3C product titanium alloy material

A technology of titanium alloys, products, applied in the field of metal materials

Inactive Publication Date: 2017-06-30
河北酷甩科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to solve the technical problem of how to popularize and apply titanium alloy materials in 3C products, and then provide a titanium alloy material for 3C products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • 3C product titanium alloy material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Take the weight percentage (wt%): Ti is 90, Fe is 0.75, C is 0.04, N is 0.05, H is 0.015, and the balance is 0. The above-mentioned 3C product titanium alloy material is obtained by using the existing technology.

Embodiment 2

[0019] Take the weight percentage (wt%): Ti is 99, Fe is 0.15, C is 0.08, N is 0.04, H is 0.01, and the balance is 0. The above-mentioned 3C product titanium alloy material is obtained by using the existing technology.

Embodiment 3

[0021] Take the weight percentage (wt%): Ti is 95, Fe is 0.5, C is 0.05, N is 0.05, H is 0.015, and the balance is 0. The above-mentioned 3C product titanium alloy material is obtained by using the existing technology.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
hardnessaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a 3C product titanium alloy material. The 3C product titanium alloy material is characterized by comprising the following components in percentage by weight (wt%): 90-99% of Ti, 0.15-0.75% of Fe, greater than or equal to 0.15% of O, less than or equal to 0.08% of C, less than or equal to 0.05% of N, and less than or equal to 0.015% of H. The 3C product titanium alloy material is mainly applied to a 3C product, has the beneficial effects of tensile strength range which is increased to be greater than or equal to 530 MPa, offset yield strength which is increased to be greater than or equal to 450 MPa, hardness which is increased to be greater than or equal to 156 HB, elongation which is increased to be greater than or equal to 16%, and the like.

Description

technical field [0001] The invention relates to the field of metal materials, in particular to a titanium alloy material suitable for making metal shells of 3C products. Background technique [0002] 3C products, also known as information appliances, generally include computers, communications, and consumer electronics. [0003] At present, the traditional metal shell of 3C products is mainly made of stainless steel or aluminum alloy; its advantage is low cost, and its disadvantage is low hardness and low quality, which can no longer meet the high-grade consumption needs of consumers. [0004] Because titanium alloy materials have high hardness, tensile strength, conditional yield strength and other characteristics, but the cost is high, they are only widely used in special industries such as medical treatment and aviation, and have not been widely used in a wide range of applications. At the same time, the titanium alloy materials prepared by the existing technology cannot...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C14/00
CPCC22C14/00
Inventor 莘飞张晓娟
Owner 河北酷甩科技有限公司
PatSnap Eureka logo

PatSnap Eureka turns technology decisions into work you can execute. Powered by our Innovation Knowledge Graph, it runs expert workflows across engineering, life sciences, materials and intellectual property. Get your review-ready output in minutes.

X (Twitter)LinkedInYouTubeSubstack

© 2026 PatSnap. All rights reserved. 

Terms of Service

 | 

Privacy policy

 | 

Modern Slavery Act Transparency Statement