A high-strength sound-proof glass fiber felt floor and preparation method thereof

Abstract

The present invention relates to a high-strength and silent glass fiber felt floor applied in the field of flooring and a preparation method thereof. When the glass fiber felt is pre-treated by slurry and gluing, the gluing treatment can be performed on both sides of the glass fiber felt synchronously. With the setting of a continuous roller unit, after gluing, the paste-like adhesive coated on the surface can be smoothed and monitored at the same time, so as to timely find excessive local adhesive. At the same time, under the setting of an eccentric roller, eccentric rolling can be performed at a fixed point where excessive local adhesive is detected, so as to achieve the effect of spontaneously adjusting the uniformity of adhesive distribution, thereby greatly improving the uniformity of adhesive distribution on the glass fiber felt, so that during hot pressing and gluing, the connection stability between the glass fiber felt layer and the floor is higher, and hollowing and degumming are not easy to occur, so that the strength, stability and silent effect of the floor are effectively maintained.

Description

Technical Field

[0001] The invention relates to a glass fiber felt floor and a preparation method thereof, and in particular to a high-strength and sound-proof glass fiber felt floor applied in the field of flooring and a preparation method thereof. Background Art

[0002] Traditional PVC flooring faces two major problems in use. One is that the soundproofing effect is not good; the other is that the thermal expansion and contraction are more obvious when facing a large temperature difference.

[0003] In order to solve the above two problems, mesh fiberglass felt is generally added to the floor structure. The fiberglass felt is mainly composed of glass fiber, and its thermal shrinkage rate is very low, which can significantly improve the phenomenon of thermal expansion and contraction and increase the soundproofing effect.

[0004] However, the stability of the combination of glass fiber felt and floor structure is a difficult point. Generally, the surface of glass fiber felt needs to be treated with slurry, that is, a paste-like adhesive is coated on its surface so that during subsequent hot pressing, the adhesive will melt and bond with the floor structure. However, when applying the paste-like adhesive, excessive and uneven coating may occur in some areas. In this case, hot pressing may easily lead to hollowing in the connection between the glass fiber felt and the floor structure, which may lead to degumming and stratification during subsequent use, which will have a great impact on the stability, strength and sound-quieting effect of the floor. Summary of the invention

[0005] In view of the above-mentioned prior art, the technical problem to be solved by the present invention is that hollowing and degumming are prone to occur when glass fiber felt material is glued and hot-pressed to the floor, which affects the stability and sound-proofing effect of the floor.

[0006] In order to solve the above problems, the present invention provides a high-strength and sound-proof glass fiber felt floor, which comprises, from top to bottom, a wear-resistant layer, a printing layer, a glass fiber middle layer, a bottom layer and a sound-proof layer, and the layers are connected by hot pressing and gluing. The glass fiber middle layer comprises two middle layers and a glass fiber felt layer located between the two middle layers, and the middle layer and the glass fiber felt layer are also connected by hot pressing and gluing.

[0007] The preparation method of the high-strength sound-proof glass fiber felt floor comprises the following steps:

[0008] S1, mixing the middle layer raw materials in a mixer, putting them into an internal mixer for internal mixing after mixing, and rolling them into a sheet-like semi-finished product to obtain the middle layer, wherein the preparation process of the bottom layer is consistent with that of the middle layer, and the above process is repeated to prepare the bottom layer;

[0009] S2, pre-treating the glass fiber felt by slurry infusion, and after the pre-treatment, cutting the glass fiber felt layer according to the product size to obtain a glass fiber felt layer;

[0010] The specific operation of sizing and gluing pretreatment of glass fiber felt is as follows:

[0011] S21, firstly unwinding the glass fiber felt, and then winding it up through a winding roller, setting a direction-changing roller between the winding and unwinding, and setting a drying device near the direction-changing roller and the winding roller;

[0012] S22, the glass fiber mat between the unwinding roller and the direction-changing roller, and between the direction-changing roller and the winding roller are respectively subjected to a gluing treatment by a continuous roller unit. After the glass fiber mat is firstly glued, it is dried by a drying device and then reaches the direction-changing roller. Then, it is glued for the second time, dried again, and then wound up, so as to achieve simultaneous gluing of both sides of the glass fiber mat.

