Tape for semiconductor processing and method for manufacturing semiconductor chips

Abstract

To provide a tape for semiconductor processing, enabling to be removed by washing with unheated water while achieving both grooving resistance and wafer adhesion, and a method for manufacturing a semiconductor chip, in which the tape for semiconductor processing is used.SOLUTION: There are provided: a tape 3 for semiconductor processing in which a water-soluble film 5 and a surface protection tape 4 for protecting a circuit surface 1A of a semiconductor wafer 1 are laminated, the water-soluble film containing a high-molecular compound with a weight average molecular weight of 200,000 or more and a low-molecular compound with a molecular weight of 800 or less; and a method for manufacturing a semiconductor chip, in which the tape for semiconductor processing is used. The method for manufacturing a semiconductor chip includes the steps of: cutting a water-soluble film in a tape for semiconductor processing along a planned cutting area of a semiconductor wafer to form a groove, the water-soluble film being bonded on a circuit surface of the semiconductor wafer under unheated conditions; subjecting the semiconductor wafer to plasma processing; and washing, with unheated water, the water-soluble film having been cut.SELECTED DRAWING: Figure 2

Description

[Technical field]

[0001] The present invention relates to a tape for semiconductor processing and a method for manufacturing semiconductor chips. [Background technology]

[0002] In recent years, semiconductor chips have been rapidly becoming thinner and smaller. In particular, IC cards with built-in semiconductor IC chips, such as memory cards and smart cards, require semiconductor chips to be 75μm thick or less. Chips for LED and LCD driving devices are becoming smaller, with chips measuring 0.5mm x 0.5mm or less now available. As demand for these devices increases in the future, the need for thinner and smaller semiconductor chips is expected to grow even further. Conventionally, semiconductor chips have been manufactured by a method in which a semiconductor wafer is thinned to a predetermined thickness in a back grinding process, an etching process, or the like, and then chipped in a dicing process. In this dicing process, a blade cut method is generally used in which the semiconductor wafer is cut by a dicing blade. In this case, the cutting resistance of the blade acts directly on the semiconductor wafer during cutting, and this cutting resistance may cause minute chipping in the semiconductor chip. This chipping not only damages the appearance of the semiconductor chip, but may also damage the circuit pattern on the chip in some cases. In particular, the allowable chipping level is becoming stricter for the above-mentioned thinned or small-sized semiconductor chips, so the problem of chipping will become even more serious in the future. In addition, the blade cut method has a relatively large blade width (also called a street or scribe line), which causes a problem in that the semiconductor wafer cannot be used efficiently.

[0003] The occurrence of the above-mentioned chipping is regarded as one of the important problems to be solved, and various techniques for preventing the occurrence of chipping have been investigated. For example, a laser dicing method in which a semiconductor wafer is cut by irradiating a laser, and a pre-dicing method in which a half cut with a blade or modification with a laser is performed prior to a back-grinding process, and individualization is performed in parallel with the back-grinding process have been proposed. In such dicing methods, it is known that thermal decomposition products of the semiconductor wafer (e.g., silicon residues) generated by laser irradiation remain or accumulate on the semiconductor wafer, resulting in defects. Sheets and the like that protect the semiconductor wafer from heat caused by laser irradiation while suppressing the remaining or accumulation of such thermal decomposition products have been proposed. For example, Patent Document 1 describes "a protective sheet for laser dicing, comprising a base sheet and, on the upper surface of the base sheet," "(A) a water-soluble polymer and (B) a crosslinking agent, the weight-average molecular weight (Mw) of the water-soluble polymer (A) being 10,000 to 150,000," and "a protective layer formed by applying a protective film composition for laser dicing, the thickness of the protective layer being 100 to 5,000 nm." However, even with the above-mentioned dicing method, the semiconductor wafer must ultimately be physically split in order to be divided into individual pieces, and the occurrence of chipping cannot be effectively suppressed.

[0004] Also, a plasma dicing method has been proposed in which a semiconductor wafer is cut by spraying plasma-converted fluorine gas. The plasma dicing method can effectively suppress the occurrence of chipping because the semiconductor wafer can be divided into individual pieces by irradiating plasma. Moreover, the plasma dicing method can form streets with small widths and high linearity, so that the semiconductor wafer can be efficiently utilized, and its advantages are great. For example, Patent Document 2 describes a protective sheet used in the plasma dicing method as "a film in which a surface protective tape and a water-soluble film are laminated via an ultraviolet-curable adhesive layer, the water-soluble film being formed by partial saponification of a water-soluble polymer, and being insoluble in water at room temperature but soluble in warm water at 60°C to 100°C." [Prior art documents] [Patent documents]

[0005] [Patent Document 1] Patent No. 6055494 [Patent Document 2] JP 2010-165963 A Summary of the Invention [Problem to be solved by the invention]

[0006] However, when applying the plasma dicing method, as in Patent Document 2, a mask member is required to protect portions of the semiconductor wafer other than the streets from plasma, in addition to the surface protection tape that is peeled off after the backgrinding process. The mask member arranged on the semiconductor wafer is removed only in the area to be cut (the part located on the street) by the grooving process, which allows the plasma to be irradiated (exposed) to the streets of the semiconductor wafer. Therefore, the mask member used in the plasma dicing method is required to have grooving resistance (heat resistance) so that it is not easily deformed by the grooves that form the streets. However, when the mask member is formed from a material with high heat resistance to realize grooving resistance, there is generally a trade-off problem in that the adhesion to the semiconductor wafer and further the removability by water washing, which will be described later, are reduced.

[0007] In addition, the mask member used in the plasma dicing method needs to be removed after the dicing process is completed. For example, Patent Document 2 describes that the film can be removed by washing with hot water by making the film soluble in hot water. However, the film described in Patent Document 2 requires a process of heating to 60 to 100°C when attaching the water-soluble film and when removing the water-soluble film, which makes the work complicated.

[0008] The present invention aims to provide a semiconductor processing tape that can be removed by washing with non-heated water while achieving both grooving resistance and wafer adhesion, and also aims to provide a method for easily manufacturing semiconductor chips using the semiconductor processing tape. [Means for solving the problem]

[0009] The present inventors have conducted intensive studies in view of the above problems, and have found that a water-soluble film containing a polymeric compound having a weight-average molecular weight of 200,000 or more and a low molecular compound having a molecular weight of 800 or less is used as a plasma dicing mask, and is laminated and integrated with a surface protection tape that protects the circuit surface of a semiconductor wafer in a back grinding process to form a semiconductor processing tape, thereby enabling washing and removal with non-heated water while achieving both grooving resistance and wafer adhesion. In addition, the inventors have found that by using this semiconductor processing tape in a semiconductor chip manufacturing method including a plasma dicing process, semiconductor chips can be easily manufactured. The present invention has been completed based on these findings and further studies.

