Intermediate Heating Station

Abstract

Disclosed herein is a heating station (1) for heating a metal sheet blank (50), and a system including such a heating station (1). In particular, the heating station includes a heating chamber (10), a lower or upper heating element (11) disposed below the metal sheet blank (50) when in a heating position and configured to provide radiant heating toward the metal sheet blank (50), and a lower mask (14) disposed to prevent the radiant heating from reaching at least a first portion of the metal sheet blank (50), the lower mask (14) including a plurality of support projections (14d) protruding from a main surface (14a) of the lower mask (14) toward the metal sheet blank (50) when in the heating position and configured to support the metal sheet blank (50) during heating.

Description

[Technical field]

[0001] The present disclosure relates to an arrangement and method for manufacturing partially press hardened parts, and in particular to an arrangement and method for controlling the heating of a metal blank sheet. [Background technology]

[0002] Press-hardened parts usually exhibit a uniform strength distribution. This uniform strength distribution can lead to problems, especially for safety-related parts with high requirements on crash performance. For example, a B-pillar can absorb more energy during a crash if its lower part has a relatively high flexibility compared to its middle and upper parts, which are usually designed to be high tensile to prevent intrusion into the passenger compartment.

[0003] For example, tailored rolled blanks, tailored welded blanks, tailored tempering, tailored heating, and other techniques are used to generate soft / hard zones in press hardened parts. However, these techniques can only match material properties over a large area. Tailored rolled blanks and tailored welded blanks have several problems, such as expensive dies (needing good contact pressure), process control (due to strict process window). Tailored tempering in dies also has several problems, such as partial distortion after ejecting the part, severe die wear, and high die cost. Tailored heating with existing techniques also has several problems, such as large transition zones, repeatability, processing cost, and limited to large area parts (e.g. 1 / 3 of B-pillar).

[0004] Thus, there is a need for improved solutions that alleviate at least some of the problems discussed above. Summary of the Invention

[0005] It is an object of the present invention to provide an improved solution which alleviates the above-mentioned drawbacks associated with current solutions. It is a further object to provide a heating station for heating a sheet metal blank which allows for a highly controlled and precise heating of the sheet metal blank. It is also an object to provide a method for heating a sheet metal blank which allows for a highly controlled and precise heating of the sheet metal blank.

[0006] The invention is defined by the accompanying independent claims, embodiments of which are set out in the accompanying dependent claims, the following description and the drawings.

[0007] According to a first aspect of the present invention, a heating station for heating a metal sheet blank is provided. The heating station may comprise a heating chamber. The heating station may comprise a lower or upper heating element disposed in the heating chamber below or above the metal sheet blank when in the heating position. The heating element may be configured to provide radiant heating towards the metal sheet blank. The heating station may comprise a lower mask disposed in the heating chamber below the metal sheet blank when in the heating position. The lower mask may be adapted to a shape and size that prevents radiant heating from reaching at least a first portion of the metal sheet blank. The lower mask may be adapted to a shape and size that allows radiant heating to reach and heat at least a second portion of the metal sheet blank. The lower mask may comprise a plurality of support protrusions protruding from a main surface of the lower mask towards the metal sheet blank when in the heating position. The support protrusions of the lower mask may be configured to support the metal sheet blank during heating.

[0008] This heating station allows the production of very localized or large area soft and hard zones in the produced press hardened parts, and also allows the production of body structure parts with new crash path designs.

[0009] Adapted in shape and size may mean that the lower mask has at least one opening or recess, and may also mean that the lower mask has a planar extent that is not able to prevent some heating radiation from reaching at least a part of the metal sheet blank.

[0010] The heating chamber may be a framework that holds the insulating element and the heating element. The heating chamber may also include a first openable hatch, through which the metal sheet blank may be inserted into and removed from the heating chamber. The heating chamber may also include a second openable hatch. The first hatch may be a front hatch located at the front of the heating chamber. The second hatch may be a rear hatch located at the rear of the heating chamber. The lower mask may be removable or insertable through the rear hatch. The lower mask may be removable or insertable through the front hatch.

[0011] The heating elements of the heating station may be electrically powered or fuel fired, for example gas or oil fired. The heating elements may be configured to provide heating radiation. The heating radiation may be infrared radiation.

[0012] The lower mask may have a generally flat profile. The mask may have at least one opening or recess. In the context of a mask, an opening or recess refers to an opening that opens or closes in a transverse direction, extends through the mask, or the like. For example, an opening may be a hole that is completely bounded by the structure of the mask. For example, a recess may be a gap that also extends from the edge of the mask. Any of the masks may be provided with at least 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, or more openings or recesses. The openings or recesses may be designed to provide a desired heating pattern of the heated metal sheet blank.

[0013] In one embodiment, the supporting protrusions may protrude from the main surface of the lower mask by 0.1 to 50 mm, while in another embodiment, the supporting protrusions may protrude from the main surface of the lower mask by 1 to 30 mm, preferably 1 to 20 mm.

[0014] Also, in the heating station, radiant heating from the heating elements may be reflected off surfaces within the heating chamber, i.e., the radiant heating may be reflected towards the metal sheet blank. Thus, in the case of a heating station comprising only an upper heating element, it will be understood that the lower mask blocks the radiant heating from the upper heating element reflected towards the metal sheet blank.

[0015] According to one embodiment, the heating station may comprise a reflective surface arranged and / or configured to reflect radiant heating towards the metal sheet blank. This may facilitate reflection of radiant heating towards the metal sheet blank. The lower mask may be adapted to a shape and size that prevents radiant heating reflected off the reflective surface from reaching at least a first portion of the metal sheet blank. The reflective surface preferably has a high reflectivity, such as for example a mirror or glossy surface. The reflective surface may be made of one or more materials, such as for example Au, Ag, or Cu, and alloys thereof, i.e. Au-Ag alloys, Au-Cu alloys, Ag-Cu alloys. Such materials may be advantageously used to provide a reflective surface in some embodiments of the invention, by allowing a protective surface that can withstand a wide range of operating temperatures in the heating chamber due to a combination of a relatively high reflectivity and a relatively high melting point, generally in the range of 960-1080°C. The reflective surface may be a coating provided on an element configured to be placed under the mask in the heating chamber, or a coating deposited on a bottom surface area of ​​the heating chamber.

[0016] According to one embodiment, the heating station may comprise both a lower heating element arranged below the metal sheet blank and an upper heating element arranged above the metal sheet blank when in the heating position, and the heating station may further comprise an upper mask arranged between the upper heating element and the metal sheet blank in the heating chamber and adapted to a shape and size to prevent radiant heating from reaching at least a third portion of the metal sheet blank when in the heating position and to allow radiant heating to reach and heat at least a fourth portion of the metal sheet blank.

[0017] The upper mask may be arranged to control the radiation reaching the upper side of the metal sheet blank. Adapted shape and size may mean that the upper mask has at least one opening or recess. It may also mean that the upper mask has a planar extent that cannot prevent some heating radiation from reaching at least a part of the metal sheet blank.