[0013] S3, firstly sandwich the glass fiber felt layer between the two middle layers and perform hot pressing bonding treatment to obtain the glass fiber middle layer, and then sequentially lay the mute layer, the bottom layer, the glass fiber middle layer, the printing layer, and the wear-resistant layer from bottom to top, and then perform hot pressing treatment to bond the layers together;

[0014] S4. Post-processing: The semi-finished products after forming are subjected to PU coating curing, tempering and curing to obtain high-strength sound-proof fiberglass felt flooring.

[0015] In the above-mentioned high-strength and silent glass fiber felt floor and preparation method thereof, when the glass fiber felt is pre-treated by slurry impregnation and gluing, the gluing treatment of both sides of the glass fiber felt can be achieved simultaneously. With the setting of the continuous roller unit, after gluing, the paste-like glue coated on the surface can be smoothed and monitored at the same time, so as to timely discover the excessive glue in some areas and enable the staff to make timely adjustments, thereby greatly improving the overall gluing uniformity, so that during hot pressing and gluing, the connection between the glass fiber felt layer and the floor is more stable, and it is not easy to have hollowing and degumming, so that the strength, stability and silent effect of the floor are effectively maintained.

[0016] As a further improvement of the present application, the raw materials of the middle layer and the bottom layer are PVC, plasticizer, filler, additive, pigment, lubricant, and stabilizer. The plasticizer is one of DOP and DOTP, the filler is heavy calcium, the additive is one of ACR and a foaming regulator, the lubricant is one of zinc stearate and PE wax, the stabilizer is a calcium zinc stabilizer, and the adhesive is a polyvinyl chloride paste resin or an acrylic adhesive.

[0017] As a further improvement of the present application, in the operation of pre-treating the glass fiber mat in step S2:

[0018] The unwinding roller is located directly above the winding roller, and the two have the same rotation direction, while the direction-changing roller rotates in the opposite direction to the unwinding roller and the winding roller.

[0019] As a further improvement of the present application, the continuous roller unit includes a glue coating roller, a smoothing roller and a re-leveling roller which are sequentially arranged in the process of winding and unwinding the glass fiber mat through an electric rotating shaft;

[0020] In the roller unit close to the unwinding roller, the glue coating roller is located on the side of the smoothing roller facing the unwinding roller; in the roller unit close to the direction-changing roller, the glue coating roller is close to the side of the smoothing roller facing the direction-changing roller.

[0021] As a further improvement of the present application, a monitoring groove is bored on the outer cylindrical surface of the smoothing roller, a pressure sensor array is arranged on the inner wall of the monitoring groove facing the outside of the smoothing roller, the outer surface of the smoothing roller is wrapped with an outer layer, and the pressure sensor array is located on the inner side of the outer layer.

[0022] As a further improvement of the present application, the pressure sensor array is not in contact with the outer cladding, the outer cladding is in contact with an elastic material, and the outer cladding is in extrusion contact with the surface of the smoothing roller.

[0023] As another improvement of the present application, the continuous roller unit also includes an eccentric roller, which is located between the smoothing roller and the re-leveling roller. The eccentric roller includes an axis body and a plurality of self-eccentric roller pieces sleeved outside the axis body. Every two adjacent self-eccentric roller pieces are in contact with each other. An eccentric groove is opened on the self-eccentric roller pieces. The axis body movably penetrates the eccentric groove. An electric push rod is installed between the axis body and the inner wall of the eccentric groove away from the center of the self-eccentric roller pieces, and the extended end of the electric push rod is connected to the self-eccentric roller piece.