[0010] The above object of the present invention is achieved by the following means. <1> A semiconductor processing tape that is a laminate of a water-soluble film containing a polymeric compound with a weight-average molecular weight of 200,000 or more and a low molecular weight compound with a molecular weight of 800 or less, and a surface protection tape that protects the circuit surface of a semiconductor wafer. <2> The absorbance of the water-soluble film with respect to electromagnetic waves having a wavelength of 355 nm is 30% or more. <1> The semiconductor processing tape according to claim 1. <3> The peel strength between the water-soluble film and the surface protection tape is 1 N / 25 mm or less. <1> or <2> The semiconductor processing tape according to claim 1. <4> The thickness of the water-soluble film is 20 μm or less. <1> ~ <3> 13. The tape for semiconductor processing according to claim 12 . <5> In the water-soluble film, the content of the low molecular weight compound is 10 to 100 parts by mass per 100 parts by mass of the high molecular weight compound. <1> ~ <4> 13. The tape for semiconductor processing according to claim 12 . <6> the above <1> ~ <5> A step (a) of grinding the back surface of a semiconductor wafer in which the water-soluble film in the semiconductor processing tape according to any one of the above items is laminated to the circuit surface of the semiconductor wafer without heating; (b) supporting and fixing the semiconductor wafer to a dicing tape via a ring frame; a step (c) of peeling a surface protection tape of the semiconductor processing tape from the water-soluble film to expose the water-soluble film; (d) cutting the water-soluble film along a region to be cut of the semiconductor wafer to provide a groove; (e) subjecting the semiconductor wafer to a plasma treatment from the cut water-soluble film side to separate the semiconductor wafer; (f) a step of washing the cut water-soluble film with non-heated water to dissolve and remove it; A method for manufacturing a semiconductor chip comprising the steps of: <7> The step (d) is a step of cutting the water-soluble film by laser irradiation. <6> A method for manufacturing a semiconductor chip according to claim 1. Effect of the Invention

[0011] The present invention can provide a semiconductor processing tape that can be removed by washing with non-heated water while achieving both grooving resistance and wafer adhesion. The present invention can also provide a method for easily manufacturing semiconductor chips using the semiconductor processing tape. [Brief description of the drawings]

[0012] [Figure 1] FIG. 1 is a schematic longitudinal sectional view showing a preferred embodiment of the semiconductor processing tape of the present invention. [Diagram 2] FIG. 2 is a schematic vertical cross-sectional view illustrating step (a) in the method for producing a semiconductor chip of the present invention. [Diagram 3] FIG. 3 is a schematic vertical cross-sectional view illustrating steps (b) to (d) in the method for producing a semiconductor chip of the present invention. [Figure 4] FIG. 4 is a schematic vertical cross-sectional view illustrating steps (e) and (f) and a pick-up step in the method for producing a semiconductor chip of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0013] In the present invention, a numerical range expressed using "to" means a range including the numerical values ​​before and after "to" as the lower and upper limits. In the present invention, the term "(meth)acrylic" refers to either or both of acrylic and methacrylic. The same applies to (meth)acrylate.

[0014] [Tape for semiconductor processing] The semiconductor processing tape of the present invention is a laminated tape having a water-soluble film and a surface protection tape, and is preferably used in the manufacturing method of semiconductor chips, focusing on the water-soluble film, in step (e) (plasma dicing step) described below. Therefore, the semiconductor processing tape of the present invention can also be called a semiconductor wafer processing tape. This semiconductor processing tape has a layered structure in which a water-soluble film containing a polymeric compound with a weight-average molecular weight of 200,000 or more and a low-molecular compound with a molecular weight of 800 or less is laminated and integrated with a surface protection tape that protects the circuit surface of a semiconductor wafer. Because this semiconductor processing tape is integrated with the surface protection tape and the water-soluble film, when used in a semiconductor chip manufacturing method, the surface protection tape and the water-soluble film can be attached to the semiconductor wafer at the same time, improving work efficiency. The semiconductor processing tape of the present invention may have the above-mentioned configuration, and other configurations are not particularly limited. For example, the water-soluble film and / or the surface protection tape may have a protective layer on the surface. In addition, the water-soluble film, the surface protection tape, and other films or layers may have a single-layer structure or a multi-layer structure of two or more layers. A semiconductor processing tape 3, which is a preferred embodiment of the present invention, has a three-layer structure in which a surface protection tape 4 including a base film 4A and an adhesive layer 4B and a water-soluble film 5 are laminated in contact with each other via the adhesive layer 4B, as shown in FIG.

[0015] In the semiconductor processing tape of the present invention, the total thickness and the thickness of each layer are appropriately set according to the application, etc. For example, the total thickness of the semiconductor processing tape (total thickness of each layer) can be 100 to 800 μm.

[0016] The semiconductor processing tape of the present invention is usually in the form of a long strip, but can also be in the form of a strip, sheet, string, or other suitable shape depending on the application, etc., and can also be in a suitable shape for the semiconductor wafer to be bonded. The length and width of the semiconductor processing tape are appropriately set, and as an example, the length can be 20 m or more, and the width can be 200 to 400 mm. The semiconductor processing tape can be produced, for example, by preparing a water-soluble film and a surface protection tape, laminating them together, and adhering them with an adhesive layer.

[0017] In the semiconductor processing tape having the above layer structure, the peeling force (180° peeling force at 23° C.) between the water-soluble film and the surface protection tape (the adhesive layer if the surface protection tape has an adhesive layer) is set to such an extent that the adhesion is maintained and the surface protection tape does not peel off in the step (a) of grinding the back surface of the semiconductor wafer, and the surface protection tape can be easily peeled off from the water-soluble film before the step (d) of providing a groove in the water-soluble film. This peeling force is not uniquely determined, but from the viewpoint of the peelability of the surface protection tape from the water-soluble film, the upper limit is, for example, preferably 2N / 25mm or less, more preferably 1N / 25mm or less, and even more preferably 0.5N / 25mm or less. On the other hand, from the viewpoint of the adhesion in the grinding step, the lower limit is, for example, preferably more than 0.1N / 25mm, and more preferably 0.2N / 25mm or more. The peeling force is a value measured by a measurement method described in the examples. When the adhesive layer of the surface protection tape contains a radiation-curable adhesive, it is preferable that the adhesive layer before curing has a peel force that satisfies, for example, the above-mentioned lower limit and adheres firmly to the water-soluble film, while the adhesive layer after curing has a peel force that satisfies, for example, the above-mentioned upper limit. A water-soluble film having the above composition usually exhibits a peel strength of 0.1 N / 25 mm against the adhesive layer of a surface protection tape, and this peel strength can be appropriately adjusted by changing the composition of the water-soluble film or the adhesive layer.

[0018] (Water-soluble film) The water-soluble film is for forming a mask pattern used in the plasma treatment step in the semiconductor chip manufacturing method of the present invention, and is resistant to plasma using, for example, fluorine-based gas. This water-soluble film contains a polymeric compound with a weight-average molecular weight of 200,000 or more and a low molecular compound with a molecular weight of 800 or less, and also exhibits water solubility. The water solubility of the water-soluble film may be such that it dissolves in non-heated water (usually pure water), for example, water below 60°C, preferably water below 40°C. The lower limit of the water temperature is not particularly limited, but it can usually be 15°C, preferably 20°C. This water solubility is specifically such that, in the water washing removability test in the examples, the water-soluble film dissolves in water and can be removed without leaving any adhesive residue. When a semiconductor processing tape having such a water-soluble film exhibiting water solubility is used in a semiconductor chip manufacturing method having a plasma dicing step, it can be easily removed after the dicing step while maintaining the property of forming a predetermined mask and protecting the parts of the semiconductor wafer (circuit surface) other than the streets from plasma. This water-soluble film is a film in which a high molecular weight compound and a low molecular weight compound are mixed, and is generally a non-cured film in which these compounds do not cure (crosslink).

[0019] The polymer compound contained in the water-soluble film is usually a polymer, preferably a water-soluble polymer. The water solubility of the water-soluble polymer is not particularly limited as long as the water-soluble film can exhibit the above water solubility. The polymer compound is not particularly limited, but preferably, water-soluble polymers such as polyvinyl alcohol, polyethylene glycol, polyethylene oxide, polyvinylpyrrolidone, and poly(2-ethyl-2-oxazoline) can be used. Polyvinyl alcohol may be saponified depending on the water solubility required for the water-soluble film. The polymer as the polymer compound is usually used as a non-crosslinked body, and thus exhibits sufficient water solubility in non-heated water. The weight-average molecular weight of the polymer compound is 200,000 or more. By setting the weight-average molecular weight of the polymer compound used in combination with the low molecular weight compound to 200,000 or more, the water-soluble film can be given grooving resistance, wafer adhesion, and water-rinsing removability. The weight-average molecular weight of the polymer compound is preferably 200,000 to 3,000,000, more preferably 300,000 to 2,000,000, and even more preferably 300,000 to 1,000,000, in order to achieve a good balance between grooving resistance, wafer adhesion, and water-rinsing removability at a high level. The weight-average molecular weight of the polymer compound is a value measured by the method described in the examples. When the polymer compound (polymer) is specified by the degree of polymerization, it can be, for example, 200 to 10,000, although it depends on the molecular weight of each component constituting the polymer compound.

