laminated glass panel coating process and coated laminated glass panel

Abstract

A method for coating a laminated glass panel comprising: - providing a laminated glass panel to be coated comprising at least two sheets of glass joined by means of a polymer interlayer material; - providing a fluid decorative material; - incorporating a chemical hardener or a crosslinking catalyst into the fluid decorative material in a ratio P_cata between the mass of chemical hardener or crosslinking catalyst and the mass of decorative material in the determined fluid state; - forming at least one layer of decorative coating by applying the decorative material to the upper face of the laminated glass panel to be coated; - drying the layer of decorative coating by heating using a drying device having a setpoint temperature greater than or equal to 100°C and less than 140°C, the heating time at the setpoint temperature and / or the ratio P_cata being a function of said setpoint temperature.Figure for the abridged version: fig. 1.

Description

Title of the invention: Method for coating a laminated glass panel and coated laminated glass panel FIELD OF THE INVENTION

[0001] The present invention relates to a method of manufacturing a glass coated with a decorative layer and to such a glass.

[0002] More specifically, the invention relates to a method of coating a laminated glass panel with a decorative layer such as a reflective layer or a lacquer as well as to the coated laminated glass panel thus obtained. TECHNOLOGICAL BACKGROUND

[0003] In the field of glass coated with a decorative layer, two types of decorative layers are particularly appreciated: layers reflecting light so that the glass has the appearance of a mirror and decorative layers of the "lacquer" type, formed from a resin-rich paint and having a so-called stretched appearance.

[0004] Thus, a mirror typically consists of a monolithic glass with a thickness typically between 2 and 8 mm covered with a layer of silver which gives it its reflective power. The thickness of the silver layer is typically of the order of a few tens of nanometers and its surface mass is generally at least 700 mg / m2.

[0005] To improve the chemical and mechanical resistance of the silver layer, it can be covered with a protective varnish, most often with a thickness of the order of several micrometers.

[0006] Lacquered glass, for its part, classically consists of a monolithic glass, with a thickness typically between 2 and 12 mm, covered with a layer of decorative paint of the “lacquer” type – most often with a thickness of the order of several micrometers – which gives it the desired aesthetic appearance and which has satisfactory chemical and mechanical resistance characteristics.

[0007] These processes for coating monolithic glass, although satisfactory from an aesthetic point of view, do not make it possible to obtain sufficient mechanical resistance properties for certain applications, particularly in the building sector.

[0008] The safety of coated monolithic glasses obtained by conventional processes can be improved by means of an anti-shatter adhesive film placed on the back of the glasses and which retains the pieces of glass in the event of breakage, the mechanical performance of such a structure remaining limited since the risk of breakage is not or is only slightly modified by the presence of the anti-shatter film.

[0009] In the field of glass, it is also known to temper glass to improve its mechanical properties. Tempered glass cannot be re-cut after tempering. If we were to consider a decorative coating of tempered glass, we would therefore be limited by the shape of the piece of tempered glass before coating. It is understood that this choice is very limiting for applications in the building industry such as cupboard doors, tables, wall surfaces, which are often made to measure.

[0010] In the field of glass, it is still known to laminate glass to improve its mechanical properties. Laminated glass is an assembly of glass sheets and plastic interlayers, particularly in the form of a film, generally made of polyvinyl butyral (PVB) or ethylene vinyl acetate (EVA). The presence of the interlayer material increases the mechanical resistance to breakage and prevents the formation of splinters.

[0011] Various processes have been described which make it possible to obtain laminated glass mirrors or lacquered laminated glass, the decorative layer being interposed, or equivalently sandwiched, between two sheets of glass.

[0012] In particular, document GB224160 describes a method for obtaining a laminated glass mirror in which: - a reflective coating is deposited on a first sheet of glass, - then a second sheet of glass is glued onto the first sheet using of an adhesive such as polyvinyl butyral (PVB)

[0013] the reflective coating being interposed between the two sheets of glass.

[0014] Starting from such a method, it is not possible to simply reverse the order of the components to position the reflective coating on an external face of the final product. Indeed, on the one hand the reflective coating (or any other decorative coating) thus positioned would then be mechanically damaged by the calendering or transport rollers used for assembling the two sheets, and on the other hand the autoclaving phase on an industrial scale presents a risk of deterioration of the coatings of the layers of a given panel and of bonding of the glass panels to each other.

[0015] In addition, the optical defects of the mirror formed by the method of GB224160 are determined by those of the glass layer on which the reflective coating is deposited.

[0016] Similarly, WO2009 / 081077 describes a lacquered laminated glass in which a layer of lacquer is sandwiched between two sheets of glass, the assembly being subjected to a heat treatment under pressure to ensure the bond between the sheets of glass. Such a method requires the use of a lacquer that is resistant to heat treatment under pressure, which limits the choice of colors. In addition, the good adhesion of PVB can be affected, particularly in the case of varnishes with solvents. aqueous. Which presents future risks of delamination of the product.

[0017] The invention thus aims to propose a method for coating a laminated glass panel with a decorative layer making it possible to obtain a coated laminated glass panel having resistance to impacts and / or perforation and an ability to retain shards at least as good as those obtained by the methods of the prior art and improved optical and decorative properties compared to the methods of the prior art. Summary of the invention

[0018] Thus, the invention relates to a method of coating a laminated glass panel comprising: - a laminated glass panel to be coated is provided comprising at least two glass sheets and in which at least two successive glass sheets are assembled by means of a polymer interlayer material forming, after assembly, an interlayer, the laminated glass panel to be coated having at least one upper face to be coated; - a flowing decorative material is provided; - a chemical hardener or a crosslinking catalyst is incorporated into the fluid decorative material in a ratio P_cata between the mass of chemical hardener or crosslinking catalyst and the mass of decorative material in the determined fluid state; - at least one decorative coating layer (13) is formed by applying the decorative material in the fluid state in which the chemical hardener or the crosslinking catalyst is incorporated on the upper face (1 lal) of the laminated glass panel to be coated; - the decorative coating layer is dried by heating the laminated glass panel thus covered using a drying device with a set temperature greater than or equal to 100°C and less than 140°C, the heating time (t_chauff) of the laminated glass panel to the set temperature (T_ext) and / or the ratio P_cata of the mass of chemical hardener or crosslinking catalyst and the mass of decorative material in the fluid state during incorporation being a function of said set temperature (T_ext).

