Abstract

A method for manufacturing a single-sided contact photovoltaic device (1), comprising the steps of: a) providing a photovoltaically active substrate (3) defining a plurality of alternating hole collecting zones (3a) and electron collecting zones (3b) arranged in parallel strips; b) depositing a conductive layer (5) over said zones (3a, 3b); c) depositing at least one conductive path (9) so as to extend along at least a portion of each of said zones (3a, 3b); d) selectively forming a dielectric layer (7) over each of the adjacent zones (3a, 3b) so as to leave exposed areas free of the dielectric at the interfaces between said zones (3a, 3b); e) etching the conductive layer (5) in the exposed areas; f) abutting a plurality of interconnection conductors (11a, 11b) so as to electrically interconnect at least some of the hole collecting zones (3a) with one another and to electrically interconnect at least some of the electron collecting zones (3b) with one another; A method for providing the above.

Description

[Technical field]

[0001] The project leading to this application has received funding from the European Union EU Horizon 2020 research and innovation programme under grant agreement No. 727523.

[0002] The present invention relates to the field of photovoltaic (PV) devices. More particularly, the present invention relates to single-sided contact solar cells. [Background technology]

[0003] Single-sided contact solar cells are constructed so that the electrical interconnections between the individual photovoltaic junctions are all located on one side of the solar cell, usually the back side of the solar cell, i.e., the side that faces away from the sun during use, and so that the electrical interconnections do not obscure the photovoltaic active area of ​​the device. Many back-contact PV cells use copper or silver bus bars that electrically connect with conductive fingers made of screen-printed silver paste that are arranged to collect current from the hole-collecting and electron-collecting zones of the PV device. These bus bars and fingers are printed in several steps on a selectively deposited insulating layer to ensure that the bus bars only contact the correct fingers and do not shunt current to the incorrect fingers. This requires the deposition of a significant amount of material, particularly silver material, which is expensive and uneconomical in terms of material costs, and also requires a large number of steps and relatively long processing times.

[0004] WO 2014 / 124675 A1 presents a partial solution to this problem by using back-contacted solar cells with a busbarless grid design that includes interrupted fingers interconnected with wires. However, the manufacture of such cells is complicated, particularly because a dielectric layer is provided over the entire surface of the cell and must be penetrated by the finger material to make electrical contact with the underlying photovoltaic active substrate. The choice of SiNx, SiOx or AlyOx as the dielectric layer requires multiple fabrication steps. [Prior art documents] [Patent documents]

[0005] [Patent Document 1] International Publication No. 2014 / 124675 Brochure Summary of the Invention [Problem to be solved by the invention]

[0006] SUMMARY OF THE PRESENT EMBODIMENT It is therefore an object of the present invention to at least partially overcome the above-mentioned shortcomings in the prior art. [Means for solving the problem]

[0007] This object is achieved by a method for producing a single-sided contacted photovoltaic device as claimed in claim 1.

[0008] The method comprises the following steps: a) providing a photovoltaically active substrate comprising one or more layers defining a plurality of alternating hole collecting zones (such as p-type semiconductor zones) and electron collecting zones (such as n-type semiconductor zones) arranged in adjacent parallel strips in the plane of the photovoltaically active substrate to define photovoltaic junctions. The substrate may be, for example, a wafer of monocrystalline silicon, which may further comprise, depending on the photovoltaic technology applied, one or more layers formed thereon to define silicon heterojunction cells constituting the substrate. Other PV technologies may also be possible in which the hole collecting zones and electron collecting zones are similarly arranged.

[0009] Further, as a method step, b) depositing, directly or indirectly, on the surface of said zone, a conductive layer, such as a layer of transparent conductive oxide (TCO), doped polycrystalline silicon, metal or similar material, which typically covers 90% to 100% of said zone.

[0010] Further, as a method step, c) depositing at least one conductive path on the conductive layer so as to extend along at least a portion of each zone, so that each zone has its own conductive path located thereon.

[0011] Further, as a method step, d) selectively forming a dielectric layer (ie, an insulating layer) over each zone so as to leave exposed areas free of dielectric at the junctions between adjacent zones.

