Abstract

A sandwich panel (100) comprises: a core layer (1) having a honeycomb structure; and a plurality of skin layers (2) that are disposed on both surfaces of the core layer (1). The skin layers (2) each comprise two or more prepregs (21) which are stacked on one another with a sheet (22), which is obtained by a papermaking process, interposed therebetween.

Description

[Technical field]

[0001] The present invention relates to a sandwich panel and a method for manufacturing a sandwich panel. More particularly, the present invention relates to a sandwich panel, a method for manufacturing a sandwich panel, and a molding material set for a sandwich panel. [Background technology]

[0002] A sandwich panel is composed of a hollow honeycomb core with a hexagonal cross section and a pair of skin materials such as prepregs bonded to both sides of the honeycomb core. Sandwich panels, which are characterized by their light weight and high rigidity, are used, for example, in structural components for aircraft.

[0003] Various methods have been disclosed for manufacturing sandwich panels. For example, a common method is described in Patent Document 1. This document discloses a method for forming a secondary bond, in which prepregs are laminated, the binder resin in the prepregs is cured in an autoclave under a vacuum bag state, and then composite prepregs are assembled on both sides of a honeycomb core via a film-like adhesive, and the film-like adhesive is cured by applying pressure at a high temperature. [Prior art documents] [Patent documents]

[0004] [Patent Document 1] Patent Publication No. 2020-1268 Summary of the Invention [Problem to be solved by the invention]

[0005] However, conventional sandwich panels such as that disclosed in Patent Document 1 have room for improvement in terms of further improving their mechanical strength. [Means for solving the problem]

[0006] The present inventors have conducted extensive research to improve the mechanical strength of sandwich panels and have discovered that the use of a new paper-formed sheet is effective, thus completing the present invention.

[0007] According to the present invention, the following sandwich panel and related techniques are provided.

[0008] [1] A sandwich panel comprising a core layer having a honeycomb structure and a plurality of skin layers provided on both sides of the core layer, At least one of the skin layers is formed by laminating two or more prepregs with paper sheets interposed therebetween. [2] The sandwich panel according to [1], The sandwich panel comprises a sheet made of a thermosetting resin and short reinforcing fibers. [3] A sandwich panel according to [1] or [2], The thickness of the paper sheet is 5 μm or more and 150 μm or less. [4] A sandwich panel according to any one of [1] to [3], A sandwich panel, wherein the ratio (volume %) of the thermosetting resin to the total volume of the papermaking sheet is 10 volume % or more and 70 volume % or less. [5] A sandwich panel according to any one of [2] to [4], A sandwich panel, wherein the thermosetting resin of the papermaking sheet contains one or more resins selected from the group consisting of phenolic resins, epoxy resins, unsaturated polyester resins, melamine resins and polyurethane resins. [6] A sandwich panel according to any one of [2] to [5], A sandwich panel, wherein the fiber filler of the papermaking sheet includes one or more fibers selected from metal fibers, carbon fibers, glass fibers, ceramic fibers, polyamide fibers, aramid fibers, polyimide fibers, polyvinyl alcohol fibers, polyester fibers, acrylic fibers, polyparaphenylene benzoxazole fibers, polyethylene fibers, polypropylene fibers, polyacrylonitrile fibers, and ethylene vinyl alcohol fibers. [7] A sandwich panel according to any one of [1] to [6], The prepreg is a sandwich panel made using a sheet-like base material made of one or more types of fibers selected from aramid fibers, polyester fibers, polyphenylene sulfide fibers, carbon fibers, graphite fibers, glass fibers, and silicon carbide fibers. [8] A sandwich panel according to any one of [1] to [7], The prepreg comprises, as a binder resin, one or more resins selected from the group consisting of a phenolic resin, an epoxy resin, an unsaturated polyester resin, a melamine resin, and a polyurethane resin. [9] A sandwich panel according to any one of [1] to [8], The prepreg has a thickness of 50 μm or more and 500 μm or less.

[10] A sandwich panel according to any one of [1] to [9], The core layer is made of aramid fibers.

[11] A sandwich panel according to any one of [1] to

[10] , The sandwich panel is used as an aircraft panel.

[12] A method for manufacturing a sandwich panel comprising a core layer having a honeycomb structure and a plurality of skin layers provided on both sides of the core layer, comprising: At least one of the skin layers is formed by laminating two or more prepregs with a papermaking sheet interposed therebetween, a step of disposing the skin layers on each surface of the core layer; an integration step of integrating the core layer and the skin layer by a heating and pressurizing treatment; A method for manufacturing a sandwich panel comprising:

[13] A method for producing a sandwich panel according to

[12] , comprising the steps of: The integration step is carried out at 100 to 200° C. and 1 to 20 kgf / m 2 A method for manufacturing a sandwich panel, the method being carried out under the conditions of:

[14] A method for producing a sandwich panel according to

[12] or

[13] , comprising the steps of: In the placing step, the skin layers are placed on each surface of the core layer by stacking one of the prepregs, the papermaking sheet, and the other of the prepregs in that order.