[0019] Thanks to these provisions, it is possible to industrially manufacture coated laminated glass panels without bubbling or yellowing of the interlayer material from already assembled laminated glass panels.

[0020] According to one embodiment of the method for coating a laminated glass panel, the polymer interlayer material is chosen from polyvinyl butyral, ethylene vinyl acetate, an ionoplast polymer, thermoplastic polyurethane and a casting resin.

[0021] These different polymer interlayer materials have different characteristics in terms of refractive index, mechanical strength and hydrophobicity, which makes it possible to modulate the optical and / or mechanical properties and / or humidity resistance of the coated laminated glass panel depending on its future use.

[0022] The coating process also makes it possible to manufacture a mirror-type glass panel and lacquered glass with a reduced carbon footprint over the lifetime of the product. Indeed, laminated glass is around five times stronger and around one hundred times more rigid than monolithic glass. It can therefore be expected that the renewal of mirrors / lacquered glass made of laminated glass will be less frequent than that of mirrors / lacquered glass of the prior art.

[0023] According to one embodiment of the method for coating a laminated glass panel, at least one decorative coating layer consists either of a layer of reflective material and one or more layers of protective varnish or of one or more layers of lacquer and optionally one or more layers of protective varnish.

[0024] This arrangement makes it possible, from the same generic process, to form mirror-type laminated glass panels and colored laminated glass panels using a lacquer, these two types of laminated glass panels not having the same uses.

[0025] According to one embodiment of the method for coating a laminated glass panel, the ratio P_cata of the mass of chemical hardener or crosslinking catalyst and the mass of decorative material in the fluid state is greater than 0.1%.

[0026] Such a proportion of chemical hardener makes it possible to limit the maximum surface temperature reached by the glass panel, so that the interlayer polymer material does not bubble or yellow and that the crosslinking of the decorative coating layer is satisfactory with a drying time at this maximum surface temperature which is limited and particularly acceptable in an industrial process.

[0027] According to one embodiment of the method for coating a laminated glass panel, - if the set temperature of the drying device (T_ext) is chosen in the range [100°C, 120°C], said heating time (t_chauff) in the drying device is greater than or equal to 7.5 minutes and said ratio P_cata is chosen in the range [0.1%; 5%], - and if the set temperature of the drying device (T_ext) is chosen in the range [120°C, 140°C], said heating time (t_chauff) in the drying device is less than or equal to 7.5 minutes and greater than or equal to 3 minutes and said ratio P_cata is chosen in the range [0.1%; 5%]. These parameter ranges make it possible to obtain a coated laminated glass panel without bubbling or yellowing of the polymer interlayer material, with particularly satisfactory crosslinking of the decorative coating layer and in production times that are entirely compatible with use on an industrial and automated scale. According to one embodiment of the method for coating a laminated glass panel, the chemical hardener or crosslinking catalyst is chosen from acid catalysts and optionally from hydrofluoric acid, phosphoric acid and paratoluenesulfonic acid.

[0028] These chemical hardeners and crosslinking catalysts have the advantage of allowing a sufficient lowering of the crosslinking temperature to avoid bubbling problems.

[0029] The invention also relates to a laminated glass panel comprising at least two glass sheets and in which at least two successive glass sheets are assembled by means of a polymeric interlayer material, the laminated glass panel having an upper face (liai) and a lower face (llbl), in which the upper face of the laminated glass panel (11 a 1 ) is coated with at least one decorative coating layer (13) formed from a fluid decorative material in which a chemical hardener or a crosslinking catalyst has been incorporated and the polymeric interlayer material does not have any bubbling defect observable to the naked eye and the decorative coating layer (13) withstands at least twenty round trips in the crumpling test.

[0030] Such a glass panel can be obtained by the process according to the invention and, thanks to the lamination, has good mechanical strength and chip retention, as well as improved optical and / or decorative properties compared to the coated glass panels of the prior art.

[0031] According to one embodiment of the laminated glass panel, the decorative coating layer withstands at least two hundred back-and-forth movements in the crumpling test. Such resistance is suitable for the majority of applications of the coated laminated glass panel, particularly in the building or furniture sectors.

[0032] According to one embodiment of the laminated glass panel, at least one decorative coating layer is made up of: - either a layer of reflective material and one or more layers of protective varnish, - either one or more layers of lacquer and optionally one or more layers of protective varnish.

[0033] According to one embodiment of the laminated glass panel, the polymer interlayer material is tinted.

[0034] It is thus possible to obtain a tinted mirror whose tint is controlled by means of that of the polymer interlayer material, the coloring of which is easy to implement and can be done in a wide range of colors.

[0035] According to one embodiment of the laminated glass panel, heating means are incorporated into the polymer interlayer material or into at least one of the at least two glass sheets.

[0036] The invention finally relates to the use of a laminated glass panel in the field of construction or furniture. Brief description of the drawings

[0037] Embodiments of the invention will be described below with reference to the drawings, briefly described below:

[0038] [Fig-1] represents a side view of a laminated glass panel coated according to the invention.

[0039] [Fig.2a] is a photograph of a laminated glass panel coated by silver plating and deposition of a layer of protective varnish, the assembly being heated to 170°C for 2 minutes, according to a prior art method, on which the bubbling of the polymer interlayer material is observed.

[0040] [Fig.2b] is a photograph of the coated laminated glass panel of [Fig.2a], just after deposition of the protective varnish layer and just before the heating step according to the prior art method.

[0041] [Fig.3] represents the temperature profile followed by the external surface of the decorative coating layer, monitored by means of six thermocouples distributed over this surface during the drying of the decorative coating layer according to a prior art method in the case of the coated laminated glass panel obtained in [Fig.2a].

[0042] [Fig.4] represents the temperature profiles followed by the external surface of the decorative coating layer, monitored by means of six thermocouples distributed over this surface during the drying of the decorative coating layer according to the six heating profiles tested to obtain the results of table 1.

[0043] [Fig.5] represents the theoretical evolution of the temperature T of the upper glass sheet of a coated laminated glass panel within the framework of a simplified thermal model.

