Catalyst systems for reforming in cycle flow reactors

Abstract

A catalytic system for hydrocarbon reforming is provided, as well as a method for using such a catalytic system. The catalytic system may be deposited or otherwise coated on a surface or structure, such as a monolith, to achieve improved activity and / or structural stability. The metal oxide support layer may correspond to a thermally stable metal oxide support layer, such as a metal oxide support layer that is thermally stable at temperatures between 800°C and 1600°C. The catalytic system may be useful in a cyclic reaction environment, such as a reverse flow reactor or other type of reactor operated with flows in opposite directions and at different times within a reaction cycle.

Description

CROSS-REFERENCE TO RELATED APPLICATIONS

[0001] This application claims priority to and the benefit of U.S. Provisional Application No. 63 / 090,880, filed October 13, 2020, the disclosure of which is incorporated herein by reference in its entirety. [Technical field]

[0002] The present invention relates to compositions suitable for use in hydrocarbon reforming in high temperature environments. [Background technology]

[0003] A reverse flow reactor is an example of a reactor type that is useful for use in processes with cyclic reaction conditions. For example, due to the endothermic nature of the reforming reaction, additional heat needs to be consistently introduced into the reforming reaction environment. Reverse flow reactors can provide an efficient way of introducing heat into the reaction environment. After a portion of the reaction cycle is used for reforming or another endothermic reaction, a second portion of the reaction cycle can be used for combustion or another exothermic reaction to add heat to the reaction environment in preparation for the next reforming step. U.S. Pat. Nos. 7,815,873 and 8,754,276 provide examples of reverse flow reactors being used to perform various endothermic processes in a cyclic reaction environment.

[0004] Endothermic reactions such as reforming can benefit from a substantial amount of available catalytic surface area. Ceramic monolith structures are an example of a structure type that can provide high available surface area. One option may be to use a monolith that represents a packed array of cells or channels through which the reactant gas passes. A washcoat may be added to such a monolith to provide catalytic activity.

[0005] US Patent Application Publication No. 2020 / 0030778 describes a monolith structure for use in hydrocarbon reforming, the monolith structure being composed of a mixture of one or more dopant metal oxides and one or more structural oxides. The dopant metals and structural oxides are selected based on the relative Gibbs free energy values ​​of the dopant metal oxides and structural oxides. NiO and Al2O3 are listed as examples of suitable combinations of dopant metal oxides and structural oxides for forming the monolith structure. Summary of the Invention

[0006] In various embodiments, a hydrocarbon reforming catalyst system and a support structure are provided. The hydrocarbon reforming catalyst system includes a catalyst having reforming activity. The catalyst system further includes a metal oxide support layer that is thermally stable at 800° C. to 1600° C. and includes stabilized zirconia, perovskite, pyrochlore, spinel, hibonite, zeolite, corundum group oxide, or a combination thereof. The hydrocarbon reforming catalyst system and the metal oxide support layer may represent a catalyst system supported by one or more surfaces of a support structure. The hydrocarbon reforming catalyst system may represent (or account for) 0.5% or more by weight of the combined weight of the catalyst system and the support structure.

[0007] In another aspect, a method of forming a catalyst system is provided. The method includes forming a catalyst system comprising a metal oxide support layer and a catalyst that is thermally stable at 800° C. to 1600° C. The catalyst may have reforming activity and may include Ni, Rh, Ru, Pd, Pt, Cu, Ir, or combinations thereof. The metal oxide support layer may include stabilized zirconia, perovskite, pyrochlore, spinel, hibonite, zeolite, corundum group oxide, or combinations thereof. The method further includes supporting the catalyst system on one or more surfaces of a support structure. The method further includes annealing the supported catalyst system and support structure at an annealing temperature of 1000° C. or greater to form an annealed catalyst system and support structure. Additionally, the method includes exposing the annealed catalyst system and support structure to cyclic reforming conditions including a peak temperature of 1000° C. or greater in the presence of a hydrocarbon feed to form H2. The cyclic reforming conditions may include a reforming step and a regeneration step. Optionally, the annealing temperature may be greater than the peak temperature.

[0008] In another embodiment, a method for reforming hydrocarbons in a cyclic reaction environment is provided. The method includes reacting a mixture comprising a fuel and 0.1% by volume or more of O2 under combustion conditions in a combustion zone within a reactor, and heating one or more surfaces in the reaction zone to a regenerated surface temperature of 1000° C. or more. The 0.1% by volume or more of O2 may comprise 120% or more of the stoichiometric molar amount of O2 for combustion of the fuel. The reaction zone may include a catalyst system supported on one or more surfaces of a support structure. The method for reforming hydrocarbons in a cyclic reaction environment includes reacting a mixture comprising a fuel and 0.1% by volume or more of O2 under combustion conditions in a combustion zone within a reactor, and heating one or more surfaces in the reaction zone to a regenerated surface temperature of 1000° C. or more. The 0.1% by volume or more of O2 may comprise 120% or more of the stoichiometric molar amount of O2 for combustion of the fuel. The reaction zone may include a catalyst system supported on one or more surfaces of a support structure. a The reactant stream (or reactant stream) is heated to a temperature of 100° C., and the reactant stream is heated to a temperature of 100° C. a Optionally, the method for reforming hydrocarbons in a cyclic reaction environment may further include exposing the reactant stream to one or more surfaces in a reaction zone. Additionally, the method for reforming hydrocarbons in a cyclic reaction environment may further include exposing the reactant stream to one or more surfaces in a reaction zone such that a product stream comprising H2 is formed. a The reaction zone comprises exposing the reactant stream to a catalyst system at a temperature of 1000°C or greater. a The direction of flow for the reactant stream may be reversed relative to the direction of flow for the mixture. The catalyst system may comprise a catalyst having reforming activity and comprising Ni, Rh, Ru, Pd, Pt, Cu, Ir, or a combination thereof, and a metal oxide support layer comprising an oxide of stabilized zirconia, perovskite, pyrochlore, spinel, hibonite, zeolite, corundum, or a combination thereof. The metal oxide support layer may optionally be thermally phase stable between 800°C and 1600°C. [Brief description of the drawings]

[0009] [Figure 1]Figure 1 shows an example of the operation of a reverse flow reactor. Figure 1A shows the reforming step of the reforming reaction. Figure 1B shows the regeneration step of the reforming reaction. [Diagram 2] Figure 2 shows an example of a reverse flow reactor. [Diagram 3] Figure 3 shows an example of a catalyst system deposited on the surface of a honeycomb monolith. [Figure 4] Figure 4 shows an example of a temperature profile for performing steam reforming (or steam reforming) in a reverse flow reactor. [Diagram 5] FIG. 5 shows the SEM images of the NiAl2O4 catalyst system washcoated onto the monolith after exposure to cyclic reforming conditions. [Figure 6] FIG. 6 shows the SEM image of the Rh2O3 / α-Al2O3 catalyst system washcoated onto the monolith after 750 h of exposure to cyclic reforming conditions. [Figure 7] FIG. 7 shows the conversion (or percent conversion) of methane when reformed under cyclic reforming conditions in the presence of various catalyst systems. [Figure 8] FIG. 8 shows another SEM image of the surface of the NiAl2O4 catalyst system after exposure to cyclic reforming conditions. [Figure 9] FIG. 9 shows the conversion (or percent conversion) of methane when reformed under cyclic reforming conditions in the presence of various catalyst systems. [Figure 10] FIG. 10 shows the conversion (or percent conversion) of methane when reformed under cyclic reforming conditions in the presence of a monolith supported catalytic system composed of NiAl2O4. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0010] All numerical values ​​in the detailed description and claims of this specification may be interpreted as being "about" or "approximately" and take into account experimental error and variations that would be expected by one of ordinary skill in the art.

[0011] overview In various embodiments, a catalyst system for hydrocarbon reforming is provided along with a method for using the catalyst system. The catalyst system may be deposited or otherwise coated on a surface or structure (such as a monolith) to achieve improved activity and / or structural stability. In this description, a catalyst system is defined as including at least one catalyst corresponding to one or more catalytic metals (optionally in the form of a metal oxide) and at least one metal oxide support layer. In some embodiments, the catalyst and the metal oxide support layer may be simultaneously coated on the monolith, for example, in the form of a washcoat layer on the support. In some embodiments, the catalyst may be mixed with the metal oxide support layer. Alternatively, the catalyst and the metal oxide support layer may be sequentially deposited, such that the metal oxide support layer is deposited first, followed by the catalyst. In some embodiments, the metal oxide support layer may correspond to a thermally stable metal oxide support layer, such as a metal oxide support layer that is thermally stable at temperatures between 800° C. and 1600° C. Optionally, an intermediate bonding layer may be applied to at least a portion of the monolith or other structure prior to deposition of the catalyst system. The catalyst system may be useful for use in a cyclic reaction environment, such as a reverse flow reactor or other type of reactor operated with flows in opposite directions and different times within a reaction cycle. Reaction conditions in a cyclical reaction environment may involve temperature and / or pressure swings within a reaction cycle.

[0012] To use the catalyst system in a cyclic reaction environment, the catalyst system may be coated or otherwise supported on a structure or surface that will typically be present in the reaction environment during the reforming process cycle. For example, the catalyst system may be applied as a washcoat to the surface of one or more monoliths or other structures that are placed in the reactor. Such monoliths or other structures may contain a large number of cells or channels per unit surface area to substantially increase the amount of structural surface area that can be coated with the catalyst system. In some embodiments, the catalyst system may be deposited on a monolith or other structure that is composed of a low surface area material that is phase stable under high temperature reforming conditions. In such embodiments, the catalyst system and monolith or other structure may be annealed at or above the processing temperature prior to use. This may provide additional structural stability to the catalyst system, unexpectedly increasing the amount of time that the catalyst system can substantially retain a desired level of reforming activity.

[0013] Figure 3 shows an example of a portion of a monolith 300 that includes a catalyst system 310 deposited (or otherwise coated) on the surface of the monolith 300. In the example shown in Figure 3, a portion of the monolith corresponds to a regular pattern of square cells that allow reactant gas (a reactant gas, such as a reformed feed gas stream) to pass through the cells. In other embodiments, any convenient type of cell shape, such as round or hexagonal, can be used. The catalyst system 310 corresponds to a layer including catalyst 312 and metal oxide support 314 coated on the surface of the cells of the monolith.

[0014] In some embodiments, at least one catalyst in the catalyst system may correspond to a catalyst comprising Ni. NiAl2O4 is an example of a catalyst system that may initially correspond to Ni (or NiO when oxidized) as the catalyst and Al2O3 as the metal oxide support. During exposure to cyclic reforming conditions, at least a portion of NiO and Al2O3 may combine to form a spinel phase structure corresponding to NiAl2O4. Another example of a catalyst system comprising Ni in the catalyst may correspond to NiO as the catalyst and yttrium stabilized zirconia (YSZ) as the metal oxide support. Yet another example of a catalyst system comprising Ni in the catalyst may correspond to NiO as the catalyst and perovskite oxide as the metal oxide support.

[0015] Optionally, further advantages may be gained by using the catalyst system in conjunction with a modified regeneration step or reaction cycle that includes a heat incorporation step. In such optional embodiments, the modified regeneration step may include additional oxygen so that the catalyst system is brought to a more highly oxidized state during the subsequent reforming step.

[0016] In some embodiments, the catalyst system may represent one or more catalysts in a single zone. In other embodiments, the catalyst system may represent multiple zones. Optionally, in such embodiments, at least one catalyst zone may contain a different catalyst than a catalyst in a second catalyst zone.

[0017] Reforming of hydrocarbons to form syngas is a potentially desirable pathway to reduce or minimize CO2 emissions associated with hydrocarbon fuels. Reforming can convert hydrocarbon fuels to H2 and CO or CO2, a fuel with no CO2 emissions. By separating H2 from carbon oxides at a single location, some of the difficulties associated with preventing CO2 emissions can be reduced or minimized. However, due to the elevated temperatures required for hydrocarbon reforming, it is a challenge to balance efficient reforming of hydrocarbons with energy consumption and the operational life of the equipment.

[0018] As an option to improve the energy efficiency of the reforming process, a reaction system such as a reverse flow reactor may be used, or another type of reaction system in which the flow passes through the reactor in opposing directions between the reforming and regeneration steps (heating steps). Reverse flow reactors (and other similar types of reactors) can provide several types of advantages. First, by using multiple steps with different flows during the reaction cycle, heat can be provided to the reaction zone where reforming occurs by performing combustion in or near the reaction zone. This can reduce or minimize heat losses while still adding heat to the reaction zone. The use of opposing flows (or streams) can provide additional advantages in terms of establishing a desired temperature profile in the reaction zone. Although reverse flow reactors are used herein as an example of such types of systems, it will be understood that reverse flow reactors are included as an example of reactors that can provide such advantages.

[0019] While reverse flow reactors offer various advantages, they can present challenges with respect to maintaining the desired run times. The high temperatures introduced into the reverse flow reactor for reforming can result in breakdown of materials. In particular, the cyclic high temperature environment, including reducing and oxidizing conditions, can pose problems for catalyst systems. In various embodiments, catalyst systems are provided that can provide the desired catalytic activity for reforming and can maintain the desired activity for longer times (or extended periods) in the presence of a reactive environment of cyclic reducing and oxidizing conditions at elevated temperatures.

[0020] High temperature reforming catalyst system - NiAl 2 O 4 and NiO / NiAl 2 O 4 In some embodiments, the catalyst system may represent a mixture of NiO and Al2O3. Under cyclic high temperature reforming conditions, NiO and Al2O3 react to form a mixed phase of NiO, NiAl2O4, and / or Al2O3. Additionally, upon cyclic exposure to oxidizing and reducing conditions, the catalyst may be in a substantially fully oxidized state (e.g., NiO, NiAl2O4, Al2O3 ... 4、 The catalyst system may be changed (or converted) from a fully oxidized state, such as a combination of oxides including Al2O3, etc., to a variety of states that include at least some Ni metal supported on the surface. In this description (or discussion), a catalyst system that includes both NiO and Al2O3 is referred to as a NiAl2O4 catalyst system.

[0021] A catalyst in which NiO and Al2O3 are combined (or compounded) to form NiAl2O4 with a stoichiometric molar ratio of Al to Ni of approximately 2.0 (i.e., a 2:1 ratio of Al to Ni) can form NiAl2O4 without leaving excess NiO or Al2O3. Thus, one option for forming a NiAl2O4 catalyst is to combine NiO and Al2O3 to a stoichiometric molar ratio of Al to Ni of approximately 2.0. In some other embodiments, the catalyst may include excess NiO relative to the amount of alumina in the support, with at least some NiO present in a fully oxidized state. In such embodiments, the molar ratio of Al to Ni in the catalyst may be less than 2.0. For example, the molar ratio of Al to Ni in the NiO / NiAl2O4 catalyst can be 0.1-2.0, or 0.1-1.9, or 0.1-1.5, or 0.5-2.0, or 0.5-1.9, or 0.5-1.5, or 1.0-2.0, or 1.0-1.9, or 1.2-1.5, or 1.5-2.0, or 1.5-1.9. In yet other embodiments, excess Al2O3 relative to the amount of Ni can be included in the catalyst, with at least some Al2O3 being in a fully oxidized state. In such embodiments, the molar ratio of Al to Ni in the catalyst can be greater than 2.0. For example, the molar ratio of Al to Ni in the NiAl2O4 / Al2O3 catalyst can be from 2.0 to 10, or from 2.1 to 10, or from 2.0 to 5.0, or from 2.1 to 5.0, or from 2.0 to 4.0, or from 2.1 to 4.0.

[0022] In various embodiments, the NiAl2O4 catalyst may be incorporated into a washcoat that is applied to a surface or structure within the reactor, such as, for example, a monolith. By providing NiO and Al2O3 as a catalytic system that is deposited on a separate monolith (with NiAl2O4 subsequently formed under cycling conditions), the activity of the catalyst can be maintained for an unpredictably long period of time compared to the use of monoliths that have NiO and Al2O3 directly incorporated into the monolith structure.

[0023] When a composition is formed that includes both nickel oxide and alumina, NiO and Al2O3 may react to form a compound corresponding to NiAl2O4. However, when NiO (optionally nickel oxide in the form of NiAl2O4) is subjected to reducing conditions, divalent Ni is reduced to form metallic Ni. Thus, under cyclic reforming conditions that include both high temperature oxidizing and reforming environments, at least a portion of the NiAl2O4 catalyst may cycle (or cyclically) between states corresponding to Ni metal and Al2O3 and NiAl2O4. Such cyclical transitions between states are believed to result in the NiAl2O4 catalyst exhibiting unexpectedly enhanced activity over longer periods of time (or longer periods). Without being bound to a particular theory, it is believed that at least a portion of such longer term enhanced activity is due to the ability of Ni to "re-disperse" during successive oxidation cycles. This re-dispersion is believed to occur at least in part due to the formation of NiAl2O4 from NiO and Al2O3. Catalyst sintering is a known phenomenon for many types of catalysts, where exposure to reducing conditions at elevated temperatures can cause the catalyst to "agglomerate" (or agglomerate) at the surface. Thus, even if the surface area of ​​the underlying surface remains high, catalyst agglomeration (or agglomeration) reduces the amount of available catalytically active sites (as the catalyst sinters and forms lower (or smaller) surface area deposits at the underlying surface). In contrast, it is believed that the cyclical transition between the above states can maintain good dispersion of Ni in the NiAl2O4 catalyst system and maintain catalytic activity. It is believed that further advantage can be gained by using a sufficient amount of excess oxygen during the regeneration step so that all available Ni is oxidized (and back) to NiO and / or NiAl2O4.

