherein the first PGM component is palladium (Pd).

[0030] Embodiment 5: The LT-CO oxidation catalyst composition of any one of embodiments 1 to 4, wherein the first PGM component is platinum (Pt).

[0031] Embodiment 6: The LT-CO oxidation catalyst composition of any one of embodiments 1 to 5, wherein the OSC comprises a rare earth metal oxide in an amount ranging from about 0.1 to about 100 weight percent, based on the total weight of the OSC alone.

[0032] Embodiment 7: The LT-CO oxidation catalyst composition according to any one of embodiments 1 to 6, wherein the rare earth metal oxide is ceria.

[0033] Embodiment 8: The LT-CO oxidation catalyst composition of any one of embodiments 1 to 7, wherein the first promoter metal is present in an amount of about 0.1 to about 10% by weight of the OSC alone, calculated on a metal oxide basis.

[0034] Embodiment 9: The LT-CO oxidation catalyst composition of any one of embodiments 1 to 8, wherein the first promoter metal is present in an amount of about 0.5 to about 4% by weight of the OSC alone, calculated on a metal oxide basis.

[0035] Embodiment 10: The LT-CO oxidation catalyst composition of any one of embodiments 1 to 9, wherein the first promoter metal is tin (Sn) or an oxide thereof.

[0036] Embodiment 11: The LT-CO oxidation catalyst composition of any one of embodiments 1 to 10, wherein the OSC is ceria, the first PGM component is Pd, Pt, or a combination thereof, and the first promoter metal is Sn or an oxide thereof.

[0037] Embodiment 12: The LT-CO oxidation catalyst composition of any one of embodiments 1 to 11, wherein the first PGM component is present at about 2 wt.% and the Sn is present at about 1 wt.%.

[0038] Embodiment 13: The LT-CO oxidation catalyst composition of any one of embodiments 1 to 12, further comprising a first refractory metal oxide selected from the group consisting of alumina, silica, zirconia, titania, yttria, and combinations thereof.

[0039] Embodiment 14: The LT-CO oxidation catalyst composition of any one of embodiments 1 to 13, further comprising a first zeolite.

[0040] Embodiment 15: The LT-CO oxidation catalyst composition of any one of embodiments 1 to 14, wherein the first zeolite comprises one or more small pore zeolites having 6-8 membered ring structures.

[0041] Embodiment 16: The LT-CO oxidation catalyst composition according to any one of embodiments 1 to 15, wherein the one or more small pore zeolites are selected from the group consisting of chabazite, zeolite A, and combinations thereof.

[0042] Embodiment 17: The LT-CO oxidation catalyst composition of any one of embodiments 1 to 16, wherein the first zeolite comprises one or more medium pore or large pore zeolites having 10-12 membered ring structures.

[0043] Embodiment 18: The LT-CO oxidation catalyst composition of any one of embodiments 1 to 17, wherein the one or more medium pore or large pore zeolites are selected from the group consisting of beta zeolite, Y zeolite, ferrierite, ZSM-5, and combinations thereof.

[0044] Embodiment 19: The LT-CO oxidation catalyst composition of any one of embodiments 1 to 18, further comprising an alkaline earth metal component.

[0045] Embodiment 20: The LT-CO oxidation catalyst composition of any one of embodiments 1 to 19, wherein the alkaline earth metal component is an oxide of magnesium, calcium, strontium, barium, or a combination thereof.

[0046] Embodiment 21: A catalyst article comprising: a substrate having an inlet end and an outlet end defining an overall length; and a first washcoat comprising the LT-CO oxidation catalyst composition of any one of embodiments 1-20 disposed on at least a portion of the substrate.

[0047] Embodiment 22: The catalyst article of embodiment 21, further comprising a diesel oxidation catalyst (DOC) composition comprising: a second washcoat comprising a second zeolite, wherein the second zeolite is impregnated with a second PGM component; and a third washcoat comprising a third zeolite and a second refractory metal oxide, wherein the third zeolite, the second refractory metal oxide, or both are impregnated with the third PGM component.

[0048] Embodiment 23: The catalytic article of embodiment 21 or 22, wherein the second refractory metal oxide is impregnated with a second promoter metal.

[0049] Embodiment 24: The catalytic article of any one of embodiments 21-23, wherein the second PGM component comprises Pt, Pd, or a combination thereof.

[0050] Embodiment 25: The catalytic article of any one of embodiments 21-24, wherein the second PGM component comprises Pt and Pd present in a weight ratio of Pt:Pd of about 1:10 to about 10:1.

[0051] Embodiment 26: The catalytic article of any one of embodiments 21-25, wherein the third PGM component comprises Pt, Pd, or a combination thereof.

[0052] Embodiment 27: The catalytic article of any one of embodiments 21 to 26, wherein the second zeolite and the third zeolite each comprise a hydrothermally stable zeolite in the form of a 6-12 membered ring structure.

[0053] Embodiment 28: The catalyst article of any one of embodiments 21-27, wherein the second zeolite and the third zeolite are each independently selected from the group consisting of ZSM-5, beta, mordenite, Y zeolite, chabazite, ferrierite, and combinations thereof.

[0054] Embodiment 29: The catalytic article of any one of embodiments 21-28, wherein the first, second, and third washcoats of the catalytic article are layered or zoned.

[0055] Embodiment 30: A catalytic article according to any one of embodiments 21 to 29, wherein a first washcoat is coated on a substrate, a second washcoat is coated on the first washcoat, and a third washcoat is coated on the second washcoat.

[0056] Embodiment 31: A catalytic article according to any one of embodiments 21 to 29, wherein a first washcoat is coated on a substrate, a third washcoat is coated on the first washcoat, and a second washcoat is coated on the third washcoat.

[0057] Embodiment 32: A catalytic article according to any one of embodiments 21 to 29, wherein a third washcoat is coated on the substrate, a second washcoat is coated on the third washcoat, and a first washcoat is coated on the second washcoat.

[0058] Embodiment 33: A catalytic article according to any one of embodiments 21 to 29, wherein a second washcoat is coated on an inlet end of the substrate, a third washcoat is coated on an outlet end of the substrate, and a first washcoat is coated over the second washcoat and the third washcoat.

[0059] Embodiment 34: The catalyst article of any one of embodiments 21-29 having a zoned configuration, wherein a first washcoat is disposed on the substrate from either the inlet end or the outlet end for about 10% to about 90% of the total length, a second washcoat is disposed on the substrate from either the inlet end or the outlet end for about 90% to about 10% of the total length, and a third washcoat is coated on the first washcoat and the second washcoat.

[0060]

[0041] Embodiment 35: The first washcoat has a coating density of at least about 0.5 g / in 3 35. The catalyst article of any one of embodiments 21-34, wherein the catalyst article is present on the substrate at a loading of about 1.0.

[0061] Embodiment 36: The catalytic article of any one of embodiments 21-35, wherein the substrate is a honeycomb substrate in the form of a wall-flow filter or a flow-through monolith.

[0062] Embodiment 37: A catalyst article for mitigating exhaust gas emissions from a lean-burn engine, the catalyst article comprising: a substrate having an inlet end and an outlet end defining an overall length; a first washcoat comprising an oxygen storage component (OSC), a first platinum group metal (PGM) component, a first promoter metal, and optionally a first refractory metal oxide, wherein the OSC is impregnated with the first PGM component and the first promoter metal; and a second washcoat comprising a first zeolite, wherein the first zeolite is impregnated with the second PGM component. and a third washcoat comprising a second zeolite and a second refractory metal oxide, wherein the second zeolite, the second refractory metal oxide, or both are impregnated with a third PGM component and optionally a second promoter metal, wherein the first, second, and third washcoats are each disposed on at least a portion of the substrate in a layered or zoned configuration, and the catalytic article is effective for oxidizing carbon monoxide and hydrocarbons under cold start conditions.

[0063] Embodiment 38: The catalytic article of embodiment 37, wherein the first washcoat further comprises a small pore zeolite, a large pore zeolite, an alkaline earth metal component, or a combination thereof.

[0064] Embodiment 39: The catalytic article of any one of embodiments 21 to 38, wherein the cold start condition comprises an exhaust gas temperature of less than about 150° C.

[0065] Embodiment 40: The catalytic article of any one of embodiments 21 to 39, further comprising a hydrocarbon (HC) trapping composition.

[0066] Embodiment 41: Low-temperature NO x41. The catalytic article of any one of embodiments 21-40, further comprising an adsorbent (LT-NA) composition.

[0067] Embodiment 42: Lean NO x 42. The catalytic article of any one of embodiments 21-41, further comprising a capture (LNT) composition.

[0068] Embodiment 43: An exhaust gas treatment system for treating a lean-burn engine exhaust gas stream containing hydrocarbons, carbon monoxide, nitrogen oxides, and particulate matter, the exhaust gas treatment system comprising: a lean-burn engine generating an exhaust gas stream; an exhaust conduit in fluid communication with the lean-burn engine via an exhaust manifold; and a catalytic article according to any one of embodiments 21-42 positioned downstream of the lean-burn engine and in fluid communication with the exhaust gas stream.

[0069] Embodiment 44: Soot filter, selective catalytic reduction (SCR) catalyst, urea injection component, ammonia oxidation (AMOx) catalyst, low temperature NO x Absorbent (LT-NA), and Lean NO x 44. The exhaust gas treatment system of embodiment 43, further comprising one or more additional components selected from the group consisting of: a trap (LNT).

[0070] Embodiment 45: The exhaust gas treatment system of embodiment 43 or 44, wherein the lean-burn engine is a diesel engine.

[0071] Embodiment 46: A method for treating a lean-burn engine exhaust gas stream, comprising contacting the exhaust gas stream with the catalytic article of any one of embodiments 21-42 or the exhaust gas treatment system of any one of embodiments 43-45.

[0072] Embodiment 47: A method for reducing CO and / or HC levels in an exhaust gas stream, comprising contacting the exhaust gas stream with the catalytic article of any one of embodiments 21-42 or the exhaust gas treatment system of any one of embodiments 43-45 for a time and at a temperature sufficient to reduce the CO and / or HC levels in the gas stream.

[0073] Embodiment 48: The method of embodiment 47, wherein the CO and / or HC levels in the exhaust gas stream are reduced by at least 30% compared to the CO and / or HC levels in the gas stream prior to contact with the catalytic article.

[0074] These and other features, aspects, and advantages of the present disclosure will become apparent upon reading the following detailed description in conjunction with the accompanying drawings, which are briefly described below. The present invention includes any combination of two, three, four, or more of the above-described embodiments, and any combination of two, three, four, or more features or elements described in this disclosure, regardless of whether such features or elements are explicitly combined in the description of a particular embodiment herein. It is intended that this disclosure be read as a whole such that separable features or elements of the disclosed invention should be considered combinable in any of its various aspects and embodiments, unless the context clearly indicates otherwise. Other aspects and advantages of the present invention will become apparent hereinafter. [Brief description of the drawings]

[0075] To provide an understanding of embodiments of the present invention, reference is made to the accompanying drawings, in which reference numerals indicate components of exemplary embodiments of the present invention. The drawings are merely examples and should not be construed as limiting the present invention. The disclosure described herein is illustrated by way of example, and not by way of limitation, in the accompanying figures. For simplicity and clarity of illustration, features illustrated in the figures have not necessarily been drawn to scale. For example, the dimensions of some features may be exaggerated relative to other features for clarity. Moreover, where considered appropriate, reference numerals may be repeated among the figures to indicate corresponding or similar elements.

