Resist underlayer composition and method of forming patterns using the same

Abstract

To provide a resist underlayer composition that does not cause resist pattern collapse even in a fine patterning process and has improved sensitivity to an exposure light source, thereby capable of improving patterning performance and energy efficiency.SOLUTION: A resist underlayer composition comprises: a polymer with a specific structure having a heterocyclic group including a nitrogen atom in a ring; a photoacid generator having a mass reduction rate of 0% after 3 minutes from the initiation of measurement during thermogravimetric analysis at 205°C in an air atmosphere; and a solvent.SELECTED DRAWING: Figure 1

Description

[Technical field]

[0001] The present invention relates to a composition for a resist underlayer film and a pattern forming method using the same. [Background technology]

[0002] Recently, the semiconductor industry has been evolving from patterns with a size of hundreds of nanometers to ultra-fine technology with patterns with a size of several to tens of nanometers. To realize such ultra-fine technology, effective lithographic techniques are essential.

[0003] Lithographic techniques involve coating a photoresist film onto a semiconductor substrate such as a silicon wafer to form a thin film, then irradiating it with active energy rays such as ultraviolet light through a mask pattern on which a device pattern is drawn.Then, the substrate is developed and etched using the resulting photoresist pattern as a protective film, forming a fine pattern on the substrate surface that corresponds to the pattern.

[0004] As semiconductor patterns are successively miniaturized, the thickness of the photoresist layer is required to be thinner, and therefore the thickness of the resist underlayer film is also required to be thinner. The resist underlayer film must not collapse the photoresist pattern even if it is thin, and must have good adhesion to the photoresist and be formed with a uniform film thickness. In addition, the resist underlayer film is required to have improved sensitivity, such as a high refractive index and a low absorption coefficient for the light used in photolithography. [Prior art documents] [Patent documents]

[0005] [Patent Document 1] Korean Patent Publication No. 10-2023-0020811 Summary of the Invention [Problem to be solved by the invention]

[0006] An object of the present invention is to provide a composition for a resist underlayer film which does not cause resist pattern collapse even in a fine patterning process, has improved sensitivity to an exposure light source, and can improve patterning performance and energy efficiency.

[0007] Another object of the present invention is to provide a pattern forming method using the above-mentioned composition for a resist underlayer film. [Means for solving the problem]

[0008] A composition for a resist underlayer film according to one embodiment includes a polymer including at least one of a structural unit represented by the following chemical formula 1 and a structural unit represented by the following chemical formula 2, a photoacid generator having a mass loss rate of 0% 3 minutes after the start of thermogravimetric analysis at 205° C. in an air atmosphere, and a solvent:

[0009] [ka]

[0010] In the above Chemical Formula 1 and Chemical Formula 2, Each A is independently a heterocyclic group containing a nitrogen atom in the ring, L 1 ~L 6 each independently represents a single bond, a substituted or unsubstituted alkylene group having 1 to 10 carbon atoms, a substituted or unsubstituted heteroalkylene group having 1 to 10 carbon atoms, a substituted or unsubstituted cycloalkylene group having 3 to 20 carbon atoms, a substituted or unsubstituted heterocycloalkylene group having 2 to 20 carbon atoms, a substituted or unsubstituted arylene group having 6 to 20 carbon atoms, a substituted or unsubstituted heteroarylene group having 3 to 20 carbon atoms, or a combination thereof; X 1 ~X 5 each independently represents a single bond, -O-, -S-, -S(=O)-, -S(=O)2-, -C(=O)-, -(CO)O-, -O(CO)O-, or -NR a- (where R a is a hydrogen atom, a deuterium atom, or an alkyl group having 1 to 10 carbon atoms), or a combination thereof; Y 1 ~Y 3 each independently represents a hydroxy group, a substituted or unsubstituted alkyl group having 1 to 10 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 10 carbon atoms, a substituted or unsubstituted alkynyl group having 2 to 10 carbon atoms, a substituted or unsubstituted heteroalkyl group having 1 to 10 carbon atoms, a substituted or unsubstituted heteroalkenyl group having 2 to 10 carbon atoms, a substituted or unsubstituted heteroalkynyl group having 2 to 10 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3 to 20 carbon atoms, a substituted or unsubstituted heterocycloalkyl group having 2 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 20 carbon atoms, a substituted or unsubstituted heteroaryl group having 3 to 20 carbon atoms, or a combination thereof; * indicates a connection point.

[0011] A in the above Chemical Formula 1 and Chemical Formula 2 may be at least one selected from the group consisting of heterocyclic groups represented by the following Chemical Formulae A-1 to A-4:

[0012] [ka]

[0013] In the above chemical formulae A-1 to A-4, * indicates a linking point to another atom or group.

[0014] In the above Chemical Formula 1 and Chemical Formula 2, L 1 ~L 6 each independently represents a single bond, a substituted or unsubstituted alkylene group having 1 to 10 carbon atoms, a substituted or unsubstituted heteroalkylene group having 1 to 10 carbon atoms, or a combination thereof; X in the above Chemical Formula 1 and Chemical Formula 2 1 ~X 5each independently represents a single bond, -O-, -S-, -C(=O)-, -(CO)O-, -O(CO)O-, or a combination thereof; Y in the above Chemical Formula 1 and Chemical Formula 2 1 ~Y 3 may each independently be a substituted or unsubstituted alkyl group having 1 to 10 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 10 carbon atoms, a substituted or unsubstituted heteroalkyl group having 1 to 10 carbon atoms, a substituted or unsubstituted heteroalkenyl group having 2 to 10 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3 to 20 carbon atoms, a substituted or unsubstituted heterocycloalkyl group having 2 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 20 carbon atoms, or a combination thereof.

[0015] The photoacid generator preferably contains at least one selected from the group consisting of a compound represented by the following chemical formula 3, an imide derivative in which a nitrogen atom is substituted with a sulfonic acid (salt) group, and a cyanurate derivative in which a nitrogen atom is substituted with a sulfonic acid (salt) group:

[0016] [ka]

[0017] In the above chemical formula 3, R 2 ~R 4 each independently represents a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 20 carbon atoms, a substituted or unsubstituted alkynyl group having 2 to 20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, or a combination thereof; Z - is a monovalent anion.

[0018] R in the above chemical formula 3 2 ~R 4may each independently be an alkyl group having 1 to 20 carbon atoms in which at least one hydrogen atom is substituted with a halogen atom, an aryl group having 6 to 30 carbon atoms in which at least one hydrogen atom is substituted with a halogen atom, or a combination thereof.

[0019] The photoacid generator may be at least one selected from the group consisting of compounds represented by the following formulas 4 to 7:

[0020] [ka]

[0021] In the above chemical formula 4, R 21 , R 31 , and R 41 are each independently a halogen atom; n21, n31, and n41 are each independently an integer of 0 to 5, where at least one of n21, n31, and n41 is 1 or greater:

[0022] [ka]

[0023] In the above Chemical Formula 5 to Chemical Formula 7, R 51 , R 61 , R 62 , and R 71 each independently represents a deuterium atom, a hydroxy group, a halogen atom, a nitro group, a cyano group, -COOH, a substituted or unsubstituted alkoxy group having 1 to 20 carbon atoms, a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 20 carbon atoms, a substituted or unsubstituted alkynyl group having 2 to 20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, or a combination thereof; R 52 , R63 , and R 72 each independently represents a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 20 carbon atoms, a substituted or unsubstituted alkynyl group having 2 to 20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3 to 20 carbon atoms, a substituted or unsubstituted bicycloalkyl group having 5 to 30 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, or a combination thereof; n51 is an integer from 0 to 2, n71 is an integer from 0 to 6.

[0024] The structural unit represented by Chemical Formula 1 above may be a structural unit represented by Chemical Formula 1-1 or 1-2 below, and the structural unit represented by Chemical Formula 2 above may be at least one selected from the group consisting of structural units represented by Chemical Formulas 2-1 to 2-3 below.

[0025] [ka]

[0026] [ka]

[0027] The photoacid generator may be at least one selected from the group consisting of a compound represented by the following chemical formula 4-1, a compound represented by the following chemical formula 4-2, a compound represented by the following chemical formula 5-1, a compound represented by the following chemical formula 6-1, and a compound represented by the following chemical formula 7-1.

[0028] [ka]

[0029] The weight average molecular weight of the polymer may be from 1,000 g / mol to 300,000 g / mol.