[0024] It is noted that by providing both NiO as a catalyst and Al2O3 as a metal oxide support layer as part of the catalyst system, alumina is provided as part of the catalyst system to form NiAl2O4. This reduces or minimizes Ni interaction with alumina that may be present in the monolith composition, and therefore reduces or minimizes degradation of the underlying monolith when exposed to successive high temperature oxidation and reduction cycles.

[0025] Although NiAl2O4 could potentially be used as a structural material to form a monolith, it was unexpectedly discovered that the use of NiAl2O4 as a washcoat for a separate (or separate) structure (e.g., a structure such as a monolith) could maintain catalytic activity for a substantially longer (or significantly longer) time. US Patent Application Publication No. 2020 / 0030778 describes the use of a monolith composed of a combination of NiO and Al2O3 as a structure (or structure) to provide reforming catalytic activity under cyclic high temperature reforming conditions. However, it is believed that the cyclic transition of states for a monolith composed at least in part of NiAl2O4 may contribute to structural failure of the monolith. Since monolith structures typically contain a large number of cells or passages per unit area (or unit area), structural failure of the monolith may result in the cells becoming clogged or even collapsing, resulting in a significant reduction in the available surface area exposed to the reactant gas stream in the reforming environment.

[0026] In some embodiments, NiAl2O4 can be used as the catalyst system when a single catalytic zone is used in the reforming reactor. In some embodiments where multiple catalytic zones are present, NiAl2O4 can be used as the catalyst system in the highest temperature zone, the intermediate temperature zone, or a combination thereof.

[0027] Other Ni-containing catalytic systems NiO supported on yttria-stabilized zirconia (NiO / YSZ) is another example of a Ni-containing catalyst system that can be used for reforming. Although α-Al2O3 is phase stable, it reacts with NiO at high temperatures to form NiAl2O4. However, YSZ is not believed to react with Ni (NiO) at high temperatures. Thus, in the NiO / YSZ system, cyclic oxidation and reduction of Ni to NiO and back to Ni occurs, but redispersion is not believed to occur. However, NiO / YSZ can still provide stable reforming activity in a cyclic high temperature reforming environment. In some embodiments, an intermediate oxide layer of α-Al2O3 may be first deposited as a washcoat on the monolith to aid in the bonding of NiO / YSZ to the monolith. Then, a NiO / YSZ layer may be deposited on the intermediate oxide layer.

[0028] NiO / YSZ represents an alternative type of catalyst system, since YSZ is a phase-stable support that does not react with Ni to form a different material. To determine the stability of the support oxide layer, a first sample of NiO / YSZ was subjected to calcination at 1300 °C and a second sample was steamed in air at 1000 °C. X-ray diffraction was used to confirm that no phase change had occurred. However, based on Brunauer-Emmett-Teller (BET) surface area analysis, the surface area of ​​the NiO / YSZ sample was approximately 53 m before calcination and steaming. 2 / g, and after baking and steaming, it is about 5m 2 / g.

[0029] Yet another example of a Ni-containing catalyst system is NiO on a perovskite oxide, e.g., Sr 0.65 La 0.35 It may be TiO3(SLT) or the like.

[0030] Reforming Catalysts and Metal Oxide Support Layers - General In various embodiments, one option for adding a reforming catalyst to a monolith is to coat the monolith with a mixture of the catalyst (optionally in oxide form) and a metal oxide support layer. For example, a powder of the catalyst oxide and a metal oxide support layer may be used to form a washcoat that is applied to the monolith (or other structure). This can result in a catalyst system in which the catalyst is mixed within or distributed in the metal oxide support layer, as opposed to the catalyst being deposited on top of the metal oxide support layer. In other words, at least a portion of the catalyst system can represent a mixture (or blend) of the catalyst and the support layer. In other embodiments, any convenient technique can be used to deposit or otherwise coat the catalyst system on the monolith or other structure. The weight of the catalyst system provided on the monolith (or other structure) may represent 0.1% to 10% by weight of the total weight of the catalyst system and monolith, alternatively 0.5% to 10% by weight, alternatively 2.0% to 10% by weight, alternatively 0.1% to 6.0% by weight, alternatively 0.5% to 6.0% by weight, alternatively 2.0% to 6.0% by weight.

[0031] In some embodiments, the catalyst system may include a thermally stable (or heat-stable) metal oxide support layer. A thermally stable metal oxide support layer corresponds to a metal oxide that is thermally stable against structural phase changes at temperatures between 800° C. and 1600° C. In some embodiments, such a thermally stable metal oxide support layer is more than 20 μm thick. 2 The thermally stable metal oxide coating can be formed by coating the surface with a metal oxide powder (such as by coating the surface with a washcoat) having a surface area of ​​0.5 m / g or less. For example, the metal oxide powder used to form the thermally stable metal oxide coating can be 0.5 m / g or less. 2 / g~20m 2 / g, or alternatively, 1.0 m 2 / g~20m 2 / g or 5.0m 2 / g~20m 2The catalyst may have a surface area of ​​1000° C. / g. High temperature reforming refers to reforming at temperatures of 1000° C. or more, 1100° C. or more, or 1200° C. or more, such as up to 1500° C. or even higher. In various embodiments, the catalyst may be annealed at temperatures of 1000° C. or more, 1100° C. or more, 1200° C. or more, or 1300° C. or more, such as up to 1600° C. or even higher. Such temperatures may be substantially equivalent to or higher than the peak temperatures to which the catalyst is exposed during the reforming process cycle. Annealing temperatures that are substantially equivalent to the peak temperatures may correspond to annealing temperatures that differ from the peak temperatures by a range (or difference) of 0° C. to 50° C.

[0032] As an example of a thermally stable metal oxide layer, alumina has various phases including α-Al2O3, γ-Al2O3, and θ-Al2O3. Metal powder of α-Al2O3 is 2 In contrast, the γ-Al2O3 and θ-Al2O3 phases have much higher surface areas, and metal powders used in γ-Al2O3 and / or θ-Al2O3 washcoat solutions typically have surface areas of 20 m 2 / g. Phases such as θ-alumina or γ-alumina are conventionally considered to be superior support structures for deposited catalysts because the larger surface area per gram of θ-alumina or γ-alumina allows for the availability of more catalytically active sites than α-alumina. However, phases such as γ-Al2O3 and θ-Al2O3 are not thermally phase stable at temperatures between 800°C and 1600°C. At such high temperatures, phases such as γ-Al2O3 and θ-Al2O3 may undergo a phase transition to a more stable phase. For example, at elevated temperatures, γ-Al2O3 first transforms into Δ-Al2O3 at around 750°C, then Δ-Al2O3 transforms into θ-Al2O3 at around 950°C, and then θ-Al2O3 transforms into α-Al2O3 upon further exposure to elevated temperatures of 1000°C-1100°C. As such, α-Al2O3 is a type of Al2O3 that is thermally phase stable at temperatures between 800°C-1600°C.

[0033] Without being bound by any particular theory, it is believed that such phase changes during exposure to elevated temperatures may contribute to the degradation of the catalyst and / or the structure supporting the catalyst. However, by using a phase-stable support at elevated annealing temperatures and annealing the catalyst at elevated annealing temperatures, the resulting catalyst can substantially maintain its initial catalytic activity level for an extended period of time. It is noted that the initial catalytic activity achieved by depositing a catalyst on a monolith formed from a phase-stable, low surface area per gram material may be lower than if the catalyst were deposited on a similar monolith formed from a material with a high surface area per gram. However, it has been found that such initial activity advantage of the higher surface area is rapidly lost during exposure to cyclic high temperature reforming conditions.

[0034] By way of further example, and without being bound by any particular theory, γ-Al2O3 is a transition alumina that may be viewed as a defect oxyhydroxide, with a spinel-related crystal structure. 8 / 3 □ 1 / 3 It has been formulated as an alumina spinel with defect sites with the formula of AlO4, where □ is an open cation site. 2.5 □ 0.5 O 3.5 (OH) 0.5 Such γ-Al2O3 is thermally unstable with respect to α-Al2O3. Although θ-Al2O3 is more crystalline, has a smaller surface area, and has a lower hydroxide content than γ-Al2O3, θ-Al2O3 contains defect sites (i.e., vacant cation sites) and is thermally unstable with respect to α-Al2O3. Thus, both γ-Al2O3 and θ-Al2O3 have defect sites (□) that can react with multivalent cations (or metal oxides). Both Rh(O) and Ni(O) can react to form denser phases, where Rh and Ni are less chemically accessible for catalytic reactions than their oxide or metallic states. Even in the absence of reactions with Rh or Ni, γ-Al2O3 and θ-Al2O3 are thermodynamically unstable with respect to α-Al2O3 (or more so than α-Al2O3) under high temperature conditions.

[0035] The use of thermally stable metal oxides in a catalyst system in combination with annealing the catalyst system on a monolith at high temperatures can provide unexpected longer term activity benefits and structural stability benefits. Without being bound to any particular theory, when a catalyst system containing a non-thermally stable metal oxide is used as a coating on a monolith, exposing such a catalyst system to a cyclic high temperature reforming environment can result in structural degradation of the catalyst system. Such structural degradation of the catalyst system can contribute to a reduction in available catalytic sites, possibly due to the catalyst becoming embedded in the degraded structure and / or the catalyst additionally sintering or agglomerating as the non-thermally stable metal oxide in the catalyst system transforms to a lower surface area phase. Such structural degradation can be seen, for example, by examining the catalyst system on a monolith after exposure to a cyclic high temperature reaction environment. For conventional catalyst systems, the catalyst system can be easily scraped off from the underlying structure after exposure to a cyclic high temperature reaction environment. Additionally, a substantial reduction in activity may also be observed.

[0036] On the other hand, when a catalyst system including a thermally stable metal oxide is used, the catalytic activity of the catalyst in the catalyst system can be unexpectedly maintained for a long run length with little or no loss of activity. Additionally, after exposure to a cyclic high temperature reforming environment, the catalyst system can be unexpectedly maintained strongly attached or coated to the underlying monolith or other structure. It is noted that because thermally stable metal oxides typically have a relatively small surface area, the initial catalytic activity can be lower than that of a conventional system. This is believed to be because the number of available catalytic sites is initially reduced. However, because thermally stable metal oxides cannot undergo a phase transition when exposed to heat, the catalytic activity of the catalyst system including the thermally stable metal oxide can be maintained. Due to the rapid deactivation of the conventional catalyst or catalyst system, the activity of the conventional catalyst system can rapidly fall below that of the catalyst system using the thermally stable metal oxide.

[0037] Additionally, further improvements can be achieved by annealing the catalyst system and underlying monolith (or other support structure) at temperatures substantially the same as or higher than the peak temperatures to which the support structure is exposed during the reforming process.

[0038] The difference between using a catalyst system that includes a thermally stable metal oxide and one that does not use a thermally stable oxide is that the catalyst system that includes a thermally stable oxide may have improved adhesion to the underlying support structure after exposure to a cyclic high temperature reforming environment.

[0039] The adhesion of the washcoat after operation (or after run) can be quantified by the amount of force required to detach the washcoat. In the prior art, washcoats composed of theta and gamma alumina were detached with minimal force, such as an amount of force similar to a paint brush stroke (weak). In operations involving phase-stable supports, the force required to detach the washcoat is greater (or higher), similar to the force required to scrape off dried epoxy on a glass surface (strong). Because of this difference, only a small amount of washcoat can be detached from the phase-stable materials, while a larger amount of washcoat can be detached from the gamma and theta supports.

[0040] Other methods for evaluating the adhesion of washcoats include, but are not limited to, (i) the thermal cycling method, (ii) the mechanical attrition method, and (iii) the air-knife method. As a non-limiting example, the thermal cycling method may be performed by heating the washcoated material to an elevated temperature in the range of 800°C to 1300°C, cooling to ambient temperature, and repeating such cycles at least five times. As another non-limiting example, the mechanical attrition method (or mechanical attrition test) may be performed by placing the washcoated material in a plastic container and shaking the container on a vibrating table for at least 30 minutes.

[0041] The adhesion of the washcoated material can be determined by subjecting the washcoated structure to thermal cycling conditions and then measuring the desorbed material from the change in mass before and after mechanical attrition testing. Prior to thermal cycling, the weight of the washcoat on the support structure can be determined. The washcoated structure can then be exposed to thermal cycling conditions. The thermal cycling conditions can correspond to the thermal cycling methods described above, or the washcoated structure can be exposed to cyclic high temperature reforming conditions for at least five reaction cycles. Catalyst systems including thermally stable supports can provide good adhesion after mechanical attrition testing, corresponding to retention of 80% or more by weight of the original washcoat, or retention of 90% or more by weight of the original washcoat, or retention of 95% or more by weight of the original washcoat. On the other hand, catalyst systems that do not include a thermally stable support may retain less than 75% by weight of the original washcoat when exposed to cyclic high temperature conditions and subjected to mechanical abrasion testing.

[0042] The catalyst system can be applied to the monolith or other structure, for example, by applying the catalyst system as a washcoat suspension. To form the washcoat suspension, the catalyst system can be added to water, thereby forming an aqueous suspension having a solids content of 10% to 50% by weight. For example, the aqueous suspension can include 10% to 50% solids, 15% to 40% solids, or 10% to 30% solids. Optionally, an acid or base can be added to the aqueous suspension to lower or raise the pH, respectively, to change the particle size distribution of the alumina catalyst and / or binder particles. For example, acetic acid or another organic acid can be added to achieve a pH of 3 to 4. The suspension can then be subjected to a ball mill (or other process) to achieve a desired particle size for the catalyst particles, such as a particle size of 0.5 μm to 5 μm. After milling, the suspension may be stirred until time of use to ensure a substantially uniform distribution of the particles in the solution.

[0043] The washcoat suspension may then be applied to the monolith structure to achieve the desired amount of catalyst (such as nickel or rhodium) provided on the monolith surface. By way of illustration, in one embodiment, a washcoat thickness of 10 microns was achieved by forming a washcoat equivalent to 10% by weight of the monolith structure. Any convenient type of monolith structure may be used to provide a substantial surface area for the support of catalyst particles. The washcoat may be applied to the monolith such that cells are formed whose inner surfaces are coated with the catalyst. One option by which the washcoat may be applied is to immerse or otherwise submerge the monolith in the washcoat suspension.

[0044] After excess washcoat is removed from the cell channels, the catalyst system coated on the monolith may optionally (or selectively) be subjected to drying. Drying may correspond to heating at 100° C. to 200° C. for 0.5 hours to 24 hours. After optional drying, calcination may be performed. In some embodiments, calcination may correspond to heating at 200° C. to 800° C. for 0.5 hours to 24 hours.

[0045] In other embodiments, a high temperature calcination step may be used such that the calcination temperature for the catalytic system coated on the monolith is substantially similar to or higher than the peak temperatures that the monolith will be exposed to during the cyclic high temperature reforming reaction. For monoliths in the high temperature zone, this may correspond to calcining the catalytic system coated on the monolith at temperatures of 800° C. or higher, 1000° C. or higher, 1200° C. or higher, or 1300° C. or higher, such as up to 1600° C., or even higher in some cases. It is noted that if multiple catalytic zones are present, the calcinations may be different for monoliths in different catalytic zones.

[0046] It has been an unexpected discovery that calcination at temperatures similar to or higher than the peak temperatures in the cyclic high temperature reforming process can provide, to an unexpected extent, improved activity for the catalyst system and / or improved adhesion of the catalyst system to the underlying monolith. Without being bound to a particular theory, it is believed that exposing the monolith and deposited catalyst system to high (or elevated) temperatures prior to exposing the catalyst to the cyclic reaction environment can aid in the formation of a stable interface between the catalyst system and the monolith. Such a stable interface can then have improved resistance to the high temperature oxidizing and / or reducing environment of the reforming process, providing improved stability for the retention of the catalyst system on the surface of the monolith.

[0047] In various embodiments, suitable catalytic metals may include, but are not limited to, Ni, Co, Fe, Pd, Rh, Ru, Pt, Ir, Cu, Ag, Au, Zr, Cr, Ti, V, Mo, Nb, and combinations thereof. The catalytic metal may be selected based on the desired type of catalytic activity. Such catalytic metals may be used in the form of metal oxides in the catalyst. In some embodiments, Ni, Rh, Ru, Pd, Pt, Ir, Cu, Co, or combinations thereof may be used as suitable catalytic metals for reforming hydrocarbons to produce hydrogen in the presence of H2O and / or CO2. The weight of the catalytic metal oxide in the catalytic system may range from 0.1 wt% to 70 wt%, or from 1.0 wt% to 60 wt%, or from 2.0 wt% to 50 wt%, based on the total weight of the catalytic system. In some embodiments where the catalytic metal corresponds to a precious metal or noble metal, the weight of the catalytic metal oxide in the catalyst system may range from 0.1 wt % to 10 wt %, from 0.2 wt % to 7.0 wt %, or from 0.5 wt % to 4 wt %.

