Method and apparatus for recovering carbon from carbon-containing gas

Abstract

The purpose of the present invention is to provide a method for recovering carbon from a carbon-containing gas, wherein carbon contained in a carbon-containing gas including carbon monoxide can be recovered and recycled. The method for recovering carbon from a carbon-containing gas is characterized by comprising: a step for separating carbon from carbon monoxide by bringing a carbon-containing gas including carbon monoxide into contact with a porous material; and a step for recovering the carbon, wherein moisture and hydrogen contained in the carbon-containing gas satisfy expression (1). In expression (1), [H2O] represents the concentration (vol%) of moisture contained in a reformed mixed gas, and [H2] represents the concentration (vol%) of hydrogen contained in the reformed mixed gas.

Description

[Technical field]

[0001] The present invention relates to a method and an apparatus for recovering carbon from a carbon-containing gas containing carbon monoxide. In particular, the present invention relates to a method and an apparatus for recovering carbon contained in a carbon-containing gas containing carbon monoxide, the carbon-containing gas being contained in a blast furnace gas, exhaust gas, or the like discharged from various industries. [Background technology]

[0002] All industries are being asked to reduce carbon dioxide emissions, including in accordance with the SDGs and the Paris Agreement. Methods for reducing the amount of carbon dioxide contained in exhaust gases include either replacing industrial processes that generate carbon dioxide with processes that do not use carbon, or removing carbon from the carbon dioxide-containing gases that are emitted. In the latter method, the carbon dioxide is generally removed from the exhaust gases either as is or as a carbon compound other than carbon dioxide (e.g., hydrocarbons).

[0003] As a countermeasure technology for reducing carbon dioxide, a technology has been reported in which a monohydric alcohol and carbon dioxide are reacted using cerium oxide as a catalyst to produce a carbonate ester (see, for example, Patent Document 1). That is, Patent Document 1 discloses a method for producing a carbonate ester using a catalyst structure for producing a carbonate ester, and discloses that a monohydric alcohol and carbon dioxide are reacted in the presence of the catalyst structure and a hydrating material to produce a carbonate ester.

[0004] Furthermore, a technology for efficiently removing carbon dioxide from a gas to be treated that contains carbon dioxide has been disclosed (for example, see Patent Document 2). That is, Patent Document 2 discloses a method for directly contacting the gas with an adsorbent in a reaction vessel to which water is supplied and discharged, thereby separating carbon dioxide directly from the gas to be treated. The method for separating carbon dioxide from the gas to be treated described in Patent Document 2 involves washing an adsorbent that has been poisoned and has a reduced amount of carbon dioxide adsorption with water, thereby washing away the poisoning components (acids, metal salts, etc.) attached to the adsorbent and exposing the surface of the adsorbent, thereby recovering the carbon dioxide adsorption capacity of the adsorbent. [Prior art documents] [Patent documents]

[0005] [Patent Document 1] International Publication No. 2020 / 013135 [Patent Document 2] International Publication No. 2018 / 179351 [Non-patent literature]

[0006] [Non-Patent Document 1] Materials Transactions, Vol.58, No.12(2017)pp.1742 to 1748 “Development of Manufacturing Principle of Porous Iron by Carbothermic Reduction of Composite of Hematite and Biomass Char” Summary of the Invention [Problem to be solved by the invention]

[0007] However, the above-mentioned conventional techniques have the following problems. That is, the countermeasure techniques for reducing carbon dioxide, such as the technique for producing carbonate esters disclosed in Patent Documents 1 and 2, all separate and remove carbon dioxide as it is or as a carbon compound, and are not methods that can recover the carbon contained in carbon dioxide itself. In addition, carbon dioxide gas can be reformed into carbon monoxide by the water-gas shift reaction. Therefore, if there is a method that can recover carbon itself from carbon monoxide, it would be possible to recover carbon from carbon dioxide by a method that combines the reaction with the water-gas shift reaction. However, there is a problem in that no method has been proposed that can recover carbon from carbon monoxide.

[0008] The present invention has been made in consideration of the above circumstances, and has an object to provide a method and apparatus for recovering carbon from a carbon-containing gas, which can recover carbon contained in carbon monoxide gas and recycle the carbon. [Means for solving the problem]

[0009] The method for recovering carbon from a carbon-containing gas according to the present invention, which advantageously solves the above-mentioned problems, includes a step of contacting a carbon-containing gas that contains carbon monoxide and satisfies formula (1) with a porous material to separate carbon from the carbon monoxide, and a step of recovering the carbon.

number

[0010] The method for recovering carbon from a carbon-containing gas according to the present invention includes the steps of: (a) contacting the carbon-containing gas with the porous material in an atmosphere of 500 to 800°C; (b) contacting the carbon-containing gas with the porous material in an atmosphere of 1.0 to 10 atm; (c) the porous material has an open porosity of 50 to 99% as measured by Archimedes' method; (d) the porous material contains at least one selected from iron, platinum, nickel, cobalt, rhodium and palladium; (e) the porous material is one or two types of iron selected from iron oxide and reduced iron; (f) the carbon-containing gas contains carbon monoxide generated by a reforming reaction of a raw material gas containing carbon dioxide, the raw material gas being heated to 800 to 1200°C to obtain a mixed gas by supplying hydrogen gas to the raw material gas; (g) the mixed gas contains all or a portion of the off-gas generated after contacting the carbon-containing gas with the porous material; (h) supplying hydrogen gas so that the hydrogen concentration in the mixed gas is 58 volume percent or more; (i) It is believed that a more preferable solution would be to remove moisture contained in the raw material gas and moisture generated by the reforming reaction of the raw material gas.