[0030] The content of the photoacid generator in the composition for resist underlayer film can be 10 parts by mass to 100 parts by mass based on 100 parts by mass of the polymer.

[0031] The content of the polymer in the composition for a resist underlayer film may be 0.1% by mass to 50% by mass based on the total mass of the composition for a resist underlayer film.

[0032] The content of the photoacid generator in the composition for resist underlayer film may be 0.01% by mass to 30% by mass based on the total mass of the composition for resist underlayer film.

[0033] The resist underlayer film composition can further contain at least one polymer selected from the group consisting of acrylic resins, epoxy resins, novolac resins, glycoluril resins, and melamine resins.

[0034] The resist underlayer film composition may further include an additive that is a surfactant, a thermal acid generator, a plasticizer, or a combination thereof.

[0035] According to another embodiment, there is provided a method for forming a pattern, the method including: forming a film to be etched on a substrate; applying a resist underlayer film composition according to an embodiment onto the film to be etched to form a resist underlayer film; forming a photoresist pattern on the resist underlayer film; and sequentially etching the resist underlayer film and the film to be etched using the photoresist pattern as an etching mask. Effect of the Invention

[0036] According to the present invention, a composition for a resist underlayer film can be provided that prevents collapse of a resist pattern even in a fine patterning process, improves sensitivity to an exposure light source, and can improve patterning performance and energy efficiency. [Brief description of the drawings]

[0037] [Figure 1] 1 is a schematic cross-sectional view illustrating a pattern forming method using a resist underlayer film composition according to one embodiment of the present invention. FIG. [Diagram 2] 1 is a schematic cross-sectional view illustrating a pattern forming method using a resist underlayer film composition according to one embodiment of the present invention. FIG. [Diagram 3] 1 is a schematic cross-sectional view illustrating a pattern forming method using a resist underlayer film composition according to one embodiment of the present invention. FIG. [Figure 4] 1 is a schematic cross-sectional view illustrating a pattern forming method using a resist underlayer film composition according to one embodiment of the present invention. FIG. [Diagram 5] 1 is a schematic cross-sectional view illustrating a pattern forming method using a resist underlayer film composition according to one embodiment of the present invention. FIG. [Figure 6] 1 is a schematic cross-sectional view illustrating a pattern forming method using a resist underlayer film composition according to one embodiment of the present invention. FIG. [Figure 7] 1 is a schematic cross-sectional view illustrating a pattern forming method using a resist underlayer film composition according to one embodiment of the present invention. FIG. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0038] DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will now be described in detail with reference to exemplary embodiments thereof, so that those skilled in the art will be able to easily practice the present invention. However, the present invention may be embodied in many different forms and should not be construed as being limited to the embodiments set forth herein.

[0039] In the drawings, the thickness of layers and regions is exaggerated to clearly show them, and similar parts are designated by the same reference numerals throughout the specification. When a part such as a layer, film, region, or plate is "on" another part, this includes not only when it is "directly on" the other part, but also when there is another part between them. Conversely, when a part is "directly on" another part, it means that there is no other part between them.

[0040] Hereinafter, unless otherwise defined in the present specification, "substituted" or "substituted" means that a hydrogen atom in a compound is replaced with a deuterium atom, a halogen atom (F, Br, Cl, or I), a hydroxy group, a nitro group, a cyano group, an amino group, an azide group, an amidino group, a hydrazino group, a hydrazono group, a carbonyl group, a carbamoyl group, a thiol group, an ester group, a carboxy group or a salt thereof, a sulfonic acid group or a salt thereof, a phosphate group or a salt thereof, an alkyl group having 1 to 30 carbon atoms, or an alkenyl group having 2 to 30 carbon atoms. , an alkynyl group having 2 to 30 carbon atoms, an aryl group having 6 to 30 carbon atoms, an arylalkyl group having 7 to 30 carbon atoms, an alkoxy group having 1 to 30 carbon atoms, a heteroalkyl group having 1 to 20 carbon atoms, a heteroarylalkyl group having 3 to 20 carbon atoms, a cycloalkyl group having 3 to 30 carbon atoms, a cycloalkenyl group having 3 to 15 carbon atoms, a cycloalkynyl group having 6 to 15 carbon atoms, a heterocyclic group having 2 to 30 carbon atoms, and combinations thereof.

[0041] Furthermore, two adjacent substituents among the substituted halogen atoms (F, Br, Cl, or I), hydroxyl groups, nitro groups, cyano groups, amino groups, azide groups, amidino groups, hydrazino groups, hydrazono groups, carbonyl groups, carbamoyl groups, thiol groups, ester groups, carboxy groups or salts thereof, sulfonic acid groups or salts thereof, phosphate groups or salts thereof, alkyl groups having 1 to 30 carbon atoms, alkenyl groups having 2 to 30 carbon atoms, alkynyl groups having 2 to 30 carbon atoms, aryl groups having 6 to 30 carbon atoms, arylalkyl groups having 7 to 30 carbon atoms, alkoxy groups having 1 to 30 carbon atoms, heteroalkyl groups having 1 to 20 carbon atoms, heteroarylalkyl groups having 3 to 20 carbon atoms, cycloalkyl groups having 3 to 30 carbon atoms, cycloalkenyl groups having 3 to 15 carbon atoms, cycloalkynyl groups having 6 to 15 carbon atoms, and heterocyclic groups having 2 to 30 carbon atoms may be condensed with each other to form a ring.

[0042] In this specification, unless otherwise defined, "hetero" means containing 1 to 3 heteroatoms of at least one type selected from the group consisting of N (nitrogen atom), O (oxygen atom), S (sulfur atom), Se (selenium atom), and P (phosphorus atom).

[0043] As used herein, the term "aryl group" refers to a group having one or more aromatic hydrocarbon moieties, and broadly includes a form in which the aromatic hydrocarbon moieties are linked by a single bond, and a form in which the aromatic hydrocarbon moieties are directly or indirectly fused to a non-aromatic fused ring. The aryl group includes a monocyclic, polycyclic, or fused polycyclic (i.e., rings sharing adjacent pairs of carbon atoms) functional group.

[0044] In this specification, "heterocyclic group" is a concept that includes heteroaryl group. In addition, it means that in a ring compound such as an aryl group, a cycloalkyl group, a condensed ring thereof or a combination thereof, at least one heteroatom selected from N, O, S, P and Si is contained instead of carbon (C). When the heterocyclic group is a condensed ring, the entire heterocyclic group or each ring may contain at least one heteroatom.

[0045] More specifically, the substituted or unsubstituted aryl group and / or the substituted or unsubstituted heterocyclic group are a substituted or unsubstituted phenyl group, a substituted or unsubstituted naphthyl group, a substituted or unsubstituted anthracenyl group, a substituted or unsubstituted phenanthryl group, a substituted or unsubstituted naphthacenyl group, a substituted or unsubstituted pyrenyl group, a substituted or unsubstituted biphenyl group, a substituted or unsubstituted terphenyl group, a substituted or unsubstituted quaterphenyl group, a substituted or unsubstituted chrysenyl group, a substituted or unsubstituted triphenyl group, a substituted or unsubstituted ter ... A phenylenyl group, a substituted or unsubstituted perylenyl group, a substituted or unsubstituted indenyl group, a substituted or unsubstituted furanyl group, a substituted or unsubstituted thiophenyl group, a substituted or unsubstituted pyrrolyl group, a substituted or unsubstituted pyrazolyl group, a substituted or unsubstituted imidazolyl group, a substituted or unsubstituted triazolyl group, a substituted or unsubstituted oxazolyl group, a substituted or unsubstituted thiazolyl group, a substituted or unsubstituted oxadiazolyl group, a substituted or unsubstituted thiadiazolyl group, a substituted or unsubstituted pyridinyl group, a substituted or unsubstituted pyrimidinyl group, a substituted or unsubstituted pyrazinyl group, a substituted or unsubstituted triazinyl group, a substituted or unsubstituted benzofuranyl group, a substituted or unsubstituted benzothiophenyl group, a substituted or unsubstituted benzimidazolyl group, a substituted or unsubstituted indolyl group, a substituted or unsubstituted quinolinyl group, a substituted or unsubstituted isoquinolinyl group, a substituted or unsubstituted quinazolinyl group, a substituted or unsubstituted quinoxalinyl group, a substituted or unsubstituted naphthyridinyl group, a substituted or unsubstituted substituted or unsubstituted benzoxazinyl group, substituted or unsubstituted benzothiazinyl group, substituted or unsubstituted acridinyl group, substituted or unsubstituted phenazinyl group, substituted or unsubstituted phenothiazinyl group, substituted or unsubstituted phenoxazinyl group, substituted or unsubstituted fluorenyl group, substituted or unsubstituted dibenzofuranyl group, substituted or unsubstituted dibenzothiophenyl group, substituted or unsubstituted carbazolyl group, pyridoindolyl group, benzopyridoxazinyl group, benzopyridothiazinyl group, 9,9-dimethyl-9,10-dihydroacridinyl group, a combination thereof, or a combination thereof condensed with each other, but are not limited thereto.

