Glass-ceramic article and method of forming a plurality of features therein

Abstract

Glass-ceramic articles include a primary ceramic phase and an article thickness defined between a first major surface and a second major surface. Glass-ceramic articles include a plurality of features within an interior of the glass-ceramic article. The plurality of features include an amorphous glass phase. Methods of forming the plurality of features in the glass-ceramic article include emitting a burst of pulses from a laser that impinge the glass-ceramic article to form the plurality of features. In aspects, the burst of pulses melts a portion of a primary ceramic phase to form a feature comprising an amorphous glass phase within an interior of the glass-ceramic article.

Description

ATTORNEYDOCKETNO. SP23-332GLASS-CERAMIC ARTICLE AND METHOD OF FORMING A PLURALITY OFFEATURES THEREIN

[0001] This application claims the benefit of priority under 35 U.S.C. § 119 of U.S.Provisional Application Serial No.63 / 600,752 filed on November 20, 2023, the content of which is relied upon and incorporated herein by reference in its entirety. FIELD

[0002] The present disclosure relates generally to a glass-ceramic article and amethod of forming a plurality of features therein and, more particularly, to a glass-ceramic article comprising a plurality of features within an interior of the glass-ceramic article and methods of forming a plurality of features in a glass-ceramic article using a laser. BACKGROUND

[0003] It is known to use an apparatus in display devices including liquid crystaldisplays (LCDs) and the like to light a display. It is known to use glass-ceramics for the housings of consumer electronic devices, including display devices. However, there is a need to improve the fracture toughness of glass-ceramics. SUMMARY

[0004] The aspects of the disclosure can provide glass-ceramic articles including aplurality of features internal to the glass-ceramic article. As demonstrated by the Examples herein, the plurality of features interior to the glass-ceramic article increase a fracture toughness KIC of the glass-ceramic article (e.g., relative to a glass-ceramic article without the plurality of features by 10% or more, from about 10% to about 35%, or from about 10% to about 20%). Without wishing to be bound by theory, it is believed that the plurality of features interior to the glass-ceramic article increases the fracture toughness KICby deflecting cracks and / or interrupting crack propagation within the glass-ceramic article. Also, a tilt angle of the features of the plurality of features can be controlled to further increase the fracture toughness.

[0005] Methods of the present disclosure can form the plurality of features interiorto the glass-ceramic article by impinging a focused (e.g., line focus) laser beam (e.g.,ATTORNEYDOCKETNO. SP23-332 plurality of pulses) within the glass-ceramic article. The pulsed laser can quickly form the plurality of features. The shape and / or length of the features can be controlled by adjusting the beam shape, focusing optics, and other properties of an optical apparatus including the laser.

[0006] Aspect 1. A glass-ceramic article comprising:a first major surface, a second major surface opposite the first major surface, and an article thickness defined therebetween; a primary ceramic phase; and a plurality of features within an interior of the glass-ceramic article, the plurality of features comprising an amorphous glass phase, a height in a direction of the article thickness.

[0007] Aspect 2. The glass-ceramic article of aspect 1, wherein a minimumdistance between a feature of the plurality of features and the first major surface is in a range from about 10 micrometers to about 100 micrometers.

[0008] Aspect 3. The glass-ceramic article of any one of aspects 1-2, wherein a tiltangle relative to the direction of the article thickness of a feature of the plurality of features is in a range from about 0° to about 60°.

[0009] Aspect 4. The glass-ceramic article of aspect 3, wherein the tilt angle is ina range from about 30° to about 60°.

[0010] Aspect 5. The glass-ceramic article of aspect 3, wherein the tilt angle is ina range from about 0° to about 30°.

[0011] Aspect 6. The glass-ceramic article of any one of aspects 1-5, wherein a firstset of features of the plurality of features are arranged in a line between the first major surface and the second major surface.

[0012] Aspect 7. The glass-ceramic article of aspect 6, wherein the height of a firstfeature in the first set of features is in a range from about 5 micrometers to about 500 micrometers.

[0013] Aspect 8. The glass-ceramic article of aspect 6, wherein the height of a firstfeature in the first set of features as a percentage of the article thickness is in a range from about 5% to about 30%.ATTORNEYDOCKETNO. SP23-332

[0014] Aspect 9. The glass-ceramic article of any one of aspects 1-5, wherein theheight of the feature of the plurality of features as a percentage of the article thickness is in a range from about 50% to about 95%.

[0015] Aspect 10. The glass-ceramic article of any one of aspects 1-9, wherein eachfeature of the plurality of features extends along a corresponding axis, and a distance between the axes of an adjacent pair of features of the plurality of features is in a range from about 30 micrometers to about 300 micrometers.

[0016] Aspect 11. The glass-ceramic article of any one of aspects 1-5, wherein eachfeature of the plurality of features extends along a corresponding axis, and a first axis of a first feature of the plurality of features is colinear with a second axis of a second feature of the plurality of features.

[0017] Aspect 12. The glass-ceramic article of any one of aspects 10-11, whereina width of a feature of the plurality of features perpendicular to the axis of the feature is in a range from about 500 nanometers to about 200 micrometers.

[0018] Aspect 13. The glass-ceramic article of aspect 12, wherein the width of thefeature is in a range from about 10 micrometers to about 50 micrometers.

[0019] Aspect 14. The glass-ceramic article of any one of aspects 1-13, wherein afracture toughness KICof the glass-ceramic article is about 1.9 MPa√m or more.

[0020] Aspect 15. The glass-ceramic article of aspect 14, wherein the fracturetoughness KICis in a range from about 1.95 MPa√m to about 2.1 MPa√m.

[0021] Aspect 16. The glass-ceramic article of any one of aspects 1-13, wherein afracture toughness KIC of the glass-ceramic article is greater than a fracture toughness KIC of another glass-ceramic article identical to the glass-ceramic article but without the plurality of features by about 5% or more.

[0022] Aspect 17. The glass-ceramic article of aspect 16, wherein the fracturetoughness KICof the glass-ceramic article is greater than the fracture toughness KICof the another glass-ceramic article identical to the glass-ceramic article but without the plurality of features by from about 10% to about 20%.

[0023] Aspect 18. The glass-ceramic article of any one of aspects 1-17, whereinthe primary ceramic phase comprises β-spodumene, β-quartz, nepheline, cordierite, spinel, lithium disilicate, or a combination thereof.ATTORNEYDOCKETNO. SP23-332

[0024] Aspect 19. The glass-ceramic article of any one of aspects 1-18, wherein afeature of the plurality of features is surrounded by the primary ceramic phase.

[0025] Aspect 20. The glass-ceramic article of any one of aspects 1-19, whereinthe article thickness is in a range from about 100 micrometers to about 5 millimeters.

[0026] Aspect 21. A method of forming a plurality of features in a glass-ceramicarticle, the glass-ceramic article comprising a primary ceramic phase, a first major surface, a second major surface opposite the first major surface, and an article thickness defined between the first major surface and the second major surface, the method comprising: adjusting a lens to create a line focus within the glass-ceramic article; emitting a burst of pulses from a laser; transmitting the burst of pulses through the lens; and impinging the burst of pulses on the glass-ceramic article to form the plurality of features, wherein the burst of pulses melts a portion of the primary ceramic phase to form a feature of the plurality of features comprising an amorphous glass phase, the plurality of features comprising a height in a direction of the article thickness, and the plurality of features are formed within an interior of the glass-ceramic article.

[0027] Aspect 22. The method of aspect 21, wherein a pulse of the burst of pulsescomprising an energy in a range from about 1 microjoule to about 50 microjoules, and pulses of the burst of pulses are generated at a rate from about 50 kilohertz to about 1 megahertz.

[0028] Aspect 23. The method of any one of aspects 21-22, wherein an opticalwavelength associated with the burst of pulses is in a range from about 300 nanometers to about 1500 nanometers.

[0029] Aspect 24. The method of aspect 23, wherein the optical wavelength is in arange from about 700 nanometers to about 1200 nanometers.

[0030] Aspect 25. The method of any one of aspects 21-24, wherein a pulse widthof a pulse of the burst of pulses is in a range from about 500 femtoseconds to about 50 nanoseconds.

[0031] Aspect 26. The method of aspect 25, wherein the pulse width is in a rangefrom about 1 picosecond to about 10 picoseconds.ATTORNEYDOCKETNO. SP23-332

[0032] Aspect 27. The method of any one of aspects 21-26, wherein a length of theline focus is in a range from about 10 micrometers to about 1 millimeter.

[0033] Aspect 28. The method of any one of aspects 21-24, wherein a shape of apulse of the burst of pulses is Gaussian, Bessel, or Airy.

[0034] Aspect 29. The method of any one of aspects 21-28, further comprisingimpinging the burst of pulses on a spatial light modulator to generate a plurality of spatially distinct beam spots for each pulse of the burst of pulses, and impinging the plurality of spatially distinct beam spots on the generate a set of features of the plurality of features.

[0035] Aspect 30. The method of any one of aspects 21-29, wherein a minimumdistance between a feature of the plurality of features and the first major surface is in a range from about 10 micrometers to about 100 micrometers.

[0036] Aspect 31. The method of any one of aspects 21-30, wherein a tilt anglerelative to the direction of the height of a feature of the plurality of features is in a range from about 0° to about 60°.

[0037] Aspect 32. The method of aspect 31, wherein the tilt angle is in a range fromabout 30° to about 60°.

[0038] Aspect 33. The method of aspect 31, wherein the tilt angle is in a range fromabout 0° to about 30°.

[0039] Aspect 34. The method of any one of aspects 21-33, wherein a first set offeatures of the plurality of features are arranged in a line between the first major surface and a second major surface.

[0040] Aspect 35. The method of aspect 34, wherein the burst of pulses forms thefirst set of features.

[0041] Aspect 36. The method of any one of aspects 21-33, wherein each featureof the plurality of features extends along a corresponding axis, and a first axis of a first feature of the plurality of features is colinear with a second axis of a second feature of the plurality of features.

[0042] Aspect 37. The method of any one of aspects 34-35, wherein the height ofa first feature in the first set of features is in a range from about 5 micrometers to about 500 micrometers.ATTORNEYDOCKETNO. SP23-332

[0043] Aspect 38. The method of any one of aspects 34-35, wherein the height ofa first feature in the first set of features as a percentage of the article thickness is in a range from about 5% to about 30%.

[0044] Aspect 39. The method of any one of aspects 31-33, wherein the height ofthe feature of the plurality of features as a percentage of the article thickness is in a range from about 50% to about 95%.

