Method for welding sheet metal parts

Abstract

The present invention relates to a method for butt welding of flat sheet metal plates 1, 2 in a welding machine, in which the two sheet metal plates 1, 2 are positioned on a transport unit 37 by a feeding means and fixed by a holding means, in which two edges 4, 5 of the two sheet metal plates 1, 2 to be welded to each other are juxtaposed butt-together with as little gap as possible and welded to each other by a welding laser 6, in which a gap width 7 of the gap is measured and the welding process is controlled by this measurement value. According to the invention, the gap width 7 is measured using a reflected light method and the actual gap width 9 is measured using a transmitted light method, so that a defect area 8 or defect volume in the gap can be better estimated.

Description

[Technical field]

[0001] The invention relates to a method for butt welding of sheet metal parts, in particular, but not exclusively, in vehicle body construction, according to the preamble of claim 1. [Background technology]

[0002] For the production of sheet metal parts in the body structure, modern manufacturing methods are used which - possibly after sheet metal ridge preparation - produce welded parts, so-called tailored blanks (TWB), from individual sheet metal panels. In known welding methods, in particular laser welding, the sheet metal panels are fed into a fixed welding tool and welded. Nowadays, in particular, it is advantageously used for plates to be made up of different material quality grades or sheet metal thicknesses, which makes it possible to adapt various positions of a later structural member to its local future loads, which would otherwise require additional reinforcing members. Today, in the automotive industry, door rings made of TWB are manufactured, which consist of up to eight individual parts, with the gap formation differing due to the shape and manufacturing tolerances between the individual parts, and the sheet metal thickness of the individual parts also differing. Furthermore, for efficient production, the fact that the gap conditions from door ring to door ring can differ, whereby different types of gap conditions can occur, is a difficulty. The suppression of the V-shaped gap then embodies the greatest challenge.

[0003] Poor welding quality may result in unwanted seam cracks in the door ring during crash testing, a risk that cannot be accepted in door ring production due to reliability considerations, because crashes in real situations are fatal in the automotive industry with correspondingly dramatic consequences. At the present time, methods are known for closing variable gaps up to 0.3 mm with the addition of filler wire. One challenge is to dynamically close variable gaps of up to about 1 mm with the addition material (wire) and with high weld quality, depending on the respective welding operation (material of the structural parts to be welded).

[0004] In the known welding methods, in particular laser welding, there are two known methods: In the first method, the sheet metal panels are precisely positioned, tensioned and welded with a movable welding head, while in the other method, the sheet metal panels are fed into a fixed position welding tool and welded. In order to machine gap widths of up to about 0.3 mm, both methods require high mechanical precision.

[0005] In the patent document 1, a method and an apparatus for carrying out the method are described, but it is not disclosed how the precise positioning of the welding tool is performed in comparison with the actual seam course. As a result, the inaccuracies in the plates and the positional deviations of the seam path lead to imprecise weld seams.

[0006] In the patent DE 10 200 03 03 52 A1 a method is described for continuous butt seam welding of sheet metal panels, in which the relative position of the sheet metal panels and thus the precision of the seam gap are maintained within a predefined tolerance range, while deliberately omitting a precise mechanical alignment of the sheets to be welded together. Instead, the gap width and the gap position are detected here by means of a sensor system and the beam tool is made to follow the sheet metal abutments of both sheet metal panels.Furthermore, by means of a control circuit, the power of the welding beam and the necessary cooling capacity (gas, water) for the welding process can be permanently adapted.Such a system requires high maintenance costs.

[0007] A challenge in laser welding is that the gap conditions from component to component can differ, resulting in different gap conditions such as A gap, V gap, parallel gap, zero gap, or a mixture of these. A known method for determining the gap size is the reflected light method, whereby light is emitted via a light source towards the gap, this light is reflected by the metal surface and evaluated by a camera arranged on the same side of the sheet metal as the light source. A known reflected light method is, for example, laser line evaluation, which is based on laser triangulation, in which a laser line is projected onto the surfaces of both sheet metal plates. The projected laser line is essentially perpendicular to the sheet metal edge that forms the gap. The reflected laser line strikes the camera at a certain angle, depending on the distance or gap shape. By evaluating the visualized laser line, the gap width can therefore be determined.

[0008] However, such systems are not always able to provide accurate gap measurements, especially when it cannot be guaranteed that the same side of the sheet metal panel always faces upwards, and the measurement system may provide an inaccurate gap measurement.

