Preparation process of plastic transfer wood grain wine box

Abstract

The invention provides a preparation process of a plastic transfer wood grain wine box. The preparation process based on the plastic transfer printing wood grain wine box comprises the steps that S1, a required wood grain pattern is created through computer aided design, design is conducted according to the size and design requirements of the wine box, the type and specification of a required wood grain transfer printing film are determined, and S2, the surface of the wine box is cleaned up, and dirt, grease and other impurities are removed. High-precision pattern transfer can be realized through heat transfer printing, so that a transfer pattern is clear and rich in details, and the thermal transfer printing material can be suitable for complex patterns and textures, has relatively high durability and scratch resistance, and can keep bright and stable patterns in long-term use; according to the cold transfer printing method, the transfer printing process can be completed at a low temperature, so that the heat sensitivity and deformation risk of the material are reduced, after cold transfer printing is completed, the pattern can be used immediately without waiting for the curing or drying process, and the damage to the transferred part cannot be caused.

Description

Technical Field

[0001] The invention relates to the technical field of wine box preparation, and in particular to a preparation process of a plastic transfer wood grain wine box. Background Art

[0002] There are many packaging boxes on the market now that are made of wood products. At present, wood packaging boxes are generally made by cutting wood boards into small pieces and then manually splicing (screw splicing, glue splicing) into a complete wooden box. Although this kind of packaging box looks high-end, its value mainly reflects the grade of the product, and it does not have any other practical functions. Using wood for packaging is not environmentally friendly, wastes wood resources, and the appearance shape and surface decoration are single and easy to be affected by moisture. Plastic transfer wood grain is a technology that transfers wood grain patterns to the surface of plastic to achieve the appearance of wood grain on plastic products. This technology is often used in the production of plastic products such as furniture, decorations and packaging materials. Through high-quality wood grain transfer film and advanced transfer technology, the wood grain pattern on plastic products can present realistic texture and details, which is almost indistinguishable from real wood. Wood grain transfer film provides a variety of different types of wood grain pattern options, including oak, walnut, cherry, etc. This allows a variety of wood grain effects to be achieved on plastic products to meet different styles and needs. In addition to texture, wood grain transfer film can also provide a variety of color options. Through the right color matching, you can create a rich and diverse wood grain appearance, making plastic products more vivid and attractive. Plastic transfer wood grain not only gives plastic products a beautiful appearance, but also provides additional protection. Transfer coatings can increase the surface's wear resistance, scratch resistance and water resistance, extending the product's service life. Plastic transfer wood grain technology has a certain degree of customizability, and different wood grain effects can be produced according to customer needs and design requirements, but the current transfer wood grain will have the problem of peeling during use. Summary of the invention

[0003] 1. Technical issues to be resolved

[0004] In view of the shortcomings of the prior art, the present invention provides a preparation process for a plastic transfer wood grain wine box, which solves the problem of peeling.

[0005] (II) Technical solution

[0006] To achieve the above objectives, the present invention is implemented through the following technical solutions: 1. A preparation process of a plastic transfer wood grain wine box, characterized in that it includes:

[0007] S1. Use computer-aided design to create the required wood grain pattern, design it according to the size and design requirements of the wine box, and determine the required wood grain transfer film type and specifications;

[0008] S2. Clean the surface of the wine box to remove dirt, grease and other impurities. Use a damp cloth to thoroughly clean the surface of the wine box, making sure the surface is smooth and dry, and check for any damage or uneven areas.

[0009] S3, cut the selected wood grain transfer film into appropriate size to cover the entire surface of the wine box, and ensure that the size of the cut transfer film matches the wine box;

[0010] S4. Place the wine box on the transfer device and ensure that the wine box is fixed and stable to prevent movement or shaking;

[0011] S5. Activate the wood grain transfer film in water until the film begins to become soft and removable. Place the activated transfer film flat on the surface of the wine box, ensuring that the wood grain pattern is aligned with the surface of the wine box and avoiding bubbles or wrinkles.

[0012] S6. Start the transfer equipment and set the appropriate temperature, pressure and transfer time according to the equipment requirements so that the wood grain pattern is transferred to the surface of the wine box. After the transfer is completed, tear off the transfer film from the surface of the wine box to ensure that the transfer pattern is not damaged;

[0013] S7. Place the wine box in a drying device to heat and cure the transfer pattern. After curing, add a clear coat or varnish to protect the wood grain pattern and increase the gloss and texture of the appearance.

