CURABLE COMPOSITION AND METHOD FOR BONDING SUBSTRATES THEREOF - Patent application

Abstract

A curable composition, specifically a two-component composition, is described that includes a silane-modified polymer and an epoxy resin terminated with epoxy end groups, and the composition further includes a curing compatibilizer having at least one silane group and at least two amine groups. The curable composition exhibits enhanced adhesive strength and good elongation at break. A method for applying the curable composition to the surface of a substrate is also provided.

Description

[Technical field]

[0001] The present disclosure relates to a curable composition, particularly a two-part curable composition, and a method for applying the same onto a surface of a substrate. The curable composition exhibits enhanced adhesive strength and good elongation at break. [Background technology]

[0002] Silane-modified polymers (SMPs), also known as silylated polymers, are versatile, high-value industrial resins that have been widely accepted for a wide variety of applications. Silane-modified polymer (SMP) adhesives / sealants are becoming increasingly popular due to their many advantages, including low VOC, no isomers and no bubbles, and a good balance of performance properties and durability. Specifically, SMP adhesives are superior to silicone adhesives in that they exhibit higher adhesive strength and can be overcoated with additional paint or coating materials. In addition, SMP adhesives are more durable than adhesives formulated with polyurethane prepolymers.

[0003] SMP adhesives / sealants are used in a variety of applications, such as prefabricated construction (PC), residential decoration, transportation [vehicles, ships, automobiles, aircraft, and high-speed rail (HSR)], industrial assembly, and household products. However, these applications usually require high adhesive strength, especially for transportation, industrial assembly, and household products. For example, a significant number of customers are seeking SMP adhesives with adhesive strengths higher than 5.0 MPa and elongation at break of about 100%. Such high requirements for mechanical strength are generally considered to be a big challenge for SMP adhesives, since many of the commercially available SMP adhesives can only achieve low adhesive strengths of about 3.0-4.0 MPa. Numerous efforts have been made by many researchers to modify factors such as fillers, resin ratios, adhesion promoters, and catalysts, but none of these prior art studies can achieve adhesive strengths as high as 5.0 MPa.

[0004] Without being limited to a particular theory, it is believed that the low adhesive strength of existing SMP-based adhesives is at least partially due to the absence of any chemical bonds between the SMP phase and other phases used in combination with it. Prior art two-component (2K) adhesive compositions are shown in Figure 1, in which the incorporation of various additives (curing agents, catalysts, accelerants, surfactants, etc.) and compatibilizers establishes little or no chemical bonds between the SMP and epoxy phases, such that the resulting blend contains chemically isolated SMP and epoxy phases and therefore exhibits low cohesion and low adhesive strength.

[0005] After continuous research, the present inventors have surprisingly developed a two-component composition that can achieve one or more of the above goals. Specifically, it has been found that when a specific compound having both curing and compatibilizing functions is included in the 2K curable composition of the present application, the adhesive strength can be further enhanced to a desired level. Summary of the Invention

[0006] The present disclosure provides unique curable compositions, specifically two-part curable compositions, and methods for applying the curable compositions onto the surface of a substrate.

[0007] In a first aspect of the present disclosure, the present disclosure provides a curable composition, specifically at least one silane-modified polymer; at least one epoxy resin terminated with an epoxy end group; and a curing compatibilizer having at least one silane group and at least two amine groups in the same molecule.

[0008] In a second aspect of the disclosure, the disclosure provides a method for applying the curable composition onto a surface of a substrate, the method comprising: (1) combining a silane-modified polymer, an epoxy resin, and a curing compatibilizer to form a precursor blend; (2) applying the precursor blend onto a surface of the substrate; and (3) curing the precursor blend or allowing the precursor blend to cure.

[0009] It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory only and are not restrictive of the invention, as claimed. [Brief description of the drawings]

[0010] [Figure 1] FIG. 1 is a schematic diagram of a prior art 2K curable composition. [Diagram 2] 1 is a schematic diagram of an embodiment of a 2K curable composition described herein. [Diagram 3] 1 shows a reaction scheme for a hydrosilylation reaction for preparing an SMP according to certain embodiments of the present disclosure. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0011] Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs, and all publications, patent applications, patents, and other references mentioned herein are incorporated by reference.

[0012] As disclosed herein, "and / or" means "and, or alternatively." Unless otherwise stated, all ranges are inclusive of the endpoints. All percentages and ratios are calculated by weight and all molecular weights are number average molecular weights unless otherwise stated.

[0013] According to various embodiments of the present disclosure, the curable composition of the present disclosure is a "two-component", "two-part", or "two-package" type composition comprising component (A) having a silane-modified polymer and component (B) having an epoxy resin. In the context of the present disclosure, the terms "part (A)", "component (A)", "silane-modified polymer component (A)", and "silane-modified polymer part (A)" can be used interchangeably and refer to the component containing the silane-modified polymer, and the terms "part (B)", "component (B)", "epoxy resin part (B)", and "epoxy resin component (B)" can be used interchangeably and refer to the component containing the epoxy resin. Components (A) and (B) are transported and stored separately and combined shortly or immediately before being applied to the surface of the substrate. According to one embodiment of the present disclosure, a curing compatibilizer is included in component (A).

[0014] Once combined, the reactive groups of each component, such as the epoxy end groups in the epoxy resin, the silane / siloxane groups in the SMP, the amine and silane / siloxane groups in the cured compatibilizer, and any other reactive groups contained in other additives or reactants, react with each other to establish a chemically integrated combination of SMP-epoxy resin. According to various embodiments of the present disclosure, once combined, the SMP phase is chemically bonded to the epoxy resin via the cured compatibilizer. Without being limited to a particular theory, an exemplary embodiment of the present disclosure is shown in FIG. 2. It should be noted that in FIG. 2, the SMP phase and the epoxy resin phase are shown integrated into the epoxy-SMP phase, but this does not mean that the SMP molecules and the epoxy resin molecules are directly covalently bonded, but rather assumes that the integration of the two phases can be achieved by the action of the cured compatibilizer. A comparison of FIG. 1 and FIG. 2 clearly shows the difference between the chemically integrated combination of the present application and the chemically isolated systems of the prior art. According to the most preferred embodiment of the present disclosure, the curable composition contains only the curing compatibilizer to achieve the functions of both curing agent and compatibilizer, and does not contain any additional curing agent or compatibilizer other than the curing compatibilizer, i.e., the chemical integration of the SMP phase and the epoxy resin phase is achieved by the sole action of the curing compatibilizer, and no additional reagents are required for the integration process.

