Kitchen and bath brick-smashing-free waterproof agent

Abstract

The component A and the component B of the brick-smashing-free waterproof agent for kitchens and bathrooms are diluted by adding 3 times of clear water according to the weight ratio respectively, the diluted component A and the diluted component B are mixed together and uniformly stirred, and permeate into a mortar layer and a concrete structure layer along ceramic tile gaps under the action of self gravity to generate a chemical reaction to generate water-insoluble crystals, so that the waterproof agent for kitchens and bathrooms is formed. According to the brick-smashing-free waterproof agent for the kitchen and bathroom, water leakage channels of capillary pores and capillary seams are blocked, and on the premise that a decorative layer is not damaged, the nano silicon waterproof agent component in the brick-smashing-free waterproof agent for the kitchen and bathroom can generate secondary hydration reaction with free calcium and magnesium ions in a mortar layer and a concrete structure layer to form water-insoluble crystals; and the mortar layer and the concrete structure layer under the ceramic tile are formed into a dense whole again, so that the waterproof and leaking stoppage effects are achieved.

Description

Technical Field

[0001] The invention relates to a waterproof material for repairing and treating leakage in kitchens, toilets and bathrooms, in particular to a waterproof material for repairing and treating ground leakage in kitchens, toilets and bathrooms which does not require bricks to be smashed and does not damage a decorative layer. Background Art

[0002] The kitchen, toilet and bathroom, which are commonly referred to as the kitchen and bathroom, are areas with large water consumption inside a building. Although waterproofing treatment is carried out in the early stage of decoration, they become the hardest hit areas for water leakage during the later use due to various reasons such as aging of the waterproof layer, erosion of domestic water, leakage in details such as pipe floor drains, etc. At present, it has become the main trend to treat kitchen and bathroom leakage without breaking bricks. The common repair methods for treating kitchen and bathroom leakage without breaking bricks mainly include the following situations.

[0003] Sealing treatment with inorganic rigid plugging materials: Use inorganic rigid plugging materials such as Leak-proof and Water-proof to seal the gaps between tiles, so that the tile surface becomes a complete whole, ensuring that water will not penetrate into the structure through the tile joints. This treatment measure has low cost, but the material is not easy to embed into smaller gaps, and the tile joints need to be widened, which can easily cause damage to the decorative layer. In addition, the inorganic rigid plugging material is exposed on the surface. Under the influence of thermal expansion and contraction, building vibration, and human trampling in the later stage, the plugging material is easy to separate from the base layer, resulting in waterproof failure.

[0004] Treatment with special waterproofing agent for bathroom and kitchen repair (patent application number 200910119173.4): This invention patent has good waterproofing effect, but the A and B components in this invention patent are strong alkaline and strong acid, respectively, which will cause corrosion to construction workers or indoor items to a certain extent.

[0005] Treatment of deep penetrating and solidifying non-destructive waterproofing agent for indoor use in buildings (patent application number 201310511829.3): This invention patent includes two components, A and B. Components A and B penetrate into the leaking gaps according to the construction procedures in sequence, and after natural mixing, a water-insoluble gel-like solid substance is generated and solidified in the gaps to block the leakage channels. Component A and component B waterproofing agents are both water-soluble products. After construction, the floor can be easily cleaned with a mop, and no new pollution is caused to the construction site; however, because components A and B are constructed separately in sequence in this treatment method, the procedures are more complicated and the construction time is longer. Summary of the invention

[0006] Aiming at the problems existing in various waterproof materials and corresponding construction methods on the current market, the present invention proposes a kitchen and bathroom waterproofing agent without brick-breaking, thereby optimizing product performance.

[0007] The invention discloses a kitchen and bathroom waterproofing agent that does not require brick breaking, which is a two-component aqueous liquid waterproofing agent, including component A and component B, wherein the component A comprises: 54% of liquid sodium silicate, 5.4% of nano silicon waterproofing agent, 0.6% of triethanolamine, and 40% of deionized water; the component B comprises: 16% of inorganic medium-strong acid, and 84% of deionized water.

[0008] The functional principle of the present invention is as follows: the components A and B of the kitchen and bathroom tile-free waterproof agent are diluted with 3 times of clean water according to the weight ratio respectively, and the diluted components A and B are mixed together, stirred evenly, and poured on the floor tiles. Under the action of their own gravity, they penetrate into the mortar layer and the concrete structure layer along the gaps between the tiles, and chemical reactions occur to generate water-insoluble crystals, which block the water leakage channels of the capillary pores and capillary cracks. On the premise of not damaging the decorative layer, the mortar layer and the concrete structure layer under the tiles become a dense whole again, thereby achieving a waterproof and leak-proof effect.

