Soft light brick with super anti-fouling coating and preparation method of soft light brick
The substrate is prepared by wet ball milling method, sandblasting and spraying hardener and composite antifouling agent, which solves the problems of poor stain resistance, hardness, wear resistance and weather resistance of soft light bricks, and achieves higher hardness, weather resistance and stain resistance.
CN120208640AActive Publication Date: 2025-06-27GUANGDONG DEER NEW MATERIALS CO LTD +1
5 Cites 1 Cited by
Patent Information
- Application Number
- CN202510685224.9
- Authority / Receiving Office
- CN · China
- Patent Type
- Applications(China)
- Current Assignee / Owner
- Filing Date
- 2025-05-27
- Publication Date
- 2025-06-27
- Estimated Expiration
- 2045-05-27
AI Technical Summary
Technical Problem
The poor stain resistance, hardness, wear resistance and weather resistance of soft light tiles lead to easy to be affected by stains in daily use, reducing aesthetics and shortening service life.
Method used
Wet ball milling method is used to mix kaolin, quartz sand, feldspar, clay and dispersant, and after pressing, microwave drying and sintering, a substrate is formed, and then sandblasting is carried out and hardener and composite antifouling agent is sprayed to form soft light tiles with super antifouling coating.
Benefits of technology
It significantly improves the hardness, weather resistance, stain resistance, wear resistance and self-repair performance of soft light tiles, extends the service life and improves the aesthetics.
✦ Generated by Eureka AI based on patent content.
Abstract
The invention discloses a soft light brick with a super anti-fouling coating and a preparation method of the soft light brick, and belongs to the technical field of soft light brick preparation. The preparation method of the soft light brick with the super anti-fouling coating comprises the following steps: step 1, mixing kaolin, quartz sand, feldspar, clay and a dispersing agent, carrying out wet ball milling, and standing after ball milling to obtain a mixture; 2, the mixture is pressed, subjected to microwave drying and sintered, and a matrix is obtained; and step 3, carrying out sand blasting treatment on the matrix, then spraying a hardening agent, then spraying a composite anti-fouling agent, curing and polishing to obtain the soft light brick with the super anti-fouling coating. The soft light brick prepared by the method has excellent stain resistance, hardness, wear resistance and weather resistance.