[0012] Further, as a method step, e) etching the conductive layer in the exposed areas to remove the conductive layer material in the exposed areas and thus prevent shorting between adjacent zones, where a dielectric, which may be for example a resist material (e.g. photoresist, a thermosetting polymer or similar material), a self-assembled monolayer or other etch-resistant substance, acts as an etch mask to selectively etch the conductive layer, thereby leaving the underlying substrate exposed.

[0013] Further, as a method step, f) abutting a plurality of interconnect conductors to electrically interconnect at least a portion of the hole collecting zones to one another and to electrically interconnect at least a portion of the electron collecting zones to one another.

[0014] This method is particularly simple and uses a dielectric layer that serves a dual role, i.e. as an etch mask for etching the conductive layer and as part of the structure of the photovoltaic device, which reduces the number of processing steps to a minimum.

[0015] Advantageously, each zone has a number of conductive paths separated by gaps provided on each zone, with the gaps of each zone facing the conductive paths of the adjacent zone. Alternatively, each zone has an interrupted conductive path on each zone. This arrangement allows the interconnect conductors to be easily provided without the risk of electrical contact with a conductive path located on the wrong zone, thereby causing a shunt current. In effect, the interconnect conductors for the hole collecting zones pass between the conductive paths of the electron collecting zones and vice versa.

[0016] Alternatively, each conductive path may be continuous, and in step d) the dielectric layer is formed to a greater thickness or width to expose the conductive paths where electrical connection between the conductive paths and the interconnect conductor is not desired, and to a lesser thickness or width where electrical connection between the conductive paths and the interconnect conductor is desired.

[0017] Alternatively, each conductive path may be in the shape of a hollow quadrilateral, with each zone having one or more hollow quadrilateral conductive paths located above each zone. Such a shaped conductive path has two potential contact points for the interconnect wiring, which reduces the chance of a connection not being made when the interconnect wiring is abutted. In such a case, each quadrilateral shaped conductive path may be filled with InSn, BiSnAg or a similar solder material after step c) but before step f).

[0018] Advantageously, the dielectric material is an organic material such as a thermal resist, a photoresist, a polymer, or a self-assembled monolayer.

[0019] In any case, at least one conductive path may be completely embedded within the selectively formed dielectric layer, or may protrude from the dielectric layer, particularly if it has a continuous conductive path.

[0020] Advantageously, after step e) but before step f), an optional insulating layer can be applied on the areas of the substrate exposed by etching in step e) to eliminate any risk of electrical shunting caused by the conductors. Such a layer of insulator is separate from the dielectric layer described above and ensures that the interconnect conductors do not come into contact with the substrate and make undesired electrical contact.

[0021] Advantageously, step d) comprises at least one of the following steps:

[0022] Deposition of a dielectric layer followed by selective removal, for example by photolithography, laser ablation or similar techniques.

[0023] Selectively depositing a dielectric layer.

[0024] Selectively depositing dielectric stripes to demarcate the boundaries of the dielectric layer, followed by selectively depositing a dielectric layer between the dielectric stripes.

[0025] Advantageously, a layer of InSn, BiSnAg or similar solder material is provided on the conductive tracks and / or interconnect conductors, which improves the connection between the conductive tracks and the interconnect wiring.

[0026] Advantageously, step f) comprises applying heat and pressure to the electrical interconnection traces to at least partially embed the electrical interconnection traces in a dielectric material. If the dielectric is a photoresist material, this softens and / or melts the material and bonds the interconnection traces to the conductive tracks. Furthermore, if either or both of the interconnection traces and the conductive tracks have a layer of InSn, BiSnAg or similar solder material provided thereon, this layer of solder material can be melted to further improve the electrical connection.

[0027] Advantageously, the selectively formed dielectric remains in the finished photovoltaic device, minimizing the number of processing steps. If the dielectric itself is transparent, the resulting photovoltaic device can be used in a bifacial PV module so that reflected light striking the backside can also be collected.

