Method for making metal copper flowerpot

Abstract

This invention discloses a metallic copper flowerpot and its manufacture technique. It utilizes the material property of copper metal and adopts the precise lost wax casting method to obtain the blank casting, including the following steps:moulding real-form wax model, making shell body for wax model, dewaxing of shell body, laking shell body, heat-insulating shell body and pouring, cooling and clearing blank casting, and it features that in the step of making shell body for wax model, multiple iron wires are wrapped round the shell body. This invention makes the flower pot diversity in mouldings, be exquisite and fine, have stereo-feeling artistic design on the surface of finished product, and thus the metallic copper flower pot becomes a high-grade delicate variety of flowerpot.

Description

technical field

[0001] The invention relates to a method for manufacturing a flowerpot. Background technique

[0002] Traditional flower pots include baked clay pots, purple sand pots, ceramic flower pots, marble flower pots, white marble flower pots, glass, plastic and other flower pots. The shape is single and repetitive, and the shape is mainly flat, and the shape is not rich in changes. The surface of the flower pot is only decorated with painted and colored glaze, which has no three-dimensional effect and is easy to break. Furthermore, the larger the size of the flower pot, the thicker the wall thickness, such as the cast copper flower pots already sold on the market. Limited by the manufacturing process, it is difficult for manufacturers to produce cast copper flowerpots that are large in size, heavy in weight, and large-scale thin-walled (wall thickness is 3-6 mm). Contents of the invention

[0003] The purpos...

Examples

Embodiment Construction

[0008] The following are preferred embodiments of the present invention:

[0009] 1. Mold the real sample wax type. Use the model to make the paraffin wax mold into a real sample of flower pot wax, after appearance modification (the tolerance of the size of the wax mold and the surface roughness determine the fineness of the surface of the casting blank), and weld the wax pouring system.

[0010] 2. Wax shell. (1) The shell of the wax sample is made by investment casting. In order to ensure the fineness of the process pattern, the first layer should be covered with quartz sand with a particle size of about 0.053-0.106, and the bonding paint for the remaining layers , is made of high-alumina bauxite containing not less than 75% aluminum oxide. When the third layer is cultivated, iron wires start to be wound. The thickness and gap size of the iron wires depend on the size of the specifications. The diameter of the iron wire is selected between 1-5mm, the iron wire is crossed a...

technical field

[0001] The invention relates to a method for manufacturing a flowerpot. Background technique

[0002] Traditional flower pots include baked clay pots, purple sand pots, ceramic flower pots, marble flower pots, white marble flower pots, glass, plastic and other flower pots. The shape is single and repetitive, and the shape is mainly flat, and the shape is not rich in changes. The surface of the flower pot is only decorated with painted and colored glaze, which has no three-dimensional effect and is easy to break. Furthermore, the larger the size of the flower pot, the thicker the wall thickness, such as the cast copper flower pots already sold on the market. Limited by the manufacturing process, it is difficult for manufacturers to produce cast copper flowerpots that are large in size, heavy in weight, and large-scale thin-walled (wall thickness is 3-6 mm). Contents of the invention

[0003] The purpos...

Examples

Embodiment Construction

[0008] The following are preferred embodiments of the present invention:

[0009] 1. Mold the real sample wax type. Use the model to make the paraffin wax mold into a real sample of flower pot wax, after appearance modification (the tolerance of the size of the wax mold and the surface roughness determine the fineness of the surface of the casting blank), and weld the wax pouring system.

[0010] 2. Wax shell. (1) The shell of the wax sample is made by investment casting. In order to ensure the fineness of the process pattern, the first layer should be covered with quartz sand with a particle size of about 0.053-0.106, and the bonding paint for the remaining layers , is made of high-alumina bauxite containing not less than 75% aluminum oxide. When the third layer is cultivated, iron wires start to be wound. The thickness and gap size of the iron wires depend on the size of the specifications. The diameter of the iron wire is selected between 1-5mm, the iron wire is crossed a...