[0015] Without being limited to a particular theory, it is believed that the incorporation of a specially designed curing compatibilizer in the composition of the present disclosure can effectively achieve a chemically integrated combination of SMP-epoxy resin, thereby successfully enhancing the adhesive strength of the resulting composition to a level as high as 5.0 MPa, and even up to 8 MPa, while retaining its good elongation properties.

[0016] According to various embodiments of the present disclosure, the curable composition of the present disclosure is a two-component composition that can be an adhesive, a sealant, a coating, or a concrete, preferably a 2K adhesive or a 2K sealant. The curable composition of the present disclosure can be applied onto the surface of a substrate to form a coating film, a concrete layer, or a sealant layer thereof, achieving the functions of physical / chemical protection, sound / heat / radiation barrier, filling material, supporting / transporting / construction structure, decorative layer, or sealing / sealing / waterproof layer. In addition, when the curable composition of the present disclosure is used as an adhesive, it can be used to bond two or more identical or different substrates together. According to some embodiments of the present disclosure, the substrate is at least one member selected from the group consisting of metal, masonry, concrete, paper, cotton, fiberboard, paperboard, wood, woven or nonwoven fabric, elastomer, polycarbonate, phenolic resin, epoxy resin, polyester, polyethylene carbonate, synthetic and natural rubber, silicone, and silicone polymer. According to another embodiment of the present disclosure, the substrate is a polymer substrate selected from the group consisting of polymethyl methacrylate, polypropylene carbonate, polybutene carbonate, polystyrene, acrylonitrile-butadiene-styrene resin, acrylic resin, polyvinyl chloride, polyvinyl alcohol, polycarbonate, polyethylene terephthalate, polyurethane, polyimide, and copolymers thereof. According to another embodiment of the present disclosure, the substrate is selected from the group consisting of wood, polystyrene, nylon, and acrylonitrile-butadiene-styrene.

[0017] Silane Modified Polymer (SMP) According to various embodiments of the present disclosure, component (A) is a component that includes a silane-modified polymer. The SMP can be a polymer having a silane group. For example, the SMP can be represented by the following formula I: R 1 m (R 2 O) (3-m) Si-R 7 -(polymer main chain -R 8 -SiR 3 n (R4 O) (3-n) Formula I wherein the polymer backbone is derived from a polyol, more preferably from at least one polyisocyanate and at least one polyol, and optionally, at least one -R 9 -SiR 5 s (R 6 O) (3-s) Functionalized with R 1 , R 2 , R 3 , R 4 , R 5 , and R 6 each independently represents a hydrogen atom or a C1-C6 alkyl group; each of m, n, and s represents an integral of 0, 1, or 2; R 7 , R 8 , and R 9 each independently represents a direct bond, -O-, a divalent (C1-C6 alkylene) group, -O-(C1-C6 alkylene) group, -N(R N )-(C1-C6 alkylene) group, or -C(=O)-N(R N )-(C1-C6 alkylene) group, R N represents a hydrogen atom or a C1-C6 alkyl group.

[0018] According to certain embodiments of the present disclosure, the polymer backbone may be derived from a polyether polyol or a polyester polyol. According to preferred embodiments of the present disclosure, the polymer backbone is a polyurethane backbone derived from the reaction of at least one polyisocyanate with at least one polyol, as described above.

[0019] In the context of this disclosure, "silane modification", "hydrosilylation", and "silylation" refer to the group "R 1 m (R 2 O) (3-m) Si-R 7 -", "-R 8 -SiR 3 n (R 4 O) (3-n) " and "-R9 -SiR 5 s (R 6 O) (3-s) " to the polymer backbone in the SMP, and all of the above-mentioned silicone-containing substituents (groups R 1 -, R 2 O-, R 3 -, R 4 O-, R 5 - and R 6 These groups, collectively referred to as "silane groups," are referred to as "silane groups" even though O- may actually represent hydrogen, hydroxyl, alkyl, or alkoxy groups. 1 m (R 2 O) (3-m) Si-R 7 -" and "-R 8 -SiR 3 n (R 4 O) (3-n) " represents a terminal group attached to the end of the SMP, and -R 9 -SiR 5 s (R 6 O) (3-s) represents at least one side group attached to an intermediate repeat unit of the polymer backbone.

[0020] In the context of this disclosure, C1-C6 alkyl groups include methyl, ethyl, n-propyl, i-propyl, n-butyl, i-butyl, sec-butyl, t-butyl, n-pentyl, i-pentyl, tert-pentyl, neopentyl, and n-hexyl, and C1-C6 alkylene includes methylene, ethylene, propylene, butylene, pentamethylene, and hexamethylene.

[0021] According to less preferred embodiments of the present disclosure, the polymer backbone is derived from a polyol and the SMP represented by formula I may be prepared by reacting at least one reactive capping group (such as, for example, an allyl group) attached to the polyol (i.e., the polymer backbone) with a trialkoxysilane group via a hydrosilylation reaction, or by reacting a polyisocyanate with a polyol to form a polyurethane intermediate, i.e., the polymer backbone, which is then functionalized with a silanizing agent.

[0022] According to a preferred embodiment of the present disclosure, the polyurethane intermediate is a polyurethane chain having an isocyanate end group, and the silanizing agent comprises a silane group at one end and an isocyanate-reactive group (such as a hydroxyl or amine group) at the other end. In the context of the present disclosure, the amine group can be a primary or secondary amine group.

[0023] According to another preferred embodiment of the present disclosure, the polyurethane intermediate is a polyurethane chain having a hydroxyl end group, and the silanizing agent includes a silane group at one end and an isocyanate group at the other end.

[0024] In various embodiments, the polyisocyanate compound for preparing the polymer backbone (polyurethane chain) is an aliphatic, cycloaliphatic, aromatic, or heteroaryl compound having at least two isocyanate groups. In a preferred embodiment, the polyisocyanate compound is a C4-C 12 Aliphatic polyisocyanates, C6-C containing at least two isocyanate groups 15 Alicyclic or aromatic polyisocyanates, C7-C containing at least two isocyanate groups 15The polyisocyanate compound may be selected from the group consisting of m-phenylene diisocyanate, 2,4-toluene diisocyanate and / or 2,6-toluene diisocyanate (TDI), various isomers of diphenylmethane diisocyanate (MDI), carbodiimide modified MDI products, hexamethylene-1,6-diisocyanate, tetramethylene-1,4-diisocyanate, cyclohexane-1,4-diisocyanate, hexahydrotoluene diisocyanate, hydrogenated MDI, naphthylene-1,5-diisocyanate, isophorone diisocyanate (IPDI), or mixtures thereof. In general, the amount of polyisocyanate compound may vary based on the actual requirements of the SMP and the resulting curable composition. For example, as one illustrative embodiment, the content of the polyisocyanate compound may be 15% by weight to 60% by weight, or 20% by weight to 50% by weight, or 23% by weight to 40% by weight, or 25% by weight to 38% by weight, based on the total weight of the SMP.