[0018] The upper mask may have a generally flat profile. The upper mask may have at least one opening or recess. In the context of a mask, an opening or recess refers to an opening that opens or closes in a transverse direction, extends through the mask, or the like. For example, an opening may be a hole that is completely bounded by the structure of the mask. For example, a recess may be a gap that also extends from the edge of the mask. At least 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, or more openings or recesses may be provided in any of the masks. The openings or recesses may be designed to provide a desired heating pattern of the heated metal sheet blank. The upper and lower masks may be similarly designed with respect to the layout of the openings or recesses such that at least one first portion and at least one third portion of the metal sheet blank are aligned with each other.

[0019] According to one embodiment, the lower mask may be configured to be operatively movable from a first position towards a second position. The first position may be a position where the lower mask is in a position close to the bottom surface of the heating chamber. The first position may be a position where the lower mask is in a position where the metal sheet blank can be easily inserted into the heating chamber. The metal sheet blank can be received and supported by the lower mask. The lower mask may be operatively movable upwards while supporting the metal sheet blank. The second position may correspond to a heating position, i.e. a position where the metal sheet blank supported on the lower mask is in a heating position. By making the lower mask operatively movable, the metal sheet blank can be placed in a heating position where precise heating can be facilitated. Also, the movement of the lower mask may be controlled manually or automatically. Thus, the heating of the metal sheet blank can be even autonomous. The heating station may comprise a lifting device configured to move the lower mask between the first and second positions. The lifting device may be moved by a pneumatic or electric actuator, preferably a servomotor-driven linear unit. The actuator(s) may be configured to control the lower mask via a support structure, which may be accessible via a floor or a side of the heating chamber. In embodiments where the heating station includes an upper mask, movement of the lower mask to the second position may be in a direction toward the upper mask.

[0020] According to one embodiment, the lower mask may comprise at least one opening or recess through which radiative heating may reach and heat said at least second portion of the metal sheet blank. Alternatively, a lower mask may be provided that does not have an opening or recess, the lower mask being limited in planar extent such that it cannot prevent some heating radiation from reaching and heating at least a portion of the metal sheet blank.

[0021] According to an additional embodiment, the upper mask may comprise at least one opening or recess through which radiative heating may reach and heat at least a fourth portion of the metal sheet blank. Alternatively, an upper mask may be provided that does not have an opening or recess, the upper mask being limited in planar extent such that it cannot prevent some heating radiation from reaching and heating at least a portion of the metal sheet blank.

[0022] One of the upper and lower masks may include at least one opening or recess, and the other of the upper and lower masks may be provided without the corresponding at least one opening or recess, such that a portion of the metal sheet blank may be exposed to radiant heating from only one direction, either from above or below.

[0023] The heating chamber may comprise adjustment means for independently adjusting the position of the upper and / or lower mask in the heating chamber in a direction parallel to a horizontal plane, whereby the upper and / or lower masks may be adjusted in position relative to one another to align any openings or recesses in the upper and lower masks, or to position the upper and lower masks to enable targeted radiative heating of a zone from one direction only.

[0024] According to one embodiment, the upper mask may be stationary in a predetermined position, and the lower mask may be movable toward the upper mask and may carry the metal sheet blank in the heating position. Optionally, the upper mask may be configured to be operatively movable relative to the heating chamber of the heating station. In that case, the upper mask may be movable between a first position and a second position. In the first position, the upper mask may be in a locked position locked in a predetermined position by a locking means. In the second position, the upper mask may be supported by the lower mask arranged in the first position. In an additional exemplary embodiment, the upper mask may be configured to be movable toward the lower mask, and the lower mask moves toward the upper mask while supporting the metal sheet blank. The main surface of the upper mask may be the bottom surface of the upper mask, i.e. the surface facing the metal sheet blank. Also, the movement of the upper mask may be controlled by a lifting device similar to that configured to control the movement of the lower mask. The movements of the upper and lower masks may be controlled by the same lifting device. The lifting device may be moved by a pneumatic or electric actuator, preferably a servomotor driven linear unit.

[0025] According to one embodiment, the heating station may comprise a support pin extending through said at least one opening or recess in the lower mask. The support pin may be configured to support the metal sheet blank inserted into the heating station. By providing the support pin, the metal sheet blank may be received by the support pin in such a way that the lower mask is easy to receive the metal sheet blank. In one embodiment, besides extending through at least one opening or recess in the lower mask, one or more support pins may be configured to extend through a support pin opening in the lower mask. Thus, if the at least one opening or recess in the lower mask is not sufficient to support the metal sheet blank when inserted into the heating chamber, a support pin may be in an additional position and extend through a dedicated support pin opening in the lower mask. Such a support pin opening may be strictly configured to have only a width sufficient for the support pin to pass through. This may improve the stability of the metal sheet blank when inserted into the heating chamber. The heating station may include 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, or more support pin(s). The support pin(s) may be positioned to provide stability to the metal sheet blank when inserted into the heating chamber. The heating chamber may also include a support shelf configured to provide stability to the metal sheet blank when inserted into the heating chamber. The support shelf may be positioned inside the heating chamber. The support shelf may have an upper surface at the same vertical height as the tips of the support pins. The support shelf may provide additional stability to the metal sheet blank when inserted into the heating chamber for easier receipt by the lower mask.

[0026] According to yet another embodiment, the heating station may be configured to receive the metal sheet blank such that the metal sheet blank is supported by said support pins when the lower mask is in the first position. The lower mask may be configured to support the metal sheet blank by the support protrusions of the lower mask when moved to the second position. According to this embodiment, the received metal sheet blank may be prepared to be supported by the lower mask more precisely.

[0027] According to yet another embodiment, the upper and lower masks may be made of steel or aluminum. The upper and lower masks may be made of stainless steel. This embodiment may facilitate controlled heating of the masks and therefore the metal sheet blank during heating.

[0028] According to yet another embodiment, the upper mask may comprise spacing protrusions protruding from a major surface of the upper mask towards the sheet metal blank when in the heating position. According to this embodiment, air may pass between the sheet metal blank and the upper mask when in the heating position. The spacing protrusions on the upper mask may be configured to contact the sheet metal blank when in the heating position. The spacing protrusions may protrude from the major surface of the upper mask to an extent equal to that of the support protrusions of the lower mask.

[0029] According to yet another embodiment, the upper and lower masks may be interchangeable from the heating station, whereby the upper and lower masks may be exchanged for different sets having different sizes, shapes, materials and / or layouts regarding the layout of at least one opening or recess in each mask, so that the same heating station may be reconfigured for heating sheet metal blanks intended for processing into different types of press hardened parts.

[0030] According to yet another embodiment, the support pins may be placed on a support structure, which may be more adaptable to manage the weight of the sheet metal blank placed on the support pins.

[0031] According to yet another embodiment, the support structure may be replaceable from the heating station, where the support pins may be positioned with a high degree of freedom and have a layout that corresponds to a particular lower mask, and the lower mask as well as the support structure may be replaced simultaneously or successively with each other.