[0045] Aspect 40. The method of any one of aspects 31-34, wherein each featureof the plurality of features extends along a corresponding axis, and a distance between the axes of an adjacent pair of features of the plurality of features is in a range from about 30 micrometers to about 300 micrometers.

[0046] Aspect 41. The method of aspect 35 or aspect 40, wherein a width of afeature of the plurality of features perpendicular to the axis of the feature is in a range from about 500 nanometers to about 200 micrometers.

[0047] Aspect 42. The method of aspect 41, wherein the width of the feature is ina range from about 10 micrometers to about 50 micrometers.

[0048] Aspect 43. The method of any one of aspects 31-42, wherein a fracturetoughness KICof the glass-ceramic article is about 1.9 MPa√m or more.

[0049] Aspect 44. The method of aspect 43, wherein the fracture toughness KIC isin a range from about 1.95 MPa√m to about 2.1 MPa√m.

[0050] Aspect 45. The method of any one of aspects 31-42, wherein a fracturetoughness KIC of the glass-ceramic article is greater than a fracture toughness KIC of another glass-ceramic article identical to the glass-ceramic article but without the plurality of features by about 5% or more.

[0051] Aspect 46. The method of aspect 45, wherein the fracture toughness KIC ofthe glass-ceramic article is greater than the fracture toughness KICof the another glass- ceramic article identical to the glass-ceramic article but without the plurality of features by from about 10% to about 20%.

[0052] Aspect 47. The method of any one of aspects 31-46, wherein the primaryceramic phase comprises β-spodumene, β-quartz, nepheline, cordierite, spinel, lithium disilicate, or a combination thereof.ATTORNEYDOCKETNO. SP23-332

[0053] Aspect 48. The method of any one of aspects 31-47, wherein a feature ofthe plurality of features is surrounded by the primary ceramic phase.

[0054] Aspect 49. The method of any one of aspects 31-48, wherein the articlethickness is in a range from about 100 micrometers to about 5 millimeters. BRIEF DESCRIPTION OF THE DRAWINGS

[0055] These and other features, aspects and advantages are better understoodwhen the following detailed description is read with reference to the accompanying drawings, in which:

[0056] FIG. 1 illustrates a cross-sectional side view of exemplary glass-ceramicarticle with a plurality of features according to aspects of the present disclosure;

[0057] FIG. 2 illustrates a cross-sectional side view of another exemplary glass-ceramic article with a plurality of features according to aspects of the present disclosure;

[0058] FIG. 3 is an enlarged view 3 of FIG. 2 illustrating a set of features of theplurality of features;

[0059] FIG. 4 illustrates a cross-section taken along the line 4-4 in FIG. 3;

[0060] FIG. 5 illustrates an optical apparatus that can be used in a method ofmaking a plurality of features in a glass-ceramic article;

[0061] FIG. 6 is an enlarged view 6 of FIG. 5 illustrating a line focus within theglass-ceramic article;

[0062] FIG. 7 illustrates a configuration for determining fracture toughness KIC ina double-cantilever beam method;

[0063] FIG. 8 illustrates a cross-sectional view of a glass-ceramic article with aplurality of features having an amorphous glass phase from a scanning electron microscope (SEM);

[0064] FIG. 9 is a top cross-sectional view of a glass-ceramic article in theconfiguration for the double-cantilever beam method;

[0065] FIG.10 illustrates a side of the glass-ceramic article with a plurality of laserlines and associated plurality of features in the configuration for the double-cantilever beam method;ATTORNEYDOCKETNO. SP23-332

[0066] FIG. 11 illustrates a side of the glass-ceramic article with a plurality oflaser lines and associated plurality of features at an inclination angle of 45° with crack deflection in the double-cantilever beam method;

[0067] FIG.12 illustrates a side of the glass-ceramic article with a plurality of laserlines and associated plurality of features at an inclination angle of 30° with crack deflection in the double-cantilever beam method;

[0068] FIG.13 illustrates a side of the glass-ceramic article with a plurality of laserlines and associated plurality of features at an inclination angle of 0° with crack deflection in the double-cantilever beam method;

[0069] FIG. 14 illustrates a top cross-sectional view of the glass-ceramic articlewith crack deflection in the double-cantilever beam method; and

[0070] FIG. 15 illustrates a cross-sectional view of the glass-ceramic article withthe plurality of features having an amorphous glass phase with crack deflection in the double-cantilever beam method as imaged using a scanning electron microscope (SEM).

[0071] Throughout the disclosure, the drawings are used to emphasize certainaspects. As such, it should not be assumed that the relative size of different regions, portions, and substrates shown in the drawings are proportional to its actual relative size, unless explicitly indicated otherwise. DETAILED DESCRIPTION

[0072] Aspects will now be described more fully hereinafter with reference to theaccompanying drawings in which example aspects are shown. Whenever possible, the same reference numerals are used throughout the drawings to refer to the same or like parts.

[0073] FIGS. 1-2 illustrate cross-sectional views of glass-ceramic articles 101 and201 comprising a plurality of features 111 and 211 in accordance with aspects of thedisclosure. Unless otherwise noted, a discussion of features of aspects of one planarization layer or coated article can apply equally to corresponding features of any aspects of the disclosure. For example, identical part numbers throughout the disclosure can indicate that, in some aspects, the identified features are identical to one another and that the discussion of the identified feature of one aspect, unless otherwise noted, can apply equally to the identified feature of any of the other aspects of the disclosure.ATTORNEYDOCKETNO. SP23-332

[0074] As shown in FIGS. 1-2, the glass-ceramic article 101 and 201 comprises asubstrate 103 comprises a first major surface 105 and a second major surface 107 oppositethe first major surface 105. In aspects, the first major surface 105 can extend along a firstplane, the second major surface 107 can extend along a second plane, and / or the secondplane can be parallel to the first plane. As used herein, an article thickness 109 is definedbetween the first major surface 105 and the second major surface 107 as an averagedistance therebetween. In aspects, the article thickness 109 can be about 10 micrometers(µm) or more, about 25 µm or more, about 50 µm or more, about 75 µm or more, about 100 µm or more, about 125 µm or more, about 150 µm or more, about 200 µm or more, about 250 µm or more, about 300 µm or more, about 400 µm or more, about 500 µm or more, about 700 µm or more, about 1000 µm or more, about 5 millimeters (mm) or less, about 2 mm or less, about 1 mm or less, about 800 µm or less, about 600 µm or less, about 500 µm or less, about 300 µm or less, about 200 µm or less, about 150 µm or less, or about100 µm or less. In aspects, the article thickness 109 can range from about 10 µm to about5 mm, from about 25 µm to about 5 mm, from about 50 µm to about 5 mm, from about 75 µm to about 5 mm, from about 100 µm to about 5 mm, from about 125 µm to about 2 mm, from about 150 µm to about 1 mm, from about 200 µm to about 800 µm, from about 250 µm to about 600 µm, from about 300 µm 500 µm, from about 400 µm to about 500 µm, or any range or subrange therebetween. In aspects, although not shown, the article thickness109 can be substantially constant along a significant amount of the substrate 103, forexample due to a substantially parallel arrangement of the first major surface 105 and thesecond major surfaces 107. Alternatively, although not shown (e.g., rather than extendingparallel to one another), the major surfaces may extend at an acute angle relative to one another, wherein a local distance therebetween can vary along a length and / or a width ofthe substrate 103.

[0075] The substrate 103 can comprise primary ceramic phase. In aspects, thesubstrate 103 can be a ceramic-based material, for example, with the primary ceramic phaseand an optional amorphous phase (not including the plurality of features 111 and 211discussed herein). As used herein, “ceramic-based” includes both ceramics and glass- ceramics, wherein glass-ceramics have one or more crystalline phases and an amorphous, residual glass phase. Ceramic-based materials may be strengthened (e.g., chemicallyATTORNEYDOCKETNO. SP23-332 strengthened). In aspects, a ceramic-based material can be formed by heating a glass-based material to form ceramic (e.g., crystalline) portions. In further aspects, ceramic-based materials may comprise one or more nucleating agents that can facilitate the formation of crystalline phase(s). In aspects, ceramic-based materials can comprise one or more oxides, nitrides, oxynitrides, carbides, borides, and / or silicides. Example aspects of ceramic oxides include zirconia (ZrO2), zircon (ZrSiO4), titania (TiO2), hafnium oxide (Hf2O), yttrium oxide (Y2O3), iron oxides, beryllium oxides, vanadium oxide (VO2), fused quartz, cristobalite, mullite (a mineral comprising a combination of aluminum oxide and silicon dioxide), and spinel (MgAl2O4). Example aspects of ceramic nitrides include silicon nitride (Si3N4), aluminum nitride (AlN), gallium nitride (GaN), beryllium nitride (Be3N2), boron nitride (BN), tungsten nitride (WN), vanadium nitride, alkali earth metal nitrides (e.g., magnesium nitride (Mg3N2)), nickel nitride, and tantalum nitride. Example aspects of oxynitride ceramics include silicon oxynitride, aluminum oxynitride, and a SiAlON (a combination of alumina and silicon nitride and can have a chemical formula, for example, Si12-m-nAlm+nOnN16-n, Si6-nAlnOnN8-n, or Si2-nAlnO1+nN2-n, where m, n, and the resulting subscripts are all non-negative integers). In aspects, the primary ceramic phase of thesubstrate 103 can comprise β-spodumene, β-quartz, nepheline, cordierite, spinel, lithiumdisilicate, or a combination thereof.

[0076] In aspects, the glass-ceramic article can comprise a composition, based on100 mol% of the glass-ceramic article of: from about 50 mol% to about 75 mol% SiO2, from about 55 mol to about 65 mol%, from about 59 mol% to about 64 mol%, from about 60 mol% to about 63 mol%), from about 1 mol% to about 5 mol% Al2O3 (e.g., from about 1.0 mol% to about 4 mol%, from about 1.0 mol% to about 3 mol%, from about 1.2 mol% to about 2.0 mol%), from about 10 mol% to about 40 mol% Li2O (e.g., from about 15 mol% to about 35 mol%, from about 20 mol% to about 30 mol%, from about 22 mol% to about 27 mol%), from about 0 mol% to about 5 mol% Na2O (e.g., from about 0.5 mol% to about 4 mol%, from about 1.0 mol to about 3 mol, from about 1.5 mol% to about 2.5 mol%), from about 0 mol% to about 5 mol% MgO (e.g., from about 0 mol% to about 3 mol%, from about 0 mol% to about 1 mol%, from about 0 mol% to about 0.5 mol%), from about 2 mol% to about 10 mol% CaO (e.g., from about 4 mol% to about 9 mol%, from about 5 mol% to about 8 mol%, from about 6 mol% to about 7 mol%), from about 0.1 molATTORNEYDOCKETNO. SP23-332 to about 3 mol% P2O5 (e.g., from about 0.5 mol% to about 2.5 mol%, from about 1.0 mol% to about 2.2 mol%, from about 1.5 mol% to about 2.0 mol%), and from about 0 mol% to about 5 mol% F- (e.g., from about 0.1 mol% to about 4 mol%, from about 0.5 mol% to about 3, from about 1.0 mol% to about 2.0 mol%). In further aspects, the primary ceramic phase can be lithium disilicate. In even further aspects, the primary ceramic phase can comprise lithium disilicate as a primary ceramic phase and apatite (e.g., fluoroapatite) as a secondary phase.

