Preparation method of orange-flavored reconstituted tobacco and orange-flavored reconstituted tobacco

Abstract

The invention provides a preparation method of orange-flavored reconstituted tobacco and the orange-flavored reconstituted tobacco. The preparation method comprises steps as follows: taking, soaking, drying and grinding fresh orange peels, adding orange peel powder to a paper base during coating, and performing coating, drying and the like. According to the method, after the powder with the proper particle size is prepared from the orange peels, a coating technology is organically combined, various properties of the reconstituted tobacco are improved, effective ingredients of the orange peels are applied to preparation of the reconstituted tobacco more scientifically and efficiently, compared with common reconstituted tobacco with no orange peel powder added, the prepared orange-flavored reconstituted tobacco is higher in smoke concentration, better in fragrance texture and richer in fragrance, the synergistic effect of the fragrance of fresh oranges and effective ingredients of a coating liquid is played, and prepared cigarettes are fine, lasting and smooth in smoke and higher in overall oral comfort degree.

Description

technical field

[0001] The invention relates to the technical field of tobacco, and more specifically, to a method for preparing orange-flavored reconstituted tobacco leaves and orange-flavored reconstituted tobacco leaves. Background technique

[0002] Reconstituted tobacco (Reconstituted Tobacco), also known as tobacco sheet, homogeneous tobacco or reconstituted tobacco, has the characteristics of high filling value, good combustion performance, and low tar release. It is important for cigarettes to replace or partially replace traditional shredded tobacco with reconstituted tobacco. It is one of the effective means to reduce the harm of charcoal.

[0003] The process of preparing reconstituted tobacco leaves by the papermaking method usually includes soaking and extracting tobacco raw materials, concentrating the extract as a coating solution, refining the soaked slag to prepare a paper base, and coating the coating solution on The reconstituted tobacco leaves are obtain...

Examples

Embodiment 1

[0032] S1. Commercially purchased oranges, take fresh orange peel, soak in boiling water (100°C) for 10 seconds, take out and drain the water, and dry in an oven at 40°C until the moisture content is 12%;

[0033] S2. Use a 200-gram swing-type high-speed universal pulverizer (model: DFY-200) to pulverize the orange peel to obtain orange powder; the particle size of the powder is 60-120 mesh;

[0034] S3. Add orange powder to the paper base, the addition amount is 20% of the mass of the reconstituted tobacco leaf paper base, coat the reconstituted tobacco leaf paper base, and the coating amount is 40% to 45%, and the coated reconstituted tobacco leaves Dry at 105°C until the moisture content is 12%.

[0035] The coating liquid is prepared by adopting the following raw materials and preparation method: soaking and extracting tobacco stems and tobacco powder respectively. The conditions for the steeping and extraction of the tobacco stems are that the ratio of solid to liquid is...

Embodiment 2

[0042] S1. Commercially purchased oranges, take fresh orange peel, soak in boiling water (100°C) for 10 seconds, take out and drain the water, and dry in an oven at 40°C until the moisture content is 12%;

[0043] S2. Use a 200-gram swing-type high-speed universal pulverizer (model: DFY-200) to pulverize the orange peel to obtain orange powder; the particle size of the powder is 60 mesh;

[0044] S3. Add orange powder to the coating solution, the amount added is 20% relative to the mass of the reconstituted tobacco leaf paper base, and the reconstituted tobacco leaf paper base is coated with a coating amount of 40% to 45%, and the coated The reconstituted tobacco leaves were dried at 105°C until the moisture content was 12%.

[0045]The coating liquid is prepared by adopting the following raw materials and preparation method: soaking and extracting tobacco stems and tobacco powder respectively. The conditions for the steeping and extraction of the tobacco stems are that the r...

Embodiment 3

[0049] Others are the same as in Example 1, except that in S3, orange powder is added to the coating solution, the addition amount is 10% relative to the mass of the reconstituted tobacco paper base, and the coating amount is 40%.