[0028] The invention further relates to a single-sided contact photovoltaic device comprising:

[0029] a photovoltaically active substrate, such as a single crystal silicon wafer, defining a plurality of alternating hole collecting zones (e.g., p-type semiconductor zones) and electron collecting zones (e.g., n-type semiconductor zones) arranged in parallel strips in the plane of the layer;

[0030] · a conductive layer, made of transparent conductive oxide (TCO), doped microcrystalline silicon, metal or similar material, disposed directly or indirectly on the zones and patterned in such a way that the interfaces between adjacent zones are free of transparent conductive oxide, thus preventing short circuits between zones of different types;

[0031] at least one conductive path extending along at least a portion of each zone;

[0032] · A dielectric (i.e., insulator) layer located on the conductive layer;

[0033] A plurality of interconnect conductors arranged to electrically interconnect at least a portion of the hole collecting zones to one another and to electrically interconnect at least a portion of the electron collecting zones to one another.

[0034] The device is simple and can be manufactured by the methods described above in a minimal number of steps.

[0035] Advantageously, the dielectric material is an organic material such as a photoresist or a self-assembled monolayer.

[0036] Advantageously, an insulating layer may be disposed on at least the part of the substrate exposed by the etching, i.e. at the interface between the zones, to eliminate any risk of the interconnect conductors making undesired electrical contact with the substrate.

[0037] Further details of the invention will become clearer from the following description taken in conjunction with the accompanying drawings, in which: [Brief description of the drawings]

[0038] [Figure 1] FIG. 1 is a schematic plan view of a photovoltaic device according to a first embodiment of the present invention. [Diagram 2] FIG. 2 is a schematic partial cross-sectional view taken along line AA in FIG. [Diagram 3] 2 is a schematic partial cross-sectional view taken along line BB in FIG. 1; [Figure 4a] 2 is a schematic partial cross-sectional view along line BB of FIG. 1 for a method according to the invention; [Figure 4b] 2 is a schematic partial cross-sectional view along line BB of FIG. 1 for a method according to the invention; [Figure 4c] 2 is a schematic partial cross-sectional view along line BB of FIG. 1 for a method according to the invention; [Figure 4d]2 is a schematic partial cross-sectional view along line BB of FIG. 1 for a method according to the invention; [Diagram 5] FIG. 2 is a schematic plan view of a photovoltaic device according to a further embodiment of the present invention. [Figure 6] FIG. 6 is a schematic partial cross-sectional view taken along line BB in FIG. 5. [Figure 7] FIG. 2 is a schematic plan view of a photovoltaic device according to a further embodiment of the present invention. [Figure 8] FIG. 8 is a schematic partial cross-sectional view taken along line BB in FIG. [Figure 9] FIG. 2 is a schematic plan view of a photovoltaic device according to a further embodiment of the present invention. [Figure 10] 10 is a schematic partial cross-sectional view taken along line BB in FIG. 9. [Figure 11] FIG. 2 is a schematic plan view of a photovoltaic device according to a further embodiment of the present invention. [Figure 12] FIG. 12 is a schematic partial cross-sectional view taken along line BB in FIG. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0039] 1 to 3 show a first modified example of a photovoltaic device 1 according to the present invention, where FIG. 1 is a plan view of the cell 1, FIG. 2 is a partial cross-sectional view taken along line AA, and FIG. 3 is a partial cross-sectional view taken along line BB.

[0040] The cell 1 comprises at least one photovoltaically active substrate 3, which includes alternating zones of hole collecting zones 3a (such as p-type semiconductor zones) and electron collecting zones 3b (such as n-type semiconductor zones) constituting a photovoltaic junction, which upon exposure to light collect holes and electrons, respectively, thereby generating a voltage between each type of zone 3a and 3b. The zones 3a, 3b extend parallel to one another in the plane of the layer 3, as is commonly known. The interface between each pair of adjacent zones 3a, 3b is indicated by a dashed line.

[0041] The photovoltaically active substrate 3 may be of any suitable photovoltaic technology, for example the silicon heterojunction technology based on crystalline silicon wafers in which the zones 3a, 3b are defined by depositing appropriately doped thin or stacked layers on the wafer, or the silicon homojunction technology in which the zones 3a, 3b are formed by incorporating suitable dopants into a monocrystalline silicon wafer. It should be noted that in the sense of the present invention, the substrate 3 should not necessarily be considered monolithic, but may also be an assembly of layers (wafer, doped layer, tunnel layer, passivation layer, etc.) in the above mentioned heterojunction technology, etc. Furthermore, any other suitable PV technology may be used in which the zones 3a, 3b are formed as adjacent zones.