[15] A method for producing a sandwich panel according to

[12] or

[13] , comprising the steps of: Prior to the placing step, A skin layer forming step of laminating one of the prepregs, the papermaking sheet, and the other of the prepregs in this order and integrating them by heating and pressurizing to obtain the skin layer, In the placing step, A method for manufacturing a sandwich panel, comprising: disposing the skin layers on each side of the core layer via a hot melt adhesive.

[16] A method for producing a sandwich panel according to

[15] , comprising the steps of: The skin layer forming process is carried out at 100 to 200° C. and 10 to 50 kgf / m 2 A method for manufacturing a sandwich panel, in which the sandwich panel is heated and pressurized under the conditions of

[17] A molding material set for a sandwich panel including a core layer having a honeycomb structure, a plurality of prepregs, and a plurality of paper sheets, A molding material set for sandwich panels, wherein a plurality of the prepregs are laminated via the papermaking sheets to form a plurality of skin layers, and the skin layers are configured to be provided on both sides of the core layer, respectively. Effect of the Invention

[0009] According to the present invention, a technique is provided that can improve the mechanical strength of a sandwich panel. [Brief description of the drawings]

[0010] [Figure 1] FIG. 1 is a schematic cross-sectional view showing a sandwich panel according to an embodiment of the present invention. [Diagram 2] FIG. 2 is a schematic cross-sectional view showing a first example of a method for manufacturing a sandwich panel according to the present embodiment. [Diagram 3] A schematic cross-sectional view showing a second example of a method for manufacturing a sandwich panel according to this embodiment. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0011] In this specification, the expression "a to b" in the explanation of a numerical range means from a to b, unless otherwise specified. For example, "1 to 5% by mass" means "1% by mass to 5% by mass." Hereinafter, embodiments of the present invention will be described with reference to the drawings. In all the drawings, the same components are given the same reference numerals and the description will be omitted as appropriate.

[0012] <Sandwich panel> As shown in Fig. 1, the sandwich panel 100 according to this embodiment includes a core layer 1 having a honeycomb structure and a skin layer 2 provided on each of both sides of the core layer 1. In other words, the skin layer 2 is provided on one side (upper surface) of the core layer 1, and a skin layer 2 is also provided on the other side (lower surface). In this embodiment, an example in which the skin layer 2 is formed by laminating two prepregs 21 with a papermaking sheet 22 interposed therebetween will be described, but this is not limiting. For example, the skin layer 2 may be formed by laminating three prepregs 21 with the papermaking sheet 22 interposed therebetween, or a layer of four or more prepregs may be used.

[0013] Hereinafter, each component of the sandwich panel 100 will be described in detail.

[0014] [Core layer] The core layer 1 is a sheet-like plate member having a structure with high strength and light weight, and has a honeycomb structure. The honeycomb structure is a known structure having a plurality of substantially regular hexagonal through holes penetrating from the upper surface to the lower surface.

[0015] Examples of the substrate constituting the honeycomb structure of the core layer 1 include aramid fibers, paper, balsa wood, plastic, aluminum, titanium, glass, and alloys thereof molded into a honeycomb shape by a known method. Among them, from the viewpoints of heat resistance and weight reduction, it is preferable that the substrate constituting the honeycomb structure of the core layer 1 contains aramid fibers.

[0016] The core layer 1 is preferably in the form of a woven fiber cloth as a substrate, which improves processability into a honeycomb structure and allows the sandwich panel 100 to be made lighter. In addition, when the core layer 1 is a fiber cloth, it is preferable to form a sheet-like member by impregnating a core layer substrate having a honeycomb structure with a binder resin. This further enhances the strength and light weight. The binder resin is not particularly limited, and the same one as that of the skin layer 2 described later can be used.

[0017] The thickness of the core layer 1 is not particularly limited, but may be, for example, 1 mm or more and 50 mm or less, 3 mm or more and 40 mm or less, or 5 mm or more and 30 mm or less.

[0018] The size of each core cell in the core layer 1 is not particularly limited, but may be, for example, 1 mm or more and 10 mm or less on a side.

[0019] The surface area (upper and lower surfaces) of the core layer 1 is not limited, but may be, for example, the surface area of ​​one sandwich panel 100, or may be the total surface area of ​​a plurality of sandwich panels. This makes it possible to obtain a plurality of panels by cutting out one sandwich panel 100 into individual pieces, thereby improving productivity. For example, the surface area (upper and lower surfaces) of the core layer 1 can be large, for example, 1 m 2 It may be more than that.

[0020] Moreover, the core layer 1 may be subjected to various surface treatments on the inside and / or outside from the viewpoint of improving corrosion resistance and heat resistance.

[0021] [Skin layer] The skin layer 2 constitutes the outer surface of the sandwich panel 100 and is the outermost layer. The skin layer 2 of this embodiment is formed by laminating two layers of prepreg 21 with a paper-made sheet 22 interposed therebetween. More specifically, the skin layer 2 is preferably obtained by hardening the binder resin in the prepreg 21 and firmly adhering it to the paper-made sheet 22. That is, the prepreg 21 contains a binder resin, and during the manufacturing process of the sandwich panel 100, a part of the binder resin permeates the paper-made sheet 22 and hardens, thereby improving the adhesion at the interface between the prepreg 21 and the paper-made sheet 22. The prepreg 21 and the paper-made sheet 22 that constitute the skin layer 2 will be described in detail below.

