Naturally degradable microcapsules and their manufacturing method

Abstract

The present invention relates to a method for producing microcapsules. Microcapsules produced by the method of the present invention can exhibit high versatility, spontaneous degradability, and long-term stability, and can stably carry active substances within the capsules even in the presence of surfactants.

Description

[Technical field]

[0001] The present invention relates to a method for producing naturally degradable microcapsules and to microcapsules produced by said method. [Background technology]

[0002] It uses an encapsulation method to effectively deliver active ingredients, and even with a small dose, it can deliver the active ingredients accurately, reducing problems related to side effects, maintaining the stability of the active ingredients, and costs. Therefore, it is used in various forms and for various purposes in industrial fields, such as targeted delivery of drugs in the medical / pharmacy field, maintaining the stability of fragrances and releasing the fragrance at the time desired by the user in sanitary products, maintaining the stability of active substances from external stimuli such as light and heat in the cosmetics field and delivering them to the skin, as an insecticide in the agricultural field, and improving the stability and absorption efficiency of nutritional ingredients in the food field.

[0003] International organizations point out that microcapsules are one of the causes of microplastic pollution (materials made by humans with a diameter of 5 mm or less that do not decompose and accumulate when discharged into the environment, causing serious environmental pollution). However, capsules made from inorganic particles to avoid the category of microplastics are vulnerable to tension and impacts that occur during drying and are easily broken down, and capsules made from natural polymers have the problem that the active ingredients inside the capsules are eluted due to the inherent microporosity of the material, making it difficult to maintain the stability of the capsules. If cross-linking is used to reduce microporosity and increase stability, degradability is reduced. In addition, if a material with an ester bond introduced to easily decompose is used, there is the problem that it cannot withstand the harsh conditions of the dosage form (pH changes, temperature changes) and decomposes before use, but there is no known or no solution to this problem at present.

[0004] In fact, in the natural environment, decomposition of substances occurs through microorganisms, light, hydrolysis, etc., and the decomposition method by microorganisms and light is specified for the decomposition of substances specified in the international standard measurement method. More specifically, according to the OECD 301D test method, if the decomposition by microorganisms in a dark room at room temperature for 28 days is 60% or more, it is classified as a "substance that is immediately decomposed," if it is 20-60%, it is a "substance that is biodegradable," and if it is 20% or less, it is a "substance that is not decomposable." According to the OECD 316 test method, a method for measuring the degree of decomposition that occurs when light is irradiated using a xenon lamp for 12 hours a day for a total of 30 days under aqueous conditions is presented. In the actual natural environment, when hydrocarbon substances are decomposed into water and carbon dioxide, there are cases where a photocatalyst is introduced to promote decomposition because light alone does not have enough energy to induce chemical decomposition, but there is a limit in that it is difficult to completely decompose substances whose main components are hydrocarbon chains, such as polyethylene, polypropylene, and polystyrene.

[0005] On the other hand, active ingredients are usually monomolecular substances with high permeability or high oxidizing properties, and therefore there is a problem of oxidation caused by the penetration of oxidizing substances such as oxygen, active oxygen, and free radicals from the external environment. Therefore, there is growing interest in methods to improve the isolation of the capsule membrane to maintain capsule stability. Materials used for encapsulation to effectively support active ingredients are used in a wide spectrum, from organic polymers to inorganic materials, and methods such as polymer interfacial polymerization, layer-by-layer through ionic bonding, and solidification through solubility changes due to pH have been proposed to reduce the permeability of the capsule membrane. However, even if the capsule membrane is strengthened by these methods, there is a limit in that the active ingredient is eluted in the harsh environment in the presence of surfactants, ionic components, and solvents in the dosage form.

[0006] For example, capsules made by interfacial polymerization of polyurea have excellent release performance of active ingredients, but it has been reported that the active ingredients are dissolved by surfactants, resulting in stability problems. As another example, US 9,944,886 B2 and [J. Hitchcock et., Long-Term Retention of Small, Volatile Molecular Species within Metallic Microcapsules, ACS Appl.Mater.Interfaces 2015, 7, 27, 14808-14815] report that capsules made of polymethacrylate, a highly hydrophobic material, are dissolved in organic solvents within a few minutes. To solve this problem, a method was used to improve capsule stability by coating the capsules with metals that have an atomic distance of several Å and prevent active ingredients from escaping, but the materials that can be used are limited to gold and silver, limiting commercialization. In another example, in US Pat. No. 9,943,487 B2, dopamine is coated on the outer wall of the capsule to increase its stability against heat and organic solvents, but the manufacturing method is difficult, limiting its commercialization.

[0007] Therefore, there is a need to develop a capsule material that will not decompose and pollute the environment when released into the environment, that is highly versatile and stable, that is easy to manufacture, is highly economical, and allows the activity of the active ingredient to be easily adjusted. [Prior art documents] [Patent documents]

[0008] [Patent Document 1] US 9,944,886 B2 [Patent Document 2] US 9,943,487 B2 [Non-patent literature]

[0009] [Non-Patent Document 1] J. Hitchcock et., Long-Term Retention of Small, Volatile Molecular Species within Metallic Microcapsules, ACS Appl.Mater.Interfaces 2015, 7, 27, 14808-14815 Summary of the Invention [Problem to be solved by the invention]

[0010] The present inventors conducted research to develop microcapsules that maintain long-term stability by preventing the leaching of the active substance carried therein and have excellent biodegradability. As a result, they confirmed that by preparing a Pickering emulsion using a first encapsulation component, a second encapsulation component, a first capsule strengthening component and a second capsule strengthening component and encapsulating the Pickering emulsion, it is possible to produce microcapsules that not only have high versatility and excellent biodegradability and stability, but also allow the activity of the active substance to be easily adjusted, thereby completing the present invention.

[0011] Therefore, an object of the present invention is to provide a method for producing microcapsules having high versatility, natural degradability and stability, and microcapsules produced thereby. [Means for solving the problem]

[0012] As a means for solving the above problems, the present invention provides preparing a Pickering emulsion by mixing a continuous phase 1 containing inorganic particles and a first encapsulated component with a dispersed phase 1 containing a second encapsulated component and a first capsule-strengthening component; and A method for producing microcapsules, comprising the steps of mixing the Pickering emulsion with a continuous phase 2 containing a second capsule strengthening component and encapsulating the mixture, The first encapsulation component and the second capsule strengthening component may each or all contain two or more amine or hydroxy groups; The second encapsulating component and the first encapsulation reinforcing component may each contain two or more functional groups selected from the group consisting of an amine group, an isocyanate group, an acyl halide group, a chloroformate group, and an acrylate group.

[0013] Also, the present invention provides microcapsules produced by the above-mentioned production method.

[0014] In addition, in the present invention, A microcapsule can be provided that includes an inorganic particle, a first encapsulated component, a second encapsulated component, a first capsule strengthening component, and a second capsule strengthening component.

[0015] The first encapsulation component and the second encapsulation reinforcement component may have one or more identical functional groups, which may in particular be amine groups.The second encapsulation component and the first encapsulation reinforcement component may have one or more identical functional groups, which may in particular be isocyanate groups.

[0016] The configuration of the present invention will be described in detail below.

[0017] The method for producing the microcapsules of the present invention comprises the steps of: A step of preparing a Pickering emulsion by mixing a continuous phase 1 containing inorganic particles and a first encapsulated component with a dispersed phase 1 containing a second encapsulated component and a first capsule-strengthening component; and The method includes the step of encapsulating the Pickering emulsion by mixing it with a continuous phase 2 containing a second capsule enhancing ingredient.

[0018] More specifically, the present invention involves preparing a continuous phase 1 that includes inorganic particles and a first encapsulated component.

[0019] The solvent for the continuous phase 1 may include any solvent commonly used in the art.

[0020] In one embodiment, the continuous phase 1 solvent may be distilled water.