[0046] In this specification, unless otherwise specified, "combination" means mixing or copolymerization.

[0047] In addition, in this specification, the term "polymer" can include both oligomers and polymers.

[0048] In this specification, unless otherwise specified, the "weight average molecular weight" is measured by dissolving a powder sample in tetrahydrofuran (THF) and then using 1200 series gel permeation chromatography (GPC) manufactured by Agilent Technologies (the column used is LF-804 manufactured by Shodex Corporation, and the standard sample is polystyrene manufactured by Shodex Corporation).

[0049] Additionally, in this specification, unless otherwise defined, "*" indicates a structural unit of a compound or a linking point of a moiety of a compound.

[0050] In the semiconductor industry, there is a continuing demand to reduce the size of chips. To meet this trend, there is a demand to reduce the line width of resist patterned by lithography technology to a size of several tens of nanometers. Using the pattern thus formed, the pattern is transferred to the underlying material by an etching process on the underlying substrate. However, as the resist pattern size becomes smaller, the height of the resist that can withstand the line width is limited, and as a result, the resist may not have sufficient resistance in the etching step. Therefore, when a resist material is applied thinly, when the substrate to be etched is thick, or when a deep pattern is required, a resist underlayer film has been used to compensate for this.

[0051] The resist underlayer film is required to become thinner as the resist becomes thinner, and the photoresist pattern must not collapse even when the resist underlayer film is thin. For this reason, the resist underlayer film must have excellent adhesion to the photoresist. In addition, when forming a thin resist underlayer film, it is required that the coating uniformity of the resist underlayer film composition and the flatness of the resist underlayer film produced therefrom are improved, the sensitivity to the exposure light source is improved, and the pattern formability and energy efficiency are improved.

[0052] A composition for a resist underlayer film according to one embodiment includes a polymer including at least one of a structural unit represented by the following chemical formula 1 and a structural unit represented by the following chemical formula 2, a photoacid generator that exhibits a mass loss rate of 0% 3 minutes after the start of thermogravimetric analysis (TGA) at 205° C. in an air atmosphere (air gas), and a solvent:

[0053] [ka]

[0054] In the above Chemical Formula 1 and Chemical Formula 2, Each A is independently a heterocyclic group containing a nitrogen atom in the ring, L 1 ~L 6 each independently represents a single bond, a substituted or unsubstituted alkylene group having 1 to 10 carbon atoms, a substituted or unsubstituted heteroalkylene group having 1 to 10 carbon atoms, a substituted or unsubstituted cycloalkylene group having 3 to 20 carbon atoms, a substituted or unsubstituted heterocycloalkylene group having 2 to 20 carbon atoms, a substituted or unsubstituted arylene group having 6 to 20 carbon atoms, a substituted or unsubstituted heteroarylene group having 3 to 20 carbon atoms, or a combination thereof; X 1 ~X 5 each independently represents a single bond, -O-, -S-, -S(=O)-, -S(=O)2-, -C(=O)-, -(CO)O-, -O(CO)O-, or -NRa - (where R a is a hydrogen atom, a deuterium atom, or an alkyl group having 1 to 10 carbon atoms), or a combination thereof; Y 1 ~Y 3 each independently represents a hydroxy group, a substituted or unsubstituted alkyl group having 1 to 10 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 10 carbon atoms, a substituted or unsubstituted alkynyl group having 2 to 10 carbon atoms, a substituted or unsubstituted heteroalkyl group having 1 to 10 carbon atoms, a substituted or unsubstituted heteroalkenyl group having 2 to 10 carbon atoms, a substituted or unsubstituted heteroalkynyl group having 2 to 10 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3 to 20 carbon atoms, a substituted or unsubstituted heterocycloalkyl group having 2 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 20 carbon atoms, a substituted or unsubstituted heteroaryl group having 3 to 20 carbon atoms, or a combination thereof; * indicates a connection point.

[0055] The structural units represented by Chemical Formulae 1 and 2 above, and Chemical Formulae 1-1 and 1-2, and Chemical Formulae 2-1 and 2-3 described below, are repeating units contained in the polymer according to the present invention.

[0056] In the composition for a resist underlayer film according to one embodiment, the structural unit represented by Chemical Formula 1 and the structural unit represented by Chemical Formula 2 each contain a heterocycle containing a nitrogen atom in the ring, and thus the polymer containing these structural units has sp 2 -sp 2Bonding is possible. As a result, the polymer can have high electron density. By including a polymer with high electron density, the resist underlayer film composition according to an embodiment can realize a film with a dense structure in the form of an ultrathin film. In addition, the high electron density of the polymer can have the effect of improving the light absorption efficiency during exposure of the resist underlayer film composition. In addition, by including a heterocyclic skeleton, the etching selectivity is excellent, and the energy efficiency during pattern formation after exposure using high-energy rays such as EUV (extreme ultraviolet; wavelength 13.5 nm) and E-Beam (electron beam) can be improved.

[0057] In the above chemical formula 1 and chemical formula 2, A may be each independently at least one selected from the group consisting of heterocyclic groups represented by the following chemical formulas A-1 to A-4:

[0058] [ka]

[0059] In the above chemical formulae A-1 to A-4, * indicates a linking point to another atom or group.

[0060] In one embodiment, L in Formula 1 and Formula 2 above 1 ~L 6 are each independently a single bond, a substituted or unsubstituted alkylene group having 1 to 10 carbon atoms, a substituted or unsubstituted heteroalkylene group having 1 to 10 carbon atoms, or a combination thereof, for example, but not limited to, a single bond, a substituted or unsubstituted alkylene group having 1 to 5 carbon atoms, a substituted or unsubstituted heteroalkylene group having 1 to 5 carbon atoms, or a combination thereof.

[0061] X in the above Chemical Formula 1 and Chemical Formula 2 1 ~X 5are each independently a single bond, -O-, -S-, -C(=O)-, -(CO)O-, -O(CO)O-, or a combination thereof, for example, but not limited to, -O-, -S-, -(CO)O-, or a combination thereof.

[0062] Y in the above Chemical Formula 1 and Chemical Formula 2 1 ~Y 3 are each independently a substituted or unsubstituted alkyl group having 1 to 10 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 10 carbon atoms, a substituted or unsubstituted heteroalkyl group having 1 to 10 carbon atoms, a substituted or unsubstituted heteroalkenyl group having 2 to 10 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3 to 20 carbon atoms, a substituted or unsubstituted heterocycloalkyl group having 2 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 20 carbon atoms, or a combination thereof, such as, but not limited to, a substituted or unsubstituted alkyl group having 1 to 5 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 5 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3 to 10 carbon atoms, a substituted or unsubstituted aryl group having 6 to 10 carbon atoms, or a combination thereof.

[0063] For example, the structural unit represented by the above chemical formula 1 is preferably at least one of a structural unit represented by the following chemical formula 1-1 and a structural unit represented by the following chemical formula 1-2, and the structural unit represented by the above chemical formula 2 is preferably at least one selected from the group consisting of structural units represented by the following chemical formulas 2-1 to 2-3.

[0064] [ka]

[0065] [ka]

[0066] In the above Chemical Formulae 1-1 to 1-2 and 2-1 to 2-3, * indicates a linking point.

[0067] In addition, the composition of the present invention contains a photoacid generator, and thus can selectively provide additional acid to the exposed portion of the photoresist during exposure. This can increase the deprotection reaction of the photoresist, improve the sensitivity, and improve the line width roughness (LWR) of the pattern. In addition, when the photoacid generator was subjected to thermogravimetric analysis (TGA) in an air atmosphere at a temperature of 205°C, the mass loss rate after 3 minutes from the start of the measurement was 0%, so that the photoacid generator can improve the sensitivity of the photoresist without being decomposed or volatilized at high temperatures. The detailed method of the thermogravimetric analysis of the photoacid generator is described in the Examples.