[0076] [Figure 1A] FIG. 1 is a perspective view of a honeycomb-type substrate that may include a catalyst (i.e., low temperature CO oxidation catalyst) washcoat composition according to the present disclosure. [Figure 1B] 1B is a partial cross-sectional view taken along a plane parallel to the end face of the substrate of FIG. 1A, enlarged relative to FIG. 1A, showing an enlarged view of multiple gas flow paths shown in FIG. 1 in an embodiment in which the substrate is a flow-through substrate. [Diagram 2] FIG. 1B is an enlarged cross-sectional cutaway view relative to FIG. 1A, in which the honeycomb-type substrate in FIG. 1A corresponds to a wall-flow filter. [Figure 3A] FIG. 1 is a cross-sectional view of one embodiment of a zoned catalyst article of the present disclosure. [Figure 3B] 1 is a cross-sectional view of one embodiment of a layered catalyst article of the present disclosure. [Figure 3C] FIG. 2 is a cross-sectional view of another embodiment of a layered catalyst article of the present disclosure. [Figure 4A] 1 shows a cross-sectional view of an embodiment of a layered catalyst article of the present disclosure having three washcoat layers. [Figure 4B] 1 shows a cross-sectional view of an embodiment of a layered catalyst article of the present disclosure having three washcoat layers. [Figure 4C] 1 shows a cross-sectional view of an embodiment of a layered catalyst article of the present disclosure having three washcoat layers. [Figure 4D]1 shows a cross-sectional view of an embodiment of a layered catalyst article of the present disclosure having three washcoat layers. [Figure 4E] 1 shows a cross-sectional view of an embodiment of a layered catalyst article of the present disclosure having three washcoat layers. [Figure 4F] 1 shows a cross-sectional view of an embodiment of a layered catalyst article of the present disclosure having three washcoat layers. [Figure 4G] 1 shows a cross-sectional view of an embodiment of a layered catalyst article of the present disclosure having three washcoat layers. [Figure 5A] FIG. 1 is a schematic diagram of one embodiment of an exhaust gas treatment system including a catalyst article of the present disclosure in combination with a DOC article (LT-CO / DOC), the LT-CO / DOC being located upstream of a low temperature NOx absorbent (LT-NA), a catalyzed soot filter (CSF), and a selective catalytic reduction (SCR) catalyst component. [Figure 5B] FIG. 1 is a schematic diagram of one embodiment of an exhaust gas treatment system including a catalyst article of the present disclosure in combination with a DOC article, where the LT-CO / DOC is located upstream of the CSF and SCR catalyst components and downstream of the LT-NA component. [Figure 5C] FIG. 1 is a schematic diagram of one embodiment of an exhaust gas treatment system including a LT-CO oxidation catalyst article of the present disclosure in combination with a DOC article, with the LT-CO / DOC located upstream of the LT-NA, SCR catalyst component, and CSF. [Figure 5D] FIG. 1 is a schematic diagram of one embodiment of an exhaust gas treatment system including a catalyst article of the present disclosure in combination with a DOC article, with the LT-CO / DOC located downstream of the LT-NA and upstream of the SCR catalyst component and CSF. [Figure 5E] FIG. 1 is a schematic diagram of one embodiment of an exhaust gas treatment system including a catalyst article of the present disclosure, the catalyst article including a LT-NA composition in addition to a LT-CO composition, the LT-CO / LT-NA being located upstream of a DOC, an SCR catalyst component, and a CSF catalyst component. [Figure 5F]FIG. 1 is a schematic diagram of one embodiment of an exhaust gas treatment system including a catalyst article of the present disclosure in combination with an LNT article, the LT-CO / LNT being located upstream of the DOC article, the SCR catalyst component, and the CSF. [Figure 6] 1 is a line graph showing CO conversion as a function of temperature for various catalyst composition samples of the present disclosure. [Figure 7] 1 is a line graph showing HC conversion as a function of temperature for various catalyst composition samples of the present disclosure. [Figure 8] 1 is a line graph showing CO light-off temperature as a function of tin (Sn) loading for various catalyst composition samples of the present disclosure. [Figure 9] 1 is a line graph showing CO light-off temperature as a function of tin (Sn) loading for various catalyst composition samples of the present disclosure. [Figure 10] 1 is a line graph showing CO light-off temperature as a function of tin (Sn) loading for various catalyst composition samples of the present disclosure. [Figure 11] 1 is a line graph showing CO light-off temperature as a function of tin (Sn) loading for various catalyst composition samples of the present disclosure. [Figure 12] 1 is a line graph showing CO light-off temperature as a function of tin (Sn) loading for various catalyst composition samples of the present disclosure. [Figure 13] 1 is a line graph showing CO light-off temperature as a function of tin (Sn) loading for various catalyst composition samples of the present disclosure. [Figure 14] 1 is a line graph showing HC light-off temperature as a function of tin (Sn) loading for various catalyst composition samples of the present disclosure. [Figure 15] 1 is a line graph showing HC light-off temperature as a function of tin (Sn) loading for various catalyst composition samples of the present disclosure. [Figure 16]1 is a line graph showing NO2 production as a function of tin (Sn) loading for various catalyst composition samples of the present disclosure. [Figure 17] 1 is a line graph showing NO2 production as a function of tin (Sn) loading for various catalyst composition samples of the present disclosure. [Figure 18] 1 is a line graph showing simulated exhaust gas flow conditions along with temperature and velocity profiles for the New European Driving Cycle (NEDC). [Figure 19] 1 is a line graph showing cumulative tailpipe CO emissions under the NEDC protocol for various catalyst composition samples of the present disclosure. [Figure 20] 1 is a line graph showing cumulative tailpipe HC emissions under the NEDC protocol for various sample catalyst compositions of the present disclosure. [Figure 21] 1 is a bar graph showing CO and HC conversion for various catalyst composition samples in the New European Driving Cycle (NEDC). DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0077] The present disclosure generally provides low temperature CO (LT-CO) oxidation catalyst compositions, catalyst articles, and catalyst systems including such catalyst articles suitable for oxidizing carbon monoxide (CO) and hydrocarbon (HC) emissions from lean-burn engines under cold start conditions. In particular, such articles and systems include a LT-CO oxidation catalyst composition for mitigating exhaust gas emissions from a lean-burn engine, the catalyst composition including an oxygen storage component (OSC), a first platinum group metal (PGM) component, and a promoter metal, the OSC being impregnated with the first PGM component and the promoter metal, and the oxidation catalyst composition being effective for oxidizing CO and HC under cold start conditions.

[0078] The present invention will now be described more fully hereinafter. However, the present invention may be embodied in many different forms and should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art.

[0079] definition The articles "a" and "an" herein refer to one or more than one (e.g., at least one) of the grammatical object. All ranges cited herein are inclusive. The term "about" used throughout is used to express and account for small variations. For example, "about" can mean that a numerical value may vary by ±5%, ±4%, ±3%, ±2%, ±1%, ±0.5%, ±0.4%, ±0.3%, ±0.2%, ±0.1%, or ±0.05%. All numerical values ​​are modified by the term "about", whether or not expressly stated. Numeric values ​​modified by the term "about" include the specific identified value. For example, "about 5.0" includes 5.0.

[0080] The term "reduction" refers to a decrease in amount caused by any means.

[0081] The term "associated" means, for example, "comprising," "connected to," or "in communication with," e.g., "electrically connected to" or "in fluid communication with," or connected to perform a function. The term "associated" can mean directly associated or indirectly associated, for example, through one or more other items or elements.

[0082] Average particle size is synonymous with D50, meaning that half the number of particles have a larger size and half have a smaller size. Particle size refers to the primary particles. Particle size may be measured by laser light scattering technique using dispersed or dry powders according to ASTM method D4464.

[0083] The term "catalyst" refers to a material that promotes a chemical reaction. A catalyst includes a "catalytically active species" and a "support" that carries or supports the active species. For example, a zeolite can be a support for, for example, a platinum group metal (PGM) or base metal active catalytic species. Similarly, refractory metal oxide particles can be a support for a platinum group metal catalytic species. The catalytically active species is also called a "promoter" because it promotes a chemical reaction. For example, the PGM-containing zeolite can be called a PGM-promoted zeolite. A "promoted zeolite" refers to a zeolite to which a catalytically active species has been intentionally added.

[0084] As used herein, the term "catalytic article" or "catalyst article" refers to an article that includes a substrate having a catalytic coating composition.

[0085] As used herein, "crystal size" refers to the length of one edge of a face of the crystal, preferably the longest edge, provided that the crystal is not needle-like. Direct measurement of crystal size can be performed using microscopy methods such as SEM and TEM. For example, measurement by SEM involves examining the morphology of the material at high magnification (typically 1000x to 10,000x). SEM methods can be performed by distributing a representative portion of the zeolite powder on a suitable mount, whereby the individual particles are reasonably uniformly spread across the field of view at 1000x to 10,000x magnification. From this population, a statistically significant sample of random individual crystals (e.g., 50-200) is examined and the longest dimension of the individual crystals, parallel to the horizontal line of the straight edge, is measured and recorded. Particles that are clearly large polycrystalline aggregates are not included in the measurement. Based on these measurements, the arithmetic mean of the crystal size of the sample is calculated.

[0086] "CSF" refers to a catalyzed soot filter, which is a wall-flow monolith. Wall-flow filters consist of alternating inlet and outlet channels, with the inlet channels inset into the outlet end and the outlet channels inset into the inlet end. The soot-carrying exhaust gas stream entering the inlet channels is forced through the filter wall before exiting the outlet channels. In addition to soot filtration and regeneration, ACSFs also convert CO and HC to CO to accelerate downstream SCR catalysts or to promote oxidation of soot particles at lower temperatures. 2 and H 2 For oxidation of NO to O or NO 2 The SCR catalyst composition may also be coated directly onto a wall-flow filter, known as an SCRoF.

[0087] As used herein, the phrase "catalyst system" refers to a combination of two or more catalysts, for example, a LT-CO oxidation catalyst article and a second catalyst article, which may be a diesel oxidation catalyst (DOC), LNT, or SCR. Alternatively, the catalyst system may be in the form of a washcoat, where the two catalysts are mixed together or coated as catalyst compositions in separate layers on a single substrate, such as a LT-CO / DOC, LT-CO / LT-NA, or LT-CO / LNT article.

[0088] The term "comprised of" as used in the specification and claims is intended to be an open-ended term, similar to the terms "comprise" or "contain." The term "comprised of" is not meant to exclude other possible items or elements. The term "comprised of" may be equivalent to "adapted."

[0089] "DOC" refers to a diesel oxidation catalyst that converts hydrocarbons and carbon monoxide in the exhaust gas of a diesel engine. Typically, a DOC contains one or more platinum group metals, such as palladium and / or platinum, a support material, such as alumina, a zeolite for HC storage, and optionally promoters and / or stabilizers.

[0090] In general, the term "effective" means, for example, about 35% to 100% effective, e.g., about 40%, about 45%, about 50% or about 55% to about 60%, about 65%, about 70%, about 75%, about 80%, about 85%, about 90% or about 95% effective in terms of a specified catalytic activity or storage / release activity by weight or mole.

[0091] The term "exhaust stream" or "exhaust gas stream" refers to any combination of flowing gases that may contain solid or liquid particulate matter. The stream is, for example, the exhaust of a lean-burn engine that includes gaseous components and may contain certain non-gaseous components such as liquid droplets, solid particulates, etc. The exhaust gas stream of a combustion engine typically contains products of combustion (CO 2 and H 2 O), products of incomplete combustion (carbon monoxide (CO) and hydrocarbons (HC)), oxides of nitrogen (NO x ), combustible and / or carbonaceous particulate matter (soot), and unreacted oxygen and nitrogen. As used herein, the terms "upstream" and "downstream" refer to the relative directions relative to the flow of the engine exhaust gas stream from the engine toward the tailpipe, with the engine being at the upstream location and the tailpipe and any pollution abatement articles such as filters and catalysts being downstream of the engine. The inlet end of the substrate is synonymous with the "upstream" end or the "front" end. The outlet end is synonymous with the "downstream" end or the "rear" end. The upstream zone is upstream of the downstream zone. The upstream zone may be near the engine or manifold, and the downstream zone may be further away from the engine or manifold.

[0092] The term "fluid communication" is used to refer to articles positioned in the same exhaust line, i.e., a common exhaust flow passes through articles that are in fluid communication with one another. Articles in fluid communication may be adjacent to one another in the exhaust line. Alternatively, articles in fluid communication may be separated by one or more articles, also referred to as "washcoat monoliths."

[0093] The term "functional article" in this invention means an article that includes a substrate having a functional coating composition, particularly a catalyst and / or adsorbent coating composition, disposed thereon.

[0094] As used herein, "impregnated" or "impregnation" refers to the infiltration of a catalytic material into the porous structure of a support material.

[0095] "LNT" refers to platinum group metals, ceria, and NO under lean conditions. x A catalyst containing an alkaline earth trapping material (e.g., BaO or MgO) suitable for adsorbing lean NO x Under rich conditions, NO x is released and reduced to nitrogen.

[0096] "LT-NA" refers to NO during low temperature (e.g., cold start) conditions. x Compositions suitable for adsorbing low temperature NO, e.g., components containing palladium-exchanged zeolite materials. x Under low temperature conditions, as the operating temperature of the LT-NA composition increases, the NO x is adsorbed and then released into the exhaust gas stream.

[0097] As used herein, the term "molecular sieve", such as zeolites and other zeolitic framework materials (e.g., isomorphously substituted materials), refers to materials capable of supporting catalytic PGMs or other catalytic metals in particulate form. Molecular sieves are materials based on an extensive three-dimensional network structure of oxygen ions, generally containing tetrahedral sites and having a substantially uniform pore distribution with an average pore size of 20 Angstroms (Å) or less.

[0098] The terms "on" and "above" in relation to coating layers can be used synonymously. The term "directly on" means in direct contact. Although the disclosed articles are referred to in certain embodiments as including one coating layer "on" a second coating layer, such language is intended to encompass embodiments having intervening layers where direct contact between coating layers is not required (i.e., "on" is not equivalent to "directly on").

[0099] As used herein, the term "selective catalytic reduction" (SCR) refers to the conversion of nitrogen oxides to dinitrogen (N 2 ) in a catalytic process.

[0100] As used herein, "nitrogen oxides" or "NO x " The term is NO, NO 2 , or N 2 This refers to nitrogen oxides such as O.

[0101] "Substantially free" means "little or no" or "not intentionally added," and also means having only trace and / or incidental amounts. For example, in certain embodiments, "substantially free" means less than 2% by weight (wt %), less than 1.5 wt %, less than 1.0 wt %, less than 0.5 wt %, less than 0.25 wt %, or less than 0.01 wt %, based on the weight of the total composition given.

[0102] As used herein, the term "substrate" refers to a monolith material on which a catalyst composition, i.e., a catalyst coating, is disposed, typically in the form of a washcoat. In one or more embodiments, the substrate is a flow-through monolith and a monolith wall-flow filter. Flow-through and wall-flow substrates are also disclosed, for example, in International Patent Application No. WO2016 / 070090, which is incorporated herein by reference. A washcoat is formed by preparing a slurry containing a catalyst at a particular solids content (e.g., 30% to 90% by weight) in a liquid, which is then coated onto a substrate and dried to provide a washcoat layer. Reference to a "monolith substrate" means a single structure that is homogenous and continuous from inlet to outlet. A washcoat is formed by preparing a slurry containing particles at a particular solids content (e.g., 20% to 90% by weight) in a liquid vehicle, which is then coated onto a substrate and dried to provide a washcoat layer.

[0103] As used herein, the term "support" refers to any high surface area material, usually a metal oxide material, onto which the catalytic precious metal is applied.