[0025] According to one embodiment of the present disclosure, the polyol for the polymer backbone or for preparing the polyurethane backbone is a C2-C 16 Aliphatic polyhydric alcohols, C6-C containing at least two hydroxyl groups 15 Alicyclic or aromatic polyhydric alcohols, C7-C containing at least two hydroxyl groups 15 Aromatic aliphatic polyhydric alcohols, polyester polyols having a molecular weight of 100-5,000 and an average hydroxyl functionality of 1.5-5.0, poly(C2-C3) having a molecular weight of 100-5,000, 10 ) alkylene glycol or multiple (C2-C 10 ) a polyether polyol, which is a copolymer of an alkylene glycol, a polycarbonate diol having a molecular weight of 100 to 5,000, and a combination thereof, which contains at least two amino groups, 10 Polyamines, C2-C containing at least two thiol groups10 Polythiol, C2-C containing at least one hydroxyl group and at least one amino group 10Additional comonomers selected from the group consisting of alkanolamines may also be used. According to a preferred embodiment, the polyol is a polyether polyol. In various embodiments, the polyether polyol used as the polyol has a molecular weight of 100 to 5,000 g / mol and has end point values ​​of 120, 150, 180, 200, 250, 300, 350, 400, 450, 500, 550, 600, 700, 800, 900, 1000, 1100, 1200, 1300, 1400, 1500, 1600, 1700, 1800, 1900, 2000, 2100, 220, 240, 260, 280, 290, 300, 310, 320, 330, 340, 350, 360, 370, 380, 390, 410, 420, 430, 440, 450, 500, 550, 600, 700, 800, 900, 1000, 1100, 1200, 1300, 1400, 1500, 1600, 1700, 1800, 1900, 2000, 2100, 220, 260, 270, 280, 290, 310, 320, 330, 340, 350, 360, 370, 380, 390, 410, 420, 430, The molecular weight may be in the range obtained by combining any two of 0, 2300, 2400, 2500, 2600, 2700, 2800, 2900, 3000, 3100, 3200, 3300, 3400, 3500, 3600, 3700, 3800, 3900, 4000, 4100, 4200, 4300, 4400, 4500, 4600, 4700, 4800, 4900, and 5000 g / mol. In various embodiments, the polyether polyols have an average hydroxyl functionality of 1.5 to 5.0, and may have an average hydroxyl functionality in the range obtained by combining any two of the endpoint values ​​1.6, 1.7, 1.8, 1.9, 2.0, 2.1, 2.2, 2.3, 2.4, 2.5, 2.6, 2.7, 2.8, 2.9, 3.0, 3.1, 3.2, 3.3, 3.4, 3.5, 3.6, 3.7, 3.8, 3.9, 4.0, 4.1, 4.2, 4.3, 4.4, 4.5, 4.6, 4.7, 4.8, 4.9, and 5.0. According to one preferred embodiment, the polyol has an average kinematic viscosity of 500-1,200 cSt, or 600-1,100 cSt, or 700-1,000 cSt, or 800-950 cSt, or 850-920 cSt, and an OH number of 10-100 mg KOH / g, or 12-90 mg KOH / g, or 15-80 mg KOH / g, or 16-70 mg KOH / g, or 17-60 mg KOH / g, or 18-50 mg KOH / g, or 19-40 mg KOH / g, or 20-30 mg KOH / g, or 25-28 mg KOH / g.According to a preferred embodiment of the present disclosure, the polyether polyol is selected from the group consisting of polyethylene glycol, polypropylene glycol, polytetramethylene glycol, poly(2-methyl-1,3-propane glycol), and any copolymers thereof, such as poly(ethylene oxide-propylene oxide) glycol. According to another preferred embodiment of the present disclosure, the polyether polyol comprises at least one (C2-C. 10 ) alkylene glycol or copolymers thereof, for example, the polyethylene polyol may be selected from the group consisting of polyethylene, (methoxy)polyethylene glycol (MPEG), polyethylene glycol (PEG), poly(propylene glycol), polytetramethylene glycol, poly(2-methyl-1,3-propane glycol), or copolymers of ethylene epoxide and propylene epoxide having primary or secondary hydroxyl end groups (polyethylene glycol-propylene glycol).

[0026] According to certain embodiments of the present disclosure, polyether polyols can be prepared by polymerization of one or more linear or cyclic alkylene oxides selected from propylene oxide (PO), ethylene oxide (EO), butylene oxide, tetrahydrofuran, 2-methyl-1,3-propane glycol, and mixtures thereof, with a suitable starter molecule in the presence of a catalyst. Typical starter molecules include compounds having at least one, preferably 1.5 to 3.0, hydroxyl group or one or more primary amine groups in the molecule. Suitable starter molecules having at least one, preferably 1.5 to 3.0, hydroxyl groups in the molecule are, for example, ethylene glycol, 1,2-propanediol, 1,3-propanediol, 1,2-butanediol, 1,3-butanediol, 1,4-butenediol, 1,4-butynediol, 1,5-pentanediol, neopentyl glycol, 1,4-bis(hydroxymethyl)-cyclohexane, 1,2-bis(hydroxymethyl)-cyclohexane, 1,3-bis(hydroxymethyl)-cyclohexane, 2-methylpropane-1,3-diol, methylpentanediol, diethyl The starter molecule having one or more primary amine groups in the molecule may be selected from the group consisting of ethylene glycol, triethylene glycol, tetraethylene glycol, polyethylene glycol, dipropylene glycol, polypropylene glycol, dibutylene glycol, polybutylene glycol, trimethylolpropane, glycerol, pentaerythritol, castor oil, sugar compounds such as glucose, sorbitol, mannitol and sucrose, polyhydric phenols, resols such as oligomeric condensation products of phenol with formaldehyde and Mannich condensation products of phenol with formaldehyde and dialkanolamine, and also melamine.The starter molecule having one or more primary amine groups in the molecule may be selected from the group consisting of aniline, EDA, TDA, MDA and PMDA, more preferably from the group consisting of TDA and PMDA, and most preferably TDA.When TDA is used, all isomers can be used alone or in any desired mixture.For example, 2,4-TDA, 2,6-TDA, a mixture of 2,4-TDA and 2,6-TDA, a mixture of 2,3-TDA, 3,4-TDA, 3,4-TDA and 2,3-TDA, and a mixture of all the above isomers can also be used. Catalysts for preparing polyether polyols can include alkaline catalysts such as potassium hydroxide for anionic polymerization, or Lewis acid catalysts such as boron trifluoride for cationic polymerization. Suitable polymerization catalysts can include potassium hydroxide, cesium hydroxide, boron trifluoride, or double cyanide complex (DMC) catalysts such as zinc hexacyanocobaltate or tetraphosphazenium compounds. In preferred embodiments of the present disclosure, the starting material polyether polyols include polyethylene, (methoxy)polyethylene glycol (MPEG), polyethylene glycol (PEG), poly(propylene glycol), polytetramethylene glycol, poly(2-methyl-1,3-propane glycol), or copolymers of ethylene epoxide and propylene epoxide having primary or secondary hydroxyl end groups (polyethylene glycol-propylene glycol).