[0009] In particular, such systems often provide only the gap width in the upper region of the gap, but rarely allow for a priori inference to the gap width in deeper regions.

[0010] A large gap width between both sheets to be welded induces losses of the absorbed laser energy in this gap, since part of the laser beam passes through the gap unhindered. It is certainly possible to reduce this loss to a certain extent by using a single defocus, but this in turn entails reducing the maximum light intensity of the laser beam as well.

[0011] On the other hand, at technical zero gap, the ability to heat and cut intensely, i.e. the complete penetration of the metal vapor capillary in laser beam welding, is reduced, which can be compensated to a certain extent by a reduced welding speed or, however, by an increased laser power. In summary, it can be said that in use, a conflict arises between the possibility of filling gaps and the ability to heat and cut intensely. To ensure optimal productivity, the laser source is operated at the design limits of the laser power. In many plant concepts, changing the welding speed during a welding operation is not possible due to reaction times, which generally leads to reduced productivity.

[0012] To solve the problems of workability of wide weld gaps, efficiency losses and process reliability, several attempts have been investigated so far. Thus, for example, the idea of ​​single-focus Scan-Trackers was pursued in which a laser beam with a small focal diameter (0.2 to 0.3 mm) and high light intensity was swung transversely to the welding operation. Depending on the measured gap width, the amplitude as well as the laser power are varied. Studies with commercially available system technologies for welding plates have shown, however, that at high welding speeds of about 10 m / min, the cycle length of the oscillating movement does not guarantee any complete coverage of remelted material, based on the achievable frequencies. In order to produce an acceptable weld seam, the welding speed has to be significantly reduced, which induces a loss in productivity, regardless of the gap or zero gap.

[0013] Twin-Spot-Optik in laser beam welding, i.e. the use of two spatially separated focal points on the material, is a technique which, unlike ever before, has now made a quantum leap from the laboratory to production. In the document EP 1 099 433 A1, it is intended that the laser beam has at least two focal points within the weld point or at a small spatial distance from this weld point, the distance between the focal points being continuously changed based on the measurement of the individual parameters of the welding process, in particular the welding speed and the weld quality grade. Patent document 4 relates to a laser processing device and relates to a rotating twin-spot optical system-laser processing head, which includes a laser emitter, a light guide tube for transferring the laser beam, and a focusing mirror for focusing the laser beam. The beam separating device is coupled to a drive device, the drive device being capable of rotating the beam separating device.

[0014] A welding device with twin spot optics is likewise described in US Pat. No. 5,399,633.

[0015] By means of the twin-spot optics, the laser energy distribution can be improved at will on both sides of a weld seam and defects of insufficient individual focus-energy transfer are thereby avoided. Furthermore, the beam splitter is coupled to a drive and can be rotated accordingly. The rotation of the double focus can then be performed by rotating the entire process optics or by rotating the twin spot optics module. The great advantage of this method is the possibility of adapting the power distribution to the loading position and controlling it depending on the process conditions, for example at a changed gap width. This allows a high degree of flexibility, but in particular a high process stability and weld seam quality. Studies have shown that welding with the twin-spot optical technology nevertheless provides a smaller weld depth than welding with only one laser beam at the same power level. From a manufacturing engineering point of view, however, the question of optimal parameters for the creation of the desired weld seam is very narrowly linked to the economic aspects of the entire process. The efficiency of the process and the quality of the weld seam are therefore central features of the joining method.

[0016] In order to be able to guarantee the desired quality of the welded plate as well as the quality of the entire processing process with reasonable technical expenditure and added materials, important criteria in the process for welding tailored blanks are, on the one hand, the throughput of the entire plant, i.e. how many components can be produced per hour, taking into account an acceptable rejection rate, and, on the other hand, the material expenditure in added materials.