[0032] According to yet another embodiment, the lower mask may be provided with cooling channels. The cooling channels may be arranged to extend throughout the interior of the mask. The cooling channels may be milled into one plate of material, for example aluminum or stainless steel, with another plate placed on top to seal the channels. Also, hoses supplying and / or draining cooling fluid may be fluidly connected to the mask provided with the cooling channels. According to this embodiment, the mask may be actively cooled, so that its temperature is reduced and / or controlled to an acceptable level during heating of the metal sheet blank. The cooling fluid may be water. In embodiments with an upper mask, the upper mask may also be provided with cooling channels.

[0033] According to a second aspect of the invention, there is provided a mask support arrangement for placement within a heating chamber. The mask support arrangement may comprise a support structure. The support structure may be configured to be placed within the heating chamber. The mask support arrangement may comprise a lower mask. The lower mask may be configured to be movable relative to the support structure between a first position and a second position. The lower mask may be configured to receive a metal sheet blank. The lower mask may be adapted to a shape and size that prevents radiant heating from reaching at least a first portion of the metal sheet blank. The lower mask may be adapted to a shape and size that allows radiant heating to reach and heat at least a second portion of the metal sheet blank. The lower mask of the mask support arrangement may comprise a plurality of support protrusions. The support protrusions may protrude from a main surface of the lower mask towards the metal sheet blank when in the heating position. The support protrusions may be configured to support the metal sheet blank during heating. According to this mask support arrangement, a heating station already in use may be reconfigured into a heating station according to any of the embodiments of the first aspect of the invention.

[0034] According to one embodiment, the mask support arrangement may comprise a lifting device. The lifting device may be configured to control the movement of the lower mask between the first and second positions. The lifting device may be moved by a pneumatic or electric actuator, preferably a servomotor driven linear unit.

[0035] According to one embodiment, the mask support arrangement may comprise an upper mask. The lifting device may be configured to control movement of the upper mask between the first and second positions.

[0036] The mask support arrangement may also be embodied in materials, shapes and functions that correspond to an equivalent arrangement of the heating station according to any of the embodiments described above and benefit from the advantages that these embodiments may provide. An equivalent arrangement may mean an arrangement that comprises all the structural and functional features of the heating station except for the heating chamber and the lower and / or upper heating element. In particular, it may be intended that the mask support arrangement comprises the lower mask and the support frame of the heating station according to any of the embodiments of the first aspect of the invention.

[0037] According to a third aspect of the present invention there is provided a method for heating a metal sheet blank in a heating station, the method comprising the steps of: placing a metal sheet blank in a heating chamber of a heating station; supporting a metal sheet blank on support projections projecting from a major surface of a lower mask disposed within the heating chamber; heating the metal sheet blank using radiative heating from a heating element within a heating chamber; shielding at least a portion of the metal sheet blank from radiant heating with a lower mask disposed within the heating chamber; The method may also include moving the lower mask from the first position towards the upper mask to a second position.

[0038] According to one embodiment, the step of shielding at least a portion of the metal sheet blank from radiant heating may further comprise shielding the metal sheet blank with an upper mask positioned within the heating chamber, and a lower and upper mask may be positioned on each side of the metal sheet blank.

[0039] According to one embodiment, the method may comprise a step of moving the lower mask from a first position towards a second position. The step of cooling may occur continuously during the step of heating. In the first position, the lower mask may be located near the bottom surface of the heating chamber, preferably in a position where the metal sheet blank can be easily inserted into the heating chamber. In the second position, the lower mask may be arranged to support the metal sheet blank inserted into the heating chamber via the support protrusions during heating. The step of moving the lower mask may include moving the metal sheet blank from the insertion position to the heating position. According to yet another embodiment, the lower mask is in the second position during the step of heating the metal sheet blank. This second step may be referred to as the heating position, and the metal sheet blank is supported to be located in the heating position. When moving to the second position, the lower mask may move towards the upper mask.

[0040] According to yet another embodiment, the step of placing the metal sheet blank in the heating chamber may comprise placing the metal sheet blank on at least one support pin arranged in the heating chamber, the metal sheet blank being supported on the at least one support pin when the lower mask is in a first position and being supported on the support protrusion when the lower mask is moved to a second position.

[0041] According to yet another embodiment, the method may comprise the step of cooling either the upper or lower mask. The cooling step may occur continuously throughout the heating step.

[0042] According to yet another embodiment, the method may comprise a step of placing the metal sheet blank in any kind of furnace, for example a multi-layer furnace, a chamber furnace or a roller hearth furnace. The method may comprise a step of heating the metal sheet blank in a heating chamber of the furnace. The metal sheet blank may be heated so that the material of the metal sheet blank reaches the austenitic phase. The method may comprise a step of removing the metal sheet blank from the furnace and transferring it to a heating station according to any of the above embodiments. This may be done, for example, by using a fork-type loader. Alternatively, the furnace may comprise an ejection device that ejects the metal sheet blank, once heated to the austenitizing temperature, into a position where it can be easily picked up, for example, by a fork-type loader. The method may also comprise a processing step in which the metal sheet blank is press hardened. This may be done, for example, by a tool of a processing unit that applies a force to the metal sheet blank. The method may also comprise a step of cooling the metal sheet blank. When the tool closes and reshapes the metal sheet blank, the metal sheet blank may be cooled to a temperature below the martensite level. This cooling may be performed rapidly. This method therefore allows press hardened parts to be produced from metal sheet blanks.

[0043] According to one embodiment, the method may comprise replacing the upper and / or lower mask in the heating station. The method may also comprise replacing the support structure. According to this embodiment, the heating station may be reconfigured to heat the metal sheet blank according to another required heating pattern.

[0044] According to a fourth aspect of the invention, there is provided a system for manufacturing a press hardened part. The system may comprise a furnace configured to heat a material of a metal sheet blank to an austenitic phase. The system may comprise a heating station according to any embodiment of the first aspect of the invention. The system may comprise a processing unit for press hardening the metal sheet blank into a press hardened part. The system may comprise a loading device for transferring the metal sheet blank between the furnace, the heating station and the processing unit. The system may also comprise a mask handling device for exchanging the upper mask, the lower mask and / or the support structure. The system may comprise a cooling fluid reservoir and means for supplying cooling fluid to the upper and lower masks.

