Abstract

The invention relates to a method for manufacturing an electrical conductor intended to equip electrical equipment, comprising the steps of providing (101) a bare electrical conductor made from copper and of stripping and texturizing (103) at least a portion of the bare electrical conductor using a laser device emitting radiation comprising a wavelength of between approximately 700 nm and approximately 1600 nm. figure for the abstract: figure 1

Description

Title of the invention: Method for manufacturing an electrical conductor intended to equip electrical equipment TECHNICAL FIELD OF THE INVENTION

[0001] The invention relates to a method of manufacturing an electrical conductor intended to equip electrical equipment.

[0002] The invention also relates to an electrical conductor intended to equip an electrical apparatus, obtained by implementing the method, and an electrical apparatus provided with at least one such electrical conductor. STATE OF THE ART

[0003] In the field of electrical equipment, it is known to carry out tests, in particular standardized ones, to test and verify heating caused by the passage of a current in the electrical equipment.

[0004] In particular, such electrical equipment may comprise one or more electrical conductors and heating measurements may be carried out on the electrical equipment and on its electrical conductors.

[0005] Such measurements are representative of a resistance defined by a component called volume resistance linked to the volumes and shapes of the conductive elements that the apparatus comprises and to the passage of an electric current between these different elements, and another component called contact resistance also established by the passage of the electric current between these different elements.

[0006] The various elements have specific geometries and are made from specific materials. The volume component of the resistance depends in particular on the geometry of these various electrically conductive elements and the resistivity of the materials used; while the contact component of the resistance depends in particular on the surface roughness of these various elements, their respective propensity to atmospheric corrosion, and the stresses experienced by contact and / or friction.

[0007] Contact resistance is thus intrinsically not theoretically determinable and more difficult to control than volume resistance.

[0008] To satisfy the tests, in particular the normative ones, it is necessary to have a minimum contact resistance to avoid excessive heating of the electrical equipment and to ensure reliable electrical connections within the electrical equipment and between the latter and other equipment to which it can be electrically connected.

[0009] For example, for electrical appliances of the socket type, it may be refers to IEC 60884-1.

[0010] A known solution in particular for limiting contact resistance is, for example, to use electrical conductors based on copper or copper alloy, which are covered with coatings composed of tin, silver, gold, palladium or even nickel.

[0011] For example, we speak of electrical conductors made of copper or brass, called tinned or silver-plated if they have a tin or silver coating respectively. Description of the invention

[0012] The invention relates to a method for manufacturing an electrical conductor intended to equip electrical equipment, which is simple and convenient to implement and which makes the electrical conductor particularly efficient, particularly in terms of contact resistance.

[0013] The invention thus relates, according to a first aspect, to a method for manufacturing an electrical conductor intended to equip electrical equipment, comprising the steps of providing a bare electrical conductor made from copper and of stripping and texturizing at least a portion of the bare electrical conductor using a laser device emitting radiation comprising a wavelength of between approximately 700 nm and approximately 1600 nm.

[0014] In other words, the method comprises a step of emitting a beam of laser radiation having a wavelength of between approximately 700 nm and approximately 1600 nm at a time to strip and texture at least a portion of the bare electrical conductor made from copper.

[0015] The implementation of the combined steps of stripping and texturing by laser radiation in such a range of wavelengths on a bare copper-based electrical conductor, gives a surface condition to the stripped and textured portion of the electrical conductor which makes it possible to reduce the electrical contact resistance when this electrical conductor is in contact with another electrical conductor and an electric current passes through them.

[0016] In particular, thanks to this surface state obtained by implementing the stripping and texturing steps, the inventor has noticed that it is possible to reduce the contact resistance by avoiding the addition to the conductor of an additional coating of the type depositing tin, silver, gold, palladium or even nickel etc.

[0017] A bare electrical conductor made from copper is a bare electrical conductor based on copper or based on a copper alloy.

