Paint for bathroom cabinet board material and preparation process thereof

Abstract

The invention relates to the technical field of bathroom furniture, and concretely relates to a paint for a bathroom cabinet board material and a preparation process thereof. The paint comprises the following components: 18 to 42 parts of resin, 4 to 15 parts of additive resin, 15 to 35 parts of a solvent, 4 to 12 parts of an auxiliary agent, and 40 to 60 parts of a filler. In the present application, graphite powder, quartz, mica powder, kaolinite, diamond powder are added in the paint, graphite powder, mica powder and kaolin have large pores, quartz and diamond powder are added to graphite powder, quartz and mica powder, the pores can be filled, the pores can be reduced, and the molecular interaction between the pores after filling is strong. The external water vapor attached at the surface of the paint can be effectively removed, and the paint can effectively avoid the problem that when the paint and the water vapor are in contact for a long time, water vapor penetrates into the surface of the bathroom cabinet through the surface of the paint.

Description

Technical field:

[0001] The invention relates to the technical field of bathroom furniture, in particular to a paint used for a bathroom cabinet plate and a preparation process thereof. Background technique:

[0002] In China, bathrooms are not wet and dry. Bathroom cabinets are used in bathrooms and will be in a dark and humid environment for a long time. Cabinets made of wooden boards are prone to mildew and deformation. Wooden boards breed microorganisms in a dark and humid environment, causing the ash layer on the surface of the boards to fall off easily, and the bathroom cabinet is out of shape, which seriously affects the service life of the bathroom cabinet.

[0003] In the prior art, in order to overcome the above problems, people usually stick a barrier layer on the outer layer of the bathroom cabinet. The function of the barrier layer can prevent the water vapor from the external environment from adhering to the surface of the cabinet, so as to isolate the water va...

Examples

Embodiment 1

[0032] A paint for bathroom cabinet panels, comprising: 18kg of resin, 4kg of additive resin, 15kg of solvent, 4kg of auxiliary agent, and 40kg of filler; the resin is selected from amino resin; the additive resin is selected from acrylic modified epoxy resin, Acrylic resin, epoxy resin; solvent is selected from methyl isobutyl ketone; described filler is the mixture of lithopone, talcum powder, titanium dioxide, precipitated barium sulfate, bentonite, calcium carbonate; described auxiliary agent comprises graphite powder 13 parts, quartz 4 parts, kaolinite 18 parts, diamond powder 7 parts, mica powder 14 parts.

Embodiment 2

[0034] A paint for bathroom cabinet panels, comprising: 18kg of resin, 4kg of additive resin, 15kg of solvent, 4kg of auxiliary agent, and 40kg of filler; the resin is selected from amino resin; the additive resin is selected from acrylic modified epoxy resin, Acrylic resin, epoxy resin; solvent is selected from methyl isobutyl ketone; described filler is the mixture of lithopone, talcum powder, titanium dioxide, precipitated barium sulfate, bentonite, calcium carbonate; described auxiliary agent comprises graphite powder 13 parts, 4 parts of quartz, 18 parts of kaolinite, 7 parts of diamond powder, 14 parts of mica powder;

[0035] The additive is prepared by the following method: mixing graphite powder, quartz, mica powder, kaolinite, and diamond powder into a ball mill for grinding, passing through a 40-mesh sieve, adding deionized water and stirring for 20 minutes, and then filtering. Dry, crush again, and pass through a 100-mesh sieve to obtain the auxiliary agent.

Embodiment 3

[0037] A paint for bathroom cabinet panels, comprising: 18kg of resin, 4kg of additive resin, 15kg of solvent, 4kg of auxiliary agent, and 40kg of filler; the resin is selected from amino resin; the additive resin is selected from acrylic modified epoxy resin, Acrylic resin, epoxy resin; solvent is selected from methyl isobutyl ketone; described filler is the mixture of lithopone, talcum powder, titanium dioxide, precipitated barium sulfate, bentonite, calcium carbonate; described auxiliary agent comprises graphite powder 13 parts, 4 parts of quartz, 18 parts of kaolinite, 7 parts of diamond powder, 14 parts of mica powder;

[0038] The additive is prepared by the following method: mixing graphite powder, quartz, mica powder, kaolinite, and diamond powder into a ball mill for grinding, passing through a 40-mesh sieve, adding deionized water and stirring for 20 minutes, and then filtering. Dry, crush again, and pass through a 100-mesh sieve to obtain additives;

[0039] The pain...