[0045] Also, although the first, second, third and fourth aspects have been generally described as relating to the heating of a metal sheet blank, a plurality of metal sheet blanks may be naturally received by the mask support arrangement and / or the heating station and heated by the heating station as well. A plurality of metal sheet blanks may be heated simultaneously. Also, the method may relate to heating and / or processing a plurality of metal sheet blanks, either sequentially or simultaneously. Also, the heating station according to the first aspect of the invention may comprise a mask support arrangement according to the second aspect of the invention. [Brief description of the drawings]

[0046] The present invention will now be described in detail with reference to the accompanying drawings, in which: [Figure 1] 1 shows a perspective view of a heating station according to an embodiment of the present invention. [Figure 2a] FIG. 1 shows a schematic block diagram of an arrangement according to an embodiment of the present invention. [Figure 2b] FIG. 1 shows a schematic block diagram of an arrangement according to an embodiment of the present invention. [Figure 3a] FIG. 1 shows a schematic block diagram of an arrangement according to an embodiment of the present invention. [Figure 3b] FIG. 1 shows a schematic block diagram of an arrangement according to an embodiment of the present invention. [Figure 3c] FIG. 1 shows a schematic block diagram of an arrangement according to an embodiment of the present invention. [Figure 4a] FIG. 1 shows a schematic block diagram of a part of an arrangement according to an embodiment of the present invention. [Figure 4b] FIG. 1 shows a schematic block diagram of a part of an arrangement according to an embodiment of the present invention. [Figure 5a] FIG. 1 shows a schematic block diagram of an arrangement according to an embodiment of the present invention. [Figure 5b] FIG. 1 shows a schematic block diagram of an arrangement according to an embodiment of the present invention. [Figure 5c] FIG. 1 shows a schematic block diagram of an arrangement according to an embodiment of the present invention. [Figure 5d] FIG. 1 shows a schematic block diagram of an arrangement according to an embodiment of the present invention. [Figure 5e] FIG. 1 shows a schematic block diagram of an arrangement according to an embodiment of the present invention. [Figure 5f] FIG. 1 shows a schematic block diagram of an arrangement according to an embodiment of the present invention. [Figure 5g] FIG. 1 shows a schematic block diagram of an arrangement according to an embodiment of the present invention. [Figure 6] 2 shows a flow chart of a method according to an embodiment of the present invention. [Figure 7] 2 shows a flow chart of a method according to an embodiment of the present invention. [Figure 8] 2 shows a flow chart of a method according to an embodiment of the present invention. [Figure 9] 3A-3D show schematic diagrams of the internal structure of a blank during a method process according to an embodiment of the present invention. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0047] The present invention will now be described in detail with reference to the accompanying drawings, in which preferred embodiments of the present invention are shown. However, the present invention can be embodied in many different forms and should not be construed as being limited to the embodiments described herein, but rather these embodiments are provided so that this disclosure will be comprehensive and complete, and will fully convey the scope of the present invention to those skilled in the art. In the drawings, like numbers refer to like elements. Also, in the drawings and this specification, preferred embodiments and examples of the present invention are disclosed, and although specific terms are used, they are used in a generic and descriptive sense only and not for purposes of limitation, and the scope of the present invention is set forth in the following claims.

[0048] FIG. 1 shows a perspective view of a heating station 1 according to an embodiment of the present invention. FIG. 2a shows a schematic block diagram of a heating station 1 according to an embodiment of the present invention. The heating station 1 comprises a heating chamber 10, i.e. a framework holding the insulating element and the heating elements 11, 12. The heating station 1 comprises a lower heating element 11. The heating station 1 comprises an upper heating element 2. The lower heating element 11 is arranged at the bottom of the heating chamber 10. The upper heating element 12 is arranged at the top of the heating chamber 10. For example, with reference to FIGS. 2a-2b, the lower heating element 11 and the upper heating element 12 are arranged at a distance from each other such that a metal sheet blank 50 can be placed between the lower heating element 11 and the upper heating element 12. The upper and lower heating elements 11, 12 may be electrically powered or may be ignited with a fuel, for example gas or oil. In other embodiments, the heating station 1 comprises only one of the lower and upper heating elements 11, 12.

[0049] The heating station 1 comprises a lower mask 14. The lower mask 14 is disposed in the heating chamber 10 above the lower heating element 11 and below the metal sheet blank 50 when the metal sheet blank 50 is inserted into the heating chamber 10. The lower mask 14 is configured to prevent radiant heating from reaching at least a first portion of the metal sheet blank 50. The lower mask 14 also comprises at least one opening or recess 14b, 14c through which radiant heating may reach at least a second portion of the metal sheet blank 50. The lower mask 14 also comprises a plurality of support protrusions 14d (not shown in FIG. 1 ) protruding from a main surface 14a of the lower mask 14. As shown in FIG. 1 , the main surface 14a may be the upper surface of the lower mask 14. The support protrusions 14d protrude upwards toward the metal sheet blank 50 when inserted into the heating chamber 10. The support protrusions 14d are configured to support the metal sheet blank 50 during heating. The heating station 1 also comprises an upper mask 13. In one embodiment, the upper mask 13 is positioned in the heating chamber 10 below the upper heating element 12 and above the metal sheet blank 50 when the metal sheet blank 50 is inserted into the heating chamber 10. The upper mask 13 is configured to prevent radiant heating from reaching at least a third portion of the metal sheet blank 50. The upper mask 13 also comprises at least one opening or recess 13b, 13c through which radiant heating may reach at least a fourth portion of the metal sheet blank 50.

[0050] As described above with reference to Fig. 1, the configuration 1, i.e. the heating station 1, comprises a heating chamber 10, lower and upper heating elements 11, 12, and upper and lower masks 13, 14. The heating station 1 is configured to receive a metal sheet blank 50. The metal sheet blank 50 may be preheated before being received at the heating station 1. For example, the metal sheet blank 50 may be heated in the heating chamber 22 of the furnace 20 to a temperature equal to or greater than the austenitizing temperature of the material of the blank 50, thereby bringing the material of the blank 50 into the austenitic phase. The metal sheet blank 50 may then be transferred from the heating chamber 22 of the furnace 20 to the heating station 1.

[0051] When the metal sheet blank 50 is in a position to be heated by the upper and lower heating elements 11, 12, i.e. in the heating position, in the heating chamber 10 of the heating station 1, the metal sheet blank 50 is supported by the support ridges 14d. The support ridges 14d allow air to circulate between the mask 14 and the metal sheet blank 50. The lower and upper heating elements 11, 12 provide radiant heating. At least one unexposed zone 50a of the metal sheet blank 50 is prevented from receiving heating radiation by the upper and lower masks 13, 14, while some radiant heating can reach at least one exposed zone 50b, 50c of the metal sheet blank 50 (area shown with a cross-hatched pattern in FIG. 2a).

[0052] After at least one exposed zone 50b, 50c has been heated, the metal sheet blank 50 is removed from the heating chamber 10 of the heating station 1. The metal sheet blank 50 can then be transferred from the heating chamber 10 of the heating station 1 to the treatment unit 30. In the treatment unit 30, the metal sheet blank 50 is placed in the tool 31 of the treatment unit 30. Treated by a pressing force F and possibly cooled, the metal sheet blank 50 is formed into a press-hardened part 50'. The press-hardened part 50' is provided with hardening zones 50b', 50c' corresponding to the heating zones 50b, 50c.

[0053] Fig. 2b shows a schematic block diagram of an arrangement 1 according to an embodiment of the invention. The arrangement 1, i.e. the heating station 1, comprises lower and upper heating elements 11, 12 and upper and lower masks 13, 14 as described with reference to Fig. 1. The heating station 1 is configured to receive a metal sheet blank 50 between the lower and upper heating elements 11, 12, in particular between the upper and lower masks 13, 14, as shown in dashed outline in Fig. 2b. The lower mask 14 comprises at least one opening or recess 14b, 14c. The upper mask 13 also comprises at least one opening or recess 13b, 13c. Radiant heating can reach the metal sheet blank 50 inserted in the heating chamber 10 through the openings or recesses 13b, 13c, 14b, 14c of the upper and lower masks, respectively. The lower mask 14 is provided with a support protrusion 14d protruding from the main surface 14a of the lower mask 14. As shown in Figure 2b, the major surface 14a of the lower mask may be its upper surface. The support protrusions 14d are configured to support the metal sheet blank 50 during heating. The support protrusions 14d allow air to pass between the lower mask 14 and the metal sheet blank 50 during heating.