[0042] A first side of the photovoltaically active substrate 3 (top side in Figures 2 and 3) is used for contacts. This side is typically the back side of the cell 1 and faces away from the main direction of incident light (i.e. away from the sky when installed outdoors), although it is not excluded that this side could be the front side of the cell, i.e. the side where the light is incident.

[0043] To avoid short-circuit currents between different types of zones, on each zone 3a, 3b, a transparent conductive oxide (TCO), doped polycrystalline silicon, metal or similar material (e.g., at least 1.0×10 4 A conductive layer 5, such as a layer of tin oxide (having a conductivity of 0.1 S / m), is provided in the arrangement such that there is a gap between the conductive layers 5 provided on each adjacent zone 3a, 3b. A typical spacing between adjacent conductive layers 5 is 1 μm to 1000 μm, preferably 50 μm to 400 μm. When TCO is used for the conductive layer 5, typical materials are indium doped tin oxide, indium doped zinc oxide, aluminum doped zinc oxide, boron doped zinc oxide or similar materials. The area without the conductive layer 5 is typically centered on the interface between the zones 3a and 3b, but can also be asymmetrically positioned with respect to the interface.

[0044] Over each conductive layer 5 is a patterned dielectric (i.e., insulator) layer 7 (e.g., 1.0×10 -3 3a, 3b) in which at least one conductive path 9 is at least partially embedded extending along at least a portion of each zone 3a, 3b. As shown, the conductive paths 9 are interrupted such that the center point of each conductive path 9 in any given zone 3a, 3b faces the center point of the gap between the conductive paths 9 in the adjacent zones 3b, 3a. The conductive paths 9 may be fully embedded in the dielectric layer 7 or may protrude from the dielectric layer 7. The conductive paths typically have a width of 1 μm to 300 μm, preferably 20 μm to 100 μm, and a thickness of 1 μm to 50 μm, preferably 3 μm to 20 μm. Although the sections of the conductive path 9 are shown as single lines, each zone 3a, 3b may have multiple parallel conductive paths, the number of which may vary depending on the sheet resistance of the conductive layer 5 and the sheet resistance of the substrate 3 underlying the conductive layer 5, and may have 1 to 10, preferably 1 to 4 parallel conductive paths.

[0045] The conductive tracks 9 may be formed, as is commonly known, from, for example, silver paste, copper plating, gold plating, conductive ink, or any other convenient conductive material. Silver paste is the best option among these, and can be printed, for example, by screen printing, onto the conductive layer 5, but this should not be understood to exclude others. If the conductive tracks 9 are completely embedded in the dielectric layer 7, materials that are not stable to the etchant in question can be safely used, i.e., they are protected from the etchant by the dielectric layer 7.

[0046] The dielectric layer 7 is typically organic and can be, for example, a photoresist, a self-assembled monolayer, or any other convenient layer that is selectively removable or selectively depositable, for reasons that will become apparent in the following detailed description of the method of the invention. In the case of a resist material, the typical thickness is 0.05 μm to 40 μm, more preferably 1 μm to 15 μm. Such resists are typically organic layers formed from compounds with carbon chains that are at least three carbons long, and can be cured by heat, UV light, etc. If the conductive tracks 9 are to be completely embedded in the resist material 7, the thickness of the resist material 7 covering the top of the conductive tracks should be 0.05 μm to 40 μm. The layer 7 can be a photoresist patterned by well-known lithographic techniques, a thermosetting resist deposited by screen printing or CNC controlled printing, a hot melt polymer deposited by CNC controlled printing, or (depending on the material) deposited by a vacuum process such as physical vapor deposition, chemical vapor deposition, or similar deposition. Furthermore, the dielectric material 7 is ideally transparent to visible and infrared light. This feature is particularly advantageous for bifacial applications.