[0014] S8. Check the quality and appearance of the transferred wood grain wine box. If peeling, damage or other problems are found, they can be repaired or adjusted. Depending on the specific situation, it may be necessary to re-transfer part of the pattern or perform local repairs. The repaired part uses cold transfer.

[0015] Preferably, the quality and appearance in S8 include clarity and adhesion of the pattern.

[0016] Preferably, the temperature in S6 is between 80°C and 150°C, and the pressure is 0.5 kg / cm 2 Up to 2.5kg / cm 2 .

[0017] Preferably, the material of the varnish is acrylate.

[0018] Preferably, the drying in S2 is carried out by standing and air-drying.

[0019] Preferably, the heating and curing temperature is between 100°C and 150°C.

[0020] Preferably, the transfer film is made of polyester film.

[0021] (III) Beneficial effects

[0022] The present invention provides a preparation process of a plastic transfer wood grain wine box. It has the following beneficial effects:

[0023] Thermal transfer can achieve high-precision pattern transfer, making the transferred pattern clear and rich in details, and can be applied to complex patterns and textures. It has high durability and scratch resistance, and can keep the pattern bright and stable during long-term use. Low-temperature operation is used during the repair process, and the transfer process can be completed at a lower temperature, thereby reducing the thermal sensitivity and deformation risk of the material. After the cold transfer is completed, the pattern can be used immediately without waiting for the curing or drying process, and will not cause damage to the transferred part. DETAILED DESCRIPTION

[0024] The technical solutions in the embodiments of the present invention are described clearly and completely. Obviously, the described embodiments are only part of the embodiments of the present invention, not all of the embodiments. Based on the embodiments of the present invention, all other embodiments obtained by ordinary technicians in this field without creative work are within the scope of protection of the present invention.

[0025] Embodiment 1:

[0026] An embodiment of the present invention provides a preparation process for a plastic transfer wood grain wine box, comprising the following steps: S1, using computer-aided design to create a desired wood grain pattern, the wood grain pattern including oak, walnut, and cherry, and designing according to the size and design requirements of the wine box to determine the desired wood grain transfer film type and specifications.

[0027] S2. Clean the surface of the wine box to remove dirt, grease and other impurities. Use a damp cloth to thoroughly clean the surface of the wine box. Make sure the surface is smooth and dry. Check for any damage or uneven areas. Dry by leaving it to dry.

[0028] S3. Cut the selected wood grain transfer film into appropriate size to cover the entire surface of the wine box, and ensure that the size of the cut transfer film matches the wine box. The material of the transfer film is polyester film. Polyester film is a high-strength and heat-resistant transfer film material with good transparency and weather resistance. It is suitable for the need to keep the pattern bright and durable. The transfer film also contains some auxiliary ingredients and additives to improve performance and application characteristics. The adhesive is used to provide adhesion between the transfer film and the surface of the wine box. The filler is used to adjust the thickness and optical properties of the transfer film. The anti-sticking agent is used to reduce the viscosity of the transfer film to prevent unnecessary adhesion. The antioxidant is used to prevent the material in the transfer film from oxidation and degradation. Pigments and pigment dispersants are used to provide color and pattern to the transfer film.

[0029] S4. Place the wine box on the transfer device and ensure that the wine box is fixed and stable to prevent movement or shaking.

[0030] S5. Activate the wood grain transfer film by placing it in water until the film begins to become soft and removable. Place the activated transfer film flat on the surface of the wine box, ensuring that the wood grain pattern is aligned with the surface of the wine box and avoiding bubbles or wrinkles.

[0031] S6. Start the transfer equipment and set the appropriate temperature, pressure and transfer time according to the equipment requirements so that the wood grain pattern can be transferred to the surface of the wine box. After the transfer is completed, tear off the transfer film from the surface of the wine box to ensure that the transfer pattern will not be damaged. The temperature is between 80°C and the pressure is 0.5kg / cm 2 .

[0032] S7. Place the wine box in a drying device to heat and cure the transfer pattern. After curing, add a clear coating or varnish to protect the wood grain pattern and increase the gloss and texture of the appearance. The material of the varnish is acrylic, and the heating and curing temperature is between 100°C.

