Method for preparing 7055 aluminum alloy with high intensity and high toughness
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A high-strength, high-toughness, aluminum alloy technology, applied in the field of aluminum alloy preparation technology, can solve the problems of elongation not exceeding 5%, small ingot size, inability to meet aviation and aerospace industries, etc., to solve structural efficiency, improve resistance The effect of compressive strength
Active Publication Date: 2009-02-18
NORTHEAST LIGHT ALLOY CO LTD
View PDF2 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] The purpose of the present invention is to provide a high-strength and high-toughness 7055 aluminum alloy to solve the problem that the strength of the existing 7055 aluminum alloy is only about 500MPa, the elongation is not more than 5%, and the specification of the ingot is small, which cannot meet the needs of the aviation and aerospace industries. Preparation method of aluminum alloy
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
specific Embodiment approach 1
[0007] Specific Embodiment 1: The high-strength and high-toughness 7055 aluminum alloy of this embodiment consists of Si: 0.1%, Fe: 0.15%, Cu: 2-2.6%, Mn: 0.05%, Mg: 1.8-2.3%, Cr: 0.04%, Ti: 0.06%, Zr: 0.08-0.2%, Zn: 7.6-8.4%, impurity 0.1%, and the balance made of Al.
specific Embodiment approach 2
[0008] Specific embodiment 2: In this embodiment, the weight percentage of Cu is 2.3% of the total weight of the high-strength and high-toughness 7055 aluminum alloy, that is, the high-strength and high-toughness 7055 aluminum alloy consists of Si: 0.1%, Fe: 0.15%, and Cu: 2.3% by weight percentage , Mn: 0.05%, Mg: 1.8-2.3%, Cr: 0.04%, Ti: 0.06%, Zr: 0.08-0.2%, Zn: 7.6-8.4%, impurities 0.1% and the balance are made of Al.
specific Embodiment approach 3
[0009] Specific Embodiment Three: In this embodiment, the weight percentage of Mg is 2.1% of the total weight of the high-strength and high-toughness 7055 aluminum alloy, that is, the high-strength and high-toughness 7055 aluminum alloy consists of Si: 0.1%, Fe: 0.15%, and Cu: 2.3% by weight percentage , Mn: 0.05%, Mg: 2.1%, Cr: 0.04%, Ti: 0.06%, Zr: 0.08-0.2%, Zn: 7.6-8.4%, impurities 0.1% and the balance are made of Al.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
strength
aaaaa
aaaaa
elongation
aaaaa
aaaaa
Login to View More
Abstract
This invention relates to a method for preparing high-strength and high-toughness 7055 Al alloy. Present 7055 Al alloy has strength of only 500 MPa, and elongation at breakage of only 5%. The high-strength and high-toughness 7055 Al alloy is prepared from: Si 0.1 wt.%, Fe 0.15 wt.%, Cu 2-2.6 wt.%, Mn 0.05 wt.%, Mg 1.8-2.3 wt.%, Cr 0.04 wt.%, Ti 0.06 wt.%, Zr 0.08-0.2 wt.%, Zn 7.6-8.4 wt.%, impurities 0.1 wt.%, and Al as balance. The strength of the high-strength and high-toughness 7055 Al alloy is greater than or equal to 610 MPa (100 MPa more than other 7055 Al alloys), and the elongation at breakage is greater than or equal to 6% (1% more than other 7055 Al alloys). The method can cast Phi 405X1000 mm and Phi 360X1000 mm ingots of the high-strength and high-toughness 7055 Al alloy.
Description
technical field [0001] The invention relates to a preparation process of aluminum alloy. Background technique [0002] The strength of the existing 7055 aluminum alloy is only about 500MPa, and the elongation rate is not more than 5%, and the specification of the ingot is small, which cannot meet the needs of the aviation and aerospace industries. The main reason for the above problems is that the composition of the existing 7055 aluminum alloy is not reasonable enough, and the preparation process of the 7055 aluminum alloy still has defects. Contents of the invention [0003] The purpose of the present invention is to provide a high-strength and high-toughness 7055 aluminum alloy to solve the problem that the strength of the existing 7055 aluminum alloy is only about 500MPa, the elongation is not more than 5%, and the specification of the ingot is small, which cannot meet the needs of the aviation and aerospace industries. Process for the preparation of aluminum alloys. ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More