[0068] The photoacid generator may be at least one selected from the group consisting of a compound represented by the following chemical formula 3, an imide derivative in which a nitrogen atom is substituted with a sulfonic acid (salt) group, and a cyanurate derivative in which a nitrogen atom is substituted with a sulfonic acid (salt) group.

[0069] [ka]

[0070] In the above chemical formula 3, R 2 ~R 4 are each independently a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 20 carbon atoms, a substituted or unsubstituted alkynyl group having 2 to 20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, or a combination thereof. For example, R 2 ~R 4are each independently an alkyl group having 1 to 20 carbon atoms substituted with at least one halogen atom, an aryl group having 6 to 30 carbon atoms substituted with at least one halogen atom, or a combination thereof, but are not limited to these.

[0071] In the above chemical formula 3, Z - is a monovalent anion, such as a halide anion or an organic anion containing a sulfonic acid group, such as a fluoride ion (F - ), CF3SO3 - , or C4F9SO3 - but is not limited to these.

[0072] In one embodiment, the compound represented by the above formula 3 may be a compound represented by the following formula 4:

[0073] [ka]

[0074] In the above chemical formula 4, R 21 , R 31 , and R 41 are each independently a halogen atom. Examples of halogen atoms include, but are not limited to, fluorine (F) or iodine (I).

[0075] In the above chemical formula 4, n21, n31, and n41 are each independently one of integers from 0 to 5, for example, one of integers from 0 to 3, for example, one of integers from 0 to 2, and in this case, at least one of n21, n31, and n41 is an integer of 1 or more.

[0076] In one embodiment, the compound represented by the above chemical formula 4 is at least one of a compound represented by the following chemical formula 4-1 and a compound represented by the following chemical formula 4-2.

[0077] [ka]

[0078] In the imide derivative or cyanurate derivative in which the nitrogen atom is substituted with a sulfonic acid (salt) group, the imide derivative may be a linear compound containing an imide structure, a five-membered ring compound containing an imide structure, a six-membered ring compound containing an imide structure, or a derivative thereof, and the five-membered ring and the six-membered ring may be condensed with one or more rings on one side. The nitrogen atom in the imide structure is substituted with a sulfonic acid (salt) group.

[0079] Cyanurate derivatives have at least one of the nitrogen atoms of the cyanurate substituted with a sulfonic acid (salt) group.

[0080] The sulfonic acid (salt) group substituted on the nitrogen atom can be represented as R1SO3-, where R 1 can be a monovalent organic group.

[0081] The imide derivative in which a nitrogen atom is substituted with a sulfonic acid (salt) group or the cyanurate derivative in which a nitrogen atom is substituted with a sulfonic acid (salt) group may be at least one selected from the group consisting of compounds represented by the following Chemical Formulas 5 to 7.

[0082] [ka]

[0083] In the above Chemical Formula 5 to Chemical Formula 7, R 51 , R 61 , R 62 , and R 71may each independently be a deuterium atom, a hydroxyl group, a halogen atom, a nitro group, a cyano group, -COOH, a substituted or unsubstituted alkoxy group having 1 to 20 carbon atoms, a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 20 carbon atoms, a substituted or unsubstituted alkynyl group having 2 to 20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, or a combination thereof. For example, R 51 , R 61 , R 62 , and R 71 may each independently be a deuterium atom, a hydroxyl group, a halogen atom, a substituted or unsubstituted alkoxy group having 1 to 10 carbon atoms, a substituted or unsubstituted alkyl group having 1 to 10 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 10 carbon atoms, or a combination thereof. For example, R 51 , R 61 , R 62 , and R 71 may each independently be a substituted or unsubstituted alkenyl group having 2 to 10 carbon atoms.

[0084] In the above Chemical Formula 5, n51 is one of integers from 0 to 2, and can be, for example, 0 or 1, or, for example, 0, but is not limited thereto.

[0085] In the above Chemical Formula 7, n71 is one of integers from 0 to 6, for example, any of integers from 0 to 3, such as 0 or 1, or for example, 0, but is not limited thereto.

[0086] R in the above Chemical Formula 5 to Chemical Formula 7 52 , R 63 , and R 72are each independently a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 20 carbon atoms, a substituted or unsubstituted alkynyl group having 2 to 20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3 to 20 carbon atoms, a substituted or unsubstituted bicycloalkyl group having 5 to 30 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, or a combination thereof.

[0087] For example, R in Chemical Formula 5 and Chemical Formula 7 52 and R 72 may each independently be an unsubstituted alkyl group having 1 to 20 carbon atoms, a substituted or unsubstituted bicycloalkyl group having 5 to 30 carbon atoms, an alkyl group substituted with a substituted or unsubstituted bicycloalkyl group having 5 to 30 carbon atoms, or a combination thereof. 52 and R 72 may each independently be an alkyl group having 1 to 20 carbon atoms substituted with a substituted bicycloalkyl group having 5 to 20 carbon atoms, but is not limited thereto.

[0088] In addition, R in the above chemical formula 6 63 is, for example, a substituted or unsubstituted alkyl group having 1 to 10 carbon atoms, for example, an alkyl group having 1 to 10 carbon atoms substituted with a halogen atom, for example, an alkyl group having 1 to 5 carbon atoms substituted with a fluorine atom, but is not limited to these.

[0089] For example, the compound represented by the above formula 5 may be a compound represented by the following formula 5-1. The compound represented by the above formula 6 may be a compound represented by the following formula 6-1. The compound represented by the above formula 7 may be a compound represented by the following formula 7-1.

[0090] [ka]

[0091] The above polymer has a weight average molecular weight of 1,000g / mol to 300,000g / mol, for example, 3,000g / mol to 200,000g / mol, for example, 3,000g / mol to 100,000g / mol, for example, 3,000g / mol to 90,000g / mol, for example, 3,000g / mol to 70,000g / mol, for example, 3,000g / mol to 60,000g / mol, for example, 3,000g / mol to 50,000g / mol, for example, 5,000g / mol to 50,000g / mol, for example, 5,000g / mol to 30,000g / mol, but is not limited thereto.By having a weight average molecular weight in the above range, the carbon content and solubility in a solvent of the composition for resist underlayer film containing the polymer can be adjusted and optimized.

[0092] The content of the photoacid generator in the composition of the present invention may be 10 parts by mass to 100 parts by mass based on 100 parts by mass of the polymer. The content may be, for example, 10 parts by mass to 80 parts by mass, for example, 10 parts by mass to 70 parts by mass, for example, 10 parts by mass to 60 parts by mass, for example, 20 parts by mass to 60 parts by mass, for example, 30 parts by mass to 100 parts by mass, for example, 30 parts by mass to 70 parts by mass, but is not limited thereto. By including the photoacid generator in the above content range, the amount of acid provided to the resist from the film formed from the resist underlayer film composition containing them can be optimized, and the sensitivity to the exposure light source is improved, and the patterning performance and energy efficiency are improved.

[0093] The polymer may be contained in an amount of 0.1% by mass to 50% by mass based on the total mass of the composition for resist underlayer film. More specifically, the polymer may be contained in an amount of 10% by mass to 50% by mass, for example, 20% by mass to 50% by mass, for example, 20% by mass to 30% by mass based on the total mass of the composition for resist underlayer film, but is not limited thereto. If the content of the polymer is within the above range, the thickness, surface roughness, and planarization properties of the resist underlayer film can be adjusted by including the polymer in the composition.

[0094] The photoacid generator may be included in a content of 0.01% by mass to 30% by mass based on the total mass of the composition for resist underlayer film. More specifically, the photoacid generator may be included in a content of 0.1% by mass to 30.0% by mass based on the total mass of the composition for resist underlayer film, such as 1.0% by mass to 30.0% by mass, such as 5.0% by mass to 30.0% by mass, such as 5.0% by mass to 25.0% by mass, such as 8.0% by mass to 25.0% by mass, such as 10.0% by mass to 25.0% by mass, but is not limited thereto. If the photoacid generator is included in the composition in the above content range, the thickness, surface roughness, chemical resistance, and planarization properties of the resist underlayer film can be adjusted by including the photoacid generator in the composition.

[0095] The above polymer and photoacid generator can be synthesized by appropriately referring to a conventionally known synthesis method. More specifically, a person skilled in the art can easily synthesize them by referring to the synthesis methods described in the Examples.