[0077] In aspects, the substrate 103 can be optically transparent. As used herein,“optically transparent” or “optically clear” means an average transmittance of 70% or more in the wavelength range of 400 nm to 700 nm through a 1.0 mm thick piece of a material.In aspects, the substrate 103 may have an average transmittance of 75% or more, 80% ormore, 85% or more, or 90% or more, 92% or more, 94% or more, 96% or more in the wavelength range of 400 nm to 700 nm through a 1.0 mm thick piece of the material. The average transmittance in the wavelength range of 400 nm to 700 nm is calculated by measuring the transmittance of whole number wavelengths from about 400 nm to about 700 nm and averaging the measurements.

[0078] With reference to FIGS. 1-2, the substrate 103 (e.g., glass-ceramic article101 or 201) comprises a plurality of features 111 or 211 internal to the substrate 103.Throughout the disclosure, a feature is “internal” to a substrate or “within an interior” of the substrate if the feature does not comprise nor intersect a first major surface of the substrate, any major surface opposite the first major surface (e.g., second major surface), or any edge extending between the major surfaces. In aspects, the one or more (e.g., all) ofthe plurality of features 111 or 211 can be positioned within an interior of the substrate 103(e.g., glass-ceramic article 101 or 201). For example, with reference to FIGS. 1-2, theplurality of features 111 or 211 are within an interior of the substrate 103 because they donot comprise nor do they intersect the first major surface 105, the second major surface107 (shown as opposite the first major surface 105), or any edge of the substrate. In furtheraspects, as shown in FIGS. 1-3, one or more (e.g., all) features of the plurality of features111 or 211 can be separated from the first major surface 105 by a minimum distance 116or 216 (i.e., between dashed line 115 or 215 and first major surface 105) measured in adirection 102 of the article thickness 109 that is 10 µm or more, about 20 µm or more,ATTORNEYDOCKETNO. SP23-332 about 30 µm or more, about 40 µm or more, about 50 µm or more, about 100 µm or less, about 80 µm or less, about 60 µm or less, about 50 µm or less, about 40 µm or less, orabout 30 µm or less. In further aspects, the minimum distance 116 or 216 that the one ormore (e.g., all) features of the plurality of features 111 or 211 can be separated from thefirst major surface 105 measured in a direction 102 of the article thickness 109 can be in arange from about 10 µm to about 100 µm, from about 20 µm to about 80 µm, from about 30 µm to about 60 µm, from about 40 µm to about 50 µm, or any range or subrangetherebetween. For example, in even further aspects, as shown in FIG. 1, all of the featuresof the features can be positioned a minimum distance 116 within one or more of the rangesdiscussed above in this paragraph. In further aspects, all of the plurality of features 111 (asshown in FIG. 1) or a set of the plurality of features 211 (e.g., features 214a and 214dshown in FIG. 2) can have a peripheral portion (e.g., see points 311a, 315a, and / or 315din FIG. 3) along the dashed line 115 or 215 (e.g., positioned substantially the same theminimum distance 116 or 216 from first major surface 105). In further aspects, as shownin FIGS. 1-2, one or more features of the plurality of features 111 or 211 can be positioneda minimum distance 118 or 218 from the second major surface 107 (e.g., extending alongdashed line 117 or 217). In aspects, although not shown, the dashed line may impinge theperipheral portion at a single point depending on the shape of the feature.

[0079] In aspects, one or more features of the plurality of features 111 or 211 cancomprise an amorphous glass phase. In further aspects, substantially all and / or all of thefeatures of the plurality of features 111 or 211 can comprise an amorphous glass phase. Infurther aspects, the features (e.g., features 113a, 113b, and / or 214a-214f) of the pluralityof features 111 or 211 can be surrounded by the primary ceramic phase. For example, asdiscussed with reference to FIG. 8, the plurality of features (e.g., features 805a, 805b,805c, and / or 805d) comprise an amorphous glass phase surrounded by a primary ceramicphase 801 of the substrate (e.g., glass-ceramic article). Without wishing to be bound bytheory, as described below with reference to the method of making the ceramic-based article, it is believed that impinging the substrate with electromatic radiation (e.g., a burst of pulses of a laser) modify the primary ceramic phase by melting ceramic crystals at localized portions of the substrate within the interior of the substrate to form the amorphousATTORNEYDOCKETNO. SP23-332 glass phase of features of the plurality of features surrounded by the primary ceramic phase (e.g., largely undisturbed outside of the features).

[0080] The feature 214a will be described below with the understanding that thedescription can equally apply to the features 113a-113b and / or 214b-214f of the pluralityof features 111 and / or 211. In aspects, as shown in FIG. 3, the feature 214a comprises aplurality of points 311a, 313a, 315a, and 317a defining a periphery (i.e., outer periphery)of the feature 214. Similarly, feature 214b can comprise points 311b, 313b, 315b, and317b on the periphery, feature 214d can comprise points 315d and 317d on the periphery,and / or feature 214e can comprise points 315e and 317e on the periphery. Although, thepoints define a rectangular cross-section, it is to be understood that the cross-section can be polygonal, curved, and / or curvilinear, for example, oval-shaped and / or tear-drop- shaped. As used herein, a “height” or “feature height” of a feature is defined as a maximum distance, measured as a component in the direction of the article thickness, of a path extending between points on the periphery of the corresponding feature that is entirely within the feature (excluding any incidental portion at the end-points). For example, asshown in FIG. 2-3, the feature height 212 of feature 214a is a component in the direction102 of the article thickness 109 (see FIG.2) of a path extending between points (e.g., point311a and point 313a or 317a, point 315a and point 313a or 317a) on the periphery of thefeature 214a that is entirely within the feature (other than any incidental portion at the endpoints) the maximizes the feature height 212.

[0081] In aspects, the feature height 119 and / or 212 can be about 5 µm or more,about 10 µm or more, about 20 µm or more, about 30 µm or more, about 50 µm or more, about 70 µm or more, about 100 µm or more, about 500 µm or less, about 400 µm or less, about 300 µm or less, about 250 µm or less, about 200 µm or less, about 150 µm or less, about 100 µm or less, about 80 µm or less, or about 50 µm or less. In aspects, the featureheight 119 and / or 212 can be in a range from about 5 µm to about 500 µm, from about 10µm to about 400 µm, from about 20 µm to about 300 µm, from about 30 µm to about 250 µm, from about 40 µm to about 200 µm, from about 50 µm to about 150 µm, from about 70 µm to about 100 µm, or any range or subrange therebetween. Alternatively oradditionally, for example with reference to features (e.g., features 113a-113b) of theplurality of features 111 shown in FIG. 1, the feature height 119 as a percentage of theATTORNEYDOCKETNO. SP23-332article thickness 109 can be about 50% or more, about 60% or more, about 70% or more,about 75% or more, about 80% or more, about 85% or more, about 95% or less, about 90% or less, about 85% or less, about 80% or less, about 75% or less, about 70% or less, orabout 60% or less. For example, with reference to features (e.g., features 113a-113b) ofthe plurality of features 111 shown in FIG. 1, the feature height 119 as a percentage of thearticle thickness 109 can be in a range from about 50% to about 95%, from about 60% toabout 90%, from about 65% to about 85%, from about 70% to about 80%, from about 75%to about 80%, or any range or subrange therebetween. For example, feature 113a canextend for a majority of the article thickness (e.g., feature height 119 is 50% or more of thearticle thickness 109), and / or substantially all of the features 113a-113b of the plurality offeatures 111 can comprise a feature height within one or more of the ranges discussedabove for the feature height 119. Alternatively, feature 214a can extend for less than amajority of the article thickness and / or be aligned in a line (e.g., axis 301, 316a, and / or316a) with other features (e.g., features 214b and / or 214c) between the first major surface105 and the second major surface 107. Alternatively or additionally, for example withreference to features (e.g., features 214-214f) of the plurality of features 211 shown in FIG.2, the feature height 212 as a percentage of the article thickness 109 can be about 5% ormore, about 8% or more, about 10% or more, about 12% or more, about 15% or more, about 20% or more, about 35% or less, about 30% or less, about 25% or less, about 20% or less, about 15% or less, or about 10% or less. For example, with reference to features(e.g., features 214a-214f) of the plurality of features 211 shown in FIG. 2, the featureheight 212 as a percentage of the article thickness 109 can be in a range from about 5% toabout 35%, from about 8% to about 35%, from about 10% to about 35%, from about 10% to about 30%, from about 10% to about 20%, from about 15% to about 20%, or any range or subrange therebetween. In aspects, the substantially all or all of the features of the plurality of features can comprise the same feature height, for example, within one or moreof the ranges discussed above with reference to the feature height 119 and / or 212.

[0082] In aspects, as shown in FIGS. 3-4, a feature 214e can extend along an axis316c. As shown in FIG. 3, the axis 316c of feature 214e can extend parallel to (and / or co-linear with) a path between points on the periphery of the feature 214e (e.g., path betweenpoint 315e and 317e). The axis 316c can be a central axis of the feature 214e. The axisATTORNEYDOCKETNO. SP23-332316c can extend through a centroid of the cross-section shown in FIG. 4 (taken along line4-4 in FIG. 3) and / or extend through the centroid of a plurality of cross-sections (e.g., allcross-sections) of the feature taken perpendicular to the axis. For example, as shown inFIG. 3, feature 214a extends along axis 316a, feature 214b extends along axis 316b, andfeature 214d extends along axis 316d. In aspects, as shown in FIG. 3, the axes 316a and316b of a set of features (i.e., features 214a and 214b) can be parallel and / or colinear. Inaspects, as shown in FIG. 3, a set of features (e.g., features 214a and 214b) can extendalong a common axis 301, which can be colinear with or identical to the axis 316a and / or316b that the individual features 214a and 216b extend along. Consequently, the set offeatures (e.g., features 214a, 214b, and 214c shown in FIG. 2) can be arranged in a line213a extending between the first major surface 105 and the second major surface. In furtheraspects, the plurality of features (e.g., features 214a-214f) can comprise a plurality of setsof features with the features in each set of features arranged in a line. In even further aspects, the lines associated with the plurality of sets of features can be substantiallyparallel and / or parallel to an adjacent line and / or all of the lines. Similarly, features 214dand 214e can extend along axes 316c and / or 316d that are colinear with and / or identicalto axis 303 and / or arranged in a line 213b between the first major surface 105and thesecond major surface (see FIG. 2).