[0021] In the present invention, the inorganic particles are added for the purpose of forming a Pickering emulsion, which is the basic structure of microcapsules, and may be metal, nonmetal, or a mixture thereof, but are not limited thereto. In the present invention, the inorganic particles are not limited in type as long as they are inorganic particles that are not dissolved in the aqueous phase and can be adsorbed to the dispersed phase. For example, the inorganic particles may be selected from metals such as titanium, vanadium, manganese, iron, cobalt, nickel, copper, niobium, molybdenum, ruthenium, rhodium, palladium, silver, zinc, hafnium, tantalum, tungsten, iridium, platinum, gold, indium, tin, calcium, aluminum, or magnesium; nonmetals such as silica in the form of phyllosilicate, inosilicate, sorosilicate, or tectosilicate; or mixtures thereof.

[0022] In one embodiment, the inorganic particles may be silica.

[0023] The inorganic particles may have a diameter of 1 to 900 nm, for example, a diameter of 1.5 to 750 nm, or a diameter of 2 to 500 nm.

[0024] In the present invention, the content of the inorganic particles may be 0.001 to 5 parts by weight, for example, 0.005 to 4 parts by weight, 0.01 to 3 parts by weight, 0.1 to 2 parts by weight, or 0.5 to 1.5 parts by weight, based on the weight of the entire composition for preparing microcapsules.

[0025] In the present invention, the first encapsulation component means a biodegradable polymer, which may be included in order to be dissolved in the continuous phase and undergo an interfacial polymerization reaction with the second encapsulation component present in the dispersed phase described below to form the outer wall of the capsule and to be easily degraded.

[0026] In the present invention, the first encapsulation component is not particularly limited as long as it is a biodegradable polymer having an amine group and / or a hydroxyl group in the molecule. The biodegradable polymer may be a natural component or a synthetic component, and may be a monomer, an oligomer, or a polymer. The natural component may include polysaccharides such as cellulose, hyaluronic acid, xanthan gum, chitosan, or heparin; partially modified polysaccharides such as hydroxyethyl cellulose or hydroxypropyl cellulose; nucleic acids such as DNA or RNA; proteins such as collagen, gelatin, or silk fibroin; or polypeptides such as polylysine, polyglutamic acid, or polyarginine. The synthetic component may include components having a hydroxyl group, a carboxyl group, or an amine group, such as polyester, polyphosphazene, polyamino acid, or polyorthoester.

[0027] In addition, the first encapsulation component may include not only a component containing an amine group and / or a hydroxyl group, but also a component that has been surface-modified to contain the functional group. That is, in the present invention, the first encapsulation component may include all of a component having two or more amine groups, two or more hydroxyl groups, or two or more amine groups and two or more hydroxyl groups.

[0028] The first encapsulation component may have a molecular weight of 200 Da to 1,000,000 Da, for example, a molecular weight of 500 Da to 500,000 Da, or a molecular weight of 1,000 Da to 100,000 Da. The first encapsulation component may be included in an amount of 0.01 to 20 parts by weight, for example, 0.05 to 15 parts by weight, 0.1 to 10 parts by weight, 0.5 to 5 parts by weight, 0.01 to 10 parts by weight, 0.05 to 5 parts by weight, 0.1 to 1 part by weight, or 0.25 to 0.75 parts by weight, based on the weight of the entire composition for producing microcapsules. In the present invention, if the molecular weight of the first encapsulation component is less than 200 Da or the content is less than 0.01 parts by weight, a problem of no crosslinking may occur due to a small number of functional groups that can participate in the reaction for forming the outer wall of the microcapsule. If the molecular weight of the first encapsulation component exceeds 1,000,000 Da or the content exceeds 20 parts by weight, a problem of a hydrogel being formed instead of the outer wall of the microcapsule may occur due to an increase in viscosity.

[0029] In one embodiment, the first encapsulation component may be chitosan.

[0030] The continuous phase 1 containing the inorganic particles and the first encapsulated component can be mixed with the dispersed phase 1 containing the second encapsulated component and the first capsule reinforcing component to produce a Pickering emulsion.

[0031] Thus, the present invention involves preparing a dispersed phase 1 that includes a second encapsulated component and a first capsule-strengthening component.

[0032] The solvent of the dispersed phase 1 may be selected from the group consisting of a hydrocarbon solvent with a linear or nonlinear structure, such as pentane, hexane, cyclohexane, heptane, octane, isododecane, or dodecane; a solvent containing an ether group, such as ethyl ether, butyl ether, or methyl butyl ether; a solvent containing an ester group, such as ethyl acetate, butyl acetate, or ethyl butyrate; a solvent containing a ketone group, such as methyl ethyl ketone; a solvent containing benzene, such as benzene, toluene, or xylene; a haloalkane solvent, such as dichloromethane, dichloroethane, chloroform, or carbon tetrachloride; or a silicone solvent, such as dimethicone or cyclomethicone. The solvent may be applied to the continuous phase as necessary.

[0033] In addition, the solvent may be selected from active substances to be supported in the microcapsules. In the present invention, the active substance refers to a substance that can be supported in the microcapsules and maintain its activity, and that exhibits its activity when the outer wall of the microcapsule is destroyed. When the active substance is liquid at room temperature, it may be included as a solvent of the dispersed phase. The active substance may be, but is not limited to, an aromatic oil, an ultraviolet blocking agent, a dye, a catalyst, an antioxidant, or a drug.

[0034] The continuous phase 1 can be mixed with the dispersed phase 1 containing the second encapsulation component and the first capsule strengthening component to prepare a Pickering emulsion.

[0035] The second encapsulation component and the first capsule strengthening component are materials that react with the first encapsulation component dissolved in the continuous phase to form the outer wall of the capsule and reduce the substance permeability to the capsule, and may be selected from materials that dissolve well in the dispersed phase. The second encapsulation component means a component that reacts with the first encapsulation component to form an interfacially polymerizable polymer, such as polyurea, polyurethane, polyacylamine, polyoxime, polycarbamate, polyester, polyamine ester, or polyamide, to form a capsule structure. The second encapsulation component may be a monomer, oligomer, or polymer.

[0036] The second encapsulation component may be a compound represented by Formula 1:

[0037] [ka]

[0038] In the above Chemical Formula 1, R1 is an acrylate group or an alkylene group having 1 to 50 carbon atoms substituted or unsubstituted with a heteroatom; a cyclic hydrocarbon having 3 to 60 carbon atoms; or a compound containing an alkylene group having 1 to 50 carbon atoms and a cyclic hydrocarbon having 3 to 60 carbon atoms; X1 to X4 are each independently selected from the group consisting of hydrogen, an amine group, an acyl halide group, an isocyanate group, a chloroformate group, and an acrylate group; and n is an integer of 1 or more.

[0039] In the above Chemical Formula 1, at least two of X1 to X4 have an amine group, an acyl halide group, an isocyanate group, a chloroformate group, or an acrylate group, and n may be an integer of 1 to 3.

[0040] In one embodiment, the second encapsulating component may be a polyisocyanate.

[0041] The second encapsulation component may be included in an amount of 0.001 to 10 parts by weight, for example, 0.005 to 8 parts by weight, 0.01 to 5 parts by weight, 0.05 to 1 parts by weight, 0.1 to 0.5 parts by weight, 0.001 to 0.5 parts by weight, or 0.125 to 0.375 parts by weight, based on the weight of the entire composition for preparing microcapsules. If the content of the second encapsulation component is less than 0.001 parts by weight, a problem may occur in which the outer wall of the capsule is formed too thin to be maintained even if an encapsulation reaction occurs, and if the content exceeds 10 parts by weight, a problem may occur in which the viscosity increases and capsules are not formed.