[0020] The low molecular weight compound contained in the water-soluble film is preferably a low molecular weight polymer, more preferably a water-soluble low molecular weight polymer. The water solubility of the water-soluble low molecular weight polymer is not particularly limited as long as the water-soluble film can exhibit the above water solubility. The low molecular weight compound is not particularly limited, but preferably polyvinyl alcohol and polyethylene glycol can be used. In terms of water solubility, it is preferable that the low molecular weight compound is a compound that does not undergo a chemical reaction such as a crosslinking reaction with the polymer compound. The molecular weight of the low molecular weight compound (weight average molecular weight in the case of a polymer) is 800 or less. By making the molecular weight of the low molecular weight compound used in combination with the polymer compound 800 or less, it is possible to impart grooving resistance, wafer adhesion and water-rinsing removability to the water-soluble film. The molecular weight of the low molecular weight compound is preferably 100 to 800, more preferably 200 to 800, even more preferably 200 to 600, and particularly preferably 450 to 600, in order to achieve a good balance between grooving resistance, wafer adhesion and water-rinsing removability at a high level. The weight average molecular weight of the low molecular weight compound (polymer) is a value measured by the same method as the weight average molecular weight of the polymer compound. In addition, when the low molecular weight compound (polymer) is specified by the degree of polymerization, it can be, for example, 5 to 20, although it depends on the molecular weight of each component constituting the low molecular weight compound.

[0021] The content of the polymeric compound and the low molecular compound in the water-soluble film is not particularly limited and is appropriately determined. For example, the total content of the polymeric compound and the low molecular compound in the water-soluble film is preferably 40 to 100 mass%, more preferably 60 to 100 mass%. The content of the low molecular compound is preferably 10 to 100 mass parts, more preferably 20 to 50 mass parts, relative to 100 mass parts of the polymeric compound. When the content of the low molecular compound is 10 parts by mass or more, the adhesion to the semiconductor wafer is strong, and peeling of the water-soluble film can be effectively suppressed in the step (a) of grinding the back surface of the semiconductor wafer and the step (d) of providing a groove. On the other hand, when the content is 100 parts by mass or less, deformation of the water-soluble film can be effectively suppressed in the step (d) of providing a groove, and the linearity of the region to be cut can be improved in the subsequent step (e) of dividing into individual pieces.

[0022] The water-soluble film may contain compounds other than the polymeric compounds and the low molecular compounds, such as ultraviolet absorbers, radical initiators, surfactants, labeling materials, and silane coupling agents. The ultraviolet absorbing agent can be any known agent without any particular limitation. The content of the ultraviolet absorbing agent in the water-soluble film is appropriately determined according to the absorbance of the water-soluble film. For example, the content can be 0.5 to 15% by mass, and preferably 1 to 13% by mass, based on 100 parts by mass of the polymer compound. In one preferred embodiment, the water-soluble film of the present invention does not contain a crosslinking agent, a crosslinking assistant, a radical initiator, etc. that crosslinks with a polymeric compound and / or a low molecular compound.

[0023] The absorbance of the water-soluble film for electromagnetic waves with a wavelength of 355 nm is not particularly limited, but when the semiconductor processing tape is applied to the step (d) of forming a groove by laser irradiation, the absorbance is preferably 30% or more, more preferably 50% or more, in terms of excellent groove forming ability by laser irradiation. The absorbance of the water-soluble film can be appropriately adjusted by a known ultraviolet absorbent and its content, etc., and the measurement method is the method described in the Examples. Examples of the ultraviolet absorbent include benzophenone, benzotriazole, and hydroxyphenyltriazine, and benzotriazole and hydroxyphenyltriazine are preferred from the viewpoint of energy absorption efficiency. In the present invention, the electromagnetic wave refers to electromagnetic waves among the radiation described later, and includes, for example, infrared rays, visible light, ultraviolet rays, X-rays (X-rays), and gamma rays (γ-rays).

[0024] The thickness of the water-soluble film is not particularly limited, and is appropriately determined in consideration of removability by washing with water, conditions of step (f), grooving resistance, and further suppression of edge dissolution (seapaging) in step (a) of grinding the back surface. For example, it can be 1 to 100 μm, and is preferably 20 μm or less, more preferably 5 to 20 μm, and even more preferably 5 to 10 μm, in terms of excellent suppression of the occurrence of seapage while maintaining removability by washing with water and grooving resistance.

[0025] (Surface protection tape) The surface protection tape may be any tape that is commonly used in the manufacturing method of semiconductor chips, without any particular limitation. The surface protection tape has a function of protecting the circuit surface of the semiconductor wafer in the manufacturing method of semiconductor chips, particularly in the back grinding step. The surface protection tape used in the present invention has at least a base film and an adhesive layer on the surface of the base film. In the present invention, a preferred surface protection tape 4 has a two-layer structure having an adhesive layer 4B on the surface of a base film 4A, as shown in FIG. 1. In addition to the base film and the adhesive layer, a protective layer or the like may be present. The base film and the adhesive layer may each have a single layer structure or a multi-layer structure of two or more layers. The total thickness of the surface protection tape 4 (total thickness of each layer) is not particularly limited and can be, for example, 100 to 800 μm.

[0026] The material for forming the base film is not particularly limited, and examples of the material that is preferably used include polyolefin resins such as homopolymers or copolymers of α-olefins, such as polyethylene, polypropylene, ethylene-vinyl acetate copolymer, ethylene-acrylic acid copolymer, and ionomer, or mixtures thereof; engineering plastics, such as polyethylene terephthalate, polycarbonate, and polymethyl methacrylate; and thermoplastic elastomers, such as polyurethane, styrene-ethylene-butene-styrene, and pentene copolymers. The base film can be produced by a general extrusion method. When various resins are laminated, a co-extrusion method, a lamination method, etc. can be applied. In this case, an adhesive layer may be provided between the resins, as is commonly done in the production method of normal laminate films. The thickness of the base film is preferably 30 to 200 μm from the viewpoints of strength / elongation properties and radiation transparency.

[0027] The adhesive layer may be any layer containing an adhesive, and may be formed, for example, using an adhesive composition. The adhesive composition is not particularly limited, and may be a composition containing an ordinary adhesive such as (meth)acrylic, rubber, or silicone. In terms of weather resistance, cost, etc., a (meth)acrylic adhesive is preferably used. The (meth)acrylic adhesive may be a composition containing a copolymer having a (meth)acrylic acid ester as a constituent component (hereinafter referred to as "(meth)acrylic acid ester copolymer") as an adhesive component. This composition may contain a curing agent, which will be described later, in addition to the (meth)acrylic acid ester copolymer.

[0028] Examples of the (meth)acrylic acid esters that are components of the (meth)acrylic acid ester copolymer include alkyl acrylates or alkyl methacrylates having a straight or branched alkyl group having 30 or less carbon atoms, preferably 4 to 18 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, t-butyl, isobutyl, amyl, isoamyl, hexyl, heptyl, cyclohexyl, 2-ethylhexyl, octyl, isooctyl, nonyl, isononyl, decyl, isodecyl, undecyl, lauryl, tridecyl, tetradecyl, stearyl, octadecyl, and dodecyl. The (meth)acrylic acid esters may be used alone or in combination of two or more kinds. In the components constituting the (meth)acrylic acid ester copolymer, the content of the (meth)acrylic acid ester component is preferably 80% by mass or more, more preferably 90% by mass or more, and even more preferably 95 to 99.9% by mass.