[0024] As another improvement supplement to the present application, the maximum span of the eccentric groove along the radial direction of the self-eccentric roller is not less than twice the diameter of the shaft body, the two edges of the eccentric groove cross-section in the radial direction of the self-eccentric roller are semicircular, and the diameter of the semicircle is consistent with the shaft body, and the center of the semicircle away from the electric push rod is located on the axis of the self-eccentric roller.

[0025] As another improved supplement of the present application, the pressure sensor array includes a plurality of pressure sensors, and the plurality of self-eccentric rollers correspond to the plurality of pressure sensors respectively.

[0026] In summary, when the glass fiber felt is pre-treated by slurry and gluing, the gluing treatment can be achieved on both sides of the glass fiber felt simultaneously. With the setting of the continuous roller unit, after gluing, the paste-like glue coated on the surface can be smoothed and monitored at the same time, so as to timely detect excessive local glue. At the same time, under the setting of the eccentric roller, the excessive local glue can be monitored and eccentrically rolled at a fixed point to achieve the effect of spontaneously adjusting the uniformity of the glue distribution, thereby greatly improving the uniformity of the glue distribution on the glass fiber felt, so that during hot pressing and gluing, the connection between the glass fiber felt layer and the floor is more stable, and it is not easy to have hollowing and degumming, so that the strength, stability and quietness of the floor are effectively maintained. BRIEF DESCRIPTION OF THE DRAWINGS

[0027] Figure 1 This is a schematic cross-sectional view of a floor according to a first embodiment of the present application;

[0028] Figure 2 This is a main flow chart of the first implementation method of the present application;

[0029] Figure 3 This is a schematic diagram of pre-treatment of glass fiber mat for simultaneous gluing on both sides in the first embodiment of the present application;

[0030] Figure 4 A top view of a smoothing roller according to a first embodiment of the present application;

[0031] Figure 5 This is a radial cross-sectional view of the smoothing roller of the first embodiment of the present application;

[0032] Figure 6 This is a cross-sectional view of the monitoring long groove of the smoothing roller when the gluing is uniform in the first embodiment of the present application;

[0033] Figure 7 It is a cross-sectional view of the monitoring long groove of the smoothing roller when excessive gluing occurs locally in the first embodiment of the present application;

[0034] Figure 8 This is a schematic diagram of the pretreatment of the glass fiber mat for simultaneous double-sided gluing in the second embodiment of the present application;

[0035] Fig. 9 This is a top view of an eccentric roller according to a second embodiment of the present application;

[0036] Fig.10 This is a schematic diagram of a radial cross section of an eccentric roller according to a second embodiment of the present application;

[0037] Fig.11 This is a cross-sectional schematic diagram of a self-eccentric roller sheet corresponding to a situation where excessive glue is applied locally in the second embodiment of the present application;

[0038] Fig.12 This is a top view of the second embodiment of the present application when the eccentric roller eccentrically rolls the rubber material at too many fixed points.

[0039] Description of the numbers in the figure:

[0040] 1. Gluing roller, 2. Smoothing roller, 21. Outer layer, 22. Pressure sensor, 201. Monitoring long slot, 3. Eccentric roller, 31. Self-eccentric roller piece, 32. Shaft body, 33. Electric push rod, 301. Eccentric slot. DETAILED DESCRIPTION

[0041] Two implementation modes of the present application are described in detail below with reference to the accompanying drawings.

[0042] The first implementation method:

[0043] Figure 1A high-strength and sound-proof glass fiber felt floor is shown, which comprises, from top to bottom, a wear-resistant layer, a printing layer, a glass fiber middle layer, a bottom layer and a sound-proof layer, and the layers are connected by hot pressing and gluing. The glass fiber middle layer comprises two middle layers and a glass fiber felt layer located between the two middle layers, and the middle layer and the glass fiber felt layer are also connected by hot pressing and gluing.