[0018] Preferred, simple, convenient and economical characteristics of the method according to the invention are presented below.

[0019] The bare copper-based electrical conductor may be copper or an alloy of copper, especially brass.

[0020] The laser device may be a nanosecond pulsed laser, in particular configured to emit a beam of laser radiation in pulses.

[0021] The laser device may be a pulsed fiber laser, in particular configured to emit a beam of laser radiation in pulses.

[0022] The manufacturing method may comprise a step of parameterizing the laser device, as a function of determined parameters selected from at least one of the following parameters: a wavelength, a pulse duration, an energy per pulse, a pulse frequency, a beam diameter, a scanning speed and a power.

[0023] The laser device may emit a pulsed beam of radiation having a wavelength equal to about 1070 nm.

[0024] The laser device may emit a pulsed radiation beam having a pulse duration of approximately 120 ns.

[0025] The laser device may emit a pulsed beam of radiation having an energy per pulse equal to about 300 pJ.

[0026] The laser device may emit a pulsed beam of radiation having a pulse frequency of approximately 60 kHz.

[0027] The laser device may emit a pulsed radiation beam that has a beam diameter of about 45 pm.

[0028] The laser device may comprise a scanning system with galvanometric mirrors.

[0029] The laser device may emit a pulsed radiation beam that is scanned over the at least a portion of the bare electrical conductor at a speed equal to about 2,700 mm / s.

[0030] The laser device can emit a pulsed radiation beam at an average power equal to approximately 18 W.

[0031] It will be noted that the average power corresponds to a so-called "effective" power, which is an average of the power over time. It is not a so-called peak power corresponding to the power during each pulse and which is by definition much higher than the average power since the latter takes into account the power which is zero between the pulses.

[0032] In other words, the method may comprise a step of emitting a pulsed laser radiation beam having at least one of the parameters among: a wavelength of approximately 1070 nm, a pulse duration of approximately 120 ns, an energy per pulse of approximately 300 pJ, a pulse frequency of approximately 60 kHz, a beam diameter of approximately 45 pm, a scanning speed of approximately 2700 mm / s, and an average power of approximately 18 W; this allowing the actions combined stripping and texturizing of the portion of the bare copper-based electrical conductor.

[0033] The stripping and texturizing step may be configured to form a network of craters on the at least a portion of the bare electrical conductor.

[0034] The invention also relates, according to a second aspect, to a bare electrical conductor intended to equip electrical equipment and obtained directly by implementing the method as described above, the bare electrical conductor having a network of craters on at least one stripped and textured portion.

[0035] The crater network may have a periodic pattern.

[0036] The craters may each have a recessed depression in the portion of the bare electrical conductor and a peripheral edge around the depression and projecting.

[0037] The craters may generally have a diameter equal to approximately 30 pm, taking into account the fact that the craters do not necessarily have a perfectly circular outline.

[0038] The invention also relates, according to a third aspect, to electrical equipment comprising at least one bare electrical conductor as described above.

[0039] The electrical equipment may be a circuit breaker, a differential switch, a socket or any other electrical, electronic or electrotechnical equipment comprising, for example, connection terminals or electrical connections. BRIEF DESCRIPTION OF THE FIGURES

[0040] The invention, according to an exemplary embodiment, will be well understood and its advantages will appear better on reading the detailed description which follows, given for information purposes and in no way limiting, with reference to the attached drawings.

[0041] [Fig.l] is a block diagram showing steps of a method of manufacturing a bare electrical conductor intended to equip electrical equipment, in accordance with the invention.

[0042] [Fig.2] schematically and partially represents a laser device for the implementation of at least one step of the manufacturing process of [Fig.l].

[0043] [Fig. 3] is a macroscopic view of a portion of bare electrical conductor obtained directly by implementing the manufacturing method of [Fig. 1].