[0083] Throughout the disclosure, a “tilt angle” is defined as an angle between 0°and 90° formed between the axis that the feature extends along and a direction of the articlethickness. For example, as shown in FIG. 3, the tilt angle 321 of feature 214a is defined asan angle formed between the axis 316a that the feature 214a extends along and a direction102 of the article thickness 109 (see FIGS. 1-2) (e.g., a direction normal to the first majorsurface 105 and the second major surface 107 when the major surfaces are parallel toanother). In aspects, as shown in FIG. 3, the tilt angle 321 of axes 301, 316a, and / or 316bof the features 214a and / or 214b of the plurality of features 211 and / or the correspondingline 213a can be about 0° or more, about 5° or more, about 10° or more, about 15° or more,about 20° or more, about 25° or more, about 30° or more, about 35° or more, about 40° or more, about 45° or more about 50° or more, about 55° or more, about 60° or less, about 55° or less, about 50° or less, about 45° or less, about 40° or less, about 35° or less, about 30° or less, about 25° or less, about 20° or less, about 15° or less, or about 10° or less. InATTORNEYDOCKETNO. SP23-332aspects, the tilt angle 321 of axes of the features of the plurality of features and / orcorresponding line can be in a range from about 0° to about 60°, from about 5° to about 55°, from about 10° to about 50°, from about 15° to about 45°, from about 20° to about 40°, from about 25° to about 35°, from about 25° to about 30°, or any range or subrangetherebetween. In aspects, the tilt angle 321 of axes of the features of the plurality of featuresand / or corresponding line can be about 30° or more, for example in a range from about 30° to about 60°, from about 35° to about 55°, from about 40° to about 50°, from about 40° toabout 45°, or any range or subrange therebetween. In aspects, the tilt angle 321 of axes ofthe features of the plurality of features and / or corresponding line can be about 30° or less, for example in a range from about 0° to about 30°, from about 5° to about 25°, from about 10° to about 20°, from about 15° to about 20°, or any range or subrange therebetween. It is to understand that the ranges discussed in this paragraph for the tilt angle can apply to any and / or all feature(s) of the plurality of features, lines of features, and / or axes of features of the plurality of features. In aspects, as shown in FIGS. 1-2, substantially all and / or all of the features of the plurality of features can comprise substantially the same (e.g., same) tilt angle. Alternatively, although not shown, one or more features of the plurality of features can have a different tilt angle than a tilt angle of another feature of the plurality of features.

[0084] Generally, referring to the cross-section taken along the line 4-4 in FIG. 3shown in FIG. 4, a shape of the cross-section of the feature 214e (i.e., the shape of a cross-section perpendicular to the axis) can be curved (e.g., circular, ellipsoidal shape),polygonal, curvilinear, or combinations thereof. In aspects, as shown in FIG. 4, the shapeof the feature is ellipsoidal. In further aspects, although not shown, the shape of a set of features and / or all of the features of the plurality of features can comprise substantially the same and / or the same shape perpendicular to the corresponding axis. Alternatively, one or more features of the plurality of features can comprise a different shape perpendicular to the corresponding axis than a corresponding shape of another feature.

[0085] Throughout the disclosure, a width of a feature is defined as a maximumcomponent of a distance between points on the periphery of the feature in a plane perpendicular to the axis that the feature extends along, where a path connecting the points is entirely within the feature (other than any incidental portion at the endpoints). Forexample, with reference to FIG. 4, the width 309 of the feature 214e is the maximumATTORNEYDOCKETNO. SP23-332component of a distance between points 407 and 409 on the periphery of the feature 214e,wherein the points 407 and 409 lie in a plane perpendicular to the axis 316e that the featureextends along, a path connecting the points 407 and 409 is entirely within the feature (otherthan any incidental part at the endpoints), and the points 407 and 409 maximum thecomponent corresponding to the width. In aspects, the width 309 of a feature 214e can beabout 500 nanometers (nm) or more, about 1 µm or more, about 2 µm or more, about 5 µm or more, about 10 µm or more, about 20 µm or more, about 30 µm or more, about 50 µm or more, about 80 µm or more, about 100 µm or more, about 200 µm or less, about 150 µm or less, about 120 µm or less, about 100 µm or less, about 80 µm or less, about 50 µm or less, about 30 µm or less, about 20 µm or less, about 10 µm or less, or about 5 µm or less.In aspects, the width 309 of a feature 214e can be in a range from about 500 nm to about200 µm, from about 1 µm to about 150 µm, from about 2 µm to about 120 µm, from about 5 µm to about 100 µm, from about 10 µm to about 80 µm, from about 20 µm to about 50 µm, from about 30 µm to about 50 µm, or any range or subrange therebetween. In aspects,the width 309 of a feature 214e can be about 50 µm or less, for example in a range fromabout 500 nm to about 50 µm, from about 5 µm to about 50 µm, from about 10 µm to about 50 µm, from about 20 µm to about 30 µm, or any range or subrange therebetween. Inaspects, as shown in FIGS. 1-2, a set of features and / or all of the features of the pluralityof features can have substantially the same and / or the same width. Alternatively, in aspects, although not shown, a width of one or more features of the plurality of features can be different than a width of another feature of the plurality of features.

[0086] Throughout the disclosure, a depth of the feature is the dimensionperpendicular to the width in the plane perpendicular to the feature axis. For example, withreference to FIG. 4, the depth 411 of the feature 214e is the maximum component of adistance between two points 403 and 405 on the periphery of the feature 214e that is in theplane perpendicular to the axis 316d, the component is perpendicular to a direction (e.g.,direction 104) of the width 309, a path between the points 403 and 405 is entirely withinthe feature 214e (other than any incidental part at the endpoints), and the points 403 and405 maximize the component. In aspects, although not shown, the depth can besubstantially equal to the width. Alternatively, as shown, the depth 411 can be less than theATTORNEYDOCKETNO. SP23-332width 309. In aspects, the depth 411 can be within one or more of the ranges discussedabove for the width 309.

[0087] Throughout the disclosure, a “lateral spacing” refers to a minimum distancebetween adjacent features (that are not aligned along a common axis) measured in a cross- section (e.g., plane) perpendicular to the thickness direction as a distance between points on the corresponding periphery of the features of the adjacent features. For example, withreference to FIG.3, the lateral spacing 305 between adjacent features 214a and 214d (thatare not aligned along a common axis, e.g., 301 or 303, with one another) is measured in across-section perpendicular to the direction 102 of the article thickness 109 (e.g., planeextending along dashed line 215 and / or direction 104) between point 311a (on feature214a) and point 315d (on feature 214d) on the periphery of the corresponding (adjacent)features 214a and 214d that are as close together as possible in the cross-section, wherelateral spacing is the smallest distance of all cross-sections (perpendicular to the thickness direction). Consequently, it is to be noted that the lateral spacing is less than a distance between axes that the adjacent features extend along (e.g., an on-center distance) since the lateral spacing is measured between points on the periphery of the adjacent features. Inaspects, the lateral spacing 305 between an adjacent pair of features can be about 30 µm ormore, about 50 µm or more, about 70 µm or more, about 100 µm or more, about 120 µm or more, about 150 µm or more, about 170 µm or more, about 200 µm or more, about 300 µm or less, about 270 µm or less, about 250 µm or less, about 220 µm or less, about 200 µm or less, about 170 µm or less, about 150 µm or less, about 120 µm or less, about 100µm or less, or about 70 µm or less. In aspects, the lateral spacing 305 between an adjacentpair of features can be in a range from about 30 µm to about 300 µm, from about 30 µm to about 270 µm, from about 50 µm to about 250 µm, from about 50 µm to about 220 µm, from about 70 µm to about 200 µm, from about 70 µm to about 170 µm, from about 100 µm to about 150 µm, from about 120 µm to about 150 µm, or any range or subrange therebetween. In further aspects, the lateral spacing of substantially all or all adjacent pairs of features can be within one or more of the ranges discussed above in this paragraph. In further aspects, the lateral spacing of substantially all and / or all of the adjacent pairs of features can be substantially the same and / or the same.ATTORNEYDOCKETNO. SP23-332

[0088] Throughout the disclosure, an in-line spacing of an adjacent pair of featuresarranged in a common line and / or along a common axis is measured as a minimum distance in a direction of the substrate thickness between points on the corresponding periphery ofthe features of the adjacent features. For example, with reference to FIG. 3, the in-linespacing 307 between an adjacent pair of features 214 and 214b that are in a common linebetween the first major surface and the second major surface and / or are aligned along acommon axis 301 (i.e., colinear with axes 316a and 316b) is measured as a minimumdistance in the direction 102 of the article thickness 109 (see FIGS. 1-2) between point313a or 317a on the periphery of feature 214a and point 311b or 315b of feature 214b. Inaspects, the in-line spacing 307 between an adjacent pair of features 214a and 214b canbe about 5 µm or more, about 10 µm or more, about 20 µm or more, about 50 µm or more, about 70 µm or more, about 100 µm or more, about 120 µm or more, about 150 µm or more, about 300 µm or less, about 250 µm or less, about 200 µm or less, about 150 µm orless, about 100 µm or less, or about 70 µm or less. In aspects, the in-line spacing 307between an adjacent pair of features 214a and 214b can be in a range from about 5 µm toabout 300 µm, from about 10 µm to about 250 µm, from about 20 µm to about 200 µm, from about 50 µm to about 150 µm, from about 70 µm to about 100 µm, or any range or subrange therebetween.