[0047] A number of interconnecting conductors, i.e. interconnecting wires 11a, 11b, running substantially perpendicular to the conductive tracks 9, interconnect each pair of zones 3a, 3b respectively and carry the current. For this purpose, the interconnecting wires 11a, 11b are in electrical contact with the corresponding conductive tracks 9, for example by soldering with a low-temperature solder or simply by gluing with a dielectric layer 7, if the latter is a resin such as a resist material. A technique particularly suited for interconnecting wires is described in the non-patent document "SMARTWIRE SOLAR CELL INTERCONNECTION TECHNOLOGY", Faes et al., Proc. 29, pp. 2111-2115, 2003. thEur. Photovoltaic Sol Energy Conf.), a copper wire coated with a thin low melting point alloy layer supported by a polymer foil, however, conventional wires or ribbons connected to the conductive tracks 9 by solder, conductive ink, silver paste, conductive organic coatings (such as PEDOT-PSS), mechanical contacts or similar techniques could also be used.

[0048] At least in the gaps between the stacks of conductive layers 5 and dielectric layers 7, i.e., at the interface between zones 3a and 3b, an optional insulating layer 15 (e.g., 1.0×10 -3 The insulating layer 15 may be provided with a dielectric layer 15 (having a conductivity of less than 1000 nm / m). This insulating layer 15 thus covers the areas of the substrate 3 not covered by the dielectric layer 7, eliminating the risk of the interconnect conductors 11a, 11b coming into electrical contact with the surface of the substrate 3 and causing current shunting. The insulating layer 15 is distinct from the dielectric layer 7 and is deposited in a separate (optional) step (see below). The insulating layer 15 may extend to the same height as the dielectric layer 7 above the substrate 5 or may have a thickness such that the upper surface of the insulating layer 15 is located above or below the dielectric layer 7. The material of the insulating layer 15 may be the same or different from the dielectric layer 7 (see materials also suitable for the insulating layer 15 listed for the dielectric layer 7) and may also be formed by the processes listed for this dielectric layer 7.

[0049] Alternatively, the insulating layer 5 may be deposited over the entire surface of the cell.

[0050] The completed battery 1 may then be further encapsulated (not shown), as is commonly known, for example by laminating it into a sandwich construction having a suitable transparent polymer encapsulant, a suitable front sheet, and a suitable back sheet.

[0051] Figures 4a-4c illustrate diagrammatically in cross section along line B-B a method according to the invention for manufacturing the battery 1 of figures 1-3.

[0052] As shown in Figure 4a, first the photoactive layer 3 is prepared as detailed above. As shown, this is a single crystal silicon heterojunction wafer with hole collecting zones 3a and electron collecting zones 3b already fabricated, and any other optional layers already provided on top of the photoactive layer 3.

[0053] A conductive layer 5 is then deposited directly or indirectly over the entire surface of the photoactive layer 3, and conductive tracks 9 (only one of which is shown here) are formed thereon. If the conductive tracks 9 are made from silver paste, they can simply be printed, for example by screen printing, CNC controlled printing or any other convenient type of printing. In the case of copper, the conductive tracks 9 can be deposited over the entire surface and selectively etched, as is commonly known.

[0054] A dielectric layer is then applied over the surface of the conductive layer 5 and over the conductive tracks 9. The conductive tracks 9 may be completely embedded in the dielectric layer (as shown) or may protrude from the free surface of the dielectric layer, allowing simple electrical testing of the cell 1 to be performed before the interconnection lines 11a, 11b are applied. This dielectric is an organic compound and may be, for example, a photoresist, a self-assembled monolayer or a similar material. In the case of self-assembled monolayers, this dielectric may be, for example, 12,12,13,13,14,14,15,15,15,15-nonafluoropentadecylphosphonic acid, 12,12,13,14,14,15,15,16,16,17,17-tridecafluoroseptadecylphosphonic acid, 12,12,13,13,14,14,15,15,16,16,17,17,18,18,19,19,19-heptadecafluorononadecylphosphonic acid, 10-((3,3,4,4,5,5,6,6,7,7,8,8,9,9,10,10,10-heptadecafluoro The conductive path 9 may be a self-assembled monolayer (SAM) such as 5,7,7-trimethyl-2-(4,4-dimethylpentan-2-yl)octylphosphonic acid, diethyl-12-pentafluorophenoxydodecylphosphonic acid, octadecylphosphonic acid, decylphosphonic acid, dodecylphosphonic acid, octylphosphonic acid, 10,11-bis(2,2,3,3,4,4,5,5,6,6,7,7,8,8,9,9,9-heptadecafluorononyl)icosane-1,20-diyldiphosphonic acid, or any other convenient self-assembled monolayer (SAM). The SAM layer is so thin that the conductive path 9 will protrude from the SAM layer.