[0044] [Fig. 4] is a microscopic detail view of the conductor portion bare electrical energy obtained directly by implementing the manufacturing process of [Fig.l], showing a network of craters.

[0045] [Fig.5] is a schematic view of a crater illustrated in [Fig.4].

[0046] [Fig.6] is a view taken in section along VLVI on [Fig.5].

[0047] [Fig.7] is a view similar to that of [Fig.4], showing the portion of bare electrical conductor following an electrical contact resistance test.

[0048] [Fig.8] is a view similar to that of [Fig.4], showing the portion of bare electrical conductor directly obtained by implementing a manufacturing method different from the manufacturing method according to the invention. DETAILED DESCRIPTION OF THE INVENTION

[0049] [Fig.l] represents a manufacturing method 100 of a bare electrical conductor intended to equip electrical equipment, the so-called contact resistance of which is particularly low and satisfies tests, in particular normative ones, for heating.

[0050] The manufacturing method 100 here comprises a step of providing 101 a bare electrical conductor made from copper, that is to say copper or a copper alloy, in particular brass.

[0051] The bare electrical conductor may be in the form of a blade, strip, wire, bar or any other form which can then be directly used or cut to be used in the electrical equipment.

[0052] The electrical equipment may be a circuit breaker, a differential switch, a socket or any other electrical, electronic or electrotechnical equipment comprising, for example, connection terminals or electrical connections.

[0053] The manufacturing method 100 comprises a step of parameterizing 102 a laser device, according to determined parameters selected from at least one of the following parameters: a wavelength, a pulse duration, an energy per pulse, a pulse frequency, a beam diameter, a scanning speed and a power.

[0054] The manufacturing method 100 comprises a step of stripping and texturing 103 at least a portion of the bare electrical conductor using the laser device emitting radiation comprising a wavelength of between approximately 700 nm and approximately 1600 nm.

[0055] In other words, the combined actions of stripping and texturizing the portion of the bare copper-based electrical conductor are carried out simultaneously using the laser device emitting radiation in the near infrared.

[0056] The manufacturing method 100 comprises a step of using 104 the bare copper-based electrical conductor thus stripped and textured in electrical equipment, either directly or after cutting and / or bending and / or any other shaping action necessary for its use.

[0057] [Fig.2] represents the laser device 1 configured for implementing the manufacturing method of [Fig.l].

[0058] The laser device 1 comprises a laser source 2, an optical block 3 and a control and command unit 4 configured to control and command the laser source 2 and the optical block 3.

[0059] The control and command unit 4 comprises system elements configured to execute a computer program to implement at least the step of parameterizing the laser device 1 and the step of stripping and texturing of the manufacturing method of [Fig.l].

[0060] In other words, the control and command unit 4 can be configured on the one hand to receive information representative of at least a portion of the bare copper-based electrical conductor 5 to be stripped and textured, including for example the material used and the geometric dimensions of the portion to be treated; and on the other hand to send operating parameters to the laser source 2 and / or to the optical block 3 to implement the stripping and texturing step, including at least one of the parameters among the wavelength, the pulse duration, the energy per pulse, the pulse frequency, the beam diameter, the scanning speed and the power.

[0061] In the illustrated example, the laser source 2 is configured to emit a beam of radiation in the near infrared in pulses.

[0062] In particular, the laser source 2 is here formed by a pulsed emission fiber laser, of the nanosecond pulse type, configured to emit the laser radiation beam in pulses on the portion of the bare copper-based electrical conductor 5, which comprises the following operating parameters.

[0063] The laser device 1 here emits a pulsed radiation beam which has a wavelength equal to approximately 1070 nm.

[0064] The laser device 1 here emits a pulsed radiation beam which has a pulse duration equal to approximately 120 ns.

[0065] The laser device 1 here emits a pulsed radiation beam which has an energy per pulse equal to approximately 300 pJ.

[0066] The laser device 1 here emits a pulsed radiation beam which has a pulse frequency equal to approximately 60 kHz.