[0011] Furthermore, the carbon recovery device from a carbon-containing gas according to the present invention comprises: (j) The apparatus includes a carbon separation section that separates carbon from the carbon monoxide by contacting a carbon-containing gas containing carbon monoxide with a porous material, and a carbon recovery section that recovers the carbon. Effect of the Invention

[0012] According to the present invention, it is possible to recover carbon constituting carbon monoxide contained in a carbon-containing gas and recycle the carbon. Furthermore, according to the present invention, it is possible to recover carbon from carbon dioxide by using a gas obtained by reforming carbon dioxide contained in an exhaust gas, a blast furnace gas, or the like into carbon monoxide through a reaction combined with a water-gas shift reaction. [Brief description of the drawings]

[0013] [Figure 1] FIG. 1 is a schematic diagram showing an example of a process of a carbon recovery method according to an embodiment of the present invention. [Diagram 2]2A is a schematic diagram of a carbon separation unit provided in a carbon recovery device used to carry out a carbon recovery method according to the present embodiment, and FIG. 2B is an enlarged photograph showing an example of the form of a porous material in the carbon separation unit. [Diagram 3] FIG. 1 is a schematic diagram showing an example of a process of a carbon recovery method according to an embodiment of the present invention. [Figure 4] 1 is a graph showing the hydrogen addition ratio (volume %) to the exhaust gas used in the carbon recovery method according to the present embodiment and the gas composition after reforming and H2O removal at 800°C. [Diagram 5] 1 is a graph showing the relationship between the elapsed time (min) employed for carrying out the carbon recovery method according to the present embodiment and the temperature (° C.) in the gas reforming furnace. [Figure 6] 1 is a graph showing the relationship between the aeration time (min) of a carbon-containing gas and the mass increase rate ΔW (mass %) of a porous material when the carbon recovery method according to the present embodiment is carried out. [Figure 7] 7(a) and 7(b) are photographs showing the state of iron whiskers molded into a tablet shape before and after aeration with a carbon-containing gas when the carbon recovery method according to the present embodiment is carried out. Fig. 7(a) is a photograph showing the state of the iron whiskers before aeration with a carbon-containing gas, and Fig. 7(b) is a photograph showing the state of the iron whiskers after aeration with a carbon-containing gas. [Figure 8] This is an enlarged photograph taken with a scanning electron microscope (SEM) showing the state of iron whiskers after a carbon-containing gas was passed through them. [Figure 9] 1 shows an XRD profile of iron whiskers after being aerated with a carbon-containing gas. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0014] Hereinafter, the carbon recovery method from a carbon-containing gas according to the present embodiment will be described with reference to the drawings. Each drawing is a schematic diagram and may differ from the actual one. In addition, the following embodiments are examples of devices and methods for embodying the technical idea of ​​the present invention, and the configurations thereof are not limited to those described below. In other words, the technical idea of ​​the present invention can be modified in various ways within the technical scope described in the claims.

[0015] [First embodiment] A method for recovering carbon from a carbon-containing gas according to the first embodiment will be described. The method for recovering carbon from a carbon-containing gas according to the present embodiment includes a step of contacting a carbon-containing gas containing carbon monoxide with a porous material to separate carbon from the carbon monoxide, and a step of recovering the carbon. Hereinafter, each step of the method for recovering carbon from a carbon-containing gas according to this embodiment will be described.

[0016] <Step of contacting a carbon-containing gas with a porous material to separate carbon from carbon monoxide> FIG. 1 is a schematic diagram showing an example of a process of the carbon recovery method for recovering solid carbon from a carbon-containing gas according to the present embodiment. The carbon-containing gas only needs to contain carbon monoxide, which is the raw material of the carbon to be recovered, and may contain carbon dioxide, hydrogen, moisture, and the like in addition to the carbon monoxide. However, the moisture and hydrogen contained in the carbon-containing gas must satisfy the following formula (1). The carbon-containing gas used in the carbon recovery method for recovering solid carbon from a carbon-containing gas according to the present embodiment may be a gas generated in an existing manufacturing process, such as an exhaust gas or a blast furnace gas, that is used as is. For this reason, the carbon-containing gas often contains carbon monoxide, carbon dioxide, hydrogen, and moisture.

number

[0017] Carbon monoxide contained in the carbon-containing gas is the raw material for the carbon to be recovered. The carbon that constitutes the carbon monoxide contained in the carbon-containing gas is separated from the carbon monoxide by a bimolecular decomposition reaction (I) in which two molecules of carbon monoxide are decomposed, or by a unimolecular decomposition reaction (II) in which one molecule of carbon monoxide reacts with hydrogen, as shown in the following chemical reaction formulas (I) and (II).

[0018] [ka]

[0019] [ka]

[0020] The carbon monoxide contained in the carbon-containing gas preferably has a CO / (CO+CO2) ratio of 0.5 or more, more preferably a CO / (CO+CO2) ratio of 0.7 or more. This allows solid carbon to be efficiently recovered from carbon monoxide. The carbon-containing gas may be prepared by supplying carbon monoxide, carbon dioxide, and hydrogen from respective containers filled with these gas components so that the volume ratios of these gas components are the above-mentioned predetermined ratios.

[0021] In addition, the carbon-containing gas may be a gas that uses blast furnace gas discharged from an iron-making blast furnace or exhaust gas discharged from an automobile, a gas turbine, an incinerator, a thermal power plant, or a factory as it is, so long as it contains a predetermined amount of carbon monoxide. In addition, the carbon-containing gas may be a gas that uses blast furnace gas or exhaust gas as a raw material and adjusts the above-mentioned volume ratio of carbon monoxide and carbon dioxide by adding gas components that are insufficient to these gases. In addition, the carbon-containing gas may be a gas that uses blast furnace gas or exhaust gas as a raw material and adjusts the above-mentioned volume ratio of carbon monoxide and carbon dioxide by chemically treating these gases.