[0022] [Prepreg] There are a plurality of prepregs 21, and one or two of the prepregs 21 are layers that form the outer surface of the skin layer 2 and can be the outermost layers. The prepreg 21 is obtained by impregnating a sheet-like base material with a binder resin. The sheet-like substrate may be one or more selected from aramid fiber, polyester fiber, polyphenylene sulfide fiber, carbon fiber, graphite fiber, glass fiber, and silicon carbide fiber. This can reduce the difference in linear expansion coefficient between the prepreg 21 and the core layer 1, thereby suppressing warping of the sandwich panel 100. Among these, it is more preferable to contain glass fibers in terms of obtaining high heat resistance, and it is more preferable to contain carbon fibers in terms of achieving both mechanical strength and light weight.

[0023] The binder resin may be one or more selected from the group consisting of phenolic resins, epoxy resins, unsaturated polyester resins, melamine resins, and polyurethane resins.

[0024] The thickness of the prepreg 21 is preferably 50 μm or more and 500 μm or less, more preferably 50 to 400 μm, and further preferably 50 to 300 μm.

[0025] [Paper-made sheet] The papermaking sheet 22 of the present embodiment is used to bond the plurality of prepregs 21 together. The number of papermaking sheets 22 is appropriately set according to the number of prepregs 21. The papermaking sheet 22 is preferably a sheet obtained by a papermaking method using a thermosetting resin and reinforcing short fibers as materials. That is, the papermaking sheet is obtained by dispersing the reinforcing short fibers in an excess of solvent and papermaking the same, depositing a large amount of the reinforcing short fibers in layers while uniformly entangling them. As a result, it is possible to contain a high proportion of the reinforcing short fibers, and also to improve the dispersibility and entanglement, thereby dramatically improving the mechanical strength.

[0026] The proportion (volume %) of the thermosetting resin is preferably 10 volume % or more and 70 volume % or less, more preferably 30 volume % or more and 60 volume % or less, and even more preferably 40 volume % or more and 55 volume % or less, relative to the total volume of the papermaking sheet 22. By setting the proportion of the thermosetting resin to be equal to or greater than the above lower limit, it is possible to improve the moldability of the papermaking sheet 22. On the other hand, by setting the proportion of the thermosetting resin to be equal to or less than the above upper limit, it is possible to prevent the thermosetting resin from being excessively interposed at the interface between the papermaking sheet 22 and the prepreg 21, thereby maintaining good adhesion between them, and to increase the proportion of reinforcing short fibers, thereby further improving the mechanical strength.

[0027] (thermosetting resin) As the thermosetting resin, phenol resin, epoxy resin, melamine resin, polyurethane, unsaturated polyester resin, etc. can be used. As the thermosetting resin, one or a combination of two or more of the above specific examples can be used. Among them, phenol resin and epoxy resin are preferable as the thermosetting resin.

[0028] Specific examples of the phenolic resin include novolac-type phenolic resin, resol-type phenolic resin, and aryl alkylene-type phenolic resin. As the phenolic resin, one of these may be used alone, or two or more types having different weight average molecular weights may be used in combination, or one or more types may be used in combination with their prepolymers. Among them, it is preferable to use different types of phenolic resins in combination, and it is more preferable to use, for example, a novolac-type phenolic resin and a resol-type phenolic resin in combination.

[0029] Specific examples of epoxy resins include biphenyl type epoxy resins; bisphenol type epoxy resins such as bisphenol A type epoxy resins, bisphenol F type epoxy resins, bisphenol AD ​​type, and tetramethylbisphenol F type epoxy resins; stilbene type epoxy resins; novolac type epoxy resins such as phenol novolac type epoxy resins and cresol novolac type epoxy resins; polyfunctional epoxy resins such as triphenyl type epoxy resins exemplified by triphenol methane type epoxy resins and alkyl-modified triphenol methane type epoxy resins; phenol aralkyl type epoxy resins having a phenylene skeleton, naphthol aralkyl type epoxy resins having a phenylene skeleton, and phenol aralkyl type epoxy resins having a biphenylene skeleton. phenol aralkyl type epoxy resins such as aryl type epoxy resins (biphenyl aralkyl type epoxy resins) and naphthol aralkyl type epoxy resins having a biphenylene skeleton; naphthol type epoxy resins such as dihydroxynaphthalene type epoxy resins and epoxy resins obtained by glycidyl etherification of dihydroxynaphthalene dimers; triazine nucleus-containing epoxy resins such as triglycidyl isocyanurate and monoallyl diglycidyl isocyanurate; bridged cyclic hydrocarbon compound modified phenol type epoxy resins such as dicyclopentadiene modified phenol type epoxy resins; brominated type epoxy resins such as brominated bisphenol A type and brominated phenol novolac type; tris(hydroxyphenyl)methane type epoxy resins. As the epoxy resin, one of these may be used alone, or two or more different types may be used in combination.