[0027] According to a preferred embodiment of the present disclosure, the amount of polyisocyanate is appropriately selected so that the isocyanate groups are present in a stoichiometric molar amount relative to the total molar amount of hydroxyl groups contained in the polyol and any additional additives or modifiers. According to an embodiment of the present disclosure, the polyurethane intermediate (PU backbone) has an NCO content of 2-50 wt%, preferably 6-49 wt%, preferably 8-25 wt%, preferably 10-20 wt%, more preferably 11-15 wt%, and most preferably 12-13 wt%.

[0028] The reaction between the polyisocyanate and the polyol may occur in the presence of one or more catalysts that can promote the reaction between the isocyanate group and the hydroxyl group. Without being limited to theory, the catalysts include, for example, glycine salts; tertiary amines; tertiary phosphines, such as trialkylphosphines and dialkylbenzylphosphines; morpholine derivatives; piperazine derivatives; chelates of various metals, such as those obtained from acetylacetone, benzoylacetone, trifluoroacetylacetone, ethylacetoacetate, and the like, with metals such as Be, Mg, Zn, Cd, Pd, Ti, Zr, Sn, As, Bi, Cr, Mo, Mn, Fe, Co, and Ni; acidic metal salts of strong acids, such as ferric chloride and stannic chloride; organic acids with alkali metals, alkaline earth metals, Al, Sn, Pb, Mn, Co, Ni, and the like. and Cu; tin(II) salts of organic carboxylic acids, such as organotin compounds such as tin(II) diacetate, tin(II) dioctanoate, tin(II) diethylhexanoate, and tin(II) dilaurate, as well as dialkyltin(IV) salts of organic carboxylic acids, such as dibutyltin diacetate, dibutyltin dilaurate, dibutyltin maleate, and dioctyltin diacetate; bismuth salts of organic carboxylic acids, such as bismuth octanoate; organometallic derivatives of trivalent and pentavalent As, Sb, and Bi, as well as metal carbonyls of iron and cobalt; or mixtures thereof. Generally, the content of the catalyst used herein is greater than zero and is up to 3.0% by weight, preferably up to 2.5% by weight, more preferably up to 2.0% by weight, based on the total weight of component (A).

[0029] Silane groups (especially "R 1 m (R 2 O) (3-m) Si-R 7 -", "-R 8 -SiR 3 n (R 4 O) (3-n) " and "-R 9 -SiR 5 s (R 6 O)(3-s) The silanizing agents used to introduce silanes into the SMP can be represented by the formula Silane-X, where the X group can be hydrogen, hydroxyl, an amine group, an imine group, an isocyanate group, a halogen atom (e.g., chlorine, bromine, or iodine), a ketoximato, amino, amide, acid amide, aminoxy, mercapto, or an alkenyloxy group. Examples of suitable silanizing agents include γ-aminopropylmethyldimethoxysilane, γ-aminopropylmethyldiethoxysilane, γ-aminopropyltrimethoxysilane, γ-aminopropyltriethoxysilane, γ-aminophenyltrimethoxysilane, aminoethylaminopropyltrimethoxysilane, aminoethylaminopropyltriethoxysilane, aminoethylaminoethylaminopropyltrimethoxysilane, aminoethylaminomethylmethyldiethoxysilane, (3-aminopropyl)-diethoxy-methylsilane, (3-aminopropyl)-dimethyl-ethoxysilane, (3-aminopropyl)-trimethoxysilane, N-((β- N-((β-aminoethyl)-γ-aminopropyltriethoxysilane, γ-aminopropyldimethylmethoxysilane, N-((β-aminoethyl)-γ-aminopropyltrimethoxysilane, N-phenyl-γ-aminopropyltrimethoxysilane, (aminoethylaminomethyl)phenethyltrimethoxysilane, N-((β-aminoethyl)-γ-aminopropylmethyldimethoxysilane, N-(6-aminohexyl)-3-aminopropyltrimethoxysilane, N-(2-aminoethyl)-11-aminoundecyltrimethoxysilane, N-((β-aminoethyl)-γ-aminopropylethyldiethoxylsilane, and mixtures thereof.

[0030] According to a less preferred embodiment of the present disclosure, the polymer backbone is derived exclusively from a polyol, preferably a polyether polyol or a polyester polyol. The polymer backbone may be end-capped with two or more terminal groups, such as hydroxyl groups, glycidyl groups, allyl groups, or combinations thereof. A hydrosilylation reaction may occur between the end groups of the polyol chain and the X group of the silanizing agent to form an SMP. A mechanistic scheme of the hydrosilylation reaction is shown in Figure 3, where the silanizing agent is SiH(OC2H5)3.

[0031] According to a preferred embodiment of the present disclosure, the polymer backbone is a polyurethane backbone derived from the reaction of a polyisocyanate with a polyol. The polymer backbone may be end-capped with two or more terminal groups, such as hydroxyl or isocyanate groups. A silylation reaction may occur between the end groups of the polyurethane chain and the X group of the silanizing agent to form an SMP.

[0032] According to one embodiment of the present disclosure, the molar content of the silanizing agent is selected such that the SMP has a silane functionality of 1.2-4.0, preferably 1.5-3.0, more preferably 1.8-2.5, and more preferably 2.0-2.2.