[0022] For example, blast furnace gas contains 21-23 volume % carbon monoxide, 19-22 volume % carbon dioxide, 2-3 volume % hydrogen, and 53-56 volume % nitrogen, and can be used as a carbon-containing gas as it is. Blast furnace gas is produced by partially burning coke, heavy oil, and pulverized coal charged into a blast furnace with air, turning them into reducing gas mainly composed of carbon monoxide and nitrogen, which then reduces iron ore. Therefore, by appropriately setting the combustion conditions of the coke, etc. in the blast furnace, the volume ratio of each gas component contained in the blast furnace gas can be adjusted. In addition, the volume ratio of each gas component present in the exhaust gas can be adjusted by the combustion conditions of the fuel that is the raw material of the exhaust gas.

[0023] The contact of the carbon-containing gas with the porous material and the separation of carbon from carbon monoxide contained in the carbon-containing gas are carried out in a carbon separation section of a carbon recovery apparatus used to carry out the carbon recovery method according to the present embodiment. The carbon separation section is provided with a packed bed filled with a porous material.

[0024] FIG. 2 is a schematic diagram showing an outline of a carbon separation section provided in a carbon recovery apparatus employed to carry out the carbon recovery method according to the present embodiment. As shown in FIG. 2, a porous material 102 is filled inside a reaction tower 101 provided in a carbon separation section 100 of the carbon recovery apparatus. The porous material 102 is held by a sample holder 101a provided inside the reaction tower 101. The form of the porous material 102 is not particularly limited as long as the carbon-containing gas passes through the porous material 102 and the decomposition reaction of carbon monoxide contained in the carbon-containing gas proceeds. The form of the porous material 102 may be, for example, a porous material molded into a tablet shape, a porous material molded into a honeycomb structure, a porous material molded into a flush structure, or the like, as shown in FIG. 2(b). Furthermore, the porous material may be a layered molded body. In addition, a plurality of layered molded bodies may be installed inside the reaction tower 101 as the porous material 102. In addition, a buffer layer 103 composed of granular material made of an oxide such as aluminum oxide may be provided below the porous material.

[0025] A carbon-containing gas containing carbon monoxide is supplied from the lower part of the reaction tower 101 equipped in the carbon separation unit 100. The carbon-containing gas supplied to the reaction tower 101 passes through the porous material 102 provided inside the reaction tower 101, and comes into contact with the porous material 102. The carbon monoxide contained in the carbon-containing gas is preferably contacted with the porous material 102 in the system of the carbon separation unit 100 under an atmosphere of a predetermined temperature and pressure. For this reason, the carbon separation unit 100 may be equipped with a temperature control device such as a heater for setting the inside of the system to a predetermined temperature range. The carbon-containing gas containing carbon monoxide is supplied from a supply pipe 104 installed in the lower part of the reaction tower 101. The off-gas after the carbon-containing gas containing carbon monoxide is brought into contact with the porous material 102 is discharged from an exhaust gas pipe 105.

[0026] Carbon constituting carbon monoxide contained in the carbon-containing gas is separated from carbon monoxide in the system of the carbon separation section 100. Carbon constituting carbon monoxide contained in the carbon-containing gas is separated from carbon monoxide by a bimolecular decomposition reaction (I) of carbon monoxide or a unimolecular decomposition reaction (II) of carbon monoxide, which are shown in the following chemical reaction formulas (I) and (II). The carbon separated from carbon monoxide is adsorbed on the surface of the porous material 102 or carburizes the interior of the porous material 102.

[0027] [ka] [ka]

[0028] The carbon-containing gas is preferably contacted with the porous material 102 in an atmosphere of 500 to 800°C. If the temperature at which the carbon-containing gas is contacted with the porous material 102 is 500°C or higher, the decomposition reaction of carbon monoxide is promoted, and if the temperature is 800°C or lower, the thermal energy generated by the decomposition reaction of carbon monoxide can be effectively utilized. The temperature range at which the carbon-containing gas is contacted with the porous material 102 includes, for example, a temperature condition of 500 to 800°C adopted in direct reduction ironmaking using iron as the porous material 102. The carbon-containing gas is contacted with the porous material 102 by passing the carbon-containing gas through a packed bed of the porous material 102 provided in the carbon separation unit 100 system. This allows the decomposition reaction of carbon monoxide represented by chemical reaction formulas (I) and (II) to proceed. As the decomposition reaction of carbon monoxide proceeds, carbon is separated from carbon monoxide. The carbon separated from carbon monoxide is precipitated on the surface of the porous material 102. In addition, the carbon separated from the carbon monoxide carburizes the inside of the porous material 102, and then forms a carbon-metal solid solution or a metal carbide compound with the porous material 102 inside the porous material 102.

[0029] The contact between the carbon-containing gas and the porous material 102 is preferably carried out under an atmosphere of 1.0 to 10 atm. If the pressure at which the carbon-containing gas is contacted with the porous material 102 is 1.0 atm or more, this is a pressurized condition, and the chemical equilibrium of the decomposition reaction of carbon monoxide represented by chemical reaction formulas (I) and (II) shifts in the direction of separating carbon, and the decomposition reaction of carbon monoxide is promoted, which is preferable. On the other hand, if the pressure at which the carbon-containing gas is contacted with the porous material 102 is 10 atm or less, this is preferable because safety can be ensured when operating the carbon separation unit 100 from the viewpoint of legal regulations.