[0104] As used herein, the term "washcoat" has its ordinary meaning in the art of a thin adherent coating of catalyst or other material applied to a substrate material, such as a honeycomb-type substrate, that is sufficiently porous to permit the passage of the gas stream to be treated. Washcoats containing the metal-promoted molecular sieves of the present invention may optionally include a binder selected from silica, alumina, titania, zirconia, ceria, or combinations thereof. The binder loading is about 0.1-10 wt. %, based on the weight of the washcoat. As used herein and as described in Heck, Ronald, and Farrauto, Robert, Catalytic Air Pollution Control, New York: Wiley-Interscience, 2002, pp. 18-19, a washcoat layer comprises a compositionally distinct layer of material disposed on the surface of a monolith substrate or an underlying washcoat layer. The substrate may contain one or more washcoat layers, and each washcoat layer may differ in some aspect (e.g., the physical properties of the washcoat, such as particle size or crystallite phase, may differ) and / or the chemical catalytic function may differ.

[0105] Unless otherwise indicated, "weight percent (wt %)" is based on the total composition, free of volatile materials, i.e., dry solids content. All parts and percentages are by weight, unless otherwise indicated.

[0106] As used herein, the term "zeolite" refers to a specific example of a molecular sieve that further contains silicon and aluminum atoms. Generally, zeolites are made up of corner-sharing TO 4 It is defined as an aluminosilicate with an open three-dimensional framework structure composed of tetrahedra, where T is Al or Si, or optionally P. The anionic framework charge-balancing cations are loosely associated with the framework oxygens, and the remaining pore volume is filled with water molecules. Non-framework cations are generally exchangeable and water molecules are removable.

[0107] Aluminosilicate zeolite structures do not contain phosphorus or other metals isomorphously substituted in the framework. That is, "aluminosilicate zeolites" excludes aluminophosphate materials such as SAPO, AlPO, and MeAlPO materials, while the broader term "zeolite" includes aluminosilicates and aluminophosphates. For purposes of this disclosure, SAPO, AlPO, and MeAlPO materials are considered to be non-zeolitic molecular sieves.

[0108] The zeolite is made up of individual SiO 4 / AlO 4 The silica to alumina ("SAR") molar ratio of the zeolite can vary over a wide range and is generally greater than or equal to 2. For example, the zeolite can have a SAR of from about 5 to about 1000.

[0109] Zeolites are mainly composed of (SiO 4 ) / AlO 4 They can be distinguished according to the shape of the cavity formed by the robust network structure of tetrahedra: the entrance to the cavity is formed from 6, 8, 10 or 12 ring atoms, with respect to the atoms forming the entrance opening.

[0110] Zeolites consist of secondary building units (SBUs) and composite building units (CBUs) and occur in many different framework structures. Secondary building units contain up to 16 tetrahedral atoms and are not chiral. Composite building units are not necessarily achiral and are not necessarily usable for the construction of the entire framework. For example, a group of zeolites has single tetracyclic (s4r) composite building units in their framework structures. In the tetracyclic, the "tetra" indicates the position of the tetrahedral silicon and aluminum atoms, and the oxygen atom is located between the tetrahedral atoms. Other composite building units include, for example, single hexacyclic (s6r) units, double tetracyclic (d4r) units, and double hexacyclic (d6r) units. The d4r units result from the combination of two s4r units. The d6r units result from the combination of two s6r units. A d6r unit has 12 tetrahedral atoms.

[0111] Typically, any framework type of zeolite, e.g., ABW, ACO, AEI, AEL, AEN, AET, AFG, AFI, AFN, AFO, AFR, AFS, AFT, AFX, AFY, AHT, ANA, APC, APD, AST, ASV, ATN, ATO, ATS, ATT, ATV, AVL, AWO, AWW, BCT, BEA, BEC, BIK, BOG, BPH, BRE, CAN, CAS, SCO, CFI, SGF, CGS, CHA, CHI, CLO, CON, CZP, DAC, DDR, DFO, DFT, DOH, DON, EAB, EDI, EEI, EMT, EON, EPI, ERI, ESV, ETR, EUO, FAU, FER, FRA, GIS, GIU, GME, GON, GOO, HEU, IFR, IFY, IHW, IRN, ISV, ITE, ITH, ITW, IWR, IWW, JBW, KFI, LAU, LEV, LIO, LIT, LOS, LOV, LTA, LTL, LTN, MAR, MAZ, MEI, MEL, MEP, MER, MFI, MFS, MON, MOR, MOZ, MSO, MTF, MTN, MTT, MTW, MWF, MWW, NAB, NAT, NES, NON, NPO, NPT, NSI, OBW, OFF, OSI, OSO, OWE, PAR, PAU, PHI, PON, RHO, RON, RRO, RSN, RTE, RTH, RUT, RWR, RWY, SAO, SAS, SAT, SAV, SBE, SBS, SBT, SFE, SFF, SFG, SFH, SFN, SFO, SFW, SGT, SOD, SOS, SSY, STF, STI, STT, TER, THO, TON, TSC, UEI, UFI, UOZ, USI, UTL, VET, VFI, VNI, VSV, WIE, WEN, YUG, ZON, or a framework type that is a combination thereof may be used.

[0112] For example, the zeolite may include a framework type selected from the group consisting of AEI, BEA (beta zeolite), CHA (chabazite), FAU (zeolite Y), FER (ferrierite), MFI (ZSM-5), and MOR (mordenite). Non-limiting examples of zeolites having the AEI, BEA, CHA, FAU, FER, MFI, or MOR structure include chabazite, faujasite, zeolite Y, ultrastable zeolite Y, beta zeolite, mordenite, silicalite, zeolite X, and ZSM-5.

[0113] For example, the zeolite may have the chabazite crystal structure, also referred to as the CHA structure by the International Zeolite Association. Zeolite CHA framework type molecular sieves have the approximate formula: (Ca, Na 2 , K 2 , Mg)Al 2 SiO 12 6H 2The zeolite chabazite includes naturally occurring tectosilicate minerals of the zeolite group having a zeolite structure with a zeolite structure of 0 (e.g., hydrated aluminum silicate). Three synthetic forms of zeolite chabazite are described in "Zeolite Molecular Sieves," by DW Breck, published in 1973 by John Wiley & Sons, which is incorporated herein by reference. The three synthetic forms reported by Breck are Zeolite KG, described in Barrer et al., J. Chem. Soc., p. 2822 (1956), Zeolite D, described in British Patent No. 868,846 (1961), and Zeolite R, described in U.S. Pat. No. 3,030,181, which is incorporated herein by reference. The synthesis of another synthetic form of zeolite chabazite SSZ-13 is described in U.S. Pat. No. 4,544,538. The synthesis of silicoaluminophosphate 34 (SAPO-34), a synthetic form of a non-zeolitic molecular sieve having the chabazite crystal structure, is described in U.S. Patent No. 4,440,871 and U.S. Patent No. 7,264,789, each of which is incorporated herein by reference in its entirety. A method for making yet another synthetic non-zeolitic molecular sieve having the chabazite structure, SAPO-44, is described, for example, in U.S. Patent No. 6,162,415, which is incorporated herein by reference in its entirety.

[0114] Zeolites are crystalline materials with fairly uniform pore sizes ranging from about 3 to 10 angstroms in diameter, depending on the type of zeolite and the type and amount of cations contained in the zeolite lattice. The pore sizes are defined by the ring diameter. As used herein, the term "small pore" refers to pore openings smaller than about 5 angstroms, e.g., pore openings on the order of about 3.8 angstroms.

[0115] Small pore zeolites contain channels defined by up to eight tetrahedral atoms. The phrase "eight-ring" zeolites refers to zeolites having eight-ring pore openings and double hexagonal secondary structural units, and having a cage-type structure resulting from the connection of double hexagonal structural units by four rings.

[0116] Exemplary small pore molecular sieves include framework types ACO, AEI, AEN, AFN, AFT, AFX, ANA, APC, APD, ATT, CDO, CHA, DDR, DFT, EAB, EDI, EPI, ERI, GIS, GOO, IHW, ITE, ITW, LEV, KFI, MER, MON, NSI, OWE, PAU, PHI, RHO, RTH, SAT, SAV, SIV, THO, TSC, UEI, UFI, VNI, YUG, ZON, and mixtures or intergrowths thereof.

[0117] Medium pore zeolites contain channels defined by 10-membered rings. Exemplary medium pore zeolites include framework types AEL, AFO, AHT, BOF, BOZ, CGF, CGS, CHI, DAC, EUO, FER, HEU, IMF, ITH, ITR, JRY, JSR, JST, LAU, LOV, MEL, MFI, MFS, MRE, MTT, MVY, MWW, NAB, NAT, NES, OBW, PAR, PCR, PON, PUN, RRO, RSN, SFF, SFG, STF, STI, STT, STW, SVR, SZR, TER, TON, TUN, UOS, VSV, WEI, WEN, and mixtures or intergrowths thereof.

[0118] Large pore zeolites contain channels defined by 12-membered rings. Exemplary large pore zeolites include framework types AFI, AFR, AFS, AFY, ASV, ATO, ATS, BEA, BEC, BOG, BPH, BSV, CAN, CON, CZP, DFO, EMT, EON, EZT, FAU, GME, GON, IFR, ISV, ITG, IWR, IWS, IWV, IWW, JSR, LTF, LTL, MAZ, MEI, MOR, MOZ, MSE, MTW, NPO, OFF, OKO, OSI, RON, RWY, SAF, SAO, SBE, SBS, SBT, SEW, SFE, SFO, SFS, SFV, SOF, SOS, STO, SSF, SSY, USI, UWY, VET, and mixtures or intergrowths thereof.

[0119] All methods described herein can be performed in any suitable order unless otherwise indicated herein or clearly contradicted by context. The use of any and all examples or exemplary language (e.g., "such as") provided herein is intended only to better describe the materials and methods and does not limit the scope unless otherwise claimed. No language in the specification should be construed as indicating any non-claimed element as essential to the practice of the disclosed materials and methods.

[0120] All U.S. patent applications, pregrant publications and patents mentioned herein are incorporated by reference in their entirety.

[0121] LT-CO oxidation catalyst composition The present disclosure provides a LT-CO oxidation catalyst composition that includes an oxygen storage component (OSC), a first platinum group metal (PGM) component, and a first promoter metal, wherein the OSC is impregnated with the first PGM component and the first promoter metal, and wherein the LT-CO oxidation catalyst composition is effective for oxidizing carbon monoxide and hydrocarbons under cold start conditions.

[0122] Oxygen Storage Components As used herein, an oxygen storage component (OSC) is a component that has multiple oxidation states and can store oxygen (O 2 ) or nitrogen oxides (NO x ) or under reducing conditions with carbon monoxide (CO), hydrocarbons (HC) or hydrogen (H 2) can be actively reacted with a reductant such as a rare earth metal oxide. Certain exemplary OSCs are rare earth metal oxides, which refer to one or more oxides of the scandium, yttrium, and lanthanum series as defined in the Periodic Table of the Elements. In some embodiments, the OSC comprises a rare earth metal oxide in an amount ranging from about 0.1 to about 100 weight percent, based on the weight of the OSC alone. By "weight of OSC alone" is meant the weight of the OSC without additional components such as PGMs or promoter metals (i.e., the weight of the OSC before the first PGM or promoter metal is impregnated). Thus, it is contemplated that the OSC may comprise more than one metal oxide, for example, a mixture of one or more rare earth metal oxides. In some embodiments, the OSC consists of a single rare earth metal oxide (i.e., 100 weight percent). In some embodiments, the OSC comprises ceria in combination with one or more other oxides, including, for example, zirconium (Zr), titanium (Ta), lanthanum (La), praseodymium (Pr), neodymium (Nd), niobium (Nb), yttrium (Y), samarium (Sm), gadolinium (Gd), and combinations comprising at least two of the foregoing metals. Such combinations are sometimes referred to as mixed oxide composites. For example, "ceria-zirconia composite" refers to a composite comprising ceria and zirconia without specifying the amount of either component. Suitable ceria-zirconia composites include, but are not limited to, composites having a ceria content ranging from about 5% to about 95%, preferably from about 5% to about 75%, more preferably from about 10% to about 70% by weight (e.g., at least about 5%, at least about 10%, at least about 20%, at least 30%, at least 40%, at least 50%, at least 60%, at least 70%, at least 80%, at least 90%, or at least about 95% by weight ceria) based on the total weight of the ceria-zirconia composite. In some embodiments, the OSC is 100% ceria. In some embodiments, the ceria has a high surface area. As used herein, "high surface area ceria" refers to a composite having a ceria content of 60 m when fresh (i.e., not hydrothermally treated at high temperature).2 / g。 Ceria having a surface area of ​​more than 1.5 μm / g.

[0123] platinum group metals As used herein, "PGM" refers to platinum group metals. Platinum group metals include platinum (Pt), palladium (Pd), ruthenium (Ru), rhodium (Rh), osmium (Os), iridium (Ir), and mixtures thereof. As used herein, "PGM component" refers to platinum group metals or compounds or complexes thereof that decompose or are otherwise converted to a catalytically active form, typically the metal or respective metal oxide, upon calcination or use of the catalyst. For example, the PGM may be in a metallic form with a zero valence, or the PGM may be in an oxide form. The PGM component may include PGMs in any valence state. In some embodiments, the PGM component is a metal or an oxide thereof, including, but not limited to, platinum or an oxide thereof.

[0124] In certain embodiments, the first PGM component includes a combination of platinum group metals, such as a combination of platinum and palladium. Exemplary weight ratios of such combinations include Pt:Pd of about 1:10 to about 10:1, more typically Pt:Pd of about 1 or more:1, Pt:Pd of about 1.5 or more:1, or Pt:Pd of about 2 or more:1. In other embodiments, the first PGM component includes platinum or palladium. In certain embodiments, the first PGM component is Pd. In certain embodiments, the first PGM component is Pt. The concentration of the first PGM component (e.g., Pt and / or Pd) can vary, but is typically about 1% to about 10% by weight based on the weight of the OSC alone (e.g., about 1% to about 4% by weight based on the weight of the OSC alone).