[0042] The first capsule strengthening component is a material capable of increasing the density of the outer wall of the microcapsule, and may include a material having a ring structure or an inorganic material. The first capsule strengthening component has low compatibility with the continuous phase and the dispersed phase, and may be included to prevent the active substance held inside the capsule from dissolving out when it is formed into the outer wall of the capsule, or to delay the dissolution rate.

[0043] The first capsule strengthening component may include a component having a ring structure that can react with the first encapsulation component and / or the second capsule strengthening component to form an interfacially polymerizable polymer, such as polyurea, polyurethane, polyacylamine, polyoxime, polycarbamate, polyester, polyamine ester, or polyamide, to create a capsule structure.

[0044] The first capsule reinforcing component may be one or more compounds selected from the group consisting of a monomer represented by the following formula 2, methylene diphenyl diisocyanate, naphthalene diisocyanate, and isophorone diisocyanate; an oligomer thereof; or a polymer thereof:

[0045] [ka]

[0046] In the formula 2, R2 to R7 may each independently include hydrogen; an alkyl group having 1 to 5 carbon atoms; an alkenyl group having 2 to 5 carbon atoms; an alkyl isocyanate group having 1 to 5 carbon atoms; an isocyanate group; an alkyl acyl halide group having 1 to 5 carbon atoms; an acyl halide group; an alkyl chloroformate group having 1 to 5 carbon atoms; a chloroformate group; an alkyl acrylate group having 1 to 5 carbon atoms; or an acrylate group, and at least one of R2 to R7 in the formula 2 may include one of an isocyanate group, an acyl halide group, a chloroformate group, or an acrylate group. In the formula 2, the monomer may be a polymer in which 1 to 13 monomers are polymerized. If the monomer is 13 or more, the stiffness of the material increases, so that the capsule may easily break during the production process, or the capsule may not be able to maintain its shape due to tension generated during drying.

[0047] In one embodiment, the first capsule reinforcing component may be an isocyanate-containing component such as methyldiphenyldiisocyanate, naphthalene diisocyanate, isophorone diisocyanate, or xylene diisocyanate.

[0048] The first capsule strengthening component is capable of reacting with the amine group or hydroxy group of the first encapsulation component together with the second encapsulation component, and may be selected to have different functional groups depending on whether or not the first encapsulation component contains an amine group or a hydroxy group in its molecule.

[0049] In one embodiment, when the first encapsulation component has two or more amine groups, the first capsule reinforcement component and / or the second encapsulation component may each have two or more acrylate groups or isocyanate groups. In the microcapsules according to the present invention, when the first encapsulation component has an amine group and the first capsule reinforcement component and / or the second encapsulation component have an acrylate group, a poly-β-aminoester microcapsule can be formed; when the first capsule reinforcement component and / or the second encapsulation component have an isocyanate group, a polyurea microcapsule can be formed.

[0050] In the present invention, the component having an isocyanate group is methylene diisocyanate, 1,4-phenylene diisocyanate, tolylene-2,4-diisocyanate, 1-chloromethyl-2,4-diisocyanatobenzene, 4-chloro-6-methyl-1,3-phenylene diisocyanate, 1,3-bis(1-isocyanato-1-methylethyl)benzene, 3,3'-dimethyl-4,4'-biphenylene diisocyanate, diisocyanate), 3,3'-dichloro-4,4'-diisocyanato-1,1'-biphenyl, 4,4'-oxybis(phenylisocyanate), 4,4'-methylenebis(phenylisocyanate), 4,4'-methylenebis(2,6-diethylphenyl isocyanate), isophorone diisocyanate, trans-1,4-cyclohexylene diisocyanate diisocyanate), 1,3-bis(isocyanatomethyl)cyclohexane, 4,4'-methylenebis(cyclohexylisocyanate)(4,The isocyanate may be selected from the group consisting of 4'-Methylenebis(cyclohexyl isocyanate), diisocyanatobutane, hexamethylenediisocyanate, diisocyanatooctane, diisocyanatododecane, and 1,6-diisocyanato-2,2,4-trimethylhexane, but is not limited thereto.

[0051] In the present invention, the component having an acrylate group is, for example, ethylene glycol diacrylate, di(ethylene glycol) diacrylate, tri(ethylene glycol) diacrylate, tetra(ethylene glycol) diacrylate, poly(ethylene glycol) diacrylate, propylene glycol diacrylate, di(propylene glycol) diacrylate, tri(propylene glycol) diacrylate, tetra(propylene glycol) diacrylate, poly(propylene glycol) diacrylate, butanediol diacrylate, hexane ... diacrylate, Hexanediol ethoxylate diacrylate, Neopentyl glycol propoxylate(1 PO / OH) diacrylate, Trimethylolpropane ethoxylate(1 EO / OH) methyl ether diacrylate, Neopentyl glycol diacrylate, Pentaerythritol triacrylateThe alkyl acrylate may be selected from the group consisting of, but is not limited to, trimethylolpropane triacrylate, trimethylolpropane propoxylate triacrylate, tris[2-(acryloyloxy)ethyl]isocyanurate, trimethylolpropane ethoxylate triacrylate, di(trimethylolpropane)tetraacrylate, pentaerythritol tetraacrylate, and hydroxypivalyl hydroxypivalate bis[6-(acryloyloxy)hexanoate].

[0052] In another embodiment, when the first encapsulation component has two or more hydroxy groups, the first capsule reinforcement component and / or the second encapsulation component may each have two or more isocyanate groups, acyl halide groups, chloroformate groups or acrylate groups. When the first encapsulation component has hydroxy groups and the first capsule reinforcement component and / or the second encapsulation component have isocyanate groups, polyurethane microcapsules can be formed; when the first capsule reinforcement component and / or the second encapsulation component have acyl halide groups, chloroformate groups or acrylate groups, polyester microcapsules can be formed.

[0053] In the present invention, the component having a chloroformate group may be selected from the group consisting of ethylene bis(chloroformate), diglycolyl chloride, oxydiethylene bis(chloroformate), tri(ethylene glycol) bis(chloroformate), 1,4-phenylene bis(chloroformate), Bisphenol A bis(chloroformate), and Bisphenol Z bis(chloroformate), but is not limited thereto.

[0054] In the present invention, the component having an acyl halide group may be selected from the group consisting of malonyl chloride, succinyl chloride, glutaryl chloride, adipoyl chloride, pimeloyl chloride, suberoyl chloride, sebacoyl chloride, azelaic acid dichloride, and dodecanedioyl dichloride, but is not limited thereto.

[0055] The first capsule strengthening ingredient may be included in an amount of 0.001 to 10 parts by weight, for example, 0.005 to 8 parts by weight, 0.01 to 5 parts by weight, 0.05 to 1 parts by weight, 0.1 to 0.5 parts by weight, or 0.125 to 0.375 parts by weight, based on the weight of the entire composition for preparing microcapsules. If the content of the first capsule strengthening ingredient is less than 0.001 parts by weight, a problem may occur in which the outer wall of the capsule is formed too thin to be maintained even if an encapsulation reaction occurs, and if it exceeds 10 parts by weight, a problem may occur in which the viscosity increases and capsules are not formed.

[0056] In the present invention, the step of mixing the continuous phase 1 and the dispersed phase 1 to form a Pickering emulsion may be to stir the continuous phase 1 containing inorganic particles and a first encapsulation component, and the dispersed phase 1 containing a second encapsulation component and a first capsule reinforcing component. At this time, the stirring conditions for the components to react may be a stirring speed of 10 to 16,000 rpm, for example, 50 to 13,000 rpm, 100 to 10,000 rpm, at room temperature, for example, 20 to 30° C. The encapsulation reaction that is carried out thereafter forms a capsule membrane by reacting a reactive polymer at the interface between the dispersed phase and the continuous phase, which are not mixed with each other, so that the capsule size can be controlled by forming a Pickering emulsion before the encapsulation reaction occurs.