[0030] The porous material 102 that is contacted with the carbon-containing gas containing carbon monoxide preferably has an open porosity of 50% or more and 99% or less, more preferably 80% or more, as measured by Archimedes' method. If the open porosity of the porous material 102 is 50% or more, the carbon-containing gas containing carbon monoxide passes through the pores of the porous material 102, promoting the decomposition reaction of carbon monoxide, and carbon can be separated from the carbon monoxide. The carbon separated from the carbon monoxide is adsorbed inside the pores of the porous material 102. On the other hand, if the open porosity of the porous material 102 is 99% or less, the porous material 102 is preferably able to maintain thermal shock resistance caused by the carbon-containing gas containing carbon monoxide supplied to the porous material 102. The size of the pores of the porous material 102 is preferably 10 μm or more in diameter. The open porosity of the porous material is measured by the Archimedes method, and specifically, the value measured by the measurement method defined in the Japanese Industrial Standards (JIS R2205; 1992) can be used as the open porosity of the porous material 102.

[0031] The porous material 102 that is brought into contact with the carbon-containing gas containing carbon monoxide preferably contains at least one selected from iron, platinum, nickel, cobalt, rhodium, and palladium. That is, the porous material 102 may be composed of one metal element selected from iron, platinum, nickel, cobalt, rhodium, and palladium, or may be composed of a combination of two or more metal elements. Furthermore, the porous material 102 may be a metal compound containing one metal element selected from iron, platinum, nickel, cobalt, rhodium, and palladium as a carbide, oxide, carbonate, sulfate, oxalate, or the like.

[0032] Among these metals that are used as the porous material 102 that is brought into contact with a carbon-containing gas containing carbon monoxide, iron, platinum, and nickel are preferred. When platinum or nickel is used as the porous material 102, the platinum or nickel acts as a catalyst for the decomposition reaction of carbon monoxide and is less likely to deteriorate as a catalyst for the decomposition reaction, which is preferable. In addition, when platinum or nickel is used as the porous material 102, solid carbon is precipitated as graphite alone by the decomposition reaction of carbon monoxide, which is preferable.

[0033] It is more preferable that the porous material 102 with which the carbon-containing gas containing carbon monoxide is contacted is iron. By using iron as the porous material 102, it is possible to obtain austenite (γ-iron) formed by the carbon separated from carbon monoxide by the decomposition reaction of carbon monoxide carburizing the porous material 102 and then dissolving in iron. It is also preferable that the porous material 102 is used as the porous material 102, since it is possible to obtain cementite (iron carbide) formed by the carbon separated from carbon monoxide by the decomposition reaction of carbon monoxide carburizing the porous material 102 and then reacting with iron. Austenite (γ-iron) and cementite (iron carbide) formed by the carbon separated from carbon monoxide by the decomposition reaction of carbon monoxide carburizing the iron of the porous material 102 have the same hardness as hardened steel, and can be used as a raw material for iron making as it is. Furthermore, it is preferable that the porous material 102 with which the carbon-containing gas is contacted is at least one or two kinds of iron selected from iron oxide and reduced iron.

[0034] It is particularly preferable that the porous material 102 that is brought into contact with the carbon-containing gas containing carbon monoxide is an iron whisker. The iron whisker is a metal crystal that grows in a whisker-like shape from the crystal surface toward the outside. When compressive stress occurs near the surface of the crystal, new crystals grow toward the outside of the original crystal to relieve the stress, and are formed. The starting point of the crystal growth of the iron whisker is small, and the iron whisker tends to continue to grow continuously. For this reason, the iron whisker is formed as a very long and whisker-like single crystal, and has a length of 10 μm or more for a diameter of about 1 μm. When the iron whisker is adopted as the porous material 102 that is brought into contact with the carbon-containing gas containing carbon monoxide, the carbon separated from the carbon monoxide by the decomposition reaction of the carbon monoxide carburizes the iron whisker, and iron whiskers composed of austenite (γ-iron) or iron whiskers composed of cementite (iron carbide) can be obtained.

[0035] The iron whiskers, which are the porous material 102 with which the carbon-containing gas containing carbon monoxide is brought into contact, can be produced, for example, by the method for producing iron whiskers described in Non-Patent Document 1. According to this method for producing iron whiskers, the open porosity of the porous material 102 is 90% or more, and iron whiskers with pore diameters of 10 μm or more can be obtained. The iron whiskers obtained by this method for producing iron whiskers also have a high open porosity, and can therefore be suitably used as the porous material 102 used in the method for recovering carbon from a carbon-containing gas of this embodiment. Note that even if a metal other than iron, such as platinum, is used as the metal for the porous material 102 with which the carbon-containing gas is brought into contact, the porous material 102 can be produced in the same manner.

[0036] <Carbon recovery process> The method for recovering carbon from a carbon-containing gas according to the present embodiment includes a step of recovering carbon separated from carbon monoxide. The step of recovering carbon is carried out, for example, in a system of a carbon recovery unit. Here, recovering carbon includes recovering carbon separated from carbon monoxide and precipitated on the surface of the porous material 102 or the inner surfaces of the pores of the porous material 102. Furthermore, recovering carbon includes recovering carbon as a carbon-metal solid solution formed by the reaction of carbon separated from carbon monoxide and carburizing the porous material 102 with a metal element contained in the porous material 102, or as a metal carbide compound.

