Fine denier acetate silk elastic double-faced fabric and production process thereof

A double-sided fabric and production process technology, applied in the direction of fabrics, textiles, textiles and papermaking, can solve the problems of difficult production, low strength, easy to fluff, etc., and achieve the effect of saving production time, strong satin feeling, and fine silk surface.

CN114507927APending Publication Date: 2022-05-17佛山市格绫丝绸有限公司
7 Cites 0 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
Publication Date
2022-05-17

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention discloses a fine denier acetate silk elastic double-faced fabric and a production process thereof, and belongs to the technical field of textiles. The method comprises the following steps of fabric texture design, warp and weft processing, fabric weaving, fabric dyeing and finishing and finished product inspection. According to the fabric texture design, fine denier diacetate fiber yarn is adopted as warp yarn, double-component elastic polyester SSY high stretch yarn is adopted as weft yarn, and the texture is 4 / 4 double-face texture; the warp yarn treatment process comprises the steps of twisting, shaping, splitting and warp lifting, drafting and reed passing; the weft yarn treatment process comprises the steps of spooling, twisting, shaping and rewinding; the fabric dyeing and finishing process comprises the steps of dyeing pretreatment, dyeing and soft padding, drying and shaping. According to the production process, the fine-denier diacetate fibers are adopted as the warps, so that the prepared fabric is stronger in silk feeling, softer in hand feeling and finer and smoother in silk surface, the warp density of the fabric reaches 100 pieces / cm or above, the acetic acid proportion is 55% or above, and the fabric can better reflect the excellent performance of the diacetate fibers.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to the technical field of textiles, in particular to a fine-denier acetate silk elastic double-sided fabric and a production process thereof. Background technique

[0002] Diacetate silk products on the market, the weight is 100g / m 2 There are basically no light satin fabrics on the left and right. It is necessary to produce a thin satin that can replace silk and can reflect the excellent performance of diacetate silk: smooth as silk, elegant drape, pearl-like luster, beautiful and attractive curves, high elasticity, and Products that are environmentally friendly, comfortable, novel, and bring beauty and enjoyment to people must be realized through optimized technology in order to truly reflect the unique style characteristics of their products. Among them, the low strength is the main reason for the difficulty in the production of the above-mentioned diacetate silk products, especially for high-density warp yarns, which are ve...

Examples

Embodiment 1

[0030] A production process of fine-denier acetate silk elastic double-sided fabric, the process flow is:

[0031] Fabric design → warp and weft yarn processing → fabric weaving → fabric dyeing and finishing → finished product inspection;

[0032] Among them, the warp processing process is: twisting → shaping → warp lifting → drafting → reeding;

[0033] The weft yarn processing flow is: winding → twisting → shaping → rewinding;

[0034] Fabric dyeing and finishing process: pre-dyeing treatment → dyeing → soft padding drying and setting.

[0035] Among them: in the fabric design process, the warp yarn is made of 45D / 25F diacetate fiber fine denier yarn with a twist of 1200T / m, the weft yarn is made of 50D / 24F two-component elastic polyester SSY high elastic yarn with a twist of 1800T / m and a weave of 4 / 4 double-sided tissue (such as figure 1 shown), the warp density is 100-110 / cm.

[0036] Warp yarn processing process: twisting → shaping → warp splitting → threading → ree...

Embodiment 2

[0044] A production process of fine-denier acetate silk elastic double-sided fabric, the process flow is:

[0045] Fabric design → warp and weft yarn processing → fabric weaving → fabric dyeing and finishing → finished product inspection;

[0046] Among them, the warp processing process is: twisting → shaping → warp lifting → drafting → reeding;

[0047] The weft yarn processing flow is: winding → twisting → shaping → rewinding;

[0048] Fabric dyeing and finishing process: pre-dyeing treatment → dyeing → soft padding drying and setting.

[0049] Among them: in the fabric design process, the warp yarn is made of 45D / 25F glossy acetate yarn with a twist of 1200T / m, the weft yarn is made of 50D / 24F bi-component polyester SSY with a twist of 1800T / m, and the weave is 4 / 4 double-sided weave ( Such as figure 1 shown), the warp density is 100-110 / cm.

[0050]Warp yarn processing process: twisting → shaping → warp splitting → threading → reeding, in which the twisting process is ...

Embodiment 3

[0058] A production process of fine-denier acetate silk elastic double-sided fabric, the process flow is:

[0059] Fabric design → warp and weft yarn processing → fabric weaving → fabric dyeing and finishing → finished product inspection;

[0060] Among them, the warp processing process is: twisting → shaping → warp lifting → drafting → reeding;

[0061] The weft yarn processing flow is: winding → twisting → shaping → rewinding;

[0062] Fabric dyeing and finishing process: pre-dyeing treatment → dyeing → soft padding drying and setting.

[0063] Among them: in the fabric design process, the warp yarn is made of 45D / 25F glossy acetate yarn with a twist of 1200T / m, the weft yarn is made of 50D / 24F bi-component polyester SSY with a twist of 1800T / m, and the weave is 4 / 4 double-sided weave ( Such as figure 1 shown), the warp density is 100-110 / cm.

[0064] Warp yarn processing process: twisting → shaping → warp splitting → threading → reeding, in which the twisting process is...