[0054] The lower mask 14 is also configured to be movable relative to the heating chamber 10 of the heating station 1, as shown in Figures 3a-3c. The lower mask 14 is configured to be movable from a first position and a second position, and in the first position, the lower mask 14 is located near the bottom surface of the heating chamber 10, preferably in an insertion position where the metal sheet blank 50 can be easily inserted into the heating chamber 10 on the support arrangement 15, as shown in Figures 2b and 3a. The lower mask 14 is configured to move towards the upper mask 13, as shown in Figure 3b, such that the support protrusions 14d support the metal sheet blank 50. In the second position, i.e. the heating position, the lower mask 14 is configured to support the metal sheet blank 50 inserted into the heating chamber 10 during heating, as shown in Figure 3c.

[0055] In one exemplary embodiment, the upper mask is stationary in a predetermined position, and the lower mask 14 moves towards the upper mask 13, carrying the metal sheet blank 50 in the heating position. Optionally, the upper mask 13 is also configured to be movable relative to the heating chamber 10 of the heating station 1. In that case, the upper mask 13 may be movable between a first position and a second position. In the first position, the upper mask 13 may be in a locking position locked in a predetermined position by a locking means 13x. In the second position, the upper mask 13 may be supported by the lower mask 14 in the first position. In a further exemplary embodiment, the upper mask 13 is configured to be movable towards the lower mask 14, and the lower mask 14 moves towards the upper mask 13 while supporting the metal sheet blank 50. Optionally, the upper mask 13 comprises a spacing protrusion 13d protruding from a main surface of the upper mask 13. The major surface of the upper mask 13 may be the bottom surface of the upper mask 13. The spacing projections 13d and the support projections 14d may hold the metal sheet blank 50 in place during heating. The upper and lower masks 13, 14 may be provided in aluminum or stainless steel. The upper and lower masks 13, 14 may also be provided with cooling channels for cooling the upper and lower masks 13, 14. Cooling may be achieved by flowing a fluid throughout the cooling channels to remove heat from the upper and lower masks 13, 14. The cooling channels may extend generally in various directions within the upper and lower masks 13, 14. The cooling fluid may be water.

[0056] As shown in Figs. 1, 2b, 3a-3c, 4a-4b, the heating station 1 may include support pins 15x extending through at least one opening or recess 14b, 14c of the lower mask 14. The lower mask 14 may be provided with support pin openings 14e through which the support pins 15x may pass. The upper mask 13 may also be provided with support pin openings 13e through which the support pins 15x may pass. The support pin openings 13e, 14e may be sized and shaped to closely receive the support pins 15x and allow them to move in and out of the support pin openings 13e, 14e. The support pins 15x are configured to support the metal sheet blank 50 when placed in the heating chamber 10 of the heating station 1. The support pins 15x may also be configured to support the metal sheet blank 50 so that the lower mask 14 can easily receive the metal sheet blank 50 as it moves toward the upper mask 13 and support it during heating.

[0057] FIG. 4a shows a schematic diagram of a part 14 of configuration 1 according to an embodiment of the present invention. The part 14, i.e. the lower mask 14, is shown in a typical shape as seen above. The lower mask 14 is provided with a main surface 14a, which is the upper surface of the lower mask 14. The lower mask 14 may also comprise at least one opening or recess 14b, through which heating radiation may reach the metal sheet blank 50 inserted in the heating chamber 10. The lower mask 14 may be provided with support pin openings 14e through which the support pins 15x may pass. The support pin openings 14e may be formed to a size and shape to closely receive the support pins 15x and allow them to move in and out of the support pin openings 14e. In one typical embodiment, the support pin openings 14e are circular openings. The support pins 15x may also be provided on a support structure 15 (shown in dashed lines). The support structure 15 may comprise the support pins 15x.

[0058] Fig. 4b shows a part 13 of configuration 1 according to an embodiment of the present invention. The part 13, i.e. the upper mask 13, is shown in a typical shape as can be seen below. The upper mask 13 is provided with a main surface 13a, which is the bottom surface of the upper mask 13. The upper mask 13 also comprises at least one opening or recess 13b, 13c, through which heating radiation may reach the metal sheet blank 50 inserted in the heating chamber 10. The upper mask 13 may also comprise a spacing projection 13d arranged along its main surface for abutting the metal sheet blank 50 (not shown) during heating. Similarly, the upper mask 13 may also be provided with a support pin opening 13e through which a support pin 15x may pass.

[0059] Also, the upper and lower masks 13, 14 may be interchangeable from the heating station 1. The heating station 1 may thus consist of a set of upper and lower masks 13, 14 selected from a collection of sets of upper and lower masks 13, 14 differing in material, size and / or shape and in terms of openings or recesses 13b, 13c, 14b, 14c allowing heating radiation to reach the metal sheet blank during heating. The support structure 15 may likewise be interchangeable.

[0060] Figures 5a-5g show a block diagram of arrangement 1 according to one embodiment of the present invention. Arrangement 1, i.e. heating station 1, is shown in a side view. Figures 5a-5g also show how the set of upper and lower masks 13, 14 is exchanged for a new set of upper and lower masks 13', 14'. A new set of upper and lower masks 13', 14' is usually required when a new type of press hardened part 50' is produced.

[0061] FIG. 5a shows the heating station 1 when the lower mask 14 is in a first position and the upper mask 13 is in a locked position. The upper mask 13 is locked in place by the locking means 13x. The lower mask 14 moves upwards towards the upper mask 13 so as to contact the upper mask 13, as shown in FIG. 5b. The upper mask 13 is then released from the locking means 13x, as shown in FIG. 5c. At this time, the upper mask 13 is supported by the lower mask 14. As shown in FIG. 5d, the lower mask 14 moves downwards, carrying the upper mask 13 to the released position. The support pins 15x are configured in one embodiment to protrude through the support pin openings 14e, 13e of both the lower mask 14 and the upper mask 13. The upper mask 13, the lower mask 14, and the support structure 15 can all be removed from the heating chamber 10 of the heating station 1, as shown in FIG. 5e. The interior of the heating chamber 10 can be accessed by a hatch. The hatch may be opened so that the upper mask 13, the lower mask 14, and the support structure 15 may be removed. The hatch may then be closed to retain heat within the heating chamber 10. The upper mask 13, the lower mask 14, and the support structure 15 may be removed using a mask handling device (not shown). The mask handling device may be configured to remove the upper mask 13, the lower mask 14, and the support structure 15 from the heating chamber 10. The mask handling device may be configured to remove the upper mask 13, the lower mask 14, and the support structure 15 and place them in a storage unit. The mask handling device may also be configured to optionally remove a new set of upper mask 13', lower mask 14', and support structure 15' from the storage unit as shown in FIG. 5f. A new set of upper mask 13', lower mask 14' and support structure 15' is placed in the heating chamber 10 of the heating station 1, and the lower mask 14' moves upwards carrying the upper mask 13'. The upper mask 13' is fixed in place using the locking means 13x. The lower mask 14' then moves again to the first position. The locking means 13x holding the upper masks 13, 13' may be configured to automatically release the upper mask 13 when it is pushed up by the lower mask.The locking means 13x may further be configured to automatically re-secure the upper mask 13' when the upper mask 13' comes into contact with the locking means 13x.