[0009] The beneficial effects of the present invention are as follows: the kitchen and bathroom non-smashing brick waterproofing agent is a two-component waterproofing material, the diluted solutions of the A and B components are mixed together and constructed at the same time, it is liquid in the early stage, starts to thicken and gradually solidifies in about 60 minutes, and can effectively ensure that the waterproofing agent fully penetrates into the mortar layer and the concrete structure layer, chemically reacts to generate water-insoluble crystals, and blocks the water leakage channels of the capillary pores and capillary cracks, and at the same time, the nano-silicon waterproofing agent component in the kitchen and bathroom non-smashing brick waterproofing agent can produce a secondary hydration reaction with the free calcium and magnesium ions in the mortar layer and the concrete structure layer to form water-insoluble crystals, which complement each other with the crystals that block the capillary pores and capillary cracks, and achieve a reliable waterproofing effect. DETAILED DESCRIPTION

[0010] The present invention discloses a production process embodiment of a brick-breaking-free waterproofing agent for kitchens and bathrooms.

[0011] Component A: Measure by weight, take 54kg of liquid sodium silicate, 5.4kg of nano-silicon waterproofing agent, and 0.6kg of triethanolamine and add them into the running mixer in sequence. After all the above materials are added, continue to stir evenly for 30 minutes, then add 40kg of deionized water and stir again for 60 minutes. After stopping the machine, filter the mixed liquid to remove impurities, and then package it to obtain 100kg of component A of the kitchen and bathroom non-brick waterproofing agent.

[0012] Component B: Measure by weight, take 16kg of inorganic medium-strong acid and 84kg of deionized water, put them into a rubber plastic bucket in sequence, use an air pump to fully stir, continue stirring for 30 minutes, and then package to obtain 100kg of component B of the kitchen and bathroom non-brick waterproofing agent.

[0013] The invention discloses a construction and application method of a kitchen, bathroom and tile-breaking-free waterproofing agent.

[0014] Use a trowel or wallpaper knife to remove the loose dirt in the seams of the floor decoration layer, clean up the garbage on the floor, and then block the floor drain.

[0015] Take the same weight of components A and B of the kitchen and bathroom non-smashing brick waterproofing agent, pour component A of the kitchen and bathroom non-smashing brick waterproofing agent into a large bucket, dilute it with 3 times the weight ratio of clean water, and stir it evenly; at the same time, pour component B into another bucket, dilute it with 3 times the weight ratio of clean water, stir it evenly, then pour the diluted solution of component B into the diluted solution of component A and stir it thoroughly.

[0016] Pour the evenly stirred mixture of components A and B onto the floor tiles, and sweep with a broom from low to high to ensure that the liquid penetrates into each gap between the floor tiles. The sweeping time should be continued for about 60 minutes. When the fluidity of the waterproofing agent weakens, release the remaining material from the floor drain. At the same time, rinse the floor drain with clean water immediately, and clean the floor with a clean mop or sponge.

[0017] The invention can be applied to the leakage control of renovated indoor spaces of units and families, bathrooms, toilets, balconies, kitchens and large commercial bathing places, and can achieve waterproofing and leakage control without destroying the ground decoration layer.

Claims

1. A kitchen and bathroom waterproofing agent that does not require brick breaking, characterized by: It is a two-component product prepared by the following ingredients in percentage by weight: Component A: 54% liquid sodium silicate, 5.4% nano-silicon waterproofing agent, 0.6% triethanolamine, 40% deionized water; Component B: 16% inorganic medium-strong acid, 84% deionized water; Components A and B are diluted with 3 times clean water by weight respectively, and the diluted components A and B are mixed together and stirred evenly, and then poured on the floor tiles. Under the action of their own gravity, they penetrate into the mortar layer and the concrete structure layer along the gaps between the tiles, and chemical reactions occur to form water-insoluble crystals, which block the water leakage channels of the capillary pores and capillary cracks. At the same time, the nano-silicon waterproofing agent component in the kitchen and bathroom free brick waterproofing agent can produce secondary hydration reaction with the free calcium and magnesium ions in the mortar layer and the concrete structure layer to form water-insoluble crystals, which complement each other with the crystals that block the capillary pores and capillary cracks. On the premise of not destroying the decorative layer, the mortar layer and the concrete structure layer under the tiles become a dense whole again, thereby achieving a waterproof and leak-proof effect.