[0048] The catalytic metal may be selected to provide long-term stable performance in a particular temperature zone of the catalytic bed. This may allow for stable methane conversion (or methane conversion rate), phase stability with the metal oxide support, and reduced or minimized sintering of the catalytic metal. As an example involving three catalytic zones, the catalytic system in the highest temperature catalytic zone (e.g., 800-1250°C), which is exposed to the highest temperatures and some of the most severe temperature swings, may be composed of Ni as the catalytic metal (NiO as the catalytic metal oxide) and Al2O3 as the metal oxide support. It is noted that such a catalytic system may be at least partially converted to NiAl2O4 during a portion (or a portion or part) of the cyclic reforming process. Such a catalytic system may be formed, for example, using a mixture of NiO and Al2O3 as a washcoat on an α-Al2O3 monolith. In such an example, the catalyst system in the intermediate temperature catalytic zone (e.g., 600-1150°C) may be comprised of Ni and Rh as catalytic metals (NiO and Rh2O3 as catalytic metal oxides) and Al2O3 as the metal oxide support. To form such a catalytic system, a mixture of NiO and Rh2O3 as catalytic materials and Al2O3 (optionally and preferably α-Al2O3) as the metal oxide support material may be washcoated onto a monolith comprised of 95 wt% α-Al2O3, 4 wt% SiO2 and 1 wt% TiO2. In such an example, the catalyst system in the low temperature catalytic zone (e.g., 400-1050°C) may be comprised of Rh as catalytic metals (Rh2O3 as catalytic metal oxide) and α-Al2O3 as the metal oxide support. To form such a catalyst system, a mixture of Rh2O3 and α-Al2O3 as catalytic materials may be washcoated onto a monolith composed of 93 wt% α-Al2O3, 5 wt% SiO2, and 2 wt% MgO.

[0049] In various embodiments, suitable metals for the metal oxide support layer in the catalytic system include, but are not limited to, Al, Si, Mg, Ca, Sr, Ba, K, Na, Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Mn, Fe, Ni, Co, Y, La, Ce, and combinations thereof. The metal (or metals) for the metal oxide support may be selected such that the metal oxide support is not substantially converted to metallic form under the reducing conditions that are experienced (or present) in the cyclic reaction environment. As an example, when the catalytic metal oxide is NiO, one option for the metal oxide support is Al2O3, preferably α-Al2O3. Another example of a suitable metal oxide support (optionally combined with NiO as the catalytic metal oxide) is a mixture (or combination) of Al2O3 with SiO2, MgO, and / or TiO2. For such examples, SiO2 may combine (or compound) with Al2O3 to form a mullite phase that may increase resistance to thermal shock and / or mechanical failure. Additionally or alternatively, for such examples, MgO and / or TiO2 may be added. The weight of the metal oxide support in the catalyst bed may range from 1.0 wt% to 40 wt%, or 2.0 wt% to 30 wt%, or 3.0 wt% to 20 wt%, based on the total weight of the monolith of the catalyst bed.

[0050] In various embodiments, the metal oxide support layer (e.g., a thermally stable metal oxide support layer) may correspond to at least one oxide selected from those referred to as corundum, stabilized zirconia, perovskite, pyrochlore, spinel, hibonite, zeolite, and mixtures (or mixtures) thereof. The weight of the metal oxide support may be 1.0 wt.% to 40 wt.%, or 2.0 wt.% to 30 wt.%, or 3.0 wt.% to 20 wt.%, based on the total weight of the monolith and catalyst system.

[0051] One category of metal oxide support layers may represent the traditional refractory oxides commonly used in the formation of supported catalysts. For example, metal oxide supports may be α-Al2O3, LaAlO3, LaAl 11 O 18 , MgO, CaO, ZrO2, TiO2, CeO2, Y2O3, La2O3, SiO2, Na2O, K2O, and mixtures (or admixtures) thereof. This group may be defined herein as oxides that "belong to corundum", even though many of the oxides do not have a corundum lattice structure. For example, CeO2 and MgO both have a halite crystal structure. α-Al2O3 has Al in 2 / 3 of the available octahedral sites. 3+ It consists essentially of oxygen ions arranged in a hexagonal close-packed system with ions densely packed together. LaAlO3, often abbreviated as LaAlO, is an optically transparent ceramic oxide with a distorted perovskite structure. 11 O 18 can be formed through the solid-state reaction of LaAlO3 and α-Al2O3. 11 O 18The plate-like crystals of are particularly useful as metal oxide supports because the catalytic metals can be trapped between the plate-like crystal structures, which inhibits sintering of the slight (or minute) catalytic metals in the active material washcoated onto the monolith of the catalyst bed. Additional examples of oxides selected from the corundum group include, but are not limited to, i) 95 wt. % α-Al2O3 and 5 wt. % SiO2, ii) 93 wt. % α-Al2O3, 5 wt. % SiO2, and 2 wt. % MgO, iii) 94 wt. % α-Al2O3, 4 wt. % SiO2, 2 wt. % MgO, and 1 wt. % Na2O, iv) 95 wt. % α-Al2O3, 4 wt. % SiO2, and 1 wt. % Na2O, based on the weight of the metal oxide support. % of TiO2, v) 7 wt. % of CeO2 and 93 wt. % of MgO, vi) 5 wt. % of CaO and 95 wt. % of α-Al2O3, vii) 5 wt. % of MgO, 5 wt. % of CeO2 and 90 wt. % of α-Al2O3, viii) 20 wt. % of ZrO2 and 80 wt. % of CeO2, ix) 5 wt. % of CeO2, 20 wt. % of ZrO2 and 75 wt. % of α-Al2O3, and x) 6 wt. % of La2O3 and 94 wt. % of α-Al2O3.

[0052] Another category of metal oxide for the metal oxide support layer corresponds to stabilized zirconia. In this description, stabilized zirconia as a metal oxide support is defined as an oxide that includes zirconia (ZrO2, zirconium oxide) and at least one additional oxide that corresponds to Y2O3, CaO, MgO, HfO2, CeO2, SiO2, Sc2O3, La2O3, Al2O3, and mixtures (or mixtures) thereof. Pure ZrO2 undergoes a phase transformation from monoclinic (monoclinic stable at room temperature) to tetragonal (about 1173°C) and then cubic (about 2370°C) structure. If the metal oxide support is formed from pure zirconia, it may break (or be damaged) at a lower temperature as it transforms from tetragonal to monoclinic structure, thereby resulting in volume expansion. To alleviate such problems, pure ZrO2 may be stabilized to a cubic polymorph over a wider temperature range. This is because the crystal lattice is 4+ Some of the ions (with an ionic radius of 0.082 nm) are replaced by slightly larger ions, e.g., Y 3+The doping of zirconia can be achieved by replacing ions from ions (ionic radius of 0.096 nm) and / or other additive oxides. The resulting doped zirconia material is called stabilized zirconia. In the present invention, the weight of the additive oxide in the stabilized zirconia can be 5% to 70% by weight, or 6% to 60% by weight, or 7% to 500% by weight, based on the total weight of the stabilized zirconia composition. A preferred stabilized zirconia is yttria (Y2O3) stabilized zirconia, which is often abbreviated as YSZ. YSZ is a metal oxide support in which the cubic crystal structure of zirconia is made stable at room temperature by the addition of yttria in an amount of 10% to 30% by weight, based on the total weight of the YSZ. Other examples of stabilized zirconia as a metal oxide support include, but are not limited to, i) 10 wt. % Sc2O3 stabilized zirconia (ScSZ), ii) 6 wt. % Sc2O3 and 1 wt. % Al2O3 stabilized zirconia (ScAlSZ), iii) 65 wt. % CeO2 stabilized zirconia (CSZ), and iv) 30 wt. % CeO2 and 20 wt. % Al2O3 stabilized zirconia (CeAlSZ).

[0053] Yet another category of metal oxides for the metal oxide support layer corresponds to perovskites. Perovskites as metal oxide supports are based on a cubic perovskite structure of the general formula (ABO3). The “A” and “B” sites can be doped with a host of metal cations within size constraints. This allows tuning of the properties of the metal oxide support to achieve various objectives. The A-site cations are larger than the B-site cations. The ideal conformation has the B-site cations in 6-fold coordination surrounded by anion octahedra and the A-site cations in 12-fold cuboctahedral coordination. Since the relative ionic size requirements for the stability of the cubic structure are quite stringent, slight buckling and distortion can lead to several lower-symmetry distorted versions in which the coordination number of the A-site cations, the coordination number of the B-site cations, or both are reduced. As such, doped perovskite structures have the formula A x A' 1-x B y B' 1-y O 3-n where A or A' is an element selected from La, Sr, Ba, Ca, Zr and Y, B or B' is an element selected from Mg, Al, Ti, Cr, Mn, Fe, Co, Ni, Cu, Ga, Zr, Y and Zn, both x and y are independently a number selected in the range of 0.0 to 1.0, and n is a number in the range of 0.0 to 0.5. Examples of perovskite structures for the metal oxide support layer include, but are not limited to, SrTiO3, CaTiO3, YAlO3, LaMnO3, LaCoO3, and the like. 0.4 Ni 0.6 O3(LCN), Sr 0.65 La 0.35 TiO3(SLT), BaZr 0.8 Y 0.2 O3 (BZY), La 0.8 Sr 0.2 MnO3(LSM), La0.6 Sr 0.4 Co 0.2 Fe 0.8 O3(LSCF),Ba 0.5 Sr 0.5 Co 0.8 Fe 0.2 O3 (BSCF), La 0.6 Sr 0.4 Co 0.8 Cr 0.2 O3 (LSCC), La 0.6 Sr 0.4 Co 0.8 Mn 0.2 O3 (LSCM), La 0.8 Sr 0.2 FeO3(LSF), and Y 0.1 Ba 0.9 CoO3(YBC) is one example.

[0054] Yet another category of metal oxides for metal oxide support layers corresponds to pyrochlore. Pyrochlore as a metal oxide support is based on the mineral pyrochlore crystal structure of the general formula A2B2O7, where the "A" and "B" species are generally rare earth or transition metal species. The pyrochlore structure is a superstructure derivative of the simple fluorite structure. As such, similar to the perovskite structure, the doped pyrochlore structure has the chemical formula A x A' 2-x B y B' 2-y O 7-n where A or A' is an element selected from La, Sr, Ba, Ca, Gd, Bi, Dy, Tl, Cd and Y, B or B' is an element selected from Zr, Ti, Cr, Mn, Fe, Co, Ni, Ru, Mo and Re, both x and y are numbers independently selected in the range of 0.0 to 2.0, and n is a number in the range of 0.0 to 0.5. Examples of pyrochlore structures for metal oxide support layers include, but are not limited to, La2Zr2O7, Gd 1.9 Ca 0.1 Ti2O 6.9, Bi2Ru2O7, Dy2Ti2O7, Y2Mo2O7, Tl2Ru2O7, and Cd2Re2O7.

[0055] Yet another category of metal oxides for metal oxide support layers corresponds to spinels. Spinels as metal oxide supports are based on the spinel structure of general formula AB2O4, in which the O anions are arranged in a cubic close-packed lattice, with "A" and "B" cations occupying some or all of the octahedral and tetrahedral sites of the lattice. Although the charges of A and B in the prototypical spinel structure are +2 and +3, respectively (A 2+ B 3+ 2O 2- Other combinations are possible, including divalent, trivalent or tetravalent cations, including Mg, Zn, Fe, Mn, Al, Cr, Ti and Si. A and B may be the same metal with different valences, such as the Fe3O4 (Fe 2+ Fe 3+ 2O 2- 4), it is the most abundant of the spinel group. As such, the spinel structure can be represented by the chemical formula AB2O4, where A is an element selected from Mg, Be, Zn, Fe, Ni, Co, Mn, Cu, Ti, Si and mixtures (or combinations) thereof, and B is an element selected from Al, Mg, Fe, Mn, Cr, Co, V and mixtures (or combinations) thereof. Examples of spinel structures for metal oxide supports include, but are not limited to, MgAl2O4, BeAl2O4, ZnAl2O4, FeAl2O4, NiAl2O4, MnAl2O4, (Mg,Fe)Al2O4, CuFe2O4, (Fe,Mn,Zn)(Fe,Mn)2O4, MnFe2O4, MgFe2O4, NiFe2O4, TiFe2O4, (Zn,Fe)Fe2O4, FeCr2O4, NiCr2O4, MgCr2O4, ZnCr2O4, Mn 1.5 Co 1.5 O4, FeV2O4, MgV2O4, (Mg,Fe)2SiO4 and BeMgAl4O8.

[0056] Yet another category of metal oxides for the metal oxide support layer corresponds to hibonite, which has the general formula AB 12 O 19 The present invention is based on the mineral hibonite crystal structure, where "A" is an element selected from Mg, Ca, Sr, Ba, Fe, Ni, Co, La, Ce, Y, and mixtures (or combinations) thereof, and "B" is an element selected from Al, Si, Ti, Zr, Hf, Mg, Ca, and mixtures (or combinations) thereof. Examples of hibonite structures for metal oxide supports include, but are not limited to, CaAl 12 O 19 , (Ca, Ce)(Al, Ti, Mg) 12 O 19 , (Ca, Ce, La) (Al, Ti, Mg) 12 O 19 , and (Fe,Mg)Al 12 O 19 Hibonite (Ca, Ce) (Al, Ti, Mg) 12 O 19 The plate-like crystals can be useful as metal oxide supports since catalytic metals can be trapped between the plate-like crystal structures, which can suppress sintering of catalytic metals in the active metal washcoated onto the monolith of the catalyst bed.

[0057] Yet another category of metal oxides for the metal oxide support layer corresponds to zeolites. In the present description, zeolites as metal oxide supports refer to aluminosilicate materials composed of Si, Al, O, H, optionally further containing metals including Na, Ca, K, Mg, Ti, Sn, Zn and mixtures thereof, which are members of a family of microporous solids known as molecular sieves. The term molecular sieve refers to the specific property of such materials to selectively remove (or filter) molecules primarily based on a size exclusion process. This is due to a highly regular pore structure of molecular dimensions. The maximum size of molecules or ionic species that can enter the pores of a zeolite is controlled by the dimensions of the channels. These are conventionally defined by the ring size of the aperture, e.g., "8-ring" refers to a closed loop consisting of eight tetrahedrally coordinated silicon (or aluminum) atoms and eight oxygen atoms. Such rings are not necessarily perfectly symmetrical due to a variety of causes including distortion induced by the bonds between the units required to form the overall structure, or the coordination of some of the oxygen atoms of the rings to cations within the structure. Zeolites as metal oxide supports in the present invention include over 245 unique frameworks (or structures) formed on an industrial scale and over 40 naturally occurring zeolite frameworks (or structures). Some examples of zeolites that can be used as metal oxide supports include USY zeolite, L zeolite, mordenite, ferrierite, beta zeolite, ZSM-5, MCM-68, and mixtures (or combinations) thereof. Such zeolites are particularly useful as metal oxide supports for active materials for the low temperature catalytic zone of the RFR. Some zeolite frameworks (or structures) are known to be structurally stable up to about 750° C. The stable micropores of zeolites provide extensive surface area for catalytic metal dispersion.Other examples of zeolites as metal oxide supports include various types of faujasites, which may include faujasite-Na, faujasite-Mg, and faujasite-Ca. The faujasites all have the same basic formula (Na2,Ca,Mg). 3.5 [Al7Si 17 O 48 ] 32(H2O) and vary in the amount of sodium, magnesium and calcium. Faujasite, like other zeolites, is synthesized from an alumina source, such as sodium aluminate, and a silica source, such as sodium silicate. Other aluminosilicates, such as kaolin, are also used. The components are dissolved in a basic environment, such as aqueous sodium hydroxide, and crystallized at 70°C to 300°C. After crystallization, faujasite is in the sodium form and can be ion-exchanged with ammonia to improve stability. The ammonium ions are later removed by calcination, which puts the zeolite in its acidic form. Depending on the silica-to-alumina ratio of the framework (or structure), synthetic faujasite zeolites are divided into X and Y zeolites. In X zeolites, the silica-to-alumina ratio is 2-3, whereas in Y zeolites, the ratio is 3 or more. The negative charge of the framework is balanced by the positive charges of the cations in the non-framework sites. Such zeolites have ion exchange, catalytic and adsorption properties. The stability of the zeolite increases with the silica to alumina ratio (or ratio of silica to alumina) of the framework. It is also influenced by the type and amount of cations located in the non-framework sites. For catalytic cracking, Y zeolites are often used in rare earth-hydrogen exchanged form. By using thermal, hydrothermal or chemical methods, some of the alumina can be removed from the Y zeolite framework, resulting in high silica Y zeolites. Such zeolites are used in cracking and hydrocracking catalysts. Complete delamination results in faujasite-silica. Yet another example of a zeolite that can be used as a metal oxide support layer is of the formula (Ca,Na2,K2,Mg)Al2Si4O 12Chabazite, with 6H2O. Recognized varieties include chabazite-Ca, chabazite-K, chabazite-Na, and chabazite-Sr, depending on the prominence of the cations represented. Chabazite typically crystallizes in the triclinic crystal system with rhombohedral shaped crystals.

[0058] Structures (monoliths) for supported catalytic systems One purpose of using a monolith or other support structure in a reforming environment is to increase the available surface area to hold the deposited catalyst / catalyst system. To accomplish this, some monoliths correspond to structures with many (or many) cells or passages that allow gas flow through the monolith. Since each individual cell provides a surface area for catalyst deposition, the inclusion of a large number of cells or passages per unit area can substantially increase the available surface area for the catalyst.