[0044] The preparation method of the high-strength sound-proof glass fiber felt floor comprises the following steps:

[0045] S1, mixing the middle layer raw materials in a mixer, putting them into an internal mixer for internal mixing after mixing, and rolling them into a sheet-like semi-finished product to obtain the middle layer, wherein the preparation process of the bottom layer is consistent with that of the middle layer, and the above process is repeated to prepare the bottom layer;

[0046] S2, pre-treating the glass fiber felt by slurry infusion, and after the pre-treatment, cutting the glass fiber felt layer according to the product size to obtain a glass fiber felt layer;

[0047] S3, firstly sandwich the glass fiber felt layer between the two middle layers and perform hot pressing bonding treatment to obtain the glass fiber middle layer, and then sequentially lay the mute layer, the bottom layer, the glass fiber middle layer, the printing layer, and the wear-resistant layer from bottom to top, and then perform hot pressing treatment to bond the layers together, wherein the wear-resistant layer is made of the surface paper of the wear-resistant material aluminum oxide impregnated with melamine resin, and the printing layer is printing paper made by computer simulation;

[0048] S4. Post-processing: The semi-finished products after forming are subjected to PU coating curing, tempering and curing to obtain high-strength sound-proof fiberglass felt flooring.

[0049] The raw materials of the middle layer and the bottom layer are PVC, plasticizer, filler, additive, pigment, lubricant and stabilizer. Among them, by weight, the middle layer includes 70-100 parts of PVC, 1-20 parts of plasticizer, 0-200 parts of filler, 0-10 parts of additive, 0-5 parts of pigment, 0-2 parts of lubricant and 1-5 parts of stabilizer; the bottom layer includes 80-110 parts of PVC, 1-20 parts of plasticizer, 0-400 parts of filler, 0-10 parts of additive, 0-5 parts of pigment, 0-5 parts of lubricant and 1-5 parts of stabilizer. In specific implementation, the appropriate amount of ingredients can be selected within the range according to actual needs.

[0050] The plasticizer is one of DOP and DOTP, the filler is heavy calcium, the auxiliary agent is one of ACR and a foaming regulator, the lubricant is one of zinc stearate and PE wax, the stabilizer is a calcium zinc stabilizer, and the adhesive is one of polyvinyl chloride paste resin or acrylic adhesive.

[0051] The sound-proofing layer is made of common sound-proofing materials, such as silicone rubber.

[0052] like Figure 3, the specific operation of the sizing and gluing pretreatment of glass fiber felt is as follows:

[0053] S21, firstly unwinding the glass fiber felt, and then winding it up through a winding roller, setting a direction-changing roller between the winding and unwinding, and setting a drying device near the direction-changing roller and the winding roller;

[0054] S22, the glass fiber mat between the unwinding roller and the direction-changing roller, and between the direction-changing roller and the winding roller are respectively subjected to a gluing treatment by a continuous roller unit. After the glass fiber mat is firstly glued, it is dried by a drying device and then reaches the direction-changing roller. Then, it is glued for the second time, dried again, and then wound up, so as to achieve simultaneous gluing of both sides of the glass fiber mat.

[0055] Among them, the glue used for gluing is PVC paste resin or acrylic glue.

[0056] In the operation of pre-treating the glass fiber mat in step S2:

[0057] The unwinding roller is located directly above the winding roller, and the two have the same rotation direction, while the direction-changing roller rotates in the opposite direction to the unwinding roller and the winding roller.

[0058] The continuous roller unit includes a coating roller 1, a smoothing roller 2 and a flattening roller which are sequentially arranged in the process of winding and unwinding the glass fiber mat through an electric rotating shaft, and the flattening roller is a cylindrical structure with a smooth surface;

[0059] In this embodiment, the smoothing roller is installed above the fiberglass felt through an electric lifting assembly. When the smoothing roller 2 detects that there is too much glue locally when smoothing the glue, the electric lifting assembly can be used to control the smoothing roller to move down and be flush with the glue coating roller 1. The electric shaft is then used to control its rotation to rotate and roll the surface of the fiberglass felt, so that the excess glue locally can be dispersed around, and the glue on the entire surface of the fiberglass felt can be evenly distributed. When it is subsequently hot-pressed and glued to the floor, the connection stability will be better. When in use, it is less likely to have hollowing or degumming, thereby improving the overall strength, stability and quietness of the floor.