[0089] As utilized herein, the fracture toughness KIC is measured by the doublecantilever beam (DCB) method schematically illustrated in FIG. 7. The KIC values weremeasured on glass-ceramic substrates before any chemical strengthening treatment. TheDCB specimen geometry 701 is shown in FIG. 7 with important parameters being thecrack length a, applied load P, cross-sectional dimensions w (not shown – correspondingwidth of the sample other than a location with the crack-guiding groove) and 2h, and thethickness of the crack-guiding groove b (not shown). The samples were cut into rectanglesof width 2h = 1.25 cm and a thickness ranging from w = 0.3 mm to 1 mm with the overalllength of the sample (which is not a critical dimension) varying from 5 cm to 10 cm. Holes 703a and 703b were drilled on both ends with a diamond drill to provide a means ofattaching the sample to a sample holder and to the load (for applying applied load P). Acrack “guiding groove” (crack-guiding groove) was cut down the length of the sample on both flat faces using a wafer dicing saw with a diamond blade, leaving a “web” of material,ATTORNEYDOCKETNO. SP23-332approximately half the total plate thickness (dimension b perpendicular to the view shownin FIG. 7 and corresponding to the thickness present between edges 705a and 705b of thecrack-guiding groove), with a height of 180 μm corresponding to the blade thickness(corresponding to a distance between edges 705a and 705b of the crack-guiding groove).The high precision dimensional tolerances of the dicing saw allow for minimal sample-to- sample variation. The samples were mounted in a metal sample holder with a steel wire in the bottom hole of the sample. The samples were also supported on the opposite end to keep the samples level under low loading conditions. A spring in series with a load cell(FUTEK, LSB200) was hooked to the upper hole 703a which was then extended, togradually apply load p, using rope and a high precision slide. The crack was monitoredusing a microscope having a 5 µm resolution attached to a digital camera and a computer. The applied stress intensity, KP, was calculated using the following equation (III): +2.32ℎ^൨For each sample, a crack was first initiated at the tip of the web, and then the starter crackwas carefully sub-critically grown until the ratio of dimensions a / h was greater than 1.5,which is required for the above equation to accurately calculate stress intensity. At thispoint the crack length a was measured and recorded using a traveling microscope with5 μm resolution. A drop of toluene was then placed into the crack groove and wicked along the entire length of groove by capillary forces, pinning the crack from moving until thefracture toughness is reached. The load p was then increased until sample fracture occurred,and the critical stress intensity KIC calculated from the failure load and sample dimensions,with KP being equivalent to KIC due to the measurement method. As shown in FIG. 7,samples of the glass-ceramic article comprise a plurality of features 711 extending throughthe crack-guiding groove (with only 4 feature lines and / or features shown in FIG. 7,although it is to be understood that more features can be present in other aspects, for example spanning an entire dimension of the sample).

[0090] In aspects, the fracture toughness KIC of the glass-ceramic article can beabout 1.9 MPa√m or more (e.g., about 1.90 MPa√m or more), about 1.93 MPa√m or more, about 1.95 MPa√m or more, about 1.97 MPa√m or more, about 2.00 MPa√m or more (e.g., about 2.0 MPa√m or more), about 2.03 MPa√m or more, about 2.05 MPa√m or more, aboutATTORNEYDOCKETNO. SP23-332 2.07 MPa√m or more, about 2.10 MPa√m or more (e.g., about 2.1 MPa√m or more), about 2.20 MPa√m or less (e.g., about 2.2 MPa√m or less), about 2.17 MPa√m or less, about 2.15 MPa√m or less, about 2.12 MPa√m or less, about 2.10 MPa√m or less (e.g., about 2.1 MPa√m or less), about 2.07 MPa√m or less, about 2.05 MPa√m or less, about 2.03 MPa√m or less, or about 2.00 MPa√m or less (e.g., about 2.0 MPa√m or less). In aspects, the fracture toughness KICof the glass-ceramic article can be in a range rom about 1.9 MPa√m to about 2.2 MPa√m (e.g., from about 1.90 MPa√m to about 2.20 MPa√m), from about 1.93 MPa√m to about 2.17 MPa√m, from about 1.95 MPa√m to about 2.15 MPa√m, from about 1.97 MPa√m to about 2.12 MPa√m, from about 2.00 MPa√m to about 2.10 MPa√m (e.g., from about 2.0 MPa√m to about 2.1 MPa√m), from about 2.03 MPa√m to about 2.07 MPa√m, from about 2.05 MPa√m to about 2.07 MPa√m, or any range or subrange therebetween. In exemplary aspects, the fracture toughness KICof the glass-ceramic article can be about 1.9 MPa√m or more, from about 1.95 MPa√m to about 2.15 MPa√m, or from about 2.00 MPa√m to about 2.1 MPa√m. As discussed herein, the plurality of features interior to the glass-ceramic article increase a fracture toughness KIC of the glass-ceramic article by deflecting cracks and / or interrupting crack propagation within the glass-ceramic article.

[0091] In aspects, a fracture toughness KIC of the glass-ceramic article (inaccordance with aspects of the present disclosure) can be greater than a corresponding fracture toughness KICof another glass-ceramic article identical to the glass-ceramic article but without the plurality of features. In further aspects, the fracture toughness KIC of the glass-ceramic article (in accordance with aspects of the present disclosure) can be greater than a corresponding fracture toughness KIC of another glass-ceramic article identical to the glass-ceramic article but without the plurality of features (as a percentage of the fracture toughness KICof the another glass-ceramic article) can be about 5% or more, about 7% or more, about 10% or more, about 12% or more, about 15% or more, about 17% or more, about 25% or less, about 22% or less, about 20% or less, about 17% or less, about 15% or less, or about 12% or less. In further aspects, the fracture toughness KIC of the glass-ceramic article (in accordance with aspects of the present disclosure) can be greater than a corresponding fracture toughness KIC of another glass-ceramic article identical to the glass- ceramic article but without the plurality of features (as a percentage of the fractureATTORNEYDOCKETNO. SP23-332 toughness KIC of the another glass-ceramic article) can be in a range from about 5% to about 25%, from about 7% to about 22%, from about 10% to about 20%, from about 12% to about 20%, from about 15% to about 17%, or any range or subrange therebetween. In exemplary aspects, the increase in fracture toughness KICcan be about 5% or more, from about 10% to about 20%, or from about 12% to about 17%.

[0092] Methods of making a glass-ceramic article comprising a plurality of featureswill now be discussed with reference to the optical apparatus shown in FIGS. 5-6. Inaspects, methods can use an optical apparatus 501 in a method of making a glass-ceramicarticle comprising a plurality of features. Referring now to FIG. 5, an optical apparatus501 for producing the laser beam 509 that is phase modified such that it forms a line focus601 (see FIG.6) within the substrate (e.g., glass-ceramic) a and has a quasi-non-diffractingcharacter in the substrate using the phase-altering optical element 511 is schematicallydepicted. The optical apparatus 501 can include the laser 507 that outputs the laser beam509, the phase-altering optical element 511, and, in some aspects, a lens assembly 515. Thelaser 507 may be configured to output laser beams 509, for example, pulsed laser beams orcontinuous wave laser beams. In aspects, the laser 507 may output a laser beam 509comprising an optical wavelength of about 200 nm or more, about 300 nm or more, about 500 nm or more, about 700 nm or more, about 900 nm or more, about 1100 nm or more, about 1500 nm or less, about 1300 nm or less, about 1200 nm or less, about 1100 nm or less, about 1000 nm or less, about 900 nm or less, about 800 nm or less, about 700 nm orless, 500 nm or less, or about 400 nm or less. In aspects, the laser 507 may output a laserbeam 509 comprising an optical wavelength in a range from about 200 nm to about 1500nm, from about 300 nm to about 1500 nm, from about 500 nm to about 1300 nm, from about 500 nm to about 1200 nm, from about 700 nm to about 1100 nm, from about 700 nm to about 1000 nm, from about 700 nm to about 900 nm, or any range or subrange therebetween. For example, optical wavelengths of a laser beam emitted by the laser can be 1064 nanometers (nm), 1030 nm, 532 nm, 530 nm, 355 nm, 343 nm, or 266 nm, or 215nm. In aspects, the laser 507 may output a laser beam 509 comprising an optical wavelengthof about 700 nm or more, for example, in a range from about 700 nm to about 1500 nm, from about 700 nm to about 1300 nm, from about 700 nm to about 1200 nm, from about 900 nm to about 1100 nm, from about 900 nm to about 1000 nm, or any range or subrangeATTORNEYDOCKETNO. SP23-332therebetween. In exemplary aspects, the laser 507 may output a laser beam 509 comprisingan optical wavelength in a range from about 300 nm to about 1500 nm or from about 700 nm to about 1200 nm.

[0093] The laser beam 509 used to form features in the substrate may be well suitedfor materials that are transparent to the selected laser wavelength and the substrate may bepositioned such that the laser beam 509 output by the laser 507 irradiates the substrate, forexample, after impinging on the phase-altering optical element 511 and thereafter, the lensassembly 515. Further, the beam path 513 may extend from the laser 507 to the substratesuch that when the laser 507 outputs the laser beam 509, laser beam 509 traverses (orpropagates along) the beam path 513. In further aspects, the laser 507 can comprise a gaslaser, an excimer laser, a dye laser, or a solid-state laser. Example aspects of gas lasers include helium, neon, argon, krypton, xenon, helium-neon (HeNe), xenon-neon (XeNe), carbon dioxide (CO2), carbon monoxide (CO), coper (Cu) vapor, gold (Au) vapor, cadmium (Cd) vapor, ammonia, hydrogen fluoride (HF), and deuterium fluoride (DF). Example aspects of excimer lasers include chlorine, fluorine, iodine, or dinitrogen oxide (N2O) in an inert environment comprising argon (Ar), krypton (Kr), xenon (Xe), or a combination thereof. Example aspects of dye lasers include those using organic dyes, for example, rhodamine, fluorescein, coumarin, stilbene, umbelliferone, tetracene, or malachite green dissolved in a liquid solvent. Example aspects of solid-state lasers include crystal lasers, fiber lasers, and laser diodes. Crystal-based lasers comprise a host crystal doped with a lanthanide, or a transition metal. Example aspects of host crystals include yttrium aluminum garnet (YAG), yttrium lithium fluoride (YLF), yttrium othoaluminate (YAL), yttrium scandium gallium garnet (YSSG), lithium aluminum hexafluoride (LiSAF), lithium calcium aluminum hexafluoride (LiCAF), zinc selenium (ZnSe), zinc sulfide (ZnS), ruby, forsterite, and sapphire. Example aspects of dopants include neodymium (Nd), titanium (Ti), chromium (Cr), cobalt (Co), iron (Fe), erbium (Er), holmium (Ho), thulium (Tm), ytterbium (Yb), dysprosium (Dy), cerium (Ce), gadolinium (Gd), samarium (Sm), and terbium (Tb). Example aspects of solid crystals include ruby, alexandrite, chromium fluoride, forsterite, lithium fluoride (LiF), sodium chloride (NaCl), potassium chloride (KCl), and rubidium chloride (RbCl). Laser diodes can comprise heterojunction or PIN diodes with three or more materials for the respective p-type,ATTORNEYDOCKETNO. SP23-332 intrinsic, and n-type semiconductor layers. Example aspects of laser diodes include AlGaInP, AlGaAs, InGaN, InGaAs, InGaAsP, InGaAsN, InGaAsNSb, GaInP, GaAlAs, GaInAsSb, and lead (Pb) salts. Some laser diodes represent exemplary aspects because of their size, tunable output power, and ability to operate at room temperature (i.e., about 20°C to about 25°C).