[0029] The (meth)acrylic acid ester copolymer may contain components other than the (meth)acrylic acid ester (also referred to as other components). Examples of the other components include carboxyl group-containing monomers such as (meth)acrylic acid, carboxyethyl (meth)acrylate, carboxypentyl (meth)acrylate, itaconic acid, maleic acid, fumaric acid, and crotonic acid, acid anhydride monomers such as maleic anhydride and itaconic anhydride, hydroxyl group-containing monomers such as hydroxyalkyl (meth)acrylate (preferably, the alkyl group of the (meth)acrylic acid ester is substituted with a hydroxy group), styrenesulfonic acid, allylsulfonic acid, 2-(meth)acrylamido-2-methylpropanesulfonic acid, (meth) Examples of the monomers include sulfonic acid group-containing monomers such as acrylamidopropanesulfonic acid, sulfopropyl (meth)acrylate, and (meth)acryloyloxynaphthalenesulfonic acid, phosphoric acid group-containing monomers such as 2-hydroxyethyl acryloyl phosphate, (meth)acrylamide, (meth)acrylic acid N-hydroxymethylamide, (meth)acrylic acid alkylaminoalkyl esters (e.g., dimethylaminoethyl methacrylate, t-butylaminoethyl methacrylate, etc.), N-vinylpyrrolidone, acryloylmorpholine, vinyl acetate, styrene, acrylonitrile, etc. These constituents may be used alone or in combination of two or more kinds.

[0030] In the solid components of the adhesive layer, the content of the (meth)acrylic acid ester copolymer (the content converted into the state before reaction with the curing agent or photopolymerizable compound described below) is preferably 80 mass% or more, more preferably 90 mass% or more, and even more preferably 95 to 99.9 mass%.

[0031] The curing agent that may be contained in the (meth)acrylic adhesive is not particularly limited, and for example, the curing agents described in JP 2007-146104 A can be used. For example, epoxy compounds having two or more epoxy groups in the molecule such as 1,3-bis(N,N-diglycidylaminomethyl)cyclohexane, 1,3-bis(N,N-diglycidylaminomethyl)toluene, 1,3-bis(N,N-diglycidylaminomethyl)benzene, N,N,N,N'-tetraglycidyl-m-xylylenediamine, 2,4-tolylenediisocyanate, 2,6-tolylenediisocyanate, 1,3-xylylenediisocyanate, 1,4-xylylenediisocyanate, and diphenylmethane-4,4'-diisocyanate and other isocyanate compounds having two or more isocyanate groups in the molecule. aziridine compounds having two or more aziridinyl groups in the molecule, such as tetramethylol-tri-β-aziridinyl propionate, trimethylol-tri-β-aziridinyl propionate, trimethylolpropane-tri-β-aziridinyl propionate, and trimethylolpropane-tri-β-(2-methylaziridine)propionate are also included. The content of the curing agent may be adjusted according to the desired adhesive strength, and is preferably 0.01 to 10 parts by mass, more preferably 0.1 to 5 parts by mass, based on 100 parts by mass of the (meth)acrylic acid ester copolymer.

[0032] The (meth)acrylic adhesive can be a radiation-curable adhesive containing a photopolymerizable compound and a photopolymerization initiator in addition to the above adhesive component. By containing an adhesive component, a photopolymerizable compound, and a photopolymerization initiator, the adhesive layer can be cured by irradiation with radiation (preferably ultraviolet light), thereby reducing the adhesive strength of the adhesive layer. As such a photopolymerizable compound, for example, low molecular weight compounds having at least two or more photopolymerizable carbon-carbon double bonds in the molecule that can be three-dimensionally reticulated by irradiation with light, or oligomers obtained by polymerizing them, as described in JP-A-60-196956 and JP-A-60-223139, can be used. The photopolymerizable compound is not particularly limited, and examples thereof include trimethylolpropane tri(meth)acrylate, pentaerythritol di(meth)acrylate, pentaerythritol tri(meth)acrylate, pentaerythritol tetra(meth)acrylate, dipentaerythritol monohydroxypenta(meth)acrylate, dipentaerythritol hexa(meth)acrylate, neopentyl glycol di(meth)acrylate or 1,4-butylene glycol di(meth)acrylate, 1,6-hexanediol di(meth)acrylate, (poly)ethylene glycol di(meth)acrylate, (poly)propylene glycol di(meth)acrylate, epoxy (meth)acrylate ((meth)acrylic acid adduct of epoxy compound), polyester (meth)acrylate ((meth)acrylic acid adduct of polyester), and urethane (meth)acrylate ((meth)acrylic acid adduct of urethane). The photopolymerization initiator is not particularly limited, and for example, the photopolymerization initiators described in JP-A-2007-146104 or JP-A-2004-186429 can be used. Specifically, isopropyl benzoin ether, isobutyl benzoin ether, benzophenone, Michler's ketone, chlorothioxanthone, benzyl methyl ketal, α-hydroxycyclohexyl phenyl ketone, 2-hydroxymethyl phenyl propane, etc. can be used.

[0033] As the radiation-curable adhesive, in addition to the combination of the above-mentioned (meth)acrylic acid ester copolymer and a low molecular weight compound having at least two radiation-polymerizable carbon-carbon double bonds in the molecule, it is also preferable to use a copolymer having a (meth)acrylic acid ester as a constituent component, in which the repeating unit constituting this copolymer has a radiation-polymerizable carbon-carbon double bond (hereinafter referred to as a "radiation-polymerizable (meth)acrylic copolymer"). A radiation-polymerizable (meth)acrylic copolymer is a copolymer having reactive groups in the copolymer molecule that can undergo polymerization reaction when irradiated with radiation, particularly ultraviolet light. Such reactive groups are ethylenically unsaturated groups, i.e., groups having a carbon-carbon double bond (ethylenically unsaturated bond), such as vinyl groups, allyl groups, styryl groups, (meth)acryloyloxy groups, and (meth)acryloylamino groups. The radiation-polymerizable (meth)acrylic copolymer is not particularly limited, and examples thereof include (meth)acrylic copolymers obtained by reacting a (meth)acrylic copolymer having a functional group a with a compound having a functional group b capable of reacting with the functional group a and a radiation-polymerizable carbon-carbon double bond (hereinafter referred to as a "radiation-polymerizable compound having functional group b"). Examples of the (meth)acrylic copolymer having a carbon-carbon double bond include the same materials as those described in paragraphs

[0036] to

[0055] of JP2014-192204A.

[0034] In the radiation-polymerizable compound having the functional group b, examples of the functional group b include a carboxyl group, a hydroxyl group, an amino group, a cyclic acid anhydride group, an epoxy group, and an isocyanate group. Specific examples of radiation-polymerizable compounds having the functional group b include acrylic acid, methacrylic acid, cinnamic acid, itaconic acid, fumaric acid, phthalic acid, 2-hydroxyalkyl acrylates, 2-hydroxyalkyl methacrylates, glycol monoacrylates, glycol monomethacrylates, N-methylol acrylamide, N-methylol methacrylamide, allyl alcohol, N-alkylaminoethyl acrylates, N-alkylaminoethyl methacrylates, acrylamides, methacrylamides, maleic anhydride, itaconic anhydride, fumaric anhydride, phthalic anhydride, glycidyl acrylate, glycidyl methacrylate, allyl glycidyl ether, and polyisocyanate compounds in which some of the isocyanate groups have been urethanized with a monomer having a hydroxyl group or a carboxyl group and a radiation-polymerizable carbon-carbon double bond. In the reaction between the (meth)acrylic copolymer having the above functional group a and the radiation-polymerizable compound having the above functional group b, the acid value, hydroxyl value, etc. can be appropriately set by leaving unreacted functional groups.

[0035] The radiation-polymerizable (meth)acrylic copolymer can be obtained by solution polymerization in various solvents. As the organic solvent in the case of solution polymerization, ketones, esters, alcohols, and aromatics can be used. In general, it is preferable to use a solvent that is a good solvent for acrylic polymers and has a boiling point of 60 to 120°C. For example, toluene, ethyl acetate, isopropyl alcohol, benzene, methyl cellosolve, ethyl cellosolve, acetone, methyl ethyl ketone, etc. can be used. As the polymerization initiator, radical generators such as azobis-based such as α,α'-azobisisobutylnitrile and organic peroxide-based such as benzoyl peroxide can be used. In this case, a catalyst and a polymerization inhibitor can be used in combination as necessary, and a copolymer with a desired molecular weight can be obtained by adjusting the polymerization temperature and polymerization time. The synthesis method is not limited to solution polymerization, and other methods such as bulk polymerization and suspension polymerization can also be used.