[0055] In the illustrated variant, in FIG. 4b, the dielectric layer 7 is patterned by a well-known selective UV exposure lithography process, through a mask 13, using laser ablation or similar techniques. In the case of a photoresist, which may be a positive or negative resist, depending on the type of resist used, either the exposed or the unexposed parts of the dielectric layer 7 are then sequentially removed using a solvent. Alternatively, in an embodiment not shown, the dielectric layer 7 may be deposited in a patterned manner, for example by printing, thus eliminating the step of selective removal. As a result, the area directly adjacent to the interface of zones 3a and 3b is free of dielectric 7 and therefore exposed to erosion from the etchant.

[0056] The patterned dielectric layer 7 is then used as a mask to etch the underlying conductive layer 5, resulting in discrete contacts with the underlying zones 3a, 3b without current shunting between them, as shown in FIG. 4c. This etching can be carried out, for example, with dilute acid, after which the workpiece is rinsed. If an insulating layer 15 is present, it is then deposited, for example by screen printing, CNC controlled printing or a similar technique, as shown diagrammatically by the arrows. If the insulating layer 15 is not deposited selectively in the gaps between the regions of the dielectric layer 7, but over the entire surface, other deposition processes such as vacuum processes (i.e. PVD, CVD in the function of the material) can be used.

[0057] Subsequently, as shown in FIG. 4d, the interconnection wires 11a, 11b are abutted as machine supported wires or ribbons or as a "smart wire" type assembly as described above. Heat and pressure may be applied during this step, so that the interconnection wires 11a bond to the corresponding conductive tracks 9. As described in the cited publications (which are incorporated by reference in their entirety) if the interconnection wires 11a, 11b are coated with a low temperature solder material, this low temperature solder material melts and solders together the conductive tracks 9 and the interconnection wires 11a, 11b at the contact points. Similarly, if the conductive tracks 9 are made of, for example, copper and coated with a low temperature solder material, this low temperature solder material melts and solders the conductive tracks 9 to the interconnection wires 11a, 11b at the required points.

[0058] Furthermore, when the conductive tracks 9 are completely embedded in the dielectric material 7, whether or not the interconnection lines 11a, 11b and / or conductive tracks 9 are coated with a low temperature solder, application of heat at a sufficient temperature will cause the dielectric material 7 to soften and / or melt, if the dielectric material is a resist material, such that contact is established with the conductive tracks 9. Upon cooling, the resist material bonds the interconnection lines 11a, 11b as desired at the predetermined locations where they contact the conductive tracks.

[0059] Typical processing conditions for this step include lamination at 70°C-250°C, preferably 90°C-170°C, under a partial vacuum with a load pressure of 10 kPa-100 kPa (0.1 bar-1 bar), preferably 60 kPa-100 kPa (0.6 bar-1 bar), with the temperature being chosen as appropriate depending on the properties of the dielectric 7 and any solder material present on the interconnection traces 11a, 11b and / or conductive paths 9.

[0060] Typical properties of photoresist materials suitable as dielectric 7 are given in the table below.

[0061] [Table 1]

[0062] Figures 5 and 6 show a further variant of a photovoltaic device 1 according to the invention in views similar to those of Figures 1 and 3. In this variant, the conductive tracks 9 are continuous and run parallel to each other for their entire length.

[0063] To prevent shunting, the dielectric layer 7 is thicker in the zones (indicated by dots) where no connection is made between the interconnection lines 11a, 11b and the conductive tracks 9. The example shown in FIG. 6 represents a section along line BB in FIG. 5, where the area of ​​the dielectric layer 7 (resist layer in this example) is thinner on zone 3b than on zone 3a. As a result, when the interconnection lines 11a, 11b are applied and heated, contact is made only with the conductive tracks 9 on zone 3a, but not with the conductive tracks 9 on zone 3b, leaving an amount of resist that insulates the interconnection lines 11b from the underlying conductive tracks 9 and prevents shunting. The exact amount of heat, pressure and time for applying the interconnection lines 11a, 11b can be determined by routine experimentation to ensure electrical connection when desired and avoid it when not desired.