[0062] 5a-5g further illustrate a mask support arrangement 40. The mask support arrangement 40 comprises a support structure 15 and a lower mask 14 configured to be arranged so as to be movable relative to the support structure 15 between a first position and a second position. The mask support arrangement 40 may also comprise an upper mask 13. The mask support arrangement 40 may be interchangeable with a mask support arrangement 40' having a different set of upper and lower masks 13', 14'.

[0063] Fig. 6 shows a flow chart of a method 100 according to an embodiment of the present invention. The method 100 of heating a metal sheet blank 50 in a heating station 1 according to any embodiment of the first aspect of the present invention comprises a step 101 of placing the metal sheet blank 50 in a heating chamber 10 of the heating station 1. The method 100 comprises a step 102 of supporting the metal sheet blank 50 on a support protrusion 14d protruding from a main surface 14a of a lower mask 14 arranged in the heating chamber 10. The method 100 comprises a step 104 of heating the metal sheet blank 50 using radiant heating from heating elements 11, 12 in the heating chamber 10. The method 100 comprises a step 105 of shielding at least a part of the metal sheet blank 50 from radiant heating using a lower mask 14 and an upper mask 13 arranged in the heating chamber 10, the lower and upper masks 14, 13 being arranged on either side of the metal sheet blank 50, respectively. The method 100 may also include a step 103 of moving the lower mask 14 from a first position towards the upper mask 13 to a second position. In the first position, the lower mask 14 may be near the bottom surface of the heating chamber 10, preferably in a position where the metal sheet blank 50 can be easily inserted into the heating chamber 10. In the second position, the lower mask 14 may be arranged to support the metal sheet blank 50 inserted into the heating chamber via the support protrusions 14d during heating. The step 103 of moving the lower mask 14 may include moving the metal sheet blank 50 from the insertion position to the heating position. The method 100 may also include a step 106 of cooling the upper and / or lower masks 13, 14. The step 106 of cooling the upper and / or lower masks 13, 14 may occur before step 101, after step 105, or anywhere in between. The step 106 of cooling may occur continuously throughout the step 104 of heating.

[0064] FIG. 7 shows a flow chart of a method 100' according to an embodiment of the present invention. The method 100' may comprise a step 107 of placing the metal sheet blank in any type of furnace 20, for example a multi-layer furnace, a chamber furnace or a roller hearth furnace. The method 100' may comprise a step 108 of heating the metal sheet blank 50 in the heating chamber 22 of the furnace 20. The metal sheet blank 50 may be heated so that the material of the metal sheet blank 50 reaches the austenitic phase. Also, if the metal sheet blank 50 is coated with a coating material, the chemical transformation of the coating may be started during the heating step 108 and may not necessarily be completed. The method 100' may comprise a step 109 of removing the metal sheet blank 50 from the furnace 20. This may be done, for example, using a fork-type loading device. Alternatively, the furnace 20 may comprise an ejector that ejects the metal sheet blank 50, once heated to the austenitizing temperature, into a position where it can be easily picked up, for example into a fork-type loading device. The austenitized metal sheet blank 50 is then transferred to the heating station 1. The method 100' may comprise steps 101, 102, 103, 104, 105, 106 of the method 100. When the metal sheet blank 50 is transferred into the heating station 1, the heating chamber door opens and the fork loader moves horizontally into the heating station 1 and then lowers the metal sheet blank 50 onto the support pins 15x of the heating station 1. The fork loader is then withdrawn from the heating station 1 and the door is closed with the metal sheet blank 50 remaining in the heating chamber 10. At this time, the lower mask 14 moves upwards towards the metal sheet blank 50 (103). The lower mask 14 interacts with the metal sheet blank 50 and lifts the metal sheet blank 50 off the support pins 15x. At this time, the lower mask 14 carries the sheet metal blank 50 via the support protrusions 14d that are configured so that the lower mask 14 receives the sheet metal blank 50 at a predetermined position, which may be, for example, horizontal. The lower mask 14 and the sheet metal blank 50 together continue their upward movement towards the upper mask 13.When the lower mask 14 reaches a position adjacent to the upper mask 13 while keeping the metal sheet blank in place between them, the heating step 104 is started. The area(s) of the metal sheet blank 50 exposed to radiant heating from the lower heating element 11 and the upper heating element 12 may be heated so that the temperature(s) of the area(s) are kept at the austenite level. The area(s) covered by the mask may then start to cool slowly. The heating step 104 may be completed when the covered area(s) have cooled to a temperature between the austenite and martensite levels. The lower mask 14 may then start moving from the second position to the first position, carrying the metal sheet blank 50 downward. The metal sheet blank 50 is received by the support pins 15x and the lower mask 14 moves completely to the first position where the metal sheet blank 50 can be easily removed from the heating chamber 10. The door of the heating chamber 10 may be opened and then a fork loader may remove the metal sheet blank 50 from the heating station 1. The method 100' may further comprise a step 110 of placing the metal sheet blank in the processing unit 30. This may for example also be performed by a fork loader. The method 100' may also comprise a processing step 111 in which the metal sheet blank is press hardened. This may for example be performed by a tool 31 of the processing unit 30 applying a force F to the metal sheet blank. The method 100' may also comprise a step 112 of cooling the metal sheet blank 50. When the tool 31 closes, thereby reshaping the metal sheet blank 50, the metal sheet blank 50 may be cooled to a temperature below the martensite level. This cooling 112 may be performed rapidly. Thus, a press hardened part 50' may be produced from the metal sheet blank 50 by the method 100'.