[0050] The reconstituted tobacco leaves obtained in Example 3 were cut into shreds according to the existing conventional methods, rolled and then fitted with cellulose acetate filters to make sample cigarettes, and the smoke obtained from the reconstituted tobacco leaves without adding orange peel powder was used as a control cigarette, and all sample cigarettes were The rolling specifications of the samples are the same, and 10 professional smokers conduct sensory evaluation. Compared with the control smoke, the sample smoke evaluation results are as follows: the smoke concentration is moderate, the aroma texture is better, the clarity is better, and the aroma is transparent. Compared with the control sample, it has improved, the aroma is medium, ...

technical field

[0001] The invention relates to the technical field of tobacco, and more specifically, to a method for preparing orange-flavored reconstituted tobacco leaves and orange-flavored reconstituted tobacco leaves. Background technique

[0002] Reconstituted tobacco (Reconstituted Tobacco), also known as tobacco sheet, homogeneous tobacco or reconstituted tobacco, has the characteristics of high filling value, good combustion performance, and low tar release. It is important for cigarettes to replace or partially replace traditional shredded tobacco with reconstituted tobacco. It is one of the effective means to reduce the harm of charcoal.

[0003] The process of preparing reconstituted tobacco leaves by the papermaking method usually includes soaking and extracting tobacco raw materials, concentrating the extract as a coating solution, refining the soaked slag to prepare a paper base, and coating the coating solution on The reconstituted tobacco leaves are obtain...

Examples

Embodiment 1

[0032] S1. Commercially purchased oranges, take fresh orange peel, soak in boiling water (100°C) for 10 seconds, take out and drain the water, and dry in an oven at 40°C until the moisture content is 12%;

[0033] S2. Use a 200-gram swing-type high-speed universal pulverizer (model: DFY-200) to pulverize the orange peel to obtain orange powder; the particle size of the powder is 60-120 mesh;

[0034] S3. Add orange powder to the paper base, the addition amount is 20% of the mass of the reconstituted tobacco leaf paper base, coat the reconstituted tobacco leaf paper base, and the coating amount is 40% to 45%, and the coated reconstituted tobacco leaves Dry at 105°C until the moisture content is 12%.

[0035] The coating liquid is prepared by adopting the following raw materials and preparation method: soaking and extracting tobacco stems and tobacco powder respectively. The conditions for the steeping and extraction of the tobacco stems are that the ratio of solid to liquid is...

Embodiment 2

[0042] S1. Commercially purchased oranges, take fresh orange peel, soak in boiling water (100°C) for 10 seconds, take out and drain the water, and dry in an oven at 40°C until the moisture content is 12%;

[0043] S2. Use a 200-gram swing-type high-speed universal pulverizer (model: DFY-200) to pulverize the orange peel to obtain orange powder; the particle size of the powder is 60 mesh;

[0044] S3. Add orange powder to the coating solution, the amount added is 20% relative to the mass of the reconstituted tobacco leaf paper base, and the reconstituted tobacco leaf paper base is coated with a coating amount of 40% to 45%, and the coated The reconstituted tobacco leaves were dried at 105°C until the moisture content was 12%.

[0045]The coating liquid is prepared by adopting the following raw materials and preparation method: soaking and extracting tobacco stems and tobacco powder respectively. The conditions for the steeping and extraction of the tobacco stems are that the r...

Embodiment 3

[0049] Others are the same as in Example 1, except that in S3, orange powder is added to the coating solution, the addition amount is 10% relative to the mass of the reconstituted tobacco paper base, and the coating amount is 40%.

[0050] The reconstituted tobacco leaves obtained in Example 3 were cut into shreds according to the existing conventional methods, rolled and then fitted with cellulose acetate filters to make sample cigarettes, and the smoke obtained from the reconstituted tobacco leaves without adding orange peel powder was used as a control cigarette, and all sample cigarettes were The rolling specifications of the samples are the same, and 10 professional smokers conduct sensory evaluation. Compared with the control smoke, the sample smoke evaluation results are as follows: the smoke concentration is moderate, the aroma texture is better, the clarity is better, and the aroma is transparent. Compared with the control sample, it has improved, the aroma is medium, ...