Heterojunction solar cell and preparation method thereof
By using a high doping upper limit carbon oxide layer and a silicon substrate to form a PN junction in a silicon-based heterojunction battery, the problem of low doping efficiency is solved, the battery efficiency and stability are improved, and high-efficiency solar cells are achieved performance.
Patent Information
- Application Number
- CN202411421555.3
- Authority / Receiving Office
- CN · China
- Patent Type
- Applications(China)
- Current Assignee / Owner
- Filing Date
- 2022-11-14
- Publication Date
- 2025-01-10
AI Technical Summary
The doping efficiency of the p-type doped layer in existing silicon-based heterojunction batteries is low, resulting in weakening of electric field and low battery efficiency.
Using a carbon silicon oxide layer as the PN junction material, through n-type or p-type doping treatment, the atomic percentage of carbon elements is greater than the atomic percentage of oxygen elements, increasing the doping limit, and forming a multi-layer structure on the silicon substrate to improve the battery performance.
The doping limit of dopant and the efficiency of solar cells are improved, the loss of hydrogen elements and the defect density are reduced, and the stability of the carbon silicon oxide layer and doping activation concentration are enhanced.
Smart Images
Figure CN119300472A_ABST
Abstract
Description
[0001] This application is a divisional application of the invention patent application filed on May 02, 2023, with application number 202211419460.9, and the invention name is "Heterojunction solar cell and preparation method". Technical Field
[0002] The present application mainly relates to the photovoltaic field, and specifically to a heterojunction solar cell and a preparation method thereof. Background Art
[0003] Silicon-based heterojunction cells are one of the current mainstream high-efficiency solar cell technologies. They have the advantages of simple structure, high conversion efficiency and low temperature coefficient, and are one of the important directions for the development of solar cells. The structure and process flow of silicon-based heterojunction cells are relatively simple. They use an n-type or p-type doped silicon substrate as the base layer, forming an intrinsic amorphous silicon layer and a p- or n-type amorphous silicon layer on one side of the silicon substrate, and forming an intrinsic amorphous silicon layer and an n-type amorphous silicon layer on the other side of the silicon substrate. Among them, the p- or n-type amorphous silicon layer forms a PN junction with the n-type or p-type doped silicon substrate.
[0004] In the silicon-based heterojunction battery in the prior art, the p-type doped layer is amorphous silicon doped with boron, but due to the upper limit of the doping amount, the doping efficiency of the p-type doped layer is low, resulting in a weakened electric field at the PN junction on the back of the battery, increased recombination of photogenerated carriers, and ultimately low battery efficiency.
[0005] Therefore, how to increase the upper limit of doping of dopants and improve battery efficiency is an urgent problem to be solved. Summary of the invention
[0006] The technical problem to be solved by the present application is to provide a heterojunction solar cell and a preparation method thereof, wherein the solar cell has the advantages of a high upper limit of doping and high cell efficiency.
[0007] The technical solution adopted by the present application to solve the above-mentioned technical problems is a heterojunction solar cell, comprising: a silicon substrate, which is treated with n-type or p-type doping and has a relative front and back sides; a first passivation layer and a second passivation layer, which are sequentially arranged on the front side of the silicon substrate; a third passivation layer and a fourth passivation layer, which are sequentially arranged on the back side of the silicon substrate; and a silicon oxycarbide layer, which is arranged on a side of the fourth passivation layer away from the silicon substrate, wherein the silicon oxycarbide layer is treated with n-type or p-type doping to form a PN junction with the silicon substrate, and the atomic percentage of the carbon element in the silicon oxycarbide layer is greater than the atomic percentage of the oxygen element.
[0008] In one embodiment of the present application, the first passivation layer is hydrogenated amorphous silicon oxide, and the second passivation layer is hydrogenated nanocrystalline silicon.
[0009] In one embodiment of the present application, the third passivation layer is hydrogenated amorphous silicon, and the fourth passivation layer is hydrogenated nanocrystalline silicon.
[0010] In one embodiment of the present application, the silicon substrate is n-type doped, and the silicon oxycarbide layer is p-type doped.