[0036] In addition, the adhesive composition constituting the adhesive layer 3 may appropriately contain a release agent, a tackifier, an adhesion regulator, a surfactant, or other modifiers, etc. Also, it may contain an inorganic compound filler.

[0037] The pressure-sensitive adhesive layer can be formed by applying the pressure-sensitive adhesive composition onto a substrate such as a release film, drying the composition, and then transferring the composition onto the surface of the substrate film.

[0038] There are no particular limitations on the thickness of the adhesive layer so long as it does not impede adhesion to the water-soluble film and does not cause infiltration of dust or grinding water during grinding, but a thickness of 5 to 100 μm is usually appropriate.

[0039] [Method of manufacturing semiconductor chips] Next, the method for producing a semiconductor chip of the present invention (hereinafter, sometimes simply referred to as the production method of the present invention) has the following steps, and a semiconductor chip can be simply produced by subjecting a semiconductor wafer to the treatment of each step. Therefore, the method for producing a semiconductor chip of the present invention can also be said to be a method for treating a semiconductor wafer. The manufacturing method of the present invention is a method of sequentially carrying out the following steps (a) to (f) in the stated order, and other steps employed in manufacturing methods for semiconductor chips may also be appropriately carried out before step (a), between each step, or after step (f). Step (a): The water-soluble film of the semiconductor processing tape of the present invention is applied to the circuit of a semiconductor wafer. A process of grinding the back surface of a semiconductor wafer that is bonded to a substrate without heating. Step (b): The semiconductor wafer obtained in step (a) is diced on a ring frame. The process of supporting and fixing the Step (c): Peeling the surface protection tape of the semiconductor processing tape from the water-soluble film a step of exposing the water-soluble film Step (d): Cutting the water-soluble film along the intended cutting area of ​​the semiconductor wafer to form grooves. Process Step (e): The semiconductor wafer is subjected to plasma treatment from the cut water-soluble film side. A process for dividing the semiconductor wafer into individual pieces. Step (f): A step of washing the cut water-soluble film with non-heated water to dissolve and remove it.

[0040] The semiconductor wafer used in the manufacturing method of the present invention is a wafer having a circuit surface (also called a pattern surface) on one side of which a circuit or the like of a semiconductor element is formed, and examples of such wafers include silicon wafers, SiC wafers, GaAs wafers, and GaN wafers. In the present invention, the circuit side refers to the side of the semiconductor wafer on which a pattern such as a circuit of a semiconductor element is formed, and the back side refers to the side opposite to the circuit side on which no circuit is formed (non-circuit side). This circuit side has lattice-like streets in a plan view. Here, the streets refer to the cutting lines of the semiconductor wafer.

[0041] In the manufacturing method of the present invention, with respect to the processes other than those related to the semiconductor processing tape of the present invention, processes in a normal semiconductor chip manufacturing method can be applied without any particular limitations. The equipment and materials used in the manufacturing method of the present invention can be any equipment and materials that have been conventionally used for processing or treating semiconductor wafers, without any particular limitations, and the operating conditions of the equipment can be set appropriately.

[0042] The manufacturing method of the present invention will be specifically described with reference to the drawings, focusing on the processing related to the semiconductor processing tape of the present invention. In the following description and drawings, the same or corresponding elements are given the same reference numerals, and duplicated explanations will be omitted. Figures 2 to 4 are schematic vertical cross-sectional views (cross-sectional views cut in the thickness direction along the diameter direction of a semiconductor wafer) showing a preferred embodiment of the manufacturing method of the present invention.

[0043] In the manufacturing method of the present invention, prior to step (a), as shown in FIG. 2(a-1), the semiconductor processing tape 3 and the semiconductor wafer 1 are laminated so that the water-soluble film 5 of the semiconductor processing tape 3 of the present invention contacts the circuit surface 1A of the semiconductor wafer 1, and are bonded together under non-heating. In the present invention, non-heating refers to a temperature of, for example, less than 60°C, preferably 40°C or less. The lower limit temperature is not particularly limited, but can usually be 15°C, preferably 20°C. The method of bonding the semiconductor processing tape 3 and the semiconductor wafer 1 can be applied by a normal method without any particular limitation, but since the water-soluble film 5 has sufficient adhesion (adhesiveness) to the semiconductor wafer 1, they can be bonded by simply laminating them, and if necessary, further applying pressure. During lamination, a semiconductor processing tape 3 of the same size as or smaller than the semiconductor wafer 1 is used so that the tape does not protrude beyond the outer periphery of the semiconductor wafer 1 when laminated to the semiconductor wafer 1. This makes it possible to prevent damage such as burning of the semiconductor processing tape 3 (water-soluble film 5) protruding from the semiconductor wafer 1 by plasma, for example, in the singulation step (e) described below.

[0044] Next, the back surface 1B of the semiconductor wafer 1 having the water-soluble film 5 of the semiconductor processing tape 3 bonded to the circuit surface 1A, as shown in Fig. 2(a-1), is ground (step (a)). As a result, the semiconductor wafer 1 having the semiconductor processing tape 3 bonded to the circuit surface 1A and thinned to a predetermined thickness can be obtained, as shown in Fig. 2(a-2). The method for grinding the back surface 1B of the semiconductor wafer 1 is not particularly limited, and may be a commonly applied back grinding (BG) process or an etching process, with the BG process being preferred. The method and conditions in step (a) may be those of the ordinary type.

[0045] In the manufacturing method of the present invention, next, as shown in FIG. 3(b), the semiconductor wafer 1 obtained in step (a) is supported and fixed to a dicing tape 11 via a ring frame 12 (step (b)). The ring frame 12 and dicing tape 11 used in step (b), as well as the method of supporting and fixing, may be any commonly used method or may be applied without any particular limitation. For example, the dicing tape 11 may be a laminated tape of a base film 11A and a pressure-sensitive adhesive layer 11B, and specifically, the tape described in Patent Document 2 may be used.

[0046] 3(c), the surface protection tape 4 (base film 4A and adhesive layer 4B) of the semiconductor processing tape 3 is peeled off from the water-soluble film 5 (step (c)). In this way, the surface protection tape 4 is removed to expose the water-soluble film 5, and the semiconductor wafer 1 having the water-soluble film 5 bonded to the circuit surface 1A is obtained. The surface protection tape 4 may be peeled off with a force equal to or greater than the peeling force between the water-soluble film 5 and the surface protection tape 4, and when the adhesive layer 4B contains a radiation-curable adhesive, the adhesive layer 4B is cured by irradiating radiation from the surface protection tape 4 side, whereby the surface protection tape 4 becomes easy to peel off from the water-soluble film 5. A typical method can be used as a specific method for peeling off the surface protection tape 4. In the present invention, radiation means light rays such as ultraviolet rays, or ionizing radiation such as electron beams, and is preferably ultraviolet rays.