[0096] The resist underlayer film composition according to an embodiment may contain a solvent. The solvent is not particularly limited as long as it has sufficient solubility and / or dispersibility for the polymer and the compound. Specific examples of the solvent may include, but are not limited to, propylene glycol, propylene glycol diacetate, methoxypropanediol, diethylene glycol, diethylene glycol butyl ether, tri(ethylene glycol) monomethyl ether, propylene glycol monomethyl ether, propylene glycol monomethyl ether acetate, cyclohexanone, ethyl lactate, γ-butyrolactone, N,N-dimethylformamide, N,N-dimethylacetamide, N-methyl-2-pyrrolidinone, methyl 2-hydroxyisobutyrate, acetylacetone, ethyl 3-ethoxypropionate, or combinations thereof.

[0097] The resist underlayer film composition according to an embodiment may further include at least one polymer selected from an acrylic resin, an epoxy resin, a novolac resin, a glycoluril resin, and a melamine resin, in addition to the polymer, the compound, and the solvent, but is not limited thereto.

[0098] In addition, the resist underlayer film composition according to another embodiment may further include additives including a surfactant, a thermal acid generator, a plasticizer, or a combination thereof.

[0099] The surfactant can be used to improve coating defects caused by an increase in solid content concentration during the formation of the resist underlayer film.Specific examples of the surfactant include, but are not limited to, alkylbenzenesulfonate, alkylpyridinium salt, polyethylene glycol, and quaternary ammonium salt.

[0100] Examples of the thermal acid generator that can be used include, but are not limited to, acidic compounds such as p-toluenesulfonic acid, trifluoromethanesulfonic acid, pyridinium p-toluenesulfonate, salicylic acid, sulfosalicylic acid, citric acid, benzoic acid, hydroxybenzoic acid, and naphthalenecarboxylic acid, and / or benzoin tosylate, 2-nitrobenzyl tosylate, and other organic sulfonic acid alkyl esters.

[0101] The plasticizer is not particularly limited, and various types of plasticizers known in the art can be used. Examples of the plasticizer include low molecular weight compounds such as phthalates, adipic esters, phosphates, trimellitates, and citrates, polyether-based, polyester-based, and polyacetal-based compounds.

[0102] The additive may be contained in an amount of 0.001 to 40 parts by mass relative to 100 parts by mass of the composition for resist underlayer film. If the content of the additive is within the above range, the solubility of the composition for resist underlayer film can be improved without changing the optical properties of the composition for resist underlayer film.

[0103] According to another embodiment, there is provided a resist underlayer film prepared using the above-mentioned composition for a resist underlayer film. The resist underlayer film may be in a form including a cured product obtained by, for example, coating the composition for a resist underlayer film on a substrate and then curing the composition through a heat treatment process.

[0104] Hereinafter, a method for forming a pattern using the above-mentioned composition for a resist underlayer film will be described with reference to Fig. 1 to Fig. 7. Fig. 1 to Fig. 7 are schematic cross-sectional views for explaining the method for forming a pattern using the composition for a resist underlayer film according to the present invention.

[0105] Referring to Fig. 1, first, an object to be etched is prepared. An example of the object to be etched may be a thin film 102 formed on a semiconductor substrate 100. Hereinafter, only the case where the object to be etched is the thin film 102 will be described. In order to remove contaminants remaining on the thin film 102, the surface of the thin film is cleaned. The thin film 102 may be, for example, a silicon nitride film, a polysilicon film, or a silicon oxide film.

[0106] Next, the above-mentioned composition for a resist underlayer film is coated on the surface of the cleaned thin film 102 by applying a spin coating method.

[0107] Thereafter, drying and baking processes are performed to form a resist underlayer film 104 on the thin film. The baking process can be performed at 100° C. to 500° C., for example, at 100° C. to 300° C. A more specific description of the composition for the resist underlayer film has been given above in detail, so it will be omitted to avoid duplication.

[0108] 2, a photoresist is coated on the resist underlayer film 104 to form a photoresist film 106. Then, a first baking process is performed to heat the substrate 100 on which the photoresist film 106 is formed. The first baking process can be performed at a temperature of 90°C to 120°C.

[0109] 3, the photoresist film 106 is selectively exposed to light. To explain an exposure process for exposing the photoresist film 106 as an example, an exposure mask having a predetermined pattern formed thereon is positioned on a mask stage of an exposure tool, and an exposure mask 110 is aligned on the photoresist film 106. Then, light is irradiated onto the exposure mask 110, so that a predetermined portion of the photoresist film 106 formed on the substrate 100 selectively reacts with the light transmitted through the exposure mask 110.

[0110] Examples of light that can be used in the exposure process include short wavelength light such as i-rays, which are active energy rays having a wavelength of 365 nm, KrF excimer lasers having a wavelength of 248 nm, and ArF excimer lasers having a wavelength of 193 nm. Other examples include EUV (Extreme ultraviolet), which has a wavelength of 13.5 nm and corresponds to extreme ultraviolet rays.

[0111] The exposed regions 106b of the photoresist film 106 form polymers through a crosslinking reaction such as condensation between organometallic compounds, and thus have a different solubility from the unexposed regions 106a of the photoresist film 106.

[0112] Next, a second baking process is performed on the substrate 100. The second baking process can be performed at a temperature of 90° C. to 200° C. By performing the second baking process, the exposed region 106b of the photoresist film 106 becomes less soluble in a developer.

[0113] As shown in FIG. 4, the resist underlayer film 104 formed from the resist underlayer film composition according to an embodiment is formed by dissolving an acid (H + By providing the resist pattern 107, the difference in solubility in a developer between the unexposed region 106a and the exposed region 106b of the photoresist film 106 can be made larger, thereby improving the line roughness of the photoresist pattern and ensuring excellent pattern formability.

[0114] Referring to FIG. 5, the photoresist film 106a corresponding to the non-exposed region is dissolved and removed using an organic solvent developer such as 2-heptanone, and the photoresist film 106b remaining after development forms a photoresist pattern 108.

[0115] As described above, the developer used in the pattern formation method according to an embodiment can be an organic solvent.Examples of the organic solvent used in the pattern formation method according to an embodiment can include ketones such as methyl ethyl ketone, acetone, cyclohexanone, and 2-heptanone, alcohols such as 4-methyl-2-propanol, 1-butanol, isopropanol, 1-propanol, and methanol, esters such as propylene glycol monomethyl ether acetate, ethyl acetate, ethyl lactate, n-butyl acetate, and butyrolactone, aromatic compounds such as benzene, xylene, and toluene, or combinations thereof.

[0116] However, the photoresist pattern according to an embodiment is not limited to being formed as a negative tone image, and may be formed to have a positive tone image. In this case, examples of developers that can be used to form a positive tone image include quaternary ammonium hydroxide compounds such as tetraethylammonium hydroxide, tetrapropylammonium hydroxide, tetrabutylammonium hydroxide, or combinations thereof.

[0117] As described above, the photoresist pattern 108 formed by exposure to light having a wavelength such as i-line (wavelength 365 nm), KrF excimer laser (wavelength 248 nm), ArF excimer laser (wavelength 193 nm), and high-energy light such as extreme ultraviolet (EUV, Extreme UltraViolet; wavelength 13.5 nm) and E-Beam (electron beam) can have a thickness width of 5 nm to 100 nm. As an example, the photoresist pattern 108 can be formed with a width of, for example, 5 nm to 90 nm, 5 nm to 80 nm, 5 nm to 70 nm, 5 nm to 60 nm, 5 nm to 50 nm, 5 nm to 40 nm, 5 nm to 30 nm, 5 nm to 20 nm, or 5 nm to 10 nm.

[0118] On the other hand, the photoresist pattern 108 may have a pitch with a half pitch of 50 nm or less, such as 40 nm or less, such as 30 nm or less, such as 20 nm or less, such as 10 nm or less, and a line width roughness of 5 nm or less, 3 nm or less, 2 nm or less, 1 nm or less.

[0119] Then, the photoresist pattern 108 is used as an etching mask to etch the resist underlayer film 104. Through this etching process, an organic film pattern 112 as shown in FIG.

[0120] The formed organic film pattern 112 may also have a width corresponding to the photoresist pattern 108. The etching may be performed by dry etching using an etching gas, for example, CHF3, CF4, Cl2, O2, or a mixture thereof. As described above, the resist underlayer film formed using the resist underlayer film composition according to an embodiment has a high etching rate, and therefore, a smooth etching process can be performed in a short time.