[0037] Carbon decomposed by the decomposition reaction of carbon monoxide contained in the carbon-containing gas is precipitated on the surface of the porous material 102 or on the inner surfaces of the pores of the porous material 102. Carbon separated by the decomposition reaction of carbon monoxide contained in the carbon-containing gas carburizes the inside of the porous material 102 and reacts with the metal elements constituting the porous material 102 to form a carbon solid solution or a metal carbide compound. Carbon separated by the decomposition reaction of carbon monoxide contained in the carbon-containing gas is precipitated on the surface of the carbon solid solution or the metal carbide compound.

[0038] The step of recovering carbon can be performed by a carbon recovery unit included in a carbon recovery device employed to carry out the carbon recovery method according to this embodiment. The carbon recovery unit recovers carbon separated from carbon monoxide deposited on the surface of the porous material 102. The carbon recovery unit may include a sieve or the like for separating the separated solid carbon from the porous material 102. The carbon, or the carbon-metal solid solution or metal carbide compound separated by the sieve or the like is recovered in the carbon recovery unit.

[0039] The solid carbon separated from the carbon monoxide can be recovered by a powder separation operation using a carbon recovery section equipped with a sieve or the like. In addition, when the separated carbon carburizes the inside of the porous material 102 and reacts with the metal elements constituting the porous material 102 to become a carbon-metal solid solution or a metal carbide compound, the carbon can be recovered by recovering the carbon-metal solid solution or the metal carbide compound itself as it is. In addition, when the recovered carbon is used as a raw material for iron making, it is more preferable to use iron as the porous material 102, since the recovered carbon and the porous material 102 can be used together as a raw material for iron making without the need for a separation operation.

[0040] As described above, in the method for recovering carbon from a carbon-containing gas according to this embodiment, a carbon-containing gas containing carbon monoxide is brought into contact with the porous material 102 to promote the decomposition reaction of carbon monoxide, and carbon is separated and recovered as separated solid carbon, or a carbon-metal solid solution or metal carbide compound containing the carbon. Furthermore, the carbon recovery device used in the method for recovering carbon from a carbon-containing gas according to this embodiment includes the carbon separation section 100 and a carbon recovery section, and thereby can recover solid carbon separated from carbon monoxide, or a carbon solid solution or metal carbide compound containing the carbon.

[0041] The carbon recovered by the method for recovering carbon from a carbon-containing gas according to the present embodiment can be utilized, for example, as an energy source for power generation or the like, as an auxiliary material charged into a converter for thermal compensation of molten iron, as a raw material for iron making before quenching, etc. In other words, the method for recovering carbon from a carbon-containing gas according to the present embodiment can effectively utilize carbon as a recyclable resource by using carbon recovered from a carbon-containing gas that contains carbon monoxide.

[0042] As described above, according to the method for recovering carbon from a carbon-containing gas according to this embodiment, carbon constituting carbon monoxide gas contained in the carbon-containing gas can be recovered as solid carbon and the carbon can be recycled.

[0043] [Second embodiment] A carbon recovery method from a carbon-containing gas according to the second embodiment will be described. The carbon recovery method from a carbon-containing gas according to this embodiment is characterized in that, in the carbon recovery method according to the above embodiment, the carbon-containing gas contains carbon monoxide generated by a reforming reaction of a raw material gas in which a mixed gas obtained by supplying hydrogen to a raw material gas containing carbon dioxide is heated to 800 to 1200°C. That is, the carbon recovery method from a carbon-containing gas according to this embodiment is the same as each step included in the carbon recovery method according to the first embodiment, except that a carbon-containing gas containing carbon monoxide is prepared from a mixed gas using a raw material gas containing carbon dioxide as a raw material. Therefore, the carbon recovery method from a carbon-containing gas according to this embodiment will not be described in detail for the same steps as those included in the carbon recovery method according to the first embodiment. Below, a characteristic step included in the carbon recovery method from a carbon-containing gas according to this embodiment will be described.

[0044] Fig. 3 is a schematic diagram showing an example of a process of the carbon recovery method for recovering carbon from a carbon-containing gas according to the present embodiment. As shown in Fig. 3, the carbon-containing gas containing carbon monoxide is produced by using blast furnace gas, exhaust gas, or the like as a raw material gas, adding hydrogen gas, and carbon dioxide and water vapor, which are off-gases generated in the carbon separation section 100, to the raw material gas, reforming the mixed gas by a water-gas shift reaction, and removing moisture contained in the reformed gas. The carbon recovery device for carrying out the carbon recovery method from a carbon-containing gas according to the present embodiment may include, in addition to the above carbon recovery device, for example, a raw material gas storage section, a gas reforming section, a hydrogen supply section, a moisture removal section, and the like.

[0045] A raw material gas containing carbon dioxide and carbon monoxide is passed through a gas reforming unit such as a gas reforming furnace. The raw material gas is stored in a raw material gas storage unit. Examples of the raw material gas containing carbon dioxide and carbon monoxide include blast furnace gas and exhaust gas.

[0046] The raw gas storage unit stores raw gas such as blast furnace gas and exhaust gas supplied from the outside. Specifically, the raw gas is blast furnace gas discharged from an iron-making blast furnace, and exhaust gas discharged from automobiles, gas turbines, incinerators, thermal power plants, and factories, and contains carbon monoxide, carbon dioxide, hydrogen, water, nitrogen oxides, sulfur oxides, and the like. For this reason, the raw gas storage unit is preferably made of a material capable of storing the raw gas and is a container with excellent heat resistance and pressure resistance. The raw gas storage unit is connected to the gas reforming unit by a raw gas supply pipe. The raw gas is supplied to the gas reforming unit by the raw gas supply pipe.