[0059] In general, the monolith or other structure used to support the catalyst / catalyst system may be formed from a material of formula PQ, where P may be at least one metal selected from the group consisting of Al, Si, Mg, Ca, Sr, Ba, K, Na, Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Mn, Fe, Ni, Co, Y, La, Ce, and mixtures thereof. Q denotes an oxide. Thus, the monolith material (PQ) is a metal oxide.

[0060] In some preferred embodiments, the metal oxide may correspond to aluminum oxide (aka alumina), Al2O3. The preferred Al2O3 in the present invention is α-Al2O3. While α-Al2O3 is the preferred crystalline phase, there is another phase that includes sodium oxide (Na2O), an impurity that is sometimes unavoidable in α-Al2O3, namely Na2O(Al2O3). 11 Or NaAl5O8 may be present.

[0061] Optionally, the monolith or structure material (PQ) may be α-Al2O3 containing at least one additive oxide selected from the group consisting of SiO2, MgO, CaO, TiO2, Na2O, KO or mixtures (or combinations) thereof. The weight of the additive oxide in the monolith material composition may range from 0.1% to 15% by weight, alternatively from 0.1% to 10% by weight, alternatively from 2.0% to 8.0% by weight, based on the total weight of the monolith material composition. As non-limiting examples, the monolithic material (PQ) may be: i) 95 wt.% α-Al2O3 and 5 wt.% SiO2; ii) 93 wt.% α-Al2O3, 5 wt.% SiO2, and 2 wt.% MgO; iii) 93 wt.% α-Al2O3, 4 wt.% SiO2, 2 wt.% MgO, and 1 wt.% Na2O; and iv) 95 wt.% α-Al2O3, 4 wt.% SiO2, and 1 wt.% TiO2.

[0062] In other embodiments, the monolithic material (PQ) may be partially or substantially (or predominantly) composed of non-alumina-based oxides. As non-limiting examples, the monolithic material (PQ) may be silica (SiO2), magnesia (MgO), ceria (CeO2), titania (TiO2), zirconia (ZrO2), cordierite (2MgO 2Al2O32SiO2), mullite (3Al2O32SiO2), aluminum titanate (Al2TiO5), magnesium aluminate (MgAl2O4), calcium stabilized zirconia (CaO-ZrO2), magnesium stabilized zirconia (MgO-ZrO2), yttria stabilized zirconia (Y2O3-ZrO2), yttria (Y2O3), barium zirconate (BaZrO3), strontium zirconate (SrZrO3), and mixtures (or combinations) thereof. Further examples of potential monolithic materials include SiC, Si3N4, yttrium stabilized zirconia, and Al2TiO5 ceramics. It is noted that SiC and Si3N4 do not follow the PQ structural formula.

[0063] In some embodiments, the monolithic material (PQ) may further comprise supplemental components. Such supplemental components may aid in easy extrusion and represent additional structural components within the monolithic material composition. For example, the monolithic material composition may further comprise one or more silicates comprising a metal selected from the group consisting of Al, Si, Ca, Mg, K, Na, Y, Zr, Hf, Ti, Cr, Mn, Fe, Ni, Co, and mixtures thereof. One example is bentonite, which is an aluminum phyllosilicate clay based on montmorillonite. Different types of bentonite are each named after the respective major elements, such as potassium (K), sodium (Na), calcium (Ca), and aluminum (Al). For example, the chemical formula of sodium bentonite is Al2H2Na2O 13 Si4. Although some hydroxyl ions (OH-) may be present in silicates, under high temperature calcination and sintering conditions, such hydroxyl groups can be converted to the oxide form. Yet another example is talc, which has the formula Mg3Si4O 10 It is a clay mineral composed of hydrated magnesium silicate of (OH)2. Due to its characteristics of elementary cleavage and non-uniform flat fractures, it is foliated in two-dimensional plate morphology, which has advantages in the extrusion of monolithic materials.

[0064] In various embodiments, the monolith or other structure providing the surface for the reforming catalyst system may be prepared by manufacturing methods such as, but not limited to, conventional ceramic powder manufacturing and processing methods, such as mixing, milling, degassing, kneading, pressing, extruding, casting, drying, calcining, and sintering. The starting materials may represent suitable ceramic powders and organic binder powders in appropriate volumetric ratios. Certain process steps may be controlled or adjusted to obtain desired grain sizes and porosity ranges and performance characteristics, including by including various manufacturing, property, conditioning, and processing additives and agents as are commonly known to those skilled in the art. For example, two or more oxide powders may be mixed in the presence of an organic binder and one or more suitable solvents for a time sufficient to substantially disperse the powders in one another. As another example, precursors of the oxides present in the monolith may be dissolved in water in the desired ratios, sprayed, dried, and calcined to form a mixed powder. Such precursors include, but are not limited to, chlorides, sulfates, nitrates, and mixtures (or combinations) thereof. The calcined powder may be further mixed in the presence of an organic binder and a suitable solvent, thereby creating a mixed "dough". The mixed material "dough" may then be placed in a die or form, extruded, and dried or otherwise formed into the desired shape. The resulting "green body" may be sintered (or fired) at a temperature range of about 1200°C to 1700°C for at least 10 minutes, such as 10 minutes to 10 hours, and in some cases 10 minutes to 48 hours or longer.

[0065] The sintering operation may be carried out in an oxidizing, reducing or inert atmosphere, at ambient pressure or under reduced pressure or vacuum. For example, the oxidizing atmosphere may be air or oxygen, the inert atmosphere may be argon, and the reducing atmosphere may be hydrogen, CO / CO2 or H2 / H2O mixtures. The sintered body is then cooled, typically to ambient conditions. The cooling rate may be controlled to provide a desired set of grain and pore structure and performance characteristics for a particular composition.

[0066] In some embodiments, the monolith material (PQ) may further comprise an intermediate bonding layer. The intermediate bonding layer may be applied to the monolith surface prior to washcoating with an active material comprising a metal oxide support and a catalytic metal. The intermediate bonding layer provides better adhesion to the washcoated active material. The intermediate bonding layer is a metal oxide, (M). x O y where (M) is at least one metal selected from the group consisting of Al, Si, Mg, Ca, Sr, Ba, K, Na, Ti, Zr, Hf, V, Nb, Ta, Cr, Mo, W, Mn, Fe, Ni, Co, Y, La, Ce, and mixtures (or combinations) thereof. Aluminum oxide (aka alumina), Al2O3, is a preferred metal oxide for the bond layer. As an example of how to form an intermediate bond layer, the selected metal oxide (M) x O y may be dispersed in a solution, thereby forming a slurry. The slurry may then be washcoated onto the monolith. The selected metal oxide (M) x O y The washcoated monolith is dried and sintered at a temperature ranging from 1100°C to 1600°C to form an intermediate bonding layer.

[0067] It has been found that limiting the maximum porosity (or porosity) in the final sintered body tends to effectively limit, if not practical, the interconnectivity of the pore spaces with each other to an extent that increases or maximizes the volumetric heat capacity of the sintered body. The porosity range for the monolith or other structure may depend on the performance characteristics of the final component desired, but is within a range defined by one or more minimum porosity values ​​and one or more maximum porosity values, or any set of values ​​not specifically recited between the minimum and maximum. Examples of suitable porosity values ​​are 0% to 20% porosity by volume, or 0% to 15% porosity by volume, or 0% to 10% porosity by volume, or 0% to 5% porosity by volume.

[0068] The sintered monoliths and / or other formed ceramic structures may have any convenient shape suitable for use as a surface for receiving a catalyst or catalytic system. An example of a monolith may be an extruded honeycomb monolith. A honeycomb monolith may be an extruded structure with thin walls and many (e.g., a plurality, meaning more than one) small gas flow passages or routes arranged parallel therebetween. Small reactors may contain a single monolith, while larger reactors may contain many monoliths, and even larger reactors may be largely (or substantially) filled with many honeycomb monolith arrangements. Each monolith is formed by extruding a monolith block and may have a shape (e.g., square, triangular, or hexagonal) in cross section, and may be formed to have the shape of such blocks stacked on top of each other in two or three dimensions, top to bottom, front to back, and side to side. Monoliths may be attractive as reactor internals because they offer high heat transfer capacity with minimal pressure drop.

[0069] In some embodiments, the honeycomb monolith may be characterized as having an open frontal area or geometric void volume of 25% to 55%, a passage density of 50 to 2000 holes or cells per square inch (CPSI), or a passage density of 100 to 900 cells per square inch, or a passage density of 100 to 600 cells per square inch. For example, in one embodiment, the passages (or conduits) may have a diameter / characteristic cell side length of only a few millimeters, such as on the order of millimeters. A reactor media element, such as a monolith or alternative bed media, may be characterized as having a 50 ft2 of space based on the volume of the first reactor used to carry the reactants. -1 ~3000ft -1 (~0.16km -1 From ~10km -1 ) or 100ft -1 ~2500ft -1 (~0.32km -1 From ~8.2km -1 ) or 200ft -1 ~2000ft -1 (~0.65km -1 From ~6.5km -1 ) in the range of 100-150° C. Such relatively large surface area per unit volume values ​​can aid in achieving relatively rapid changes in temperature through (or across) the reactor (e.g., such as generally represented by a relatively steep slope of the graph of the exemplary temperature gradient profile shown in FIG. 1(a) or FIG. 1(b)).

[0070] The reactor media component has a high volumetric heat transfer coefficient (e.g., 0.02 cal / cm 3 s℃ or higher, or 0.05cal / cm 3s℃ or above, or 0.10cal / cm 3 s °C or higher); have low resistance to flow (low pressure drop); have an operating temperature range that matches (or coincides or matches) the highest temperature encountered in regeneration; have high thermal shock resistance, and / or have a high bulk heat capacity (e.g., 0.10 cal / cm 3 s℃ or above, or 0.20cal / cm 3 s °C or higher). As well as high surface area values, such relatively high volumetric heat transfer coefficient values ​​and / or other properties may aid in achieving relatively rapid changes in temperature through (or across) the reactor (e.g., as generally represented by the relatively steep slopes of the graphs of the exemplary temperature gradient profiles shown in Figures 1(a) and 1(b) of Figure 1). The foregoing values ​​are averages based on the volume of the reactor used to transport reactants.

[0071] In various embodiments, an adequate heat transfer rate (or thermal conductivity or rate) may be characterized by a heat transfer parameter (ΔTHT) below 500° C., below 100° C., or below 50° C. The parameter ΔTHT herein is the ratio of the bed average volumetric heat transfer rate required for recuperation to the volumetric heat transfer coefficient hv of the bed. The volumetric heat transfer rate (e.g., cal / cm) that is sufficient for recuperation is 3 sec) is calculated by multiplying the gas flow rate (e.g., g / sec) by the gas heat capacity (e.g., cal / g °C) and the desired end-to-end temperature change (excluding any reaction, e.g., °C) by the volume (e.g., cm) of the reactor (or portion of the reactor) traversed by the gas. 3 The volumetric heat transfer coefficient of the bed, hv, can be calculated by dividing the volumetric heat transfer coefficient by an area-based coefficient (e.g., cal / cm 2 s℃) and specific surface area for heat transfer (av, e.g. cm 2 / cm 3 ) and is often referred to as the wetted area of ​​the packing.

[0072] Multiple Zone Catalyst Systems In some embodiments, the catalyst system may use multiple (or a number or a plurality of) catalysts to further improve the reforming. In such embodiments, different regions of the reaction zone may contain different catalysts. Due to the nature of the reverse flow reactor, a temperature profile may be created within the reactor such that one reaction zone (or some reaction zones) is at a higher temperature while another reaction zone (or some reaction zones) is at a lower temperature. By using a catalyst system that includes multiple catalysts, the catalysts in the reaction zones may be selected to provide improved activity versus temperature in the reaction zone based on the temperature profile.

[0073] Figure 4 shows an example of a temperature profile obtained during steam reforming of a methane feed in a 12-inch (~30 cm) pilot-scale reverse-flow reactor. The pilot-scale reactor contained multiple catalyst zones, with the first zone (hotter zone) containing a nickel-based catalyst while the second zone (cooler zone) contained a rhodium-based catalyst. For the pilot reactor used to generate the temperature profile in Figure 4, the reforming zone of the reactor corresponds to 4-12 inches of the reactor. The 0-4 inch portion of the reactor corresponds to the inlet end of the reactor for the regeneration gas stream. The point (or location) approximately 4 inches into the reactor corresponds to the point (or location) where combustion of the regeneration gas stream occurs. As shown in Figure 4, the temperature profile at the end of the regeneration step is higher than the temperature profile at the end of the reforming step. This is due to the cycle of consuming heat during reforming and replenishing heat during regeneration. However, the general shape of the temperature profile is similar after both the reforming and regeneration steps, and the general shape of the temperature profile appears to be present at intermediate times as well.

[0074] Based on the example temperature profile shown in Figure 4, during operation of a reverse flow reactor for reforming, certain zones in the reactor will be at higher temperatures while other zones of the reactor will be at intermediate or lower temperatures. Because the locations of the high temperature, intermediate and low temperature zones are relatively stable during a reaction cycle, it has been found that further advantages can be obtained by using a catalyst that has improved activity for the type of temperature in a given zone of the reactor.

[0075] When multiple catalytic zones are used in the reactor, any convenient number of zones may be used. Thus, when multiple catalytic zones are present, the number of catalytic zones may be from 2 zones to 10 zones, or from 2 zones to 6 zones, or from 3 zones to 10 zones, or from 3 zones to 6 zones. Of course, it is also possible to have a single catalytic zone, and in some embodiments, the number of catalytic zones may be from 1 zone to 10 zones, or from 1 zone to 6 zones.

[0076] The temperature profile of FIG. 4 may be used to illustrate the concept of using multiple catalytic zones. One way to organize catalytic zones having a temperature profile similar to that of FIG. 3 may be to use two zones corresponding to a high temperature catalytic zone and a low temperature catalytic zone. For example, for a reactor used to generate the temperature profile of FIG. 4, 4-6 inches (or 4-7 inches) of the reactor may represent the high temperature zone and 6-12 inches (or 7-12 inches) of the reactor may represent the low temperature zone. Another option may be to use three zones, with a high temperature zone, a medium temperature zone, and a low temperature zone. For example, for a reactor used to generate the temperature profile of FIG. 4, 4-6 inches may represent the high temperature zone, 6-9 inches may represent the medium temperature zone, and 9-12 inches may represent the low temperature zone. Still other options of organizing the reactor into two zones, three zones, four zones, or any other convenient number of zones are also available depending on the desired catalyst system and temperature profile of the reactor.

[0077] In some embodiments, when different catalyst systems are used in different zones, the zones can be characterized based on the peak temperatures in the different zones. For example, the peak temperature in a first zone can be 100° C. or more, or 200° C. or more, or 300° C. or more higher than the peak temperature in a second zone, and such difference can be 700° C. or even more. The peak temperature in a zone refers to the point (or location) in the zone that has the highest average temperature at the end (or terminal, termination or completion) of the regeneration step. The average temperature at the end (or terminal, termination or completion) of the regeneration cycle can be calculated based on averaging the temperatures at the end (or terminal, termination or completion) of the regeneration step over 10 full cycles.

[0078] Changes in regeneration process It is noted that NiO / NiAl2O4 is an example of a catalytic system in which the catalytic metal may be converted from an oxidized state to a reduced metallic state under high temperature reforming conditions. To the extent that such reduction of the catalytic metal occurs, it has been found that it is desirable to return the catalytic metal to a fully oxidized state prior to the next reforming step.

[0079] In various embodiments, returning the reduced metals to a fully oxidized state prior to the next reforming step may be accomplished by increasing the amount of excess oxygen used during the regeneration (combustion) step used to add heat to the reactor. Conventionally, the amount of oxygen used during the regeneration step is slightly more than the stoichiometric amount required for complete combustion of the fuel used during the regeneration step. In the present description, 100% of the molar stoichiometric amount of oxygen is defined as the stoichiometry of oxygen required for the combustion of all fuel introduced during the regeneration step. An amount of oxygen greater than 100% of the molar stoichiometric amount of oxygen corresponds to excess oxygen. For example, 120% of the molar stoichiometric amount of oxygen corresponds to using 20% ​​more moles than are required for stoichiometric combustion. This can be referred to as a 20% excess molar amount of oxygen. Due to the large flow volumes and high superficial gas velocities already present, the addition of additional gas to either the regeneration or reforming steps is generally undesirable. However, increasing the amount of excess oxygen used in the regeneration step can improve reforming activity by allowing reduced catalytic metals formed in the reforming step to be oxidized during the regeneration step. In various embodiments, the amount of oxygen used in the regeneration step can correspond to 120% or more of the molar stoichiometric amount, or 125% or more, or 130% or more, or 140% or more, or up to 200% or more. This corresponds to 20% or more, or 25% or more, or 30% or more, or 40% or more of excess molar oxygen, for example up to 100% or more.

[0080] Process Example - Reverse Flow Reforming and Regeneration In various embodiments, the reforming of hydrocarbons may be carried out under steam reforming conditions in the presence of H2O in the reaction environment, under dry reforming conditions in the presence of CO2, or under conditions in the presence of both H2O and CO2. As a general overview of operation in a swing reactor reforming, such as a reverse flow reactor, a portion of the regeneration step or reaction cycle may be used to provide heat to the reactor. Reforming may then occur in the reactor during a portion of the reforming step or cycle, while the reforming reaction consumes heat provided in the reactor regeneration step. In the reactor regeneration, fuel and oxidant are introduced into the reactor at the regeneration end of the reactor. The beds and / or monoliths in the regeneration section of the reactor typically do not contain a catalyst for reforming, although they may absorb heat. Heat is transferred from the regeneration section to the fuel and oxidant as they pass through the regeneration section. Combustion does not occur immediately, instead the location of combustion is controlled to occur in the middle section of the reactor. The flow of reactant continues during the regeneration step, resulting in additional heat from combustion being transferred to the reforming end (or reforming terminal) of the reactor.