[0017] In the above mentioned solutions and methods, it is usually a drawback that only the gap width and the gap position are measured, however, the gap geometry is not taken into account. 3 shows in this context various gap geometries, which are essentially induced by the cutting process. Similarly, even if both sheet metal plates now contact at one point in the cut surface and there is now associated zero gap, there are also areas where the plates do not touch. To obtain an optimal welding result, the missing volume in this region should typically be filled with material during the welding process. For this purpose, however, not only the gap width at one location but also the gap geometry needs to be detected or at least estimated. In known methods, this is not the case, as the gap width is detected at only one position, usually in the region of the sheet metal surface. [Prior art documents] [Patent documents]

[0018] [Patent Document 1] US Patent No. 5,328,083A [Patent Document 2] European Patent No. 0817698 B1 [Patent Document 3] German Patent No. 101 13 471 B4 [Patent Document 4] Chinese Patent No. 203124961U Specification [Patent Document 5] European Patent Application Publication No. 3 572 178 A1 Summary of the Invention [Problem to be solved by the invention]

[0019] The problem underlying the present invention is therefore to provide a method, in which the above-mentioned drawbacks are eliminated. [Means for solving the problem]

[0020] This problem is solved by the features set forth in claim 1. Advantageous embodiment variants are set forth in the dependent claims. Effect of the Invention

[0021] According to the present invention, therefore, The gap width is measured using a reflected light method and the actual gap width is measured using a transmitted light method, and Therefore, the defect area or defect volume in the gap can be estimated more accurately. The actual gap width means the minimum distance between both sheet metal edges, i.e. the inside clearance area between the plates.

[0022] The reflected light method is preferably a laser line method, i.e. a laser triangulation method, in which a laser line is projected perpendicularly to the gap course onto the sheet metal surface and the shape of the line is evaluated.

[0023] In the transmitted light method, light is emitted through the gap and detected by a camera on the oppositely located sheet metal sides. By corresponding image evaluation, the inside width between the two sheet metal plates (actual gap) can be determined.

[0024] The invention presented here thus allows, alongside the measurement of the gap width by the reflected light method, also the visualization or measurement of the actual gap between the plates to be welded together, so that the defect volume can be estimated and the welding process can be optimally controlled.

[0025] Advantageously, a filler wire is supplied to the laser welding process, and by improved gap measurement the optimum required amount of added material (filler wire) can be better detected, and the optimum amount of wire is supplied by controlling the supply speed of the added wire, whereby a better quality of the weld seam and a reduction in the amount of added wire required can be achieved.

[0026] Accordingly, the production costs can be generally reduced by the proposed method.

[0027] Overall, the presented method provides better productivity and therefore better process quality in comparison with other known methods.

[0028] Advantageously, the evaluation of the measurement results for the determination of the defect volume between both ridges is carried out during the welding process using image-technical methods.

[0029] It is likewise of value if perforations in the produced weld seam are detected using further lighting devices and their associated cameras.

[0030] Advantageously, the reflected light method uses a light source for monochromatic light.

[0031] It is advantageous if the gap width and the actual gap width are continuously measured and evaluated.

[0032] Even better results are obtained when the reflected light method is used to measure the gap width: And possibly this can also be achieved if the transmitted light method is used on the upper and lower sides of the sheet metal plate for measuring the actual gap width.

[0033] The method according to the invention is particularly well suited for the production of tailored blanks in vehicle body construction.

[0034] The invention and the problems of the current measuring methods are explained further below on the basis of examples and in conjunction with the figures. [Brief description of the drawings]

[0035] [Figure 1] FIG. 2 is a schematic illustration of one exemplary side view of a laser welding process according to the present invention; [Diagram 2] FIG. 13 is a cross-sectional view of a sheet metal ridge after a cutting process. [Diagram 3] 1A-1D are cross-sectional views of possible configurations of cutting edges in a schematic illustration; [Figure 4] FIG. 2 is a cross-sectional view of a gap between two contacting sheet metal plates in a schematic illustration. [Diagram 5] FIG. 1 shows, in a schematic illustration, two non-contacting sheet metal plates with a real gap and gap illumination according to the prior art. [Figure 6] 1 also shows, in a schematic illustration, a gap measurement using transmitted light. [Figure 7] FIG. 2 is a cross-sectional view of a gap between two non-contacting sheet metal plates in a schematic illustration. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0036] The same reference numbers in different figures indicate the same features in each.

[0037] FIG. 1 shows one embodiment of a laser welding process 35 according to the invention for processing sheet metal plates 1, 2, which are positioned, by way of example, but without being limited thereto, on a transport unit 37 which is movable exclusively in the feed direction TR. In a first process step, the sheet metal plates 1, 2 are positioned on the transport unit 37 by means of feeding means (not shown) and are clamped by means of holding means (not shown). The gap position and the gap width are then detected. This is done by means of the upper camera 20 and, optionally, by means of the lower camera 21 as well. Additionally, both cameras 20, 21 are provided with a lower lighting device 18 and an upper lighting device 19, respectively, located opposite each other.