[0047] Next, hydrogen gas supplied from the hydrogen supply unit is added to the gas reforming unit to obtain a mixed gas. Furthermore, such a mixed gas may contain all or a part of the off-gas obtained after the carbon-containing gas is brought into contact with the porous material 102 in the carbon recovery method from a carbon-containing gas according to the first embodiment. The off-gas is exhaust gas obtained after the carbon-containing gas containing carbon monoxide is brought into contact with the porous material 102. Since the off-gas contains carbon dioxide, the amount of carbon dioxide contained in the mixed gas can be increased by including the off-gas in the mixed gas. Then, the system of the gas reforming unit filled with the mixed gas is heated to 800 to 1200°C. When the system of the gas reforming unit is heated to within this temperature range, the carbon dioxide in the mixed gas present in the system of the gas reforming unit undergoes a water-gas shift reaction with hydrogen according to the following chemical reaction formula (III) to generate carbon monoxide and water.

[0048] [ka]

[0049] The water-gas shift reaction of carbon dioxide and hydrogen is a reversible reaction, and in a region where the reaction temperature exceeds 500°C, the chemical equilibrium of the water-gas shift reaction is biased toward the production of carbon monoxide. Therefore, in the method for recovering carbon from a carbon-containing gas of this embodiment, by setting the temperature in the gas reforming unit to 800 to 1200°C, carbon dioxide can be efficiently converted to carbon monoxide and a larger amount of carbon monoxide can be produced as a raw material for carbon to be separated. That is, in the method for separating carbon from a carbon-containing gas of this embodiment, by setting the temperature in the gas reforming unit to 800 to 1200°C, carbon dioxide can be efficiently reformed into carbon monoxide.

[0050] The water gas shift reaction that proceeds in the gas reforming section is a reaction between carbon monoxide gas and hydrogen in a mixed gas containing a raw material gas and hydrogen gas supplied from a hydrogen supplying section. Here, hydrogen is preferably supplied so that the hydrogen concentration in the mixed gas is 58% by volume or more. If the hydrogen concentration in the mixed gas is 58% by volume or more, the ratio of carbon monoxide gas can be increased in the water gas shift reaction, and carbon separated from carbon monoxide can be recovered in the subsequent process of separating carbon from carbon monoxide, which is preferable. The condition for the hydrogen concentration in the mixed gas to be 58% by volume or more is a condition under which carbon monoxide increases in the water gas shift reaction in a temperature range of 800 to 1200°C. Such a condition is derived from the relationship between the temperature and the equilibrium constant of the water gas shift reaction. The upper limit of the hydrogen concentration in the mixed gas may be less than 100% by volume, and the upper limit of the hydrogen concentration in the mixed gas may be determined according to the carbon dioxide concentration. In addition, it is preferable to use hydrogen derived from a non-fossil fuel as the hydrogen of the hydrogen gas supplied from a hydrogen supplying section installed outside the gas reforming section. This is preferable because it is possible to further suppress the emission of carbon dioxide. The supply amount of hydrogen gas supplied from the hydrogen supply unit can be set taking into consideration the amount of hydrogen contained in the raw material gas such as blast furnace gas and exhaust gas.

[0051] In this manner, in the gas reforming unit, a water-gas shift reaction of a mixed gas containing the raw material gas supplied from the raw material gas supply unit, the hydrogen gas supplied from the hydrogen supply unit, and the off-gas supplied from the carbon separation unit is carried out. For this reason, the gas reforming unit is preferably a container having a capacity, heat resistance, and pressure resistance sufficient to carry out the water-gas shift reaction of the mixed gas.

[0052] The hydrogen supply unit only needs to be able to supply hydrogen gas to the gas reforming unit under specified conditions. When hydrogen is supplied by storing hydrogen in a gaseous state at high pressure, the hydrogen supply unit is made of special stainless steel, aluminum alloy, polymer composite material, or the like. When hydrogen is supplied by storing hydrogen in a liquid form, the hydrogen supply unit is preferably a double-structured container including a vacuum area. When hydrogen is supplied by storing hydrogen in a metal, the hydrogen supply unit is preferably made of a hydrogen storage alloy.

[0053] The mixed gas is reformed by the water-gas shift reaction to produce a reformed gas. This reformed gas is supplied to a moisture removal section. The reformed gas contains moisture contained in the raw gas and moisture generated by the reforming reaction. Therefore, the moisture contained in the reformed gas after the water-gas shift reaction is removed by passing through the moisture removal section. The moisture can be removed by a method of passing the mixed gas through an adsorbent packed layer provided in the moisture removal section, a method of passing the mixed gas through a separation membrane, or the like. The reformed gas present in the gas reforming furnace system after the water-gas shift reaction must have the moisture contained in the raw gas and the moisture generated by the reforming reaction removed so as to satisfy the following formula (1).

[0054]

number

[0055] By making the moisture concentration of the reformed gas satisfy the above formula (1), the carbon recovery efficiency in the carbon recovery step is increased, which is preferable. The dehumidified gas from which moisture has been removed is supplied to the carbon separation section 100 as a carbon-containing gas containing carbon monoxide.

[0056] Thus, in the method for recovering carbon from a carbon-containing gas according to the second embodiment, a raw material gas such as a blast furnace gas or exhaust gas is used as a raw material, hydrogen is supplied to the raw material gas, carbon dioxide is converted to carbon monoxide by a water-gas shift reaction, and moisture is further removed to prepare a carbon-containing gas containing carbon monoxide. In the method for recovering carbon from a carbon-containing gas according to the second embodiment, the carbon-containing gas containing carbon monoxide is brought into contact with a porous material to advance the decomposition reaction of carbon monoxide, thereby separating carbon from the carbon monoxide and recovering it as separated solid carbon, or a carbon solid solution or metal carbide compound containing the carbon. Note that the raw material gas, mixed gas, and dehumidified gas in the second embodiment contain carbon monoxide, and therefore these gases are carbon-containing gases containing carbon monoxide.