[0011] In one embodiment of the present application, a fifth passivation layer is further included, which is disposed on a side of the second passivation layer away from the silicon substrate, wherein the material of the fifth passivation layer is hydrogenated n-type microcrystalline or nanocrystalline silicon oxycarbide.
[0012] In one embodiment of the present application, it also includes a first transparent conductive oxide film and a second transparent conductive oxide film, the first transparent conductive oxide film is arranged on a side of the fifth passivation layer away from the silicon substrate, and the second transparent conductive oxide film is arranged on a side of the silicon oxycarbide layer away from the silicon substrate.
[0013] In one embodiment of the present application, an anti-reflection film is further included, which is disposed on a side of the first transparent conductive oxide film away from the silicon substrate.
[0014] In one embodiment of the present application, it also includes a first electrode and a second electrode, the first electrode and the second electrode are in contact with the first transparent conductive oxide film and the second transparent conductive oxide film respectively, wherein the first electrode and / or the second electrode are manufactured by electroplating or chemical plating.
[0015] In one embodiment of the present application, the atomic percentage of the carbon element in the silicon oxycarbide layer is equal to or greater than 7 times the atomic percentage of the oxygen element.
[0016] In order to solve the above technical problems, the present application also proposes a method for preparing a heterojunction solar cell, comprising the steps of: providing an n-type or p-type silicon wafer, wherein the n-type or p-type silicon wafer has a relative front side and back side; sequentially forming a first passivation layer and a second passivation layer on the front side of the n-type or p-type silicon wafer; sequentially forming a third passivation layer and a fourth passivation layer on the back side of the n-type or p-type silicon wafer; and forming a carbide oxide layer on a side of the fourth passivation layer away from the n-type or p-type silicon wafer, wherein the carbide oxide layer is treated with n-type or p-type doping to form a PN junction with the n-type or p-type silicon wafer, and the atomic percentage of carbon element in the carbide oxide layer is greater than the atomic percentage of oxygen element.
[0017] The heterojunction solar cell of the present application uses a doped silicon carbide layer and an n-type or p-type silicon wafer to form a PN junction, which increases the doping upper limit of the dopant in the silicon carbide layer, thereby improving the performance of the solar cell. The carbon element and the oxygen element have a fixing effect on the hydrogen element in the silicon carbide layer, which is beneficial to reduce the loss of the hydrogen element. BRIEF DESCRIPTION OF THE DRAWINGS
[0018] In order to make the above-mentioned objects, features and advantages of the present application more obvious and easy to understand, the specific implementation methods of the present application are described in detail below with reference to the accompanying drawings, wherein:
[0019] Figure 1 is a cross-sectional schematic diagram of a heterojunction solar cell according to an embodiment of the present application;
[0020] Figure 2 It is an exemplary flow chart of a method for preparing a heterojunction solar cell according to an embodiment of the present application. DETAILED DESCRIPTION
[0021] In order to make the above-mentioned objects, features and advantages of the present application more obvious and easy to understand, the specific implementation methods of the present application are described in detail below with reference to the accompanying drawings.
[0022] In the following description, many specific details are set forth to facilitate a full understanding of the present application, but the present application may also be implemented in other ways different from those described herein, and therefore the present application is not limited to the specific embodiments disclosed below.
[0023] As shown in this application and claims, unless the context clearly indicates an exception, the words "a", "an", "an" and / or "the" do not refer to the singular and may also include the plural. Generally speaking, the terms "include" and "comprise" only indicate the inclusion of the steps and elements that have been clearly identified, and these steps and elements do not constitute an exclusive list. The method or device may also include other steps or elements.
[0024] In addition, it should be noted that the use of words such as "first" and "second" to define components is only for the convenience of distinguishing the corresponding components. If not otherwise stated, the above words have no special meaning and cannot be understood as limiting the scope of protection of this application. In addition, although the terms used in this application are selected from well-known and commonly used terms, some terms mentioned in the specification of this application may be selected by the applicant at his or her discretion, and their detailed meanings are explained in the relevant parts of the description of this article. In addition, it is required to understand this application not only by the actual terms used, but also by the meaning implied by each term.