[0030] (short fiber reinforcement) Examples of reinforcing short fibers include one or more types selected from metal fibers, carbon fibers, glass fibers, ceramic fibers, polyamide fibers, aramid fibers, polyimide fibers, polyvinyl alcohol fibers, polyester fibers, acrylic fibers, polyparaphenylene benzoxazole fibers, polyethylene fibers, polypropylene fibers, polyacrylonitrile fibers, and ethylene vinyl alcohol fibers. Among these, metal fibers, carbon fibers, and glass fibers are preferred from the viewpoint of obtaining high mechanical strength.

[0031] The content of the reinforcing short fibers is preferably adjusted appropriately depending on the total content together with the content of any inorganic filler described below. The total content of the reinforcing short fibers and inorganic filler in the entire papermaking sheet 22 is preferably 50 to 95 volume %, more preferably 60 to 90 volume %, and even more preferably 70 to 80 volume %. By setting the total content of the reinforcing short fibers and the inorganic filler to be equal to or greater than the above lower limit, good mechanical strength can be maintained throughout the papermaking sheet 22. On the other hand, by setting the total content of the reinforcing short fibers and the inorganic filler to be equal to or less than the above upper limit, good moldability can be maintained.

[0032] The papermaking sheet 22 of the present embodiment may further contain other components such as a thermoplastic resin, pulp fiber, an inorganic filler, and a flocculant depending on the purpose.

[0033] (thermoplastic resin) Examples of the thermoplastic resin in this embodiment include α-olefin resins and copolymers using α-olefins, polyester resins, and polystyrene resins. Examples of α-olefin resins and copolymers using α-olefins include polyethylene and polypropylene. Among them, polyethylene is preferable, and high density polyethylene (HDPE) is more preferable. When the papermaking sheet 22 contains high density polyethylene (HDPE), the interlaminar fracture toughness of the carbon fiber reinforced plastic laminate 10 can be effectively improved. The polyester resin may be one or more selected from polyethylene terephthalate resin (PET), polybutylene terephthalate resin (PBT), polytrimethylene terephthalate resin (PTT), and the like. The content of the thermoplastic resin in the entire papermaking sheet 22 is preferably 0.5 to 15% by volume, more preferably 1 to 10% by volume, and even more preferably 2 to 8% by volume.

[0034] (Pulp fiber) The paper sheet 22 according to this embodiment may contain pulp fibers in order to improve the handleability of the paper sheet 22 during the manufacturing process. The pulp fiber is not particularly limited, but examples thereof include cellulose fibers such as linter pulp and wood pulp, natural fibers such as kenaf, jute, and bamboo, pulp-like fibers obtained by fibrillating organic fibers such as para-type wholly aromatic polyamide fibers and copolymers thereof, aromatic polyester fibers, polybenzazole fibers, meta-type aramid fibers and copolymers thereof, acrylic fibers, acrylonitrile fibers, polyimide fibers, and polyamide fibers. As the pulp fiber, one or a combination of two or more of the above specific examples can be used. The content of pulp fibers in the entire paper sheet 22 is preferably 0.5 to 15 volume %, more preferably 1 to 10 volume %, and even more preferably 2 to 8 volume %.

[0035] (Inorganic filler) In this embodiment, the inorganic filler is used to increase the mechanical strength. Examples of inorganic fillers include one or more selected from calcium sulfate, barium sulfate, aluminum hydroxide, magnesium hydroxide, aluminum oxide (alumina), crystalline or fused silica, surface-treated silica, talc, kaolin, clay, mica, dolomite, wollastonite, glass fiber, carbon fiber, glass beads, zircon, and molybdenum compounds. Among them, from the viewpoint of easily improving the balance between mechanical strength and moldability of the entire papermaking sheet 22, fused silica is preferred, clay is more preferred, and a mixture of these is also possible.

[0036] The inorganic filler may be surface-treated. For example, the surface treatment may be performed with a coupling agent such as a silane coupling agent. This can suppress the aggregation of the inorganic filler and provide good dispersibility. As the coupling agent, for example, primary aminosilanes such as γ-aminopropyltriethoxysilane and γ-aminopropyltrimethoxysilane can be used. When a coupling agent is used, its content is not particularly limited, but is preferably 0.05 to 3 parts by weight, and more preferably 0.1 to 2 parts by weight, relative to 100 parts by weight of the inorganic filler.

[0037] (Flocculant) The papermaking sheet 22 according to the present embodiment may contain, for example, a flocculant, which allows any resin component and the reinforcing short fibers to be aggregated into a flock-like state.

[0038] (Other Ingredients) The papermaking sheet 22 according to this embodiment may further include, for example, papermaking agents, ion exchange agents, flocculants, conductivity imparting agents, flame retardants, flame retardant assistants, pigments, dyes, lubricants, release agents, compatibilizers, dispersants, crystal nucleating agents, plasticizers, heat stabilizers, antioxidants, coloring inhibitors, UV absorbers, flowability modifiers, foaming agents, antibacterial agents, vibration damping agents, deodorizing agents, sliding property modifiers, and antistatic agents.

