Anorthite material and preparation method thereof

By utilizing the tailings after titanium extraction and adding silica, clay, wollastonite and other materials, the problem of shortage of bauxite resources and unutilized tailings in the production of anorthite materials has been solved, and low-cost, environmentally friendly production has been achieved. Preparation of anorthite materials, suitable for refractory materials or glass raw materials.

CN101544503AInactive Publication Date: 2009-09-30WUHAN UNIV OF SCI & TECH
1 Cites 3 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
Filing Date
2009-04-24
Publication Date
2009-09-30
Estimated Expiration
Not applicable · inactive patent

AI Technical Summary

Technical Problem

The existing production of anorthite materials relies on high-cost bauxite resources, and the tailings after titanium extraction cannot be effectively utilized, resulting in high production costs and waste of resources.

Method used

The tailings after titanium extraction are used as raw materials, and materials such as silica, clay and wollastonite are added to adjust the composition and process to prepare anorthite materials, including adding these materials to molten and cold tailings and conducting Calcined to form anorthite material.

Benefits of technology

It reduces production costs, efficiently utilizes industrial waste residue, provides an environmentally friendly solution, and simplifies the process, so that the prepared materials can be used for refractory materials or glass raw materials.

✦ Generated by Eureka AI based on patent content.
Patent Text Reader

Abstract

The invention relates to an anorthite material and a preparation method thereof. The adopted technical proposal comprises the following steps of: according to (ZL200510019664.3) patent technology, namely a method for preparing titanium and a titanium alloy by utilizing titanium-containing furnace slag, taking molten tailings which is extracted with the titanium alloy as a raw material, adding 20 to 50 weight percent of silica, 0 to 60 weight percent of clay and 0 to 40 percent aedelforsite, and cooling a melt to obtain the anorthite material after the mixture is completely molten and a bath composition is uniform; or taking cold tailings extracted with the titanium alloy as the raw material, adding 20 to 50 weight percent of the silica, 0 to 60 weight percent of the clay and 0 to 40 percent the aedelforsite, carrying out mix grinding on the raw material and the admixture until the particle size is less than 0.1 mm, performing blank compression, and calcining the mixture at a temperature of between 1,200 and 1,400 DEG C to obtain the anorthite material. The method takes the tailings extracted with the titanium as the raw material, saves precious bauxite resources, has low cost, ensures that industrial residue is utilized with high added value, is environment-friendly and has simple process.
Need to check novelty before this filing date? Find Prior Art

Citation Information

Patent Citations

  • Method of preparing titanium and titanium alloy using titanium containing furnace clinker

    CN1757772A

Cited By

  • Anorthite light-weight and heat insulation refractory material and preparation method thereof

    CN101781120B

  • Preparation method for vanadium-titanium-silicon-iron alloy

    CN103866144A

  • A kind of preparation method of vanadium titanium ferrosilicon alloy

    CN103866144B