[0033] In general, the amount of SMP may vary based on the actual requirements of the resulting curable composition. As one illustrative embodiment, the content of SMP may be 10% to 90% by weight, or 10% to 85% by weight, or 10% to 80% by weight, or 10% to 75% by weight, or 10% to 70% by weight, or 20% to 65% by weight, or 30% to 60% by weight, or 40% to 58% by weight, or 50% to 56% by weight, or 52% to 55% by weight, based on the total weight of the curable composition.

[0034] Epoxy Resin In various embodiments of the present disclosure, component (B) comprises an epoxy resin having at least one, and preferably two, epoxy end groups.

[0035] An epoxy resin can be any polymeric material that contains epoxy functionality. Compounds that contain reactive epoxy functionality may vary widely and include polymers that contain epoxy functionality or blends of two or more epoxy resins. Epoxy resins can be saturated or unsaturated, aliphatic, cycloaliphatic, aromatic, or heterocyclic, and can be substituted. In some embodiments, an epoxy resin can include a polyepoxide. Polyepoxide refers to a compound or mixture of compounds that contain two or more epoxy moieties. Polyepoxides include partially advanced epoxy resins that are the reaction product of a polyepoxide with a chain extender, the reaction product having an average of two or more unreacted epoxide units per molecule. Aliphatic polyepoxides can be prepared from the reaction of epihalohydrins with polyglycols. Other specific examples of aliphatic epoxides include trimethylpropane epoxide, and diglycidyl-1,2-cyclohexanedicarboxylate. Other compounds include epoxy resins such as, for example, glycidyl ethers of polyhydric phenols (i.e., compounds having an average of two or more aromatic hydroxyl groups per molecule).

[0036] In one embodiment, the epoxy resins utilized in the curable compositions of the present disclosure include those resins produced from epihalohydrins and phenols or phenol-type compounds. Phenol-type compounds include compounds having an average of two or more aromatic hydroxyl groups per molecule. Examples of phenol-type compounds include dihydroxyphenols, biphenols, bisphenols, halogenated biphenols, halogenated bisphenols, hydrogenated bisphenols, alkylated biphenols, alkylated bisphenols, trisphenols, phenol-aldehyde resins, novolac resins (which are the reaction products of phenols and simple aldehydes, such as formaldehyde), halogenated phenol-aldehyde novolac resins, substituted phenol-aldehyde novolac resins, phenol-hydrocarbon resins, substituted phenol-hydrocarbon resins, phenol-hydroxybenzaldehyde resins, alkylated phenol-hydroxybenzaldehyde resins, hydrocarbon-phenol resins, hydrocarbon-halogenated phenol resins, hydrocarbon-alkylated phenol resins, or combinations thereof. Specifically, phenol-type compounds include resorcinol, catechol, hydroquinone, bisphenol A, bisphenol AP (1,1-bis(4-hydroxyphenyl)-1-phenylethane), bisphenol F, bisphenol K, tetrabromobisphenol A, phenol-formaldehyde novolac resins, alkyl-substituted phenol-formaldehyde resins, cresol-hydroxybenzaldehyde resins, dicyclopentadiene-phenolic resins, dicyclopentadiene-substituted phenolic resins, tetramethylbiphenol, tetramethyl-tetrabromobisphenol, tetramethyltribromobisphenol, and tetrachlorobisphenol A. In some embodiments, the epoxy resin of the composition may have a functionality of at least 1.5, at least 3, or even at least 6.

[0037] In some embodiments, the epoxy resins utilized in epoxy component (B) include those resins produced from epihalohydrins and amines. Suitable amines include diaminodiphenylmethane, aminophenol, xylylenediamine, aniline, or combinations thereof.

[0038] In some embodiments, epoxy resins utilized in the epoxy component include those resins produced from epihalohydrins and carboxylic acids. Suitable carboxylic acids include phthalic acid, isophthalic acid, terephthalic acid, tetrahydrophthalic acid and / or hexahydrophthalic acid, endomethylenetetrahydrophthalic acid, isophthalic acid, methylhexahydrophthalic acid, or combinations thereof.

[0039] In some embodiments, the epoxy resin is an advanced epoxy resin that is the reaction product of one or more epoxy resins, as described above, with one or more phenolic type compounds and / or one or more compounds having an average of two or more aliphatic hydroxyl groups per molecule. Alternatively, the epoxy resin may be a phenolic type compound having a hydrocarbon backbone, preferably C1-C 40 It may react with carboxyl-substituted hydrocarbons, which are compounds having a hydrocarbon backbone and one or more carboxyl moieties, preferably two or more, most preferably two. 40 The hydrocarbon backbone may be a straight or branched chain alkane or alkene, and optionally contains oxygen. Fatty acids and fatty acid dimers are among the useful carboxylic acid-substituted hydrocarbons. Fatty acids include caproic acid, caprylic acid, capric acid, octanoic acid, decanoic acid, lauric acid, myristic acid, palmitic acid, stearic acid, palmitoleic acid, oleic acid, linoleic acid, linolenic acid, erucic acid, pentadecanoic acid, margaric acid, arachidic acid, and dimers thereof.

[0040] In some embodiments, the epoxy resin is the reaction product of a polyepoxide and a compound containing two or more isocyanate moieties or polyisocyanates. For example, the epoxy resin produced in such a reaction can be an epoxy-terminated polyoxazolidone.

[0041] In one particular embodiment, the epoxy resin component is a blend of a brominated epoxy resin and a phenolic novolac epoxy resin.

[0042] According to various embodiments of the present application, the epoxy resin has a molecular weight of 100 to 20,000 grams per mole (g / mol), or 500 to 15,000 g / mol, or 800 to 12,000 g / mol, or 1,000 to 10,000 g / mol, or 2,000 to 9,000 g / mol, or 3,000 to 8,000 g / mol, or 4,000 to 7,000 g / mol, or 5,000 to 6,000 g / mol. According to various embodiments of the present application, the epoxy resin has an epoxy functionality of 1.2 to 10, or 2 to 9, or 3 to 8, or 4 to 7, or 5 to 6. In general, the amount of epoxy resin may vary based on the actual requirements of the resulting curable composition. For example, as one illustrative embodiment, the epoxy resin content can be 5 wt% to 70 wt%, or 7 wt% to 68 wt%, or 10 wt% to 65 wt%, or 11 wt% to 60 wt%, or 12 wt% to 50 wt%, or 14 wt% to 40 wt%, or 15 wt% to 30 wt%, or 17 wt% to 25 wt%, or 18 wt% to 22 wt%, based on the total weight of the curable composition.