[0044] In the drawings, like references designate identical or similar objects. DETAILED DESCRIPTION

[0045] The invention relates to a method for coating a glass panel comprising:

[0046] - a laminated glass panel to be coated is provided comprising at least two sheets of glass and in which at least two successive sheets of glass are assembled by means of a polymer interlayer material forming after assembly a layer in interlayer 12, the laminated glass panel to be coated having at least one upper face liai; - a decorative material is provided in a fluid state; - a chemical hardener or a crosslinking catalyst is incorporated into the decorative material in the fluid state in a ratio P_cata between the mass of chemical hardener or crosslinking catalyst and the mass of decorative material in the fluid state determined;

[0047] - at least one layer of decorative coating 13 is formed by applying the decorative material in a fluid state in which the chemical hardener or crosslinking catalyst is incorporated on the upper face 1 lal of the laminated glass panel to be coated; - the decorative coating layer is dried by heating the laminated glass panel thus covered using a drying device whose set temperature T_ext is greater than or equal to 100°C and less than 140°C, the heating time t_chauff of the laminated glass panel at this set temperature T_ext and the ratio P_cata of the mass of chemical hardener or crosslinking catalyst and the mass of decorative material in the fluid state during incorporation being chosen as a function of the set temperature T_ext.

[0048] The laminated glass panel to be coated therefore comprises at least two glass sheets among which an upper glass sheet 11a and a lower glass sheet 11b are defined.

[0049] Any type of flat glass (or possibly curved by the bending processes known to those skilled in the art, when it comes to coating curved surfaces) can be used for each of the glass sheets.

[0050] Each sheet of glass is by definition monolithic.

[0051] In one embodiment, one or more of the at least two glass sheets are produced by the "float" process making it possible to obtain a flat and smooth glass sheet with very good precision, or by drawing or rolling processes.

[0052] In one embodiment, at least one or all of the glass sheets are tempered.

[0053] In one embodiment, the upper glass sheet 11a, one face of which will ultimately be coated with at least one layer of decorative coating 13 at the end of the method according to the invention, is not made of tempered glass. Tempered glass may in fact have microdeformations capable of altering the decorative qualities of the coating, in particular in the case where this coating is obtained by a silvering process.

[0054] In the case where none of the glass sheets are tempered, the laminated glass panel has the advantage of being able to be recut to the desired dimensions and / or for downgrading the edges if their characteristics are not satisfactory at the end. of the process.

[0055] No limitation is imposed on the dimensions of the at least two sheets of glass, apart from those linked to the manufacturing process of each of the sheets of glass and to the assembly process.

[0056] In particular, the thickness of a glass sheet may be between 2 and 12 mm, or even more, depending on the final use of the coated laminated glass panel. For example, a thickness of 2 mm to 6 mm, or even 2 mm to 5 mm or 2 mm to 4 mm or even 2 mm to 3 mm, and in particular equal to 2 mm, 3 mm, 4 mm, 5 mm or 6 mm, for one or more of the at least two glass sheets may be envisaged.

[0057] The at least two sheets of glass may have two by two thicknesses and / or compositions that are identical or not.

[0058] The at least two glass sheets are superimposed on each other in a stacking direction (Z'Z) and assembled two by two by means of at least one polymer interlayer material, so that after assembly, at least one interlayer layer 12 is interposed (or equivalently sandwiched) between at least two successive glass sheets, as shown in [Fig.l].

[0059] Regardless of the number of superimposed glass sheets (two or more), the laminated glass panel to be coated therefore comprises at least: - an upper glass sheet 11a, the external face of which to the assembly is intended to receive the coating and constitutes the so-called upper face 11a of the laminated glass panel to be coated, - and a lower glass sheet 11b consisting of the glass sheet furthest from the upper glass sheet 11a in the stacking direction (Z'Z) and whose external face to the assembly constitutes the lower face 11b1 of the laminated glass panel to be coated.

[0060] The polymeric interlayer material may comprise one or more polymers.

[0061] In particular, the polymeric interlayer material may be polyvinyl butyral. (PVB). PVB has the following advantages, among others:

[0062] - PVB has a refractive index close to that of silicon-glass. soda-lime commonly used for making glazing, so that the interlayer sheet is invisible or almost invisible.

[0063] - PVB also makes it possible to absorb shocks very effectively and to retain fragments of glass in the event of breakage of the glazing.

[0064] It may also be ethylene vinyl acetate (EVA). The hydrophobic properties of EVA are particularly advantageous if the coated glass panel is intended to be installed in a humid environment or outdoors: the risk of delamination over time due to humidity is reduced by the use of EVA for the interlayer 12 of polymer material.

[0065] It is also possible to use a polymer interlayer material called "ionoplast", in particular of the SentryGlass® type, which makes it possible to form laminated glasses which do not exhibit bubbling or yellowing defects even when they are exposed during their implementation to high temperatures, up to 80°C.

[0066] In another embodiment, the interlayer material may also be thermoplastic polyurethane (also called TPU or “Thermoplastic PolyUrethan”) or a casting resin (or equivalently “CIP” (“Cast In Place”) resin).

[0067] The interlayer material may be tinted before assembly, so as to give a particular coloring to the laminated glass panel in association with the decorative coating once the panel is coated.

[0068] Once the laminated glass panel to be coated has been provided, a decorative material in a fluid state is provided.

[0069] The decorative material in the fluid state may in particular be in the liquid state with a more or less significant viscosity, this viscosity being adapted to allow the deposition of a layer of decorative material on the laminated glass panel, for example by means of a roller or a spray gun or even a curtain machine.

[0070] The decorative material may be a lacquer.

[0071] A lacquer is a non-transparent coating, which may be translucent, but which is generally opaque, and which comprises, before drying, a solvent in which at least one pigment and at least one polymeric resin are dissolved, as well as optionally mineral fillers.

[0072] The function of pigments is to provide the desired color and opacity.

[0073] The polymer resin acts as a binder: it is used to bind the pigments and the case where appropriate, mineral fillers after drying.

[0074] The binder is preferably based on acrylic resin. The binder may also be based on alkyd resin or a polyurethane binder.

[0075] For example, the decorative material may be a lacquer of the Glassolux type (produced by Fenzi ®) or equivalent.

[0076] The lacquer can be applied, for example, using a curtain machine, a roller or a gun in one or more passes.

[0077] The choice of the number of passes for depositing the lacquer, and consequently the number of layers of lacquer, can be determined in particular as a function of the desired opacity and / or the desired mechanical resistance.