[0060] In the continuous roller unit close to the unwinding roller, the glue coating roller 1 is located on the side of the smoothing roller 2 facing the unwinding roller; in the continuous roller unit close to the changing roller, the glue coating roller 1 is close to the side of the smoothing roller 2 facing the changing roller, which effectively ensures that the slurry application on the front and back sides is a process of first gluing and then drying.

[0061] like Figure 4 and Figure 5A monitoring long groove 201 is cut on the outer cylindrical surface of the smoothing roller 2. A pressure sensor array is arranged on the inner wall of the monitoring long groove 201 facing the outside of the smoothing roller 2. The pressure sensor array includes a plurality of pressure sensors. The outer surface of the smoothing roller 2 is wrapped with an outer layer 21. The pressure sensor array is located inside the outer layer 21. The pressure sensor array does not contact the outer layer 21. The outer layer 21 is in contact with an elastic material, and the outer layer 21 is in compression contact with the surface of the smoothing roller 2. Figure 6 The smoothing roller 2 rotates to squeeze the surface of the glass fiber felt after gluing. When the glue material on the surface of the glass fiber felt is evenly distributed after being glued by the gluing roller 1, the outer layer 21 of the mouth of the monitoring long groove 201 is in a straight state and does not contact the pressure sensor 22 at this time. Figure 7 When there is more rubber in some parts, during the rotation of the smoothing roller 2, when the mouth of the monitoring long groove 201 is facing directly downward, the excess rubber squeezes the outer layer 21, causing it to deform toward the side of the pressure sensor 22, and then squeezes the pressure sensor 22 to generate force data. Based on this, it can be judged whether the rubber on the surface of the glass fiber felt is uniform, which is convenient for determining whether to control the smoothing roller to roll the glass fiber felt surface to further improve the uniformity.

[0062] When the glass fiber felt is pre-treated with slurry and gluing, the gluing treatment can be achieved on both sides of the glass fiber felt simultaneously. With the setting of the continuous roller unit, the paste-like adhesive coated on the surface can be smoothed after gluing, and it can be monitored at the same time to facilitate timely detection of excessive local adhesive, so that the staff can make timely adjustments, thereby greatly improving the overall gluing uniformity, making the connection between the glass fiber felt layer and the floor more stable during hot pressing and gluing, and less prone to hollowing and degumming, so that the strength, stability and quietness of the floor are effectively maintained.

[0063] The second implementation method:

[0064] Figure 8 It is shown that, based on the first embodiment, this embodiment adds an eccentric roller 3, and the rest of the parts are consistent with the first embodiment.

[0065] Figure 9-10As shown, the continuous roller unit also includes an eccentric roller 3, which is located between the smoothing roller 2 and the re-smoothing roller. The eccentric roller 3 includes a shaft 32 and a plurality of self-eccentric roller pieces 31 sleeved outside the shaft 32. The plurality of self-eccentric roller pieces 31 correspond to a plurality of pressure sensors respectively. Every two adjacent self-eccentric roller pieces 31 are in contact with each other. An eccentric groove 301 is cut on the self-eccentric roller piece 31. The shaft 32 movably penetrates the eccentric groove 301. The shaft 32 and the eccentric groove 301 are away from the self-eccentric roller. An electric push rod 33 is installed between the inner walls at the center of the sheet 31, and the extended end of the electric push rod 33 is connected to the self-eccentric roller sheet 31. The maximum span of the eccentric groove 301 along the radial direction of the self-eccentric roller sheet 31 is not less than twice the diameter of the shaft body 32. The two edges of the cross-section of the eccentric groove 301 in the radial direction of the self-eccentric roller sheet 31 are both semicircular, and the diameter of the semicircle is consistent with the shaft body 32. The center of the semicircle away from the electric push rod 33 is located on the axis of the self-eccentric roller sheet 31.