[0057] In the present invention, "Pickering emulsion" refers to an emulsion form in which the interface is stabilized by solid particles. Pickering emulsion has the advantage of being less hazardous to the environment because it can be made without using an emulsifier. However, in order to apply Pickering emulsion to products, there are problems in that the stability problem due to shear stress in the reactive group and the long-term stability problem must be solved.

[0058] The present invention also includes a step of encapsulating the Pickering emulsion by mixing it with a continuous phase 2 containing a second capsule enhancing ingredient.

[0059] The solvent for the continuous phase 2, like the solvent for the continuous phase 1, may include any solvent commonly used in the art.

[0060] In the present invention, the second capsule strengthening component may be one or more compounds selected from the group consisting of a monomer represented by the following formula 3, melamine, and benzidine disulfonic acid; an oligomer thereof; or a polymer thereof:

[0061] [ka]

[0062] In the above formula 3, R 13 may each independently include hydrogen; an amine group; a hydroxy group; an alkyl group having 1 to 5 carbon atoms; an alkylamine group having 1 to 5 carbon atoms; a hydroxyalkyl group having 1 to 5 carbon atoms; or an alkenyl group having 2 to 5 carbon atoms, and the above Chemical Formula 3 includes R to R 13 Any one or more of the above may be a compound that includes one of an amine group or a hydroxy group.

[0063] In one embodiment, the second capsule strengthening ingredient may be phenylenediamine, aminobenzylamine, or benzidine disulfonic acid.

[0064] In the above step, since the second capsule strengthening ingredient is highly reactive, it must be uniformly coated on the capsule wall to form a stable microcapsule, and therefore the second capsule strengthening ingredient may be added after the Pickering emulsion is prepared.

[0065] The second capsule strengthening ingredient may be 0.001 to 10 parts by weight, for example, 0.005 to 8 parts by weight, 0.01 to 5 parts by weight, 0.05 to 3 parts by weight, 0.1 to 1 part by weight, or 0.5 to 0.75 parts by weight, based on the weight of the entire composition for preparing microcapsules. If the content of the second capsule strengthening ingredient is less than 0.001 parts by weight, a problem may occur in which the outer wall of the capsule is formed too thin to be maintained even if an encapsulation reaction occurs, and if it exceeds 10 parts by weight, a problem may occur in which the viscosity increases and capsules are not formed.

[0066] In the present invention, the first encapsulated component and the second encapsulated component may be contained in a weight ratio of 1:0.1 to 100, for example, a weight ratio of 1:0.1 to 50, a weight ratio of 1:0.1 to 25, a weight ratio of 1:0.1 to 10, a weight ratio of 1:0.1 to 1, a weight ratio of 1:0.25 to 1, a weight ratio of 0.3 to 0.8, or a weight ratio of 0.4 to 0.6, and the first encapsulated component and the first capsule strengthening component may be contained in a weight ratio of 1:0.1 to 1, for example, a weight ratio of 1:0.25 to 1, a weight ratio of 0.3 to 0.8, or a weight ratio of 0.4 to 0.6. In addition, the first encapsulated component, the second encapsulated component and the first capsule strengthening component may be contained in a weight ratio of 1:0.1-100:0.1-1, for example, a weight ratio of 1:0.1-50:0.1-1, a weight ratio of 1:0.1-25:0.1-1, a weight ratio of 1:0.1-10:0.1-1, a weight ratio of 1:0.1-1:0.1-1, a weight ratio of 1:0.25-1:0.25-1, a weight ratio of 1:0.3-0.8:0.3-0.8, or a weight ratio of 1:0.4-0.6:0.4-0.6.

[0067] In addition, the present invention may further include a capsule-strengthening inorganic precursor together with the second capsule-strengthening component in the above step. The capsule-strengthening inorganic precursor may be applied to both the inside and outside of the microcapsules, and may be included to form a membrane separate from the capsule wall to seal the active substance inside the capsule so that it does not dissolve or to delay the dissolution rate. It may also play a role in controlling the breakability of the capsule to help release the active substance at the appropriate time.

[0068] The capsule-reinforcing inorganic precursor may be a compound represented by the following formula 4:

[0069] [ka]

[0070] In the above formula 4, R 14 ~R 17 may each independently be hydrogen; an alkoxy group having 1 to 5 carbon atoms; an alkyl group having 1 to 5 carbon atoms; or a hydrocarbon compound having 1 to 5 carbon atoms containing one or more functional groups selected from the group consisting of an amine group, a thiol group, a hydroxyl group, a carbonyl group, a carboxy group, and an ether group.

[0071] The capsule reinforcing inorganic precursor may be selected from the group consisting of, but is not limited to, tetramethyl orthosilicate, tetraethyl orthosilicate, tetrapropyl orthosilicate, tetrabutyl orthosilicate, trimethoxysilane, methyltrimethoxysilane, ethyltrimethoxysilane, propyltriethoxysilane, methylpropylmethoxysilane, methylpropyltriethoxysilane, aminopropyltrimethoxysilane, and mercaptopropyltrimethoxysilane.

[0072] In one embodiment, the capsule reinforcing inorganic precursor may be tetraethylorthosilicate, methyltrimethoxysilane, or aminopropyltrimethylethoxysilane.

[0073] The capsule-reinforcing inorganic precursor may be included in an amount of 0.01 to 10 parts by weight, for example, 0.005 to 8 parts by weight, or 0.01 to 5 parts by weight, based on 100 parts by weight of the total microcapsules. If the content of the capsule-reinforcing inorganic precursor is less than 0.001 parts by weight, the capsules may not be provided with excellent stability, and if it exceeds 10 parts by weight, the inorganic capsules formed may easily break.

[0074] The encapsulation reaction may occur due to contact between reactive polymers. In order to control the reaction rate, the reaction may be carried out at a temperature of 0 to 100° C., for example, at a temperature of 10 to 90° C., for 1 to 48 hours, for example, 2 to 24 hours. The stirring condition may be 10 to 6,000 rpm, for example, 50 to 5,000 rpm, or 100 to 4,000 rpm.

[0075] In the following examples, it was confirmed that a first encapsulation component and a second capsule reinforcement component were used in combination, and that microcapsules prepared by using the second encapsulation component and the first capsule reinforcement component in combination exhibited excellent stability and biodegradability. In particular, when the first encapsulation component and the second capsule reinforcement component were each a compound containing an amine group, and the second encapsulation component and the first capsule reinforcement component were each a compound containing an isocyanate group, it was confirmed that the microcapsules prepared by using the combination of the above components had the most excellent stability and biodegradability.

[0076] In the present invention, the method for producing the microcapsules may further include a step of adsorbing natural decomposition promoting particles to the microcapsules. The natural decomposition promoting particles may be selected from the group consisting of titanium oxide, zinc oxide, zirconium oxide, tungsten oxide, platinum, platinum oxide, and gold chloride, but are not limited thereto. The natural decomposition promoting particles may be included in the first solution (continuous phase). The natural decomposition promoting particles may have a diameter of 1 to 900 nm, for example, a diameter of 1.5 to 750 nm, or a diameter of 2 to 500 nm. If the size of the natural decomposition promoting particles is smaller than 1 nm, a problem may occur in that the natural decomposition promoting effect is difficult to be exhibited.

[0077] The natural decomposition-promoting particles may be biodegradation / or photodecomposition-promoting particles, and preferably photodecomposition-promoting particles.

[0078] The natural decomposition promoting particles may be contained at a concentration of 0.1 to 10,000 ppm, for example, 1 to 8,000 ppm, or 2 to 5,000 ppm. If the concentration of the natural decomposition promoting particles is lower than 0.1 ppm, the decomposition promoting effect is not exhibited, and if it is higher than 10,000 ppm, the particles may interfere with light transmission, not exhibit the decomposition promoting effect, and affect the viscosity, resulting in a problem that the encapsulation reaction does not occur.