[0078] The thickness of the lacquer deposited can be between 10 and 100 micrometers.

[0079] The decorative material can also be a reflective material after drying.

[0080] The decorative material may for example include silver, which may include others be deposited by oxidation-reduction by bringing into contact a nitrate solution of ammoniacal silver with a reducing solution.

[0081] The decorative material is therefore supplied in the fluid state, insofar as it notably comprises one or more solvents.

[0082] In known methods of coating non-laminated glass with a decorative material in the fluid state, the fluid decorative material is deposited directly on one face of the non-laminated glass so as to form a decorative coating layer and this decorative coating layer is dried.

[0083] Thus, in the case of a conventional lacquering process, the drying of the lacquer is obtained by passing it through an oven at a temperature above 160°C. Typically, Glassolux lacquers require heating for at least 2.5 minutes at a temperature of at least 160°C.

[0084] Similarly, in the case of a conventional silvering process, the layer of protective varnish is applied above the layer of reflective material, for example by means of a curtain varnisher, the drying of the varnish being carried out by passing it through an oven so that the temperature reached at the surface of the layer of protective varnish is greater than 170°C for at least two minutes.

[0085] In summary, lacquers as well as varnishes conventionally used in the manufacture of mirrors are single-component paints which require sufficient thermal energy to crosslink and achieve the expected performance levels in terms of chemical (anti-corrosion) and mechanical (scratch) resistance, for which it is customary to keep the glass panel in an oven so that the temperature reached on the surface of the protective varnish layer is greater than 170°C for at least two minutes.

[0086] Whatever the method of depositing the decorative coating layer, it is noted that drying by heating at high temperature is implemented in the processes for coating non-laminated glass conventionally used in the field of monolithic glasses and is necessary to obtain good crosslinking of this decorative coating layer, and this moreover in an acceptable duration in an industrial manufacturing process.

[0087] Unfortunately, these processes cannot be directly transposed to laminated glass panels since the heating step causes the interlayer material to bubble.

[0088] [Fig.2a] is a photograph of a laminated glass panel of the Stadip® 44.2 type produced by Saint-Gobain coated with a decorative coating layer of the silver layer + protective varnish type after conventional heat treatment, i.e. heating in an infrared oven so that the surface temperature of the laminated glass panel is equal to 170°C for a period of two minutes, [Fig.2b] corresponding to the same laminated glass panel just before treatment thermal.

[0089] It can be seen in [Fig.2a] that the coating process according to the prior art causes bubbling of the interlayer material, including quite far from the edges, bubbling which is not present just before the heating step as shown in [Fig.2b].

[0090] It is not profitable to consider such processes followed by a step of cutting the edges and downgrading them.

[0091] Throughout the heating drying step following the deposition of the decorative coating in the case of the glass panel of [Fig.2b], the temperature profile followed by the external surface of the decorative coating layer was monitored by means of six thermocouples distributed over this surface. This profile is reproduced in [Fig.3].

[0092] It can be seen in [Fig. 3] that all points on the external surface of the protective layer reach a temperature above 170°C for at least 30 seconds and a temperature above 140°C for at least 2 minutes and 30 seconds.

[0093] In addition to bubbling, drying by heat treatment can in certain cases lead to yellowing of the polymer interlayer material, which can be troublesome in particular cases of decorative coatings according to the invention. Yellowing is particularly to be avoided in the case where the decorative coating is of the mirror type since it alters the color of the image reflected by the mirror. This problem can also be noticeable and troublesome in the case where the decorative coating comprises a light-colored lacquer.

[0094] It therefore appears essential to modify the methods for drying the decorative coating layer 13 of the prior art if it is sought to form a decorative coating layer 13 on an external face of a laminated glass panel.

[0095] The application of the decorative layer on an external face of the laminated glass already formed is a mandatory step of the process according to the invention, despite its difficulty of implementation because it has several advantages.

[0096] Firstly, this makes it possible to modify the appearance of a laminated glass panel manufactured beforehand, possibly on another production line, and to choose the decorative coating afterwards, possibly on a case-by-case basis.

[0097] Secondly, the superposition of at least two sheets of glass under the decorative coating layer makes it possible to improve the optical quality of the coated laminated glass, particularly in the case where the aim is to form a laminated glass mirror. Indeed, each sheet of glass has flatness defects whose pitch is of the order of a meter and optical defects whose pitch is of the order of 1 cm to 10 cm, but which cannot all be found superimposed on each other when the two sheets of glass are assembled. The optical distortions of the laminated glass coated on its external face are therefore less than if the coating had been inserted between the two sheets of glass.

[0098] The inventors initially considered reducing the set temperature T_ext of the drying device, and / or the maximum temperature reached on the surface of the laminated glass panel and / or the time during which this maximum surface temperature is reached (or the heating time t_chauff at the set temperature, this heating time t_chauff being correlated to the maximum surface temperature reached and to the time during which it is reached, as shown in example 2) in the case of a laminated and non-monolithic glass panel. A pure and simple reduction of these parameters is not obviously done because it leads to insufficient crosslinking of the decorative coating layer 13, in particular - where appropriate - of the lacquer layer or the protective varnish layer, so that the decorative coating layer will not be sufficiently resistant for its subsequent handling or use.For example, problems of flaking of the decorative coating layer 13 are observed when handling a given coated laminated glass panel and of sticking of the coated laminated glass panels together during possible passages in an autoclave, or even of insufficient resistance to corrosion.

[0099] To overcome the technical problem of obtaining a suitably crosslinked decorative coating layer within an acceptable time for an industrial process (in particular for a continuous manufacturing process, in which the laminated glass panel to be coated is moved at constant speed on a production line), typically of the order of a few minutes or a few tens of minutes, the inventors have therefore considered using chemical hardeners or chemical catalysts.

[0100] In particular, it may be envisaged to incorporate into the decorative material in the fluid state a total proportion of one or more crosslinking catalysts and / or chemical hardeners P_cata equal to or greater than 0.1%, or even equal to or greater than 0.5% by mass, 1% by mass, 2% by mass of the decorative material in the fluid state, 2.5% by mass of the decorative material in the fluid state and optionally less than 10% by mass of the decorative material in the fluid state, or even less than 5% by mass of the decorative material in the fluid state.