[0081] After a sufficient time has elapsed, the combustion reaction is stopped. Remaining combustion products and / or reactants may be optionally purged. The reforming step or part of the reaction cycle may then be initiated. Reactants for reforming may be introduced into the reforming end of the reactor, thus providing an effective counter-flow to the flow in the regeneration. The beds and / or monoliths in the reforming section of the reactor may include a catalyst for reforming. In various embodiments, at least a portion of such catalyst may correspond to a catalyst formed from a ceramic composition as described herein. As reforming occurs, heat introduced into the reforming zone during combustion may be consumed by the endothermic reforming reaction. After leaving the reforming zone, the reformed products (and unreacted reactants) are no longer exposed to the reforming catalyst. As the reformed products pass through the regeneration zone, heat may be transferred from the products to the regeneration zone. After a sufficient amount of time has elapsed, the reforming process may be stopped, the remaining reformed products may optionally be collected or purged from the reactor, and the cycle may begin again with the regeneration step.

[0082] The reforming reactions carried out in the reactor may correspond to the reforming of methane and / or other hydrocarbons, using steam reforming in the presence of HO; using dry reforming in the presence of CO; or using "bi" reforming in the presence of both HO and CO. Example stoichiometries for steam, dry and "bi" reforming of methane are shown in equations (1)-(3). (1) Dry reforming: CH4 + CO2 = 2CO + 2H2 (2) Steam reforming: CH4 + H2O = CO + 3H2 (3) "Bi" reforming: 3CH4 + 2H2O + CO2 = 4CO + 8H2

[0083] As shown in equations (1)-(3), dry reforming can have a lower H2 to CO ratio than steam reforming. A steam-only reforming reaction can typically have a H2 to CO ratio of about 3, such as 2.5-3.5. In contrast, a reforming reaction carried out in the presence of CO2 can have a substantially lower ratio, perhaps approaching or even below 1.0. By using a combination (or combination) of CO2 and H2O in reforming, the reforming reaction can potentially be controlled to have a wide variety of H2 to CO ratios in the resulting syngas.

[0084] It is noted that the ratio of H2 to CO in the syngas may depend on the water gas shift equilibrium. Although the above stoichiometries indicate approximately 1 or approximately 3 for dry reforming and steam reforming, respectively, the equilibrium amounts of H2 and CO in the syngas may differ from the reaction stoichiometry. The equilibrium amounts may be determined based on the water gas shift equilibrium, which relates the concentrations of H2, CO, CO2, and H2O based on the following reaction: (4)H2O+CO<=>H2+CO2

[0085] Most reforming catalysts, such as rhodium and / or nickel, may act as water gas shift catalysts. Thus, if the reaction environment that produces H2 and CO contains H2O and / or CO2, the initial stoichiometry from the reforming reaction may be altered based on the water gas shift equilibrium. Such equilibrium is also temperature dependent, with higher temperatures favoring the production of CO and H2O. It is noted that higher temperatures may improve the rate at which equilibrium is reached. As a result, being able to perform reforming reactions at elevated temperatures may potentially provide several advantages. For example, instead of performing steam reforming in an environment with excess H2O, CO2 may be added to the reaction environment. This may allow both a lower ratio of H2 to CO that would result based on the dry reforming stoichiometry, as well as a lower ratio of H2 to CO that would result based on the water gas shift equilibrium. Alternatively, if a higher CO to H2 ratio is desired, CO2 may be removed from the environment and the ratio of H2O to CH4 (or other hydrocarbons) may be controlled to produce the desired type of syngas. This could potentially allow for the production of syngas with H2 to CO ratios of 0.1-15, or 0.1-3.0, or 0.5-5.0, or 1.0-10, by selecting the appropriate amounts of feed components.

[0086] The reforming reactions shown in equations (1)-(3) are endothermic reactions. One of the challenges in commercial scale reforming can be providing heat to efficiently carry out the reforming reactions while reducing or minimizing the introduction of additional components to the desired synthesis gas product. Cyclic reaction systems, such as reverse flow reactor systems, can provide the desired heat by having a cycle that includes a reforming step and a regeneration step. In the regeneration step, combustion can occur in a selected area of ​​the reactor. Gas flow during regeneration can assist in transferring such heat from the combustion zone to additional parts of the reforming zone in the reactor. The reforming step can be a separate step in the cycle, whereby the incorporation of products from combustion into the reactants and / or products from reforming can be reduced or minimized. The reforming step can consume heat, so that the temperature of the reforming zone can be reduced. As the product from the reforming passes through the reactor, the reforming product may pass through a second zone lacking reforming or water gas shift catalyst. This may allow the reaction product to be cooled prior to exiting the reactor. Heat transferred from the reforming product to the reactor may be used to increase the temperature of the reactor for a subsequent combustion or regeneration step.

[0087] One common source of methane is natural gas. In some applications, natural gas containing associated hydrocarbons and impurity gases may be used as a feed for the reforming reaction. The natural gas feed may be sweetened and / or dehydrated natural gas. Natural gas typically contains various concentrations of associated gases such as ethane and other alkanes, preferably at lower concentrations than methane. The natural gas feed may contain impurities such as H2S and nitrogen. More generally, the hydrocarbon feed for reforming may contain any convenient combination of methane and / or other hydrocarbons. Optionally, the reforming feed may contain hydrocarbonaceous compounds such as alcohols or mercaptans that are similar to hydrocarbons but contain one or more heteroatoms different from carbon and hydrogen. In some embodiments, the additional components present in the feed may represent impurities such as sulfur that may be adsorbed onto the catalyst monolith in the reduction cycle (e.g., reforming step). Such impurities may be oxidized in the next cycle to form sulfur oxides and reduced by the release of additional sulfur-containing components (or other impurity-containing components) into the reaction environment.

[0088] In some embodiments, the feed for reforming contains 5 wt. % or more of C hydrocarbons, such as ethane or propane, based on the total weight of the hydrocarbons in the feed for reforming. 2+ Component or 10% by weight or more, or 15% by weight or more, or 20% by weight or more, and up to 50% by weight or more of C such as ethane or propane 2+It is noted that nitrogen and / or other gases that are non-reactive in the combustion environment (e.g., H2O, CO2, etc.) may be present in the feed for reforming. In embodiments that correspond to an on-board reforming environment, such non-reactive products may be optionally introduced in the feed, for example, based on recycling of exhaust gases fed into the reformer. Additionally or alternatively, the feed for reforming may contain 40% by weight or more of methane, or 60% by weight or more, or 80% by weight or more, or 95% by weight or more of methane, for example, in embodiments having a feed that is substantially (or predominantly) composed of methane (e.g., a feed that is 98% by weight or more composed of methane). In embodiments where the reforming corresponds to steam reforming, the molar ratio of steam molecules to carbon atoms in the feed may be between 0.3 and 4.0. It is noted that methane has one carbon atom per molecule and ethane has two carbon atoms per molecule. In an embodiment where the reforming corresponds to dry reforming, the molar ratio of CO2 molecules to carbon atoms in the feed may be between 0.05 and 3.0.

[0089] Within the reforming zone of a reverse flow reactor, the temperature may vary across the zone due to the nature of how heat is added to the reactor and / or due to the kinetics of the reforming reaction. The hottest part of the zone is typically found near the middle of the reactor. Such middle part may be referred to as the mixing zone where combustion is initiated during regeneration. At least a portion of the mixing zone may represent a portion of the reforming zone if the monolith with the reforming catalyst extends into the mixing zone. As a result, the location where combustion starts during regeneration may typically be near the end of the reforming zone in the reactor. As one moves from the center of the reactor to the end of the reactor, the temperature decreases. As a result, the temperature at the beginning of the reforming zone (at the end of the reactor) may be lower (or may be cooled) than the temperature at the end of the reforming zone (at the middle of the reactor).

[0090] As reforming reactions occur, the temperature in the reforming zone may be reduced. The rate (or rate of reduction) of temperature may be related to the kinetic factors of the amount of hydrocarbons available for reforming and / or temperature at a given location in the reforming zone. As the reforming feed moves through the reforming zone, reactants in the feed may be consumed, thereby reducing the amount of reforming occurring at downstream locations. However, an increase in the temperature of the reforming zone as reactants move across the reforming zone may lead to an increase in the reaction rate.

[0091] At approximately 500° C., the reaction rate for reforming may be sufficiently reduced that no or little additional reforming occurs. As a result, in some embodiments, as the reforming reaction proceeds, the beginning of the reforming zone may cool sufficiently to effectively stop the reforming reaction in a portion of the reforming zone. This may move the location in the reactor where reforming begins to a portion further downstream relative to the beginning of the reforming zone. If a sufficient portion of the reforming zone has a temperature below 500° C., or below 600° C., the reforming step in the reaction cycle may be stopped to allow regeneration. Alternatively, based on the amount of heat introduced into the reactor in the regeneration, the reforming portion of the reaction cycle may be stopped based on the amount of reaction time such that the amount of heat consumed during reforming (and heat lost to the environment) approximately balances the amount of heat added during regeneration. After the reforming process is stopped, the syngas product still remaining in the reactor may optionally be recovered prior to the start of the regeneration step of the reaction cycle.

[0092] The regeneration process may then begin. During regeneration, fuel, such as methane, natural gas, or H2, and oxygen may be introduced into the reactor and burned. The location at which the fuel and oxidant are allowed to mix may be controlled in any convenient manner, for example by introducing the fuel and oxidant through separate channels. By delaying combustion during regeneration until the reactants reach the center of the reactor, the non-reforming end of the reactor may be kept at a lower (or cooler) temperature. This may result in a temperature peak in the middle of the reactor. The temperature peak may be located in the part of the reactor that contains the reforming catalyst. During the regeneration cycle, the temperature of the reforming reactor may be raised sufficiently to allow reforming in the reforming part of the cycle. This may result in peak temperatures in the reactor of 1100°C or higher, or 1200°C or higher, or 1300°C or higher, and potentially even higher.

[0093] The relative time lengths and reactant flow rates for the reforming and regeneration portions of the process cycle may be selected to balance the heat provided during regeneration with the heat consumed during reforming. For example, one option may be to select the reforming step to have a similar length as the regeneration step. Based on the flow rates of the hydrocarbons, H2O and / or CO2 during the reforming step, the endothermic heat demand of the reforming reaction may be determined. Such heat demand may then be used to calculate the flow rates for the combusted reactants in the regeneration step. Of course, in other embodiments, the heat balance between reforming and regeneration may be determined in other ways, such as by determining the desired flow rates of the reactants and selecting the cycle length such that the heat provided by regeneration is balanced with the heat consumed during reforming.

[0094] In addition to providing heat, the reactor regeneration step in the reaction cycle may allow for the removal of coke from the catalyst in the reforming zone. In various arrangements, one or more types of catalyst regeneration may potentially occur in the regeneration step. One type of catalyst regeneration may correspond to removing coke from the catalyst. During reforming, a portion of the hydrocarbons introduced into the reforming zone may form coke instead of forming CO or CO2. Such coke may potentially block access to catalytic sites (e.g., metal sites, etc.) of the catalyst. In some embodiments, the formation rate may be increased in parts of the reforming zone exposed to higher temperatures (e.g., parts of the reforming zone exposed to temperatures of 800° C. or higher, or 900° C. or higher, or 1000° C. or higher). In the regeneration step, oxygen may be present as the temperature of the reforming zone is increased. At least a portion of the coke generated during reforming may be removed as CO or CO2 at the temperature achieved during regeneration.

[0095] Due to temperature differences (or variations) across the reactor, several options may be used to characterize the temperature in the reactor and / or in the reforming zone of the reactor. One option for characterizing the temperature may be based on the average bed or monolith temperature in the reforming zone. In a realistic setting, determining the temperature in the reactor requires the presence of a measurement device such as a thermocouple. Rather than attempting to measure the temperature in the reforming zone, the average (bed or monolith) temperature in the reforming zone may be defined based on the average of the temperature at the beginning of the reforming zone and the temperature at the end (or terminal, termination or completion) of the reforming zone. Another option may characterize the peak temperature in the reforming zone after a regeneration step in the reaction cycle. In general, the peak temperature may occur at or near the end (or terminal, termination or completion) of the reforming zone and may depend on where combustion is initiated in the reactor. Yet another option may characterize the temperature difference at a given location in the reaction zone at different times in the reaction cycle. For example, a temperature difference may be determined between the temperature at the end (or end, termination or completion) of the regeneration step and the temperature at the end (or end, termination or completion) of the reforming step. Such a temperature difference may be characterized at the location of the peak temperature within the reactor, at the inlet of the reforming zone, at the outlet of the reforming zone, or at any other convenient location.

[0096] In various embodiments, reaction conditions for reforming hydrocarbons include an average reforming zone temperature of 400° C. to 1200° C. (or higher); a peak temperature in the reforming zone of 800° C. to 1500° C.; a temperature difference at the peak temperature location between the end (or end, termination or completion) of the regeneration step and the end (or end, termination or completion) of the subsequent reforming step of 25° C. or higher, or 50° C. or higher, or 100° C. or higher, or 200° C. or higher, up to 800° C. or higher; These may include one or more of the following: a temperature difference at the inlet of the reforming zone between the end (or end, termination or completion) of the regeneration step and the end (or end, termination or completion) of the subsequent reforming step of up to 800°C or higher; and a temperature difference at the outlet of the reforming zone between the end (or end, termination or completion) of the regeneration step and the end (or end, termination or completion) of the subsequent reforming step of 25°C or more, or 50°C or more, or 100°C or more, or 200°C or more, up to 800°C or higher.

[0097] In various embodiments relating to the average reforming zone temperature, the average temperature for the reforming zone may be 500° C. to 1500° C., or 400° C. to 1200° C., or 800° C. to 1200° C., or 400° C. to 900° C., or 600° C. to 1100° C., or 500° C. to 1000° C. Additionally or alternatively, the peak temperature for the reforming zone (perhaps corresponding to a position of the reforming zone close to a position for combustion of the regenerative reactant) may be 800° C. to 1500° C., or 1000° C. to 1400° C., or 1200° C. to 1500° C., or 1200° C. to 1400° C.

[0098] Additionally or alternatively, reaction conditions for reforming hydrocarbons include pressures of 0 psig to 1500 psig (10.3 MPa), or pressures of 0 psig to 1000 psig (6.9 MPa), or pressures of 0 psig to 550 psig (3.8 MPa), and a reaction time of 1000 hours. -1 ~50,000hr -1The gas hourly space velocity of the reforming reactant may be included. The gas hourly space velocity corresponds to the volume of the reactant relative to the volume of the monolith per unit time. The volume of the monolith is defined as the volume of the monolith if it were a solid cylinder.

[0099] In some embodiments, an advantage of operating the reforming reaction at elevated temperatures may be the ability to convert substantially all of the methane and / or other hydrocarbons in the reforming feed. For example, for reforming processes in which water is present in the reforming reaction environment (i.e., steam reforming or "bi" reforming), reaction conditions may be suitable for 10 wt% to 100 wt% methane conversion, 20 wt% to 80 wt% methane conversion, 50 wt% to 100 wt% methane conversion, 80 wt% to 100 wt% methane conversion, 10 wt% to 98 wt% methane conversion, or 50 wt% to 98 wt% methane conversion in the reforming feed. Additionally or alternatively, the reaction conditions may be suitable for a hydrocarbon conversion of 10% to 100% by weight, a hydrocarbon conversion of 20% to 80% by weight, a hydrocarbon conversion of 50% to 100% by weight, a hydrocarbon conversion of 80% to 100% by weight, a hydrocarbon conversion of 10% to 98% by weight, or a hydrocarbon conversion of 50% to 98% by weight in the reformate feed.

[0100] In other embodiments, for reforming processes in which carbon dioxide is present in the reforming reaction environment (i.e., dry reforming or "bi" reforming), the reaction conditions may be suitable for 10 wt% to 100 wt% methane conversion, 20 wt% to 80 wt% methane conversion, 50 wt% to 100 wt% methane conversion, 80 wt% to 100 wt% methane conversion, 10 wt% to 98 wt% methane conversion, or 50 wt% to 98 wt% methane conversion in the reforming feed. Additionally or alternatively, the reaction conditions may be suitable for a hydrocarbon conversion of 10% to 100% by weight, a hydrocarbon conversion of 20% to 80% by weight, a hydrocarbon conversion of 50% to 100% by weight, a hydrocarbon conversion of 80% to 100% by weight, a hydrocarbon conversion of 10% to 98% by weight, or a hydrocarbon conversion of 50% to 98% by weight in the reformate feed.

[0101] In some alternative embodiments, the reforming reaction may be carried out under dry reforming conditions, where the reforming is carried out with CO as a reagent and with reduced or minimized amounts of H2O in the reaction environment. In such alternative embodiments, the goal of the reforming reaction may be to produce a synthesis gas with a ratio of H2 to CO of 1.0 or less. In some embodiments, the temperature of the reforming may correspond to the temperature range described for steam reforming. Optionally, in some embodiments, the dry reforming reaction may be carried out at a lower temperature of 500°C to 700°C, or 500°C to 600°C. In such embodiments, the ratio of H2 to CO may be 0.3 to 1.0, or 0.3 to 0.7, or 0.5 to 1.0. Carrying out the dry reforming reaction under such conditions may lead to substantial coke formation, which may require removal during regeneration to maintain catalyst activity.