[0094] In aspects, as depicted in FIG. 5, the lens assembly 515 can comprise twosets of lenses, each set comprising the first lens 519 positioned upstream of the second lens521. The first lens 519 may collimate the laser beam 509 within a collimation space 517between the first lens 519 and the second lens 521 and the second lens 521 may focus thelaser beam 509. Further, the most downstream positioned second lens 521 of the lensassembly 515 may focus the laser beam 509 into the substrate, which may be positioned atan imaging plane of this second lens 521. In aspects, the first lens 519 and the second lens521 may each comprise plano-convex lenses. When the first lens 519 and the second lens521 each comprise plano-convex lenses, the curvature of the first lens 519 and the secondlens 521 may each be oriented toward the collimation space 517. In other aspects, the firstlens 519 may comprise other collimating lenses and the second lens 521 may comprise ameniscus lens, an aspherical lens, or another higher-order corrected focusing lens. Inoperation, the lens assembly 515 may control the position of the line focus 601 along thebeam path 513. Further, the lens assembly 515 may comprise an 8F lens assembly, asdepicted in FIG. 5, a 4F lens assembly comprising a single set of first and second lenses519, 521, or any other known or yet to be developed lens assembly 515 for focusing thelaser beam 509 into the line focus 601 and / or along the beam path 513. Moreover, it shouldbe understood that some aspects may not include the lens assembly 515 and instead, thephase-altering optical element 511 may focus the laser beam 509 into the line focus 601.

[0095] Referring still to FIG. 5, the phase-altering optical element 511 can bepositioned within the beam path 513 between the laser 507 and the substrate 103, inparticular, between the laser 507 and the lens assembly 515 such that the laser beam 509impinges on the phase-altering optical element 511 before the laser beam 509 is focusedinto the line focus 601 and directed into the substrate. In aspects, as shown in FIG. 5, theoptical apparatus 501 can be configured such that the laser 507 is positioned such that thebeam path 513 is redirected by the phase-altering optical element 511 and the laser beamATTORNEYDOCKETNO. SP23-332509 reflects off the phase-altering optical element 511 when the laser beam 509 impingeson the phase-altering optical element 511. In further aspects, the phase-altering opticalelement 511 may comprise an adaptive phase-altering optical element 527, for example, aspatial light modulator (SLM), a deformable mirror, an adaptive phase plate (ADP), or any other optical element configured to be actively altered to control a change in phase appliedby the optical element to the laser beam 509. In even further aspects, the SLM can beoptically controlled and / or digitally controlled. For example, although not shown, the laser can be positioned such that the beam path extends through the phase-altering optical element (e.g., an aspheric optical element, a static phase plate, and / or an axicon – elliptical axicon or oblong axicon) and the laser beam traverses the phase-altering optical element when the laser beam impinges on the phase-altering optical element. An exemplary aspect of a static phase plate is a beam block, which can comprise portions that block (e.g., reflect)a portion of the laser beam 509 while comprising portions that focus and / or alter the phaseof the laser beam 509. Thus, in aspects, the phase-altering optical element 511 can be arefractive optical element and in other aspects, the phase-altering optical element 511 canbe a reflective optical element. In operation, impinging on the laser beam 509 on the phase-altering optical element 511 alters the phase of the laser beam 509 and when directed intothe substrate, a portion of the laser beam 509 comprising the line focus 601 within thesubstrate can comprise a different angle within the substrate 103 than the angle of the beampath 513 through the lens assembly due to differences in the index of refraction betweenthe material of the substrate and the medium that the beam path 513 travels through. Forsimplicity, the angle of the line focus 601 and the beam path 513 are shown as the samewith the understanding that the angles may be different in practice.

[0096] Without wishing to be bound by theory, after the laser beam 509 has beenphase modified by the phase-altering optical element 511, the laser beam 509 can beaberrated when the laser beam is upstream from the substrate, for example, when the laserbeam 509 is in free space, and the laser beam 509 is aberrated when the laser beam 509 isincident on the first major surface of the substrate. Once refracted at the first major surfaceof the substrate, the laser beam 509 can exhibit a quasi-non-diffracting character and thushas minimal to no aberrations within the substrate. Without wishing to be bound by theory, the conversion from an aberrated beam to a non-aberrated beam at the first major surfaceATTORNEYDOCKETNO. SP23-332 of the substrate can be accompanied by an increase in Rayleigh range, which may increase with increasing deviation of the angle of incidence. Without wishing to be bound by theory,the laser beam 509 may comprise a higher Rayleigh range within the substrate than in freespace or in positions upstream or incident to the first major surface. For example, theRayleigh range of the laser beam 509 within the substrate may be 10 to 1000 times greaterthan the Rayleigh range outside (e.g. upstream) the substrate. For example, after phasemodification, the laser beam 509 outside (e.g. upstream) the substrate may comprise aRayleigh range of 30 µm and the Rayleigh range of the laser beam 509 within the substratemay be 1 mm. Indeed, in aspects, the laser beam 509 can be refracted at the first majorsurface of the substrate. The refracting can increase the dimensionless divergence factorFD of a Rayleigh range ZR of the laser beam 509 by a factor of at least 10, for example,from 10 to 1000, from 10 to 500 from 10 to 100, or the like.

[0097] Referring again to FIG. 5, in aspects, the phase-altering optical element 511may comprise an adaptive phase-altering optical element 527, which can apply a phasealteration to the laser beam 509 using a phase mask. The adaptive phase-altering opticalelement 527 may be communicatively coupled to a controller 503, for example, using oneor more communications pathways 505, which may comprise any pathway for providingpower signals, control signals, or the like, for example, optical fiber, electrical wire, wireless protocols, or the like. In operation, the controller 503 may provide control signalsto the adaptive phase-altering optical element 527 to control the specific phase alteration(e.g., modulation, phase mask, or the like) applied by the adaptive phase-altering opticalelement 527 such that the adaptive phase-altering optical element 527 applies a specificphase alteration to the laser beam 509, for example, based on a phase function. In aspects,the adaptive phase-altering optical element 527 can comprise a spatial light modulator(SLM), which is a transmissive or reflective device that may spatially modulate theamplitude and / or the phase of a laser beam 509 in at least one dimension. In operation, thespatial light modulator (SLM) may apply a selective, configurable phase alteration to thelaser beam 509 based on control signals from the controller 503. In aspects, the adaptivephase-altering optical element 527 can comprise a deformable mirror, which is a mirrorwhose surface can be deformed in response to control signals, for example, control signalsfrom the controller 503, to alter the wavefront of the laser beam 509, which may alter theATTORNEYDOCKETNO. SP23-332phase of the laser beam 509. For example, a deformable mirror may be configured to applya phase mask. Further, in aspects, the adaptive phase-altering optical element 527 cancomprise an adaptive phase plate, which is a phase plate (or phase plate assembly) that canapply selective and controllable phase alteration to the laser beam 509 in response tocontrol signals, for example, control signals from the controller 503. For example, theadaptive phase plate may be two or more phase plates moveable relative to one another(e.g., based on control signals from the controller 503) to alter the phase change they applyto the laser beam 509 based on their relative positioning.

[0098] In aspects, methods of forming the plurality of features in a glass-ceramicarticle comprise providing a glass-ceramic article. Glass-ceramic articles can be provided by purchase or formed by ceramming (e.g., heating to crystallize and / or grow crystals in) a glass-based substrate formed from a variety of ribbon forming techniques, for example, slot draw, down-draw, fusion down-draw, up-draw, press roll, redraw, or float. In aspects,methods can comprise adjusting a lens (e.g., a lens of the lens assembly 515, first lens 519,second lens 521, and / or adaptive phase-altering optical element 527) to create a line focus(e.g., line focus 601) within the glass-ceramic article (e.g., substrate 103) as shown inFIGS. 5-6. In aspects, the glass-ceramic article (e.g., substrate 103) can be positioned on acontact surface 525 of a stage 523 (e.g., with the second major surface 107 contacting thecontact surface 525). The stage 523 can be positioned (e.g., rotated) to achieve apredetermined angle for the features (e.g., with the beam path 513 within the substrate 103corresponding to the resulting axis 301 of one or more features of the plurality of features),for example, the stage can be positioned and / or adjusted by a signal sent from the controller503 along communication pathway 529.