[0079] In the present invention, the method for producing microcapsules may further include a step of adding a dispersion stabilizer after the encapsulation reaction. The dispersion stabilizer may be added to enhance the dispersibility of the microcapsules produced after the reaction. The dispersion stabilizer may be selected from the group consisting of, but is not limited to, gum arabic, polysaccharides, pectin, alginate, arabinogalactan, carrageenan, gellan gum, xanthan gum, guar gum, acrylate / acrylic polymers, starch, water-swellable clay, acrylate / aminoacrylate copolymers or mixtures thereof, maltodextrin, alginate esters, gelatin, protein hydrolysates or their quaternized forms, synthetic polymers or copolymers such as poly(vinylpyrrolidone-co-vinyl acetate), poly(vinyl alcohol-co-vinyl acetate), poly(maleic acid), poly(alkylene oxide), poly(vinyl methyl ether), poly(vinyl ether-co-maleic anhydride), poly(ethyleneimine), poly((meth)acrylamide), poly(alkylene oxide-co-dimethylsiloxane), and poly(aminodimethylsiloxane).

[0080] In addition, the method for preparing the microcapsules may further include a concentration and / or drying process, if necessary, and may further include a step of adjusting the pH using an acid or a base.

[0081] The method for producing microcapsules according to the present invention is shown diagrammatically in FIG.

[0082] The present invention also provides a microcapsule produced by the above-mentioned production method, i.e., a microcapsule comprising a first encapsulated component, a second encapsulated component, a first capsule reinforcing component, a second capsule reinforcing component, and inorganic particles.

[0083] In the present invention, the "microcapsule" means a capsule having a diameter in the range of 1 to 1000 μm. In the present invention, the microcapsule may have a diameter of 0.1 to 100 μm, for example, a diameter of 1 to 80 μm, or a diameter of 2 to 50 μm. The outer wall thickness of the microcapsule may be 0.03 to 10 μm.

[0084] If the diameter of the microcapsules is less than 0.1 μm, the capsules will not break, making it difficult to realize the effect of the capsules to release the active ingredients. If the diameter is more than 100 μm, the capsules may easily break or cause a foreign body sensation due to shear stress generated during the manufacturing process of the product.

[0085] The microcapsules manufactured by the manufacturing method of the present invention may have excellent stability and biodegradability. The biodegradability means a property of being naturally decomposed by microorganisms, light, etc. without a separate process or treatment. That is, the biodegradable microcapsules of the present invention may include biodegradable and photodegradable microcapsules. Therefore, the present invention can provide biodegradable microcapsules and / or photodegradable microcapsules. In the present invention, "stability" means the ability to delay or completely prevent the phenomenon in which an active substance, which is usually a monomolecular substance and has high permeability, spontaneously or involuntarily leaks from one isolated space to another space, more specifically, from the inside of the capsule to the external environment, and on the other hand, it can also include the ability to delay or completely prevent the phenomenon in which an active substance is oxidized by penetration of oxidizing substances such as oxygen, active oxygen, and free radicals from the external environment due to its strong oxidizing property. The stability according to the present invention means that the amount of the supporting material remaining in the capsule is 40% or more, preferably 50% or more, more preferably 60% or more, as compared to the amount of the initial supporting material, when the supporting material in the capsule is extracted after placing the microcapsule containing the supporting material in a surfactant aqueous solution and storing it at a temperature of 40 to 60°C for 7 days. The surfactant may include a surfactant commonly used in the art. The surfactant may be an anionic surfactant such as fatty acid sodium, monoalkyl sulfate, alkyl polyoxyethylene sulfate, alkyl benzene sulfonate, or monoalkyl phosphate; a cationic surfactant such as dialkyl dimethyl ammonium salt or alkyl benzyl methyl ammonium salt; a cationic surfactant such as alkyl sulfobetaine or alkyl carboxybetaine; or a nonionic surfactant such as polyoxyethylene alkyl ether, fatty acid sorbitan ester, fatty acid diethanolamine, or alkyl monoglyceryl ether, but is not limited thereto. In one specific example, the surfactant may be a polysorbate nonionic surfactant.

[0086] In addition, in the present invention, "biodegradability" indicates the degree of decomposition by microorganisms, and may mean that the decomposition by microorganisms is 20% or more, preferably 30% or more, and more preferably 40% or more, in a dark room at room temperature for 28 days according to the OECD 301D test method.

[0087] The term "photodegradable" may mean that the decomposition due to the wavelength of light when exposed to light for 12 hours per day, for a total of 30 days, in an aqueous condition using a xenon lamp according to the OECD 316 test method is 50% or more, preferably 60% or more, and more preferably 70% or more.

[0088] Furthermore, the naturally degradable microcapsules of the present invention may refer to capsules having a naturally degradable degree of 50% or more, preferably 60% or more, and more preferably 70% or more.

[0089] In addition, the microcapsules prepared by the above-mentioned method can be used as a fragrance product, a functional substance, or a carrier for a poorly soluble substance depending on the type of the effective substance. In the present invention, the effective substance may be selected from the group consisting of aroma oils, ultraviolet blocking agents, dyes, catalysts, antioxidants, and drugs.

[0090] For example, when the effective substance is an aromatic oil, the present invention can provide a scented product containing the microcapsules. The scented product can include, but is not limited to, a scented spray, an aromatic liquid product, a cleanser, a facial cleanser, a body product, a hair product, or a fabric softener composition.

[0091] In addition, when the effective substance is an ultraviolet blocking agent, the present invention can provide a cosmetic composition for blocking ultraviolet rays comprising the microcapsules. The ultraviolet blocking agent may be an inorganic ultraviolet blocking agent such as titanium dioxide (TiO2), zinc oxide (ZnO), silicate, or talc; or an organic ultraviolet blocking agent such as isoamyl-p-methoxycinnamate, octyl methoxycinnamate, ethylhexyl triazone, oxybenzone, diethylamino hydroxybenzoyl hexyl benzoate, octocrylene octyl salicylate, butyl methoxydibenzoylmethane, octyl salicylate, benzophenone, or anthranilate, but is not limited thereto.

[0092] In addition, when the effective substance is a functional substance or a poorly soluble substance, the microcapsules of the present invention can be used as a carrier for improving the stability of the functional substance or poorly soluble substance. The functional substance or poorly soluble substance can include, but is not limited to, antioxidants such as retinol or resveratrol; or poorly soluble substances such as cholesterol or ceramide.

[0093] The advantages and features of the present invention, as well as the methods for achieving them, will become clear from the detailed experimental and manufacturing examples described below. However, the present invention is not limited to the experimental and manufacturing examples disclosed below, and may be embodied in various different forms. However, the following experimental and manufacturing examples are provided so that the disclosure of the present invention will be complete, and will fully convey the scope of the invention to those skilled in the art to which the present invention pertains. Effect of the Invention

[0094] The microcapsules produced by the production method according to the present invention can exhibit high versatility, biodegradability and long-term stability, and can stably retain active substances within the capsules even in the presence of surfactants. [Brief description of the drawings]

[0095] [Figure 1]FIG. 1 is a schematic diagram of a method for producing microcapsules according to the present invention. [Diagram 2] FIG. 2 shows a comparison of the performance / stability of microcapsules according to the present invention in the presence of surfactants after storage at 50° C. for 7 days. [Diagram 3] FIG. 3 shows the results of confirming the degree of promotion of decomposition of microcapsules according to the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0096] The present invention will be described in detail with reference to the following examples. However, the following examples are merely illustrative of the present invention, and the content of the present invention is not limited to the following examples.

[0097] The materials and reagents used in the Examples and Comparative Examples were purchased from cosmetic raw material manufacturers and commercial suppliers, and the contents shown are based on weight percent.

