Laser cladding repair process for cross shafts

A technology of laser repairing and cross shaft, which is applied in the field of laser cladding, can solve the problems of harsh use environment of cross shaft, wear of bearing block size, large heat input, etc., and achieve good wear resistance, optimization of overlap, and high fusion rate Effect

CN102828181AInactive Publication Date: 2012-12-19DANYANG HONGTU LASER TECH
5 Cites 17 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
Publication Date
2012-12-19
Estimated Expiration
Not applicable · inactive patent
Patent Text Reader

Abstract

The invention relates to a laser cladding repair process for cross shafts. The process comprises the following steps of: A. carrying out treatment on the surface of the cross shaft, and carrying out failure analysis; B. carrying out 80-150 DEG C overall preheating on the cross shaft; C. according to failure analysis results of the cross shaft, optimizing process parameters, and carrying out laser cladding, wherein adopted alloy powder comprises the following components in percentage by weight: less than or equal to 0.1% of C, 10-13% of Cr, 1.5-2.5% of B, 1-2% of Si, 0.5-1.2% of Mo, 8-12% of Mn, 6-12% of W, 5-15% of TiO2, and the balance of Fe; and D. carrying out detection. According to the laser cladding repair process for the cross shafts, disclosed by the invention, through carrying out the laser cladding on the surface of the cross shaft, the size of the cross shaft can meet the application requirements, and the hardness and the wear resistance of the cross shaft subjected to repair exceed the original hardness and the original wear resistance of the cross shaft.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to a laser cladding method, in particular to a laser cladding repair method of a cross axis. Background technique

[0002] The cross shaft is a transmission component that connects four directions of rotation. It is used in the transmission connection structure of large machinery. The manufacturing process is complicated, the cost is high, and the construction period is long. Due to the particularity of its parts, the cross shaft is required to achieve high mechanical properties with soft inside and rigid outside. Medium and low carbon steel or alloy steel with good toughness is selected as the base material. While ensuring the toughness of the central part, the outer circular surface of the connecting bearing is required to achieve high hardness and wear resistance, so the surface of this part should be carburized Quenching to improve surface hardness, strength and wear resistance. The working environment of the cross shaft is ...

Examples

Embodiment Construction

[0017] The specific steps of the laser repair process of the cross shaft of the present embodiment are as follows:

[0018] A. Treat the surface of the cross shaft to be repaired, and conduct failure analysis on the cross shaft.

[0019] Remove the dust, oil, rust, etc. on the cross shaft; measure the size of each part of the cross shaft, determine the failure part and its wear amount, and check whether the cross shaft has deformation; remove the fatigue layer of 0.5mm of the cross shaft failure part by grinding, And clean it.

[0020] B. Preheat the cross shaft as a whole, and the preheating temperature is 100°C.

[0021] C. According to the failure analysis results of the cross shaft, optimize the process parameters and perform laser cladding.

[0022] The pre-set powder feeding method is adopted, and the fast cross-flow carbon dioxide laser is used as the light source to perform continuous lap scanning on the parts to be repaired on the cross axis. Focus) is 270mm, the s...