[0099] In aspects, methods can comprise emitting a burst of pulses from the laser507, for example, traveling along the beam bath 513. In further aspects, an opticalwavelength that the laser 507 is configured to emit and / or an optical wavelength of theburst of pulses can be within one or more of the corresponding ranges discussed above (e.g., from about 300 nm to about 1500 nm or from about 700 nm to about 1200 nm). In further aspects, a pulse width of one or more pulses (e.g., in the burst of pulses) can be about 500 femtoseconds (fs) or more, about 1 picosecond or more (ps), about 5 ps or more, about 50 ps or more, about 500 ps or more, about 1 nanosecond (ns) or more, about 2 ns orATTORNEYDOCKETNO. SP23-332 more, about 5 ns or more, about 10 ns or less, about 50 ns or less, about 20 ns or less, about 5 ns or less, about 2 ns or less, about 1 ns or less, about 500 ps or less, about 200 ps or less, about 100 ps or less, about 50 ps or less, about 20 ps or less, about 10 ps or less, or about 5 ps or less. In further aspects, a pulse width of one or more pulses (e.g., in the burst of pulses) can be in a range from about 500 fs to about 50 ns, from about 1 ps to about 20 ns, from about 5 ps to about 5 ns, from about 50 ps to about 2 ns or less, from about 500 ps to about 1 ns, or any range or subrange therebetween. In further aspects, a pulse length of a pulse of the burst of pulses can be in the picosecond range, for example, from about 1 ps to about 500 ps, from about 1 ps to about 100 ps, from about 1 ps to about 50 ps, from about 1 ps to about 20 ps, from about 1 ps to about 10 ps, from about 5 ps to about 10 ps, or any range or subrange therebetween. In further aspects, an energy of a pulse of the burst of pulses can be about 1 microJoule (µJ) or more, about 5 µJ or more, about 10 µJ or more, about 20 µJ or more, about 50 µJ or less, about 40 µJ or less, about 30 µJ or less, about 20 µJ or less, or about 10 µJ or less. In further aspects, an energy of a pulse of the burst of pulses can be in a range from about 1 µJ to about 50 µJ, from about 5 µJ to about 40 µJ, from about 10 µJ to about 30 µJ, from about 10 µJ to about 20 µJ, or any range or subrange therebetween. In further aspects, a shape of a pulse of the burst of pulses can be Gaussian, Bessel, or Airy. In further aspects, pulses of the burst of pulse can be generated at a repetition rate of about 50 kiloHertz (kHz) or more, about 100 kHz or more, about 200 kHz or more, about 500 kHz or more, about 1 MegaHertz (MHz) or less, about 500 kHz or less, about 300 kHz or less, or about 100 kHz or less. In further aspects, pulses of the burst of pulse can be generated at a repetition rate in a range from about 50 kHz to about 1 MHz, from about 100 kHz to about 500 kHz, from about 200 kHz to about 300 kHz, or any range or subrange therebetween. In further aspects, number pulses in the burst of pulses can be in a range from about 100 to about 1,500, from about 100 to about 1,000, from about 100 to about 800, from about 300 to about 1,500, from about 300 to about 1,000, from about 300 to about 800, from about 600 to about 1,500, from about 600 to about 1,000, from about 600 to about 800, or any range or subrange therebetween.

[00100] In further aspects, as shown in FIG. 5, a burst of pulses travelling alongthe beam bath 513 can be transmitted through the lens (e.g., a lens of the lens assembly515, first lens 519, second lens 521, and / or adaptive phase-altering optical element 527).ATTORNEYDOCKETNO. SP23-332 In even further aspects, the burst of pulses can impinge a spatial light modulator (SLM) to form a plurality of spatially distinct beam spots for each pulse of the burst of pulses that can form a set of features that are spatially distinct, although a SLM may not be present inother aspects. In further aspects, as shown in FIGS.5-6, the burst of pulses can travel alongthe beam path 513 in a direction 502 towards the substrate 103 and impinge the glass-ceramic article (e.g., substrate 103) to form the plurality of features (e.g., see plurality offeatures 111 and / or 211 in FIGS. 1-2). As discussed above, the pulse(s) of the burst ofpulses can form the feature of the plurality of features by locally melting a portion of the primary ceramic phase to form an amorphous glass region associated with the feature. In further aspects, each pulse of the burst of pulses can form a feature of the plurality of features, although multiple pulses can impinge substantially the same location to collectively form a feature of the plurality of features in further aspects. In further aspects,as shown in FIG. 6, a pulse of the burst of pulses travelling along the beam path 513 canform a line focus 601 within the glass-ceramic article (e.g., substrate 103). In even furtheraspects, a length of the line focus 601 in the substrate 103 can be about 10 µm or more,about 20 µm or more, about 50 µm or more, about 100 µm or more, about 200 µm or more, about 500 µm or more, about 1 mm or less, about 800 µm or less, about 400 µm or less, about 200 µm or less, about 100 µm or less, about 80 µm or less, or about 40 µm or less.In even further aspects, a length of the line focus 601 in the substrate 103 can be in a rangefrom about 10 µm to about 1 mm, from about 20 µm to about 800 µm, from about 50 µm to about 400 µm, from about 100 µm to about 200 µm, or any range or subrangetherebetween. Additionally or alternatively, a length of the line focus 601 can be withinone or more of the ranges discussed above for the length of a feature of the plurality of features. In further aspects, EXAMPLES

[00101] Examples 1-4 relate to methods of creating a plurality of features withina glass-ceramic article using a pulsed laser, as described above. The pulsed laser was a Pharos ultrafast laser system (available from Light Conversion) that was operated with the solid-state laser configured to produce pulse with an optical wavelength centered at 1030 nm, a 1 ps pulse width, and a 200 kHz repetition rate, corresponding to an energy of about 5 µJ per pulse. The laser beam was focused using an 40X objective lens with a numericalATTORNEYDOCKETNO. SP23-332 aperture of 0.65 (available from Olympus) to be focused within the glass-ceramic substrate. Unless otherwise indicated, the features were formed with an on-center distance of 50 µm between adjacent features (not in a line – which corresponds to a smaller lateral spacing305 shown in FIG. 3).

[0102] For Examples 1-2, the beam shape was a Bessel beam configured to form6 features in a line (internal to the substrate and extending between the first major surface and the second major surface). For Examples 3-44, the beam shape was a Gaussian beam configured to form one long feature (internal to the substrate and extending between the first major surface and the second major surface. For Examples 1-3, the tilt angle (see tiltangle 321 in FIG. 3) was 0°, 30°, and 45°, respectively. For Examples 4 -5, the title anglewas 60° and 75°, respectively.

[00103] For Examples 1-4, the substrate comprised a substrate comprisingComposition 1 (61.2 mol% SiO2, 1.5 mol% Al2O3, 24.5 mol% Li2O, 2 mol% Na2O, 6.5 mol% CaO, 1.7 mol% P2O5, and 1.6 mol% F-) that was cerammed at 750°C for 5 minutes to produce a glass-ceramic with lithium disilicate and apatite crystal phases (i.e., primary ceramic phase).

[00104] As discussed above, FIG. 8 (Example 3) shows the plurality of features(e.g., features 805a, 805b, 805c, and / or 805d – corresponding to a second set of features913 in FIG.9) comprise an amorphous glass phase surrounded by a primary ceramic phase801 of the substrate (e.g., glass-ceramic article).

[00105] Also, FIG. 9 (Example 3) shows a top view of the substrate 103 (lookingdown the first major surface 105 of the substrate 103 that is perpendicular to the viewshown in FIG. 7). Originally, the outline of where the laser impinged the surface wasvisible (although the laser did not form features extending to the surface), which is madeclearer using the boxes in FIG. 9. As shown in FIG. 9, a first set of features 911 wasformed as two rows of features 903a and 903b that are staggered relative to one another.Also, a second set of features 913 was formed as four rows of features 905a, 905b, 905cand 905d in a staggered (or checkboard) pattern. Portions 915a and 915b are seen in FIG.9 that correspond to regions cut by the dicing saw in preparing the sample for the double- cantilever beam method.ATTORNEYDOCKETNO. SP23-332

[00106] FIG. 10 (Example 3) shows a side view of the substrate (correspondingto the view shown in FIG. 7) in the configuration for the double cantilever beamconfiguration used to determine fracture toughness (discussed above) but the method isstopped before fracture for this view. Consequently, edges 1005a and 1005b (in FIGS. 10-13) correspond to edges 705a and 705b demarcating the edges of the crack-guidinggroove. As shown in FIG. 10, a plurality of features 1011 corresponding to three sets offeatures are shown as straight lines (black) for clarity. As indicated, going from left to right,the first set of features corresponds to two lines of features (see first set of features 911 inFIG. 9), the second set of features corresponds to four lines of features (see second set offeatures 913 in FIG. 9), and the third set of features corresponds to eight lines of features.

[0107] FIG. 11 (Example 3) shows a side view of the substrate (correspondingto the view shown in FIG. 7) with crack deflection from the double-cantilever beamconfiguration (stopped before fracture but the same configuration that was used todetermine fracture toughness). FIG. 11 shows crack 1101 that was deflected (upwards) bythe plurality features 1111 (corresponding to the second set of features 913 in FIGS. 9-10).

[0108] FIG. 12 (Example 2) and FIG. 13 (Example 1) also show side views ofthe substrate (corresponding to the view shown in FIG. 7) with crack deflection in thedouble-cantilever beam configuration (stopped before fracture but the same configurationthat was used to determine fracture toughness). As shown in FIG. 12, the plurality offeatures 1211 with a tilt angle of 30° deflects the crack 1201 (upwards). As shown in FIG.13, the plurality of features 1311 with a tilt angle of 0° also deflects the crack 1301(downwards).

[00109] Table 1 presents the fracture toughness measured for Examples 1-4 andComparative Example AA. Comparative Example AA is the same substrate (i.e., glass- ceramic article) that was used for Examples 1-4, but Comparative Example AA does not have any features. As shown in Table 1, Comparative Example had a fracture toughness KICof 1.76 MPa√m while Examples 1-4 had fracture toughness KICvalues of 1.95 MPa√m or more (from 1.95 MPa√m to about 2.35 MPa√m). Also, as shown, Examples 1-5 increase the fracture toughness KIC relative to Comparative Example AA by 10% or more (e.g., from 11% to about 35%).ATTORNEYDOCKETNO. SP23-332 Table 1: Fracture Toughness for Examples 1-4 and Comparative Example AA

[00110] FIG. 14 illustrates a magnified top cross-sectional view (see FIG. 9) ofExample 4 after the fracture toughness was determined in the double-cantilever beamconfiguration. In FIG. 14, the features (e.g., features 1401, 1411, 1421, and 1431) werevisible by the solid-black lines (forming an L-shape) with the dashed lines completing theoutline of the feature. The features (e.g., features 1401, 1411, 1421, and 1431) correspondto height variation of the surface, where the crack propagation has left discernable deformations (also outlined in black) on the surface from crack deflection through thesample during testing to fracture. For example, the height associated with triangles 1403and 1433 appear to concentrate at the corners of the features, which promotes crackdeflection. Also, there are lines 1405 and additional shapes 1413 and 1423 that appear tocorrespond to be channeled to an adjacent set of rows (offset), which can deflect a propagating crack. Without wishing to be bound by theory, it is believed that the crackdeflection seen in FIG. 14 may be the result of one or more of (1) a lower strain energy inthe features, (2) a weak interface between the features and the primary ceramic phase, and / or (3) a mismatch in the coefficient of thermal expansion (CTE) between the features and the primary ceramic phase.

[00111] FIG. 15 illustrates a cross-section of Example 4 (similar to FIG. 8) butfor different features and after the fracture toughness was determined in the double-cantilever beam configuration. In FIG. 15, features 1503 and 1505 are shown with theamorphous glass phase outlined in a roughly oval shape. Additionally, swooping shapes1507 and 1509 are seen intersecting the bottom of the features 1503 and 1505 andATTORNEYDOCKETNO. SP23-332 changing the bottom of the roughly oval shape, which indicates that the strain (and stress) associated with crack propagation was concentrated into the feature before and / or instead of continuing to propagate.