[0065] FIG. 8 shows a flow chart of a method according to one embodiment of the present invention. Method 100″ relates to a procedure for exchanging a mask set. Any step of method 100″ may be incorporated into either method 100 or method 100′. Method 100″ may comprise a step of turning off the heating power of heating station 1. Method 100″ may comprise a step of preparing a mask handling unit outside heating station 1. Method 100″ may comprise a step 113 of moving lower mask 14 towards upper mask 13 so as to contact upper mask 13. Method 100″ may comprise a step 114 of releasing upper mask 13 from a fixed point. Method 100″ may comprise a step 115 of supporting upper mask 13 with lower mask 14. Method 100″ may comprise a step 116 of moving lower mask 14 supporting upper mask 13 to a release position. The release position may be a first position of lower mask 14. The method 100" may comprise a step of removing a cooling water hose connected directly or indirectly to either the upper or lower mask 13, 14, or both. The method 100" may comprise a step of opening the heating chamber 10. The method 100" may comprise a step 117 of removing the lower mask 14 supporting the upper mask 13 from the heating chamber 10. The method 100" may comprise a step of closing the heating chamber 10 after the lower mask 14 supporting the upper mask 13 has been removed from the heating chamber 10. This may result in the preservation of heat within the heating chamber 10. The method 100" may comprise a step of storing the removed set of upper and lower masks 13, 14. The method 100" may comprise a step of opening the heating chamber 10. The method 100" may include a step 118 of inserting a new set of upper and lower masks 13', 14' into the heating chamber 10 at the insertion position. The support structure 15 may also be removed along with the old set of upper and lower masks 13, 14. A support structure 15' that matches the new set of upper and lower masks 13', 14' may be inserted along with the upper and lower masks 13', 14'. The upper and lower masks 13', 14' may be inserted such that the upper mask 13' is supported by the lower mask 14'.The method 100" may comprise a step of closing the heating chamber 10 once a new set of upper and lower masks 13', 14' and optionally a support structure 15 have been inserted into the heating chamber 10. The method 100" may comprise a step 118 of moving the lower mask 14' supporting the upper mask 13' upwards from an insertion position. The method 100" may comprise a step 119 of locking the upper mask 13' to a fixed point. The method 100" may comprise a step 120 of moving the lower mask 13' to a first position, i.e. the receiving position. By performing the method 100", the heating station may be advantageously reconfigured for producing a different press hardened part 50'.

[0066] FIG. 9 shows a schematic diagram of the internal structure of the metal sheet blank during the method process according to an embodiment of the present invention. In the figure, the temperature of at least one exposed zone 50b, 50c of the blank 50, which is outside the at least one unexposed zone 50a, and the temperature of at least one unexposed zone 50a of the blank 50 are shown. In a first stage 108, the entire metal sheet blank 50 is heated to the austenitic phase in the furnace 20. Thereby, the metal sheet blank 50 is heated to a temperature equal to or higher than the austenitizing temperature of the blank, and optionally the metal sheet blank 50 is maintained at this temperature for a certain time. In a second stage 104, the metal sheet blank 50 is moved to the heating station 1, where the at least one exposed zone 50b, 50c is maintained at a temperature at which it is kept in the austenitic phase. Such a temperature may be equal to or lower than the austenitizing temperature or higher than the austenitizing temperature. The temperature of the at least one unexposed zone 50a is reduced to reach the ferrite, pearlite and bainite phases. In a third stage 111, the metal sheet blank 50 is formed and cooled in the processing unit 30. At least one exposed zone 50b, 50c, when rapidly cooled from the austenite phase, reaches the martensite phase. At least one non-exposed zone 50a, when cooled, remains in the pearlite phase reached during pre-cooling. However, at least one exposed zone 50b, 50c may have a mixture of ferrite, pearlite, bainite and / or austenite before cooling. Depending on the phase composition in the at least one exposed zone 50b, 50c before cooling, the internal structure and material strength will be different.

[0067] In the specification and drawings, preferred embodiments and examples of the invention have been disclosed and specific terms have been used, but they are used in a generic and descriptive sense and not for purposes of limitation, and the scope of the invention is set forth in the following claims. The invention as originally claimed in the present application is set forth below. [1] A heating station (1) for heating a metal sheet blank (50), comprising: A heating chamber (10); a lower or upper heating element (11, 12) disposed below or above a metal sheet blank (50) in the heating chamber (10) when in a heating position and configured to provide radiant heating towards the metal sheet blank (50); a lower mask (14) disposed within the heating chamber (10) below the metal sheet blank (50) and adapted in shape and size to prevent the radiant heating from reaching at least a first portion of the metal sheet blank (50) when in the heating position and to allow the radiant heating to reach at least a second portion of the metal sheet blank (50) to heat the at least second portion; Equipped with a heating station, the lower mask (14) including a plurality of support projections (14d) that, when in a heating position, protrude from a major surface (14a) of the lower mask (14) toward the metal sheet blank (50) and are configured to support the metal sheet blank (50) during heating. [2] The heating station according to [1], wherein when in the heating position, the heating station comprises both a lower heating element (11) arranged below the metal sheet blank (50) and an upper heating element (12) arranged above the metal sheet blank, the heating station further comprising an upper mask arranged in the heating chamber (10) between the upper heating element (12) and the metal sheet blank (50) and adapted in shape and size to prevent radiant heating from reaching at least a third portion of the metal sheet blank when in the heating position and to allow radiant heating to reach at least a fourth portion of the metal sheet blank to heat the at least fourth portion. [3] The heating station of [1] or [2], wherein the lower mask (14) is configured to be operatively movable from a first position towards a second position, and the lower mask is configured to be in the second position when the metal sheet blank is heated. [4] The heating station described in any of [1] to [3], wherein the lower mask has at least one opening or recess (14b, 14c) through which radiant heating can reach at least a second portion of the metal sheet blank (50) and heat the at least second portion. [5] The heating station according to [4], further comprising support pins (15x) extending through the at least one opening or recess (14b, 14c) in the lower mask (14) and configured to support a metal sheet blank (50) inserted within the heating station (1). [6] The heating station described in [5], wherein the heating station is configured to receive a metal sheet blank (50) such that the metal sheet blank (50) is supported by the support pins (15x) when the lower mask (14) is in the first position, and the heating station is configured to support the metal sheet blank (50) by the support protrusions (14d) when the lower mask (14) is moved to the second position. [7] The heating station according to any one of [1] to [6], wherein the upper and lower masks (13, 14) are made of steel or aluminum. [8] The heating station of [2], wherein the upper mask (13) is provided with spacing projections (13d) protruding from a main surface (13a) of the upper mask (13) towards the metal sheet blank when in the heating position. [9] The heating station according to any one of [1] to [8], wherein the upper and lower masks (13, 14) are replaceable from the heating station (1).

[10] The heating station according to [5], wherein the support pins (15x) are arranged on a support structure (15), the support structure (15) being replaceable from the heating station (1).

[11] The heating station according to any one of [1] to

[10] , wherein one of the upper and lower masks (13, 14) is provided with a cooling channel.

[12] A mask support arrangement (40) for placement within the heating chamber (10), comprising: a support structure (15) configured to be disposed within the heating chamber (10); a lower mask (14) configured to be movably arranged relative to the support structure (15) between a first position and a second position and configured to receive a metal sheet blank (50), the lower mask adapted to a shape and size that prevents radiant heating from reaching at least a first portion of the metal sheet blank (50) and allows radiant heating to reach at least a second portion of the metal sheet blank (50) to heat said at least second portion; Equipped with A mask support arrangement, wherein the lower mask (14) of the mask support arrangement (40) has a plurality of support projections (14d) that protrude from a major surface (14a) of the lower mask (14) toward the metal sheet blank (50) when in a heating position and are configured to support the metal sheet blank (50) during heating.