[0125] Promoter Metal The LT-CO oxidation catalyst composition of the present disclosure includes a promoter metal. As used herein, "promoter metal" refers to a base metal or its oxide. As used herein, "base metal" refers to a metal selected from copper, lead, iron, nickel, zinc, aluminum, tin, tungsten, molybdenum, tantalum, cobalt, bismuth, cadmium, titanium, zirconium, antimony, manganese, beryllium, chromium, germanium, vanadium, gallium, hafnium, indium, niobium, rhenium, thallium, and combinations thereof. In some embodiments, a "first promoter metal" and a "second promoter metal" are referred to. Thus, each of the first and second promoter metals is independently selected from copper, lead, iron, nickel, zinc, aluminum, tin, tungsten, molybdenum, tantalum, cobalt, bismuth, cadmium, titanium, zirconium, antimony, manganese, beryllium, chromium, germanium, vanadium, gallium, hafnium, indium, niobium, rhenium, thallium, or combinations thereof. In some embodiments, the first and second promoter metals are the same. In some embodiments, the first and second promoter metals are different from one another. In some embodiments, the first promoter metal is tin (Sn) or an oxide thereof. In some embodiments, the second promoter metal is tin (Sn) or an oxide thereof. In some embodiments, the first promoter metal, the second promoter metal, or both are manganese (Mn) or an oxide thereof. In some embodiments, the first promoter metal is present in an amount of about 0.1 to about 10% by weight of the OSC alone, calculated on the metal oxide basis. In some embodiments, the second promoter metal is present in an amount of about 0.1 to about 10% by weight of the second refractory metal oxide or the second zeolite, or both, calculated on a metal oxide basis. In some embodiments, the first promoter metal is present in an amount of about 0.5 to about 4% by weight of the OSC alone, calculated on a metal oxide basis. In some embodiments, the second promoter metal is present in an amount of about 0.5 to about 4% by weight of the second refractory metal oxide or the second zeolite, or both, calculated on a metal oxide basis.

[0126] In certain embodiments, the OSC is ceria, the first PGM component is Pd, Pt, or a combination thereof, and the first promoter metal is Sn. In certain embodiments, the OSC is ceria, the first PGM component is present at about 2 wt.% based on the weight of the OSC alone and is Pd or Pt, and the first promoter metal is present at about 1 wt.% based on the weight of the OSC alone and is Sn or an oxide thereof.

[0127] refractory metal oxide In some embodiments, the LT-CO oxidation catalyst composition may further comprise a first refractory metal oxide. As used herein, "refractory metal oxide" refers to a porous metal-containing oxide material that exhibits chemical and physical stability at high temperatures, for example, at temperatures associated with diesel engine exhaust. Exemplary refractory metal oxides include alumina, silica, zirconia, titania, yttria, ceria, praseodymia, and physical mixtures or chemical combinations thereof, including atomically doped combinations and including high surface area or activated compounds, such as activated alumina. Included are metal oxide combinations such as silica-alumina, ceria-zirconia, praseodymium-ceria, alumina-zirconia, alumina-ceria-zirconia, lanthana-alumina, lanthana-zirconia-alumina, baria-alumina, baria-lanthana-alumina, baria-lanthana-neodymia-alumina, and alumina-ceria. In some embodiments, the first refractory metal oxide is selected from the group consisting of alumina, silica, zirconia, titania, yttria, and combinations thereof. Exemplary aluminas include large pore boehmite, gamma-alumina, and delta / theta alumina. Useful commercially available aluminas include high bulk density gamma-alumina, low or medium bulk density large pore gamma-alumina, and activated aluminas such as low bulk density large pore boehmite and gamma-alumina.

[0128] Refractory metal oxides are sometimes referred to as "high surface area" refractory metal oxides. These can include materials such as high surface area alumina, also called "gamma alumina" or "activated alumina," which typically have a surface area of ​​60 m. 2 / g, usually up to about 200m 2 Exemplary refractory metal oxides exhibit a BET surface area of ​​about 50 m / g or more. 2 / g~about 300m 2 Activated aluminas include high surface area gamma-aluminas having specific surface areas of 100 nm / g. Such activated aluminas are usually mixtures of gamma and delta phases of alumina, but may also contain significant amounts of eta, kappa, and theta alumina phases. "BET surface area" refers to the N 2 It has its ordinary meaning associated with the Brunauer, Emmett and Teller method of determining surface area by adsorption. Preferably, the activated alumina has a surface area of ​​about 60 m 2 / g ~ approx. 350m 2 / g, for example, about 90m 2 / g ~ approx. 250m 2 / g.

[0129] The LT-CO oxidation catalyst composition can include any of the above named refractory metal oxides in any amount. The catalyst composition can include, for example, from about 30 to about 80 weight percent of the first refractory metal oxide.

[0130] In some embodiments, a second refractory metal oxide is mentioned. In these embodiments, "refractory metal oxide" has the same meaning as defined for the first refractory metal oxide. In some embodiments, the first and second refractory metal oxides are each independently selected. In some embodiments, the first and second refractory metal oxides are the same. In some embodiments, the LT-CO oxidation catalyst composition disclosed herein further comprises a first refractory metal oxide selected from the group consisting of alumina, silica, zirconia, titania, yttria, and combinations thereof.

[0131] Zeolite In some embodiments, the LT-CO oxidation catalyst composition may further comprise one or more zeolites. In some embodiments, a first zeolite is mentioned. In some embodiments, the first zeolite comprises one or more zeolites. In some embodiments, the one or more zeolites are small pore zeolites having a 6-8 membered ring structure (e.g., the first zeolite can be a single small pore zeolite or several different small pore zeolites). In some embodiments, the one or more small pore zeolites are selected from the group consisting of chabazite (CHA), zeolite A (LTA), and combinations thereof. In some embodiments, the first zeolite comprises one or more medium pore or large pore zeolites having a 10-12 membered ring structure (e.g., the first zeolite can be a single medium pore or large pore zeolite or several different medium pore or large pore zeolites). In some embodiments, the one or more medium or large pore zeolites are selected from the group consisting of ferrierite (FER), ZSM-5 (MFI), beta zeolite (BEA), Y zeolite (FAU), and combinations thereof.

[0132] Alkaline Earth Metal Components In some embodiments, the LT-CO oxidation catalyst composition may further include an alkaline earth metal component. As used herein, the term "alkaline earth metal component" refers to an alkaline earth metal compound, complex, or the like, which decomposes or is otherwise converted to a catalytically active form, typically a metal oxide, upon calcination or use of the catalyst. As used herein, the term "alkaline earth metal" refers to a Group II metal, such as magnesium, calcium, strontium, and barium. In some embodiments, the alkaline earth metal component is an oxide of barium, calcium, magnesium, strontium, or mixtures thereof. In some embodiments, the alkaline earth metal component is an oxide of barium. In some embodiments, the alkaline earth metal component is an oxide of magnesium. In some embodiments, the alkaline earth metal component is impregnated or disposed on the rare earth metal oxide (i.e., the rare earth metal oxide is doped with the alkaline earth metal component).

[0133] While the foregoing description provides several preferred ranges or amounts for the OSC, promoter metal, refractory metal oxide, and PGM components of the LT-CO oxidation catalyst composition, it should be noted that each disclosed range or amount for one of these components may be combined with the disclosed ranges or amounts for the other components to form new ranges or subranges, and such embodiments are also expressly contemplated by this invention.

[0134] catalyst article In one or more embodiments, the LT-CO oxidation catalyst composition of the present invention is disposed on a substrate in the form of a washcoat to form a catalyst article. The catalyst article, including the coated substrate, is part of an exhaust gas treatment system (e.g., catalyst articles include, but are not limited to, articles including the LT-CO oxidation catalyst compositions disclosed herein).

[0135] Base material Useful substrates are three-dimensional, having a length, diameter and volume similar to a cylinder. The shape does not necessarily have to conform to a cylinder. The length is the axial length defined by the inlet and outlet ends.

[0136] According to one or more embodiments, the substrate for the disclosed compositions may be composed of any material typically used to prepare automotive catalysts, and typically includes a metal or ceramic honeycomb structure. The substrate typically provides a plurality of walls onto which the washcoat composition is applied and adheres, thereby serving as a substrate for the catalyst composition.

[0137] The ceramic substrate may be made from any suitable refractory material, such as cordierite, cordierite-α-alumina, aluminum titanate, silicon titanate, silicon carbide, silicon nitride, zircon mullite, spodumene, alumina-silica-magnesia, zircon silicate, sillimanite, magnesium silicate, zircon, petalite, α-alumina, aluminosilicates, and the like.

[0138] The substrate may also be metallic and include one or more metals or metal alloys. Metal substrates may include any metal substrate having openings or "punches out" in the channel walls. Metal substrates may be used in various shapes such as pellets, corrugated sheets, or monolith forms. Specific examples of metal substrates include heat-resistant base metal alloys, particularly alloys in which iron is a substantial or major component. Such alloys may contain one or more of nickel, chromium, and aluminum, the sum of which may advantageously include at least about 15% by weight (weight percent) of the alloy, in each case based on the weight of the substrate, for example, about 10 to about 25% by weight chromium, about 1 to about 8% by weight aluminum, and 0 to about 20% by weight nickel. Examples of metal substrates include those with straight channels, those with protruding blades along the axial channels to disrupt gas flow and open gas flow communication between the channels, and those that also have holes to improve gas transport between the channels, allowing radial gas transport throughout the blades and monoliths. In particular, metal substrates are advantageously employed in close-coupled locations in certain embodiments, thereby allowing rapid heating of the substrate and, correspondingly, rapid heating of the catalyst composition (e.g., the LT-CO oxidation catalyst composition) coated therein.

[0139] Any suitable substrate for the catalytic article disclosed herein may be used, such as a monolith substrate of the type having fine parallel gas passages extending from the inlet or outlet end face of the substrate through which the passages are open to the flowing fluid stream ("flow-through substrate"). Another suitable substrate is of the type having a plurality of fine substantially parallel gas passages extending along the longitudinal axis of the substrate, typically with each passage blocked at one end of the substrate body and every other passage blocked at the opposite end face ("wall-flow filter"). Flow-through and wall-flow substrates are also disclosed, for example, in International Application WO2016 / 070090, the entire contents of which are incorporated herein by reference.

[0140] In some embodiments, the catalytic substrate comprises a honeycomb substrate in the form of a wall-flow filter or a flow-through substrate. In some embodiments, the substrate is a wall-flow filter. Flow-through substrates and wall-flow filters are further described below.

[0141] Flow-Through Substrate In some embodiments, the substrate is a flow-through substrate (e.g., a monolith substrate, including a flow-through honeycomb monolith substrate). A flow-through substrate has fine, parallel gas flow passages extending from the inlet end to the outlet end of the substrate such that the passages are open to fluid flow. The passages, which are generally linear paths from the fluid inlet to the fluid outlet, are defined by walls on which a catalytic coating is disposed such that gas flowing through the passages contacts the catalytic material. The flow passages of the flow-through substrate are thin-walled channels and can be of any suitable cross-sectional shape and size, such as trapezoidal, rectangular, square, sinusoidal, hexagonal, elliptical, circular, etc. The flow-through substrate can be ceramic or metallic, as described above.

[0142] The flow-through substrate may be, for example, about 50 in 3 ~About 1200in 3 and a cell density (inlet opening) of about 200 to about 400 cpsi, and a wall thickness of about 50 to about 200 microns or about 400 microns.

[0143] A catalytic article can be provided by applying a catalytic coating to a substrate as a washcoat (e.g., as disclosed herein). Figures 1A and 1B illustrate an exemplary substrate 2 in the form of a flow-through substrate coated with a catalytic composition as described herein. With reference to Figure 1A, the exemplary substrate 2 has a cylindrical shape and a cylindrical outer surface 4, an upstream end face 6, and a corresponding downstream end face 8 that is identical to the end face 6. The substrate 2 has a plurality of fine, parallel gas flow passages 10 formed therein. As seen in Figure 1B, the passages 10 are formed by walls 12 and extend through the carrier 2 from the upstream end face 6 to the downstream end face 8, and the passages 10 are unobstructed to allow a fluid, e.g., gas flow, to flow longitudinally through the carrier 2 and through the gas flow passages 10 thereof. As can be more easily seen in Figure 1B, the walls 12 are so dimensioned and configured such that the gas flow passages 10 have a substantially regular polygonal shape. As shown, the catalytic composition can be applied in multiple separate layers, if desired. In the illustrated embodiment, the catalyst composition consists of both a separate bottom layer 14 attached to the wall 12 of the carrier member, and a second separate top layer 16 coated above the bottom layer 14. The invention can be practiced with one or more (e.g., two, three, four or more) catalyst composition layers and is not limited to the two-layer embodiment illustrated in Figure 1B. Additional coating configurations are disclosed herein below.

[0144] Wall Flow Filter Substrate In some embodiments, the substrate is a wall-flow filter, which generally has a plurality of fine, substantially parallel gas flow passages extending along the longitudinal axis of the substrate. Typically, each passage is blocked at one end of the substrate body, and every other passage is blocked at the opposite end face. Such monolith wall-flow filter substrates may contain up to about 900 or more passages (or "cells") per square inch of cross section, although much smaller numbers may be used. For example, the substrate may have about 7 to 600, more typically about 100 to 400 cells per square inch ("cpsi"). The cells may have a rectangular, square, circular, elliptical, triangular, hexagonal, or other polygonal cross section.

[0145] FIG. 2 is a cross-sectional view of an exemplary monolith wall-flow filter substrate portion showing alternating blocked and open passages (cells). Blocked or blocked ends 100 alternate with open passages 101, with the opposite ends being open and blocked, respectively. The filter has an inlet end 102 and an outlet end 103. Arrows across the porous cell walls 104 represent exhaust gas flow entering the open cell ends, diffusing through the porous cell walls 104, and exiting the open outlet cell ends. The blocked ends 100 impede gas flow and promote diffusion through the cell walls. Each cell wall has an inlet side 104a and an outlet side 104b. The passages are enclosed by the cell walls.