[0033] S8. Check the quality and appearance of the transferred wood grain wine box. If peeling, damage or other problems are found, they can be repaired or adjusted. Depending on the specific situation, it may be necessary to re-transfer part of the pattern or perform local repairs. The repaired part uses cold transfer. The quality and appearance include the clarity and adhesion of the pattern.

[0034] Embodiment 2:

[0035] An embodiment of the present invention provides a preparation process for a plastic transfer wood grain wine box, comprising the following steps: S1, using computer-aided design to create a desired wood grain pattern, the wood grain pattern including oak, walnut, and cherry, and designing according to the size and design requirements of the wine box to determine the desired wood grain transfer film type and specifications.

[0036] S2. Clean the surface of the wine box to remove dirt, grease and other impurities. Use a damp cloth to thoroughly clean the surface of the wine box. Make sure the surface is smooth and dry. Check for any damage or uneven areas. Dry by leaving it to dry.

[0037] S3. Cut the selected wood grain transfer film into appropriate size to cover the entire surface of the wine box, and ensure that the size of the cut transfer film matches the wine box. The material of the transfer film is polyester film. Polyester film is a high-strength and heat-resistant transfer film material with good transparency and weather resistance. It is suitable for the need to keep the pattern bright and durable. The transfer film also contains some auxiliary ingredients and additives to improve performance and application characteristics. The adhesive is used to provide adhesion between the transfer film and the surface of the wine box. The filler is used to adjust the thickness and optical properties of the transfer film. The anti-sticking agent is used to reduce the viscosity of the transfer film to prevent unnecessary adhesion. The antioxidant is used to prevent the material in the transfer film from oxidation and degradation. Pigments and pigment dispersants are used to provide color and pattern to the transfer film.

[0038] S4. Place the wine box on the transfer device and ensure that the wine box is fixed and stable to prevent movement or shaking.

[0039] S5. Activate the wood grain transfer film by placing it in water until the film begins to become soft and removable. Place the activated transfer film flat on the surface of the wine box, ensuring that the wood grain pattern is aligned with the surface of the wine box and avoiding bubbles or wrinkles.

[0040] S6. Start the transfer equipment and set the appropriate temperature, pressure and transfer time according to the equipment requirements so that the wood grain pattern can be transferred to the surface of the wine box. After the transfer is completed, tear off the transfer film from the surface of the wine box to ensure that the transfer pattern will not be damaged. The temperature is between 150°C and the pressure is 2.5kg / cm 2 .

[0041] S7. Place the wine box in a drying device to heat and cure the transfer pattern. After curing, add a clear coating or varnish to protect the wood grain pattern and increase the gloss and texture of the appearance. The material of the varnish is acrylic, and the heating and curing temperature is between 150°C.

[0042] S8. Check the quality and appearance of the transferred wood grain wine box. If peeling, damage or other problems are found, they can be repaired or adjusted. Depending on the specific situation, it may be necessary to re-transfer part of the pattern or perform local repairs. The repaired part uses cold transfer. The quality and appearance include the clarity and adhesion of the pattern.

[0043] Embodiment three:

[0044] An embodiment of the present invention provides a preparation process for a plastic transfer wood grain wine box, comprising the following steps: S1, using computer-aided design to create a desired wood grain pattern, the wood grain pattern including oak, walnut, and cherry, and designing according to the size and design requirements of the wine box to determine the desired wood grain transfer film type and specifications.

[0045] S2. Clean the surface of the wine box to remove dirt, grease and other impurities. Use a damp cloth to thoroughly clean the surface of the wine box. Make sure the surface is smooth and dry. Check for any damage or uneven areas. Dry by leaving it to dry.

[0046] S3. Cut the selected wood grain transfer film into appropriate size to cover the entire surface of the wine box, and ensure that the size of the cut transfer film matches the wine box. The material of the transfer film is polyester film. Polyester film is a high-strength and heat-resistant transfer film material with good transparency and weather resistance. It is suitable for the need to keep the pattern bright and durable. The transfer film also contains some auxiliary ingredients and additives to improve performance and application characteristics. The adhesive is used to provide adhesion between the transfer film and the surface of the wine box. The filler is used to adjust the thickness and optical properties of the transfer film. The anti-sticking agent is used to reduce the viscosity of the transfer film to prevent unnecessary adhesion. The antioxidant is used to prevent the material in the transfer film from oxidation and degradation. Pigments and pigment dispersants are used to provide color and pattern to the transfer film.