[0067] The laser device 1 here emits a pulsed radiation beam which has a beam diameter equal to approximately 45 pm.

[0068] In the example illustrated, the optical block 3 of the laser device 1 comprises a galvanometric mirror scanning system, also called a scanner.

[0069] The laser device 1 here emits a pulsed radiation beam which is scanned over the portion of the bare copper-based electrical conductor 5 at a speed equal to approximately 2,700 mm / s.

[0070] The laser device 1 furthermore emits a pulsed radiation beam at an average power equal to approximately 18 W and at a peak power of the order of approximately 3 kW.

[0071] The average power corresponds to a so-called “effective” power, which is an average of the power over time, while the peak power corresponds to the power during each pulse and is by definition higher than the average power since the latter takes into account the power which is zero between the pulses.

[0072] It will be noted that the optical block 3 can allow the laser radiation beam to be focused so as to be able to produce a specific pattern on the portion of bare copper-based electrical conductor 5.

[0073] In other words, thanks to the laser device 1, the method can comprise a step of emitting a beam of laser radiation in pulses having at least one of the parameters among: a wavelength between approximately 700 nm and approximately 1600 nm and for example approximately 1070 nm, with a pulse duration of approximately 120 ns, an energy per pulse of approximately 300 pJ, a pulse frequency of approximately 60 kHz, a beam diameter of approximately 45 pm, a scanning speed of approximately 2700 mm / s, and an average power of approximately 18 W; this allowing the combined actions of stripping and texturing according to a determined pattern of the portion of the bare copper-based electrical conductor 5.

[0074] In particular, in the example illustrated in particular in Figures 3 and 4, the stripping and texturing step can be configured to form a network pattern 8 of craters on the treated portion of the bare copper-based electrical conductor 5, here in the form of a blade.

[0075] After the stripping and texturing step, the treated portion of the bare copper-based electrical conductor 5 therefore has a plurality of craters 10 forming the network 8 according to a pattern, for example periodic, with craters 10 formed generally equidistant from each other and having fairly similar geometries and dimensions.

[0076] It will be noted that the above-mentioned operating parameters are selected here to obtain a determined density of craters on the treated portion of the bare copper-based electrical conductor 5.

[0077] In [Fig.4] nine craters 10 formed on a first face are notably visible 11 of the treated portion of the bare copper-based electrical conductor 5 and each having a diameter equal to approximately 30 pm, taking into account the fact that the craters do not necessarily have a perfectly circular outline.

[0078] Each crater 10 is here produced by a single pulse from the laser device.

[0079] Alternatively, one or more craters could be made by several pulses of the laser device.

[0080] With each pulse, the heat generated makes it possible to at least partially separate non-metallic compounds present on the portion of conductor bare electrical conductor based on copper 5 and melting the material of the bare electrical conductor to take the shape of the crater 10.

[0081] The periodic pattern of the network 8 of crater 10 can be obtained by controlling in particular a displacement of the radiation beam and a triggering of the pulses.

[0082] In the example illustrated in [Fig. 5], it will be noted that the movement of the radiation beam is controlled with a so-called horizontal overlap of the scanning lines, of the order of approximately 20% to approximately 25%, on the treated portion of the bare copper-based electrical conductor 5, and almost without vertical overlap or almost, for example with a vertical overlap value, called "hatch", of the order of 55 pm.

[0083] Figures 5 and 6 schematically represent an example of crater 10 formed by the implementation of the stripping and texturing step on the treated portion of the bare copper-based electrical conductor 5.

[0084] Each crater 10 is located in a treatment zone 13 which is a zone thermally affected by the stripping and texturing step.

[0085] Each crater 10 has a depression 14 recessed in the portion of the bare copper-based electrical conductor 5, and a peripheral edge 15 around the depression 14 and projecting from the first face 11.