[0025] Flowcharts are used in the present application to illustrate the operations performed by the system according to the embodiments of the present application. It should be understood that the preceding or following operations are not necessarily performed accurately in order. On the contrary, various steps may be processed in reverse order or simultaneously. At the same time, other operations may be added to these processes, or one or more operations may be removed from these processes.
[0026] The PN junction in the heterojunction solar cell is composed of a doped silicon substrate and a material layer located on one side of the silicon substrate and doped with a dopant having a polarity opposite to that of the dopant in the silicon substrate. In conventional technology, the upper limit of doping in the material layer is relatively low. The heterojunction solar cell of the present application has the advantage of a high upper limit of doping.
[0027] Next, the heterojunction solar cell of the present application is described through specific embodiments.
[0028] Figure 1 is a cross-sectional schematic diagram of a heterojunction solar cell according to an embodiment of the present application. Figure 1 As shown, the heterojunction solar cell 100 includes a silicon substrate 110 , a first passivation layer 120 , a second passivation layer 130 , a third passivation layer 140 , a fourth passivation layer 150 and a silicon oxycarbide layer 160 .
[0029] Specifically, Figure 1 As shown, the silicon substrate 110 is treated with n-type or p-type doping. The material of the silicon substrate 110 includes one or more of single crystal silicon or polycrystalline silicon. Phosphorus (P) can be doped into the single crystal silicon through a doping process to form an n-type silicon substrate 110, or boron (B) can be doped into the single crystal silicon to form a p-type silicon substrate 110. It can be understood that the doping elements in the silicon substrate 110 are not limited to the above-mentioned phosphorus and boron elements, and can also be other elements that can form n-type and p-type silicon substrates.
[0030] In addition, the silicon substrate 110 is not limited to any specific size and shape. The silicon substrate 110 can be a circular substrate with a diameter of 200 mm, a diameter of 300 mm, or other diameters (such as 450 mm). As required, the silicon substrate 110 can also be any polygonal, square, rectangular, curved or other non-circular workpiece, such as a polygonal silicon substrate.
[0031] refer to Figure 1 As shown, the silicon substrate 110 has a front side 110a and a back side 110b opposite to each other along the thickness direction D1. The front side 110a refers to the silicon substrate 110 in the Figure 1 The upper side of the middle.
[0032] In one embodiment, the silicon substrate 110 is an n-type doped silicon substrate. For the convenience of description, unless otherwise specified, the silicon substrate 110 in the following text is an n-type doped silicon substrate.
[0033] Continue to refer Figure 1As shown, the first passivation layer 120 is disposed on the front side 111a of the silicon substrate 110, and the second passivation layer 130 is disposed on the side of the first passivation layer 120 away from the silicon substrate 110 along the thickness direction D1, that is, the first passivation layer 120 and the second passivation layer 130 are sequentially disposed on the front side 110a of the silicon substrate 110. The method of sequentially forming the first passivation layer 120 and the second passivation layer 130 on the front side 110a of the silicon substrate 110 includes: sequentially forming the first passivation layer 120 and the second passivation layer 130 on the front side 110a of the silicon substrate 110 by high frequency chemical vapor deposition (VHF-PECVD), wherein the thickness of the first passivation layer 120 is 0.8-1.5nm, and the thickness of the second passivation layer 130 is 3-4nm. In some embodiments, before forming the first passivation layer 120, the silicon substrate 110 is also subjected to damage removal cleaning and texturing treatment. The damage removal cleaning can remove damage on the front side 110a and the back side 110b of the silicon substrate 110, and the texturing treatment can form a pyramid velvet surface, thereby reducing the reflectivity of the silicon substrate 110 to light.