[0057] As described above, according to the method for recovering carbon from a carbon-containing gas according to the second embodiment, it is possible to realize recovery of carbon from carbon dioxide contained in a raw material gas such as blast furnace gas or exhaust gas by using a gas obtained by reforming carbon dioxide contained in the raw material gas into carbon monoxide through a reaction combined with a water-gas shift reaction. Note that the method for recovering carbon from a carbon-containing gas according to this embodiment can use, as the raw material gas, not only blast furnace gas discharged from an ironmaking blast furnace, but also exhaust gas discharged from automobiles, gas turbines, incinerators, thermal power plants, factories, and the like, and is therefore a carbon recovery method with an extremely wide range of applications, and its technical value is also great from the viewpoint of reducing carbon dioxide.

[0058] [Other embodiments] Although the present invention has been described above with reference to the embodiment, the present invention is not limited to the above embodiment. Various modifications that can be understood by those skilled in the art can be made to the configuration and details of the present invention within the technical scope of the present invention. EXAMPLES

[0059] <Preparation of carbon-containing gas> In the carbon recovery method from a carbon-containing gas according to the present invention, an example of recovering carbon using exhaust gas as a raw material gas is shown below. In this example, exhaust gas having the composition of each gas component shown in Table 1 below was used as the raw material gas and supplied to a gas reforming furnace. Table 1 shows the components (volume %) contained in the exhaust gas.

[0060] [Table 1]

[0061] Hydrogen of different concentrations was supplied from outside the gas reforming furnace in which the exhaust gas was present, and mixed gases to be subjected to the water-gas shift reaction were prepared. Here, the concentrations of hydrogen supplied to the exhaust gas from outside the gas reforming furnace were set to 25 volume%, 50 volume%, 75 volume%, and 100 volume%, respectively. After preparing the mixed gases, the mixed gases were heated to 800°C and reformed by the water-gas shift reaction. The water-gas shift reaction of the mixed gas is shown in the following chemical reaction formula (III).

[0062] [ka]

[0063] Furthermore, the moisture generated within the gas reformer system after the water-gas shift reaction of the mixed gas was removed. The moisture generated within the gas reformer system was removed using an adsorbent and a hydrogen separation membrane. The water generated within the gas reformer system after the water-gas shift reaction becomes water vapor. The water vapor generated within the gas reformer system is transported to a moisture removal section together with carbon monoxide, carbon dioxide, and hydrogen present within the gas reformer system. The water vapor transported to the moisture removal section is cooled within the moisture removal section and changes to a liquid state.

[0064] Figure 4 shows the component composition of the dehumidified gas from which moisture has been removed after the water-gas shift reaction of the mixed gas. Figure 4 shows that even when the concentration of hydrogen supplied to the gas reformer increases, the concentration of carbon monoxide present in the gas reforming section remains almost constant. That is, Figure 4 shows that the concentration of carbon monoxide remains almost unchanged and the concentration of carbon dioxide decreases by supplying hydrogen to the gas reforming section. On the other hand, the total amount of gas present in the gas reforming section increases by supplying hydrogen to the gas reforming section, which shows that reforming by the conversion reaction from carbon dioxide to carbon monoxide is proceeding well.

[0065] <Passing carbon-containing gas through porous materials> By passing the dehumidified gas through a porous material, carbon was separated from the carbon monoxide contained in the dehumidified gas, and the carbon that constitutes the carbon monoxide was precipitated.

[0066] The carbon separation section used in the examples includes a tubular reaction tower in which the carbonization reaction of carbon monoxide contained in the carbon-containing gas occurs, a supply pipe for supplying the carbon-containing gas from the bottom of the reaction tower, a porous material layer provided inside the reaction tower, and a supply pipe for discharging the product gas generated after the carbonization reaction. The inner diameter of the tubular reaction tower was set to 53 mm. As the porous material provided in the carbonization equipment, a plurality of iron whiskers molded into tablets with a mass of 9.3 g and an open porosity of 97.7% were used. The porous material is installed in a layer made of granular alumina balls (particle size 10 mm). The porous material was manufactured according to the manufacturing method of iron whiskers described in Non-Patent Document 1.

[0067] Carbon-containing gas consisting of nitrogen, carbon monoxide, and hydrogen was passed through a supply pipe from the bottom of the reaction tower equipped with the carbon separation section. While controlling the temperature inside the carbonization system, a specific gas was supplied to separate carbon from carbon monoxide.

[0068] As shown in FIG. 5, the temperature of the carbon separation section was heated to 750°C, (1) then nitrogen-10% by volume hydrogen was passed through for 60 minutes. (2) Nitrogen was passed through for another 10 minutes to replace the inside of the carbon separation section system with an inert atmosphere. (3) Then, nitrogen-32% by volume carbon monoxide was passed through for 300 minutes. After passing nitrogen-32% by volume carbon monoxide, nitrogen was passed through for 10 minutes to replace the inside of the carbon separation section system with an inert atmosphere, and the temperature in the carbonization equipment system was lowered from 750°C to room temperature. The pressure in the carbon separation section system was maintained at 3.0 atm.