[0047] In the manufacturing method of the present invention, next, as shown in FIG. 3(d-1), the water-soluble film 5 is cut (step (d)) along the intended cutting areas (streets, not shown in FIG. 3(d-1)) of the semiconductor wafer 1 obtained in step (c). Thus, as shown in FIG. 4(d-2), grooves 8 are provided in the water-soluble film 5 to enable irradiation of the semiconductor wafer 1 with plasma, as described below, to separate the water-soluble film 5. As a result, the intended cutting areas of the semiconductor wafer 1 are exposed at the bottom of the grooves 8. It is preferable that the width of the grooves 8 to be formed be equal to or smaller than the width of the streets. The method for cutting the water-soluble film 5 is not particularly limited as long as it can form grooves 8 in the water-soluble film 5. For example, as shown in FIG. 3(d-1), a laser grooving method in which a laser beam 7 outputted (emitted) from a laser beam irradiating means 6 is irradiated onto the water-soluble film 5 while moving the laser beam 7 relatively along the street to cut the film, and a blade grooving method in which a blade is used to cut the film, etc. can be mentioned. As the laser beam irradiating means 6, for example, the device described in Patent Document 2 can be used. The water-soluble film 5 of the semiconductor processing tape 3 is preferably a laser grooving method, which is excellent in dimensional accuracy, work efficiency, etc., because the individualized water-soluble film 5 does not soften or melt even when cut by laser irradiation, and grooves 8 of a predetermined size and shape can be formed. The groove formation conditions in the laser grooving method and the blade grooving method may be those generally used, but are appropriately set in consideration of the composition, physical properties, etc. of the water-soluble film 5. For example, the conditions for the laser grooving method may be selected from among an output of 0.3 to 4.0 W, a frequency of 50 to 100 kHz, and a processing feed rate of 1 to 800 mm / sec. The conditions for the blade grooving method may be a blade width of 100 to 300 μm and a rotation speed of 1000 to 30000 rpm.

[0048] 4(e), plasma 10A is irradiated onto the exposed portion of the semiconductor wafer 1 from the cut (diced) water-soluble film 5 side to perform plasma treatment (step (e)). In this way, the semiconductor wafer 1 is etched and diced into individual chips. The method for dividing the semiconductor wafer 1 can be any commonly used plasma dicing method without any particular limitations. In the manufacturing method of the present invention, as shown in FIG. 4(e), the method is performed under appropriate conditions using a plasma etching apparatus 10. For example, the apparatus described in Patent Document 2 can be used as the plasma etching apparatus 10. Specifically, the plasma dicing conditions can be such that a fluorine-based gas such as SF6 is introduced and the etching rate is selected from the range of 0.5 to 10 μm / s.

[0049] In the manufacturing method of the present invention, the cut (individualized) water-soluble film 5 is then washed with non-heated water (usually pure water) 9 (step (f)) as shown in Fig. 4(f). In this manner, the water-soluble film 5 is dissolved and removed to obtain the semiconductor chip 2. The method for washing and removing the water-soluble film is not particularly limited as long as it is a method for bringing the water-soluble film into contact with non-heated water. For example, a method may be used in which the assembly of individualized semiconductor chips 2 is held on a spinner table while being fixed to a ring frame 12, and cleaning water consisting of non-heated water 9 and air is sprayed from a nozzle positioned above the center of the assembly of semiconductor chips 2 while rotating the assembly of semiconductor chips 2, and then air is sprayed from an air nozzle onto the semiconductor chips 2 to dry them. Since the water-soluble film of the semiconductor processing tape of the present invention exhibits sufficient solubility in non-heated water as described above, non-heated water can be used as the water for washing the water-soluble film in this step, and this step can be carried out simply and with less energy. The temperature of the washing water can be, for example, less than 60°C, and preferably 40°C or less. The lower limit of the water temperature is not particularly limited, but can usually be 15°C, and is preferably 20°C. The water washing method is not particularly limited, and examples thereof include a method of spraying non-heated water onto the assembly of semiconductor chips, a method of applying non-heated water onto the assembly of semiconductor chips, and a method of immersing the assembly of semiconductor chips in non-heated water. The water washing conditions are appropriately determined taking into consideration the water solubility and thickness of the water-soluble film, and can be selected from conditions such as a water amount of 10 to 500 mL / min, a water washing time of 1 to 5 minutes, and a drying time of 1 to 5 minutes.

[0050] In the manufacturing method of the present invention, a pick-up step (g) can be performed to pick up the assembly of semiconductor chips 2 (diced semiconductor wafer 1) obtained in step (f) as shown in Fig. 4(g). The pick-up step (g) can be performed using a commonly used method without any particular limitation, and an example of the method is to push up the semiconductor chip 2 together with the dicing tape 11 with a pin 15 and adsorb it with a collet 16 to pick up the semiconductor chip 2 as shown in Fig. 4(g). EXAMPLES

[0051] The present invention will be described in more detail below based on examples and comparative examples, but the present invention is not limited to the following examples.

[0052] [Production of tape for semiconductor processing] <Example 1> (1) Preparation of surface protection tape 100 parts by mass of acrylic polymer containing 2-ethylhexyl acrylate as a constituent component were dissolved in ethyl acetate with 1.5 parts by mass of Coronate L (product name, manufactured by Tosoh Corporation) as a curing agent to obtain an ethyl acetate solution of adhesive. This solution was applied onto a release-treated PET film (Therapeel WZ (product name), thickness 25 μm, manufactured by Toray Industries, Inc.) so that the thickness after drying was 30 μm, and then dried by heating. Thereafter, the adhesive layer was bonded to a substrate film (Nipolon Hard 4010 (product name, manufactured by Tosoh Corporation)) made of polyethylene extrusion-formed to a thickness of 100 μm to produce a surface protection tape with a PET film.

[0053] (2) Preparation of water-soluble film A water-soluble film solution was obtained by dissolving each material shown in the "Water-soluble film" column of Table 1 in water at the mass ratio shown in the same column for 100 parts by mass of PVP-K90 (Polyvinylpyrrolidone K90 (trade name), manufactured by Fujifilm Wako Pure Chemical Industries, Ltd.). The obtained solution was applied onto a release-treated PET film (Therapeel WZ (trade name), thickness 25 μm, manufactured by Toray Industries, Inc.) so that the thickness after drying would be 25 μm, and the film was dried by heating to produce a water-soluble film with a PET film.

[0054] (3) Preparation of tape for semiconductor processing After peeling off the PET film from the surface protection tape with PET film obtained in (1) above, the adhesive layer of the surface protection tape and the water-soluble film of the water-soluble film with PET film were bonded together to produce a semiconductor processing tape having a four-layer laminate structure of base film / adhesive layer / water-soluble film / PET film.

[0055] The weight average molecular weight (Mw) of polyvinylpyrrolidone K90 and polyethylene glycol PEG600 (product names, manufactured by Sanyo Chemical Industries, Ltd.) was measured as a value (polyethylene glycol / polyethylene oxide (PEG / PEO) equivalent value) when measured by GPC (Gel Permeation Chromatography) under the following conditions. GPC conditions: Column: TSKgel SuperMultiporePW-M (6.0mm I.D. x 15cm) ·Eluent: 100mmol / L NaNO3 ·Flow rate: 0.6mL / min Detector: RI ·Temperature: 25℃ ·Injection volume: 20μL Sample preparation: A 3 mg / mL solution of the sample was prepared using pure water. The retention volume obtained by GPC measurement was converted to molecular weight using a calibration curve prepared using PEG / PEO for molecular weight calibration, which was prepared using an Agilent polyethylene glycol / polyethylene oxide standard kit.

[0056] <Examples 2 to 9 and Comparative Examples 1 to 6> In the "Preparation of water-soluble film" of Example 1, the semiconductor processing tapes of Examples 2 to 9 and Comparative Examples 1 to 6 were each produced in the same manner as in Example 1, except that the material, content (composition), and thickness forming the water-soluble film were changed to the material, content, and thickness shown in the "Water-soluble film" column of Table 1 or Table 2. In Comparative Example 6, the high molecular weight compound and the low molecular weight compound could not be mixed, and a water-soluble film could not be prepared.

[0057] The materials used in each of the examples and comparative examples are shown below, and Tables 1 and 2 show the weight average molecular weight of each material measured by the above-mentioned method. <Water-soluble film> (polymer compound) PVP-K90: Polyvinylpyrrolidone K90 (product name), manufactured by Fujifilm Wako Pure Chemical Industries, Ltd. PVP-K50: Polyvinylpyrrolidone K50 (product name), manufactured by Fujifilm Wako Pure Chemical Industries, Ltd. PEO Z : Poly(2-ethyl-2-oxazoline), weight average molecular weight 5,000, manufactured by Polymer Chemistry Innovations PVA-1: Polyvinyl alcohol, polymerization degree 1700, manufactured by Kuraray Co., Ltd. PVA-2: Polyvinyl alcohol, polymerization degree 300, manufactured by Kuraray Co., Ltd. PVP-K30: Polyvinylpyrrolidone K30 (product name), manufactured by Fujifilm Wako Pure Chemical Industries, Ltd. In addition, P.E.O. Z Although PVA-1, PVA-2 and PVP-K30 have small weight average molecular weights and do not correspond to polymer compounds, they are listed in the "polymer compounds" column in Table 2 for convenience.

[0058] (Low molecular compound) PEG600: Polyethylene glycol, manufactured by Sanyo Chemical Industries, Ltd. PEG400: Polyethylene glycol, manufactured by Sanyo Chemical Industries, Ltd. PEG1000: Polyethylene glycol, manufactured by Sanyo Chemical Industries, Ltd. PEG1540: Polyethylene glycol, manufactured by Sanyo Chemical Industries, Ltd. PVA-3: Polyvinyl alcohol, polymerization degree 500, manufactured by Kuraray Co., Ltd. Glycerin: Tokyo Chemical Industry Co., Ltd. Although PEG1000, PEG1540 and PVA-3 have a large weight average molecular weight and do not correspond to low molecular weight compounds, they are listed in the "low molecular weight compounds" column in Table 2 for convenience.

[0059] (Other Ingredients) Tinuvin 477: UV absorber, manufactured by BASF GA: Glutaraldehyde, molecular weight 100, manufactured by Nacalai Tesque <Adhesive layer> 2eha: acrylic polymer consisting of 2-ethylhexyl acrylate, manufactured by Shin-Nakamura Chemical Co., Ltd. Coronate L: The hardener shown below, manufactured by Tosoh Corporation [ka]

[0060] [test] The semiconductor processing tapes obtained in the above examples and comparative examples were tested for the following items. Among the semiconductor processing tapes in the comparative examples, some were inferior in the wafer adhesion test or groove formation test, and other tests were not performed. The results are summarized in Table 1 or Table 2.

[0061] <Test 1: Peel strength between water-soluble film and surface protection tape> Each semiconductor processing tape obtained in each Example and Comparative Example was cut into a width of 25 mm, the PET film was peeled off, and the surface of the water-soluble film was laminated to the mirror surface of a silicon wafer at a temperature of 23°C. This lamination was performed by overlapping the semiconductor processing tape on the silicon wafer and running a rubber roller with a load of 2 kg back and forth three times on the surface of the semiconductor processing tape. The maximum peel force was measured when the water-soluble film and the surface protection tape (adhesive layer) were peeled off using a Strograph VG1F (trade name, manufactured by Toyo Seiki Co., Ltd.) under conditions of 23°C, peel angle of 180°, and peel speed of 300 mm / min. The conditions other than the above conditions were in accordance with Japanese Industrial Standards (JIS) Z 0237:2009. The obtained maximum peel force (N / 25 mm) was evaluated based on the following evaluation criteria. - Evaluation Criteria - ○: Over 0.1N / 25mm, 1N / 25mm or less △: Over 1N / 25mm, 2N / 25mm or less ×: Over 2N / 25mm

[0062] <Test 2: Absorbance of water-soluble film> For each of the water-soluble films with a PET film prepared in each of the Examples and Comparative Examples, the absorbance of ultraviolet light with a wavelength of 355 nm was measured as follows. The water-soluble film solution prepared in the same manner as in each of the Examples and Comparative Examples was applied onto a PET film (thickness 38 μm) and dried by heating to obtain a coating of the water-soluble film solution. The absorbance of the obtained coating was measured in the wavelength range of 300 to 1000 nm using a spectrophotometer U-5100 (manufactured by Yamato Scientific Co., Ltd.) with a PET film on which the water-soluble film solution was not applied as a reference. The absorbance at a wavelength of 355 nm was obtained and used as the absorbance of each water-soluble film.

[0063] <Test 3: Wafer adhesion> The adhesion of each of the semiconductor processing tapes produced in each of the Examples and Comparative Examples to a semiconductor wafer was evaluated by measuring the peel force (N / 25 mm) according to the test described below. The water-soluble film solution prepared in the same manner as in the examples and comparative examples was applied onto a PET film that had been subjected to an adhesion treatment, and then dried by heating to prepare a test tape of PET film (thickness 38 μm) / water-soluble film (thickness 10 μm). The adhesion treatment was performed by subjecting the surface of the PET film to a corona treatment at a strength of 5A. Next, the obtained test tape was cut to a width of 25 mm, and the water-soluble film surface of the test tape was laminated to the mirror surface of a silicon wafer at a temperature of 23°C. This lamination was performed by overlapping the test tape on the silicon wafer and running a rubber roller with a load of 2 kg back and forth on the surface of the test tape three times. The maximum peel strength between the water-soluble film and the wafer immediately after lamination and after leaving the test tape in an environment with a temperature of 23°C and a humidity of 50 RH% for 1 hour after lamination was measured using Strograph VG1F (trade name, manufactured by Toyo Seiki Co., Ltd.) under the conditions of 23°C, peel angle of 180°, and peel speed of 300 mm / min. The conditions other than the above were in accordance with Japanese Industrial Standards (JIS) Z 0237:2009. The maximum peel strength (N / 25 mm) immediately after lamination and the maximum peel strength (N / 25 mm) after leaving for 1 hour after lamination were evaluated according to the following evaluation criteria. - Evaluation Criteria - ○: The maximum peel strength immediately after application and the maximum peel strength after leaving for 1 hour after application are both greater than 1N / 25mm △: The maximum peel strength after leaving for 1 hour after application exceeds 1N / 25mm ×: The maximum peel strength after leaving the film for 1 hour after lamination is 1N / 25mm or less, or the water-soluble film is partially peeled off from the wafer.

[0064] Groove formation resistance test (heat resistance) was conducted by groove formation test A (laser grooving resistance test) and groove formation test B (blade grooving resistance test) in order to evaluate the characteristics according to the application of the semiconductor processing tape. It is sufficient for the semiconductor processing tape to pass at least one of the groove formation tests according to the groove forming step (d) of the manufacturing method of the semiconductor chip to be used.

[0065] <Test 4: Groove formation test A (laser grooving resistance test)> The PET film was peeled off from each semiconductor processing tape obtained in each Example and Comparative Example, and the surface of the water-soluble film was laminated to the mirror surface of a silicon wafer at a temperature of 23°C. This lamination was performed by overlapping the semiconductor processing tape on the silicon wafer, and running a rubber roller with a load of 2 kg back and forth three times on the surface of the semiconductor processing tape. Thereafter, the water-soluble film exposed by peeling off the surface protection tape was cut using a laser dicer DFL7160 (trade name, manufactured by Disco) to form grooves. The laser grooving conditions were an output of 1 W, a frequency of 100 Hz, a processing speed of 50 mm / sec, and a groove width of 10 μm. The wafer portion (exposed portion of the wafer) after cutting the water-soluble film was observed with a microscope, and the groove width was measured at 10 points at a depth of 1 μm from the surface layer at intervals of 100 μm along the groove length for the formed grooves. The average value of the 10 measured widths was calculated and evaluated based on the following evaluation criteria. This test is a grooving resistance (heat resistance) test to evaluate the deformation prevention properties of the water-soluble film during the laser grooving process (a property that enables the production of semiconductor chips with excellent dimensional accuracy). Specifically, the test evaluates the property of the water-soluble film not softening or melting due to the heat of laser irradiation, and not flowing down into the grooves (exposed parts of the wafer), and allowing it to be diced into semiconductor chips of a specified size by plasma etching. - Evaluation Criteria - ○: The actual width of the formed groove is within the range of 80 to 120% of the groove formation width of 10 μm. △: The measured width of the formed groove is within the range of 60 to 140% of the groove formation width of 10 μm (excluding the range of 90 to 110%) ×: The actual width of the formed groove is less than 60% or more than 140% of the groove formation width of 10 μm.

[0066] <Test 5: Groove formation test B (blade grooving resistance test)> Wafers with water-soluble film that were rated "x" in the above <Test 4: Groove Formation Test A (Laser Grooving Resistance Test)> were used to cut the water-soluble film by blade grooving to form grooves. The wafer portion after cutting the water-soluble film (exposed portion of the wafer) was observed under a microscope, and the groove widths of the formed grooves were measured at 10 points at a depth of 1 μm from the surface layer at intervals of 100 μm along the groove length. The average of the 10 measured widths was calculated and evaluated based on the following evaluation criteria. This test is a grooving resistance (heat resistance) test to evaluate the deformation prevention properties of the water-soluble film during the blade grooving process (a property that enables the production of semiconductor chips with excellent dimensional accuracy). Specifically, the test evaluates the property of preventing the water-soluble film from entering the grooves (exposed parts of the wafer) by the blade and enabling the film to be diced into semiconductor chips of a specified size by plasma etching. - Evaluation Criteria - ○: The actual width of the formed groove is within the range of 80 to 120% of the groove formation width of 10 μm. △: The measured width of the formed groove is within the range of 60 to 140% of the groove formation width of 10 μm (excluding the range of 90 to 110%) ×: The actual width of the formed groove is less than 60% or more than 140% of the groove formation width of 10 μm.

[0067] <Test 6: Removability by washing with water> The PET film was peeled off from each of the semiconductor processing tapes obtained in each Example and Comparative Example, and the surface of the water-soluble film was laminated to the mirror surface of the silicon wafer at a temperature of 23°C. This lamination was performed by overlapping the semiconductor processing tape on the silicon wafer, and running a rubber roller with a load of 2 kg back and forth three times on the surface of the semiconductor processing tape. Thereafter, the surface protection tape was peeled off from the water-soluble film. Next, the silicon wafer having the water-soluble film was set on a spin coater (model number: manufactured by Active Co., Ltd.), and pure water with a rotation speed of 200 rpm and a water temperature of 23°C was poured on it at a water amount of 100 mL / min for 2 minutes. After washing with water in this way, it was visually confirmed whether the water-soluble film remained on the silicon wafer, and it was evaluated based on the following evaluation criteria. In the evaluation criteria of this test, "glue" refers to a mass formed when the water-soluble film swells with water. - Evaluation Criteria - ○: The water-soluble film dissolves and leaves no adhesive residue △: The adhesive residue of the water-soluble film was slight enough to be acceptable for a semiconductor chip. ×: The amount of adhesive residue of the water-soluble film exceeds the allowable amount for a semiconductor chip, or the water-soluble film does not dissolve to such an extent that it clogs the drainage groove (diameter 40 mm) of the spin coater.

[0068] <Test 7: Test to prevent seepage during back grinding process> This test (reference test) is a test to evaluate desirable properties of a water-soluble film, such as preventing excessive elution of the water-soluble film of a semiconductor processing tape during the backgrinding process. The PET film was peeled off from each semiconductor processing tape obtained in each Example and Comparative Example, and the surface of the water-soluble film was attached to the mirror surface of a silicon wafer (thickness 0.6 mm) with a diameter of 8 inches at a temperature of 23°C. The attachment was performed by overlapping the test tape on the silicon wafer and reciprocating a rubber roller with a load of 2 kg on the surface of the test tape three times. Then, the test tape was set in a grinder DGP8760 (trade name, manufactured by Disco Corporation) and the back surface of the silicon wafer was ground until the thickness of the silicon wafer became 50 μm. Dicing tape UC-334EP-110 (trade name, manufactured by Furukawa Electric Co., Ltd.) was attached to the ground surface of the obtained silicon wafer at a temperature of 23°C, and the surface protection tape was peeled off to expose the water-soluble film, and the wafer edge was observed to confirm the degree of penetration of the grinding water. The degree of penetration was measured as the maximum depth (maximum erosion amount) from the end face of the recess formed by dissolution from the end face of the water-soluble film. The peel adhesion state or the degree of penetration of the water-soluble film was evaluated based on the following evaluation criteria. - Evaluation Criteria - ○: Penetration depth is 200μm or less △: Penetration depth exceeds 200μm and is 1mm or less ×: The penetration depth was 1 mm or more, or the water-soluble film peeled off from the silicon wafer.

[0069] [Table 1]

[0070] [Table 2]

[0071] The above results reveal the following: The comparative semiconductor processing tape having a water-soluble film containing a high molecular weight compound and / or a low molecular weight compound that does not satisfy the (weight average) molecular weight requirement cannot achieve both grooving resistance and adhesion to semiconductor wafers or removability by water washing, and therefore cannot be applied to a semiconductor chip manufacturing method that includes a plasma dicing process. In contrast, the semiconductor processing tape of the embodiment, which is provided with a water-soluble film containing a polymeric compound and a low molecular compound that satisfy the (weight average) molecular weight, can balance grooving resistance (one of groove formation test A or groove formation test B), adhesion to a semiconductor wafer, and water-washing removability. Therefore, the semiconductor processing tape of the embodiment exhibits high water-washing removability that enables water-washing removal with non-heated water while balancing grooving resistance and wafer adhesion. Therefore, the semiconductor processing tape of the embodiment can protect the circuit surface of the semiconductor wafer in the back grinding process, and can easily perform the grooving process and the plasma dicing process, and is suitable for use in a semiconductor chip manufacturing method including a plasma dicing process. It can be seen that these semiconductor processing tapes enable easy manufacturing of semiconductor chips with high dimensional accuracy without chipping by using them in a semiconductor chip manufacturing method including a plasma dicing process. [Explanation of symbols]

[0072] 1. Semiconductor wafer 1A circuit side 1B Back side 2. Semiconductor chips 3. Tape for semiconductor processing 4 Surface protection tape 4A Base film 4B Adhesive layer 5. Water-soluble film 6 Laser light irradiation means 7. Laser Light 8 grooves 9 Unheated water 10 Plasma Etching Equipment 10A Plasma 11 Dicing tape 11A Base film 11B Adhesive layer 12 Ring Frame 15-pin 16 Colette

Claims

1. A semiconductor processing tape used in plasma dicing, which is a laminate of a water-soluble film containing a polymer compound with a weight-average molecular weight of 200,000 or more and a water-soluble low molecular weight polymer with a molecular weight of 800 or less, and a surface protection tape that protects the circuit surface of a semiconductor wafer.

2. 2. The tape for semiconductor processing according to claim 1, wherein the water-soluble film has an absorbance of 30% or more for electromagnetic waves having a wavelength of 355 nm.

3. 3. The semiconductor processing tape according to claim 1, wherein the peel strength between the water-soluble film and the surface protection tape is 1 N / 25 mm or less.

4. 4. The tape for semiconductor processing according to claim 1, wherein the water-soluble film has a thickness of 20 μm or less.

5. The semiconductor processing tape according to any one of claims 1 to 4, wherein the content of the water-soluble low molecular weight polymer in the water-soluble film is 10 to 100 parts by mass when the content of the polymer compound in the water-soluble film is 100 parts by mass.

6. A step (a) of grinding the back surface of a semiconductor wafer in which the water-soluble film in the semiconductor processing tape according to any one of claims 1 to 5 is laminated to the circuit surface of the semiconductor wafer without heating; (b) supporting and fixing the semiconductor wafer to a dicing tape via a ring frame; a step (c) of peeling a surface protection tape of the semiconductor processing tape from the water-soluble film to expose the water-soluble film; (d) cutting the water-soluble film along a region to be cut of the semiconductor wafer to provide a groove; (e) subjecting the semiconductor wafer to a plasma treatment from the cut water-soluble film side to separate the semiconductor wafer; (f) a step of washing the cut water-soluble film with non-heated water to dissolve and remove it; A method for manufacturing a semiconductor chip comprising the steps of:

7. 7. The method for producing a semiconductor chip according to claim 6, wherein the step (d) is a step of cutting the water-soluble film by laser irradiation.

Images