[13] A method (100) for heating a metal sheet blank (50) in a heating station (1) according to any one of [1] to

[11] , comprising: placing (101) the metal sheet blank (50) in a heating chamber (10) of the heating station (1); supporting (102) the metal sheet blank (50) on a support projection (14d) protruding from a major surface (14a) of a lower mask (14) disposed within the heating chamber (10); heating (104) the metal sheet blank (50) using radiant heating from heating elements (11, 12) within the heating chamber (10); shielding (105) at least a portion of the metal sheet blank (50) from the radiant heating with the lower mask (14) disposed within the heating chamber (10); A method for providing the above.

[14] The method according to claim 13, wherein the step (105) of shielding at least a portion of the metal sheet blank (50) from the radiant heating further comprises shielding the metal sheet blank with an upper mask (13) disposed within the heating chamber (10), the lower and upper masks (14, 13) being disposed on either side of the metal sheet blank (50).

[15] The method according to any one of claims 13 to 14, further comprising the step (103) of moving the lower mask (14) from a first position towards a second position, the lower mask (14) being in the second position during a step (104) of heating the metal sheet blank (50).

[16] 15. The method according to claim 14, wherein the step (101) of placing the metal sheet blank (50) in the heating chamber (10) comprises placing the metal sheet blank (50) on support pins (15x) arranged in the heating chamber (10), and the metal sheet blank is supported on the support pins (15x) when the lower mask (14) is in the first position and is supported on the support protrusions (14d) when the lower mask (50) is moved (103) to the second position.

[17] The method according to any of

[13] to

[16] , further comprising a step (106) of cooling either the upper or lower mask (13, 14).

Claims

1. A heating station (1) for heating a metal sheet blank (50), comprising: A heating chamber (10); a lower or upper heating element (11, 12) arranged below or above a metal sheet blank (50) in the heating chamber (10) when in a heating position and configured to provide radiant heating towards the metal sheet blank (50); a lower mask (14) disposed within the heating chamber (10) below the metal sheet blank (50) and adapted in shape and size to prevent the radiant heating from reaching at least a first portion of the metal sheet blank (50) when in the heating position and to allow the radiant heating to reach at least a second portion of the metal sheet blank (50) to heat the at least second portion; Equipped with a heating station, the lower mask (14) having a plurality of support protrusions (14d) that, when in a heating position, protrude from a main surface (14a) of the lower mask (14) toward the metal sheet blank (50) and are configured to support a bottom side of the metal sheet blank (50) during heating of the metal sheet blank (50).

2. 2. The heating station of claim 1, wherein the heating station comprises both a lower heating element (11) arranged below the metal sheet blank (50) and an upper heating element (12) arranged above the metal sheet blank when in the heating position, the heating station further comprising an upper mask arranged in the heating chamber (10) between the upper heating element (12) and the metal sheet blank (50) and adapted in shape and size to prevent radiant heating from reaching at least a third portion of the metal sheet blank when in the heating position and to allow radiant heating to reach at least a fourth portion of the metal sheet blank to heat said at least fourth portion.

3. 3. The heating station of claim 1 or 2, wherein the lower mask (14) is configured to be operatively movable from a first position towards a second position, the lower mask being configured to be in the second position when the metal sheet blank is heated.

4. A heating station according to any one of claims 1 to 3, wherein the lower mask comprises at least one opening or recess (14b, 14c) through which radiant heating can reach at least a second portion of the metal sheet blank (50) and heat said at least a second portion.

5. 5. The heating station of claim 4, further comprising support pins (15x) extending through the at least one opening or recess (14b, 14c) in the lower mask (14) and configured to support a metal sheet blank (50) inserted into the heating station (1).

6. A heating station as described in claim 5, which relies on claim 4, which relies on claim 3, wherein the heating station is configured to receive a metal sheet blank (50) such that the metal sheet blank (50) is supported by the support pins (15x) when the lower mask (14) is in the first position, and the heating station is configured to support the metal sheet blank (50) by the support protrusions (14d) when the lower mask (14) is moved to the second position.

7. A heating station according to any one of the preceding claims, wherein the lower mask (14) is made of steel or aluminium.

8. 3. A heating station as claimed in claim 2, wherein the upper mask (13) is provided with spacing projections (13d) projecting from a main surface (13a) of the upper mask (13) towards the metal sheet blank when in the heating position.

9. The heating station according to any one of the preceding claims, wherein the lower mask (14) is replaceable from the heating station (1).

10. 6. The heating station according to claim 5, wherein the support pins (15x) are arranged on a support structure (15), the support structure (15) being replaceable from the heating station (1).

11. A heating station according to any of the preceding claims, wherein the lower mask (14) is provided with cooling channels.

12. A mask support arrangement (40) for placement within a heating chamber (10), comprising: a support structure (15) configured to be disposed within the heating chamber (10); a lower mask (14) configured to be arranged to be movable relative to said support structure (15) between a first position and a second position and configured to receive a metal sheet blank (50); Equipped with the support structure (15) is configured to support the sheet metal blank (50) when the lower mask (14) is in the first position, and the lower mask is configured to support the sheet metal blank (50) when the lower mask is in the second position; said lower mask is adapted to a shape and size to prevent radiant heating from reaching at least a first portion of said metal sheet blank (50) and to allow radiant heating to reach at least a second portion of said metal sheet blank (50) to heat said at least second portion; A mask support arrangement, wherein the lower mask (14) of the mask support arrangement (40) has a plurality of support protrusions (14d) that protrude from a main surface (14a) of the lower mask (14) toward the metal sheet blank (50) when in a heating position and are configured to support a bottom side of the metal sheet blank (50) during heating of the metal sheet blank (50).

13. A method (100) for heating a metal sheet blank (50) in a heating station (1) according to any one of the preceding claims, comprising: placing (101) said metal sheet blank (50) in a heating chamber (10) of said heating station (1); supporting (102) a bottom side of the metal sheet blank (50) on a support projection (14d) protruding from a main surface (14a) of a lower mask (14) disposed in the heating chamber (10); heating (104) the metal sheet blank (50) using radiant heating from heating elements (11, 12) in the heating chamber (10); shielding (105) at least a portion of the metal sheet blank (50) from the radiant heating with the lower mask (14) disposed within the heating chamber (10); A method for providing the above.

14. 14. The method of claim 13, wherein the step (105) of shielding at least a portion of the metal sheet blank (50) from the radiant heating further comprises shielding the metal sheet blank with an upper mask (13) disposed within the heating chamber (10), the lower and upper masks (14, 13) being disposed on either side of the metal sheet blank (50).

15. 15. The method according to claim 13 or 14, further comprising the step (103) of moving the lower mask (14) from a first position towards a second position, the lower mask (14) being in the second position during the step (104) of heating the metal sheet blank (50).

16. 16. The method according to claim 15, wherein the step (101) of placing the sheet metal blank (50) in the heating chamber (10) comprises placing the sheet metal blank (50) on support pins (15x) arranged in the heating chamber (10), the sheet metal blank being supported on the support pins (15x) when the lower mask (14) is in the first position and supported on the support protrusions (14d) when the lower mask (50) is moved (103) to the second position.

17. The method according to any of claims 13 to 16, further comprising the step of cooling (106) the lower mask (14).