[0102] Example of a reverse flow reactor configuration For endothermic reactions operated at elevated temperatures, such as hydrocarbon reforming, a reverse flow reactor can provide a suitable reaction environment to provide heat for the endothermic reaction.

[0103] In a reverse flow reactor, the heat required for the endothermic reaction may be provided by forming a high-temperature heat bubble in the middle of the reactor. A two-step process (a) and (b) may be used: (a) heat is added to the reactor bed (or reactor beds) or monolith (or monoliths) via in situ combustion, and then (b) heat is removed from the reactor bed in situ via an endothermic process such as reforming, pyrolysis or steam cracking. This type of configuration may allow for consistent management and limitation of high temperature bubbles in the reactor zone (or zones) that can withstand such conditions for extended periods. The reverse flow reactor system may allow the main endothermic process and the regeneration process to be carried out substantially continuously.

[0104] The reverse flow reactor system may include a first reactor and a second reactor, the first reactor and the second reactor being arranged (or oriented) in a series relationship to each other with respect to a common flow path, and optionally preferably along a common axis. The common axis may be horizontal, vertical or other. During the regeneration process, reactants (e.g., fuel and oxygen) are combined or mixed in the reaction zone and allowed to combust in situ in the reaction zone, creating a high temperature zone or heat bubble inside the middle portion of the reactor system. The heat bubble may have a temperature that corresponds to at least approximately the initial temperature for the endothermic reaction. Typically, the temperature of the heat bubble may be greater than the initial temperature for the endothermic reaction, as heat is transferred from the heat bubble in the middle portion of the reactor toward the end of the reactor, decreasing the temperature. In some embodiments, the combining may be enhanced by a reactant mixer, which facilitates substantially complete combustion / reaction at a desired location, optionally located between the first and second reactors. The combustion process may occur such that the flow of the first and second reactants through the first reactor and at least partially through the second reactor (preferably not all through the second reactor to avoid waste heat and overheating the second reactor) continues long enough to act to transfer a (desired) majority / substantial portion of the heat generated by the reaction (e.g., heat bubbles). Flue gas may be vented from the second reactor, but preferably the majority of the heat is retained within the second reactor. The amount of heat transferred to the second reactor in the regeneration step may be limited or determined by the desired exposure time or space velocity of the hydrocarbon feed gas in the endothermic reaction environment.

[0105] After regeneration or heating of the second reactor medium (such as the phase stable monolith described herein), in the next / reverse step or cycle, reactant methane (and / or natural gas and / or another hydrocarbon) for the endothermic reaction may be fed or flowed through the second reactor from the opposite (or reverse) flow direction to that in the heating step. For example, in a reforming process, methane (and / or natural gas and / or another hydrocarbon) may be fed or flowed through the second reactor. The methane may contact the hot second reactor and mixer medium in the heat bubble region, whereby heat may be transferred to the methane for reaction energy.

[0106] For some embodiments, the basic two-step asymmetric cycle of a reverse flow regenerative bed reactor system is depicted in FIG. 1(a) and FIG. 1(b) in terms of a reactor system having two zones / reactors, a first or recuperator / quenching zone (7) and a second or reaction zone (1). The reaction zone (1) and the recuperator zone (7) may comprise a regenerative monolith and / or other regenerative structure. As used herein, a regenerative monolith or other regenerative structure comprises a material that is efficient for storing and transferring heat and is efficient for carrying out a chemical reaction. The regenerative monolith and / or other structure may represent any convenient type of material suitable for storing heat, transferring heat, and catalyzing a reaction. Examples of such structures include bedding or fillers, ceramic beads or spheres, ceramic honeycombs, ceramic tubes, extruded monoliths, and the like, provided they maintain their integrity, functionality, and can withstand prolonged exposure to extreme temperatures of 1200°C or 1400°C or 1600°C, allowing for operating margins.

[0107] For ease of depiction of Figure 1, the reactor is described herein in the context of a reforming reaction. Other convenient types of endothermic reactions may generally be carried out using a reverse flow reactor, such as the reactor shown in Figure 1.

[0108] As shown in FIG. 1(a) of FIG. 1, at the start of the “react” step of the cycle, the second end 5 of reaction zone 1 (aka the second reactor herein) may be at a higher temperature than the first end 3 (or main end 3) of reaction zone 1, and at least a portion (including first end 9) of recovery / quench zone 7 (aka the first reactor herein) may be at a lower temperature than reaction zone 1 to provide a cooling (or quench) effect on the resulting product. In embodiments where the reactor is used for reverse flow reforming, a methane-containing reactant feed (or other hydrocarbon-containing reactant feed) may be introduced into the first end 3 of reforming or reaction zone 1 via conduit (or conduits) 15. In various embodiments, the hydrocarbon-containing reactant feed may include H2O, CO2, or a combination thereof.

[0109] A feed stream provided through inlet (or inlets) 15 may absorb heat from the reaction zone 1 and endothermically react to form the desired synthesis gas product. As this process proceeds, a shift in temperature profile 2 may be formed based on the heat transfer characteristics of the system, as indicated by the arrows. If the ceramic catalyst monolith / other catalyst structure is designed to be properly heat transferable, the profile may have a relatively sharp temperature gradient, which may move across the reaction zone 1 as the reforming process proceeds. In some embodiments, a sharper temperature gradient profile may provide improved control over the reaction conditions. In embodiments where another type of endothermic reaction is performed, a similar shift in temperature profile may occur as the temperature gradient moves (or moves) across the reaction zone 1 as the reaction process proceeds.

[0110] The effluent from the reforming reaction, which may include unreacted feed components (hydrocarbons, HO, CO) as well as syngas components, exits reaction zone 1 through second end 5 at an elevated temperature, passes through recuperator 7 through second end 11, and exits through first end 9. Recuperator (or recouperator) 7 may be initially at a lower temperature than reaction zone 1. As the product from the reforming reaction (and optionally unreacted feed) passes through recuperator 7, the gas may be quenched or cooled to a temperature that is substantially close to the temperature of the recuperator at first end 9, and in some embodiments, may be quenched or cooled to about the same temperature as the regenerated feed that is introduced into recuperator (or recuperator) 7 through conduit 19 in the second step of the cycle. As the reforming effluent is cooled in recuperator zone 7, a temperature gradient 4 may be formed in the regenerator bed (or beds) of the zone and may move across recuperator zone 7 in such a step. The quench may heat the recoupler 7, which may be cooled again in a second step and subsequently subjected to another quench to prevent the size and location of the heat bubble from gradually growing through the quench reactor 7. After the quench, the reaction gas may exit the recoupler at “9” via conduit 17 and may be processed for separation and recovery of the various components.

[0111] Then (or subsequently), the second step of the cycle, referred to as the regeneration step, may begin with the reintroduction of the first and second regeneration reactants via conduit(s) 19. The first and second reactants are separately directed through the hot recoupler 7 to the second end 11 of the recoupler 7 where the first and second reactants may be combined for endothermic reaction or combustion at or near the central region 13 of the reactor system.

[0112] An example of a regeneration step is shown in FIG. 1(b) of FIG. 1. Regeneration may involve transferring recovered sensible heat from the recuperation zone (or recouper zone) 7 to the reaction zone 1, thereby thermally regenerating the reaction bed 1 for a subsequent reaction cycle. Regeneration gas / reactant may enter the recuperation zone 7, for example via a conduit (conduits 19), and flow through the recuperation zone 7 into the reaction zone 1. Doing so may cause temperature gradients 6 and 8 to move across the bed as shown by the arrows in the exemplary graph of FIG. 1(b), similar to but opposite to the graph of the temperature gradients developed in the reaction cycle of FIG. 1(a). Fuel and oxidant reactants may be combusted in a region proximate to the boundary (or interface) 13 between the recuperation zone 7 and the reaction zone 1. The heat recovered from the recuperating zone together with the heat of combustion may be transferred to the reaction zone and may thermally regenerate the regenerated reaction monolith and / or bed 1 disposed therein.

[0113] In some embodiments, some of the conduits in the channel may carry a mixture of the first and second reactants due at least in part to some mixing in the first end (17) of the first reactor. However, the number of conduits carrying a combustible mixture of the first and second reactants may be small enough that they do not react until after most of the stoichiometrically reactable reactants have exited the second end of the first reactor. The axial location of the onset of combustion or exothermic reactions in conduits carrying such a mixture of reactants may be controlled by a combination of temperature, time, and fluid dynamics. Fuel and oxygen typically require temperature- and mixture-dependent autoignition times for combustion. Nevertheless, some reactions may occur within an axial portion (or part) of the conduits carrying the mixture of reactants. However, the number of channels with such reactions may be small enough that their effect on the overall heat balance in the reactor is tolerable or insignificant, making such reactions tolerable. The design details of a particular reactor system may be selected to avoid mixing of reactants within the conduits as much as reasonably possible.

[0114] FIG. 2 shows another exemplary reactor system that may be suitable for some applications to control and defer the combustion of fuel and oxidant to achieve efficient regenerative heat. FIG. 2 depicts a single reactor system operating in a regenerative cycle. The reactor system may be considered to have two reactor zones. The recoupler 27 may be the zone where quenching occurs primarily and is provided with substantially isolated flow paths or channels for moving the quenching reactant gas through the reactor medium so that combustion is not initiated until the gas reaches proximate or within the reactor core 13 in FIG. 1. The reformer 2 may be the reactor where regenerative heat and methane (and / or hydrocarbon) reforming primarily occurs and may be considered the second reactor for purposes herein. Although the first and second reactors in the reactor system are identified as separate and distinct reactors, it is understood that the first and second reactors may be fabricated, provided, or otherwise combined into a common single reactor bed, whereby the reactor system may be described as comprising merely a single reactor that integrates both cycles within the reactor. The terms "first reactor" and "second reactor" may simply refer to individual zones within the reactor system whereby each of the steps, such as regeneration, reforming, and quenching, are performed, and do not require that separate elements be utilized for the two reactors. However, various embodiments may comprise a reactor system whereby the recoupler reactor may include conduits and channels as described herein, and the reformer reactor may similarly have conduits. Additionally or alternatively, some embodiments may include a reformer reactor that is positioned differently from the recoupler reactor bed and may contain different materials than the recoupler reactor bed.

[0115] As mentioned above, the first reactor or recoupler 27 may include various gas conduits 28 for individually channeling two or more gases through a first end 29 of the recoupler 27 and through a regenerative bed(s) disposed therein. The first gas 30 may enter a first end of a number of flow conduits 28. In addition to providing flow channels, the conduits 28 may comprise an effective flow barrier (e.g., an effectively functioning flow barrier such as a conduit wall) to prevent cross-flow or mixing between the first and second reactants and to keep the reactants effectively largely separated from one another until mixing is permitted. As mentioned above, each of the first and second channels may comprise multiple (or multiple) channels or flow paths. The first reactor may comprise multiple (or multiple) substantially parallel (or parallel) flow segments, each segmented into a first channel and a second channel.

[0116] In some embodiments, the recoupler may be comprised of one or more extruded honeycomb monoliths, as described above. Each monolith may provide a flow channel (or multiple flow channels), e.g., a flow passage, for one of the first reactant and the second reactant. Each channel preferably includes multiple conduits. Alternatively, the monolith may have one or more channels for each reactant, such that one or more channels or groups of conduits are provided that are dedicated to carrying one or more streams of the reactant, while the remainder of the conduits carry one or more streams of the other reactant. At the interface between the channels, it may be appreciated that many of the conduits may carry a mixture of the first reactant and the second reactant, although the number of such conduits is proportionally small.

[0117] In alternative embodiments, reactor media other than a monolith may be used, for example, the channel conduit / flow path may include, but is not limited to, a channel through a portion (or portions) of the reactor, may have barrier portions (e.g., barrier portions along the outer surface of a segment or within a subsegment), may not be substantially effectively permeable to gases, and / or may include more tortuous paths (e.g., paths that are not straight or tubular, convoluted, complex, winding, and / or twisted) including labyrinths (or mazes), variegated flow paths, conduits, tubes, slots, and / or pore structures suitable for preventing cross-flow of reactant gases and other means suitable for maintaining substantial separation of the first and second reactant gases from each other as they pass axially through the recoupler 27. Such other types of reactor media may also be suitable, so long as at least a portion of the media can be formed by sintering (or calcining) the ceramic catalyst components described herein and then exposing such media to reducing conditions for catalytic activation. In such embodiments, the complex flow paths may provide a longer effective flow path, increased surface area, and improved heat transfer. Such designs may be preferred for reactor embodiments having a relatively short axial length through the reactor. A longer axial reactor length may increase the pressure drop through the reactor. However, in such embodiments, the porous and / or permeable media may include, for example, at least one of a packed bed, a tile arrangement, a permeable solid media, a substantially honeycomb-type structure, a fibrous arrangement, and a mesh-type lattice structure.

[0118] In some embodiments, the reverse flow reactor may include some type of equipment or method to direct one flow stream of a plurality of reactants into a selected portion of a conduit. In the exemplary embodiment of FIG. 2, the gas distributor 31 may direct the second gas stream 32 into a second gas stream channel that is substantially isolated from or not in fluid communication with the first gas channel, shown as channel 33. As a result, at least a portion of the gas stream 33 may remain separated from the gas stream 30 during the axial passage through the recoupler 27. In some embodiments, the regenerative bed (or regenerative beds) and / or monolith (or monoliths) of the recoupler zone may comprise channels having gas or fluid barriers that isolate the first reactant channel from the second reactant channel. Thereby, both of the at least two reactant gases passing through the channel means pass sufficiently through the regenerative bed (or multiple regenerative beds) to quench the regenerative beds and absorb heat into the reactant gases prior to combining to react with each other in the combustion zone.

[0119] In various embodiments, the gases (gases including fluids) 30 and 32 may each include a component that reacts with the components of the other reactants 30 and 32, thereby causing an exothermic reaction when combined. For example, each of the first and second reactants may comprise one of a fuel gas and an oxidant gas that may combust or burn when combined with the other of the fuel gas and oxidant gas. By keeping the reactants substantially separate, the location of heat release resulting from the exothermic reaction may be controlled. In some embodiments, "substantially separated" may be defined to mean that at least 50%, or at least 75%, or at least 90% of the smallest or limiting stoichiometrically reactable amount of reactant, such as between the first and second reactant streams, is not consumed by reaction until such gas completes its axial passage through the recoupler 27. In this manner, the majority of the first reactant 30 may be kept isolated from the majority of the second reactant 32, and most of the heat release from the reaction of the combination of reactants 30 and 32 may occur after the reactants begin to exit the recoupler 27. The reactants may be gaseous, although optionally some reactants may comprise a liquid, mixture or vapor phase.

[0120] Percent reaction for such recycle streams refers to the percent of reaction possible based on the stoichiometry of the entire feed. For example, if gas 30 is composed of 100 volumes of air (80 volumes of N2 and 20 volumes of O2) and gas 32 is composed of 10 volumes of hydrogen, the maximum stoichiometric reaction would be the combustion of 10 volumes of hydrogen (H2) with 5 volumes of oxygen (O2) to form 10 volumes of H2O. In such a case, if 10 volumes of hydrogen were actually combusted in the recoupler zone (27), this would represent 100% reaction of the recycle stream. This is despite the presence of residual unreacted oxygen, which in this example was present in an amount in excess of the stoichiometric requirement. Thus, in such an example, hydrogen is the stoichiometrically limiting component. Using this definition, less than 50% reaction, or less than 25% reaction, or less than 10% reaction of the regenerator stream may occur during an axial pass through the recoupler (27).

[0121] In various embodiments, channels 28 and 33 may be comprised of ceramic (including zirconia), alumina, or other refractory material capable of withstanding temperatures in excess of 1200° C., or in excess of 1400° C., or in excess of 1600° C. Additionally or alternatively, channels 28 and 33 may be comprised of a 50 ft -1 ~3000ft -1 or 100ft -1 ~2500ft -1 or 200ft -1 ~2000ft -1 The wetted area may be 0.05 mm or less.

[0122] Referring again to FIG. 1, the reactor system may include a first reactor 7 including a first end 9 and a second end 11, and a second reactor 1 including a first end 3 (or a primary end 3) and a second end 5 (or a secondary or secondary end 5). The embodiments shown in FIGS. 1 and 2 are merely simplified for illustrative purposes and are not intended to represent all-inclusive embodiments. The term "end" of the reactor simply refers to a distal portion of the reactor away from an axial midpoint of the reactor. Thus, referring to gas entering or exiting an "end" of the reactor (such as end 9) simply means that the gas may enter or exit substantially at any of a variety of axial points between the respective end faces of the reactor and the midpoint of the reactor (preferably closer to the end faces than the midpoint). Thus, one or both of the first and second reactant gases may enter at a respective end face, while the other of the first and second reactant gases may be supplied to each end of the reactor through a slot or port at the periphery or peripheral exterior surface of that respective end of the reactor. EXAMPLES

[0123] In the following examples, the monoliths used to support the catalyst systems corresponded to monoliths with 400 cpsi (cells per square inch) and either 35% or 52% open frontal area.