[0038] The distance D between the two sheet metal plates 1 and 2 in each case depends on the contours of the sheet metal plates to be welded, with the distance D being able to be kept small in the case of a rectangular contour of the sheet metal plates 1, 2 and having to be selected larger, for example in the case of a diamond-shaped contour of the sheet metal plates 1, 2. In a second process step, the sheet metal plates 1 , 2 are joined by means of a welding laser 6 with the addition of the filler wire 10 by means of a filler wire unit 24 into one welded sheet metal plate 36 . In a third process step, the quality of the weld seam is inspected from above by a second, fixed-position quality system consisting of an upper camera 22 and a lower lighting device 31, and optionally from below by an additional, fixed-position quality system (lower camera 23 and upper lighting device 32). Subsequently, the welded sheet metal plate 36 is removed from the transport belt after release of the holding means (not shown).

[0039] FIG. 2 shows, in a schematic illustration, an edge 5 of a sheet metal plate 1 having a sheet metal thickness T1 by way of example after cutting. Due to the cutting process, the ridge 5 has a plastically deformed rollover region R, an undeformed cut region S, a broken region B, and a burr G. The ratio of cut region S to broken region B can be strongly varied.

[0040] FIG. 3 shows in a schematic representation possible configurations of the cutting edges or different gap geometries. When the left-hand sheet metal plate 1 and the right-hand sheet metal plate 2 are slid against each other, the gap geometry between both sheet metal plates 1, 2 can change from plate to plate as a result of the edge course being plastically deformed during the cutting process. This gap geometry will additionally depend on whether the sheet metal thicknesses T1, T2 of both sheet metal plates are the same or not. It is well understood here that the gap geometry varies greatly depending on the position of the sheet metal plates 1, 2. If both side surfaces of the sheet metal plates 1, 2 which are on the upper side during the cutting process also face upwards during the welding process, a completely different gap geometry is provided than if one or both side surfaces which face upwards during the cutting process face downwards during the welding process.

[0041] FIG. 4 shows, in a schematic cross-sectional view, a left-hand sheet metal plate 1 having an upper side 25 and a lower side 26 with a sheet metal thickness T1, and a right-hand sheet metal plate 2 having an upper side 25 and a lower side 26 with a sheet metal thickness T2. The two sheet metal plates 1, 2 are in contact on the underside in the area of ​​the left rollover side 27 and the right rollover side 28. In this area there is therefore no (real) gap. By means of a gap measurement using reflected light according to the prior art, the gap width 7 is detected. This detected gap width 7 normally reproduces the gap width 7 in the upper region of the gap. The hatched area indicates the missing area 8 between the two sheet metal plates 1, 2. Since the gap is now filled in the lower region, the defect area 8 can only be estimated rather imprecisely via the measured gap width 7.

[0042] 5 shows a gap measurement by reflected light in a schematic illustration. The two sheet metal plates 1 and 2 are not in contact here and therefore an actual gap is present. By actual gap is understood the gap width which corresponds to the minimum distance of the two edges 4 and 5 as viewed in cross section. Two light sources 11, 12 illuminate the actual gap, whereby a reflected light ray 13 is received by the camera 20. Light ray 14 is reflected in the upper region of the left ridge 4 in such a way that it cannot be detected by the upper camera 20. Light rays 15 and 16 are reflected many times in the region of the left ridge 4 and the right ridge 5, but cannot be detected by the camera 20 either. In this way, a gap width 7 is determined in the upper region of the sheet metal plates 1, 2, which gap width usually does not, however, correspond to the actual gap width.

[0043] FIG. 6 now shows the gap measurement using the transmitted light method on two sheet metal plates 1, 2 with a real gap. The left sheet metal plate 1 with upper side 25, lower side 26 and ridge 4 with sheet metal thickness T1 and the right sheet metal plate 2 with upper side 25, lower side 26 and ridge 5 with sheet metal thickness T2 are therefore not in contact. Via the lower lighting device 18, light 17 is emitted from below through the gap and is detected by the upper camera 20. With this gap measurement according to the transmitted light method, the actual gap width 9, ie the minimum distance between both edges 4 and 5, is measured.