[0043] Hardening Compatibilizer In the context of the present disclosure, a curing compatibilizer refers to a compound that has at least one silane group and at least two amine groups in the same molecule, and therefore can exhibit the functions of both a curing agent and a compatibilizer. According to the most preferred embodiment of the present application, the specifically defined curing compatibilizer is the only compound present in the curable composition that can achieve the functions of a curing agent and a compatibilizer, and the curable composition does not contain any additional curing agent or compatibilizer other than the curing compatibilizer.

[0044] According to one embodiment of the present disclosure, the curing compatibilizer is a compound represented by Formula II: [ka] In the formula, R 10 is selected from the group consisting of NH2(C1-C6 alkylene)-, (NH2)2CH-, (NH2)3C-, (NH2-C1-C6 alkylene)2CH-, (NH2-C1-C6 alkylene)3C-, (NH2)2CH(C1-C6 alkylene)-, (NH2)3C(C1-C6 alkylene)-, (NH2-C1-C6 alkylene)2CH(C1-C6 alkylene)-, and (NH2-C1-C6 alkylene)3C(C1-C6 alkylene)-; R 11 is selected from the group consisting of -(C1-C6 alkylene)-, -NH-(C1-C6 alkylene)-, -NH-NH-(C1-C6 alkylene)-, -NH-(C1-C6 alkylene)-NH-, -NH-(C1-C6 alkylene)-NH-(C1-C6 alkylene)-, and -NH-(C1-C6 alkylene)-NH-(C1-C6 alkylene)-NH-; R 12 and R 13each independently represents a hydrogen atom or a C1-C6 alkyl group optionally substituted with a C1-C6 alkyl group, a C1-C6 alkoxy group, a halogen atom, a C2-C6 alkenyl group, a C2-C6 alkynyl group, -Si(C1-C4 alkyl), -Si(C1-C4 alkoxy), -Si-{O-[Si(C1-C4 alkoxy)], -(C1-C6)alkylene-Si(C1-C4 alkyl), -(C1-C6)alkylene-Si(C1-C4 alkoxy), or -(C1-C6)alkylene-Si-{O-[Si(C1-C4 alkoxy)]; and t represents an integer of 0, 1, or 2, provided that at least two nitrogen atoms are present in the compound represented by formula II. It is of particular note that the curing compatibilizer may contain at least two primary amine groups, or at least two secondary amine groups, or one or more primary amine groups and at least one secondary amine group, or a combination thereof.

[0045] According to certain embodiments of the present disclosure, the curing compatibilizer comprises: [ka] is selected from the group consisting of:

[0046] In one illustrative embodiment, the content of the curable compatibilizer represented by Formula II is 4.8 wt% to 20 wt%, or 5 wt% to 18 wt%, or 6 wt% to 16 wt%, or 6.5 to 14 wt%, or 6.8 wt% to 12 wt%, or 7 wt% to 10 wt%, or 7.5 wt% to 9 wt%, or 7.8 wt% to 8.8 wt%, or 8 wt% to 8.5 wt%, based on the total weight of the curable composition.

[0047] The curing compatibilizer can either be provided and delivered as a separate component from components A and B, or can be contained in components A or B. According to a preferred embodiment of the present disclosure, the curing compatibilizer is contained in component A, i.e., as a blend with the SMP.

[0048] According to a preferred embodiment of the present disclosure, the amounts of SMP, epoxy resin, and curing compatibilizer are specifically selected such that the molar ratio of total epoxy functionality to total amine functionality can range from 1:0.95 to 0.95:1, and the molar ratio of SMP resin to epoxy resin is from 10:1 to 1:3.

[0049] Additives In various embodiments of the present disclosure, the curable composition may further include one or more additives selected from the group consisting of catalysts; moisture scavengers such as vinyl-Si[O-(C1-C4) alkyl]; chain extenders; crosslinkers; tackifiers; plasticizers such as phthalates, non-aromatic dibasic esters and phosphates, polyesters of dibasic acids with dihydric alcohols, polypropylene glycol and its derivatives, polystyrene; rheology modifiers, antioxidants; fillers such as calcium carbonate, kaolin, talc, silica, titanium dioxide, aluminum silicate, magnesium oxide, zinc oxide, and carbon black; colorants; pigments; surfactants; solvents such as hydrocarbons, acetates, alcohols, ethers, and ketones; diluents; flame retardants; anti-slip agents; antistatic agents; preservatives; biocides; UV stabilizers; thixotropic agents; anti-sagging agents such as hydrogenated castor oil, organic bentonite, calcium stearate, and combinations of two or more thereof. These additives are used in known manners and amounts. These additives may be delivered and stored as separate components and incorporated into the polyurethane composition shortly before or immediately before the combination of components (A) and (B). Alternatively, these additives may be contained in either component (A) or (B) if they are chemically inert toward reactive groups such as epoxy groups, amino groups, and silane groups.

[0050] The above-mentioned catalyst refers to a catalytic material that can further accelerate or enhance the interaction between reactive groups such as epoxy groups, amino groups, and silane groups. It is also known as a curing catalyst, and can be used independently or in combination of two or more species. Representative catalysts include dibutyltin dilaurate, dibutyltin acetoacetate, titanium acetoacetate, titanium ethyl acetoacetate complex and tetraisopropyl titanate, bismuth carboxylate, zinc octoate, blocked tertiary amine, zirconium complex, and combinations of tin compositions and silicic acid amine catalysts and Lewis acid catalysts.

[0051] According to a preferred embodiment of the present disclosure, the curable composition of the present disclosure comprises 30 wt% or less of plasticizer, or less than 28 wt%, or less than 25 wt%, or less than 24 wt%, or less than 20 wt%, or less than 18 wt%, or less than 15 wt%, or less than 12 wt%, or less than 10 wt%, or less than 8 wt%, or less than 5 wt%, or less than 2 wt%, based on the total weight of the curable composition. According to another preferred embodiment of the present disclosure, the curable composition of the present disclosure comprises 15 wt% or less of filler, or less than 12 wt%, or less than 10 wt%, or less than 8 wt%, or less than 6 wt%, or less than 4 wt%, or less than 2 wt%, based on the total weight of the curable composition. According to another preferred embodiment of the present disclosure, the curable composition of the present disclosure does not comprise a hydroxyl silane compound. According to various aspects of the present application, improved adhesive strength is successfully achieved while maintaining elongation ratio.