[0034] In one embodiment, the first passivation layer is hydrogenated amorphous silicon oxide, and the second passivation layer is hydrogenated nanocrystalline silicon. Compared with single crystal silicon oxide and amorphous silicon oxide, the use of amorphous in the first passivation layer is conducive to increasing the content of hydrogen in the first passivation layer, so that the passivation performance of the first passivation layer can be improved, and the probability of growth of epitaxial crystals at the interface can be reduced, thereby increasing the photocurrent density of the battery. In addition, the oxygen element in the first passivation layer can form a hydrogen bond with the hydrogen element, thereby preventing the hydrogen element from diffusing out of the first passivation layer. The conductivity of the second passivation layer using nanocrystalline silicon is better than that of the second passivation layer using amorphous silicon, so the resistivity of the second passivation layer can be reduced and the fill factor (FF) of the battery can be improved. The combination of the first passivation layer and the second passivation layer can ensure that the conductivity of the passivation layer meets the requirements while obtaining an excellent passivation effect. In some embodiments, the size of the nanocrystalline silicon in the second passivation layer is 2-5nm, and the crystallization rate of the second passivation layer is 10%-70%. Here, "hydrogenation" refers to the introduction of hydrogen atoms (H) into the material layer (e.g., the first passivation layer, the second passivation layer), which can neutralize the dangling bonds and defects in the material layer, thereby reducing the recombination of carriers and improving the efficiency of the battery. Unless otherwise specified, the above explanation of "hydrogenation" also applies to the following text and will not be repeated in the following text.
[0035] In another embodiment, reference Figure 1As shown, the solar cell 100 further includes a fifth passivation layer 170 disposed on a side of the second passivation layer 130 away from the silicon substrate 110. The material of the fifth passivation layer 170 is hydrogenated n-type microcrystalline or nanocrystalline carbon oxide silicon. When the carbon oxide silicon in the fifth passivation layer 170 is microcrystalline carbon oxide silicon, its grain size is 10-100nm. The atomic percentage of oxygen in the fifth passivation layer may be greater than, equal to, or less than the atomic percentage of carbon. The fifth passivation layer 170 has the functions of transmitting electrons and field passivation, which is beneficial to improving the performance of the battery.
[0036] In some embodiments, the method for manufacturing the fifth passivation layer 170 includes depositing the fifth passivation layer 170 on the side of the second passivation layer 130 away from the silicon substrate 110 by high frequency chemical vapor deposition (VHF-PECVD), and the thickness of the fifth passivation layer 170 is 10-20nm. In the previous embodiment, the material used for the second passivation layer 130 is hydrogenated nanocrystalline silicon, and the hydrogenated nanocrystalline silicon at the side where the second passivation layer 130 contacts the fifth passivation layer 170 can be used as a seed layer of n-type microcrystals or nanocrystalline silicon oxycarbide in the fifth passivation layer, which is beneficial to improving the crystallization rate of the fifth passivation layer.
[0037] Back to Figure 1 As shown, the third passivation layer 140 is located on the back side 110b of the silicon substrate 110, and the fourth passivation layer 150 is located on the side of the third passivation layer 140 away from the silicon substrate 110, that is, the third passivation layer 140 and the fourth passivation layer 150 are sequentially formed on the back side 110b of the silicon substrate 110. In some embodiments, the method of manufacturing the third passivation layer 140 and the fourth passivation layer 150 can be the same as that of the first passivation layer 120 and the second passivation layer 130, wherein the thickness of the third passivation layer 140 is 5-10nm, and the thickness of the fourth passivation layer 150 is 3-4nm.
[0038] In one embodiment, the third passivation layer is hydrogenated amorphous silicon, and the fourth passivation layer is hydrogenated nanocrystalline silicon. Compared with using hydrogenated nanocrystalline silicon as the material of the third passivation layer, using amorphous silicon helps to increase the content of hydrogen in the third passivation layer, thereby improving the passivation effect. Because high-concentration hydrogen plasma has an etching effect on amorphous silicon during the process, the thickness of the third passivation layer may be less than the designed thickness. Therefore, nanocrystalline silicon is used as the material of the fourth passivation layer, which plays a role in auxiliary passivation, thereby ensuring the passivation effect. In some embodiments, the size of the nanocrystalline silicon of the fourth passivation layer is 2-5nm, and the crystallization rate of the fourth passivation layer is 10%-70%.