[0101] The protective varnish may be chosen, in a non-limiting manner, from: commercial anti-corrosion varnishes from suppliers such as FENZI (for example FENZI One coat LF 3 grey SG, FENZI one coat WBLF 6 varnishes), VALSPAR (for example references SK1420 or SK1440) or EUROCOATINGS (for example euro-coatings glasskin007 varnish).

[0102] In the case of a lacquer, it may, without limitation, be commercial lacquers from suppliers such as FENZI (for example glassolux NG lacquer), MADER (for example madercoat LRY168 and madercoat 572 lacquers) or VALSPAR (for example reference SK3875).

[0103] As for the chemical hardener or crosslinking catalyst, it can be chosen according to the fluid decorative material.

[0104] In particular, an acid catalyst such as hydrofluoric acid, phosphoric acid, paratoluenesulfonic acid, or any other transesterification catalyst can be used.

[0105] The fluid decorative material in which at least one chemical hardener and / or at least one crosslinking catalyst has been incorporated is then deposited on the upper face liai of the laminated glass panel to be coated so as to form at least one decorative coating layer 13.

[0106] The deposition of the fluid decorative material can be carried out by means of a device for deposition of a fluid material such as a curtain coater, a roller or a gun.

[0107] The thickness of the at least one decorative coating layer may be greater than 10 micrometers.

[0108] The decorative coating layer is then dried so as to obtain its crosslinking and at least partial evaporation of the solvents.

[0109] The proportion P_cata of chemical hardener or crosslinking catalyst must be chosen to allow application of the decorative coating in a fluid state and in particular during an industrial process. In particular, this proportion may be chosen to allow application of the decorative coating by means of a device such as a curtain machine.

[0110] In particular, it is not possible to increase the proportion of chemical hardener or crosslinking catalyst in an unreasonable manner since too high a proportion causes the product to set at too low a temperature and / or too quickly. In such a case, the decorative material does not remain in the fluid state long enough to allow its application to the upper face 1 lal of the laminated glass panel to be coated.

[0111] Uncontrolled caking also leads to the obstruction of the pipes or transport elements through which the decorative material must circulate.

[0112] The duration of mass setting of the catalyst was evaluated by observation with the naked eye in the case where the crosslinking catalyst is paratoluenesulfonic acid incorporated into the fluid decorative material is One Coat LF3 from the Fenzi brand in a proportion P_cata expressed as a percentage of the mass of the fluid decorative material.

[0113] The results are grouped in Table 3 below:

[0114] [T ableaux3 ] P_cata (%) Mass setting time (qualitative h) 0.1 >24 0.5 >24 1 >24 2.5 >24 5 >24 10 9-24 25 2 50 0.5

[0115] Table 3: Mass setting time as a function of the proportion P_cata of crosslinking catalyst

[0116] It is found that an excessive proportion of chemical hardener or crosslinking catalyst leaves little time for subsequent stages of processing of the fluid decorative material, in particular for its application to the laminated glass panel to be coated.

[0117] It is therefore necessary to find a compromise between the proportion of chemical hardener or crosslinking catalyst, the drying temperature and the drying time.

[0118] A proportion P_cata of chemical hardener or crosslinking catalyst less than or equal to 10% by mass of the fluid decorative material, or even 5% by mass of the fluid decorative material, or even 2.5% by mass of the fluid decorative material may be suitable for implementing the method according to the invention.

[0119] It is also understood through these experiments that the implementation of chemical hardeners or chemical catalysts for the decorative coating layer of a laminated glass panel is not done without inventive activity: the inventors tested numerous temperature rise / fall profiles for drying by heating the laminated glass panel covered with a decorative coating layer before achieving a satisfactory result.

[0120] Part of these profiles are reproduced in [Fig.4] on an experimental campaign carried out on laminated glass panels of the Stadip® 44.2 PVB type with dimensions of 800mmx600mm silvered with a layer of thickness 700 mg / m2 on which was deposited a layer of One Coat LF3 varnish from the Fenzi brand in which was incorporated 0.5% by mass of paratoluenesulfonic acid, with a thickness equal to 50 micrometers.

[0121] The results of these experiments can be seen in Table 1 below, in which the effects of heating are shown for each test in terms of: - bubbling of the interlayer 12 (observation with the naked eye) - yellowing of the interlayer 12 (observation with the naked eye)

[0122] The crosslinking of the decorative coating layer is evaluated on the basis of a so-called ruffle test (or abrasion resistance test or “rub test”), the number of back and forth movements necessary to attack this coating being evaluated.

[0123] The reference wiping test here is as follows: using a cellulose cloth (or "pad") reinforced with polypropylene or polyester ("heavy duty cleaning cloth" reference 530276 from the TORK® brand) with dimensions of 200 mm * 100 mm, the cloth being saturated in a solvent and having a contact surface with the panel to be tested of 3 cm2, back and forth movements are carried out on the surface of the panel over a distance of 5 cm at a movement speed of between 15 m / min, the pressure exerted on the coating being controlled by means of a weight of 1 kg and therefore equal to 32.7 kPa (kilopascals).

[0124] The solvent used to saturate the cloth is xylene if the decorative coating layer 13 was formed from an organic phase fluid. The solvent used to saturate the cloth is water if the decorative coating layer was formed from an aqueous phase fluid.

[0125] The decorative coating layer 13 is said to be correctly crosslinked if no alteration of this decorative coating layer or reduction or disappearance of this decorative coating layer by dissolution in the solvent saturating the cloth is observed with the naked eye after a predetermined number N of back-and-forth movements. In particular, the predetermined number N of back-and-forth movements may be greater than or equal to 20, greater than or equal to 30, greater than or equal to 40, greater than or equal to 50, greater than or equal to 60, greater than or equal to 70, greater than or equal to 80, greater than or equal to 90, greater than or equal to 100, greater than or equal to 200, greater than or equal to 500.

[0126] [Tables 1] Test Chain speed (m / min) Maximum surface temperature reached °C Time (in s) during which the surface temperature is higher than: bubbling Yellowing Number of round trips "rub test" 100°C 120°C 130°C 1 1.5 90 0 0 0 No No 20 2 1.5 102 25 0 0 No No 20 3 1.5 131 220 85 10 No No 30 4 1.0 120 304 0 0 No No 30 5 1.0 119 280 0 0 No No 50 6 0.7 130 472 218 0 No No >200

[0127] It can be seen from Table 1 that the choice of temperature profile makes it possible to control the crosslinking of the decorative coating layer. Profiles 1 to 6 all make it possible to obtain resistance to the crumpling test greater than 20 round trips without yellowing or bubbling of the interlayer 12.