[0052] Once combined, the silane modified polymer, epoxy resin, and cured compatibilizer react with each other and gradually cure to form the target layer or structure. The curing process may be carried out at a temperature of, for example, 0°C or more, preferably 20°C or more, more preferably 60°C or more, and most preferably 80°C or more, while at the same time, 300°C or less, preferably 250°C or less, more preferably 200°C or less, and most preferably 180°C or less. The curing process may be carried out at a pressure of, for example, desirably 0.01 bar or more, preferably 0.1 bar or more, more preferably 0.5 bar or more, while at the same time, desirably 1000 bar or less, preferably 100 bar or less, and more preferably 10 bar or less. The curing process may be carried out for a predetermined time sufficient to cure the SMP-epoxy composition. For example, the curing time may be desirably 1 minute or more, preferably 10 minutes or more, more preferably 100 minutes or more, while at the same time, desirably 24 hours or less, preferably 12 hours or less, and more preferably 8 hours or less.

[0053] The uncured blend of components A and B may be applied to one or more substrates by a batch or continuous process. The uncured blend may be applied by techniques such as gravity casting, vacuum casting, automated pressure gelling (APG), vacuum pressure gelling (VPG), injection, filament winding, infusion (e.g., lay-up injection), transfer molding, preprelling, dipping, coating, potting, encapsulation, spraying, brushing, and the like. EXAMPLES

[0054] Some embodiments of the present invention will now be described in the following examples. However, the scope of the present disclosure is of course not limited to the formulations described in these examples. Rather, the examples simply relate to the invention of the present disclosure.

[0055] Information on the raw materials used in the examples is listed in Table 1 below. [Table 1]

[0056] Preparation Example: Preparation of SMP Voranol™ 4000LM (4000 g) was added to a N2-protected three-neck flask at room temperature and heated to 110° C. under a nitrogen stream. o The flask was heated at 80°C for 4 hours. o After cooling to 30° C., T12 (2.0 g) and IPDI (296.4 g) were added thereto, and the flask was heated to 80° C. o C for 4 hours. SCA-3303 (156.93 g) was then added to the flask and the mixture was heated at 80 o C for 4 h. After reaction, the resulting SMP was transferred into a sealed bottle for further characterization, formulation, and testing.

[0057] Comparative Examples 1-3, 5-6, 14-15 and Inventive Examples 4, 7-13, and 16 Different two-part curable compositions were prepared according to the formulations listed in Table 2, where Examples 1-3, 5-6, 14-15 are comparative examples that do not contain a curing compatibilizer specifically selected according to the present disclosure, and the SMP resins were prepared in the preparation examples described above.

[0058] As can be seen from Table 2, Part A contains SMP resin, hardening compatibilizer (or hardener in comparative example), and moisture scavenger, and optionally further contains plasticizer and filler, and Part B contains epoxy resin and tin catalyst. Part A and Part B were prepared separately by mixing the ingredients in separate speed mixers at a stirring speed of 2,000 rpm / min. Part A and Part B were combined and thoroughly mixed in a speed mixer at a stirring speed of 1,000 rpm / min for 20 seconds and 1,500 rpm / min for 20 seconds, then further mixed in a vacuum mixer with a pressure of 0.2 KPa at 1,000 rpm / min for 2 minutes, and finally mixed in a speed mixer at 2,000 rpm / min for 20 seconds. After the above mixing steps, the resulting blends were directly characterized or applied onto the surface of a substrate to produce film samples.

[0059] The samples prepared in the examples were characterized by the following techniques.

[0060] A. The SMPs prepared in the above preparation examples were analyzed using an Agilent 1200 model chromatograph equipped with two mixed D columns (7.8x300mm) and an Agilent refractive index detector, with the column temperature at 35°C and the detector temperature at 35°C. o It was characterized by gel permeation chromatography (GPC) using the following conditions and parameters: C, flow rate of 1.0 mL / min, mobile phase of tetrahydrofuran, injection volume of 50 μL, and detection data were collected and analyzed using Agilent GPC software based on a calibration curve obtained using narrow standards of PL polystyrene with molecular weights ranging from 316,500 to 316,580 g / mol (product no. 2010-0101).

[0061] The Mn of the SMP was measured to be 21,662 and the Mw to be 41,081, so the PDI can be calculated to be 1.90.

[0062] B. The mechanical properties of the samples prepared in Examples 1-17 were characterized according to ASTM D1708-06A. The cured films of any of the Examples were die-cut into dog-bone shaped specimens according to the procedure introduced in ASTM D1708-06A. The specimens were clamped in an Instron 5566 instrument and elongated at a constant rate of 50 mm / min. The load at yield point (if any), the maximum load carried by the specimen during the test, the load at break, and the elongation at the moment of break (elongation between grips) were recorded. The shear strength of the specimens was also measured with an Instron 5566 instrument using a bonded area of ​​2.5 cm x 2.5 cm. The measurement results are also summarized in Table 2. [Table 2] [Table 3] [Table 4]

[0063] Comparison of the comparative examples with the inventive examples shows that the introduction of the hardening compatibilizer can significantly improve various mechanical properties such as modulus (up to 2.8 MPa), shear strength up to 7.4 MPa, which can be attributed to the chemical bond formation between the epoxy and SMP resin. The relative amounts of filler and plasticizer added to the formulation can be further adjusted to achieve high shear strength up to 8.4 MPa.

[0064] On the contrary, the comparative examples do not contain specially designed curing compatibilizers and exhibit very similar adhesive strength to most commercially available SMP-based adhesives, and such low adhesion cannot fully meet the requirements of many customers in household products.As introduced in the previous paragraph, household product adhesives need to have adhesive strength of more than 5.0 MPa while retaining about 100% elongation at break so that thinner frame areas can be achieved.Some industrial assembly customers also often require SMP adhesives with higher adhesive strength to typical substrates such as galvanized steel and stainless steel.