[0039] Continue to refer Figure 1As shown, the silicon oxycarbide layer 160 is disposed on a side of the fourth passivation layer 150 away from the silicon substrate 110. The silicon oxycarbide layer is treated with n-type or p-type doping to form a PN junction with the silicon substrate 110, and the atomic percentage of carbon in the silicon oxycarbide layer is greater than the atomic percentage of oxygen. As mentioned above, the silicon substrate 110 can be an n-type silicon substrate or a p-type silicon substrate. When the silicon substrate 110 is an n-type silicon substrate, the silicon oxycarbide layer 160 is a p-type doped silicon oxycarbide layer to form a PN junction with the silicon substrate 110. Otherwise, the silicon oxycarbide layer 160 is an n-type doped silicon oxycarbide layer. For the convenience of description, the silicon oxycarbide layer 160 in the following text is p-type doped. In some embodiments, the method for forming the silicon carbide layer 160 is the same as that of the fourth passivation layer, wherein the thickness of the silicon carbide layer 160 is 5-10 nm, and the silicon carbide can be microcrystalline silicon carbide or nanocrystalline silicon carbide. When the silicon carbide is microcrystalline silicon carbide, its grain size is 10-100 nm, and when the silicon carbide is nanocrystalline silicon carbide, its grain size is 2-5 nm.
[0040] In conventional technology, boron is usually used to dope amorphous silicon to obtain a p-type doped layer, but the doping activation rate is low, so it is necessary to increase the doping amount to increase the doping activation amount, but this may lead to overdoping, thereby generating a dead layer. In addition, when boron is used to dope microcrystalline silicon to obtain a p-type doped layer, the doping upper limit of the boron element in the microcrystalline silicon is low. The present application doping of carbon oxide silicon can effectively solve the above problems. Since carbon and silicon are chemical elements of the same family, they can be efficiently incorporated into the silicon thin film structure during the preparation process to form a stable carbon silicon compound, so that the optical band gap of the solar cell can be increased. In addition, the addition of oxygen can further increase the optical band gap, and both oxygen and carbon have the effect of fixing hydrogen, thereby reducing the loss of hydrogen and causing the internal defect density of the carbon oxide silicon layer 160 to increase. At the same time, the doping upper limit of carbon oxide silicon is high, it is not easy to form a dead layer, and microcrystallization can also increase the doping activation concentration, so the use of p-type hydrogenated doped microcrystalline carbon oxide silicon can improve the performance of silicon-based heterojunction cells. On the basis of using silicon oxycarbide as the p-type layer, the present application further defines that the carbon content in the silicon oxycarbide layer is greater than the oxygen content, so that more carbon-silicon bonds can be formed in the silicon oxycarbide layer. On the one hand, compared with silicon oxide, silicon carbide has a wider band gap and a higher upper limit of doping, thereby improving the doping amount and the performance of the solar cell. On the other hand, when the doping element in the silicon oxycarbide layer is boron, the oxygen element in the silicon oxycarbide layer will combine with the boron element to form a boron-oxygen pair, causing the solar cell to attenuate. Therefore, reducing the oxygen content is conducive to reducing the combination of boron and oxygen. In some other embodiments, the atomic percentage of carbon in the silicon oxycarbide layer is equal to or greater than 7 times the atomic percentage of oxygen, so that the doping amount in the silicon oxycarbide layer can be guaranteed to meet the requirements.
[0041] In one embodiment, the solar cell further comprises a first transparent conductive oxide film and a second transparent conductive oxide film. Figure 1 As shown, the first transparent conductive oxide film 180 is disposed on the side of the fifth passivation layer 170 away from the silicon substrate 110, and the second transparent conductive oxide film 190 is disposed on the side of the fourth passivation layer 160 away from the silicon substrate 110. In some embodiments, the method for preparing the transparent conductive oxide film includes physical vapor deposition (PVD) and reactive plasma deposition (RPD), wherein the thickness of the first transparent conductive oxide film 180 and the second transparent conductive oxide film 190 is 60-80 nm. It should be noted that the thickness of the first transparent conductive oxide film 180 and the second transparent conductive oxide film 190 may be equal or unequal.
[0042] refer to Figure 1 As shown, in another embodiment, the solar cell 100 further includes a first electrode 211 and a second electrode 212. The first electrode 211 and the second electrode 212 are in contact with the first transparent conductive oxide film 180 and the second transparent conductive oxide film 190, respectively. The first transparent conductive oxide film 180 can prevent the first electrode 211 from directly contacting the fifth passivation layer 170, and the second transparent conductive oxide film 190 can prevent the second electrode 212 from directly contacting the silicon oxycarbide layer 160, thereby avoiding a significant increase in resistance.