[0128] It is recalled that these results were obtained with a proportion P_cata equal to 0.5% of paratoluenesulfonic acid incorporated in the fluid material One Coat LF3 of the Fenzi brand.

[0129] By comparing the results obtained for the six profiles, we see that the maximum surface temperature reached has an impact on crosslinking.

[0130] By comparing the results obtained for profile 4 with those obtained for profile 5, or the results obtained for profile 3 with those obtained for profile 6, it can again be seen that the speed and / or the duration during which this maximum surface temperature is reached makes it possible to modulate the crosslinking of the decorative coating layer 13.

[0131] Among the six temperature profiles described here, profile 6 makes it possible to obtain very satisfactory crosslinking of the decorative coating layer 13 with resistance to the crumpling test greater than two hundred round trips.

[0132] These experiments were carried out in parallel with the experiments of Example 1 and Example 2 described below.

[0133] These numerous experiments have enabled the inventors to define the characteristics of the drying step which, in combination with the addition of a chemical hardener or a crosslinking catalyst in the decorative material in the fluid state, allows to industrially obtain laminated glass coated with a decorative coating layer having satisfactory chemical resistance and / or mechanical resistance and improved optical and / or decorative properties compared to the prior art.

[0134] In particular, it has been demonstrated that the heating time t_chauff during which the coated laminated glass panel is dried by the heating device after this heating device has reached its set temperature T_ext, this set temperature T_ext and the ratio P_cata of the mass of chemical hardener or crosslinking catalyst and the mass of decorative material expressed as a percentage are three parameters which cannot be chosen independently of each other.

[0135] In a particular embodiment, the ratio P_cata is chosen in the range [0.1%, 5%], more particularly in the range [0.5%, 2.5%] or more particularly [0.75%, 1.25%]. In a particular embodiment, the ratio P_cata is equal to 1%. For each of the four options for choosing the proportion P_cata above, the set temperature T_ext can be chosen: - in the range [120°C; 140°C], the duration t_chauff then being less than or equal to 7.5 minutes and optionally greater than 3 minutes, - in the range [100°C; 120°C], the duration t_chauff then being greater than or equal to 7.5 minutes; in particular if the upper glass sheet 1 la is made of clear glass and has a thickness of between 2 mm and 6 mm, and if the decorative coating layer has a thickness before drying of between 50 pm and 200 pm.

[0136] In a particular embodiment, the at least one decorative coating layer (13) consists of one or more layers of lacquer.

[0137] In another embodiment, the at least one decorative coating layer comprises at least one layer of reflective material, so as to form a mirror.

[0138] The at least one layer of reflective material can be deposited by all the processes commonly used in the field of silvering.

[0139] The thickness of the layer of reflective material may be adapted to obtain a surface mass of silver greater than the standard of 700 mg / m2. Since the reflective material is subject to oxidation and has little mechanical resistance, a layer of protective varnish may be applied to the layer of reflective material.

[0140] The invention also relates to a laminated glass panel comprising at least two glass sheets and in which at least two successive glass sheets are assembled by means of a polymer interlayer material, the laminated glass panel having an upper face 11a1 and a lower face 11b1, and the upper face 11b1 of which The upper surface of the laminated glass panel liai is coated with at least one decorative coating layer 13 formed from a fluid decorative material and whose polymer interlayer material does not have any bubbling defect observable to the naked eye and withstands at least twenty round trips in the rub test, or even thirty round trips in the rub test, fifty round trips in the rub test, one hundred round trips in the rub test or even two hundred round trips in the rub test.

[0141] Such a product can at present only be obtained by means of the process according to the invention, for the reasons which have been previously explained.

[0142] In one embodiment of the coated laminated glass panel, the interlayer polymer material is tinted. In the case where the laminated glass panel is coated with a reflective material so as to form a mirror, this arrangement makes it possible in particular to obtain a tinted mirror, for example bronze in color, without having to resort to the usual processes for tinting mirrors, a process which is cumbersome and costly to implement.

[0143] In one embodiment of the coated laminated glass panel, heating means are incorporated either in the polymer interlayer material or in at least one of the two glass sheets. For example, heating microfilaments may be incorporated in PVB, or one of the two glass sheets or the glass panel may be of the EGLAS® type from Saint Gobain(R). This arrangement makes it possible to obtain a heated coated glass panel, such as a heated mirror, whose mechanical strength is improved compared to the solutions of the prior art.

[0144] The invention finally relates to the use of a laminated glass panel: - in the construction sector, in particular for the creation of decorative partition walls or floors meeting the required safety standards, - or in the field of furniture for the production of furniture including walls or decorative wall elements meeting the required safety standards, for example custom-made furniture. EXAMPLES Example 1: Crosslinking test

[0145] Operating mode:

[0146] A 3mm thick monolithic glass panel coated with a layer of Fenzi ONE COAT LF3 GREY SG varnish (Commercial reference: 23689 on the first priority date) with a thickness of 100 μm is applied using a film puller, varnish in which the paratoluenesulfonic acid crosslinking catalyst has previously been incorporated in a proportion P_cata expressed as a percentage of the mass of varnish.

[0147] The laminated glass panel thus coated is placed in a hot air oven whose set temperature is T_ext for a duration t_chauff at this set temperature.

[0148] In the case of the experiments of Example 1, the time required to reach the set temperature after inserting the laminated glass panel into the furnace is of the order of 2.5 minutes, so that the time taken for the laminated glass panel to pass through the hot air furnace is of the order of t_chauff+2.5 minutes.

[0149] After cooling, the quality of the crosslinking of the varnish layer is assessed using the Persoz hardness test.

[0150] Persoz hardness test:

[0151] The hardness test is carried out using a Persoz automatic hardness measuring pendulum, in accordance with ISO 1522.

[0152] The Persoz pendulum system makes it possible to measure the number of oscillations of a stainless steel pendulum, with a mass equal to 500 g, resting on a material (in this case on the external face of the decorative coating layer) via two tungsten carbide balls with a diameter of 8 mm, 50 mm apart.

[0153] A sample of coated laminated glass panel is inserted into the Persoz pendulum and placed coated side up.