Claims

1. 1. A curable composition comprising: at least one silane-modified polymer; at least one epoxy resin terminated with an epoxy group; Including, the curable composition further comprises a curing compatibilizer having at least one silane group and at least two amine groups in the same molecule; the curable composition does not contain any additional curing or compatibilizing agents other than the curing compatibilizing agent; The curable composition is a two-component curable composition including a component A and a component B, the silane-modified polymer and the curing compatibilizer are contained in the component A, and the epoxy resin is contained in the component B; further comprising, or not comprising, up to 15 wt. % of a filler, based on the weight of the curable composition; further comprising or not comprising 30% by weight or less of a plasticizer, based on the weight of the curable composition; The silane-modified polymer is represented by the following formula I: R １ ｍ (R ２ O) （３－ｍ） Si-R ７ -(polymer main chain) -R ８ -SiR ３ ｎ (R ４ O) （３－ｎ） Formula I wherein the polymer backbone is derived from at least one polyisocyanate and at least one polyol, and optionally, at least one -R ９ -SiR ５ ｓ (R ６ O) （３－ｓ） and functionalized with R １ , R ２ , R ３ , R ４ , R ５ , and R ６ Each of the is independently a hydrogen atom or C １ -C ６ each of m, n, and s represents an integer of 0, 1, or 2; R ７ , R ８ , and R ９ Each of is independently a direct bond, —O—, a divalent (C １ ~C ６ alkylene) group, —O—(C １ ~C ６ alkylene) group, (C １ ~C ６ alkylene)-O- group, -O-(C １ ~C ６ alkylene)-O- group, -N(R Ｎ )-(C １ ~C ６ alkylene) group, or -C(=O)-N(R Ｎ )-(C １ ~C ６ alkylene) group, R Ｎ is a hydrogen atom or C １ -C ６ represents an alkyl group, The curing compatibilizer is a compound represented by the following formula II: 【Chemistry 1】 wherein R 10 is selected from the group consisting of NH 2 (C 1 -C 6 alkylene)-, (NH 2 ) 2 CH-, (NH 2 ) 3 C-, (NH 2 -C 1 -C 6 alkylene) 2 CH-, (NH 2 -C 1 -C 6 alkylene) 3 C-, (NH 2 ) 2 CH(C 1 -C 6 alkylene)-, (NH 2 ) 3 C(C 1 -C 6 alkylene)-, (NH 2 -C 1 -C 6 alkylene) 2 CH(C 1 -C 6 alkylene)-, and (NH 2 -C 1 -C 6 alkylene) 3 C(C 1 -C 6 alkylene)-; R 11 is selected from the group consisting of -(C 1 -C 6 alkylene)-, -NH-(C 1 -C 6 alkylene)-, -NH-NH-(C 1 -C 6 alkylene)-, -NH-(C 1 -C 6 alkylene)-NH-, -NH-(C 1 -C 6 alkylene)-NH-(C 1 -C 6 alkylene)- and -NH-(C 1 -C 6 alkylene)-NH-(C 1 -C 6 alkylene)-NH-; Each of R 12 and R 13 is independently a hydrogen atom, a C 1 -C 6 alkyl group, a C 1 -C 6 alkoxy group, a halogen atom, a C 2 -C 6 alkenyl group, a C 2 -C 6 alkynyl group, -Si(C 1 -C 4 alkyl) 3 , -Si(C 1 -C 4 alkoxy) 3 , -Si-{O-[Si(C 1 -C 4 alkoxy) 3 ] 3 , -(C 1 -C 6 )alkylene-Si(C 1 -C 4 alkyl) 3 , -(C 1 -C 6 )alkylene-Si(C 1 -C 4 alkoxy) 3 , or -(C 1 -C 6 )alkylene-Si-{O-[Si(C 1 -C 4 alkoxy) 3 ] represents a C 1 -C 6 alkyl group optionally substituted with 3; t represents an integer of 0, 1, or 2; provided that there are at least two nitrogen atoms in said compound of formula II, A curable composition, wherein the content of the curable compatibilizer represented by formula II is 4.8% by weight to 20% by weight based on the total weight of the curable composition (wherein the general formula (1): -Si(R １ ) ３－ａ (X) ａ (1) (wherein, R １ each independently represents a hydrocarbon group having 1 to 20 carbon atoms, the hydrocarbon group may have a hetero-containing group, each X independently represents a hydroxyl group or a hydrolyzable group, and a is 1, 2, or 3.) and the atom adjacent to the reactive silicon group has an unsaturated bond.

2. The curing compatibilizer is 【Chemistry 2】 The curable composition of claim 1 selected from the group consisting of:

3. the polymer backbone is derived from at least one polyisocyanate and at least one polyol; The polyisocyanate contains at least two isocyanate groups. ４ -C １２ Aliphatic polyisocyanates, C containing at least two isocyanate groups ６ -C １５ Alicyclic or aromatic polyisocyanates, C containing at least two isocyanate groups ７ -C １５ araliphatic polyisocyanates, and any combination thereof; The polyol comprises at least two hydroxyl groups. ２ -C １６ Aliphatic polyhydric alcohols, C containing at least two hydroxyl groups ６ -C １５ Alicyclic or aromatic polyhydric alcohols, C containing at least two hydroxyl groups ７ -C １５ 2. The curable composition of claim 1, wherein the curable composition is selected from the group consisting of araliphatic polyhydric alcohols, polyester polyols having a molecular weight of 100 to 5,000 and an average hydroxyl functionality of 1.5 to 5.0, polyether polyols having a molecular weight of 100 to 5,000 and an average hydroxyl functionality of 1.5 to 5.0, and combinations thereof.

4. The epoxy resin is glycidyl ethers of ethylene glycol, propylene glycol, butylene glycol, hexanediol, octanediol, polypropylene glycol, dimethylolcyclohexane, neopentyl glycol, dibromoneopentyl glycol, castor oil, trimethylolpropane, trimethylolethane, pentaerythritol, sorbitol or glycerol, or alkoxylated glycerol or alkoxylated trimethylolpropane, glycidyl ethers of hydrogenated bisphenol A, F or A / F or ring-hydrogenated liquid bisphenol A, F or A / F resins; 2. The curable composition of claim 1, wherein the glycidyl ether is selected from the group consisting of bisphenol A resins, bisphenol AP resins, bisphenol F resins, bisphenol K resins, phenol-formaldehyde novolac resins, alkyl substituted phenol-formaldehyde resins, cresol-hydroxybenzaldehyde resins, dicyclopentadiene-phenolic resins, dicyclopentadiene substituted phenolic resins, and combinations thereof.

5. 2. The curable composition of claim 1, wherein the silane-modified polymer comprises 10 to 90 weight percent of the curable composition, and the epoxy resin comprises 5 to 70 weight percent of the curable composition.

6. A method for applying the curable composition according to any one of claims 1 to 5 onto a surface of a substrate, comprising the steps of: (1) combining the silane modified polymer, the epoxy resin, and the curing compatibilizer to form a precursor blend; (2) applying the precursor blend onto a surface of a substrate; (3) curing the precursor blend or allowing the precursor blend to cure.