[0039] The thickness of the paper sheet 22 of this embodiment is preferably 5 μm or more and 150 μm or less, and more preferably 10 μm or more and 100 μm or less. By setting the thickness of the papermaking sheet 22 to be equal to or greater than the above-mentioned lower limit, it is possible to improve the adhesion between the multiple prepregs 21. On the other hand, by setting the thickness of the papermaking sheet 22 to be equal to or less than the above-mentioned upper limit, it is possible to easily suppress delamination. The thickness of the papermaking sheet 22 is obtained by observing the cross-section of the sandwich panel 100, measuring the distance from the outer edge of the sheet-like base material of one prepreg 21 to the outer edge of the sheet-like base material of the other prepreg 21 multiple times, and calculating the average value. The thickness of the paper sheet 22 can be adjusted by the content of reinforcing short fibers contained in the paper sheet 22, etc.

[0040] [Manufacturing method] The paper sheet 22 of this embodiment can be obtained by a known method, for example, the following method.

[0041] First, fibers such as reinforcing short fibers and optional components such as the above-mentioned resin components (excluding the coagulant) are dispersed in a dispersion medium to prepare a slurry. The dispersion medium is not limited, and specific examples thereof include water; alcohols such as ethanol, 1-propanol, 1-butanol, and ethylene glycol; ketones such as acetone, methyl ethyl ketone, 2-heptanone, and cyclohexanone; esters such as ethyl acetate, butyl acetate, methyl acetoacetate, and methyl acetoacetate; and ethers such as tetrahydrofuran, isopropyl ether, dioxane, and furfural. Next, a flocculant is added to the dispersion liquid as necessary to form an aggregate. Note that if the reinforcing short fibers and the resin component are sufficiently aggregated to form an aggregate, the aggregation step does not need to be carried out. The slurry is then placed in a container with a mesh on the bottom to separate the dispersion medium from the aggregates, leaving the aggregates on the mesh to obtain a flat sheet-shaped aggregate. The thickness of the sheet can be adjusted by adjusting the amount of each of the materials in the material slurry or by preparing the slurry again and carrying out the separation process. Thereafter, the dispersion medium is removed by dehydration pressing and drying, and if a thermosetting resin is contained, a paper sheet 22 in a B-stage state can be obtained.

[0042] The B-stage papermaking sheet 22 is later heated and pressurized together with the prepreg 21, and if it contains a thermosetting resin, it is completely cured to become the papermaking sheet 22.

[0043] <Applications of sandwich panels> The sandwich panel 100 of the present embodiment is lightweight, has excellent mechanical strength, and can have a good balance of various performances such as heat resistance and fire resistance, and is therefore suitable for use in various types of transportation equipment. In particular, it is suitable for use in aircraft panels that require high mechanical strength and heat resistance. For example, the sandwich panel 100 can be used for aircraft interiors such as toilets and partitions, and for aircraft fixtures such as wagon housings.

[0044] <Sandwich panel manufacturing method> [First manufacturing method] Next, a first manufacturing method for the sandwich panel of this embodiment will be described. As shown in Fig. 2, the first manufacturing method is a method for integrating a core layer 1, a prepreg 21, and a papermaking sheet 22 at once. Specifically, the first manufacturing method includes the following steps: a step of laminating prepreg 21a, papermaking sheet 22, and prepreg 21b in this order on each surface of core layer 1, i.e., on the lower surface of core layer 1, and laminating prepreg 21b, papermaking sheet 22, and prepreg 21a in this order on the upper surface of core layer 1, thereby arranging skin layer 2; an integration step of integrating the core layer 1 and the skin layer 2 (the prepreg 21a, the papermaking sheet 22, and the prepreg 21b) by a heating and pressurizing treatment; Includes. Each step will be described in detail below.

[0045] First, the skin layer 2 is arranged by laminating the prepreg 21a, the papermaking sheet 22, and the prepreg 21b in this order on each surface of the core layer 1. Specifically, as shown in Fig. 2, the prepreg 21a, the papermaking sheet 22, and the prepreg 21b are laminated in this order on the lower surface of the core layer 1, and the prepreg 21b, the papermaking sheet 22, and the prepreg 21a are laminated in this order on the upper surface of the core layer 1, thereby forming the skin layer 2 on each of the upper and lower surfaces of the core layer 1. At this time, when the core layer 1 contains a thermosetting resin as a binder resin, it may be in a B-stage state before curing, but typically a cured one is used. When the prepreg 21 and the papermaking sheet 22 contain a thermosetting resin as a binder resin, both are preferably in a B-stage state before curing, and it is more preferable that at least the binder of the prepreg 21 is in a B-stage state. This allows the core layer 1, the prepreg 21, and the papermaking sheet 22 to be firmly integrated by a subsequent heating and pressurizing treatment. The prepregs 21a and 21b are substantially the same.

[0046] Next, they are integrated by a heat and pressure treatment. As shown in Fig. 2, for example, a flat pressing plate 50 is used to sandwich the skin layer 2 arranged on the outermost surface from above and below, and a heat and pressure treatment is performed. At this time, a release film may be used between the skin layer 2 and the pressing plate 50. This makes it possible to smooth the surface of the skin layer 2 and to easily peel the pressing plate 50 and the skin layer 2 after heating.