[0086] The depression 14 is open on the first face 14 and sinks towards a second face 12 of the portion of the bare copper-based electrical conductor 5, opposite the first face 11.

[0087] The crater 10 has a diameter D, here taken between the peripheral edge 15, and a depth P, here taken in the depression 14 from the first face 11 without the peripheral edge 15 projecting, towards the second face 12.

[0088] Even if the craters 10 are not perfectly round, it can be estimated that they have here a diameter D equal to approximately 30 pm and a depth of the order of approximately 2 pm.

[0089] The peripheral edge 15 of the craters 10 may furthermore extend projecting from the first face 11 by a height (not shown) of the order of approximately 1 μm.

[0090] It will be noted that this height can vary from one crater to another and that it can be adjusted in particular as a function of the scanning speed and the vertical overlap value.

[0091] [Fig.7] shows the portion of the bare copper-based electrical conductor 5 of [Fig.5], following an electrical contact resistance test.

[0092] The measurement of electrical contact resistance here makes it possible to quantify and / or qualify the technical effect of the stripping and texturing step on the portion of the bare copper-based electrical conductor 5, in particular on the network 8 of craters. 10.

[0093] The measurement was carried out by applying a copper wire subjected to a determined contact force and along a determined contact distance, on the first face 11 of the portion of the bare copper-based electrical conductor 5.

[0094] In particular, in the example illustrated, the contact force exerted on the copper wire is equal to approximately 20 N over a friction distance of approximately 1 mm.

[0095] It is possible to deduce from this measurement a distribution of the contact resistance of the portion of the bare copper-based electrical conductor 5 treated by the above-mentioned method.

[0096] In particular, this results in stronger adhesion of the copper after removal of the copper wire from the portion of the bare copper-based electrical conductor 5 treated by the above-mentioned method, as visible in [Fig. 5] where copper residues 20 are present on the first face 11.

[0097] The adhesion, synonymous with good contact with little resistance, has here taken place substantially with the peripheral edge 15 around the depressions 14 of craters 10 so that at the location of the copper residues 20, it is more difficult to distinguish the detail of the craters 10.

[0098] In comparison with [Fig.5], [Fig.8] shows a portion of bare copper-based electrical conductor 5' treated by a method different from the method described above, in that the laser device comprises a laser source configured to emit at a wavelength in the visible rather than in the near infrared, and for example at approximately 500 nm.

[0099] A network 8' of craters 10' is formed on the portion of bare copper-based electrical conductor 5', while a deposit 25' here black in color completely or almost completely covers the craters 10' so that it is impossible or almost impossible to observe depressions surrounded by projecting peripheral edges.

[0100] Such a deposit 25' is representative of solid residues, also called "slag" in English terminology, synonymous with pickling not carried out or at least insufficient, and is therefore detrimental to obtaining low contact resistance.

[0101] In the method according to the invention described above, the step of emitting the laser radiation beam having a determined wavelength in the near infrared makes it possible to both strip and texture at least a portion of the bare electrical conductor made from copper.

[0102] The implementation of the combined steps of stripping and texturing by laser radiation at such a wavelength on a bare copper-based electrical conductor thus gives a surface condition to the stripped and textured portion of the electrical conductor which makes it possible to reduce the electrical contact resistance when this bare electrical conductor is in contact with another electrical conductor and a electric current passes through them.

[0103] In particular, thanks to this surface state obtained by implementing the stripping and texturing steps, the inventor has noticed that it is possible to reduce the contact resistance by avoiding the addition to the conductor of an additional coating of the type depositing tin, silver, gold, palladium or even nickel etc.

[0104] Variants not illustrated are described below.