[0047] S4. Place the wine box on the transfer device and ensure that the wine box is fixed and stable to prevent movement or shaking.

[0048] S5. Activate the wood grain transfer film by placing it in water until the film begins to become soft and removable. Place the activated transfer film flat on the surface of the wine box, ensuring that the wood grain pattern is aligned with the surface of the wine box and avoiding bubbles or wrinkles.

[0049] S6. Start the transfer equipment and set the appropriate temperature, pressure and transfer time according to the equipment requirements so that the wood grain pattern can be transferred to the surface of the wine box. After the transfer is completed, tear off the transfer film from the surface of the wine box to ensure that the transfer pattern will not be damaged. The temperature is between 120°C and the pressure is 1.5kg / cm 2 .

[0050] S7. Place the wine box in a drying device to heat and cure the transfer pattern. After curing, add a clear coating or varnish to protect the wood grain pattern and increase the gloss and texture of the appearance. The material of the varnish is acrylic, and the heating and curing temperature is between 120°C.

[0051] S8. Check the quality and appearance of the transferred wood grain wine box. If peeling, damage or other problems are found, they can be repaired or adjusted. Depending on the specific situation, it may be necessary to re-transfer part of the pattern or perform local repairs. The repaired part uses cold transfer. The quality and appearance include the clarity and adhesion of the pattern.

[0052] Although embodiments of the present invention have been shown and described, it will be appreciated by those skilled in the art that various changes, modifications, substitutions and variations may be made to the embodiments without departing from the principles and spirit of the present invention, and that the scope of the present invention is defined by the appended claims and their equivalents.

Claims

1. A preparation process for a plastic transfer wood grain wine box, characterized in that: include: S1. Use computer-aided design to create the required wood grain pattern, design it according to the size and design requirements of the wine box, and determine the required wood grain transfer film type and specifications; S2. Clean the surface of the wine box to remove dirt, grease and other impurities. Use a damp cloth to thoroughly clean the surface of the wine box, making sure the surface is smooth and dry, and check for any damaged or uneven areas. S3, cut the selected wood grain transfer film into appropriate size to cover the entire surface of the wine box, and ensure that the size of the cut transfer film matches the wine box; S4. Place the wine box on the transfer device and ensure that the wine box is fixed and stable to prevent movement or shaking; S5. Activate the wood grain transfer film in water until the film begins to become soft and movable. Place the activated transfer film flat on the surface of the wine box, ensuring that the wood grain pattern is aligned with the surface of the wine box and avoiding bubbles or wrinkles. S6. Start the transfer equipment and set the appropriate temperature, pressure and transfer time according to the equipment requirements so that the wood grain pattern is transferred to the surface of the wine box. After the transfer is completed, tear off the transfer film from the surface of the wine box to ensure that the transfer pattern is not damaged; S7. Place the wine box in a drying device to heat and cure the transfer pattern. After curing, add a clear coat or varnish to protect the wood grain pattern and increase the gloss and texture of the appearance. S8. Check the quality and appearance of the transferred wood grain wine box. If peeling, damage or other problems are found, they can be repaired or adjusted. Depending on the specific situation, it may be necessary to re-transfer part of the pattern or perform local repairs. The repaired part uses cold transfer.

2. The preparation process of a plastic transfer wood grain wine box according to claim 1, characterized in that: The quality and appearance mentioned in S8 include the clarity and adhesion of the pattern.

3. The preparation process of a plastic transfer wood grain wine box according to claim 1, characterized in that: The temperature in S6 is between 80°C and 150°C and the pressure is 0.5 kg / cm 2 Up to 2.5kg / cm 2 .

4. The preparation process of a plastic transfer wood grain wine box according to claim 1, characterized in that: The material of the varnish is acrylate.

5. The preparation process of a plastic transfer wood grain wine box according to claim 1, characterized in that: The drying in S2 is carried out by standing and air-drying.

6. The preparation process of a plastic transfer wood grain wine box according to claim 1, characterized in that: The heating and curing temperature is between 100°C and 150°C.

7. The preparation process of a plastic transfer wood grain wine box according to claim 1, characterized in that: The transfer film is made of polyester film.