[0047] In the first production method, the heat treatment is preferably performed at 100 to 200° C., more preferably at 120 to 150° C., and the pressure treatment is preferably performed at 1 to 20 kgf / m 2 and more preferably 5 to 15 kgf / m 2 It is. By setting the temperature and pressure of the heating and pressurizing treatment to the above lower limit values ​​or more, the core layer 1 and the skin layer 2 can be firmly integrated. On the other hand, by setting the temperature and pressure of the heating and pressurizing treatment to the above upper limit values ​​or less, the skin layer 2 and the like can be appropriately integrated while preventing damage thereto. The heating and pressurizing time is adjusted appropriately depending on the temperature and pressure, but is preferably set to, for example, 30 to 90 minutes.

[0048] The heating and pressurizing treatment can be carried out in the atmosphere without the need for gas replacement, etc., which can improve productivity.

[0049] The pressing plate 50 may be a known one, for example, a metal plate such as a stainless steel plate, a tin plate, an aluminum plate, or a magnesium plate. The thickness of the pressing plate 50 is not particularly limited, but may be, for example, 0.5 mm to 10 mm, 0.8 mm to 5 mm, or 1.0 mm to 2.0 mm. By keeping the thickness within such range, a balance between rigidity and thermal conductivity can be achieved.

[0050] Through the above steps, the sandwich panel 100 is obtained.

[0051] [Second manufacturing method] Next, a second manufacturing method for the sandwich panel of this embodiment will be described. As shown in FIG. 3, the second manufacturing method includes a skin layer formation step in which prepreg 21a, papermaking sheet 22, and prepreg 21b are laminated in that order and integrated by heating and pressurizing to obtain skin layer 2, and the core layer 1 and skin layer 2 are integrated with a hot melt adhesive 3. The differences from the first manufacturing method will be described below.

[0052] In the skin layer forming process, the prepreg 21a, the papermaking sheet 22, and the prepreg 21b are laminated in this order, and are integrated by a heating and pressurizing treatment. At this time, when the prepreg 21 and the papermaking sheet 22 contain a thermosetting resin as a binder resin, it is preferable that both are in a B-stage state before being cured. This allows the prepreg 21 and the papermaking sheet 22 to be firmly integrated by the subsequent heating and pressurizing treatment.

[0053] In the second production method, the heat treatment is preferably performed at 100 to 200° C., more preferably at 120 to 150° C., and the pressure treatment is preferably performed at 10 to 50 kgf / m 2 More preferably, it is 20 to 45 kgf / m 2 It is. By setting the temperature and pressure of the heating and pressurizing treatment to the above-mentioned lower limit values ​​or more, the prepreg 21 and the papermaking sheet 22 can be firmly integrated. On the other hand, by setting the temperature and pressure of the heating and pressurizing treatment to the above-mentioned upper limit values ​​or less, the prepreg 21 and the papermaking sheet 22 can be appropriately integrated while suppressing damage to the prepreg 21 and the like. The heating and pressurizing time is adjusted appropriately depending on the temperature and pressure, but is preferably set to, for example, 30 to 90 minutes.

[0054] Next, the obtained skin layers 2 are placed on both sides of the core layer 1 with the hot melt adhesive 3 therebetween.

[0055] The hot melt adhesive 3 contains, as a main component, a non-curable resin that becomes flowable at high temperatures and returns to a non-flowable state when cooled. In other words, it melts at or above a certain temperature and develops adhesive properties. The non-curable resin may be one or more selected from the group consisting of thermoplastic resins including polyurethane, acrylonitrile, diene, acrylic, butadiene, polyamide, polyvinyl butyral, olefin, isoprene, butadiene, chloroprene, acrylonitrile, polyester, polyvinyl chloride, styrene, ethylene-vinyl acetate, fluorine, silicone, and copolymers thereof. Among these, it is more preferable that the hot melt adhesive contains polyamide as the main component.

[0056] The shape of the hot melt adhesive 3 is not particularly limited, but from the viewpoint of effectively suppressing the occurrence of voids, it is preferably in the form of a nonwoven fabric or a film.

[0057] Thereafter, in the same manner as in the first manufacturing method, a heat and pressure treatment is carried out using a pressing plate 50 or the like, and the core layer 1 and the skin layer 2 are integrated together to obtain the sandwich panel 100.

[0058] <Sandwich panel molding material set> The sandwich panel molding material set of this embodiment is a set including a core layer 1 having a honeycomb structure, a plurality of prepregs 21, and a plurality of paper-made sheets 22. That is, a plurality of prepregs 21 are laminated via papermaking sheets 22 to form a skin layer 2, and the skin layers 2 are provided on both sides of the core layer 1. By using these molding material sets, the above-mentioned sandwich panel 100 can be manufactured. In particular, by using the above-mentioned first manufacturing method, the sandwich panel 100 can be manufactured easily.

[0059] Although the embodiments of the present invention have been described above with reference to the drawings, these are merely examples of the present invention, and various configurations other than those described above can also be adopted. EXAMPLES

[0060] The present invention will be described in detail below with reference to examples, but the present invention is not limited to the descriptions of these examples.