[0098] Examples 1 to 6. Production of polyurea microcapsules

[0099] Microcapsules were prepared according to the composition in Table 1 below. First, 1 g of silica was dispersed in 68 g of distilled water, and 1 g of the first encapsulation component (hereinafter referred to as "biodegradable polymer"), which is a biodegradable polymer corresponding to each of Examples 1 to 6, was added to prepare a continuous phase 1. 0.5 g of polyisocyanate, which is the second encapsulation component, was added to 29.5 g of dodecane to prepare a dispersed phase. Then, the dispersed phase was added to the continuous phase 1 and stirred at 2,000 rpm to prepare a Pickering emulsion. Then, the Pickering emulsion was subjected to an interfacial polymerization reaction at 80° C. for 12 hours to prepare polyurea microcapsules.

[0100] Comparative Examples 1 and 2. Preparation of polyurea microcapsules

[0101] Polyurea microcapsules of Comparative Examples 1 and 2 were prepared according to the composition shown in Table 1. First, 1 g of polyethyleneimine was dissolved in 69 g of distilled water, and then a solution of 0.5 g of polyisocyanate in 29.5 g of dodecane was mixed and polymerization reaction was carried out at 80° C. for 12 hours to prepare polyurea microcapsules of Comparative Example 1.

[0102] Next, 1g of silica was dispersed in 68g of distilled water and 1g of polyethyleneimine was added at the same time to prepare continuous phase 1. 0.5g of polyisocyanate was added to 29.5g of dodecane to prepare a dispersed phase. Then, the dispersed phase was added to continuous phase 1 and a Pickering emulsion was prepared at 2,000 rpm. Then, the Pickering emulsion was subjected to an interfacial polymerization reaction at 80°C for 12 hours to prepare polyurea microcapsules of Comparative Example 2.

[0103] Experimental Example 1. Comparison of biodegradability of microcapsules containing biodegradable polymers

[0104] The biodegradability of the microcapsules prepared in Examples 1 to 6 and Comparative Examples 1 and 2 was compared. In this experimental example, the biodegradability of the microcapsules was measured by extracting the capsule wall and then using the OECD 301D method. Specifically, the OECD 301D method is a dissolved oxygen consumption measurement test method using a sealed test bottle, which is a method for measuring the biodegradability of capsules, which are water-insoluble test materials, and the biodegradability was calculated by the following general formula 1 by measuring the oxygen consumption over time (Biochemical Oxygen Demand (BOD)) relative to the theoretical oxygen demand (ThOD).

[0105]

number

[0106] [Table 1]

[0107] The biodegradability of microcapsules was measured depending on whether or not they contained a biodegradable polymer (Table 1). The encapsulation reaction occurred in all cases except for Comparative Example 1, which did not form a Pickering emulsion. The microcapsules of Examples 1 to 6, which were made from natural biodegradable polymers such as chitosan, polylysine, gelatin, silk fibroin, keratin or PAGA, showed a relatively higher biodegradability than the synthetic polymer polyethyleneimine.

[0108] Examples 7 to 9. Production of polyurea microcapsules

[0109] Polyurea microcapsules were prepared according to the composition of Table 2 below. First, 1g of silica was dispersed in 58g of distilled water, and 1g of chitosan, a biodegradable polymer (first encapsulation component), was added to prepare continuous phase 1, and 1g of phenylenediamine, a second capsule strengthening component, was added to 9g of distilled water to prepare continuous phase 2. 0.5g of a combination of polyisocyanate, a second encapsulation component, and methyldiphenyl diisocyanate, a first capsule strengthening component, was added to 29.5g of aromatic oil to prepare a dispersed phase. Then, the dispersed phase was added to the continuous phase 1 and stirred at 2,000 rpm to prepare a Pickering emulsion. Then, the continuous phase 2 was added to the Pickering emulsion, and an interfacial polymerization reaction was carried out at 80°C for 12 hours to prepare polyurea microcapsules.

[0110] Comparative Examples 3 to 7. Production of polyurea microcapsules

[0111] Microcapsules were produced according to the composition shown in Table 2. The microcapsules of Comparative Example 3 were produced in the same manner as in Examples 1 to 6, except that they did not contain the polyisocyanate, which is the second encapsulation component, and Comparative Examples 4 to 6 did not contain a biodegradable polymer.

[0112] Experimental Example 2. Comparison of stability and biodegradability of microcapsules containing capsule strengthening ingredients

[0113] The stability and biodegradability of the microcapsules prepared in Examples 7 to 9 were confirmed. In this experiment, the stability was measured as the ability of the capsules to maintain the aromatic oils in the capsules even in a harsh environment surrounded by an emulsifier. Specifically, the stability was measured by adding 1 part by weight of the microcapsules to 5 parts by weight of Tween 20 aqueous solution based on 100 parts by weight of the total composition, storing it at 50°C for 7 days, and then storing it in ethanol and a tip sonicator (Fisherbrand TM The aroma oils in the capsules were extracted using a UV spectrometer (FastTrack, Fisher Scientific, USA) and TM The content was measured using UV Vis Technology (Mettler Toledo, USA) to compare the stability. Biodegradability was measured in the same manner as in Experimental Example 1.

[0114] [Table 2]

[0115] As a result of the experiment, the microcapsules of Comparative Examples 4 to 6, which did not contain a biodegradable polymer, showed low biodegradability and stability, while the microcapsules of Comparative Examples 3, 5, and 7, which did not contain a second encapsulation component, showed low stability because the capsule wall was not formed densely. It was also confirmed that when the first capsule reinforcing component was used, the biodegradability tended to decrease depending on the amount used. On the other hand, it was confirmed that when the second encapsulation polymer and the second capsule reinforcing component were used in combination, the capsule wall was formed densely, improving the capsule stability.

[0116] Examples 10 to 18. Production of polyurea microcapsules

[0117] Polyurea microcapsules were prepared according to the composition of Table 3 below. First, 1g of silica was dispersed in 58g of distilled water, and 1g of chitosan, a biodegradable polymer, was added to prepare continuous phase 1, and 1g of the second capsule reinforcing component (phenylenediamine, aminobenzylamine, and benzidine disulfonic acid) was added to 9g of distilled water to prepare continuous phase 2. The second encapsulation component and the first capsule reinforcing component (methyldiphenyl diisocyanate, naphthalene diisocyanate, isophorone diisocyanate, and xylene diisocyanate) were added to 29.5g of aromatic oil to prepare a dispersed phase. Then, the dispersed phase was added to the continuous phase 1 and stirred at 2,000 rpm to prepare a Pickering emulsion. Then, the continuous phase 2 was added to the Pickering emulsion, and an interfacial polymerization reaction was carried out at 80°C for 12 hours to prepare polyurea microcapsules.

[0118] Experimental Example 3. Comparison of stability of microcapsules containing capsule strengthening ingredients

[0119] The stability and biodegradability of the microcapsules prepared in Examples 10 to 18 were compared. The stability and biodegradability were measured in the same manner as in Experimental Example 2.

[0120] [Table 3]

[0121] As a result of the experiment, it was confirmed that excellent biodegradability and stability were exhibited not only when phenylenediamine, but also when aminobenzylamine and benzidine disulfonic acid were used as the second capsule reinforcing component used in combination with the first encapsulation polymer, a biodegradable polymer. Also, excellent biodegradability and stability were exhibited not only when methyldiphenyldiisocyanate, but also when naphthalene diisocyanate, isophorone diisocyanate and xylene diisocyanate were used as the first capsule reinforcing component used in combination with the second encapsulation component. Therefore, the microcapsules according to the present invention can show remarkable effects in stability and biodegradability when the first encapsulation component (biodegradable polymer) is used in combination with the second capsule reinforcing component and when the second encapsulation component is used in combination with the first capsule reinforcing component.

[0122] Meanwhile, the stability of the microcapsules was relatively very low in Comparative Example 8. This is because Comparative Example 8 used cyclohexanediamine, a simple cyclic compound, not an aromatic compound, as the second capsule strengthening component in the manufacture of microcapsules, which shows that an aromatic compound, not a simple cyclic compound, is essential as the second capsule strengthening component for the stability of the microcapsules.