[0124] Example 1A - NiO / Al 2 O 3 (NiAl 2 O 4 ) The α-Al2O3 powder was dried overnight in an oven at 121°C (~250°F). The dried α-Al2O3 powder was then weighed and mixed with an appropriate amount of NiO, which corresponded to an Al:Ni molar ratio of 1.5:1 in the NiO / Al2O3 catalyst system. It is noted that such a catalyst system can form NiAl2O4 in situ after exposure to cyclic high temperature reforming conditions. The mixture was subjected to mixing in a Waring Blender. The blended material was then calcined at 1300°C (~2372°F) in a Sentro Tech Furnace with a ramp rate of 3°C / min for 4 hours to produce the desired NiO / Al2O3 catalyst system. The calcined material was cooled to room temperature. The wt% of catalytic metal (Ni) in the NiO / Al2O3 catalyst system was 38.8% (based on the weight of the catalyst system). The calcined NiO / Al2O3 catalyst system was further milled in liquid to prepare a suitable slurry and washcoated onto a monolith having 93 wt% α-Al2O3, 5 wt% SiO2 and 2 wt% MgO. The washcoated monolith was further calcined at 1200°C (2192°F) for 2 hours to ensure complete attachment (or fixation or adhesion) of the active material to the monolith. This corresponded to annealing the monolith at a temperature substantially similar to the peak temperature during subsequent exposure to cyclic high temperature reforming conditions. The final washcoated monolith was loaded into the hottest catalytic zone (e.g., 800-1250°C) of a pilot-scale reverse flow reactor unit and exposed to various cyclic process conditions for approximately 750 hours. Figure 5 shows a scanning electron microscope (SEM) image of NiO and NiAl2O4 materials present on a monolith with 93 wt% α-Al2O3, 5 wt% SiO2 and 2 wt% MgO after 750 hours. During exposure to various cycle and process conditions, the NiAl2O4 catalyst system provided stable and high methane conversion, good phase stability of the metal oxide support, little sintering of the active catalyst metals, and good adhesion to the monolith.

[0125] Examples 1B and 1C - NiAl 2 O 4 and Al 2 O 3 / NiAl 2 O 4 Additional catalyst systems and corresponding washcoated monoliths were prepared according to the method of Example 1A, varying the ratio of NiO to Al2O3. In Example 1B, the initial Al:Ni ratio was 2:1, resulting in a catalyst system with a Ni content of approximately 33.2 wt. % (based on the weight of the catalyst system), which corresponds to the stoichiometric ratio for NiAl2O4. The catalyst system with an Al:Ni ratio of 2:1 was then washcoated onto the monolith using the same procedure and with the same type of washcoat composition as for the monolith of Example 1A. For Example 1C, the initial Al:Ni ratio was 3:1, and therefore there was excess Al2O3 in the catalyst system. This resulted in a catalyst system with a Ni content of approximately 25.8 wt. %. The catalyst system was then deposited as a washcoat onto the monolith with the same type of washcoat composition as used in Examples 1A and 1B.

[0126] Example 2 – Rh / α-Al 2 O 3 In this example, the catalyst system corresponds to Rh (Rh2O3) as the catalytic metal (oxide) and α-Al2O3 as the metal oxide support layer. α-Al2O3 corresponds to a "corundum" type (or "corundum" type) oxide. To prepare such a catalyst system, α-Al2O3 powder was dried overnight in an oven at 121 °C (~250 °F). The dried α-Al2O3 powder was then weighed and a small aliquot was taken to determine the absorption factor. A solution of rhodium (III) nitrate, Rh(NO3)3·nH2O, i.e., an aqueous solution containing 9.77 wt. of Rh at 27.4% solids content, was mixed with an appropriate amount of excess H2O (if necessary) and sprayed / impregnated onto the α-Al2O3. The material was then subjected to drying at 121 °C (250 °F) for at least 2 hours. The dried material was calcined at 500°C (932°F) in a Sentro Tech Furnace using a ramp rate of 3°C / min for 4 hours to produce Rh2O3 / α-Al2O3. The calcined material was cooled to room temperature. The weight percent of catalytic metal Rh was approximately 4.0%. The calcined Rh2O3 / α-Al2O3 catalyst system was further milled in solution to prepare a suitable slurry and washcoated onto a monolith having 93 wt% α-Al2O3, 5 wt% SiO2 and 2 wt% MgO. The washcoated monolith was further calcined at 500°C (932°F) for 2 hours to ensure complete attachment (or fixation or adhesion) of the active material to the monolith. The final washcoated monoliths were loaded into the low temperature catalytic zone (e.g., 400-1050 °C) of a pilot-scale reverse flow reactor unit and exposed to various cyclic process conditions for approximately 750 hours. The desired Rh2O3 / α-Al2O3 catalytic system provided stable and high methane conversion, good phase stability of the metal oxide support, reduced or minimal sintering of the active catalytic metals, and good adhesion to the monolith.FIG. 6 shows a scanning electron microscope (SEM) image of an example of a RhO / α-AlO catalyst system washcoated onto a monolith having 93 wt. % α-AlO, 5 wt. % SiO, and 2 wt. % MgO after 750 hours.

[0127] Example 3 - NiO / YSZ In this example, the catalyst system corresponds to Ni (NiO) as the catalytic metal (oxide) and yttria-stabilized zirconia (YSZ) as the metal oxide support layer (based on stabilized zirconia oxide). A catalyst system containing 60 wt% NiO was prepared by mixing appropriate amounts of NiO powder and YSZ powder. The α-alumina slurry was washcoated onto a monolith composed of 95 wt% α-Al2O3, 4 wt% SiO2, and 1 wt% TiO2. The washcoated monolith was sintered at 1450°C for 2 hours, thereby creating an intermediate bonding layer. The NiO / YSZ active material slurry was then washcoated on top of the intermediate bonding layer and sintered at 1300°C for 2 hours. The resulting structure contained three parts: i) NiO / YSZ active material, ii) an α-Al2O3 intermediate bonding layer, and iii) a monolith composed of 95 wt% α-Al2O3, 4 wt% SiO2, and 1 wt% TiO2. A scanning electron microscope (SEM) cross-sectional image of the structure of the monolith with NiO / YSZ active material and intermediate bonding layer is shown in Figure 7.

[0128] Example 4 - NiO / SLT In this example, Ni (NiO) is the catalytic metal (oxide) and Sr 0.65 La 0.35 TiO3(SLT) is the metal oxide support layer of the catalytic system. The metal oxide support layer corresponds to the perovskite oxide. To form the catalytic system, a solution of nickel nitrate, Ni(NiO3)2·6H2O, was prepared and Sr 0.65 La 0.35 After sintering at 1300°C, the mixture was mixed with 22 wt% NiO and 78 wt% Sr 0.65 La 0.35A powder containing TiO3(SLT) was prepared. The catalyst system powder was further milled in a solution to prepare a suitable slurry for washcoating. The resulting washcoated monolith contained two parts: i) NiO / SLT catalyst system, and ii) 95 wt% α-Al2O3, 4 wt% SiO2 and 1 wt% TiO2 monolith. The catalyst system was approximately 5 wt% of the total weight of the washcoated monolith.

[0129] Example 5 – NiRh / Hibonite In this prophetic example, Ni (NiO) and Rh (Rh2O3) are used as catalysts (oxides) and hibonite (Ca,Ce) (Al,Ti,Mg) as metal oxide supports based on hibonite oxide. 12 O 19 To form the catalytic system, a mixed solution of nickel nitrate Ni(NO3)2·6H2O, rhodium(III) nitrate, Rh(NO3)3·nH2O may be prepared with an appropriate amount of excess H2O (H2O used as needed) and impregnated into hibonite powder. After calcination at 1300 °C, the mixture is composed of 10 wt% NiO, 2 wt% Rh2O3 and 88 wt% hibonite(Ca,Ce)(Al,Ti,Mg). 12 O 19 A catalyst system powder may be formed comprising the catalyst system powder. The catalyst system powder may be further milled in a solution to prepare a suitable slurry for washcoating. The resulting washcoated monolith may contain two parts, i) a NiRh / hibonite catalyst system, and ii) a monolith comprised of 93 wt. % α-Al2O3, 4 wt. % SiO2, 2 wt. % MgO, and 1 wt. % Na2O. The catalyst system may comprise approximately 5 wt. % of the total weight of the washcoated monolith.

[0130] Example 6 - Rh 2 O 3 / USY In this example, the catalyst system corresponds to Rh (Rh2O3) as the catalytic metal (oxide) and USY as the metal oxide support based on the zeolite oxide. The USY zeolite powder was dried overnight in an oven at 121°C (250°F). The dried USY zeolite powder was then weighed and a small aliquot was taken to determine the absorption factor. An aqueous solution of rhodium (III) nitrate, Rh(NO3)3·nH2O, i.e., an aqueous solution containing 9.77 wt. of Rh at 27.4% solids content, was mixed with an appropriate amount of excess H2O (if necessary) and sprayed / impregnated onto the USY zeolite. The material was then dried at 121°C (250°F) for at least 2 hours and weighed. The dried material was calcined at 500°C (932°F) in a Sentro Tech Furnace using a ramp rate of 3°C / min for 4 hours to produce powdered Rh (Rh in oxide (Rh2O3) form) calcined on USY zeolite. The calcined material was cooled to room temperature. The wt% of catalytic metal Rh in the Rh2O3 / USY zeolite catalyst system was 1.5 wt%. The calcined Rh2O3 / USY zeolite active material was further milled in solution to prepare a suitable slurry and washcoated onto a monolith composed of 93 wt% α-Al2O3, 5 wt% SiO2 and 2 wt% MgO. The washcoated monolith was further calcined at 500°C (932°F) for 2 hours to ensure complete attachment (or fixation or adhesion) of the active material to the monolith. The resulting structure consisted of two parts: i) a Rh2O3 / USY zeolite catalyst system and ii) a monolith consisting of 93 wt.% α-Al2O3, 5 wt.% SiO2 and 2 wt.% MgO.

[0131] Examples 7A, 7B, 7C - Catalyst systems with different starting alumina phases Three different types of catalyst system washcoat formulations were used to prepare multi-zone catalyst systems for hydrocarbon reforming. In this example, a multi-zone catalyst system with two catalyst zones was used. The first zone (higher temperature) corresponded to a Ni-containing catalyst and the second zone (lower temperature) corresponded to a Rh-containing catalyst. Two monoliths were used to fill the desired catalyst bed volume in each zone of the pilot-scale reactor. Thus, each catalyst system corresponded to a total of four monoliths.

[0132] For Example 7A, the first two monoliths with a Ni-containing catalyst system were prepared according to Example 1A. Thus, the catalyst was NiO and the alumina phase in the first two monoliths of Example 7A was α-Al2O3. This type of catalyst system may be capable of in situ formation of NiAl2O4 after exposure to cyclic high temperature reforming conditions. Sufficient washcoat was applied so that the weight of the NiO / α-Al2O3 catalyst system was approximately 5 wt% of the total weight of the washcoated monolith. For Example 7A, the second two monoliths with a Rh-containing catalyst system were prepared according to Example 2. Thus, the alumina phase in the second two monoliths of Example 7A was α-Al2O3. Sufficient washcoat was applied so that the weight of the Rh2O3 / α-Al2O3 catalyst system was approximately 4 wt% of the total weight of the washcoated monolith.

[0133] For Examples 7B and 7C, instead of using a catalyst system composed of a phase-stable material, a washcoat containing a higher surface area material was deposited on the monolith, and thus the washcoat used in Examples 7B and 7C did not include a thermally stable metal oxide support layer.

[0134] In Example 7B, the catalyst system for the first two washcoats corresponded to θ-Al2O3 doped with 4 wt% La, containing 30% Ni as catalyst, and formed at 1200°C. This type of composition can be expressed as 30%Ni-4%-La-θ-Al2O3. This catalyst system corresponds to an Al:Ni molar ratio of 3.7:1. It is noted that this ratio has a substantial amount of excess Al relative to the stoichiometric ratio of NiAl2O4. After depositing the washcoats, the first two monoliths of Example 7B were calcined at 500°C. For the second two monoliths of Example 7B, a washcoat having 5% Rh in 4%-La-γ-Al2O3 was washcoated onto the alumina-rich monolith. It is noted that the second two washcoats contained γ-Al2O3 rather than θ-Al2O3 of the first two washcoats. After depositing the washcoat, the second two monoliths of Example 7B were calcined at 500°C.

[0135] In Example 7C, the first two washcoats and the second two washcoats were prepared similar to Example 7B, but with different calcination temperatures for the first two monoliths: in Example 7C, a calcination temperature of 1200° C. was used after application of the washcoats (compared to the 500° C. used in the calcination of Example 7B).

[0136] Example 8 - Modifications on monoliths with different starting alumina phases The washcoated monoliths of Examples 7A, 7B and 7C were used in a pilot scale reactor to study the change in catalytic activity over time and to determine the structural stability of the washcoated monoliths. The monoliths were used to perform steam reforming of methane feed under cyclic high temperature conditions. The reaction conditions included a regeneration step and a reforming step. During the regeneration step, air was used to provide a source of oxygen for the combustion of the hydrocarbon fuel. The amount of air was sufficient to provide 10% excess O2 relative to the amount of hydrocarbon fuel used for heating. The regeneration step in each cycle was performed at a pressure of 150 psig (~1.0 MPa-g) for approximately 15 seconds. The combustion in the regeneration step was performed to provide a temperature profile similar to that shown in Figure 4, but with a target peak temperature of 1150°C at the end of the regeneration step / beginning of the reforming step. The reforming step in each cycle was performed at a pressure of 300 psig (~2.1 MPa-g) for approximately 15 seconds using methane as the hydrocarbon for reforming. The molar ratio of H2O to CH4 in the reforming process feed was 1.3.

[0137] FIG. 7 shows the average conversion (or average conversion rate) of methane in the reforming step (right plot) when the process was run over a period of 4 to 6 weeks. Due to the cooling effect of the reactor toward the end of the reforming step during a single cycle, the conversion percentage at the end of the reforming step of each cycle is somewhat smaller (or lower). This is shown by the difference in conversion when averaged over the first 10 seconds of each reforming step (left plot of FIG. 7) versus the first 15 seconds of each reforming step (right plot of FIG. 7). It is noted that shorter reforming steps can be used if a higher overall conversion maintenance is desired over the total length of the reforming step.

[0138] As shown in the right plot of FIG. 7, both Examples 7B and 7C initially provided higher conversion (or conversion rate) than Example 7A. This is consistent with the expected effect of using a higher surface area phase of alumina as the support for Examples 7B and 7C. However, as shown in the right plot of FIG. 7, the conversion activity of the catalysts in Examples 7B and 7C is not stable. Although the data is noisy, the conversion activity for the catalyst of Example 7C begins to decline almost immediately after the start of the run. This decline in activity continues until about 300 hours of cycling. At such point, the reaction of Example 7C was stopped due to the rapid loss of activity that occurred. Although Example 7B has a more gradual decline in catalyst activity, Example 7B suffers a substantial decline in activity that began well before 400 hours of operation. Between 400 and 800 hours, a similar decrease in activity over time was observed using an alternative set of cycle reforming conditions not plotted in Figure 7. At 800 hours, process conditions were restored to the original reforming conditions. By 800 hours, catalyst degradation appeared to stabilize, albeit at activity levels considerably lower than the catalyst of Example 7A. Again, such activity loss is believed to be due to degradation of the catalyst system on the reactor monolith leading to a loss of surface area available to expose the methane feed to the catalyst.

[0139] In contrast to Examples 7B and 7C, the right plot of Figure 7 shows that the catalyst system of Example 7A maintained similar activity over the entire length of the treatment run. Without being bound by any particular theory, this is believed to be due to Example 7A corresponding to a) a monolith formed from a material that is phase stable under cyclic high temperature reforming conditions, and b) a monolith that includes an oxide support layer, where interactions between the catalytic metal (e.g., Ni, etc.) and the oxide material (e.g., Al2O3, etc.) occur at the oxide support layer and do not affect the structural integrity of the monolith or other support structure underneath.

[0140] The left plot of Figure 7 shows similar results. Again, Example 7C exhibits higher activity initially (or early) than Example 7A, but the activity of Example 7C begins to decline almost immediately. Examples 7A and 7B have similar initial activity, but only Example 7A maintains such activity. As shown in both plots in Figure 7, Example 7A maintains essentially the same activity for a run length of 750 hours.

[0141] To further characterize the results from performing cyclic reforming on the catalyst system and monolith of Example 7A, at the end of the run, the alternating oxidation and reduction cycles were maintained while the peak reactor temperature was cooled to 1000° C. N2 flow was then used to cool the reactor to room temperature. After cooling, additional characterization was performed.

[0142] It is first noted that after cooling, for the first and second monoliths of Example 7A, the catalyst system was difficult to remove from the monolith below. If the catalyst or catalyst system does not contain a thermally stable metal oxide, it is typically relatively easy to separate the catalyst or catalyst system from the monolith due to structural failure. However, it has been unexpectedly discovered that by using a thermally stable supporting metal oxide for the catalyst system, the strong attachment (or fixation or adhesion) of the catalyst system to the monolith can be maintained after longer exposure to the cyclic high temperature reforming environment.