[00112] The embodiments of the disclosure can provide glass-ceramic articlesincluding a plurality of features internal to the glass-ceramic article. As demonstrated by the Examples herein, the plurality of features interior to the glass-ceramic article increase a fracture toughness KIC of the glass-ceramic article (e.g., relative to a glass-ceramic article without the plurality of features by 10% or more, from about 10% to about 35%, or from about 10% to about 20%). Without wishing to be bound by theory, it is believed that the plurality of features interior to the glass-ceramic article increases the fracture toughness KICby deflecting cracks and / or interrupting crack propagation within the glass-ceramic article. Also, a tilt angle of the features of the plurality of features can be controlled to further increase the fracture toughness.

[00113] Methods of the present disclosure can form the plurality of featuresinterior to the glass-ceramic article by impinging a focused (e.g., line focus) laser beam (e.g., plurality of pulses) within the glass-ceramic article. The pulsed laser can quickly form the plurality of features. The shape and / or length of the features can be controlled by adjusting the beam shape, focusing optics, and other properties of an optical apparatus including the laser.

[00114] Directional terms as used herein—for example, up, down, right, left, front,back, top, bottom—are made only with reference to the figures as drawn and are not intended to imply absolute orientation.

[00115] It will be appreciated that the various disclosed aspects may involvefeatures, elements, or steps that are described in connection with that aspect. It will also be appreciated that a feature, element, or step, although described in relation to one aspect, may be interchanged or combined with alternate aspects in various non-illustrated combinations or permutations.

[00116] It is also to be understood that, as used herein, the terms “the,” “a,” or“an,” mean “at least one,” and should not be limited to “only one” unless explicitly indicated to the contrary. For example, reference to “a component” comprises aspectsATTORNEYDOCKETNO. SP23-332 having two or more such components unless the context clearly indicates otherwise. Likewise, a “plurality” is intended to denote “more than one.”

[00117] As used herein, the term “about” means that amounts, sizes, formulations,parameters, and other quantities and characteristics are not and need not be exact, but may be approximate and / or larger or smaller, as desired, reflecting tolerances, conversion factors, rounding off, measurement error and the like, and other factors known to those of skill in the art. Ranges can be expressed herein as from “about” one particular value, and / or to “about” another particular value. When such a range is expressed, aspects include from the one particular value and / or to the other particular value. Similarly, when values are expressed as approximations, by use of the antecedent “about,” it will be understood that the particular value forms another aspect. Whether or not a numerical value or endpoint of a range in the specification recites “about,” the numerical value or endpoint of a range is intended to include two aspects: one modified by “about,” and one not modified by “about.” It will be further understood that the endpoints of each of the ranges are significant both in relation to the other endpoint and independently of the other endpoint.

[00118] The terms “substantial,” “substantially,” and variations thereof, as usedherein, are intended to note that a described feature is equal or approximately equal to a value or description. For example, a “substantially planar” surface is intended to denote a surface that is planar or approximately planar. Moreover, as defined above, “substantially similar” is intended to denote that two values are equal or approximately equal. In aspects, “substantially similar” may denote values within about 10% of each other, for example, within about 5% of each other, or within about 2% of each other.

[00119] Unless otherwise expressly stated, it is in no way intended that anymethod set forth herein be construed as requiring that its steps be performed in a specific order. Accordingly, where a method claim does not actually recite an order to be followed by its steps or it is not otherwise specifically stated in the claims or descriptions that the steps are to be limited to a specific order, it is in no way intended that any particular order be inferred.

[00120] While various features, elements, or steps of particular aspects may bedisclosed using the transitional phrase “comprising,” it is to be understood that alternative aspects, including those that may be described using the transitional phrases “consistingATTORNEYDOCKETNO. SP23-332 of” or “consisting essentially of,” are implied. Thus, for example, implied alternative aspects to an apparatus that comprises A+B+C include aspects where an apparatus consists of A+B+C and aspects where an apparatus consists essentially of A+B+C. As used herein, the terms “comprising” and “including”, and variations thereof shall be construed as synonymous and open-ended unless otherwise indicated.

[00121] The above aspects, and the features of those aspects, are exemplary andcan be provided alone or in any combination with any one or more features of other aspects provided herein without departing from the scope of the disclosure.

[00122] It will be apparent to those skilled in the art that various modifications andvariations can be made to the present disclosure without departing from the spirit and scope of the disclosure. Thus, it is intended that the present disclosure cover the modifications and variations of the aspects herein provided they come within the scope of the appended claims and their equivalents.

Claims

ATTORNEYDOCKETNO. SP23-332 What is claimed is:

1. A glass-ceramic article comprising:a first major surface, a second major surface opposite the first major surface, and an article thickness defined therebetween; a primary ceramic phase; and a plurality of features within an interior of the glass-ceramic article, the plurality of features comprising an amorphous glass phase, a height in a direction of the article thickness.

2. The glass-ceramic article of claim 1, wherein a minimum distance between a featureof the plurality of features and the first major surface is in a range from about 10 micrometers to about 100 micrometers.

3. The glass-ceramic article of any one of claims 1-2, wherein a tilt angle relative tothe direction of the article thickness of a feature of the plurality of features is in a range from about 0° to about 60°.

4. The glass-ceramic article of any one of claims 1-3, wherein a first set of features ofthe plurality of features are arranged in a line between the first major surface and the second major surface.

5. The glass-ceramic article of claim 4, wherein the height of a first feature in the firstset of features is in a range from about 5 micrometers to about 500 micrometers.

6. The glass-ceramic article of claim 4, wherein the height of a first feature in the firstset of features as a percentage of the article thickness is in a range from about 5% to about 30%.

7. The glass-ceramic article of any one of claims 1-3, wherein the height of the featureof the plurality of features as a percentage of the article thickness is in a range from about 50% to about 95%.ATTORNEYDOCKETNO. SP23-3328. The glass-ceramic article of any one of claims 1-7, wherein each feature of theplurality of features extends along a corresponding axis, and a distance between the axes of an adjacent pair of features of the plurality of features is in a range from about 30 micrometers to about 300 micrometers.

9. The glass-ceramic article of any one of claims 1-3, wherein each feature of theplurality of features extends along a corresponding axis, and a first axis of a first feature of the plurality of features is colinear with a second axis of a second feature of the plurality of features.

10. The glass-ceramic article of any one of claims 8-9, wherein a width of a feature of the plurality of features perpendicular to the axis of the feature is in a range from about 500 nanometers to about 200 micrometers.

11. The glass-ceramic article of any one of claims 1-10, wherein a fracture toughness KICof the glass-ceramic article is about 1.9 MPa√m or more.

12. The glass-ceramic article of any one of claims 1-10, wherein a fracture toughness KICof the glass-ceramic article is greater than a fracture toughness KICof another glass- ceramic article identical to the glass-ceramic article but without the plurality of features by about 5% or more.

13. The glass-ceramic article of any one of claims 1-12, wherein the primary ceramic phase comprises β-spodumene, β-quartz, nepheline, cordierite, spinel, lithium disilicate, or a combination thereof.

14. The glass-ceramic article of any one of claims 1-13, wherein a feature of the plurality of features is surrounded by the primary ceramic phase.ATTORNEYDOCKETNO. SP23-332 15. A method of forming a plurality of features in a glass-ceramic article, the glass- ceramic article comprising a primary ceramic phase, a first major surface, a second major surface opposite the first major surface, and an article thickness defined between the first major surface and the second major surface, the method comprising: adjusting a lens to create a line focus within the glass-ceramic article; emitting a burst of pulses from a laser; transmitting the burst of pulses through the lens; and impinging the burst of pulses on the glass-ceramic article to form the plurality of features, wherein the burst of pulses melts a portion of the primary ceramic phase to form a feature of the plurality of features comprising an amorphous glass phase, the plurality of features comprising a height in a direction of the article thickness, and the plurality of features are formed within an interior of the glass-ceramic article.

16. The method of claim 15, wherein a pulse of the burst of pulses comprising an energy in a range from about 1 microjoule to about 50 microjoules, and pulses of the burst of pulses are generated at a rate from about 50 kilohertz to about 1 megahertz.

17. The method of any one of claims 15-16, wherein an optical wavelength associated with the burst of pulses is in a range from about 300 nanometers to about 1500 nanometers, and a pulse width of a pulse of the burst of pulses is in a range from about 500 femtoseconds to about 50 nanoseconds.

18. The method of any one of claims 15-17, wherein a length of the line focus is in a range from about 10 micrometers to about 1 millimeter.

19. The method of any one of claims 15-18, further comprising impinging the burst of pulses on a spatial light modulator to generate a plurality of spatially distinct beam spots for each pulse of the burst of pulses, and impinging the plurality of spatially distinct beam spots on the generate a set of features of the plurality of features.ATTORNEYDOCKETNO. SP23-332 20. The method of any one of claims 15-19, wherein a minimum distance between a feature of the plurality of features and the first major surface is in a range from about 10 micrometers to about 100 micrometers.

21. The method of any one of claims 15-20, wherein a tilt angle relative to the direction of the height of a feature of the plurality of features is in a range from about 0° to about 60°.

22. The method of any one of claims 15-21, wherein a first set of features of the plurality of features are arranged in a line between the first major surface and a second major surface.

23. The method of any one of claims 15-21, wherein each feature of the plurality of features extends along a corresponding axis, and a first axis of a first feature of the plurality of features is colinear with a second axis of a second feature of the plurality of features.

24. The method of any one of claims 22-23, wherein the height of a first feature in the first set of features is in a range from about 5 micrometers to about 500 micrometers.

25. The method of any one of claims 15-21, wherein the height of the feature of the plurality of features as a percentage of the article thickness is in a range from about 50% to about 95%.

26. The method of any one of claims 22-24, wherein each feature of the plurality of features extends along a corresponding axis, and a distance between the axes of an adjacent pair of features of the plurality of features is in a range from about 30 micrometers to about 300 micrometers.

27. The method of any one of claims 15-26, wherein a fracture toughness KIC of the glass-ceramic article is about 1.9 MPa√m or more.ATTORNEYDOCKETNO. SP23-332 28. The method of any one of claims 15-26, wherein a fracture toughness KIC of the glass-ceramic article is greater than a fracture toughness KIC of another glass-ceramic article identical to the glass-ceramic article but without the plurality of features by about 5% or more.