[0123] Examples 19 to 22. Production of polyurea microcapsules

[0124] Microcapsules were prepared according to the composition of Table 4 below. First, 1g of silica was dispersed in 58g of distilled water and 1g of chitosan, a biodegradable polymer, was added to prepare continuous phase 1, and 1g of phenylenediamine, a second capsule reinforcing component, was added to 9g of distilled water to prepare continuous phase 2. A combination of polyisocyanate, a second encapsulation component, and methyldiphenyldiisocyanate, a first capsule reinforcing component, was added to 29.5g of aromatic oil to prepare a dispersed phase. Then, the dispersed phase was added to continuous phase 1 and stirred at 2,000 rpm to prepare a Pickering emulsion. Then, continuous phase 2 and capsule reinforcing inorganic precursors (tetraethyl orthosilicate, methyltrimethoxysilane, and aminopropyltrimethylethoxysilane) were added to the Pickering emulsion and an interfacial polymerization reaction was carried out at 80°C for 12 hours to prepare polyurea microcapsules.

[0125] Experimental Example 4. Comparison of stability and biodegradability of microcapsules containing capsule-reinforcing polymers

[0126] The stability and biodegradability of the microcapsules prepared in Examples 19 to 24 were measured by the same method as in Experimental Example 2 described above.

[0127] [Table 4]

[0128] As a result of the experiment, it was confirmed that the microcapsules of Examples 19 to 22, which further contain a capsule-reinforcing inorganic precursor, showed increased stability compared to the microcapsules of Example 10, which did not contain a capsule-reinforcing inorganic precursor. However, it was also confirmed that as the content of the capsule-reinforcing inorganic precursor increased, the capsules tended to break more easily during production, and thus the stability tended to decrease.

[0129] Examples 23 to 26. Production of microcapsules

[0130] Microcapsules were prepared according to the composition of Table 5 below. First, silica and biodegradation-promoting particles (TiO2 and ZnO) were dispersed in 58g of distilled water, and 1g of chitosan, a biodegradable polymer, was added to prepare continuous phase 1, and 1g of phenylenediamine, a second capsule reinforcing component, was added to 9g of distilled water to prepare continuous phase 2. A combination of polyisocyanate, a second encapsulation component, and methyldiphenyl diisocyanate, a first capsule reinforcing component, was added to 29.5g of aromatic oil to prepare a dispersed phase. Then, the dispersed phase was added to continuous phase 1 and stirred at 2,000 rpm to prepare a Pickering emulsion. Then, continuous phase 2 and tetraethyl orthosilicate, a capsule reinforcing inorganic precursor, were added to the Pickering emulsion, and an interfacial polymerization reaction was carried out at 80°C for 12 hours to prepare polyurea microcapsules.

[0131] Experimental Example 5. Confirmation of biodegradability of microcapsules containing biodegradation-promoting particles

[0132] The stability, biodegradability and photodegradability of the microcapsules prepared in the above-mentioned Examples were measured. The stability and biodegradability were measured in the same manner as in the above-mentioned Experimental Example 2, and the photodegradability was measured with reference to the OECD 316 method. The decomposition measurement period was about 10,000 W / m, which is the energy equivalent to 4 weeks based on the annual average amount of sunlight in Seoul. 2 The corresponding energy was irradiated using a xenon lamp with Suntest XLS+, and the decomposition rate was measured by comparing the COD (Chemical Oxygen Demand) values ​​before and after the irradiation using the following formula 2.

[0133]

number

[0134] According to the European Chemicals Agency (ECHA), the decomposition degree is not clearly defined, but in general, if a substance is decomposed by microorganisms to between 20% and 60% within four weeks, it is classified as degradable, and if it is decomposed to over 60%, it is classified as a substance that can be decomposed immediately. The definition of photodecomposition degree has not yet been clearly defined, but in the actual environment, microorganisms, sunlight, hydrolysis, thermal decomposition, etc. are all applied, and it is necessary to consider the two most influential factors, microorganisms and photodecomposition.

[0135] [Table 5]

[0136] As a result of the experiment, in the case of Examples 23 to 26, which contained biodegradation-promoting particles, it was confirmed that the addition of the biodegradation-promoting particles did not have a significant effect on the stability and biodegradability of the capsules, but promoted photodegradation.

[0137] Comparative Example 9. Production of polyurea microcapsules

[0138] Microcapsules were prepared according to the composition in Table 6 below. Tween 20, gum arabic, and pre-melamine formaldehyde solution were dispersed in 54.5g of distilled water to prepare a continuous phase. 30g of fragrance (dispersed phase) was slowly added to the continuous phase at 2,000 rpm to prepare an emulsion. After lowering the rpm to 1,000, the pH was lowered to 5 with citric acid, and the capsule formation reaction was carried out at 70°C for 3 hours. The reaction was terminated by adjusting the pH to 7.5 using tromethamine, and biodegradation-promoting particles were added and adsorbed to prepare melamine-formaldehyde resin capsules.

[0139] Comparative Example 10. Preparation of polyurea microcapsules

[0140] Microcapsules were prepared according to the composition in Table 6 below. 0.5g of polyvinyl alcohol was dissolved in 63g of distilled water to prepare a continuous phase. 1.8g of methacrylic acid, 4g of pentaerythritol triacrylate, and 0.2g of 2,2' azobis-(2-methylbutyronitrile) were dissolved in 30g of fragrance to prepare a dispersed phase. The dispersed phase was slowly added to the continuous phase at 2,000 rpm to prepare an emulsion, which was then reacted at 80°C for 6 hours to carry out a capsule formation reaction, and biodegradation-promoting particles were added and adsorbed to prepare acrylic capsules.

[0141] Experimental Example 6. Measurement of stability, biodegradability and photodegradability of microcapsules

[0142] The stability, biodegradability and photodegradability of the microcapsules prepared in the above-mentioned Examples were measured. The stability, biodegradability and photodegradability were measured in the same manner as in Experimental Example 5 above.

[0143] [Table 6]

[0144] As a result of the experiments, it was confirmed that microcapsules containing a first encapsulated component, a second encapsulated component, a first capsule strengthening component and a second capsule strengthening component, as in the present invention, have higher biodegradability, photodegradability and natural degradability than Comparative Examples 9 and 10, which do not contain such components.

[0145] Experimental Example 7. Evaluation of fragrance intensity after washing

[0146] A washing evaluation was carried out to confirm the applicability of the microcapsules prepared in the above examples as a fabric softener. First, the test fabric was a commercially available cotton towel (30 cm x 20 cm) that was washed five times in a washing machine using a standard amount of general laundry detergent and then dehydrated. 1 part by weight of the prepared microcapsules was added to an aqueous solution containing 5 parts by weight of Tween 20 based on 100 parts by weight of the total composition, and the composition was stored at 50°C for 7 days. The composition was measured to be the standard amount (0.67 ml / L washing water) and placed in a stirring washing machine, and then treated with a rinse course, dehydrated, and the cotton towel was taken out. Then, the cotton towel was dried for 12 hours at a humidity of 30% and a temperature of 25°C. At this time, 20 experienced panelists performed a sensory evaluation at three time points (immediately after washing, after drying, and after rubbing) to evaluate the fragrance intensity. The fragrance intensity was given a score ranging from 0 to 5, with the cotton towel not treated with microcapsules being given a score of 0, and this was repeated at least three times to show the average value. The sensory evaluation of the composition containing microcapsules immediately after preparation and the composition stored for 7 days are shown in Table 7 and Figure 2 below, respectively.

[0147] <Evaluation criteria> 0 points: Almost no scent left. 5 points: A lot of fragrance remains.