[0121] 7, the photoresist pattern 108 is applied as an etching mask to etch the exposed thin film 102. As a result, the thin film is formed into a thin film pattern 114.

[0122] The thin film pattern 114 formed by the previous exposure process using a short wavelength light source such as i-line (wavelength 365 nm) which is an active energy ray, KrF excimer laser (wavelength 248 nm), ArF excimer laser (wavelength 193 nm), etc. may have a width of several tens of nm to several hundreds of nm. The thin film pattern 114 formed by the exposure process using an EUV light source may have a width of 20 nm or less. EXAMPLES

[0123] The present invention will be described in more detail below through examples of the synthesis of the above-mentioned polymer and the preparation of a composition for a resist underlayer film containing the same. However, the present invention is not technically limited by the following examples.

[0124] [Polymer synthesis] (Synthesis Example 1) In a 500 ml three-neck round-bottom flask, 24.9 g of 1,3-diallyl-5-(2-hydroxyethyl)isocyanurate, 7.4 g of 2-mercaptoethanol, 0.7 g of azobisisobutyronitrile (AIBN), and 48 g of N,N-dimethylformamide (DMF) were added, and a condenser was connected. After the reaction was allowed to proceed for 16 hours at a temperature of 80°C, the reaction solution was cooled to room temperature (25°C). The reaction solution was dropped into a 1 L wide-mouth bottle containing 800 g of water while stirring to generate gum, which was then dissolved in 80 g of tetrahydrofuran (THF). Toluene was added to the resulting solution to form a precipitate, and monomers and low molecules were removed, finally obtaining polymer A composed of structural units represented by the following chemical formula 1-1 (weight average molecular weight (Mw) = 10,500 g / mol).

[0125] [ka]

[0126] In the above chemical formula 1-1, n is the number of structural units.

[0127] (Synthesis Example 2) In a 500 ml three-neck round-bottom flask, 24.9 g of 1,3,5-triallyl-1,3,5-triazinane-2,4,6-trione, 7.4 g of 2-mercaptoethanol, 0.7 g of AIBN, and 48 g of N,N-dimethylformamide were added, and a condenser was connected. After the reaction was allowed to proceed for 16 hours at a temperature of 80°C, the reaction solution was cooled to room temperature (25°C). The reaction solution was dropped into a 1 L wide-mouth bottle containing 800 g of water while stirring to produce gum, which was then dissolved in 80 g of THF. The resulting solution was used to form a precipitate using toluene, and monomers and low molecules were removed, finally obtaining polymer B composed of structural units represented by the following chemical formula 1-2 (weight average molecular weight (Mw) = 8,000 g / mol).

[0128] [ka]

[0129] (Synthesis Example 3) A reaction solution was prepared by adding 20 g of 1,3-diallyl-5,5-dimethyl-1,3-diazinan-2,4,6(1H,3H,5H)-trione, 8.4 g of 2,3-dimercapto-1-propanol, 0.5 g of azobisisobutyronitrile (AIBN), and 50 g of N,N-dimethylformamide to a 250 mL four-neck flask, and a capacitor was connected. The reaction solution was heated at 60°C for 5 hours to proceed with the reaction, and then the reaction solution was cooled to room temperature (25°C). The reaction solution was then dropped into a beaker containing 300 g of distilled water while stirring to generate gum, which was then dissolved in 30 g of THF. The resulting solution was precipitated with toluene to remove monomers and low molecular weights, and finally polymer C composed of structural units represented by the following chemical formula 2-1 was obtained (weight average molecular weight (Mw) = 3,700 g / mol).

[0130] [ka]

[0131] (Synthesis Example 4) In a 1L two-neck round-bottom flask, 148.6g (0.5mol) of 1,3,5-triglycidyl isocyanurate, 60.0g (0.4mol) of 2,2'-thiodiacetic acid, 9.1g of benzyltriethylammonium chloride, and 350g of N,N-dimethylformamide (DMF) were placed, and a condenser was connected. The temperature was raised to 100°C, and the reaction was allowed to proceed for 8 hours, after which the reaction solution was cooled to room temperature (23°C). The reaction solution was then transferred to a 1L wide-mouth bottle, washed three times with hexane, and then washed in sequence with purified water. The resulting gum-like resin was completely dissolved using 80g of THF, and then slowly dropped into 700g of toluene under stirring. The solvent was then removed to finally obtain polymer D composed of structural units represented by the following chemical formula 2-2 (weight average molecular weight (Mw) = 9,100g / mol).

[0132] [ka]

[0133] (Synthesis Example 5) A reaction solution was prepared by adding 20g of 1,3-diallyl-5-(1-hydroxyethyl)-isocyanurate, 6.0g of ethane-1,2-dithiol, 1g of azobisisobutyronitrile (AIBN), and 50g of N,N-dimethylformamide to a 250mL four-neck flask, and a condenser was connected. The reaction solution was heated at 50°C for 5 hours to proceed with the reaction, and then 10g of 3,4-difluorobenzyl mercaptan and 1g of azobisisobutyronitrile (AIBN) were added and the reaction was continued for an additional 2 hours, and the solution was cooled to room temperature. The reaction solution was then dropped into a beaker containing 300g of distilled water while stirring to produce a gum, which was then dissolved in 30g of THF. The dissolved resin solution was precipitated in toluene to remove monomolecules and low molecular weights, and finally polymer E represented by the following chemical formula 2-3 was obtained (weight average molecular weight (Mw) = 5,500 g / mol).

[0134] [ka]

[0135] [Synthesis of photoacid generator] (Synthesis Example 6) In a 500mL one-neck flask, 6g of diphenyl sulfoxide, 6.7g of iodobenzene, and 200g of dichloromethane were added. Then, 9.3g of trifluoromethanesulfonic anhydride was slowly added dropwise, and the reaction was allowed to proceed at -78°C for 30 minutes, and then allowed to react again at room temperature (25°C) for 4 hours. Then, the reaction solution was washed with distilled water, and the organic solution portion was taken to remove the solvent. The organic matter from which the solvent had been removed was dissolved in dichloromethane, and diethyl ether was slowly added dropwise. The precipitated solid was filtered and dried to obtain a compound represented by the following chemical formula 4-1.

[0136] [ka]

[0137] (Synthesis Example 7) A compound represented by the following chemical formula 4-2 was obtained in the same manner as in Synthesis Example 6, except that 3.2 g of fluorobenzene was used instead of iodobenzene.

[0138] [ka]

[0139] (Synthesis Example 8) In a 100mL one-neck flask, 1.6g of 5-norbornene-2,3-dicarboximide, 4.8g of di-tert-butyl dicarbonate, and 0.12g of 4-dimethylaminopyridine were added to 5ml of acetonitrile, and the reaction was allowed to proceed at room temperature (25°C). After this, 0.61ml of hydroxylamine (50% by mass aqueous solution) was added dropwise, and the reaction was allowed to proceed for 24 hours at room temperature. After this, 10ml of diethyl ether was added, and the generated solid was filtered, washed with diethyl ether, and dried. The dried solid was added to 15ml of distilled water, and dilute hydrochloric acid was added until the pH became 1. The undissolved hydroxy-5-norbornene-2,3-dicarboximide solid was filtered, washed with distilled water, and dried.

[0140] After that, under a nitrogen atmosphere, 1.4g of hydroxy-5-norbornene-2,3-dicarboxylic acid imide and 1.7g of tosyl chloride were added to 30ml of THF in a 100mL three-neck flask, cooled to -5°C, and then 1.6g of triethylamine was slowly added dropwise. After reacting for 24 hours, the mixture was filtered and dried at room temperature (25°C) to obtain a solid. The solid was dissolved in ethyl acetate and mixed with a 1% by mass aqueous solution of sodium bicarbonate, and the ethyl acetate layer was separated. After that, the ethyl acetate solvent was completely removed to obtain a compound represented by the following chemical formula 5-1.

[0141] [ka]

[0142] (Synthesis Example 9) A compound represented by the following chemical formula 6-1 was obtained in the same manner as in Synthesis Example 8, except that 2.1 g of 1,3-diallyl-1,3,5-triazinane-2,4,6-trione was used instead of 5-norbornene-2,3-dicarboximide.