Technical field:

[0001] The invention relates to the technical field of bathroom furniture, in particular to a paint used for a bathroom cabinet plate and a preparation process thereof. Background technique:

[0002] In China, bathrooms are not wet and dry. Bathroom cabinets are used in bathrooms and will be in a dark and humid environment for a long time. Cabinets made of wooden boards are prone to mildew and deformation. Wooden boards breed microorganisms in a dark and humid environment, causing the ash layer on the surface of the boards to fall off easily, and the bathroom cabinet is out of shape, which seriously affects the service life of the bathroom cabinet.

[0003] In the prior art, in order to overcome the above problems, people usually stick a barrier layer on the outer layer of the bathroom cabinet. The function of the barrier layer can prevent the water vapor from the external environment from adhering to the surface of the cabinet, so as to isolate the water va...

Examples

Embodiment 1

[0032] A paint for bathroom cabinet panels, comprising: 18kg of resin, 4kg of additive resin, 15kg of solvent, 4kg of auxiliary agent, and 40kg of filler; the resin is selected from amino resin; the additive resin is selected from acrylic modified epoxy resin, Acrylic resin, epoxy resin; solvent is selected from methyl isobutyl ketone; described filler is the mixture of lithopone, talcum powder, titanium dioxide, precipitated barium sulfate, bentonite, calcium carbonate; described auxiliary agent comprises graphite powder 13 parts, quartz 4 parts, kaolinite 18 parts, diamond powder 7 parts, mica powder 14 parts.

Embodiment 2

[0034] A paint for bathroom cabinet panels, comprising: 18kg of resin, 4kg of additive resin, 15kg of solvent, 4kg of auxiliary agent, and 40kg of filler; the resin is selected from amino resin; the additive resin is selected from acrylic modified epoxy resin, Acrylic resin, epoxy resin; solvent is selected from methyl isobutyl ketone; described filler is the mixture of lithopone, talcum powder, titanium dioxide, precipitated barium sulfate, bentonite, calcium carbonate; described auxiliary agent comprises graphite powder 13 parts, 4 parts of quartz, 18 parts of kaolinite, 7 parts of diamond powder, 14 parts of mica powder;

[0035] The additive is prepared by the following method: mixing graphite powder, quartz, mica powder, kaolinite, and diamond powder into a ball mill for grinding, passing through a 40-mesh sieve, adding deionized water and stirring for 20 minutes, and then filtering. Dry, crush again, and pass through a 100-mesh sieve to obtain the auxiliary agent.

Embodiment 3

[0037] A paint for bathroom cabinet panels, comprising: 18kg of resin, 4kg of additive resin, 15kg of solvent, 4kg of auxiliary agent, and 40kg of filler; the resin is selected from amino resin; the additive resin is selected from acrylic modified epoxy resin, Acrylic resin, epoxy resin; solvent is selected from methyl isobutyl ketone; described filler is the mixture of lithopone, talcum powder, titanium dioxide, precipitated barium sulfate, bentonite, calcium carbonate; described auxiliary agent comprises graphite powder 13 parts, 4 parts of quartz, 18 parts of kaolinite, 7 parts of diamond powder, 14 parts of mica powder;

[0038] The additive is prepared by the following method: mixing graphite powder, quartz, mica powder, kaolinite, and diamond powder into a ball mill for grinding, passing through a 40-mesh sieve, adding deionized water and stirring for 20 minutes, and then filtering. Dry, crush again, and pass through a 100-mesh sieve to obtain additives;

[0039] The pain...