[0146] The wall flow filter article substrate is approximately 50 cm 3 , about 100cm 3 , about 200cm 3 , about 300cm 3 , about 400cm 3 , about 500cm 3 , about 600cm 3 , about 700cm 3 So, about 800cm 3 , about 900cm 3 , or about 1000 cm 3 ~Approx. 1500cm 3 , about 2000cm 3 , about 2500cm 3 , about 3000cm3 , about 3500cm 3 , about 4000cm 3 , about 4500cm 3 , or about 5000 cm 3 The wall-flow filter substrate typically has a wall thickness of from about 50 microns to about 2000 microns, for example, from about 50 microns to about 450 microns, or from about 150 microns to about 400 microns.

[0147] The walls of the wall-flow filter are porous and generally have a wall porosity of at least about 50% or at least about 60% and an average pore size of at least about 5 microns prior to the placement of the functional coating. For example, the wall-flow filter article substrate in some embodiments will have a porosity of ≧50%, ≧60%, ≧65%, or ≧70%. For example, the wall-flow filter article substrate has a wall porosity of about 50%, about 60%, about 65% or about 70% to about 75%, about 80% or about 85% and an average pore size of about 5 microns, about 10, about 20, about 30, about 40 or about 50 microns to about 60 microns, about 70, about 80, about 90 or about 100 microns prior to the placement of the catalytic coating. The terms "wall porosity" and "substrate porosity" are synonymous and interchangeable. Porosity is the ratio of the void volume divided by the total volume of the substrate. Pore ​​size may be determined according to the ISO 15901-2 (static volume) procedure for nitrogen pore size analysis. Nitrogen pore size may be determined on a Micromeritics TRISTAR 3000 series instrument. Nitrogen pore size may be determined using the BJH (Barrett-Joyner-Halenda) calculation and a desorption point of 33. Useful wall-flow filters have high porosity, allowing high loading of catalyst composition without excessive back pressure during operation.

[0148] In some embodiments, a catalyst article of the present disclosure includes a substrate having an inlet end and an outlet end defining an overall length, and a first washcoat comprising the LT-CO oxidation catalyst composition disclosed herein disposed on at least a portion thereof. In some embodiments, the catalyst article further includes a diesel oxidation catalyst (DOC) composition comprising a second washcoat comprising one or more zeolites, wherein the one or more zeolites are impregnated with a second PGM component, and a third washcoat comprising one or more zeolites and a second refractory metal oxide, wherein one or more of the one or more zeolites or the second refractory metal oxide or both are impregnated with the third PGM component.

[0149] In another aspect, a catalyst article for mitigating exhaust gas emissions from a lean-burn engine is provided, the catalyst article comprising: a substrate; a first washcoat comprising an oxygen storage component (OSC), a first platinum group metal (PGM) component, a first promoter metal, and optionally a first refractory metal oxide, where the OSC is impregnated with the first PGM component and the first promoter metal; a second washcoat comprising a first zeolite, where the first zeolite is impregnated with the second PGM component; and a third washcoat comprising a second zeolite and a second refractory metal oxide, where the second zeolite or the second refractory metal oxide, or both, are impregnated with the third PGM component and optionally the promoter metal, wherein the catalyst article is effective to oxidize carbon monoxide and hydrocarbons under cold start conditions.

[0150] As mentioned above, in some embodiments, the catalyst article includes a first, second, and third washcoat, each of which may include or contain one or more zeolites (e.g., a second zeolite and a third zeolite). In each case, the second and third zeolites are selected from the group of zeolites previously disclosed herein. In these first, second, and third washcoats, the second and third zeolites are each independently selected from one or more zeolites, each time, as described herein. In some embodiments, the one or more zeolites are a single zeolite. In some embodiments, the one or more zeolites include a mixture of more than one zeolite, for example, two zeolites or three zeolites in a mixture. In some embodiments, the first washcoat further includes a small pore zeolite, a large pore zeolite, or a combination thereof, as described herein above. In some embodiments, the second zeolite and the third zeolite each comprise a hydrothermally stable zeolite in the form of a 6-12 membered ring structure, in some embodiments, the second zeolite and the third zeolite each are independently selected from the group consisting of ZSM-5, beta, mordenite, Y zeolite, chabazite, ferrierite, and combinations thereof.

[0151] In some embodiments, the second zeolite is impregnated with a second PGM component that is distinct from the first PGM component referred to above, but may also include, for example, Pt, Pd, or mixtures thereof. In some embodiments, the third zeolite in the mixture is impregnated with a third PGM component that is distinct from the first and second PGM components referred to herein, but may also include, for example, Pt, Pd, or mixtures thereof.

[0152] As mentioned above, in some embodiments, the catalyst article includes a first, second, and third washcoat, each of which may include or comprise a refractory metal oxide. In these washcoats, the second refractory metal oxide is independently selected from those refractory metal oxides described herein for the first refractory metal oxide. The second refractory metal oxide is typically selected from the group consisting of alumina, zirconia, silica, titania, ceria, e.g., bulk ceria, manganese oxide, zirconia-alumina, ceria-zirconia, ceria-alumina, lanthana-alumina, baria-alumina, silica, silica-alumina, and combinations thereof. Each of the first and second refractory metal oxides may be the same or different (i.e., may be independently selected for each component). In some embodiments, the first and second refractory metal oxides are the same. In some embodiments, the first and second refractory metal oxides are different. In some embodiments, the second refractory metal oxide is impregnated with a second promoter metal, the second promoter metal being as described herein above with respect to the LT-CO oxidation catalyst composition.

[0153] Further, in these second and third washcoats, the second PGM component and the third PGM component are each independently selected from those described herein for the first PGM component. Each of the first, second, and third PGM components may be the same or different (i.e., selected for each component individually). In some embodiments, the first, second, and third PGM components are the same. In some embodiments, the first, second, and third PGM components are different. In some embodiments, the first and second PGM components are the same. In some embodiments, the first and third PGM components are the same. In some embodiments, the second and third PGM components are the same. In certain embodiments, the first, second, and third PGM components all include Pt, Pd, or a combination thereof. In certain embodiments, the second PGM component includes Pt, Pd, or a combination thereof. In certain embodiments, the second PGM component comprises Pt and Pd, for example, but not limited to, Pt and Pd present in a weight ratio of Pt:Pd of about 1:10 to about 10:1, In certain embodiments, the third PGM component comprises Pt, Pd, or a combination thereof.

[0154] In some embodiments, the first washcoat further comprises a small pore zeolite, a large pore zeolite, an alkaline earth metal component, or a combination thereof, wherein the small pore zeolite, the large pore zeolite, and the alkaline earth metal component are each as previously described herein.

[0155] As previously described herein, the configuration of the washcoat can vary. All formats of disposing the washcoat on the substrate are contemplated herein, including various approaches of layering, zoning, and combinations thereof.

[0156] In some embodiments, the LT-CO oxidation catalyst article of the present disclosure is effective for oxidizing carbon monoxide and hydrocarbons under cold start conditions, hi some embodiments, the cold start conditions include an exhaust gas temperature of less than about 150° C.

[0157] In some embodiments, the LT-CO oxidation catalyst article of the present disclosure further comprises an HC trapping composition. In some embodiments, the LT-CO oxidation catalyst article is a low temperature NO x In some embodiments, the LT-CO oxidation catalyst article further comprises a sorbent (LT-NA) composition. x It further comprises a capture (LNT) composition.

[0158] Preparation of the Catalyst Composition The disclosed LT-CO oxidation catalyst composition may be prepared in some embodiments by incipient wetness impregnation. Incipient wetness impregnation technique, also called capillary impregnation or dry impregnation, is commonly used for the synthesis of heterogeneous materials, i.e., catalysts. Typically, metal precursors are dissolved in an aqueous or organic solution, and then the metal-containing solution is added to a catalyst support (e.g., a refractory metal oxide) that contains the same pore volume as the volume of the added solution. Capillary action draws the solution into the pores of the support. The solution added beyond the pore volume of the support changes the solution transport from a capillary action process to a much slower diffusion process. The catalyst can then be dried and calcined to remove volatile components in the solution and deposit the metal on the surface of the catalyst support. The maximum loading is limited by the solubility of the precursor in the solution. The concentration profile of the impregnated material depends on the mass transfer conditions in the pores during impregnation and drying. Those skilled in the art will recognize other methods for loading the PGM and promoter metal components onto the support of the present composition, such as adsorption, ion exchange, precipitation, and the like.

[0159] For example, PGMs may be impregnated into zeolites or refractory metal oxides in the preparation of the components of the LT-CO oxidation catalyst composition or article disclosed herein. In general, an aqueous solution of a soluble compound or complex of a platinum group metal is used to impregnate the support material (e.g., zeolites or refractory metal oxides). Non-limiting examples of suitable compounds include palladium nitrate, tetraamminepalladium nitrate, tetraammineplatinum acetate, and platinum nitrate. Additionally, at least a portion of the catalytically active metals may be included in the zeolite synthesis process, whereby the prepared colloid contains a structure directing agent, a silica source, an alumina source, and a metal ion source. In some embodiments, palladium and / or platinum, as well as other metal salts, may be mixed together and the mixture may be impregnated into the zeolite. The metals used in the salts may include, but are not limited to, metals selected from the group consisting of copper, iron, manganese, magnesium, cobalt, nickel, platinum, ruthenium, rhodium, and combinations thereof.

[0160] During the calcination step, or at least during the initial stages of use of the composite, such compounds are converted to the catalytically active form of the metal or its compounds. A suitable method of preparing the oxidation catalyst composition is to prepare a mixture of a solution of the desired platinum group metal compound (e.g., platinum group compound and / or palladium compound) with at least one support, such as a finely divided high surface area refractory metal oxide support, which is sufficiently dry to absorb substantially all of the solution, thereby forming a wet solid that is later combined with water to form a coatable slurry, e.g., gamma alumina. In one or more embodiments, the slurry is acidic, e.g., having a pH of about 2 to less than about 7. The pH of the slurry may be lowered by adding an appropriate amount of an inorganic or organic acid to the slurry. Considering the compatibility of the acid with the raw materials, a combination of both may be used. Inorganic acids include, but are not limited to, nitric acid. Organic acids include, but are not limited to, acetic acid, propionic acid, oxalic acid, malonic acid, succinic acid, glutamic acid, fatty acid, maleic acid, fumaric acid, phthalic acid, tartaric acid, citric acid, and the like.

[0161] Coating Composition To produce a catalytic article, a substrate disclosed herein is coated with a catalytic composition. The coating is a "catalytic coating composition" or "catalytic coating." The terms "catalytic composition" and "catalytic coating composition" are synonymous. The catalytic compositions described herein may include one or more supports or "carriers," such as refractory inorganic solid oxide porous powders that further include functionally active species.

[0162] The catalyst composition may be prepared by mixing a binder, such as ZrO, which is derived from a suitable precursor, such as zirconyl acetate or any other suitable zirconium precursor, such as zirconyl nitrate. 2The binders may be prepared using a zirconyl acetate binder. Zirconyl acetate binders, for example, provide a coating that remains homogeneous and intact after thermal aging when the catalyst is exposed to high temperatures of at least about 600° C., such as about 800° C. or higher, and a water vapor environment of about 5% or higher. Other potentially suitable binders include, but are not limited to, alumina and silica. Alumina binders include aluminum oxide, aluminum hydroxide, and aluminum oxyhydroxide. Aluminum salts and colloidal forms of alumina may also be used. Silica binders include SiO , including silicates and colloidal silica. 2 The binder composition may include any combination of zirconia, alumina, and silica. Other exemplary binders include boehmite, gamma alumina, or delta / theta alumina, as well as silica sol. When present, the binder is typically used in an amount of about 1-5 wt.% total washcoat loading. Alternatively, the binder may be zirconia- or silica-based, e.g., zirconium acetate, zirconia sol, or silica sol. When present, the alumina binder is typically used in an amount of about 0.05 g / in 3 ~Approx. 1g / in 3 is used in amounts of

[0163] coating The substrate is coated with the catalyst composition to form a catalyst article. The catalyst coating may include one or more thin, adherent coating layers disposed on and attached to at least a portion of the substrate. In some embodiments, the catalyst article may include the use of one or more catalyst layers, and combinations of one or more catalyst layers. The catalyst material may be present only on the inlet side, only on the outlet side, on both the inlet and outlet sides of the substrate wall, or the wall itself may be entirely or partially composed of the catalyst material. The catalyst coating may be on the substrate wall surface and / or within the pores of the substrate wall, i.e., "in" and / or "on" the substrate wall. Thus, the phrase "catalyst coating disposed on the substrate" means on any surface, e.g., on the wall surface and / or on the pore surface. The catalyst coating layer may include individual functional components, i.e., the LT-CO oxidation catalyst composition and the DOC catalyst composition, respectively, as described herein.

[0164] In some embodiments, the catalyst coating layer comprises a LT-CO oxidation catalyst composition described herein and a low temperature NO x The adsorbent may include a LT-NA composition. Any suitable LT-NA composition known in the art may be used, such as a LT-NA composition comprising a platinum group metal (PGM) and a molecular sieve. Suitable LT-NA compositions are disclosed, for example, in International Patent Application Publication No. WO2018 / 073750 for Li, the disclosure of which is incorporated herein in its entirety for teaching suitable LT-NA compositions.

[0165] In some embodiments, the catalyst coating layer comprises a LT-CO oxidation catalyst composition described herein and a lean NOx oxidation catalyst composition. x The scavenging (LNT) composition may include a scavenging (LNT) composition. Any suitable LNT composition known in the art may be used, such as an LNT composition including an alkaline earth component and a platinum group component. Suitable LNT compositions are disclosed, for example, in International Patent Application Publication No. WO2018 / 073750 for Li, the disclosure of which is incorporated herein in its entirety for teaching suitable LNT compositions.