[0154] The pendulum is released from an angle of 12°, the number of oscillations N2 of the pendulum is counted until the amplitude of the oscillations reaches an angle of 4°.

[0155] The more crosslinked the paint, the harder the paint surface, and consequently, the greater the number of oscillations.

[0156] Results:

[0157] The test results are grouped in Table 2 below:

[0158] [Tables2] T_ext(°C ) t_chauff (minutes) N2 for P_cata = 0.1% N2 for P_cata = 0.5% N2 for P_cata = 7% N2 for P_cata = 2.5% 80 0 57 53 50 32 80 2.5 64 54 47 31 80 5 60 56 58 40 80 7.5 66 57 57 40 100 0 63 59 57 34 100 2.5 72 64 56 43 100 5 76 73 79 71 100 7.5 88 80 98 78 120 0 62 60 50 38 120 2.5 78 82 131 122 120 5 84 108 148 129 120 7.5 137 136 159 146 140 0 66 64 106 87 140 2.5 119 124 144 133 140 5 151 146 165 151 140 7.5 175 170 174 169 160 0 99 86 115 80 160 2.5 172 168 140 128 160 5 192 193 144 132 160 7.5 193 201 152 143

[0159] Table 2: number of oscillations measured in the Persoz pendulum test as a function of T_ext, P_cata and t_chauff

[0160] It is noted that, whatever the proportion of catalyst P_cata tested between 0.1% and 2.5%, a heating time t_chauff less than or equal to 10 minutes (duration typically compatible with an industrialized process), at a set temperature T_ext = 80°C does not allow satisfactory crosslinking to be obtained, i.e. in this case a number of oscillations greater than or equal to 150 with the Persoz test.

[0161] The same applies for a set temperature T_ext = 100°C.

[0162] From T_ext = 120°C, it is found that it is possible to obtain satisfactory crosslinking provided that a heating time t_chauff and a proportion of catalyst P_cata are provided in relation to this set temperature T_ext.

[0163] In particular, the combinations: - T_ext= 120°C, t_chauff = 7.5 minutes and P_cata= 1%; - T_ext= 140°C, t_chauff = 7.5 minutes and P_cata= 0.1%; 0.5%; 1% or 2.5%; - T_ext= 140°C, t_chauff = 5 minutes and P_cata= 0.1%; 1% or 2.5%; - T_ext= 160°C, t_chauff = 2.5 minutes and P_cata= 0.1% or 0.5%; - T_ext= 160°C, t_chauff = 5 minutes and P_cata= 0.1% or 0.5%; - T_ext = 160°C, t_chauff =7.5 minutes and P_cata= 0.1%; 0.5% or 1%;

[0164] make it possible to obtain satisfactory crosslinking, i.e. for this series of experiments a number of oscillations N2 greater than or equal to 150 with the Persoz test.

[0165] Conclusion:

[0166] Inexperience from Example 1 shows that, counterintuitively, the quality of crosslinking does not always vary in the same direction as the P_cata proportion. In particular, too high a P_cata proportion can be counterproductive.

[0167] The experiment of Example 1 also proves that obtaining correct crosslinking of the decorative coating layer 13 depends on the combination of three parameters: the heating temperature of the laminated glass panel after application of the decorative material in the fluid state in which a chemical hardener or a crosslinking catalyst is incorporated, the proportion of chemical hardener or crosslinking catalyst, and the duration of this heating for drying.

[0168] This example is to be combined with the evaluation of the bubbling of the polymer interlayer material forming the interlayer 12 and optionally the yellowing of this material. To avoid any bubbling, the pair (set temperature T_ext, heating time at this set temperature t_chauff) must be chosen appropriately, the heating time being correlated to the proportion P_cata.

[0169] Example 2: estimation of the parameters T_ext, t_chauff and P_cata

[0170] A simplified model is set up to estimate the parameters of the step of drying of the decorative coating layer.

[0171] Model assumptions:

[0172] As a first approach, it is considered that the system formed by the upper glass sheet 11a and the decorative coating layer 13 has at time t a homogeneous temperature T(t) and is placed in contact with a thermostat at temperature To (To being equal to T_ext when the coated laminated glass panel is placed in a hot air oven having reached its set temperature T_ext) then.

[0173] Between two instants t and t+dt, the temperature T verifies the differential equation next:

[0174] hs (T-T0)=pc

[0175] Where V is the volume of the system, S is the surface area of ​​the system in contact with the thermostat, c is the thermal capacity of the system, p the density of the system and h the exchange coefficient characterizing the thermal transfers between the system and the thermostat.

[0176] The solution to this differential equation is written:

[0177] [Math.2] Wlü - exn / hs t \ TrTü ~ C 1J\ pcV ! l

[0178] with T; = T(t=0)

[0179] The temperature of the upper glass sheet 11a and of the decorative coating layer therefore follows an exponential type evolution of characteristic time r with: [Math.3] pc V pce 1 ~ ~hS~ ~ T"

[0180] where e =V / S is the thickness of the system along the stacking direction (Z'Z) of the coated laminated glass panel.

[0181] This evolution is represented as an example in [Fig.5] with the following parameters:

[0182] p = density of glass = 2530 kg / m3

[0183] c = specific heat capacity of the glass = 800 J / kg / K

[0184] h = 100 W / m2 / K

[0185] T; = T(t=0) = 20°C

[0186] With these parameters, the characteristic time r of the variations in temperature T is of the order of 80 seconds.

[0187] Conclusion:

[0188] We note with the assumptions of this simplistic model that in the case of heating to T_ext = 160°C, the temperature T of the coated upper glass sheet 11a quickly reaches T = 80°C then T=100°C, respectively after 45s and 68s respectively.

[0189] The temperature rise is rapid, with a limit temperature in steady state higher than the bubbling temperature of the interlayer polymer material. Thus, with such heating conditions, the interlayer polymer material will begin to bubble after a relatively short heating time t_chauff, particularly on the edges of the laminate where the heat exchanges with the interlayer 12 are amplified, then will bubble in the mass of this interlayer 12.

[0190] It is also noted that the time required for the temperature T of the system to rise from T = 80°C to T = 100°C naturally increases with the decrease in To, which makes it possible to increase the heating time t_chauff to complete the crosslinking of the varnish without causing the PVB to bubble.