[0043] In some embodiments, the method of manufacturing the first electrode and the second electrode includes electroplating or chemical plating, and the materials of the first electrode and the second electrode include one or more of metal copper, metal aluminum, metal nickel, and metal tin. Compared with screen printing of silver electrodes, manufacturing non-silver electrodes by electroplating or chemical plating has the advantage of low cost.
[0044] like Figure 1 As shown, in one embodiment, the solar cell 100 further includes an anti-reflection film 220 disposed on a side of the first transparent conductive oxide film 180 away from the silicon substrate 110. In some embodiments, the number of anti-reflection films is not limited to Figure 1 The anti-reflection film 220 may be 1 layer, or may be 2 layers, 3 layers, or any other number. The material of the anti-reflection film includes, but is not limited to, one or more of silicon nitride, silicon oxide, magnesium fluoride, and titanium oxide. The anti-reflection film 220 solar cell reflects incident light, thereby improving the utilization rate of the light of the cell.
[0045] The solar cell in the above embodiment uses a doped silicon carbide layer and a silicon substrate to form a PN junction, and limits the atomic percentage of carbon elements in the silicon carbide layer to be greater than the atomic percentage of oxygen atoms, thereby increasing the upper limit of the doping of the dopant in the silicon carbide layer, thereby improving the performance of the solar cell. The carbon element and the oxygen element have a fixing effect on the hydrogen element in the silicon carbide layer, which is beneficial to reducing the loss of the hydrogen element.
[0046] On the other hand, the present application also provides a method for preparing a heterojunction solar cell. Figure 2 The exemplary flow chart of the method for preparing a heterojunction solar cell in one embodiment of the present application is shown in FIG. Figure 1 As shown, the preparation method comprises the following steps:
[0047] Step S110: providing an n-type or p-type silicon wafer 110, wherein the n-type or p-type silicon wafer has a front side 110a and a back side 110b opposite to each other;
[0048] Step S120: sequentially forming a first passivation layer 120 and a second passivation layer 130 on the front side 110 a of the n-type or p-type silicon wafer 110 ;
[0049] Step S130: forming a third passivation layer 140 and a fourth passivation layer 150 in sequence on the back side 110 b of the n-type or p-type silicon wafer 110 ;
[0050] Step S140: forming a silicon oxycarbide layer 160 on a surface of the fourth passivation layer 150 away from the n-type or p-type silicon wafer 110, wherein the silicon oxycarbide layer 160 is treated with n-type or p-type doping to form a PN junction with the n-type or p-type silicon wafer 110, and the atomic percentage of carbon in the silicon oxycarbide layer 160 is greater than the atomic percentage of oxygen.
[0051] For other details about the method for preparing the heterojunction solar cell of the present application, please refer to the relevant description above, which will not be elaborated again.
[0052] The preparation method in the above embodiment uses a doped silicon carbide layer and an n-type or p-type silicon wafer to form a PN junction, and limits the atomic percentage of carbon elements in the silicon carbide layer to be greater than the percentage of oxygen atoms, thereby increasing the doping upper limit of the dopant in the silicon carbide layer, thereby improving the performance of the solar cell. The carbon element and the oxygen element have a fixing effect on the hydrogen element in the silicon carbide layer, which is beneficial to reducing the loss of hydrogen elements.
[0053] The basic concepts have been described above. Obviously, for those skilled in the art, the above application disclosure is only an example and does not constitute a limitation of the present application. Although not explicitly stated herein, those skilled in the art may make various modifications, improvements and amendments to the present application. Such modifications, improvements and amendments are suggested in the present application, so such modifications, improvements and amendments still belong to the spirit and scope of the exemplary embodiments of the present application.