[0166] The catalyst composition may typically be applied in the form of a washcoat containing a support having catalytically active species thereon (e.g., as described herein above). The washcoat is formed by preparing a slurry containing the catalyst composition at a particular solids content (e.g., about 10 to about 60 wt%) in a liquid vehicle, which is then applied to a substrate, dried and calcined to provide a coating layer. If multiple coating layers are applied, the substrate is dried and calcined after each layer is applied and / or after multiple layers as desired are applied. In one or more embodiments, the catalyst material is applied to the substrate as a washcoat. A binder may also be used as described above.

[0167] The above catalyst compositions are generally mixed with water independently to form a slurry for coating a catalyst substrate, such as a honeycomb-type substrate. In addition to the catalyst particles, the slurry may optionally contain binders (e.g., alumina, silica), water-soluble or water-dispersible stabilizers, promoters, associative thickeners, and / or surfactants (anionic, cationic, nonionic, or amphoteric surfactants). The typical pH range of the slurry is from about 3 to about 6. Acidic or basic species may be added to the slurry to thereby adjust the pH. For example, in some embodiments, the pH of the slurry is adjusted by the addition of aqueous ammonium hydroxide or nitric acid.

[0168] The slurry can be milled to improve particle mixing and formation of a homogenous material. Milling can be accomplished in a ball mill, continuous mill, or other similar equipment, and the solids content of the slurry can be, for example, about 20-60% by weight, more specifically, about 20-40% by weight. In one embodiment, the slurry after milling has a D of about 10 to about 40 microns, preferably 10 to about 30 microns, and more preferably about 10 to about 15 microns. 90 It is characterized by its particle size.

[0169] The slurry is then coated onto a catalytic substrate using any washcoat technique known in the art. In one embodiment, the catalytic substrate is dipped or otherwise coated with the slurry one or more times. The coated substrate is then dried at an elevated temperature (e.g., 100-150° C.) for a period of time (e.g., 10 minutes to 3 hours) and then calcined, for example, by heating at 400-600° C. for typically about 10 minutes to about 3 hours. After drying and calcination, the final washcoat coating layer can be considered to be substantially free of solvent.

[0170] After calcination, the catalyst loading achieved by the above washcoat technique can be determined by calculating the difference between the coated and uncoated weights of the substrate. As will be apparent to one skilled in the art, the catalyst loading can be modified by altering the rheology of the slurry. Furthermore, the coating / drying / calcining process to produce a washcoat can be repeated as necessary to build up the coating to a desired loading level or thickness, i.e., to apply more than one washcoat.

[0171] Washcoats can be applied such that the different coating layers are in direct contact with the substrate. Alternatively, one or more "undercoats" may be present such that the catalyst or adsorbent coating layer or at least a portion of the coating layer is not in direct contact with the substrate (rather, in contact with an undercoat). One or more "overcoats" may be present such that at least a portion of the coating layer is not directly exposed to the gas stream or atmosphere (rather, in contact with an overcoat).

[0172] The different coating layers may be in direct contact with each other without an "intermediate" overlapping zone. Alternatively, the different coating layers may not be in direct contact with a "gap" between the two zones. In the case of an "undercoat" or "overcoat", the gap between the different layers is called an "intermediate layer". An undercoat is a layer "below" a coating layer, an overcoat is a layer "on" a coating layer, and an intermediate layer is a layer "between" two coating layers. Intermediate layers, undercoats, and overcoats may contain one or more functional compositions or may be free of functional compositions.

[0173] The catalytic coating may include more than one thin attached layer, layers attached to each other, and coatings attached to the substrate. The entire coating includes individual "coating layers". The catalytic coating may advantageously be "zoned" and may include zoned catalytic layers. This may be expressed as "laterally zoned". For example, a layer may extend from the inlet end toward the outlet end and may extend over about 10%, about 20%, about 30%, about 40%, about 50%, about 60%, about 70%, about 80%, or about 90% of the substrate length. Another layer may extend from the outlet end toward the inlet end and may extend over about 10%, about 20%, about 30%, about 40%, about 50%, about 60%, about 70%, about 80%, or about 90% of the substrate length. The different coating layers may be adjacent to each other and not overlay each other. Alternatively, different layers may overlay portions of each other to provide a third, "intermediate" zone, which may extend, for example, over about 5% to about 80% of the length of the substrate, such as about 5%, about 10%, about 20%, about 30%, about 40%, about 50%, about 60%, or about 70% of the length of the substrate.

[0174] The different layers may each extend along the entire length of the substrate, or each extend along a portion of the substrate's length and partially or totally overlay or underlay one another. The different layers may each extend from either the inlet end or the outlet end.

[0175] Different catalyst compositions may be present in each separate coating layer. For example, one coating layer may include an oxidation catalyst composition without any selective sorbent composition, and a second layer may include one or more selective sorbent compositions (or consist entirely of one or more selective sorbent compositions). Thus, descriptions relating to different layers may correspond to any of these layers. A catalyst coating may include one, two, or three or more coating layers. One or more coating layers together include a catalyst composition.

[0176] Zones are defined by the relationship of coating layers when present on the catalyst article in certain embodiments of the present disclosure. There are several possible zone configurations with respect to different coating layers. For example, there may be an upstream zone and a downstream zone; there may be an upstream zone, an intermediate zone, and a downstream zone; there may be four different zones; etc. If two layers are adjacent and do not overlap, there will be an upstream zone and a downstream zone. If two layers overlap to some extent, there will be an upstream, downstream, and intermediate zone. For example, if a coating layer extends over the entire length of the substrate and a different coating layer extends a length from the outlet end and overlays a portion of the first coating layer, there will be an upstream and downstream zone. The present catalyst coating may include more than one identical layer.

[0177] 3A, 3B, and 3C show some possible coating layer configurations with two coating layers. A monolith wall-flow filter substrate wall 200 is shown with coating layers 201 and 202 disposed thereon. This is a simplified view, and in the case of a porous wall-flow substrate, the pores and coatings attached to the pore walls are not shown, and plugged ends are not shown. In FIG. 3A, coating layer 201 extends about 50% of the substrate length from the inlet toward the outlet. Coating layer 202 extends about 50% of the substrate length from the outlet toward the inlet, the coating layers being adjacent to each other, providing an inlet upstream zone 203 and an outlet downstream zone 204. In FIG. 3B, coating layer 202 extends about 50% of the substrate length from the outlet, and layer 201 extends more than 50% of the length from the inlet and overlays a portion of layer 202, providing an upstream zone 203, an intermediate zone 205, and a downstream zone 204. In Figure 3C, coating layers 201 and 202 each extend the entire length of the substrate such that layer 201 overlays layer 202. The substrate of Figure 3C does not contain a zoned coating configuration. Figures 3A, 3B, and 3C may be useful for illustrating coating compositions on wall-through substrates. Figures 3A, 3B, and 3C may also be useful for illustrating coating compositions on flow-through substrates, as described herein below. Such coating layer configurations are not limiting.

[0178] 4A-4G show an embodiment of a LT-CO oxidation catalyst article 20, in which a LT-CO oxidation catalyst composition is coated according to one or more embodiments of the present disclosure. The first washcoat comprises the LT-CO oxidation catalyst composition of the present disclosure. In some embodiments, the article further comprises a diesel oxidation catalyst (DOC) composition, the DOC composition comprising a second washcoat comprising a second refractory metal oxide, the second refractory metal oxide being impregnated with a second PGM component, and a third washcoat comprising one or more zeolites and a third refractory metal oxide, the third PGM component being impregnated with one or more of the one or more zeolites. In some embodiments, the article further comprises a LT-NA composition, the LT-NA composition comprising the second washcoat. In some embodiments, the article further comprises a LNT composition, the LNT composition comprising the second washcoat.

[0179] Referring to FIG. 4A, which illustrates one non-limiting embodiment, a third washcoat is coated on a substrate, then a second washcoat is coated on (or above) the third washcoat, and then a first washcoat is coated on (or above) the second washcoat. Referring to FIG. 4B, in other embodiments, a first washcoat is coated on a substrate, then a second washcoat is coated on (or above) the second washcoat, and then a third washcoat is coated on (or above) the second washcoat. In some embodiments, a first washcoat is coated on a substrate, a third washcoat is coated on (or above) the first washcoat, and a second washcoat is coated on (or above) the third washcoat.

[0180] In yet another embodiment, the washcoats are coated on the substrate such that one washcoat is upstream and the other washcoat is downstream. With reference to FIG. 4C, for example, the third washcoat is coated on the substrate, and then the second and first washcoats are coated above the third washcoat. With reference to FIG. 4D, the second washcoat is coated on the substrate, and then the first and third washcoats are coated above the second washcoat. With reference to FIG. 4E, in a further embodiment, the first and third washcoats are coated on the substrate, and then the second washcoat is coated above the first and third washcoats. With reference to FIG. 4F, in a further embodiment, the first and second washcoats are coated on the substrate, and then the third washcoat is coated above the first and second washcoats. 4G, the second and third washcoats are coated onto a substrate, and then the first washcoat is coated over (or above) the second and third washcoats. One skilled in the art will appreciate that any arrangement of the three washcoat layers / components is possible, in either a layered or zoned structure.

[0181] The loading of the catalytic coating on the substrate depends on substrate properties such as porosity and wall thickness. Typically, wall-flow filter catalyst loadings will be lower than catalyst loadings on flow-through substrates. Catalytic wall-flow filters are disclosed, for example, in U.S. Pat. No. 7,229,597, which is incorporated herein by reference in its entirety. The oxidation catalyst composition and / or DOC catalyst composition generally have a loading of, for example, about 0.3 to 5.5 g / in based on the substrate. 3 , or about 0.4 g / in 3 , about 0.5g / in 3 , about 0.6g / in 3 , about 0.7g / in 3 , about 0.8g / in 3 , about 0.9g / in 3, or about 1.0 g / in 3 ~ approx. 1.5g / in 3 , about 2.0g / in 3 , about 2.5g / in 3 , approx. 3.0g / in 3 , about 3.5g / in 3 , approx. 4.0g / in 3 , about 4.5g / in 3 , approx. 5.0g / in 3 , or about 5.5 g / in 3 In some embodiments, the first washcoat is present on the substrate at a concentration of at least about 0.5 g / in 3 The concentration of the catalyst composition or any other component on the substrate refers to the concentration per any one three-dimensional cross-section or zone, for example, either the cross-section of the substrate or the entire substrate.

[0182] Exhaust Gas Treatment Systems In another aspect, there is provided an exhaust gas treatment system for treating a lean-burn engine exhaust gas stream comprising hydrocarbons, carbon monoxide, nitrogen oxides, and particulate matter, the system including: a lean-burn engine generating an exhaust gas stream; an exhaust conduit in fluid communication with the lean-burn engine via an exhaust manifold; and a catalytic article of the present disclosure positioned downstream of the lean-burn engine and in fluid communication with the exhaust gas stream.

[0183] The engine may be, for example, a diesel engine operating under combustion conditions with more air than is required for stoichiometric combustion, i.e., lean conditions. In other embodiments, the engine may be an engine associated with a stationary source, such as a generator or pumping station. In some embodiments, the emissions treatment system further includes one or more additional catalytic components. The relative placement of the various catalytic components present in the emissions treatment system may vary.

[0184] In the present exhaust gas treatment systems and methods, the exhaust gas stream is received into the article or treatment system by entering at an upstream end and exiting at a downstream end. The inlet end of the substrate or article is synonymous with the "upstream" end or "front" end. The outlet end is synonymous with the "downstream" end or "rear" end. The treatment system is generally downstream of and in fluid communication with the internal combustion engine.

[0185] The systems disclosed herein include a catalyst article as disclosed herein and may further include one or more additional components. In some embodiments, the one or more additional components include a diesel oxidation catalyst (DOC), a soot filter (which may be catalyzed or uncatalyzed), a selective catalytic reduction (SCR) catalyst, a urea injection component, an ammonia oxidation catalyst (AMOx), a low temperature NOx filter, ... x Absorbent (LT-NA), Lean NO x capture (LNT), and combinations thereof.

[0186] The catalyst article may be located, for example, downstream of the DOC catalyst article. In some embodiments, the catalyst article includes a DOC catalyst composition (described above) such that a single substrate supports both the LT-CO oxidation catalyst composition and the DOC composition, thereby combining these functions in a single article (LT-CO / DOC) as disclosed herein. In some embodiments, the catalyst article further includes a LT-NA or LNT composition (described herein above) such that a single substrate supports both the LT-CO oxidation catalyst composition and the LT-NA or LNT composition, thereby combining these functions in a single article (LT-CO / LT-NA or LT-CO / LNT) as disclosed herein.

[0187] The exhaust gas treatment system of the present disclosure may further include an SCR catalyst component. In some embodiments, the LT-CO oxidation catalyst article is located upstream of the SCR catalyst component and / or the soot filter. The SCR catalyst component may be located upstream or downstream of the oxidation catalyst article and / or the soot filter. SCR catalyst components suitable for use in emissions treatment systems are capable of oxidizing NO at temperatures as high as 650° C. x In addition, the SCR catalyst components can effectively catalyze the reduction of exhaust components, even under low load conditions that are typically associated with lower exhaust temperatures, resulting in reduced NO x Preferably, the SCR catalyst component is active for the reduction of NO depending on the amount of reductant added to the system. x (e.g., NO) At least 50% of the component is N 2 Another desirable property of the SCR catalyst component is that it can be converted to O 2 and any excess NH 3 It catalyzes the reaction with N 2 As a result, NH 3 The primary objective of the present invention is to prevent the release of sulfur dioxide into the atmosphere. Useful SCR catalyst components for use in emissions treatment systems should also be heat resistant to temperatures in excess of 650° C., which may occur during regeneration of catalyzed soot filters. Suitable SCR catalyst components are described, for example, in U.S. Patent Nos. 4,961,917 and 5,516,497, each of which is incorporated herein by reference in its entirety.