[0061] (1) Preparation of paper sheet The following raw materials were used to prepare a paper sheet. (raw materials) Reinforced short fibers: Carbon fiber, Toray "T800SC" fiber length 6mm Thermosetting resin 1: Resol type phenolic resin "PR-51723" manufactured by Sumitomo Bakelite Co., Ltd. Thermosetting resin 2: Novolac phenolic resin "A-1087" manufactured by Sumitomo Bakelite Co., Ltd. Pulp fiber: Teijin's "Twaron (registered trademark) 1094" High density polyethylene: Mitsui Chemicals "SWP E400"

[0062] First, the above-mentioned thermosetting resin 1 and thermosetting resin 2 were mixed in a mixer so that the two resins were 70% by mass and 30% by mass, respectively, and then the resulting mixture was kneaded in a biaxial roll at 80°C for 5 minutes, and then cooled and pulverized to obtain a mixed resin having an average particle size of 50 μm. Next, 40% by volume of reinforcing short fibers, 50% by volume of the mixed resin, 5% by volume of pulp fibers, and 5% by volume of high-density polyethylene were added to water as a dispersion medium, and the mixture was stirred for 20 minutes to obtain a slurry with a solid concentration of 0.15% by weight. To the resulting slurry, a poly(meth)acrylic acid ester emulsion ("Himoc DR-9300" manufactured by Himo Corporation) prepared in advance was added so as to be 300 ppm relative to the solid content in the slurry, thereby flocculating the solid content in the slurry. The slurry containing the aggregates was then filtered through a 30-mesh metal screen, and the sheet-like aggregates remaining on the screen were pressed at a pressure of 3 MPa to dehydrate them to a dehydration rate of 20%. The dehydrated aggregates were dried at 70°C for 3 hours to obtain a papermaking sheet (thickness 1 mm) in a B-stage state. The dehydration rate was defined as the mass of water contained in the dehydrated sheet when the mass of water contained in the sheet-like aggregate before dehydration was taken as 100%.

[0063] (2) Sandwich panel molding material set The following sandwich panel molding material set was prepared. (Molding material set) Core layer: Aramid fiber, thickness 10mm, HRH-10-1 / 8-3.0 (HEXCEL), area 1m x 3m -Paper sheet: The sheet prepared in (1) above was used. Prepreg: A sheet-like prepreg (thickness 250 μm) was used, which was obtained by impregnating glass fiber (#7781, manufactured by HEXCEL) with phenolic resin (resole type phenolic resin, "34370" manufactured by Durez). The prepreg was in a B-stage state.

[0064] (3) Fabrication of sandwich panels <Example 1> On each surface of the core layer, a prepreg, a paper-formed sheet, and a prepreg were placed in this order, and SUS plates (thickness 1.5 mm, Rz 1.0 μm) were pressed from the top and bottom, and the prepreg was cured to form a skin layer by heating and pressurizing at 0.7 MPa, 127 ° C, and 60 minutes using a mechanical press, and the prepreg was integrated with the skin layer. After that, the SUS plates on the top and bottom surfaces were separated to obtain a sandwich panel in which the skin layer, core layer, and skin layer were laminated in this order.

[0065] <Reference example 1> Two prepregs were placed on each side of the core layer, and SUS plates (thickness 1.5 mm, Rz 1.0 μm) were pressed from the top and bottom, and the prepregs were hardened to form skin layers by heating and pressurizing at 0.7 MPa, 127°C, and 60 minutes using a mechanical press, and the core layer and the skin layers were integrated. The SUS plates on the top and bottom were then separated to obtain a sandwich panel in which the skin layer, core layer, and skin layer were laminated in this order.

[0066] <Example 2> The prepreg, papermaking sheet, and prepreg were arranged in that order, and SUS plates (thickness 1.5 mm, Rz 1.0 μm) were pressed against the top and bottom. The pieces were then integrated using a mechanical press by heating and pressurizing at 2.0 MPa, 137°C, and 60 minutes to obtain a skin layer. Next, the obtained skin layers were placed on both sides of the core layer via a hot melt adhesive (main component polyamide), and SUS plates (thickness 1.5 mm, Rz 1.0 μm) were pressed against them from the top and bottom. The layers were then laminated together using a mechanical press at 0.7 MPa, 127°C, and 60 minutes for heating and pressurization to obtain a sandwich panel.

[0067] <Reference example 2> Two prepregs were laminated and pressed onto SUS plates (thickness 1.5 mm, Rz 1.0 μm) from the top and bottom, and the laminate was subjected to a heat and pressure treatment at 2.0 MPa, 137°C, and 60 minutes using a mechanical press. Next, the cured prepregs were placed on both sides of the core layer via a hot melt adhesive (main component polyamide), and SUS plates (thickness 1.5 mm, Rz 1.0 μm) were pressed against them from the top and bottom. The sheets were then laminated together using a mechanical press at 0.7 MPa, 127°C, and 60 minutes for heating and pressurization to obtain a sandwich panel.