[0143] After removal, the catalyst system of Example 7A was characterized using X-ray diffraction (XRD). The XRD spectrum showed that all of the catalyst systems were in stable phase. For the first monolith, the catalyst system was primarily in a reduced state, as indicated by the presence of substantial peaks for Ni and α-Al2O3 while there was little NiAl2O4 present. The catalyst system for the second monolith was more oxidized with a mixture of Ni, NiO, α-Al2O3 and NiAl2O4 present. The XRD spectra for the third and fourth monoliths were similar to each other, both showing primarily Rh and α-Al2O3. Additional microscopic and elemental analyses of the catalyst systems were consistent with the XRD spectra.

[0144] Example 9 - Varying the excess oxygen in the regeneration process Prior to removal of the catalyst system from the first two monoliths of Example 7A, SEM micrographs were obtained of the surface of the catalyst system on the monoliths. Figure 8 is a representative image of the micrograph. As shown in Example 8, substantial sintering of Ni had occurred on the surface of the monoliths. It was noted in Example 8 that the first monolith was in a primarily reduced state and the second monolith was in a partially reduced state.

[0145] Without being bound to a particular theory, it is believed that the sintering observed in FIG. 8 was due to incomplete oxidation of Ni metal during the regeneration step under the regeneration conditions for the process cycle used in Example 8. In Example 8, a 10% excess of O2 relative to the stoichiometry for combustion (i.e., 10% molar excess of oxygen) was used. Based on the total amount of Ni metal in the pilot-scale reactor, the 10% molar excess of oxygen (relative to the stoichiometry for combustion) represented approximately 40%-50% of the amount of oxygen required to convert all of the Ni in the reactor from Ni metal to NiO. Given the amount of hydrogen present in the reforming environment, it is believed that substantially all of the Ni exposed in the reactor was converted from NiO to Ni during the reforming step of the cycle, and only a small portion of the Ni metal was converted back to NiO during the regeneration step.

[0146] To investigate this issue (or theory), additional reactor runs were conducted using a second group of monoliths of substantially the same composition as the monoliths of Example 7A. The second group of monoliths were used to perform methane reforming under two sets of process conditions. First, the second group of monoliths were used to perform methane reforming under the same conditions used in Example 8. This corresponded to having a molar excess of O2 used in the regeneration step that was approximately 10% in excess of the stoichiometric amount for combustion. After characterizing the amount of conversion using the conditions in Example 8, the process cycle was modified so that the molar excess of O2 in the regeneration was approximately 30%.

[0147] During each process cycle, the reactor midpoint temperature was recorded along with the average methane conversion during the first 10 seconds. Figure 9 shows the results obtained using 10 molar excess O2 and 30% molar excess O2 with the second group of monoliths. For comparison, similar data from Example 7A is shown in Figure 9. As shown in Figure 9, using a 10% molar excess O2 with new monoliths resulted in substantially the same level of methane conversion versus reactor midpoint temperature as observed in Example 7A. However, a substantial increase (or large increase) in conversion was observed when the amount of O2 in the regeneration step was increased to 30% molar excess. It is noted that approximately a 24% molar excess provided the stoichiometric minimum amount of O2 required to oxidize all of the Ni in the reactor from Ni metal to NiO (or equivalently NiAl2O4). As shown in Figure 19, using a sufficient molar excess of O2 to fully oxidize all of the Ni in the reactor resulted in a substantial increase in activity.

[0148] Additionally, after obtaining the microscopic images shown in Figure 8, the first two monoliths of Example 7A were fired at 1300°C for 4 hours in an O2 environment, and SEM images were obtained of the fired monoliths. The additional microscopic images showed that redispersion of Ni had occurred, consistent with the results shown in Figure 9.

[0149] Example 10 - NiAl 2 O 4 Ni / YSZ on a monolith composed of Additional test runs were conducted in the pilot scale reactor in which the first two monoliths were constructed from NiAl2O4. For the first two monoliths, an intermediate Al2O3 tie layer was applied to the NiAl2O4 monolith followed by the Ni / YSZ catalyst system. The catalyst system washcoat represented approximately 5 wt. % of the total weight of the catalyst system and monolith combination. The third and fourth monoliths were similar to the third and fourth monoliths of Example 7A. Thus, the third and fourth monoliths included a washcoat of the Rh / α-Al2O3 catalyst system applied to a monolith constructed from α-Al2O3.

[0150] The monolith was then subjected to cyclic high temperature reforming conditions similar to those in Example 8. Figure 10 shows the methane conversion during the test run. As shown in Figure 10, the catalytic activity was initially good, indicating that Ni / YSZ in combination with Rh / α-Al2O3 can be effectively used in multiple zones to achieve the desired reforming activity. However, after approximately 200 hours of exposure, the reforming activity substantially decreased. This is believed to be due to the collapse of the first and second monoliths. The collapse of the first and second monoliths was visually confirmed after the test run was completed. Without being bound to a particular theory, it is believed that the cyclical oxidation-reduction environment caused the rapid transformation (or conversion) of the underlying NiAl2O4 monolith between the NiAl2O4 and (Ni+Al2O3) states. It is believed that such cycling between states caused the structural breakdown of the monolith. Thus, although NiAl2O4 can potentially be used to construct monoliths, the benefits of using NiAl2O4 for reforming in a cyclic high temperature reforming environment cannot be realized over longer run lengths when NiAl2O4 is used as the monolith material. Instead, as shown in Example 8, the use of NiAl2O4 (preferably NiAl2O4 having the form NiO / NiAl2O4) as a catalyst system deposited on a phase-stable monolith provides unexpected superior structural stability.

[0151] It is noted that substantial conversion of methane still occurred even after the collapse of monoliths 1 and 2. This is believed to be due to the reforming activity provided by the Rh / α-Al2O3 on α-Al2O3 monolith catalytic system used for monoliths 3 and 4.

[0152] Additional Aspects Aspect 1: A hydrocarbon reforming catalyst system and supporting structure comprising: support structure, a catalyst having reforming activity, and A metal oxide support layer that is thermally phase stable at 800°C to 1600°C and comprises stabilized zirconia, perovskite, pyrochlore, spinel, hibonite, zeolite, oxides belonging to corundum (or oxides of the corundum group) or combinations thereof. and A hydrocarbon reforming catalyst system and support structure, wherein the catalyst and the metal oxide support layer comprise a catalyst system supported by one or more surfaces of a support structure, the catalyst system comprising 0.5 wt % or more (or alternatively 5 wt % or more) of the combined weight of the catalyst system and support structure.

[0153] Aspect 2: A method for forming a catalyst system, comprising: forming a catalyst system comprising a catalyst having reforming activity and containing Ni, Rh, Ru, Pd, Pt, Cu, Ir or a combination thereof, and a metal oxide support layer which is thermally phase stable at 800°C to 1600°C and contains an oxide belonging to stabilized zirconia, perovskite, pyrochlore, spinel, hibonite, zeolite, corundum, or a combination thereof; supporting a catalyst system on one or more surfaces of a support structure; annealing the supported catalyst system and support structure at an annealing temperature of 1000° C. or greater to form an annealed catalyst system and support structure; and exposing the annealed catalyst system and supporting structure to cyclic reforming conditions comprising a reforming step and a regeneration step, the cyclic reforming conditions including a peak temperature of 1000° C. or greater in the presence of a hydrocarbon feed to form H; Optionally, the annealing temperature is greater than said peak temperature.

[0154] Aspect 3: The method of aspect 2, wherein the regeneration step comprises a molar excess of O2 of 20% or more relative to the stoichiometric molar amount due to combustion of fuel during the regeneration step.

[0155]

[0023] Embodiment 4: The method of embodiment 2 or 3, wherein the catalyst system comprises a washcoat supported by one or more surfaces of a support structure.

[0156] Aspect 5: A method for reforming hydrocarbons in a cyclic reaction environment, comprising: reacting under combustion conditions a mixture comprising a fuel and 0.1% by volume or more of O2 in a combustion zone within a reactor, thereby heating one or more surfaces in the reaction zone (or one or more surfaces in the reaction zone) to a regenerative surface temperature of 1000° C. or more; The 0.1% by volume or greater O2 comprises 120% or greater of the stoichiometric molar amount of O2 for combustion of the fuel, the reaction zone comprising a catalyst system supported by one or more surfaces of a support structure; A reductant comprising a reformable hydrocarbon. a The reactant stream is exposed to one or more surfaces in the reaction zone, a Increasing the temperature of the reactant stream, as well as R a exposing the reactant stream to a catalyst system in a reaction zone at a temperature of at least 1000°C to form a product stream comprising H2. Consisting of Reaction zone a The flow direction for the reactant stream is opposite to the flow direction for the mixture, The catalyst system comprises a catalyst and a metal oxide support layer, the catalyst having reforming activity and comprising Ni, Rh, Ru, Pd, Pt, Cu, Ir or a combination thereof, the metal oxide support layer comprises an oxide belonging to stabilized zirconia, perovskite, pyrochlore, spinel, hibonite, zeolite, corundum or a combination thereof, and optionally (or as an option) the metal oxide support layer has thermal phase stability at 800°C to 1600°C.

[0157] Aspect 6: The method of aspect 5, wherein the 0.1% by volume or more O2 comprises 125% to 200% of the stoichiometric molar amount of O2 for combustion of the fuel.

[0158]

[0023] In a seventh embodiment, the metal oxide support layer comprises one or more metal oxides, and forming the catalyst system comprises mixing a powder comprising a catalyst with a powder comprising one or more metal oxides of the metal oxide support layer, the powder comprising one or more metal oxides of the metal oxide support layer being more than 20 μm in thickness. 2 The method according to any one of embodiments 2 to 6, having a surface area of ​​less than or equal to 1 / g.

[0159] Embodiment 8: The catalyst system, support structure or method of any one of embodiments 1 to 7, wherein the catalyst system comprises NiAl2O4.

[0160] Embodiment 9: The catalyst system, support structure or method of any one of embodiments 1-8, wherein a) the catalyst comprises a Ni-containing catalyst; b) the metal oxide support layer comprises α-Al2O3, yttria stabilized zirconia (YSZ), perovskite, or a combination thereof; c) the metal oxide support layer comprises 80 wt% or more α-Al2O3, based on the weight of the support layer; or d) a combination of two or more of a), b), and c).

[0161] Embodiment 10: The catalyst system, support structure or method of embodiment 9, wherein the Ni-containing catalyst further comprises Rh, Ru, Pd, Pt, Cu, Ir, Co, or a combination thereof.

[0162] Embodiment 11: The catalyst system, support structure or method of any of embodiments 1 to 10, wherein at least a portion of the catalyst system comprises a mixture (or a mixture or combination) of the catalyst and a metal oxide support layer.

[0163] Embodiment 12: The catalyst system, support structure or method of any one of embodiments 1 to 11, further comprising an intermediate bonding layer comprising a metal oxide, a first side of the intermediate bonding layer in contact with at least a portion of one or more surfaces of the support structure, and the catalyst system is supported on a surface of the support structure by being at least partially supported on a second side of the intermediate bonding layer, and the intermediate bonding layer optionally comprises α-Al2O3.

[0164] Embodiment 13: The catalyst system, support structure, or method of any of embodiments 1 to 12, further comprising a second catalytic zone comprising a second catalyst system, the second catalyst system comprising a second catalyst comprising Ni, Rh, Ru, Pd, Pt, Cu, Ir, or a combination thereof, the second catalyst system optionally being Rh, and the second catalyst system optionally further comprising a second metal oxide support layer that is thermally phase stable at 800° C. to 1600° C.

[0165] Embodiment 14: The catalyst system, support structure or method of any one of embodiments 1 to 13, wherein the support structure comprises a monolith having a cell density of from 50 cells per square inch to 900 cells per square inch, or the support structure comprises 80 wt.% or more of Al2O3, or a combination thereof.

[0166] Embodiment 15: The catalyst system, support structure or method of any one of embodiments 1 to 14, wherein the catalyst system comprises between 1.0% and 10% by weight of the combined weight of the catalyst system and support structure, or wherein 80% or more by weight of the catalyst system remains adhered to the support structure (or remains adhered to the support structure) after performing a mechanical friction test.

[0167] Additional embodiment A: Use of a catalyst system according to any of embodiments 1 to 15 for reforming hydrocarbons.

[0168] Additional Aspect B: A method for reforming hydrocarbons in a cyclic reaction environment, comprising: reacting a mixture comprising a fuel and at least 0.1% by volume O2 under combustion conditions in a combustion zone within a reactor, thereby heating one or more surfaces in the reaction zone (or one or more surfaces in the reaction zone) to a regenerative surface temperature of at least 800°C; the reaction zone comprises a catalyst system supported by one or more surfaces of a support structure; A reductant comprising a reformable hydrocarbon. a The reactant stream is exposed to one or more surfaces in the reaction zone, a Increasing the temperature of the reactant stream, as well as R a exposing the reactant stream to a catalyst system in a reaction zone at a temperature of at least 800°C to form a product stream comprising H2. Consisting of Reaction zone a The flow direction for the reactant stream is opposite to the flow direction for the mixture, 16. The method of claim 1, wherein the catalyst system comprises a catalyst and a metal oxide support layer, the catalyst having reforming activity and comprising Ni, Rh, Ru, Pd, Pt, Cu, Ir, or a combination thereof, the metal oxide support layer having thermal phase stability at 800° C. to 1600° C. and comprising an oxide belonging to stabilized zirconia, perovskite, pyrochlore, spinel, hibonite, zeolite, corundum, or a combination thereof, the catalyst system comprising 0.5 wt. % or more of the combined weight of the catalyst system and the support structure, and the catalyst system and support structure optionally comprising the catalyst system and support structure of any of the first to fifteenth embodiments.

[0169] While the present invention has been described and illustrated with reference to specific embodiments, those skilled in the art will recognize that the present invention is susceptible to modifications not necessarily illustrated herein, and for that reason, reference should be made only to the appended claims for purposes of determining the true scope of the present invention.

Claims

1. A hydrocarbon reforming catalyst system and supporting structure comprising: A support structure including a monolith; A catalyst having reforming activity, the catalyst comprising a Ni-containing catalyst; and A metal oxide support layer that is thermally stable at 800° C. to 1600° C. and contains α-Al 2 O 3 and 1. A hydrocarbon reforming catalyst system and support structure, wherein the catalyst and the metal oxide support layer comprise a catalyst system supported by one or more surfaces of the monolith, the catalyst system comprising NiAl 2 O 4 , and the catalyst system comprising 0.5 wt % or more of the combined weight of the catalyst system and the monolith.

2. a) The metal oxide support layer is made of α-Al, and the weight of the metal oxide support layer is 80% or more by weight. ２ O ３ 2. The hydrocarbon reforming catalyst system and support structure of claim 1, wherein the Ni-containing catalyst further comprises Rh, Ru, Pd, Pt, Cu, Ir, Co or a combination thereof; or c) a combination of a) and b).

3. and an intermediate bonding layer comprising a metal oxide, a first surface of the intermediate bonding layer contacting at least a portion of one or more surfaces of the monolith, the catalyst system being supported on a surface of the monolith by being at least partially supported on a second surface of the intermediate bonding layer, the intermediate bonding layer optionally comprising an α-Al ２ O ３ 3. The hydrocarbon reforming catalyst system and supporting structure of claim 1 or 2, comprising:

4. 4. The hydrocarbon reforming catalyst system and support structure according to any of claims 1 to 3, further comprising a second catalytic zone comprising a second catalyst system, said second catalyst system comprising a second catalyst comprising Ni, Rh, Ru, Pd, Pt, Cu, Ir or a combination thereof, said second catalyst system comprising a second metal oxide support layer that is thermally phase stable at 800°C to 1600°C, said second catalyst optionally comprising Rh.

5. The support structure comprises a monolith having a cell density of 50 to 900 cells per 6.4516 cm2, or the support structure comprises 80 wt. % or more of Al ２ O ３ 5. The hydrocarbon reforming catalyst system and supporting structure according to any one of claims 1 to 4, comprising or a combination thereof.

6. A method for forming the catalyst system and support structure of any one of claims 1 to 5, comprising the steps of: A catalyst comprising a Ni-containing catalyst and a metal oxide support layer that is thermally stable at 800° C. to 1600° C. and includes α-Al 2 O 3 to form a catalyst system including NiAl 2 O 4 ; supporting said catalyst system on one or more surfaces of a support structure comprising a monolith; annealing the supported catalyst system and the monolith at an annealing temperature of 1000° C. or greater to form an annealed catalyst system and monolith; and exposing the annealed catalyst system and monolith to cyclic reforming conditions comprising a reforming step and a regeneration step, the cyclic reforming conditions including a peak temperature of 1000° C. or greater in the presence of a hydrocarbon feed; ２ To form The method comprising:

7. a) supporting the catalyst system on one or more surfaces of the monolith comprises forming a washcoat suspension comprising the catalyst system, and exposing one or more surfaces of the support structure to the washcoat suspension to support the catalyst system on one or more surfaces of the support structure; or b) the metal oxide support layer comprises one or more metal oxides, and forming the catalyst system includes mixing a powder comprising the catalyst with a powder comprising one or more metal oxides of the metal oxide support layer, the powder comprising one or more metal oxides of the metal oxide support layer being more than 20 mm thick. ２ The method of claim 6, wherein the surface area is less than or equal to 1 / g.

8. Supporting the catalyst system on one or more surfaces of the monolith comprises: depositing an intermediate bonding layer on at least a portion of one or more surfaces of said monolith; and supporting at least a portion of said catalyst system in said intermediate binder layer; The method of claim 6, comprising:

Images