[0188] Certain illustrated exhaust gas treatment systems may be more readily understood by reference to FIGS. 5A-5D, which show schematic diagrams of non-limiting exhaust gas treatment systems according to embodiments of the present disclosure. Those skilled in the art will recognize that it may be desirable to arrange the relative positions of each item in an order different from that illustrated herein. Such alternative orderings are contemplated by the present disclosure. With reference to FIG. 5A, an exhaust gas treatment system 320 is provided in which an exhaust gas stream containing gaseous pollutants (e.g., unburned hydrocarbons, carbon monoxide, and NO) and particulate matter is conveyed from an engine 321 via line 322 to a low-temperature CO oxidation / diesel oxidation (LT-CO / DOC) catalyst article 323. In the LT-CO / DOC 323, a majority of the unburned gaseous and non-volatile hydrocarbons and carbon monoxide are combusted to form carbon dioxide and water. The exhaust stream is then conveyed via line 324 to a LT-NA catalyst article 325 for adsorption and / or storage of NO. The treated exhaust gas stream 326 is then delivered to the CSF 327, which traps particulate matter present in the exhaust gas stream. After removal of particulate matter, the exhaust gas stream is delivered via line 328 to a downstream SCR catalyst component 329, which provides treatment and / or conversion of NO. The exhaust gas is delivered to the CSF 327 via line 328 to a downstream SCR catalyst component 329, which provides treatment and / or conversion of NO. The catalyst composition is added to the exhaust gas to remove NO in the exhaust gas at a predetermined temperature in the exhaust gas before it exits the system. x The SCR catalyst component 329 passes through the SCR catalyst component 329 at a flow rate that allows sufficient time for the level of (in combination with the reductant) to decrease.

[0189] Another embodiment of an exhaust gas treatment system of the present invention is shown in Figure 5B, which shows a schematic diagram of an exhaust gas treatment system 330 according to the present disclosure. With reference to Figure 5B, an exhaust gas stream is conveyed from an engine 331 via line 332 to a low temperature NOx sorbent (LT-NA) catalyst article 333. The exhaust stream is then conveyed via line 334 to a LT-CO / DOC 335 and further via line 336 to a CSF 337. The treated exhaust gas stream 338 is conveyed to an SCR catalyst component 339 before being released into the atmosphere.

[0190] Another embodiment of an exhaust gas treatment system of the present disclosure is shown in Figure 5C, which shows a schematic diagram of an exhaust gas treatment system 340. With reference to Figure 5C, an exhaust gas stream is conveyed from an engine 341 through line 342 to a LT-CO / DOC 343 and further conveyed via exhaust gas stream 344 to a LT-NA 345. The exhaust stream is then conveyed via line 346 to an SCR catalyst component 347 and further conveyed via line 348 to a CSF 349. The treated exhaust gas stream 338 is conveyed to the SCR catalyst component 339 before exiting the system.

[0191] Another embodiment of an exhaust gas treatment system of the present invention is shown in Figure 5D, which shows a schematic diagram of an exhaust gas treatment system 350 according to the present disclosure. With reference to Figure 5D, exhaust gas stream is conveyed from engine 351 via line 352 to LT-NA catalyst article 353 and further via gas exhaust line 354 to LT-CO / DOC 355. Exhaust gas line 356 is conveyed to SCR catalyst component 357 and then exhaust stream 358 is conveyed to CSF ​​359 before exiting the system.

[0192] Another embodiment of an exhaust gas treatment system of the present invention is shown in Figure 5E, which shows a schematic diagram of an exhaust gas treatment system 360 according to the present disclosure. With reference to Figure 5E, an exhaust gas stream is conveyed from an engine 361 via line 362 to a LT-CO / LT-NA catalyst article 363 and further via gas exhaust line 364 to a DOC article 365. Exhaust gas line 366 conveys to an SCR catalyst article 367 and then exhaust stream 368 is conveyed to a CSF 369 before exiting the system.

[0193] Another embodiment of an exhaust gas treatment system of the present invention is shown in Figure 5F, which shows a schematic diagram of an exhaust gas treatment system 370 according to the present disclosure. With reference to Figure 5F, an exhaust gas stream is conveyed from an engine 371 via line 372 to a LT-CO / LNT catalyst article 373 and further via gas exhaust line 374 to a DOC article 375. Exhaust gas line 376 is conveyed to an SCR catalyst article 377 and then exhaust stream 378 is conveyed to a CSF 379 before exiting the system.

[0194] NH released from the SCR catalyst components after any of the exemplary exhaust gas treatment systems shown in FIGS. 5A-5F. 3 This NH 3 N 2 A selective ammonia oxidation catalyst (AMOx) may be provided for selectively oxidizing

[0195] Method for treating an exhaust gas stream Generally, the hydrocarbons (HC) and carbon monoxide (CO) present in the exhaust gas stream of any engine can be converted to carbon dioxide and water. 6 Typically, the hydrocarbons present in engine exhaust streams are of the C type, such as methane, although other hydrocarbons (>100%) can also be detected. 1 ~C 6 Contains hydrocarbons (i.e., lower hydrocarbons).

[0196] Aspects of the present disclosure are directed to a method for treating a lean-burn engine exhaust gas stream comprising contacting the exhaust gas stream with a catalytic article of the present disclosure or an emissions treatment system of the present disclosure.

[0197] In some embodiments, the method includes contacting a gas stream with a catalytic article or exhaust gas treatment system of the present disclosure for a time and at a temperature sufficient to reduce the CO and HC levels in the gas stream. In some embodiments, the level of hydrocarbons, such as methane, present in the exhaust gas stream is reduced by at least about 30%, or at least about 50%, or at least about 70%, or at least about 75%, or at least about 80%, or at least about 90%, or at least about 95%, compared to the level of hydrocarbons present in the exhaust gas stream prior to contact with the catalytic composition. In some embodiments, the temperature required to convert hydrocarbons, such as methane, using the catalytic composition described herein ranges from about 300° C. to about 650° C., from about 400° C. to about 600° C., or from about 450° C. to about 550° C.

[0198] In some embodiments, the catalyst composition comprising the catalyst article is new, while in other embodiments, the catalyst composition is depleted (i.e., "aged").

[0199] In some embodiments, the reduction in HC and / or CO levels is measured in terms of conversion efficiency. In some embodiments, the conversion efficiency is measured based on the light-off temperature (i.e., T 50 ) The light-off temperature is the temperature at which the catalyst composition can convert 50% of the hydrocarbons or carbon monoxide to carbon dioxide and water. Typically, the lower the light-off temperature measured for a given catalyst composition, the more efficient the catalyst composition is at carrying out catalytic reactions, such as hydrocarbon conversion.

[0200] The present articles, systems, and methods are suitable for treating exhaust gas streams from mobile emission sources such as trucks and automobiles. The present articles, systems, and methods are also suitable for treating exhaust streams from stationary sources such as power plants.

[0201] It will be readily apparent to those skilled in the relevant art that suitable modifications and adaptations to the compositions, methods, and applications described herein may be made without departing from the scope of any embodiment or aspect thereof. The compositions and methods provided are exemplary and are not intended to limit the scope of the claimed embodiments. All of the various embodiments, aspects, and options disclosed herein may be combined in all variations. The scope of the compositions, formulations, methods, and processes described herein includes all actual or potential combinations of the embodiments, aspects, options, examples, and preferences herein. All patents and publications cited herein are incorporated by reference for their specific teachings, as described, unless other specific statements of incorporation are specifically provided. EXAMPLES

[0202] The present invention is more particularly illustrated by the following examples, which are presented to illustrate the invention and should not be construed as limiting the invention. Unless otherwise specified, all parts and percentages are by weight and all weight percentages are expressed on a dry basis, i.e., water content is excluded unless otherwise indicated.

[0203] Preparation of the catalytic article Example 1: Reference Article (2% Pd on Ceria) Preparation of catalyst powder Palladium nitrate (29 grams) was diluted with 75 grams of deionized water. This solution was added to 300 grams of ceria. The mixture was homogenized and the resulting powder was dried at 120° C. for 4 hours and calcined at 500° C. for 1 hour.

[0204] Preparation of catalytic washcoat slurry 200 grams of 2% Pd / ceria powder was added to 240 grams of deionized water. The slurry was thoroughly mixed with a homogenizer and milled to a particle size of about 13. Alumina binder was added and the combination was thoroughly mixed.

[0205] Preparation of catalyst core samples Two 1 inch diameter x 3 inch long ceramic substrate cores with a cell density of 400 cells per square inch were fabricated using Pd / CeO 2 / Al 2 O 3 The cores were immersed in the slurry. Excess slurry was blown off using an air gun. The coated cores were dried by a hot air blower at 200°C for 5-10 minutes, and then calcined in an oven at 500°C for 1 hour.

[0206] Preparation of core samples for testing One of the core samples was subjected to an accelerated aging protocol to simulate field use in a vehicle. The aging conditions were set at 800°C for 16 hours in an atmosphere of 10% water, 10% oxygen, and 80% nitrogen. The second core sample was tested without aging.

[0207] Example 2: Article of the invention (Pd / Sn / Ce) Preparation of LT-CO catalyst powder (2% Pd on 1% Sn / 99% ceria) Sn acetate (5 grams) was diluted with 25 grams of acetic acid and 50 grams of deionized water. The solution was mixed for 3 minutes to homogenize the liquid. It became a beige colloidal solution. Ceria (251 grams) was added to the solution and mixed for 3 minutes. The resulting powder was grayish brown in color. The powder was dried at 120° C. for 4 hours and calcined at 500° C. for 1 hour to provide 1% Sn on ceria.

[0208] Pd nitrate (20 grams) was diluted with 40 grams of deionized water. 1% Sn on ceria powder (200 grams) was added to the Pd solution and mixed for 3 minutes to homogenize. The powder turned golden in color. The powder was dried at 120° C. for 4 hours and calcined at 500° C. for 1 hour to provide 2% Pd on a 1% Sn / 99% ceria support.

[0209] Preparation of LT-CO catalyst washcoat slurry To 210 grams of deionized water, 177 grams of 2% Pd on 1% Sn / 99% ceria powder was added. The slurry was thoroughly mixed and then milled until the resulting slurry had a particle size of about 7 microns. Finally, the alumina binder was added and mixed thoroughly.

[0210] Preparation of LT-CO catalyst core samples Two 1 inch diameter by 3 inch long ceramic substrate cores with a cell density of 400 cells per square inch were dipped into the Pd / Sn / Ce washcoat slurry. An air gun was used to blow off excess slurry. The coated cores were dried with a hot air blower at 200°C for 5-10 minutes and then fired in an oven at 500°C for 1 hour.

[0211] Preparation of LT-CO core samples for testing One of the core samples was subjected to an accelerated aging protocol to simulate field use in a vehicle. The aging conditions were set at 800°C for 16 hours in an atmosphere of 10% water, 10% oxygen, and 80% nitrogen. The second core sample was tested without aging.

[0212] Example 3: LT-CO catalyst article of the present invention (Pt / Sn / Ce) Following the procedure of Example 2, but substituting Pt for Pd, samples containing 2% Pt on ceria containing 1%-4% Sn were prepared.

[0213] Catalytic Article Evaluation Example 4: Reactor Testing of Core Samples (Steady State Light-Off) Figure 6 shows the benefit of Sn addition to ceria in CO light-off for both fresh and aged samples using Pd. Figure 7 shows the benefit of Sn addition to ceria in HC light-off for both fresh and aged samples using Pd. Activity measurements of the light-off performance were performed in a reactor with the following feed gas composition: CO = 1500 ppm, NO = 100 ppm, H 2 O = 10%, CO 2 =4.6%, O 2 =14%, C 3 H 6 = 40 ppm, CH 4 = 30 ppm, liquid HC (36% toluene / 64% decane (molar basis)) = 294 ppm C 1 .

[0214] Example 5: Powder Screening Preparation of powder samples A 6×8=48 tray powder reactor was used for the support screening study. The following procedure was used: 1. Impregnating the support with Sn acetate solution 2. Dry at 120℃ 3. Firing in air at 600℃ for 1 hour 4. Impregnation with Pd nitrate solution (if necessary) 5. Add water and Al binder (5 wt% Al on carrier) 2 O 3 ) 6. Add Pt amine solution 7. Adjust pH to 4.5 (HNO 3 (Use 8. Mill at 600 rpm for 10 minutes 9. Dry at 120℃ 10. Firing in air at 450℃ for 1 hour 11. Crush the powder and sieve it to 250-500 μm. 12. 10% H in air 2 Aging at 800 °C for 16 h in O atmosphere

[0215] Powder sample testing All samples (both new and aged) were evaluated at steady state temperatures of 120, 135, 150, 165, 180, 195, 210, 225, 250, 300, and 350° C. in a 48-tray rig as follows: - 3 minutes equilibration time for each reactor at each temperature + 30 seconds sampling time - Catalyst mass: 0.1 g (i.e. normalized to the same total PGM amount in each reactor) -GHSV:50000h-1 - Feed gas with liquid HC: 700 ppm CO, 190 ppm C1HC (130 ppm from decane, 60 ppm from propylene), 40 ppm NO, 10% O2, 6% CO 2 , and 5% H 2 O - Two runs; 30 second average data from the second run was used to rank the catalysts.

[0216] These results are shown in Figures 8–11. They show that the addition of small amounts of Sn (0.5–4%) to the ceria support in the presence of 2–4% Pd promoted CO light-off for both fresh and aged samples.