[0064] Although not shown, if one considers the portion along line CC in FIG. 5, it is clear that the dielectric layer 7 on zone 3a is thicker than the dielectric layer 7 on zone 3b, so that the interconnect wiring 11b contacts the correct conductive path 9 on zone 3b.

[0065] Regarding the deposition of the dielectric layer 7, since the thickness of the dielectric layer 7 varies depending on where the connection is to be made, the dielectric layer 7 can be deposited in two steps to create two layers overlapping each other, or after forming the resist layer as in Figure 4, additional photoresist material can be deposited, for example by CNC controlled printing, screen printing or similar techniques, before or after patterning the dielectric 7, to create thicker areas where no contact is to be made. Additionally, it is also possible to use two different dielectric materials to create the bulk and thicker portions of the dielectric layer 7.

[0066] Figures 7 and 8 show a further variant of a photovoltaic device 1 according to the invention. This variant differs from the variant of Figures 1 to 3 in that the bulk of the dielectric layer 7, which is also a resist layer, is deposited in two stages. The first of these is the selective deposition of relatively thin resist stripes 7a (shown as dotted lines in Figure 7), which are deposited by CNC-controlled printing, screen-printing or a similar technique so as to delimit the entire area of ​​the dielectric layer. Such thin stripes can be printed relatively accurately by screen-printing or CNC-controlled printing, and after curing form dam walls between which the remainder of the dielectric layer 7 can be printed, for example by screen-printing. These thin dielectric stripes 7a form a barrier to precisely define the boundaries of the dielectric, preventing the dielectric from bleeding from one zone 3a to another 3b and preventing current shunting due to unetched parts of the conductive layer 5 that should be removed. It should be noted that the thin dielectric stripes 7a can be of the same material as the remainder of the dielectric layer 7, or of a different material.

[0067] This same principle can be applied to the embodiments of FIGS.

[0068] 9 and 10 show yet another variation of the photovoltaic device 1 according to the invention, which differs from the variation of FIG. 1 in that each conductive track 9 is formed as a closed hollow elongated quadrilateral with its major axis aligned with the major axis of the zones 3a, 3b. This arrangement provides two connection points between each conductive track 9, reducing the possibility of the conductive track 9 not connecting with the corresponding interconnection wire 11a, 11b. It is also possible to join each quadrilateral track 9 with relatively thick joint conductive tracks to adjacent tracks, and the thick areas of the dielectric 7 in the embodiment of FIGS. 5 and 6 are used to prevent undesired connections with these joint conductive tracks. Furthermore, in a variation not shown, the hollow interior of the conductive tracks 9 can be filled with InSn, BiSnAg or similar low temperature solder alloys in order to obtain a larger conductor area while minimizing the amount of silver used.

[0069] 11 and 12 show a further variant of a photovoltaic device 1 according to the invention, in which the conductive tracks 9 are also quadrilateral in shape, several quadrilaterals extending along each zone 3a, 3b adjacent to the edge of the corresponding zone 3a, 3b, and arranged in a row, alternating from one zone to the next as in FIG.

[0070] The vias 9 are arranged to act as dam walls to prevent overflow of the dielectric 7 selectively deposited within the vias 9, for example by screen printing, CNC printing or similar techniques. Alternatively, a low temperature solder material can be provided within each quadrilateral via 9, as described above in connection with Figures 9 and 10.

[0071] 7 and 8, the relatively thin stripes 7a of the dielectric (again shown by dotted lines) function as insulating dam walls, extending between each quadrilateral conductive path 9 in the extensions of the sides of each quadrilateral conductive path 9 that run parallel to the zones 3a, 3b. Thus, when the dielectric 7 is provided within the dam walls formed by the conductive paths 9 and the relatively thin stripes 7a of the dielectric, the dielectric 7 cannot spread across the interface between the zones 3a, 3b and cannot cause current division.

[0072] It should be noted that the conductive paths 9 extending perpendicular to the zones 3a, 3b can be omitted and the conductive paths 9 are thus formed from parallel conductor pairs.

[0073] Of course, further different configurations of the conductive tracks 9 are possible.

[0074] In view of the above, it can be seen that the manufacture of all variations of the photovoltaic device 1 of the present invention is relatively simple and can be carried out with a minimum of steps and minimal material costs. If the dielectric 7 is a thermally curable resist, a photoresist, or a self-assembled monolayer, it does not need to be removed and can be left in the device.