[0143] [ka]

[0144] (Synthesis Example 10) In a 100mL one-neck flask, 2g of 1,8-naphthalimide, 4.8g of di-tert-butyl dicarbonate, and 0.12g of 4-dimethylaminopyridine were added to 5ml of acetonitrile, and the reaction was allowed to proceed at room temperature (25°C). After this, 0.61ml of hydroxylamine (50% by mass aqueous solution) was dropped, and the reaction was allowed to proceed at room temperature (25°C) for 24 hours. After this, 10ml of diethyl ether was added, and the solid generated was filtered, washed with diethyl ether, and dried. The dried solid was put into 15ml of distilled water, and dilute hydrochloric acid was added until the pH became 1. The undissolved N-hydroxynaphthalimide solid was filtered, washed with distilled water, and then dried.

[0145] Next, under a nitrogen atmosphere, 1.7 g of N-hydroxynaphthalimide and 2.2 g of 7,7-dimethyl-2-oxabicyclo[2.2.1]heptan-1-yl methanesulfonyl chloride were added to 30 ml of THF in a 100 mL three-neck flask and cooled to -5°C, and then 1.6 g of triethylamine was slowly added dropwise. After reacting for 24 hours, the mixture was filtered at room temperature (25°C) and dried to obtain a solid. The solid was dissolved in ethyl acetate and mixed with a 1% by mass aqueous solution of sodium bicarbonate, and the ethyl acetate layer was separated. After this, the ethyl acetate solvent was completely removed to obtain a compound represented by the following chemical formula 7-1.

[0146] [ka]

[0147] [Production of composition for resist underlayer film] Example 1 Polymer A obtained in Polymerization Example 1 and 1.2 g of the compound represented by Chemical Formula 4-1 obtained in Synthesis Example 6 as a photoacid generator in a mass ratio of 100:50, 0.4 g of PD1174 (crosslinking agent, manufactured by Tokyo Chemical Industry Co., Ltd.), and 0.02 g of pyridinium p-toluenesulfonate (PPTS) were mixed and completely dissolved in propylene glycol monomethyl ether to a solid content concentration of 3 mass %. The mixture was then diluted with an additional solvent to produce a resist underlayer film composition according to Example 1.

[0148] Example 2 A composition for a resist underlayer film was produced in the same manner as in Example 1, except that the compound represented by Chemical Formula 4-2 obtained in Synthesis Example 7 was used instead of the compound represented by Chemical Formula 4-1.

[0149] Example 3 A composition for a resist underlayer film was produced in the same manner as in Example 1, except that the compound represented by Chemical Formula 5-1 obtained in Synthesis Example 8 was used instead of the compound represented by Chemical Formula 4-1.

[0150] Example 4 A composition for a resist underlayer film was produced in the same manner as in Example 1, except that the compound represented by Chemical Formula 6-1 obtained in Synthesis Example 9 was used instead of the compound represented by Chemical Formula 4-1.

[0151] Example 5 A composition for a resist underlayer film was produced in the same manner as in Example 1, except that the compound represented by Chemical Formula 7-1 obtained in Synthesis Example 10 was used instead of the compound represented by Chemical Formula 4-1.

[0152] Example 6 A composition for a resist underlayer film was produced in the same manner as in Example 1, except that Polymer B obtained in Polymerization Example 2 was used instead of Polymer A.

[0153] Comparative Example 1 1.2 g of the polymer A obtained in Polymerization Example 1, 0.4 g of PD1174 (crosslinking agent, manufactured by Tokyo Chemical Industry Co., Ltd.), and 0.02 g of pyridinium p-toluenesulfonate (PPTS) were mixed and completely dissolved in propylene glycol monomethyl ether to a solid content concentration of 3 mass %. The mixture was then diluted with an additional solvent to produce a composition for a resist underlayer film.

[0154] Comparative Example 2 A composition for a resist underlayer film was produced in the same manner as in Comparative Example 1, except that Polymer B was used instead of Polymer A.

[0155] Comparative Example 3 A composition for resist underlayer film was prepared in the same manner as in Example 1, except that a compound represented by the following chemical formula 8 (NDI-105, manufactured by Midori Chemical Industry Co., Ltd.) was used instead of the compound represented by the chemical formula 4-1.

[0156] [ka]

[0157] Comparative Example 4 A composition for resist underlayer film was produced in the same manner as in Example 1, except that a compound represented by the following chemical formula 9 (NDI-109, manufactured by Midori Chemical Industry Co., Ltd.) was used instead of the compound represented by the chemical formula 4-1.

[0158] [ka]

[0159] [Evaluation: Thermogravimetric analysis (TGA) of photoacid generator] The compounds represented by the above chemical formulas 4-1, 4-2, 5-1, 6-1, 7-1, 8, and 9 were each measured for mass loss (%) by maintaining the compound at an isothermal temperature of 205°C for 10 minutes in an air atmosphere using a simultaneous thermogravimetry and differential thermal analyzer, TGA / DSC3+ (manufactured by Mettler Toledo Co., Ltd.). At this time, the mass was measured 3 minutes after the start of the measurement, and compared with the mass before the measurement, and the mass loss (unit: %) is shown in Table 1 below.

[0160] [Table 1]

[0161] [Evaluation: Exposure characteristics evaluation] The compositions produced in Examples 1 to 6 and Comparative Examples 1 to 4 were each applied onto a silicon wafer by spin coating, and then heat-treated on a hot plate at 205°C for 60 seconds to form a resist underlayer film with a thickness of 50 Å. Thereafter, a photoresist solution was applied onto the resist underlayer film by spin coating, and then heat-treated on a hot plate at 110°C for 1 minute to form a photoresist layer. The photoresist layer was exposed to a 200μC / cm exposure using an electron beam exposure device (manufactured by Elionix Co., Ltd.). 2 ~2000μC / cm 2 After exposure in the range of 1:1, the photoresist layer was heat-treated at 150°C for 60 seconds. Next, the photoresist layer was developed with a 2.38 mass% aqueous solution of tetramethylammonium hydroxide (TMAH) and then rinsed with pure water for 15 seconds to form a photoresist pattern with 50 nm lines and spaces (L / S). Next, the optimal exposure dose for the photoresist pattern was evaluated, and the results are shown in Table 2. Here, the exposure dose for developing a 50 nm line and space pattern size at 1:1 was defined as the optimal exposure dose (Eop, μC / cm). 2 ) and the smaller this value, the better the sensitivity. The minimum CD is defined as the smallest size at which the lines of the pattern are barely connected or disintegrated and the pattern is well formed. The smaller the minimum CD value, the better the resolution.

[0162] [Table 2]

[0163] Referring to Table 2 above, it can be seen that the resist underlayer film formed from the composition according to the embodiment has superior fine pattern (50 nmL / S) formability and sensitivity compared to the resist underlayer film formed from the composition according to the comparative example.

[0164] [Evaluation: Line width roughness (LWR) evaluation] The compositions according to Examples 1 to 6 and Comparative Examples 1 to 4 were each applied onto a silicon wafer by spin coating, and then heat-treated on a hot plate at 205°C for 60 seconds to form a resist underlayer film with a thickness of 50 Å. Then, a photoresist solution was applied onto the resist underlayer film by spin coating, and then heat-treated on a hot plate at 110°C for 1 minute to form a photoresist layer. The obtained photoresist layer was exposed to light using an electron beam lithography device (manufactured by Elionix Co., Ltd., acceleration voltage 100 keV) under conditions of a line width of 30 nm and a space width between lines of 30 nm. Next, after heat treatment at 95°C for 60 seconds, the resist was developed with a 2.38 mass% aqueous solution of tetramethylammonium hydroxide (TMAH) for 60 seconds, and rinsed with pure water for 15 seconds to form a resist pattern.

[0165] Line width roughness (LWR) was measured by observing a pattern formed with a width of 30 nm with a scanning electron microscope (length measuring SEM) S-9260 (manufactured by Tachi Hi-Tech Co., Ltd.) and measuring the distance from the reference line where the edge should be within a 2 μm range of the edge in the length direction of the pattern. The results are shown in Table 2 above, and the smaller the value of line width roughness (LWR), the better.

[0166] Referring to Table 2 above, it can be seen that the resist underlayer film obtained from the composition of the example has a smaller LWR value than the resist underlayer film obtained from the composition of the comparative example, and therefore the pattern is more uniform.