[0105] The manufacturing method may comprise a step of parameterizing the laser device, as a function of determined parameters selected from at least one of the following parameters: a wavelength, a pulse duration, an energy per pulse, a pulse frequency, a beam diameter, a scanning speed and a power, with the laser device which can emit a pulsed radiation beam which has a wavelength of between approximately 700 nm and approximately 1600 nm, which has a pulse duration of between approximately 80 ns and 160 ns, which has an energy per pulse of between approximately 200 pJ and approximately 400 pJ, which has a pulse frequency of between approximately 40 kHz and approximately 80 kHz, which has a beam diameter of between approximately 30 pm and approximately 60 pm, which is scanned at a speed of between approximately 2000 mm / s and approximately 3500 mm / s,and which operates at an average power of between approximately 16 W and 22 W.,

[0106] Such operating parameters are selected to obtain a determined density of craters on the treated portion of the bare copper-based electrical conductor, and may depend in particular on the reflectivity and conductivity properties of the portion of the bare electrical conductor, for example variable if it is copper, brass, etc.

[0107] The laser device may be devoid of a galvanometric mirror scanning system.

[0108] The network of craters may have a periodic pattern different from that illustrated in [Fig.5] in particular, and may have a diameter of, for example, between approximately 20 pm and approximately 40 pm.

[0109] More generally, the invention is not limited to the examples described and represented.

Claims

Claims

1. Method for manufacturing an electrical conductor intended to equip electrical equipment, comprising the steps of providing (101) a bare electrical conductor made from copper (5) and of stripping and texturizing (103) at least a portion of the bare electrical conductor using a laser device (1) emitting radiation comprising a wavelength of between approximately 700 nm and approximately 1600 nm.

2. Manufacturing method according to claim 1, characterized in that the bare copper-based electrical conductor (5) is made of copper or a copper alloy, in particular brass.

3. Manufacturing method according to one of claims 1 and 2, characterized in that the laser device (1) is a nanosecond pulsed laser emitting a beam of laser radiation in pulses.

4. Manufacturing method according to any one of claims 1 to 3, characterized in that the laser device (1) is a pulsed emission fiber laser emitting a beam of laser radiation in pulses.

5. Manufacturing method according to any one of claims 1 to 4, characterized in that the laser device (1) emits a pulsed radiation beam which has a wavelength equal to approximately 1070 nm.

6. Manufacturing method according to any one of claims 1 to 5, characterized in that the laser device (1) emits a pulsed radiation beam which has a pulse duration equal to approximately 120 ns.

7. Manufacturing method according to any one of claims 1 to 6, characterized in that the laser device (1) emits a pulsed radiation beam which has an energy per pulse equal to approximately 300 pJ.

8. Manufacturing method according to any one of claims 1 to 7, characterized in that the laser device (1) emits a pulsed radiation beam which has a pulse frequency equal to approximately 60 kHz.

9. Manufacturing method according to any one of claims 1 to 8, characterized in that the laser device (1) emits a pulsed radiation beam which has a beam diameter equal to approximately 45 pm.

10. Manufacturing method according to any one of claims 1 to 9, characterized in that the laser device emits (1) a pulsed radiation beam which is scanned over the at least one portion of the bare electrical conductor at a speed equal to approximately 2,700 mm / s.

11. Manufacturing method according to any one of claims 1 to 10, characterized in that the laser device (1) emits a pulsed radiation beam at an average power equal to approximately 18 W.

12. Manufacturing method according to any one of claims 1 to 11, characterized in that the stripping and texturizing step (103) is configured to form a network (8) of craters (10) on the at least one portion of the bare electrical conductor (5).

13. Bare electrical conductor intended to equip electrical equipment, characterized in that it is obtained directly by implementing the method according to any one of claims 1 to 12, and that it has a network (8) of craters (10) on at least one stripped and textured portion.

14. Bare electrical conductor according to claim 13, characterized in that the network (8) of craters (10) has a periodic pattern and / or the craters (10) each have a depression (14) recessed in the portion of the bare electrical conductor and a peripheral edge (15) around the depression and projecting.

15. Electrical apparatus comprising at least one bare electrical conductor according to one of claims 13 and 14.