[0075] Thanks to the absence of busbars, the photovoltaic device 1 according to the invention is particularly suitable for bifacial applications in which light arriving on the backside of the device 1 is also converted into electricity. Typically, a busbar or large area conductor on the backside of the device 1 (i.e. the side facing away from the sky) would block most of the light incident on the backside, reducing efficiency. The relatively small area of ​​the conductors in the device of the invention blocks less backside incident light, thus improving efficiency. In such applications, the dielectric 7 (and the relatively thin stripes 7a of the dielectric, if present) are preferably nearly transparent to the wavelengths of interest that can be photoconverted by the device 1, to avoid shading by the dielectric 7.

[0076] Although the invention has been described with reference to specific embodiments, variations thereto can be made without departing from the scope of the invention as defined in the appended claims.

Claims

1. A method for producing a single-sided contacted photovoltaic device (1), comprising the steps of: a) providing a photovoltaically active substrate (3) defining a plurality of alternating hole collecting zones (3a) and electron collecting zones (3b) arranged in parallel strips, followed by: b) depositing a conductive layer (5) over said zones (3a, 3b), followed by c) depositing at least one conductive path (9) extending along at least a part of each of said zones (3a, 3b), followed by d) selectively forming a dielectric layer (7) over each of said zones (3a, 3b) so as to leave exposed areas free of dielectric at the interfaces between adjacent zones (3a, 3b), followed by e) etching said conductive layer (5) in said exposed areas, followed by f) providing a plurality of interconnecting conductors (11a, 11b) to electrically interconnect at least some of said hole collecting zones (3a) with one another and to electrically interconnect at least some of said electron collecting zones (3b) with one another; A method for providing the above.

2. 2. The method according to claim 1, wherein each of said zones (3a, 3b) has a plurality of conductive tracks (9) separated by gaps formed on each of said zones (3a, 3b), said gaps of each of said zones (3a, 3b) facing the conductive tracks (9) of said adjacent zones (3b, 3a).

3. 2. The method of claim 1, wherein each of the conductive paths (9) is continuous, and in step d) the dielectric layer (7) is formed to a greater thickness or width where an electrical connection between the conductive path (9) and the interconnecting conductors (11a, 11b) is not desired, and to a lesser thickness or width where an electrical connection between the conductive path (9) and the interconnecting conductors (11a, 11b) is desired.

4. 2. The method according to claim 1, wherein each of the conductive paths (9) is in the shape of a hollow quadrilateral.

5. 5. The method according to claim 4, wherein each of said zones (3a, 3b) comprises a plurality of hollow quadrilateral-shaped conductive tracks (9) located above each of said zones (3a, 3b).

6. A method according to claim 4 or 5, characterized in that after step c) but before step f), each of the quadrilateral-shaped conductive tracks (9) is filled with a solder material.

7. The method according to any one of the preceding claims, wherein the dielectric layer (7) is an organic material, including a photoresist or a self-assembled monolayer.

8. 8. The method according to claim 7, wherein the at least one conductive path (9) is completely embedded in the selectively formed dielectric layer (7) or protrudes from the selectively formed dielectric layer (7).

9. The method according to any one of the preceding claims, comprising after step e) and before step f) the step of applying an insulating layer (15) onto at least a part of the photovoltaically active substrate 3 in the areas etched in step e).

10. The method according to any one of claims 1 to 9, wherein step d) comprises: - depositing and subsequently selectively removing said dielectric layer (7), - selectively depositing said dielectric layer (7), - selectively depositing dielectric stripes (7a) to demarcate the boundaries of the dielectric layer (7), followed by selectively depositing the dielectric layer (7) between the dielectric stripes; The method comprises at least one of:

11. The method according to any one of the preceding claims, wherein a layer of solder material is provided on the conductive tracks (9) and / or the interconnect conductors (11a, 11b).

12. The method according to any one of claims 1 to 11, wherein step f) comprises applying heat and pressure to the interconnect conductors (11a, 11b) to at least partially embed the interconnect conductors (11a, 11b) in the dielectric (7).

13. The method according to any one of the preceding claims, wherein the selectively formed dielectric layer (7) remains in the completed photovoltaic device.