[0054] At the same time, the present application uses specific words to describe the embodiments of the present application. For example, "one embodiment", "an embodiment", and / or "some embodiments" refer to a certain feature, structure or characteristic related to at least one embodiment of the present application. Therefore, it should be emphasized and noted that "one embodiment" or "an embodiment" or "an alternative embodiment" mentioned twice or more in different positions in this specification does not necessarily refer to the same embodiment. In addition, some features, structures or characteristics in one or more embodiments of the present application can be appropriately combined.
[0055] In some embodiments, numbers describing the number of components and attributes are used. It should be understood that such numbers used in the description of the embodiments are modified by the modifiers "about", "approximately" or "substantially" in some examples. Unless otherwise specified, "about", "approximately" or "substantially" indicate that the numbers are allowed to vary by ±20%. Accordingly, in some embodiments, the numerical parameters used in the specification and claims are approximate values, which may change according to the required features of individual embodiments. In some embodiments, the numerical parameters should take into account the specified significant digits and adopt the general method of retaining digits. Although the numerical domains and parameters used to confirm the breadth of their range in some embodiments of the present application are approximate values, in specific embodiments, the setting of such numerical values is as accurate as possible within the feasible range.
Claims
1. A heterojunction solar cell, characterized in that: include: A silicon substrate, wherein the silicon substrate is n-type or p-type doped and has a front side and a back side opposite to each other; A first passivation layer and a second passivation layer are sequentially arranged on the front surface of the silicon substrate; A third passivation layer and a fourth passivation layer are sequentially disposed on the back side of the silicon substrate; A silicon oxycarbide layer is disposed on a side of the fourth passivation layer away from the silicon substrate, wherein the silicon oxycarbide layer is treated with n-type or p-type doping to form a PN junction with the silicon substrate, and the atomic percentage of carbon in the silicon oxycarbide layer is greater than the atomic percentage of oxygen.
2. The solar cell according to claim 1, wherein: The first passivation layer is hydrogenated amorphous silicon oxide, and the second passivation layer is hydrogenated nanocrystalline silicon.
3. The solar cell according to claim 1, wherein: The third passivation layer is hydrogenated amorphous silicon, and the fourth passivation layer is hydrogenated nanocrystalline silicon.
4. The solar cell according to claim 1, wherein: The silicon substrate is n-type doped, and the silicon oxycarbide layer is p-type doped.
5. The solar cell according to claim 4, characterized in that It also includes a fifth passivation layer, which is arranged on a side of the second passivation layer away from the silicon substrate, wherein the material of the fifth passivation layer is hydrogenated n-type microcrystalline or nanocrystalline silicon oxycarbide.
6. The solar cell according to claim 5, characterized in that It also includes a first transparent conductive oxide film and a second transparent conductive oxide film. The first transparent conductive oxide film is arranged on a side of the fifth passivation layer away from the silicon substrate, and the second transparent conductive oxide film is arranged on a side of the silicon oxycarbide layer away from the silicon substrate.
7. The solar cell according to claim 6, characterized in that It also includes an anti-reflection film, which is arranged on a side of the first transparent conductive oxide film away from the silicon substrate.
8. The solar cell according to claim 6, wherein: It also includes a first electrode and a second electrode, wherein the first electrode and the second electrode are in contact with the first transparent conductive oxide film and the second transparent conductive oxide film respectively, wherein the first electrode and / or the second electrode are manufactured by electroplating or chemical plating.
9. The solar cell according to claim 1, wherein: The atomic percentage of the carbon element in the silicon oxycarbide layer is equal to or greater than 7 times the atomic percentage of the oxygen element.
10. A method for preparing a heterojunction solar cell, characterized in that: Includes steps: Providing an n-type or p-type silicon wafer, wherein the n-type or p-type silicon wafer has a front side and a back side opposite to each other; Sequentially forming a first passivation layer and a second passivation layer on the front side of the n-type or p-type silicon wafer; forming a third passivation layer and a fourth passivation layer in sequence on the back side of the n-type or p-type silicon wafer; as well as A silicon oxycarbide layer is formed on a surface of the fourth passivation layer away from the n-type or p-type silicon wafer, wherein the silicon oxycarbide layer is treated with n-type or p-type doping to form a PN junction with the n-type or p-type silicon wafer, and the atomic percentage of carbon element in the silicon oxycarbide layer is greater than the atomic percentage of oxygen element.