[0191] More complex purely theoretical modeling and / or experimental results can be used for the choice of T_ext, t_chauff and P_cata.

[0192] In particular, if the Biot number of the system is such that the hypothesis on the homogeneity of the temperature T is not experimentally verified, it can be agreed that, as a precaution, to avoid bubbling of the polymer interlayer material, heating must be stopped at the latest when the temperature T of the system is equal to the limit temperature T_lim for which bubbling of the polymer interlayer material is observed, from which a safety margin M_sec is subtracted.

[0193] Furthermore, the decorative coating layer 13, however thin it may be, plays a role of thermal shield delaying the transfer of heat.

[0194] The thermal effusivity of the glass constituting the upper glass sheet 11a can also impact the characteristic time of heat transfer to the polymer interlayer material.

[0195] For example, all of these influencing factors can be taken into account by considering that the parameters of the drying step must be chosen in such a way that the temperature T_max reached by the system, and in particular by the external surface of the system, after a heating time t_chauff is equal to T_lim - M_sec.

[0196] In particular in the case of the coated laminated glass panel used for example 1 whose polymer interlayer material is PVB, it can be considered that the combination of heating times t_chauff and temperature T_ext = T_0 corresponding to the hatched area in [Fig.5] between the curves T_0 = 100°C and T_0 = 140°C is suitable, provided that the proportion of chemical hardener or crosslinking catalyst is compatible with the corresponding heating times t_chauff. List of reference signs

[0197] 1: coated laminated glass panel

[0198] 1 la: upper glass sheet

[0199] 1 lal: upper face of the laminated glass panel to be coated

[0200] 11b: lower glass sheet

[0201] 1 Ibl: lower face of the laminated glass panel to be coated

[0202] 12: interlayer of polymer material

[0203] 13: decorative coating layer

Claims

Claims

1. A method of coating a laminated glass panel comprising: - providing a laminated glass panel to be coated comprising at least two glass sheets (11a, 11b) and in which at least two successive glass sheets are assembled by means of a polymer interlayer material forming after assembly an interlayer (12), the laminated glass panel to be coated having at least one upper face (11a1) to be coated; - providing a fluid decorative material; - incorporating a chemical hardener or a crosslinking catalyst into the fluid decorative material in a ratio P_cata between the mass of chemical hardener or crosslinking catalyst and the mass of decorative material in the determined fluid state;- at least one decorative coating layer (13) is formed by applying the decorative material in the fluid state in which the chemical hardener or crosslinking catalyst is incorporated on the upper face (1 lal) of the laminated glass panel to be coated; - the decorative coating layer is dried by heating the laminated glass panel thus covered by means of a drying device whose set temperature (T_ext) is greater than or equal to 100°C and less than 140°C, the heating time (t_chauff) of the laminated glass panel to the set temperature (T_ext) and / or the ratio P_cata of the mass of chemical hardener or crosslinking catalyst and the mass of decorative material in the fluid state during incorporation being a function of said set temperature (T_ext).;

2. A method of coating a laminated glass panel according to claim 1 wherein the polymeric interlayer material is selected from polyvinyl butyral, ethylene vinyl acetate, an ionoplast polymer, thermoplastic polyurethane and a casting resin.

3. A method of coating a laminated glass panel according to one of the preceding claims, wherein the at least one decorative coating layer consists either of a layer of reflective material and one or more layers of protective varnish or of one or more layers of lacquer and optionally one or more layers of protective varnish.

4. A method of coating a laminated glass panel according to one of the following: preceding claims wherein the ratio P_cata of the mass of chemical hardener or crosslinking catalyst and the mass of decorative material in the fluid state is greater than 0.1%.

5. Method for coating a laminated glass panel according to one of the preceding claims, wherein: - if the set temperature of the drying device (T_ext) is chosen in the range [100°C, 120°C], said heating time (t_chauff) by means of the drying device is greater than or equal to 7.5 minutes and said ratio P_cata is chosen in the range [0.1%; 5%] - and if the set temperature of the drying device (T_ext) is chosen in the range [120°C, 140°C], said heating time (t_chauff) by means of the drying device is less than or equal to 7.5 minutes and greater than or equal to 3 minutes and said ratio P_cata is chosen in the range [0.1%; 5%].

6. A method of coating a laminated glass panel according to one of the preceding claims, in which the chemical hardener or the crosslinking catalyst is chosen from acid catalysts and optionally from hydrofluoric acid, phosphoric acid and paratoluenesulfonic acid.

7. Laminated glass panel comprising at least two glass sheets and in which at least two successive glass sheets are assembled by means of a polymer interlayer material, the laminated glass panel having an upper face (11a) consisting of an external face to the assembly of an upper glass sheet (11a) and a lower face (11b 1 ) consisting of an external face to the assembly of a lower glass sheet (11b), characterized in that: - the upper face of the laminated glass panel (11a1) is coated with at least one decorative coating layer (13) consisting of a fluid in organic phase formed from a fluid decorative material in which a chemical hardener or a crosslinking catalyst has been incorporated, - the polymer interlayer material does not have any bubbling defect observable to the naked eye,and the decorative coating layer (13) withstands at least twenty round trips to the wrinkle test, Wherein said wrinkle test comprises:, Using a cellulose cloth reinforced with polypropylene or polyester measuring 200mm x 100mm, the cloth being saturated with xylene and having a contact surface with the panel to be tested of 3 cm2, back and forth movements are carried out on the surface of the panel over a distance of 5 cm at a speed of movement between 15 m / min, the pressure exerted on the coating being controlled by means of a weight of 1 kg and therefore equal to 32.7 kPa (kilopascals).

8. A laminated glass panel according to claim 7, the decorative coating layer (13) of which withstands at least two hundred back-and-forth movements in the crumpling test.

9. Laminated glass panel according to any one of claims 7 and 8 in which the at least one decorative coating layer consists of: - either a layer of reflective material and one or more layers of protective varnish, - or one or more layers of lacquer and optionally one or more layers of protective varnish.

10. A laminated glass panel according to any one of claims 7 to 9 wherein the polymeric interlayer material is tinted.

11. A laminated glass panel according to any one of claims 7 to 10 wherein heating means are incorporated in the polymeric interlayer material or in at least one of the at least two glass sheets.

12. Use of a laminated glass panel according to any one of claims 7 to 11 in the field of construction or furniture.