[0069] <Capture of separated carbon> Carbon separated from carbon monoxide was recovered by passing a carbon-containing gas through the porous material. The recovered carbon is powdered solid carbon precipitated on the surface of the porous material molded into a tablet shape, and a carbon solid solution or a metal carbide compound formed inside the porous material. Therefore, by comparing the mass of the porous material before and after passing the carbon-containing gas through it, the increase rate ΔW (mass%) of the mass of the porous material before and after passing the carbon-containing gas through it can be evaluated as the recovery rate of carbon obtained by separating it from carbon monoxide contained in exhaust gas, etc.

[0070] Fig. 6 is a graph showing the relationship between the time (min) for passing a carbon-containing gas through a porous material and the rate of increase in the mass of the porous material, ΔW (mass%). As shown in Fig. 6, the rate of increase in the mass of the porous material, ΔW (mass%), increases with the time (min) for passing a carbon-containing gas through the porous material. In other words, it was found that the decomposition reaction of carbon monoxide progresses with the passage of the time (min) for passing a carbon-containing gas through the porous material, carbon separated from carbon monoxide is precipitated, or a carbon-metal solid solution or a metal carbide compound is generated, and the mass of the porous material increases.

[0071] Figure 7 is a photograph showing the state of iron whiskers molded into tablet form before aerating a carbon-containing gas (Figure 7(a)), and the state of iron whiskers molded into tablet form after aerating a carbon-containing gas (Figure 7(b)). As is clear from Figure 7, the iron whiskers after aerating a carbon-containing gas were no longer able to maintain the shape they had before aerating the carbon-containing gas, when they were molded into tablet form. Furthermore, a qualitative analysis was carried out on the iron whiskers after aerating a carbon-containing gas. As a result, the surface of the iron whiskers after aerating a carbon-containing gas was covered with solid carbon separated from carbon monoxide.

[0072] FIG. 8(a) is an enlarged photograph taken by a scanning electron microscope (SEM) showing the state of iron whiskers after passing a carbon-containing gas through them. FIG. 8(b) is an enlarged photograph of the area surrounded by the dashed line in FIG. 8(a). FIG. 9 is an XRD profile of the iron whiskers after passing a carbon-containing gas through them. As shown in FIGS. 8 and 9, it has become clear that by passing a carbon-containing gas through the iron whiskers, the iron whiskers contain solid carbon that has been separated from carbon monoxide resulting from the decomposition reaction of carbon monoxide contained in the carbon-containing gas and precipitated on the surface, and cementite (iron carbide) that has been formed by carburizing the carbon.

[0073] In this way, by using the method for recovering carbon from a carbon-containing gas according to the present invention, it is possible to recover carbon separated from carbon monoxide by the decomposition reaction of carbon monoxide contained in a carbon-containing gas derived from a raw material gas such as an exhaust gas. Furthermore, by using the method for recovering carbon from a carbon-containing gas according to the present invention, it is possible to recover a carbon solid solution or a metal carbide compound formed by carburizing a porous material and reacting with the porous material as separated carbon. [Industrial Applicability]

[0074] The method for recovering carbon from a carbon-containing gas according to the present invention uses a gas obtained by reforming carbon dioxide contained in a raw gas such as an exhaust gas into carbon monoxide, and can realize the recovery of carbon from carbon dioxide contained in a raw gas such as an exhaust gas. Therefore, the method is extremely useful in industries that emit carbon dioxide, such as the steelmaking industry, energy-related industries such as coal-fired power generation, the chemical industry, the pulp and paper industry, and the food processing industry. [Explanation of symbols]

[0075] 100 Carbon Separation Section 101 Reactor 101a Sample holder 102 Porous materials (iron whiskers) 103 Buffer layer (aluminum ball) 104 Supply pipe (for carbon-containing gas) 105 Exhaust gas pipe

Claims

1. contacting a carbon-containing gas, including carbon monoxide, with a porous material to separate carbon from the carbon monoxide; and recovering the carbon, the porous material is iron and has an open porosity of 50 to 99% as measured by Archimedes' method; A method for recovering carbon from a carbon-containing gas, characterized in that the moisture and hydrogen contained in the carbon-containing gas satisfy formula (1). In the above formula (1), [H ２ O] represents the moisture concentration (volume %) contained in the reformed mixed gas, and [H ２ ] represents the hydrogen concentration (volume %) contained in the reformed mixed gas.

2. 2. The method for recovering carbon from a carbon-containing gas according to claim 1, wherein the carbon-containing gas is contacted with the porous material in an atmosphere at 500 to 800°C.

3. 3. The method for recovering carbon from a carbon-containing gas according to claim 1, wherein the carbon-containing gas is contacted with the porous material in an atmosphere of 1.0 to 10 atm.

4. 3. The method for recovering carbon from a carbon-containing gas according to claim 1 or 2, wherein the porous material is one or two types of iron selected from iron oxide and reduced iron.

5. The carbon-containing gas contains carbon monoxide generated by a reforming reaction of a raw material gas containing carbon dioxide, the raw material gas being heated to 800 to 1200°C to obtain a mixed gas.

2. The method of claim 1, wherein the mixed gas optionally comprises all or a portion of the off-gas after contacting the carbon-containing gas with the porous material.

6. 6. The method for recovering carbon from a carbon-containing gas according to claim 5, wherein hydrogen gas is supplied so that the hydrogen concentration in the mixed gas is 58% by volume or more.

7. 7. The method for recovering carbon from a carbon-containing gas according to claim 5, wherein moisture contained in the raw material gas and moisture generated by a reforming reaction of the raw material gas are removed.

8. a carbon separation section that separates carbon from the carbon monoxide by contacting a carbon-containing gas containing carbon monoxide with a porous material; a carbon recovery section for recovering the carbon, wherein the porous material is iron and has an open porosity of 50 to 99% as measured by Archimedes' method.