[0044] Figure 7 now shows a gap measurement according to the invention, where the gap is measured simultaneously by reflected light mode (as illustrated in Figure 5) and by transmitted light mode (as illustrated in Figure 6). The two sheet metal plates 1, 2 are not in contact in the example under consideration here. By means of the reflected light method, the gap width 7 is measured in the upper area of ​​the sheet metal plates 1 and 2. By means of the transmitted light method, the actual gap width 9 is determined. In the example at issue here, the reflected light beam and the transmitted light beam are detected by a common camera 20. If the actual gap width 9 is subtracted from the detected gap width 7, then a false gap width 3 results. The false gap area 29 is the gap area that exists under the false gap width 3. Using the erroneous gap width 3 and the sheet metal thicknesses T1, T2, the erroneous gap area 29 can be estimated. From the measurement of the actual gap width 9 and the known sheet metal thicknesses T1, T2, the actual gap area 30 can be determined. The sum of the detected actual gap area 30 and the estimated erroneous gap area 29 results in the defect area 8, and thus the defect volume can be estimated.

[0045] 1, the reflected light method is not only used on the upper side of the sheet metal plates 1, 2, but also on the lower side. For this purpose, two light sources 38 and 39 are provided below the sheet metal plates. The light beams of these light sources 38, 39 are reflected by the sheet metal plates and the gaps and detected by the lower camera 21, which likewise detects the transmitted light of the upper lighting device 19. [Explanation of symbols]

[0046] 1 Left side sheet metal plate 2 Right side sheet metal plate 3. False Gap Width 4 Sheet metal ridge 5 Sheet metal ridge 6 Welding Laser 7 Gap width measured using the reflected light method 8. Missing Area 9 Actual gap width 10 Filled wire 11 Light source 12 light source 13 rays of light 14 rays 15 Rays 16 rays 17 light 18 Lower lighting device 19 Upper lighting device 20 Upper camera 21 Lower Camera 22 Upper camera 23 Lower camera 24 Filling wire unit 25 Upper surface of sheet metal plate 26 Underside of sheet metal plate 27 Rollover left side 28 Rollover right side 29 False Gap Area 30 Actual gap area 31 Lower lighting device 32 Upper lighting device 35 Laser Welding Process 36 Welded sheet metal plate 37 Transport unit 38 Light source 39 Light source TR transport direction R Rollover area S cutting area B Damage area G Rolled up part D Sheet metal spacing D T1 Sheet metal thickness of the left plate T2 Sheet metal thickness of the right plate

Claims

1. A method for butt welding of flat sheet metal plates (1, 2) in a welding machine, comprising: The two sheet metal plates (1, 2) are positioned on the conveying unit (37) by a supplying means and fixed by a holding means; Two edges (4, 5) of two sheet metal plates (1, 2) to be welded together are placed side by side with as little gap as possible and welded together by a welding laser (6), The method, wherein a gap width (7) of the gap is measured and the welding process is controlled by this measurement, The gap width (7) is measured simultaneously using a reflected light method and the actual gap width (9) is measured using a transmitted light method; and This allows the defect area (8) or defect volume in the gap to be estimated; The method comprising:

2. 2. The method according to claim 1, wherein the reflected light method is a laser line method, i.e., a laser triangulation method.

3. 3. The method according to claim 1, characterized in that the laser welding process (35) is fed with a filler wire (10).

4. 4. The method of claim 3, wherein filler wire supply is controlled in proportion to the estimated defect volume.

5. The evaluation of the measurement results for the determination of the defect volume between both of the ridges (4, 5) comprises:

5. A method according to claim 1, characterized in that it is carried out during the welding process using image technological methods.

6. 6. The method according to claim 1, further comprising the step of: after the welding process, using lighting devices (31, 32) and their associated cameras (22, 23), perforations in the produced weld seam can be detected.

7. 7. The method according to claim 1, wherein the reflected light method uses a light source (11, 12) for monochromatic light.

8. 8. The method according to claim 1, wherein the gap width (7) and the actual gap width (9) are continuously measured and evaluated.

9. 7. The method according to claim 1, wherein a common camera (20) is used for the reflected light mode and the transmitted light mode.

10. 9. The method according to claim 1, wherein the reflected light method is used on the upper and lower sides of the sheet metal plates (1, 2) for measuring the gap width (7).

11. 11. The method according to claim 1, wherein the transmitted light method is used on the upper and lower sides of the sheet metal plates (1, 2) for measuring the actual gap width (9).

12. 12. Use of a method according to any one of claims 1 to 11 for the production of tailored blanks in a vehicle body structure.