[0167] Although specific embodiments of the present invention have been described and illustrated above, the present invention is not limited to the described embodiments, and it is obvious to those skilled in the art that various modifications and variations can be made without departing from the spirit and scope of the present invention. Therefore, such modifications or variations should not be understood separately from the technical spirit or perspective of the present invention, and the modified embodiments should belong to the scope of the claims of the present invention. [Explanation of symbols]

[0168] 100 boards, 102 Thin Films, 104 Resist underlayer film, 106 Photoresist film, 106a non-exposed area, 106b exposed area; 107 Acid (H + ), 108 Photoresist pattern, 110 mask, 112 Organic film pattern, 114 Thin film pattern.

Claims

1. A polymer including at least one of a structural unit represented by the following chemical formula 1 and a structural unit represented by the following chemical formula 2: A photoacid generator that, when subjected to thermogravimetric analysis at 205° C. in an air atmosphere, has a mass loss rate of 0% after 3 minutes from the start of the measurement, and solvent, A composition for a resist underlayer film comprising: 【Chemistry 1】 In the above Chemical Formula 1 and Chemical Formula 2, Each A is independently a heterocyclic group containing a nitrogen atom in the ring, L １ ~L ６ each independently represents a single bond, a substituted or unsubstituted alkylene group having 1 to 10 carbon atoms, a substituted or unsubstituted heteroalkylene group having 1 to 10 carbon atoms, a substituted or unsubstituted cycloalkylene group having 3 to 20 carbon atoms, a substituted or unsubstituted heterocycloalkylene group having 2 to 20 carbon atoms, a substituted or unsubstituted arylene group having 6 to 20 carbon atoms, a substituted or unsubstituted heteroarylene group having 3 to 20 carbon atoms, or a combination thereof; X １ ~X ５ are each independently a single bond, -O-, -S-, -S(=O)-, -S(=O) ２ -, -C(=O)-, -(CO)O-, -O(CO)O-, -NR ａ - (where R ａ is a hydrogen atom, a deuterium atom, or an alkyl group having 1 to 10 carbon atoms), or a combination thereof; Y １ ~Y ３ are each independently a hydroxy group, a substituted or unsubstituted alkyl group having 1 to 10 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 10 carbon atoms, a substituted or unsubstituted alkynyl group having 2 to 10 carbon atoms, a substituted or unsubstituted heteroalkyl group having 1 to 10 carbon atoms, a substituted or unsubstituted heteroalkenyl group having 2 to 10 carbon atoms, a substituted or unsubstituted heteroalkynyl group having 2 to 10 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3 to 20 carbon atoms, a substituted or unsubstituted heterocycloalkyl group having 2 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 20 carbon atoms, a substituted or unsubstituted heteroaryl group having 3 to 20 carbon atoms, or a combination thereof; * indicates a connection point.

2. The composition for a resist underlayer film according to claim 1, wherein A in the chemical formula 1 and the chemical formula 2 is independently at least one selected from the group consisting of heterocyclic groups represented by the following chemical formulas A-1 to A-4: 【Chemistry 2】 In the above Chemical Formulae A-1 to A-4, * indicates a linking point to another atom or group.

3. In Formula 1 and Formula 2, L １ ~L ６ each independently represents a single bond, a substituted or unsubstituted alkylene group having 1 to 10 carbon atoms, a substituted or unsubstituted heteroalkylene group having 1 to 10 carbon atoms, or a combination thereof; In the above formula 1 and formula 2, X １ ~X ５ each independently represents a single bond, —O—, —S—, —C(═O)—, —(CO)O—, —O(CO)O—, or a combination thereof, Y in Formula 1 and Formula 2 １ ~Y ３ are each independently a substituted or unsubstituted alkyl group having 1 to 10 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 10 carbon atoms, a substituted or unsubstituted heteroalkyl group having 1 to 10 carbon atoms, a substituted or unsubstituted heteroalkenyl group having 2 to 10 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3 to 20 carbon atoms, a substituted or unsubstituted heterocycloalkyl group having 2 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 20 carbon atoms, or a combination thereof.

4. 2. The resist underlayer film composition according to claim 1, wherein the photoacid generator is a compound represented by the following chemical formula 3, or comprises an imide derivative in which a nitrogen atom is substituted with a sulfonic acid (salt) group, or a cyanurate derivative in which a nitrogen atom is substituted with a sulfonic acid (salt) group: 【Chemistry 3】 In the above formula 3, R ２ ~R ４ are each independently a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 20 carbon atoms, a substituted or unsubstituted alkynyl group having 2 to 20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, or a combination thereof; Z － is a monovalent anion.

5. R in Formula 3 ２ ~R ４ are each independently an alkyl group having 1 to 20 carbon atoms substituted with at least one halogen atom, an aryl group having 6 to 30 carbon atoms substituted with at least one halogen atom, or a combination thereof.

6. The photoacid generator is at least one selected from the group consisting of compounds represented by the following chemical formulas 4 to 7: 【Chemistry 4】 In the above Chemical Formula 4, R ２１ , R ３１ , and R ４１ are each independently a halogen atom; n21, n31, and n41 each independently represent an integer from 0 to 5; In this case, at least one of n21, n31, and n41 is 1 or more; 【Chemistry 5】 In Chemical Formula 5 to Chemical Formula 7, R ５１ , R ６１ , R ６２ , and R ７１ each independently represents a deuterium atom, a hydroxyl group, a halogen atom, a nitro group, a cyano group, -COOH, a substituted or unsubstituted alkoxy group having 1 to 20 carbon atoms, a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 20 carbon atoms, a substituted or unsubstituted alkynyl group having 2 to 20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3 to 20 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, or a combination thereof; R ５２ , R ６３ , and R ７２ each independently represents a substituted or unsubstituted alkyl group having 1 to 20 carbon atoms, a substituted or unsubstituted alkenyl group having 2 to 20 carbon atoms, a substituted or unsubstituted alkynyl group having 2 to 20 carbon atoms, a substituted or unsubstituted cycloalkyl group having 3 to 20 carbon atoms, a substituted or unsubstituted bicycloalkyl group having 5 to 30 carbon atoms, a substituted or unsubstituted aryl group having 6 to 30 carbon atoms, or a combination thereof; n51 is an integer from 0 to 2; n71 is an integer from 0 to 6.

7. The composition for a resist underlayer film according to claim 1, wherein the structural unit represented by Chemical Formula 1 is at least one of a structural unit represented by Chemical Formula 1-1 and a structural unit represented by Chemical Formula 1-2 below, and the structural unit represented by Chemical Formula 2 is at least one selected from the group consisting of structural units represented by Chemical Formulas 2-1 to 2-3 below: 【Chemistry 6】 【Chemistry 7】 In the above Chemical Formulae 1-1 to 1-2 and 2-1 to 2-3, * indicates a linking point.

8. The composition for a resist underlayer film according to claim 1, wherein the photoacid generator is at least one selected from the group consisting of a compound represented by the following chemical formula 4-1, a compound represented by the following chemical formula 4-2, a compound represented by the following chemical formula 5-1, a compound represented by the following chemical formula 6-1, and a compound represented by the following chemical formula 7-1. 【Chemistry 8】

9. 2. The resist underlayer film composition according to claim 1, wherein the weight average molecular weight of the polymer is 1,000 g / mol to 300,000 g / mol.

10. 2. The resist underlayer film composition according to claim 1, wherein the photoacid generator is contained in an amount of 10 parts by mass to 100 parts by mass based on 100 parts by mass of the polymer.

11. 2. The composition for a resist underlayer film according to claim 1, wherein the polymer is contained in an amount of 0.1% by mass to 50% by mass based on the total mass of the composition for a resist underlayer film.

12. The composition for a resist underlayer film according to claim 1, wherein the photoacid generator is contained in an amount of 0.01% by mass to 30% by mass based on the total mass of the composition for a resist underlayer film.

13. 2. The resist underlayer film composition according to claim 1, further comprising at least one polymer selected from the group consisting of acrylic resins, epoxy resins, novolac resins, glycoluril resins, and melamine resins.

14. The resist underlayer film composition according to claim 1 , further comprising an additive selected from the group consisting of a surfactant, a thermal acid generator, a plasticizer, and combinations thereof.

15. forming a film to be etched on a substrate; A step of forming a resist underlayer film by applying the composition for a resist underlayer film according to any one of claims 1 to 14 onto the film to be etched; forming a photoresist pattern on the resist underlayer film; sequentially etching the resist underlayer film and the film to be etched using the photoresist pattern as an etching mask; A pattern forming method comprising: