Method for removing metal contaminants from acidic solutions containing scandium

Abstract

To provide a system for removing at least one kind of a metal contaminant from a stock solution comprising Sc.SOLUTION: There is provided a process for removing at least one kind of a metal contaminant from a stock solution comprising Sc, comprising the steps of: a) contacting the stock solution with an ion exchange resin capturing Sc and the at least one kind of a metal contaminant so as to produce a metal ion exchange resin complex; and b) scrubbing the metal resin complex with a scrubbing solution comprising a carboxylate ion, so as to produce a Sc ion exchange resin complex and a spent carboxylate solution, which can be treated by electrodialysis to regenerate the carboxylate ion required for scrubbing.SELECTED DRAWING: None

Description

[Technical field]

[0001] CROSS-REFERENCE TO RELATED APPLICATIONS This application claims priority to and the benefit of U.S. Provisional Application No. 62 / 667,797, filed May 7, 2018, the entire contents of which are incorporated herein by reference.

[0002] This specification relates to the recovery of scandium, and in particular to a method for removing / cleaning low concentration metal contaminants from acidic solutions containing scandium. [Background technology]

[0003] Scandium can be present in low concentrations, such as 10-100 g / t, in many different titanium dioxide raw materials, including natural ores (ilmenite, rutile, etc.) and man-made products (titanium slag, synthetic rutile, etc.).

[0004] During the upgrading of titanium dioxide raw materials (ilmenite, titanium slag, etc.) or during the conversion of titanium dioxide raw materials to titanium dioxide pigments and titanium metal, aqueous solutions containing scandium are produced. Examples of solutions containing scandium include spent hydrochloric acid from titanium dioxide raw material upgrading operations, waste eluates from titanium pigment plants, waste eluates from titanium metal plants, etc. Such solutions can be treated with ion exchange resins to recover the scandium.

[0005] However, some of the residual structurally similar metallic impurity elements, such as titanium, thorium and zirconium, are difficult to separate from such scandium-containing solutions, and there is a need to reduce the concentrations of these similar impurities in order to simplify and improve the production of high purity (e.g., >99 wt%) scandium oxide. Summary of the Invention

[0006] In one embodiment, a method for removing at least one metal contaminant from a storage solution containing Sc is provided, the method comprising: a) contacting the storage solution with an ion exchange resin to capture the Sc and the at least one metal contaminant to produce a metal ion exchange resin complex; and b) washing the metal resin complex with a wash solution comprising a salt having a carboxylate ion to produce a Sc ion exchange resin complex and a spent carboxylate solution.

[0007] In another aspect, there is provided a method, as described herein, wherein the carboxylate ion has a pKa in the range of 2.5 to 4.0.

[0008] In yet another aspect, there is provided a method, as described herein, wherein the salt comprises an alcohol moiety adjacent to the carboxylate ion.

[0009] In still yet another aspect, there is provided a method as described herein, wherein a carboxylate ion is capable of combining with at least one metal contaminant to produce a soluble metal contaminant complex.

[0010] In yet still another aspect, there is provided a method as described herein, wherein prior to step a), the method comprises ai) providing a first solution comprising Sc, at least one metal contaminant and excess metal ions; a-ii) contacting the first solution with an ion exchange resin; a-iii) adding a strong acid to the ion exchange resin to dissolve and remove the excess metal ions from the ion exchange resin as an excess metal ion acidic solution; and a-iv) forming a stock solution.

[0011] In still yet another aspect, there is provided a method, as described herein, wherein the excess metal ions include at least one of iron (Fe), magnesium (Mg), aluminum (Al), calcium (Ca), and combinations thereof.

[0012] In still yet another aspect, there is provided a method, as described herein, wherein the excess metal ion comprises Fe.

[0013] In yet still another embodiment, there is provided a method as described herein, further comprising eluting Sc from the ion exchange resin complex with an alkaline solution to produce a soluble Sc solution.

[0014] In still yet another aspect, there is provided a method, as described herein, wherein the alkaline solution comprises a hydroxide, carbonate or bicarbonate.

[0015] In still yet another aspect, there is provided a method, as described herein, wherein the at least one metal contaminant is at least one of titanium (Ti), thorium (Th), and zirconium (Zr).

[0016] In still yet another aspect, there is provided a method as described herein, wherein the at least one metal contaminant is Ti.

[0017] In still yet another aspect, there is provided a method, as described herein, wherein the salt is at least one of citrate, tartrate, malate, malonate, lactate, or a combination thereof.

[0018] In still yet another aspect, there is provided a method, as described herein, wherein the salt is a citrate salt.

[0019] In yet still another aspect, there is provided a method, as described herein, wherein the ion exchange resin comprises at least one of the following functional groups: sulfonic acid, phosphonic acid, phosphinic acid, phosphonic acid monoethyl / diethyl ester, phosphonic acid / tertiary amine, phosphonic acid / dimethyl ester, and combinations thereof.

[0020] In still yet another aspect, there is provided a method as described herein, wherein the temperature of the wash solution is 65° C. or less.

[0021] In still yet another aspect, there is provided a method as described herein, wherein the temperature of the wash solution is between 20°C and 65°C.

[0022] In still yet another aspect, there is provided a method as described herein, wherein the wash solution has a pH between 3.0 and 4.0.

[0023] In still yet another aspect, there is provided a method as described herein, wherein the wash solution has a pH of about 3.8.

[0024] In yet another embodiment, c) regenerating the wash solution from the spent carboxylate solution. The method described herein further comprises:

[0025] In yet still another aspect, there is provided a method as described herein, wherein regenerating the depleted carboxylate solution comprises ci) precipitating metal-containing solids from the depleted carboxylate solution in an alkaline solution; c-ii) separating the metal-containing solids from the depleted carboxylate solution to form a depleted carboxylate solution; and c-iii) electrodialyzing the depleted carboxylate solution to produce a regenerated carboxylate solution.

[0026] In still yet another aspect, there is provided a method, as described herein, wherein the alkaline solution comprises a hydroxide.

[0027] In yet still another embodiment, there is provided a method as described herein further comprising c-iv) returning the regenerated carboxylate solution to step b) as a wash solution.

[0028] In yet another aspect, a method for removing at least one of titanium (Ti), thorium (Th) and zirconium (Zr) from a storage solution containing Sc is provided, the method comprising: a) contacting the storage solution with an ion exchange resin to incorporate Sc and at least one of Ti, Th and Zr to produce a metal-resin complex; and b) washing the metal-resin complex with a wash solution comprising a salt having citrate ions to produce a Sc ion exchange resin complex and a spent carboxylate solution.

[0029] In yet still another aspect, there is provided a method as described herein, wherein citrate ions binding with at least one of Ti, Th, and Zr produces soluble Ti, Th, and Zr contaminant complexes.

[0030] In yet still another aspect, there is provided a method as described herein, wherein prior to step a), the method comprises ai) providing a first solution comprising Sc, at least one of Ti, Th, and Zr, and excess metal ions; a-ii) contacting the first solution with an ion exchange resin; a-iii) adding a strong acid to the ion exchange resin to dissolve and remove the excess metal ions from the ion exchange resin as an excess ion acidic solution; and a-iv) forming a stock solution.

[0031] In still yet another aspect, there is provided a method as described herein, wherein the excess metal ions are Fe, Mg, Al and combinations thereof.

[0032] In still yet another aspect, there is provided a method, as described herein, wherein the excess metal ion comprises Fe.

[0033] In yet still another embodiment, there is provided a method as described herein, further comprising eluting Sc from the ion exchange resin complex with an alkaline solution to produce a soluble Sc solution.

[0034] In still yet another aspect, there is provided a method, as described herein, wherein the alkaline solution comprises a hydroxide, carbonate or bicarbonate.

[0035] In yet still another aspect, there is provided a method, as described herein, wherein the ion exchange resin comprises at least one of the following functional groups: sulfonic acid, phosphonic acid, phosphinic acid, phosphonic acid monoethyl / diethyl ester, phosphonic acid / tertiary amine, phosphonic acid / dimethyl ester, and combinations thereof.

[0036] In still yet another aspect, there is provided a method as described herein, wherein the temperature of the wash solution is 65° C. or less.

[0037] In still yet another aspect, there is provided a method as described herein, wherein the temperature of the wash solution is between 20°C and 65°C.

[0038] In still yet another aspect, there is provided a method as described herein, wherein the wash solution has a pH between 3.0 and 4.0.

[0039] In still yet another aspect, there is provided a method as described herein, wherein the wash solution has a pH of about 3.8.

[0040] In yet still another embodiment, there is provided a method as described herein further comprising c) regenerating the wash solution from the spent carboxylate solution.

[0041] In yet still another aspect, there is provided a method as described herein, wherein regenerating the depleted carboxylate solution comprises ci) precipitating metal-containing solids from the depleted carboxylate solution in an alkaline solution; c-ii) separating the metal-containing solids from the depleted carboxylate solution to form a depleted carboxylate solution; and c-iii) electrodialyzing the depleted carboxylate solution to produce a regenerated carboxylate solution.

[0042] In still yet another aspect, there is provided a method, as described herein, wherein the alkaline solution comprises a hydroxide.

[0043] In yet still another embodiment, there is provided a method as described herein further comprising c-iv) returning the regenerated carboxylate solution to step b) as a wash solution.

[0044] Reference is now made to the attached figures. [Brief description of the drawings]

[0045] [Figure 1] FIG. 1 shows a flow diagram of an ion exchange process according to one embodiment of the method for removing / removing contaminants from an acidic solution containing scandium described herein. [Diagram 2] FIG. 2 shows a flow diagram of a scandium recovery process according to one embodiment combined with the method for removing / cleaning low concentrations of metal contaminants from acidic solutions containing scandium described herein. [Diagram 3] FIG. 3 shows a flow diagram of a method for regenerating citrate according to one embodiment combined with a method for removing / cleaning low concentrations of metal contaminants from an acidic solution containing scandium as described herein. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0046] The present disclosure relates to a method for removing at least one metal contaminant from a storage solution containing scandium. Scandium is present in a variety of storage solutions. In a method for improving the quality of titanium raw material, scandium is typically found in hydrochloric acid stored with some titanium at concentrations of about 30-40 mg / L and 300-400 mg / L, respectively. In such embodiments, storage solutions that can be used to recover Sc may have a mass ratio Ti / Sc of about 5 to about 50, about 5 to about 20, and about 10. In another embodiment, the storage solution may have a mass ratio Ti / Sc of about 10.

[0047] Titanium dioxide raw materials used in the chloride process for producing TiO2 pigments and in the production of titanium metal by the Kroll process can also be used to recover scandium. In those embodiments, nearly all of the scandium present in the raw materials ends up as waste chloride salts. This salt can be dissolved in weak hydrochloric acid to produce a waste chloride solution that can be neutralized, for example with lime, to precipitate the metal impurities in the form of waste solid hydroxides. Analysis of a typical titanium raw material shows that the estimated concentrations of Sc and Ti in the waste chloride solutions of these two processes are 25-100 mg / L Sc and about 5 g / L Ti before neutralization. In those embodiments, the waste chloride solutions can potentially be used to recover Sc, with a mass ratio Ti / Sc between 50 and 200.

[0048] Titanium dioxide raw material used in the sulfate process for producing TiO2 pigments can also be used to recover scandium, where a spent sulfuric acid solution is produced containing about 10-50 mg / L Sc and about 2-5 g / L Ti. Typical compositions of spent sulfuric acid are described in Li et al. (2018) and U.S. Patent No. 9,102,999. In this embodiment, the sulfuric acid solution has a mass ratio Ti / Sc that varies between about 100 and 400.

[0049] The present disclosure relates to a method for removing at least one metal contaminant from a scandium storage solution. The term "removing metal contaminants" is understood as removing one or more metal contaminants present in low concentrations in a solution containing scandium. In one embodiment, the metal contaminants are present in a scandium-containing storage solution at a concentration of less than 1 g / L, and in some embodiments, in a range of 0.2-0.4 g / L in a scandium-containing storage solution. Metal contaminants that may be removed by the methods described herein include titanium (Ti), thorium (Th) and zirconium (Zr), which have physical and chemical similarities to scandium (Sc). In a preferred embodiment, the metal contaminant to be removed is titanium. Ti has similar atomic size and properties to Sc. Sc and Ti are elements 21 and 22, respectively, in the periodic table.

[0050] The methods described herein include the use of ion exchange resins. An "ion exchange resin" is understood to be a resin that has an affinity for metal ion contaminants (e.g., iron, magnesium aluminum, titanium, thorium, copper and / or zirconium) as well as the metal ion of interest (e.g., scandium metal ion). The methods described herein allow the removal of metal ion contaminants from the metal ion of interest using ion exchange resins.

[0051] As used herein, a storage solution is an aqueous (acidic) solution containing scandium (Sc) and contaminants. In some embodiments, the storage solution containing scandium may be treated to remove suspended solid particles and reduce dissolved contaminants, particularly iron (Fe), magnesium (Mg) and / or aluminum (Al). As shown herein, suspended solids or high concentrations of dissolved contaminants such as iron (Fe) in the stored ion exchange solution may block the untreated solution from passing through the ion exchange column. Thus, a storage solution that has been treated to remove contaminants is understood to be one in which the concentration of contaminants does not block the ion exchange resin and does not create excessive operating pressures. In embodiments, the storage solution may be subjected to a (selective) solvent extraction before contacting the ion exchange resin. In another embodiment, the storage solution may be (selective) precipitated before contacting the ion exchange resin. In yet another embodiment, the storage solution may be placed in contact with the ion exchange resin and may further undergo an acid wash step before the removal step (as described below and shown in FIG. 1).

[0052] In the first step of the removal method, the storage solution is contacted with an ion exchange resin. The term "contacting the storage solution" is understood as bringing the solution into intimate contact with the ion exchange resin. This can be performed in various ways known to those skilled in the art. In a preferred embodiment, the solution is pumped through a column holding an ion exchange resin. The contacting step allows the resin to take up some of the contaminants as well as scandium, forming a metal-resin complex.

[0053] In a second step of the stripping method, the metal-resin complex is washed with a wash solution to remove at least a portion of the contaminants and further obtain a scandium ion exchange resin complex and a spent carboxylate solution. In the disclosed method, the wash solution has a maximum temperature of about 65° C., in some embodiments a temperature between about 40° C. and about 50° C., and in some embodiments a temperature of about 50° C.

[0054] The wash solution may also be a compound having at least one (and in some embodiments, multiple) carboxylate ion with a pKa in the range of 2.5 to 4. The carboxylate ion may be provided from an organic polyacid, where at least one carboxylate ion is neutralized (deprotonated with another cation). In some embodiments, the carboxylate ion may be present in citrate, tartrate, malate, malonate, lactate, as well as combinations thereof. In embodiments where citrate provides the carboxylate ion, the pH of the wash solution may be between about 3.0 and 4.0, but in some embodiments, between 3.0 and 3.8. In embodiments, the pH of the wash solution may be at least about 3.0, 3.1, 3.2, 3.3, 3.4, 3.5, 3.6, 3.7, 3.8 or 3.9 and / or no greater than about 4.0, 3.9, 3.8, 3.7, 3.6, 3.5, 3.4, 3.3, 3.2 or 3.1.

[0055] The compounds of the wash solution may also contain an alcohol moiety adjacent to the carboxylate ion.

[0056] In some embodiments, the wash solution is prepared in situ prior to adding the wash solution to the resin by neutralizing at least one carboxylate ion present in the organic polyacid (e.g., citric acid, tartaric acid, malic acid, and / or lactic acid, etc.). This can be done by combining the organic polyacid with a base (e.g., NaOH, KOH, or NH4OH) until such neutralization is achieved. In some embodiments, not all of the carboxylate moieties of the organic polyacid are neutralized. In certain embodiments, the organic polyacid is combined with a base under conditions that allow for a single carboxylate moiety to be neutralized by the organic polyacid molecule. For example, if the carboxylate ions are provided from citric acid, a sodium citrate solution is prepared and used as the wash solution.

[0057] In some embodiments, the carboxylate ions during the washing process may combine with at least a portion of the contaminants present in the metal ion exchange resin complex to produce at least a soluble metal contaminant complex. The term "soluble metal contaminant complex" refers to a complex between a metal contaminant (which necessarily excludes scandium) and a compound that contains a carboxylate ion. The soluble metal contaminant complex is then removed from the ion exchange resin by flushing with a washing solution.

[0058] Once the washing process is completed, the scandium loaded on the ion exchange resin can be further treated to elute the scandium and obtain a purified solid scandium product. In combination or in parallel, the spent carboxylate solution can be discarded or further regenerated to a washing solution (as shown in Figure 3). Briefly, the spent carboxylate solution can be regenerated by precipitating the solids of the spent carboxylate solution with an alkali (e.g. NaOH solution), separating the metal-containing solids and removing the impurities from the carboxylate solution, and then electrodialyzing the purified carboxylate solution. If necessary, the regenerated carboxylate solution can be used as a washing solution.

[0059] The attached Figures 1 and 2 together show a process 1 for recovering scandium from a storage solution, where Figure 1 relates to sector 3 of the process related to ion exchange and Figure 2 relates to sector 5 of the process related to the recovery and purification of scandium.

[0060] The operation 10, ion exchange adsorption, will now be described in more detail. Solid particles of ion exchange resin 11 are placed in a column and retained. A storage solution 12 containing scandium is passed through the column and contacts the ion exchange resin 11 retained in the column. The storage solution 12 containing scandium can be any one of a number of inorganic acids capable of extracting scandium, including hydrochloric acid (HCl), sulfuric acid (H2SO4), phosphoric acid (H3PO4), nitric acid (HNO3) and combinations thereof. In a preferred embodiment, the storage solution contains or is hydrochloric acid obtained from upgrading titanium dioxide raw material (ilmenite, titanium slag, etc.) or spent acid produced during the conversion of titanium dioxide raw material to titanium dioxide pigment or titanium metal. The ion exchange resin adsorbs scandium (Sc) as well as many other elements, which are considered herein as "metal contaminants", such as iron (Fe), titanium (Ti), zirconium (Zr), thorium (Th), magnesium (Mg), aluminum (Al), calcium (Ca), etc.

[0061] The ion exchange resin 11 contains at least one functional group selected from the group consisting of sulfonic acid, phosphonic acid, phosphinic acid, phosphonic acid monoethyl / diethyl ester, phosphonic acid / tertiary amine, phosphonic acid / dimethyl ester, and combinations thereof.

[0062] Purolite® S957 is commercially available as a macroporous chelating resin and is an embodiment of an ion exchange resin. Purolite® resin has two functional groups, sulfonic acid cation exchange sites (-SO3H) and phosphonic acid chelating sites (-PO(OH)2), as shown in Formula 1. [ka]

[0063] Without wishing to be bound by any theory, it is believed that scandium, titanium, and thorium in the storage solution 12 are Sc 3+ , TiO2 + , Th 4+This assumption is supported by literature data on the separation of Sc, Ti, and Th in acidic chloride solutions (Wood et al., 2006; Comb et al., 2009). a et al. 1987; Buettner et al., 2012 and Zebroski et al., 1951).

[0064] The sulfonic acid group is reacted with a proton (H + ) to metal ions (M n+ ) can be exchanged for [ka] In the formula, (r) represents the species on the resin surface, and (aq) represents the species in the bulk aqueous solution.

[0065] This is Fe 3+ , Al 3+ , Mg 2+ and Ca 2+ This is believed to be the mechanism by which the contaminants adhere to the resin. Thus, by passing a stronger acid solution, such as concentrated regenerated or purchased pure hydrochloric acid, through the resin, some of the contaminants (especially Fe) can be substantially removed from the resin.

[0066] In contrast, phosphonic acid groups form slightly different bonds with aqueous metal ions.

[0067] Adsorption with phosphonic acid groups in weak acid solutions can be generalized by reactions (2) and (3). [ka]

[0068] In strong acid solutions, metal ions can form strong coordination complexes with the oxygen of the P=O bond of the phosphoryl group, as generalized in reaction (4). [ka]

[0069] For some metal ions, the bond between the phosphonic acid group and the metal cation is so strong that it cannot be reversed by simply increasing the acidity of the solution, i.e., by reversing reactions (2), (3), or (4). The ion Sc 3+ , TiO 2+ , Th 4+ and possibly ZrO 2+ may form such a strong complex with the phosphonate group that it cannot be removed by strong acid washes, and another, stronger aqueous complexing agent may be required to cleave the phosphonate-metal bond.

[0070] Thus, the ion exchange adsorption operation 10 produces two process streams: scandium-lean storage acid 13 ("extraction raffinate") which exits the column, and resin 15 in the column which retains scandium and some of the metal ion impurities such as Fe, Mg, Al, Ca, Ti, Th, Zr.

[0071] Returning to FIG. 1, operation 20 ("Wash Fe, etc.") is a first optional operation of washing ion exchange resin 11 in which bulk / excess metal ions (Fe, Mg, Al, Ca, etc. that may have been removed by reaction (1)) found in storage solution 12 and bound on resin 15 are removed. This first bulk wash of resin 15 is performed with a strong acid 22, preferably The first impurity wash acid 22 may be a mixed acid, preferably with HCl, having a concentration of 10-25 wt% HCl. Thus, the first wash acid 22 is in the general concentration range of regenerating acids. It is believed that the first wash acid 22 protonates the sulfonic acid groups releasing large amounts of ions Fe, Mg, Al, Ca and other impurities (as well as some Sc, Ti, Th and Zr ions) from the resin 11. The first wash acid 22 leaves the column via an Fe-impurity wash raffinate solution 23 containing dissolved Fe impurities. The first wash operation 20 provides a resin 25 in a column suitable for the contaminant removal method described herein.

[0072] After operation 20, scandium and any remaining similar metal (Ti, Th and Zr) impurity complex / complexes remain on the resin 25, possibly bound to phosphonic acid groups. In this removal method (operation 30: "Washing Ti etc."), a carboxylate wash solution 32 is added to the column, which is or contains a salt. In a preferred embodiment, the carboxylate wash solution 32 comprises or is a sodium citrate solution having a pH of 3.0-4.0 (and in some embodiments, the pH is 3.8) and a temperature between ambient and 65°C (and in some embodiments, 50°C). The carboxylate wash solution 32 is intended to remove most of the adsorbed similar metal (Ti, Th and Zr) impurities from the resin, but not scandium. The carboxylate wash solution 32 leaves the column via a spent carboxylate ion solution 33, which contains dissolved and adsorbed metals, and enters the resin 35.

[0073] Without wishing to be bound by any theory, titanium may form strong aqueous complexes with the citrate ion. For example, [Ti(Hcit)3] 2- Complex anion (where "cit" is the citrate anion, C6H5O7 3- ) predominates at pH 3-4. The titanium washing operation can be understood based on reaction (5). [ka]

[0074] Sodium citrate (NaH2cit) solution can be prepared by neutralizing citric acid (H3cit) solution to pH 3-4, preferably pH 3.8. In the above titanium washing reaction, the stoichiometric ratio of titanium (Ti) and citrate (cit) is equal to 3.

[0075] It is speculated that thorium can form a strong soluble citrate complex at a pH of about 3.8, and therefore a significant proportion of thorium can be washed off when the loaded resin is washed with a sodium citrate solution, even more so when the washing temperature is from ambient to about 50° C., or even higher depending on the thermal stability limits of the resin.

[0076] 1, scandium can optionally be removed from the resin ("elution" at step 40) with an aqueous alkaline solution 43, typically a solution of sodium carbonate, sodium bicarbonate, sodium hydroxide, potassium carbonate, potassium bicarbonate, potassium hydroxide, ammonium carbonate, ammonium bicarbonate, and ammonium hydroxide in the concentration range of 5-20 wt%, and in some embodiments, a sodium carbonate solution at a concentration of about 15 wt%. The aqueous alkaline solution 43 exits the column along with an eluate 45 (containing the scandium).

[0077] In optional steps 50 and 60, the resin removed with the alkaline solution may be washed with water and regenerated with fresh hydrochloric acid (e.g., 5-15 wt% HCl) to complete the adsorption step (step 10). ) can be used again.

[0078] Without wishing to be bound by any theory, it is known that scandium is easily removed from Sc-loaded ion exchange resins using sodium carbonate solution. When sodium carbonate is in excess, the mechanism is thought to be as follows: [ka]

[0079] As shown in FIG. 2, once the scandium has eluted from the column it can be further purified. The scandium-containing "eluate" 45 is still fairly alkaline, but can be filtered or centrifuged (operation 70: solid / liquid separation) to remove any entrapped solids (residual compounds formed by metal ion hydrolysis). The solids 77 from operation 70 can be washed, neutralized with some acid, and discarded as residue 85 (operation 80). After operation 70, the scandium-containing "eluate" 75 is substantially unchanged from the eluate 45. In operation 90, the eluate 75 can be neutralized (e.g., pH 6.5) with a strong acid 93 (e.g., 18-35 wt % HCl) to precipitate solid crude (impure) scandium hydroxide / carbonate / bicarbonate 95. The solid crude scandium precipitate 95 can be washed and recovered by solid / liquid separation (operation 100) as washed solid crude (impure) scandium hydroxide / carbonate 105. In operation 110, scandium can be leached from the crude scandium precipitate 105 with an acid solution 113 (18-35 wt % HCl), preferably at pH 2.5 and 90° C. The product of operation 110 is a slurry 115 made up of scandium-containing leachate and undissolved solids. After further solid-liquid separation (operation 120), a scandium leachate 125 is obtained. The solution 125 can be treated with oxalic acid 133 to precipitate scandium oxalate crystals in the slurry 135 (operation 130). The scandium oxalate crystals 145 can be recovered by filtration (operation 140) and are finally calcined at about 900° C. for several hours to produce a scandium oxide product 155 (operation 150).

[0080] Those skilled in the art will appreciate that the final purity of the scandium oxide product 155 is directly affected by the initial purity of the scandium eluate 45 that enters purification. The methods described herein improve the purity of the scandium eluate, thereby increasing the final purity of the scandium oxide product.

[0081] FIG. 3 further illustrates the advantages of the method for removing scandium when sodium citrate is used as the wash solution and in particular how sodium citrate can be regenerated by electrodialysis, which provides a significant cost advantage to the present process. The spent carboxylate (citric acid) ion solution 33 obtained in operation 30 can be precipitated with sodium hydroxide 36 (in operation 30a). The impurity slurry 37 can be separated in operation 30b with discarded impurities 38 containing titanium separated from the aqueous phase 39 (filtrate) of the electrodialyzed citrate in operation 30c. The sodium citrate solution 39b after mixing and pH control is ready to be returned to the Ti wash operation 30 as regenerated carboxylate wash solution 39b. The regenerated sodium hydroxide solution 39a can be returned to operation 30a or mixed with (fresh) citric acid 39c in operation 30d to form a new sodium citrate solution 39d, which can be used as the carboxylate wash solution 32.

[0082] Example 1 Step 10 - Ion exchange adsorption A glass column measuring 61 cm (24 in) in height and 2.54 cm (1 in) in internal diameter was packed with 250 mL of Purolite® S957 resin to treat the hydrochloric acid stock solution of a TiO2 slag upgrading plant.

[0083] The storage solution 12 was pre-filtered to remove any suspended solids greater than 5 μm in size. After pre-filtration, the storage solution ("feed solution") 12 was pumped through a column packed with resin for scandium adsorption. In one adsorption test, the flow rate of the storage solution 12 through the column was kept constant at 1.32 L / h or 5.28 bed velocities per hour (BV / h) using a peristaltic pump. The column was heated to 55°C with hot water. Samples were taken from the outflow at various time intervals and analyzed for various elements. In addition, the scandium-poor storage acid 13 (herein identified as total extract raffinate) that exited the column ("extract raffinate") was collected and analyzed. Table 1 shows the analysis of the feed solution (storage acid with Sc) 12 and the total extract raffinate 13 after 200 BV (50 L).

[0084] [Table 1]

[0085] As shown in Table 1, the resin has a high affinity for scandium (Sc), zirconium (Zr), titanium (Ti) and thorium (Th). The resin also shows a significant affinity for iron (Fe).

[0086] Step 20 - Ion washing The scandium and other metal ion loaded resin from run 10 was treated successively with two acids for the first impurity wash stream 22, first with 2 L (8 BV) of industrially regenerated 18 wt % hydrochloric acid ("Wash Feed 1") and then with 1 L (4 BV) of pure 18 wt % hydrochloric acid ("Wash Feed 2") as described above, to see if some of the iron adsorbed on the resin could be removed. The temperature of the wash test was 55°C and the flow rate was constant at 0.66 L / h (2.64 BV / h). Table 2 below shows the analysis of the wash feed and the accumulated wash effluents ("Wash Raffinate 1" and "Wash Raffinate 2").

[0087] [Table 2]

[0088] As shown in Table 2, some of the adsorbed iron and approximately 10% of the adsorbed titanium were removed. The exact percentage of iron washed could not be estimated due to inaccuracies in the iron analysis. However, testing of subsequent process steps (operations 30-150) showed that performing operation 20 effectively prevented any contamination of the final scandium oxide product with iron.

[0089] Operation 30 - Cleaning of titanium, thorium and zirconium After the acid wash operation 20, the resin of Example 1 was washed with 1.5 L (6 BV) of pure water at a constant flow rate of 2.64 L / h (10.56 BV / h) at ambient temperature. The washed resin was then treated with a sodium citrate carboxylate wash solution 32 to remove most of the adsorbed titanium. The sodium citrate solution was previously prepared from a 15 wt % citric acid solution neutralized to pH 3.8 with sodium hydroxide. A total of 2.5 L (10 BV) of sodium citrate solution was pumped through the column at a constant flow rate of 0.66 L / h (2.64 BV / h) and ambient temperature. Table 3 below shows the composition of the accumulated titanium wash eluate 33 ("Wash Raffinate 3").

[0090] [Table 3]

[0091] Some titanium (about 25 wt%) was removed, as shown in Table 3. Some thorium and some zirconium that had accumulated in the column, essentially undetected, were also removed.

[0092] In another similar experiment, another capsule containing 15 wt% sodium citrate heated to 50°C was The wash was repeated with Carboxylate wash solution 32, all other conditions remaining the same. The results, shown in Table 4 below, clearly show that higher temperatures result in better washing of titanium, thorium and zirconium ions, with titanium in particular being completely removed from the resin.

[0093] [Table 4]

[0094] Procedure 40 - Dissolution of Scandium After washing with the sodium citrate solution, the resin was washed with 1.5 L (6 BV) of purified water at a constant flow rate of 2.64 L / h (10.56 BV / h) at ambient temperature (run 40). After washing with water, the resin was treated with a solution containing 15 wt% sodium carbonate. A total of 1.25 L (5 BV) of sodium carbonate solution was pumped through the column at a constant flow rate of 1.98 L / h (7.92 BV / h) and ambient temperature.

[0095] Table 5 provides the composition of the accumulated Sc eluate 45, which is rich in scandium ("eluate"), when the titanium, thorium and zirconium wash (operation 30) is carried out at room temperature (about 25°C).

[0096] [Table 5]

[0097] From Table 5, it can be estimated that about 95% or more of the scandium was recovered from the eluate. This result indicates that the eluate containing some titanium and some zirconium was not washed out in the previous operation 30.

[0098] Example 2 Procedure 30 - High temperature cleaning of titanium, thorium and zirconium with more concentrated sodium citrate solutions Table 6 shows a comparison of the composition of accumulated spent carboxylate ion solution 33 when cleaning titanium, thorium and zirconium using a 20 wt % sodium citrate solution at pH 3.5 at 50° C. and room temperature (25° C.).

[0099] [Table 6]

[0100] As can be seen from Table 6, when the second wash (run 30) was performed with a relatively warm carboxylate wash solution 32 of sodium citrate, the amounts of titanium, zirconium and thorium removed from the resin were even greater.

[0101] Operations 50 and 60 - Resin Cleaning and Regeneration After elution, the resin was rinsed one last time with pure water at ambient temperature and finally treated with 10 wt% hydrochloric acid (HCl) solution to restore its active components and regenerate the resin for use in scandium recovery in another adsorption-wash-elution cycle.

[0102] Example 3 Procedure 40 - Leaching of scandium without prior cleaning of titanium, thorium and zirconium After the acid wash (operation 20), the resin was washed with 1.5 L (6 BV) of purified water at a constant flow rate of 2.64 L / h (10.56 BV / h) at ambient temperature. After the water wash, the resin was not subjected to further washing, but was immediately treated with an alkaline solution 43 containing 15 wt % sodium carbonate to elute the scandium adsorbed on the resin.

[0103] During elution, a white precipitate was observed to form inside the column. This precipitate became very deep until a visible mass formed. Eventually the column became blocked and elution had to be stopped. Analysis of the aqueous solution filtered through the resin indicated that the solidified mass was rich in titanium.

[0104] Example 4 Procedure 30a-30d - Regeneration of sodium citrate solution About 25 L of wash raffinate 23 recovered in run 30 was treated with sodium hydroxide 36 to raise the pH to about 12. In this manner, titanium and other impurities in the form of solid hydroxides were precipitated (run 30a). The resulting impurity slurry 37 was filtered and the impure solids discarded (38) (run 30b).

[0105] 16 L of the filtrate was used as the anolyte in the electrodialysis test (run 30c) performed in an electrodialysis apparatus. Sodium hydroxide solution (8 L of 17 g / L NaOH) was used as the catholyte in the same electrodialysis apparatus. The electrodialysis apparatus consisted of (a) 12 compartments separated by alternating cation exchange and bipolar membranes, (b) a stainless steel cathode at one end and (c) a dimensionally stable anode (DSA) made of platinum / iridium coated titanium at the other end. Each membrane had a length of 380 cm 2 Both the anolyte and the catholyte were recirculated in a closed circuit between the reservoir and each electrodialysis compartment.

[0106] The test lasted for about 1 hour and 55 minutes. A concentrated solution of sodium hydroxide (8 L of 116 g / L NaOH) was prepared on the cathode side and a concentrated solution of sodium citrate (153 g / L citrate at pH 3.8) was prepared on the anode side. The current density was 150 mA / cm 2 (1500A / m 2 ). The current efficiency for producing sodium citrate was found to be equal to 81%, the current efficiency for producing sodium hydroxide was found to be 85%, and the estimated energy consumption was 1.63 kWh / kg for sodium citrate and 2.60 kWh / kg for sodium hydroxide. The overall reaction can be written in simplified form as follows: [ka]

[0107] The regenerated sodium citrate wash solution 32 is used in the titanium and thorium wash (operation 30), while the regenerated sodium hydroxide is used to precipitate impurities in the wash raffinate 33 (operation 30a) and in producing fresh (regenerated) sodium citrate solution by mixing with fresh citric acid solution until a final pH of 3.8 is reached.

[0108] Testing in Example 3 shows that at least 50% of the sodium citrate and sodium hydroxide can be regenerated in approximately 2 hours, providing a significant cost advantage to washing with sodium citrate (i.e., the present invention).

[0109] The above description is intended to be illustrative only, and those skilled in the art will understand that changes can be made to the described embodiments without departing from the invention disclosed. Still other modifications that fall within the scope of the invention will be apparent to those skilled in the art in light of a review of the present disclosure, and such modifications are intended to be included within the scope of the appended claims.

[0110] References Y.Li et al., Hydrometallurgy, vol.178(2018). U.S. Patent No. 9,102,999. SAWood et al.,Ore Geol.Rev.,vol.28(2006),pp.57-102. P. Comba and A. Merbach, Inorg. Chem., vol26(1987), pp.1315-1323. KMBuettner and AMValentine,Chem.Rev.,vol.112(2012),pp.1863-1881. ELZebroski et al., Am. Chem. Soc., vol. 73 (1951), pp. 5646-5650. [1] A method for removing at least one metal contaminant from a storage solution containing Sc, the method comprising: a) contacting the storage solution with an ion exchange resin to incorporate Sc and the at least one metal contaminant to produce a metal ion exchange resin complex; b) washing the metal-resin complex with a wash solution comprising a salt having a carboxylate ion with a pKa in the range of 2.5 to 4.0 to produce a Sc ion exchange resin complex and a spent carboxylate solution. [2] The method of [1], wherein the carboxylate ion is capable of combining with the at least one metal contaminant to produce a soluble metal contaminant complex. [3] Prior to step a), the process further comprises: ai) providing a first solution comprising Sc, said at least one metal contaminant and excess metal ions; a-ii) contacting the first solution with the ion exchange resin; a-iii) dissolving and removing the excess metal ions from the ion exchange resin by adding a strong acid to the ion exchange resin to form an acidic solution of the excess metal ions; a-iv) forming the preservation solution. [4] The method according to [3], wherein the excess metal ions include at least one of iron (Fe), magnesium (Mg), aluminum (Al), calcium (Ca), and combinations thereof. [5] The method according to [4], wherein the excess metal ions include Fe. [6] The method according to any one of [1] to [5], further comprising dissolving Sc from the ion exchange resin complex with an alkaline solution to produce a soluble Sc solution. [7] The method of [6], wherein the alkaline solution contains a hydroxide, carbonate or bicarbonate. [8] The method according to any one of [1] to [7], wherein the at least one metal contaminant is titanium (Ti), thorium (Th), or zirconium (Zr). [9] The method according to [8], wherein the at least one metal contaminant is Ti.

[10] The method according to any one of [1] to [9], wherein the salt is at least one of citrate, tartrate, malate, malonate, lactate, and combinations thereof.

[11] The method according to

[10] , wherein the salt is a citrate salt.

[12] The method according to any one of [1] to

[11] , wherein the ion exchange resin contains at least one of the following functional groups: sulfonic acid, phosphonic acid, phosphinic acid, phosphonic acid monoethyl / diethyl ester, phosphonic acid / tertiary amine, phosphonic acid / dimethyl ester, and combinations thereof.

[13] The method according to any one of [1] to

[12] , wherein the temperature of the cleaning solution is 65°C or lower.

[14] The method according to

[13] , wherein the temperature of the cleaning solution is between 20°C and 65°C.

[15] The method according to any one of [1] to

[14] , wherein the cleaning solution has a pH between 3.0 and 4.0.

[16] The method according to any one of [1] to

[15] , wherein the cleaning solution has a pH of about 3.8.

[17] c. The method according to any one of [1] to

[16] , further comprising regenerating the cleaning solution from the spent carboxylate solution.

[18] The regeneration of the spent carboxylate solution, ci) precipitating metal-containing solids from the spent carboxylate solution in an alkaline solution; c-ii) separating said metal-containing solids from said spent carboxylate solution to form a decontaminated carboxylate solution; and c-iii) electrodialyzing the depleted carboxylate solution to produce a regenerated carboxylate solution.

[19] The method of

[18] , wherein the alkaline solution contains a hydroxide.

[20] The method of

[18] or

[19] , further comprising c-iv) returning the regenerated carboxylate solution to step b) as the wash solution.

[21] A method for removing at least one of titanium (Ti), thorium (Th) and zirconium (Zr) from a storage solution containing Sc, the method comprising: a) contacting the storage solution with an ion exchange resin to incorporate Sc and at least one of Ti, Th, and Zr to produce a metal-resin complex; b) washing the metal resin complex with a wash solution comprising a salt having citrate ions at a pH between 3.0 and 4.0 to produce a Sc ion exchange resin complex and a spent carboxylate solution.

[22] The method of

[21] , wherein the citrate ions binding with the at least one of Ti, Th and Zr produce soluble Ti, Th and Zr contaminant complexes.

[23] Prior to step a), the process further comprises: ai) providing a first solution containing Sc, said at least Ti, Th and Zr, and an excess of metal ions; a-ii) contacting the first solution with the ion exchange resin; a-iii) dissolving and removing the excess metal ions from the ion exchange resin by adding a strong acid to the ion exchange resin to form an acidic solution of excess ions; a-iv) forming the preservation solution.

[24] The method of

[23] , wherein the excess ions are Fe, Mg, Al and combinations thereof.

[25] The method according to

[24] , wherein the excess metal ions include Fe.

[26] The method according to any one of

[21] to

[25] , further comprising dissolving Sc from the ion exchange resin complex with an alkaline solution to produce a soluble Sc solution.

[27] The method of

[26] , wherein the alkaline solution comprises a hydroxide, carbonate or bicarbonate.

[28] The method according to any one of

[21] to

[27] , wherein the ion exchange resin contains at least one of the following functional groups: sulfonic acid, phosphonic acid, phosphinic acid, phosphonic acid monoethyl / diethyl ester, phosphonic acid / tertiary amine, phosphonic acid / dimethyl ester, and combinations thereof.

[29] The method according to any one of

[21] to

[28] , wherein the temperature of the cleaning solution is 65°C or lower.

[30] The method according to

[29] , wherein the temperature of the cleaning solution is between 20°C and 65°C.

[31] The method according to any one of

[21] to

[30] , wherein the cleaning solution has a pH of about 3.8.

[32] c. The method according to any one of

[21] to

[31] , further comprising regenerating the cleaning solution from the used carboxylate solution.

[33] The regeneration of the spent carboxylate solution, ci) precipitating metal-containing solids from said spent carboxylate solution in an alkaline solution; c-ii) separating said metal-containing solids from said spent carboxylate solution to form a decontaminated carboxylate solution; and c-iii) electrodialyzing the depleted carboxylate solution to produce a regenerated carboxylate solution.

[34] The method of

[33] , wherein the alkaline solution comprises a hydroxide.

[35] The method of

[33] or

[34] , further comprising c-iv) returning the regenerated carboxylate solution to step b) as the wash solution.

Claims

1. 1. A system for removing at least one metal contaminant from a storage solution comprising Sc, the system comprising: a first compartment containing a storage solution containing said at least one metal contaminant; a column containing Sc and an ion exchange resin for capturing the at least one metal contaminant to produce a metal ion exchange resin complex; a second compartment containing a wash solution comprising a salt having a carboxylate ion with a pKa in the range of 2.5 to 4.0, said wash solution for washing said metal ion exchange resin complex to produce a Sc ion exchange resin complex and a spent carboxylate solution; a pump for pumping the storage solution from the first compartment to the column for contacting the storage solution with the ion exchange resin; and a pump for pumping said wash solution from said second compartment to said column for washing said metal ion exchange resin complex with said wash solution; Including, the system.

2. The Sc in the storage solution is Sc ３＋ The system of claim 1, wherein the compound is present in the ionic form of

3. 3. The system of claim 1 or 2, wherein the carboxylate ion is capable of combining with the at least one metal contaminant to produce a soluble metal contaminant complex.

4. The system of claim 1 , wherein the preservation solution is an aqueous acidic solution.

5. The system of claim 1 , wherein the at least one metal contaminant is titanium (Ti), thorium (Th), or zirconium (Zr).

6. The system of claim 5 , wherein the at least one metallic contaminant is Ti.

7. 7. The system of claim 1, wherein the salt is at least one of citrate, tartrate, malate, malonate, lactate, and combinations thereof.

8. The system of claim 7 , wherein the salt is a citrate salt.

9. 9. The system of any one of claims 1 to 8, wherein the ion exchange resin comprises at least one of the following functional groups: sulfonic acid, phosphonic acid, phosphinic acid, phosphonic acid monoethyl / diethyl ester, phosphonic acid / tertiary amine, phosphonic acid / dimethyl ester, and combinations thereof.

10. 10. The system of claim 1, wherein the cleaning solution has a pH between 3.0 and 4.

0.

11. The system of claim 10 , wherein the cleaning solution has a pH of about 3.

8.

12. 12. The system of claim 1, wherein the pump is a peristaltic pump.

13. 13. The system of claim 1, wherein the ion exchange resin is a solid particulate ion exchange resin.

14. 14. The system of claim 1, wherein the preservation solution comprises one or more of hydrochloric acid, sulfuric acid, phosphoric acid, and nitric acid.

15. The system of claim 14 , wherein the preservation solution comprises hydrochloric acid.

16. 16. The system of claim 1, wherein the ion exchange resin is a macroporous chelating resin.

17. 17. The system of claim 16, wherein the ion exchange resin has sulfonic acid cation exchange sites and phosphonic acid chelating sites.

18. 18. The system of claim 1, wherein the column is made of glass.

19. 19. The system of claim 1, wherein the carboxylate ions are present in citrate, tartrate, malate, malonate, lactate, or combinations thereof.