[0148] [Table 7]

[0149] As shown in Table 7 and Figure 2, in the cases of Examples 7, 8, 10 and 19, which include a biodegradable polymer, an encapsulating polymer and a capsule-reinforcing polymer, capsule stability and fragrance were strong. In particular, it was confirmed that Example 19, which used a capsule-reinforcing inorganic precursor, maintained the best stability and fragrance. In addition, it was confirmed that Examples 23 and 25, which used natural decomposition-promoting particles, maintained similar levels of stability and fragrance to Example 19. From the above results, it was confirmed that the application of natural decomposition-promoting particles did not affect the performance of the capsules.

[0150] Experimental Example 8. Confirmation of decomposition promotion effect

[0151] In order to confirm the decomposition promoting effect of the microcapsules of the present invention, the capsules of Example 25 to which the natural decomposition promoting particles were added were diluted with distilled water to a concentration of 500 ppm. Then, the degree of decomposition caused by natural sunlight was compared by measuring the change in capsule size over time using a particle size analyzer (Mastersizer 3000, Malvern). In order to confirm the decomposition promoting effect, a transparent container, an opaque container, and a specially made polypropylene container with opaque walls (50 cm x 50 cm x 50 cm) were filled with 100 L of water under water-based conditions to a depth of 15 cm, and the container was fixed to confirm the degree of decomposition caused by natural sunlight by measuring the change in size over time (Figure 3).

[0152] As shown in Figure 3, the capsules were decomposed and reduced in size after 25 days in sunlight, and it was confirmed that the capsules decomposed in water, but no decomposition occurred in an opaque container, and the capsules did not change in size. From the above results, it can be confirmed that the capsules are stable in the product form, but decomposition occurs when they are released into the environment after use.

Claims

1. preparing a Pickering emulsion by mixing a continuous phase 1 containing inorganic particles and a first encapsulated component with a dispersed phase 1 containing a second encapsulated component and a first capsule-strengthening component; and A method for producing microcapsules, comprising the steps of mixing the Pickering emulsion with a continuous phase 2 containing a second capsule strengthening component and encapsulating the mixture, the first encapsulation component is a biodegradable polymer; the first encapsulation component and the second capsule strengthening component each contain an amine group or a hydroxy group; when the first encapsulation component and the second encapsulation reinforcement component have an amine group, the second encapsulation component and the first encapsulation reinforcement component have an acrylate group or an isocyanate group; when the first encapsulation component and the second encapsulation reinforcement component have a hydroxy group, the second encapsulation component and the first encapsulation reinforcement component have an isocyanate group, an acyl halide group, a chloroformate group, or an acrylate group; The first capsule reinforcing component is one or more compounds selected from the group consisting of a monomer represented by the following formula 2, methylene diphenyl diisocyanate, naphthalene diisocyanate, and isophorone diisocyanate; an oligomer thereof; or a polymer thereof: [Formula 1] In the formula 2, R 2 to R 7 are each independently selected from the group consisting of hydrogen; an alkyl group having 1 to 5 carbon atoms; an alkenyl group having 2 to 5 carbon atoms; an alkyl isocyanate group having 1 to 5 carbon atoms; an isocyanate group; an alkyl acyl halide group having 1 to 5 carbon atoms; an acyl halide group; an alkyl chloroformate group having 1 to 5 carbon atoms; a chloroformate group; an alkyl acrylate group having 1 to 5 carbon atoms; and an acrylate group; At least one of R 2 to R 7 in Chemical Formula 2 is a compound containing one of an isocyanate group, an acyl halide group, a chloroformate group, and an acrylate group.

2. The method for producing naturally degradable microcapsules according to claim 1, further comprising the step of adsorbing naturally decomposition-promoting particles to the capsules.

3. The method for producing biodegradable microcapsules according to claim 1, wherein the second encapsulation component is a compound represented by the following chemical formula 1: [Case 2] In Formula 1, R １ is a compound containing an alkylene group having 1 to 50 carbon atoms, which is substituted or unsubstituted with an acrylate group or a heteroatom; a cyclic hydrocarbon having 3 to 60 carbon atoms; or an alkylene group having 1 to 50 carbon atoms and a cyclic hydrocarbon having 3 to 60 carbon atoms, X １ ~X ４ are each independently selected from the group consisting of hydrogen, an amine group, an acyl halide group, an isocyanate group, a chloroformate group, and an acrylate group; n is an integer of 1 or more.

4. The method for producing the naturally degradable microcapsules according to claim 1, wherein the second capsule strengthening component is one or more compounds selected from the group consisting of a monomer represented by the following chemical formula 3, melamine, and benzidine disulfonic acid; an oligomer thereof; or a polymer thereof: [C3] In the above formula 3, R ８ ~R １３ are each independently selected from the group consisting of hydrogen; an amine group; a hydroxy group; an alkyl group having 1 to 5 carbon atoms; an alkylamine group having 1 to 5 carbon atoms; a hydroxyalkyl group having 1 to 5 carbon atoms; and an alkenyl group having 2 to 5 carbon atoms; The formula 3 is R ８ ~R １３ Any one or more of the above is a compound containing one of an amine group or a hydroxy group.

5. The method for producing naturally degradable microcapsules according to claim 1 , wherein the Pickering emulsion further comprises a capsule-strengthening inorganic precursor.

6. The method for producing biodegradable microcapsules according to claim 5, wherein the capsule-strengthening inorganic precursor is a compound represented by the following chemical formula 4: [C4] In Formula 4, R １４ ~R １７ are each independently hydrogen; an alkoxy group having 1 to 5 carbon atoms; an alkyl group having 1 to 5 carbon atoms; or a hydrocarbon compound having 1 to 5 carbon atoms containing one or more functional groups selected from the group consisting of an amine group, a thiol group, a hydroxyl group, a carbonyl group, a carboxyl group, and an ether group.

7. The method for producing naturally decomposable microcapsules according to claim 2, characterized in that the naturally decomposition-promoting particles are selected from the group consisting of titanium oxide, zinc oxide, zirconium oxide, tungsten oxide, platinum, platinum oxide, and gold chloride.

8. The method for producing naturally degradable microcapsules according to claim 1, characterized in that the Pickering emulsion contains an active substance selected from the group consisting of perfume oils, UV blocking agents, dyes, catalysts, antioxidants and drugs.

9. A microcapsule produced according to any one of claims 1 to 8.

10. A fabric softener composition comprising the microcapsules according to claim 9.

11. The composition comprises a first encapsulated component, a second encapsulated component, a first capsule reinforcing component, a second capsule reinforcing component, and inorganic particles. the first encapsulation component is a biodegradable polymer; the first encapsulation component and the second capsule strengthening component each contain an amine group or a hydroxy group; when the first encapsulation component and the second encapsulation reinforcement component have an amine group, the second encapsulation component and the first encapsulation reinforcement component have an acrylate group or an isocyanate group; when the first encapsulation component and the second encapsulation reinforcement component have a hydroxy group, the second encapsulation component and the first encapsulation reinforcement component have an isocyanate group, an acyl halide group, a chloroformate group, or an acrylate group; The first capsule reinforcing component is one or more compounds selected from the group consisting of a monomer represented by the following formula 2, methylene diphenyl diisocyanate, naphthalene diisocyanate, and isophorone diisocyanate; an oligomer thereof; or a polymer thereof: [C5] In the formula 2, R 2 to R 7 are each independently selected from the group consisting of hydrogen; an alkyl group having 1 to 5 carbon atoms; an alkenyl group having 2 to 5 carbon atoms; an alkyl isocyanate group having 1 to 5 carbon atoms; an isocyanate group; an alkyl acyl halide group having 1 to 5 carbon atoms; an acyl halide group; an alkyl chloroformate group having 1 to 5 carbon atoms; a chloroformate group; an alkyl acrylate group having 1 to 5 carbon atoms; and an acrylate group; At least one of R 2 to R 7 in Formula 2 is a compound containing one of an isocyanate group, an acyl halide group, a chloroformate group, and an acrylate group.