[0066] When force data is generated on a pressure sensor in the pressure sensor array, the electric push rod 33 on the corresponding eccentric roller 31 can be controlled to shorten. Figure 11-Figure 12 , making the corresponding self-eccentric roller piece 31 eccentric with the other self-eccentric roller pieces 31. At this time, the eccentric roller 3 can be controlled to rotate by the electric shaft to rotate the eccentric roller 3 as a whole. At this time, the self-eccentric roller piece 31 and the shaft body 32 are offset from the axis, and eccentric rotation occurs. During the rotation, the excessive rubber is rolled. At this time, before the flattening roller rolls the fiberglass felt, the excessive rubber is rolled at a predetermined point in advance, so that the local excess rubber is pre-dispersed outward to a certain extent, so that the subsequent flattening roller can better distribute the rubber evenly during rolling.

[0067] In addition, it is worth noting that when the pressure sensor 22 is triggered, the corresponding eccentric roller 31 and one or more eccentric rollers 31 on both sides of the eccentric roller 31 can be synchronously eccentrically misaligned with the shaft 32, thereby achieving a better eccentric rolling effect on excess rubber.

[0068] Compared with the first embodiment, in this embodiment, after finding excessive local rubber, under the setting of the eccentric roller, eccentric rolling can be performed at a fixed point where the local excessive rubber is detected, so as to achieve the effect of spontaneously adjusting the uniformity of the rubber distribution. Compared with the first embodiment in which only the flattening roller is used to perform indiscriminate rolling to eliminate the excessive local rubber, in this embodiment, the eccentric roller 3 can be used to perform local fixed-point rolling before the flattening roller rolling, so that the excessive local rubber can be diffused outward in advance, so that the rubber can be restored to a uniform distribution during the subsequent indiscriminate rolling, so that the subsequent flattening roller rolling will not easily cause the situation that the rolling is difficult to be uniform due to the excessive local rubber, thereby further improving the uniformity of the rubber distribution on the surface of the glass fiber felt.

[0069] In view of current practical needs, the above-mentioned implementation mode adopted in this application is not limited to the scope of protection. Various changes made within the knowledge scope of technical personnel in this field without departing from the concept of this application still fall within the scope of protection of the present invention.