[0217] Similarly, Figures 12 and 13 show that the addition of small amounts of Sn (1–4%) to the ceria support in the presence of 2% Pt promoted CO light-off for both fresh and aged samples.

[0218] Figures 14 and 15 show that the addition of small amounts of Sn (1-4%) to the ceria support in the presence of 2% Pt promoted HC light-off for both fresh and aged samples.

[0219] Figures 16 and 17 show that the addition of small amounts of Sn (1–4%) to the ceria support in the presence of 2% Pt significantly reduced the NO 2This indicates that formation has increased.

[0220] Example 4: Reactor testing of core samples (dynamic conditions) Both new and aged core samples were evaluated under simulated NEDC (New European Driving Cycle) conditions. The simulated exhaust gas flow conditions, along with the temperature and speed profiles of the NEDC cycle, are shown in Figure 18.

[0221] FIG. 19 shows the reduction in cumulative tailpipe CO emissions under the NEDC protocol for exemplary Pd / ceria oxidation catalyst compositions of the present disclosure promoted with Mg, Sn, or Mn.

[0222] FIG. 20 shows the reduction in cumulative tailpipe HC emissions under the NEDC protocol for exemplary Pd / ceria oxidation catalyst compositions of the present disclosure promoted with Mg, Sn, or Mn.

[0223] Example 6. Preparation and evaluation of multi-layer core samples Sample A - an article of the present invention. Bottom layer catalyst powder 212 grams of ceria and 54 grams of zeolite (chabazite) were weighed and mixed thoroughly. 8 grams of Sn acetate were weighed and mixed with 30 grams of acetic acid and 25 grams of DI-H. 2 The Sn-containing mixture was added to the ceria+zeolite powder and mixed thoroughly. The wet powder had a greenish gray color. The powder was dried at 120° C. for 4 hours and calcined at 500° C. for 1 hour. 37 grams of Pd nitrate was weighed out and mixed with 50 grams of DI-H. 2 The Pd mixture was added to the calcined Sn / ceria / zeolite powder and mixed thoroughly. The powder was dried at 120° C. for 4 hours and calcined at 500° C. for 1 hour.

[0224] Bottom layer catalyst washcoat slurry 386 grams of DI-H 2Weighed out 100g of sintered cellulose, added the previous calcined powder to the water and mixed thoroughly. Added 2 grams of Ba hydroxide and mixed thoroughly. Added 1 gram of tartaric acid and mixed thoroughly. Grinded to a particle size of 9.2 microns. Finally, added 28 grams of alumina binder and mixed thoroughly.

[0225] Preparation of catalyst core samples (1) Two 1 inch diameter by 3 inch long ceramic substrate cores with a cell density of 400 cells per square inch were dipped into the bottom washcoat slurry. An air gun was used to blow off excess slurry. The coated cores were dried with a hot air blower at 200°C for 5-10 minutes and then fired in an oven at 500°C for 1 hour.

[0226] Interlayer catalyst slurry 402 grams of DI-H 2 0 was weighed and 195 grams of 2% Pd / Ferrierite / ZSM-5 was added (FER / MFI ratio 10:1). Mixed thoroughly to a particle size of 5.1 microns. 91 grams of H-Beta Zeolite was added and mixed thoroughly. pH=3.7 and solids concentration in the slurry was 33.9.

[0227] Preparation of catalyst core samples (2) The core coated with the bottom layer was immersed in the intermediate layer slurry. The coated core was dried at 200°C for 5-10 minutes with a hot air blower, and then baked in an oven at 500°C for 1 hour.

[0228] Top layer catalyst slurry 282 grams of 5% Si on alumina and 29 grams of alumina containing 5% Mn were weighed out. 58 grams of Pt-amine solution was weighed out and mixed with 80 grams of DI-H 2 Dilute with 325 g DI-HO. 2O was added and mixed thoroughly. Ball milled for 2 hours until a particle size of 17.5 microns was reached. 15 grams of ZSM-5, 44 grams of Si binder, and 6 grams of Al binder were added and mixed thoroughly.

[0229] Preparation of catalyst core samples (3) The core coated with the bottom and middle layers was immersed in the top layer slurry. The coated core was dried at 200°C for 5-10 minutes with a hot air blower and then fired in an oven at 500°C for 1 hour. The resulting core sample had a Pt / Pd ratio of 13:17 and a Pt / Pd weight of 150 g / ft 3 The PGM loading was 1.2 g / L.

[0230] Sample B - Article of the present invention. Sample B was prepared in the same manner as Sample A, except that the arrangement of the washcoat layers was changed so that the middle layer slurry of Sample A was coated onto the core as the bottom layer, and the bottom layer slurry of Sample A was coated as the middle layer. The top layer remained the same.

[0231] Sample C (reference item) Bottom layer catalyst washcoat slurry 5 g of Pd and 10 g of Pt were impregnated onto 5% silica-coated alumina (1000 g). 2000 grams of DI-H 2 The DI-HO was weighed together with the impregnated PGM powder. 2 Barium hydroxide was added to O. The powder was ground to a particle size of less than 10 microns.

[0232] Preparation of catalyst core samples (1) Two 1 inch diameter by 3 inch long ceramic substrate cores with a cell density of 400 cells per square inch were immersed in the Pd / Pt / alumina / Ba slurry. An air gun was used to blow off excess slurry. The coated cores were dried with a hot air blower at 200°C for 5-10 minutes and then fired in an oven at 500°C for 1 hour.

[0233] Top inlet zone catalyst washcoat slurry 2.5 g of Pd and 2.5 g of Pt are impregnated into 5% silica-coated alumina (200 g). 450 grams of DI-H 2 The DI-HO was weighed together with the impregnated PGM powder. 2 Barium hydroxide (5 g) was added to the slurry. 200 g of zeolite Fe-Beta (1.2% Fe) was added to the slurry. Alumina binder was added and the mixture was milled to a particle size of less than 10 microns.

[0234] Preparation of catalyst core samples (2) The bottom coated core was immersed halfway into the top inlet zone slurry. An air gun was used to blow off excess slurry. The coated core was dried by a hot air blower at 200°C for 5-10 minutes.

[0235] Top exit zone catalyst washcoat slurry 14 g of Pt was impregnated onto 5% silica-coated alumina (300 g). 450 grams of DI-H 2 The DI-HO was weighed together with the impregnated PGM powder. 2 Zeolite Beta (60 g) was added to 0. Alumina binder was added. Nitric acid and acetic acid were added to adjust the pH to 4.5. Continuously milled at 2500 rpm until the particle size was less than 10 microns.

[0236] Preparation of catalyst core samples (3) The previously coated core from (2) was immersed halfway into the previously top exit zone slurry. Excess slurry was blown off using an air gun. The coated core was dried by a hot air blower at 200°C for 5-10 minutes. The resulting core sample had a Pt / Pd ratio of 3:1 and a Pt / Pd content of 150 g / ft 3 The PGM loading was 1.2 g / L.

[0237] Preparation of core samples for testing All samples were incubated in 10% H 2 O, 10% O 2 , remaining N 2 The mixture was aged at 800° C. for 16 hours in a tube furnace under an atmosphere of 0.1%.

[0238] Reactor testing of core samples All samples were evaluated under simulated European Urban Driving Cycle (EUDC) conditions as described in Example 3. The results for the aged samples are shown in Figure 21 and summarized in Table 1.

[0239] [Table 1]

[0240] The Sn-Ce-containing samples, Samples A and B, showed superior CO conversion performance relative to the catalyst coated in the reference zone (reference, Sample C), regardless of where the Sn-Ce compound was placed (bottom or middle layer).

Claims

1. 1. A low temperature carbon monoxide (LT-CO) oxidation catalyst composition for abating exhaust gas emissions from a lean-burn engine, comprising: an oxygen storage component (OSC) comprising ceria, a first platinum group metal (PGM) component selected from palladium (Pd), platinum (Pt) and combinations thereof; and a first promoter metal selected from tin (Sn) or an oxide thereof; the OSC is impregnated with the first PGM component and the first promoter metal; the first promoter metal is present in an amount of from 1% to 4% by weight of the OSC alone, calculated on a metal oxide basis; An LT-CO oxidation catalyst composition, wherein the LT-CO oxidation catalyst composition is effective for oxidizing carbon monoxide and hydrocarbons under cold start conditions.

2. 2. The LT-CO oxidation catalyst composition of claim 1, wherein the first PGM component is present in an amount of from 1% to 10% by weight of the OSC alone.

3. 10. The LT-CO oxidation catalyst composition of claim 1, wherein the OSC comprises rare earth metal oxide in an amount ranging from 0.1 wt. % to 100 wt. %, based on the total weight of the OSC alone.

4. 2. The LT-CO oxidation catalyst composition of claim 1, wherein said first PGM component is present at 2 wt. % and said Sn is present at 1 wt.

5. 10. The LT-CO oxidation catalyst composition of claim 1, further comprising a first refractory metal oxide selected from the group consisting of alumina, silica, zirconia, titania, yttria, and combinations thereof.

6. The LT-CO oxidation catalyst composition of claim 1, further comprising a first zeolite, said first zeolite being one or more small pore zeolites having a 6-8 membered ring structure, and one or more medium pore or large pore zeolites having a 10-12 membered ring structure.

7. 7. The LT-CO oxidation catalyst composition of claim 6, wherein the one or more small pore zeolites are selected from the group consisting of chabazite, zeolite A, and combinations thereof, and the one or more medium pore or large pore zeolites are selected from the group consisting of beta zeolite, Y zeolite, ferrierite, ZSM-5, and combinations thereof.

8. The LT-CO oxidation catalyst composition of claim 1, further comprising an alkaline earth metal component selected from the oxides of magnesium, calcium, strontium, barium, or combinations thereof.

9. A method of manufacturing a pipe comprising: a first washcoat comprising the LT-CO oxidation catalyst composition of claim 1 disposed on at least a portion of said substrate.

10. A method of manufacturing a pipe comprising: a substrate having an inlet end and an outlet end defining an overall length; a first washcoat comprising a low temperature carbon monoxide (LT-CO) oxidation catalyst composition disposed on at least a portion of the substrate; a diesel oxidation catalyst (DOC) composition, The DOC composition comprises: a second washcoat comprising a second zeolite, the second zeolite being impregnated with a second PGM component; a third washcoat comprising a third zeolite and a second refractory metal oxide, wherein the third zeolite, the second refractory metal oxide, or both, are impregnated with a third PGM component; The low temperature carbon monoxide (LT-CO) oxidation catalyst composition comprises: an oxygen storage component (OSC), a first platinum group metal (PGM) component, and a first promoter metal; A catalyst article, wherein said OSC is impregnated with said first PGM component and said first promoter metal, and said LT-CO oxidation catalyst composition is effective for oxidizing carbon monoxide and hydrocarbons under cold start conditions.

11. The catalytic article of claim 10, wherein the second refractory metal oxide is impregnated with a second promoter metal.

12. The catalyst article of claim 10 , wherein the second PGM component comprises Pt, Pd, or a combination thereof.

13. 11. The catalyst article of claim 10, wherein the second zeolite and the third zeolite each comprise a hydrothermally stable zeolite in the form of a 6-12 membered ring structure, and the second zeolite and the third zeolite each are independently selected from the group consisting of ZSM-5, beta, mordenite, Y zeolite, chabazite, ferrierite, and combinations thereof.

14. The catalyst article of claim 10, wherein the first, second, and third washcoats of the catalyst article are layered or zoned.

15. 15. The catalyst article of claim 14 having a zoned configuration, wherein the first washcoat is disposed on the substrate from either the inlet end or the outlet end for 10% to 90% of the total length, the second washcoat is disposed on the substrate from either the inlet end or the outlet end for 90% to 10% of the total length, and the third washcoat is coated over the first washcoat and the second washcoat.

16. The first washcoat has a coating thickness of at least 0.5 g / in ３ 10. The catalytic article of claim 9, wherein the catalyst is present on the substrate at a loading of

17. 10. The catalytic article of claim 9, wherein the substrate is a honeycomb substrate in the form of a wall-flow filter or a flow-through monolith.

18. 15. The catalytic article of claim 14, wherein the first washcoat further comprises a small pore zeolite, a large pore zeolite, an alkaline earth metal component, or a combination thereof.

19. 10. The catalytic article of claim 9, wherein the cold start condition comprises an exhaust gas temperature of less than 150°C.

20. The catalyst article of claim 9, further comprising a hydrocarbon (HC) trapping composition, a low temperature NO x adsorbent (LT-NA) composition, or a lean NO x trapping (LNT) composition.

21. 1. An exhaust gas treatment system for treating a lean-burn engine exhaust gas stream containing hydrocarbons, carbon monoxide, nitrogen oxides, and particulate matter, said exhaust gas treatment system comprising: a lean burn engine generating an exhaust gas stream; an exhaust conduit in fluid communication with the lean-burn engine through an exhaust manifold; and the catalytic article of claim 9 positioned downstream of the lean-burn engine and in fluid communication with the exhaust gas flow.

22. Soot filters, selective catalytic reduction (SCR) catalysts, urea injection components, ammonia oxidation (AMOx) catalysts, low temperature NO ｘ Absorbent (LT-NA) and Lean NO ｘ 22. The exhaust gas treatment system of claim 21, further comprising one or more additional components selected from the group consisting of: a trap (LNT).

23. 10. A method for treating a lean-burn engine exhaust gas stream comprising contacting the exhaust gas stream with the catalytic article of any one of claims 9.

24. 10. A method for reducing CO and / or HC levels in an exhaust gas stream comprising contacting the exhaust gas stream with a catalytic article according to any one of claims 9 for a time and at a temperature sufficient to reduce the CO and / or HC levels in the gas stream.

25. 25. The method of claim 24, wherein the CO and / or HC levels in the exhaust gas stream are reduced by at least 30% compared to the CO and / or HC levels in the gas stream before contact with the catalytic article.