[0068] (4) Measurement The following measurements were carried out on each of the obtained sandwich panels, and the results are shown in Table 1. Flexural strength: Measured according to ASTM-D7249. · Peel strength: The peel strength between the core layer and the skin layer was measured according to ASTM-D1781.

[0069] [Table 1]

[0070] This application claims priority based on Japanese Patent Application No. 2022-161532, filed on October 6, 2022, the disclosure of which is incorporated herein in its entirety. [Explanation of symbols]

[0071] 1 Core layer 2. Skin layer 21 Prepreg 21a Prepreg 21b Prepreg 22 Paper Sheet 100 Sandwich Panel

Claims

1. A sandwich panel comprising a core layer having a honeycomb structure and a plurality of skin layers provided on both sides of the core layer, At least one of the skin layers is formed by laminating two or more prepregs with a papermaking sheet interposed therebetween, The sandwich panel, wherein the papermaking sheet contains a thermosetting resin and reinforcing short fibers, and the thermosetting resin is dispersible in water when uncured.

2. 2. A sandwich panel according to claim 1, The thickness of the papermaking sheet is 5 μm or more and 150 μm or less.

3. A sandwich panel according to claim 1 or 2, A sandwich panel, wherein the ratio (volume %) of the thermosetting resin to the total volume of the papermaking sheet is 10 volume % or more and 70 volume % or less.

4. A sandwich panel according to claim 1 or 2, A sandwich panel, wherein the thermosetting resin of the papermaking sheet contains one or more resins selected from the group consisting of phenolic resins, epoxy resins, unsaturated polyester resins, melamine resins and polyurethane resins.

5. A sandwich panel according to claim 1 or 2, A sandwich panel, wherein the reinforcing short fibers of the papermaking sheet include one or more types selected from metal fibers, carbon fibers, glass fibers, ceramic fibers, polyamide fibers, aramid fibers, polyimide fibers, polyvinyl alcohol fibers, polyester fibers, acrylic fibers, polyparaphenylene benzoxazole fibers, polyethylene fibers, polypropylene fibers, polyacrylonitrile fibers, and ethylene vinyl alcohol fibers.

6. A sandwich panel according to claim 1 or 2, The prepreg is a sandwich panel formed using a sheet-like base material made of one or more fibers selected from aramid fibers, polyester fibers, polyphenylene sulfide fibers, carbon fibers, graphite fibers, glass fibers, and silicon carbide fibers.

7. A sandwich panel according to claim 1 or 2, The prepreg comprises, as a binder resin, one or more resins selected from the group consisting of a phenolic resin, an epoxy resin, an unsaturated polyester resin, a melamine resin, and a polyurethane resin.

8. A sandwich panel according to claim 1 or 2, The sandwich panel, wherein the prepreg has a thickness of 50 μm or more and 500 μm or less.

9. A sandwich panel according to claim 1 or 2, The core layer is made of aramid fibers.

10. A sandwich panel according to claim 1 or 2, The sandwich panel is used as an aircraft panel.

11. A method for manufacturing a sandwich panel comprising a core layer having a honeycomb structure and a plurality of skin layers provided on both sides of the core layer, At least one of the skin layers is formed by laminating two or more prepregs with a papermaking sheet interposed therebetween, A step of dispersing a thermosetting resin and reinforcing short fibers in water and then forming the dispersion into a paper sheet; a step of disposing the skin layers on each surface of the core layer; an integration step of integrating the core layer and the skin layer by a heating and pressurizing treatment; A method for manufacturing a sandwich panel comprising:

12. A method for producing a sandwich panel according to claim 11, comprising the steps of: The integration process is carried out at 100 to 200° C. and 1 to 20 kgf / m ２ A method for manufacturing a sandwich panel, the method being carried out under the conditions of:

13. A method for producing a sandwich panel according to claim 11 or 12, comprising the steps of: In the placing step, the skin layers are placed on each surface of the core layer by stacking one of the prepregs, the papermaking sheet, and the other of the prepregs in that order.

14. A method for producing a sandwich panel according to claim 11 or 12, comprising the steps of: Prior to the placing step, A skin layer forming step of laminating one of the prepregs, the papermaking sheet, and the other of the prepregs in this order and integrating them by heating and pressurizing to obtain the skin layer, In the placing step, A method for manufacturing a sandwich panel, comprising: disposing the skin layers on each side of the core layer via a hot melt adhesive.

15. A method for producing a sandwich panel according to claim 14, comprising the steps of: The skin layer forming process is carried out at 100 to 200° C. and 10 to 50 kgf / m ２ A method for manufacturing a sandwich panel, in which the sandwich panel is heated and pressurized under the conditions of

16. A molding material set for a sandwich panel including a core layer having a honeycomb structure, a plurality of prepregs, and a plurality of papermaking sheets, The papermaking sheet includes a thermosetting resin and reinforcing short fibers, and the thermosetting resin has dispersibility in water when uncured, A molding material set for sandwich panels, wherein a plurality of the prepregs are laminated via the papermaking sheets to form a plurality of skin layers, and the skin layers are configured to be provided on both sides of the core layer, respectively.