Claims

1. A method for preparing a high-strength sound-proof glass fiber felt floor, characterized in that: The floor comprises, from top to bottom, a wear-resistant layer, a printing layer, a glass fiber middle layer, a bottom layer and a sound-proof layer, and the layers are connected by hot pressing and gluing. The glass fiber middle layer comprises two middle layers and a glass fiber felt layer located between the two middle layers, and the middle layer and the glass fiber felt layer are also connected by hot pressing and gluing. The preparation method of the high-strength sound-proof glass fiber felt floor comprises the following steps: S1, mixing the middle layer raw materials in a mixer, putting them into an internal mixer for internal mixing after mixing, and rolling them into a sheet-like semi-finished product to obtain the middle layer, wherein the preparation process of the bottom layer is consistent with that of the middle layer, and the above process is repeated to prepare the bottom layer; S2, pre-treating the glass fiber felt by slurry infusion, and after the pre-treatment, cutting the glass fiber felt layer according to the product size to obtain a glass fiber felt layer; The specific operation of pretreatment of glass fiber felt pulping is as follows: S21, firstly unwinding the glass fiber felt, and rewinding it through a reel, setting a direction-changing roller between the reeling and unwinding, and setting a drying device near the direction-changing roller and near the reeling roller; S22, the glass fiber mat between the unwinding roller and the direction-changing roller, and between the direction-changing roller and the winding roller are respectively subjected to a gluing treatment by a continuous roller unit. After the glass fiber mat is firstly glued, it is dried by a drying device and then reaches the direction-changing roller. Then, it is glued for the second time, dried again, and then wound up, so as to achieve simultaneous gluing of both sides of the glass fiber mat. S3, firstly sandwich the glass fiber felt layer between the two middle layers and perform hot pressing bonding treatment to obtain the glass fiber middle layer, and then sequentially lay the mute layer, the bottom layer, the glass fiber middle layer, the printing layer, and the wear-resistant layer from bottom to top, and then perform hot pressing treatment to bond the layers together; S4, post-processing: the semi-finished product after forming is subjected to PU coating curing, tempering and curing to obtain a high-strength silent glass fiber felt floor; In the operation of pre-treating the glass fiber mat in step S2: The unwinding roller is located directly above the winding roller, and the two have the same rotation direction, and the direction of rotation of the direction-changing roller is opposite to that of the unwinding roller and the winding roller; The continuous roller unit comprises a glue coating roller (1), a smoothing roller (2) and a re-smoothing roller which are arranged in sequence during the winding and unwinding process of the glass fiber mat via an electric rotating shaft; The releveling roller is installed above the glass fiber mat via an electric lifting assembly. When the releveling roller (2) detects that there is too much glue locally when smoothing the glue, the electric lifting assembly controls the releveling roller to move down and be flush with the glue coating roller (1). The electric shaft then controls the releveling roller to rotate and roll the surface of the glass fiber mat. In the roller unit close to the unwinding roller, the glue coating roller (1) is located on the side of the smoothing roller (2) facing the unwinding roller; in the roller unit close to the direction-changing roller, the glue coating roller (1) is located on the side of the smoothing roller (2) facing the direction-changing roller; The outer cylindrical surface of the smoothing roller (2) is provided with a monitoring long groove (201), and a pressure sensor array is arranged on the inner wall of the monitoring long groove (201) facing the outside of the smoothing roller (2). The outer surface of the smoothing roller (2) is wrapped with an outer cladding (21), and the pressure sensor array is located on the inner side of the outer cladding (21); the pressure sensor array does not contact the outer cladding (21), the outer cladding (21) is made of elastic material, and the outer cladding (21) is in compression contact with the surface of the smoothing roller (2).

2. The method for preparing a high-strength sound-proof glass fiber felt floor according to claim 1, characterized in that: The raw materials of the middle layer and the bottom layer are PVC, plasticizer, filler, additive, pigment, lubricant and stabilizer. The plasticizer is one of DOP and DOTP, the filler is heavy calcium, the additive is one of ACR and foaming regulator, the lubricant is one of zinc stearate and PE wax, and the stabilizer is calcium zinc stabilizer.

3. The method for preparing a high-strength sound-proof glass fiber felt floor according to claim 1, characterized in that: The continuous roller unit further comprises an eccentric roller (3), wherein the eccentric roller (3) is located between the smoothing roller (2) and the re-smoothing roller, wherein the eccentric roller (3) comprises an axle (32) and a plurality of self-eccentric roller pieces (31) sleeved outside the axle (32), wherein each two adjacent self-eccentric roller pieces (31) are in contact with each other, an eccentric groove (301) is formed on the self-eccentric roller pieces (31), wherein the axle (32) movably penetrates the eccentric groove (301), and an electric push rod (33) is installed between the axle (32) and an inner wall of the eccentric groove (301) away from the center of the self-eccentric roller pieces (31), and an extended end of the electric push rod (33) is connected to the self-eccentric roller pieces (31).

4. The method for preparing a high-strength sound-proof glass fiber felt floor according to claim 3, characterized in that: The maximum span of the eccentric groove (301) along the radial direction of the self-eccentric roller (31) is not less than twice the diameter of the shaft (32); both edges of the cross section of the eccentric groove (301) in the radial direction of the self-eccentric roller (31) are semicircular, and the diameter of the semicircle is consistent with that of the shaft (32); the center of the semicircle away from the electric push rod (33) is located on the axis of the self-eccentric roller (31).

5. The method for preparing a high-strength sound-proof glass fiber felt floor according to claim 4, characterized in that: The pressure sensor array comprises a plurality of pressure sensors, and the plurality of self-eccentric roller sheets (31) respectively correspond to the plurality of pressure sensors.

Images