A kind of processing method of wicker raw material wicker

Abstract

The invention relates to the technical field of wickerwork artware and discloses a treatment method of wickerwork raw material wickers. The method comprises the following steps that (1) newly-cut wickers are dewatered through natural drying, the high temper of the wickers is improved, heating treatment is conducted in alkaline water, thus peeling is facilitated, the glossiness of the wickers can be improved, and cold treatment is conducted after peeling; (2) the wickers subjected to cooling treatment are immediately steeped through a steeping solution A, the steeping solution can be rapidly adsorbed by fibers with negative charges under the effect of positive charges in the aqueous solution, a thin film is formed on the surface of each fiber, binding force among the fibers is reinforced, and shrinkage deformation of the fibers is prevented; and (3) the wickers are heated and baked in a drying oven after being steeped by the steeping solution A and then put into a steeping solution B for steeping, the steeping solution B has oxidation resistance and heat stability, connection points among the fibers are protected, and heating deformation of the fibers is prevented.

Description

technical field

[0001] The invention belongs to the technical field of willow weaving handicrafts, and in particular relates to a processing method for willow weaving raw material wicker. Background technique

[0002] Willow is one of the traditional Chinese folk handicrafts. In ancient times, it was only used as an ordinary daily utility, and it did not rise until the last few decades of the 20th century, and it gradually became an item for export in some parts of China. There are three willow weaving production bases in China: Shandong, Henan and Anhui. Willow weaving is a traditional national handicraft, which has established a perfect image of natural, pollution-free, high-quality and low-cost in many countries, and has increasingly shown economic value and social benefits. Willow craft products have been developed in our district for nearly 20 years. It once participated in the "Canton Fair" and obtained a final product number that has been used until now. With the ...

Examples

Embodiment 1

[0015] A processing method of willow wicker as raw material, comprising the following steps:

[0016] (1) Dry the freshly cut wicker in the sun for 2 days, bundle them into small bundles and put them in a water tank. Stir to dissolve, heat at 90°C, heat for 1 hour, cool down naturally after heating, take out the wicker, use tweezers to remove the bark of the wicker, and put the peeled wicker in an environment of minus 15°C for 8 hours ;

[0017] (2) Take out the refrigerated wicker, put it into the soaking solution A for 2 hours, the soaking solution A is made of the following ingredients in terms of mass percentage: 1.1% polyethyleneimine, 0.8% melamine formaldehyde resin, epoxy 0.6% for polyamide resin, 0.3% for polyvinyl alcohol, 0.2% for succinic acid chisulphonate, 0.1% for lignosulfonate, and the rest is water. The temperature is controlled at 5 ° C for 1 hour before soaking, and the rest is soaked The time temperature is 15°C;

[0018] (3) After soaking in soaking so...

Embodiment 2

[0022] A processing method of willow wicker as raw material, comprising the following steps:

[0023] (1) Dry the freshly cut wicker in the sun for 2 days, bundle them into small bundles and put them in a water tank. Stir to dissolve, the heating temperature is 95°C, and the heating time is 1.5 hours. After heating, cool down naturally, take out the wicker, use tweezers to remove the bark of the wicker, and put the peeled wicker in the environment of minus 12°C for 9 hours. ;

[0024] (2) Take out the refrigerated wicker, put it into the soaking solution A and soak for 2.5 hours. The soaking solution A is made of the following ingredients in terms of mass percentage: 1.15% polyethyleneimine, 0.9% melamine formaldehyde resin, epoxy 0.7% for polyamide resin, 0.4% for polyvinyl alcohol, 0.25% for succinic acid chitosulfonate, 0.15% for lignosulfonate, and the rest is water. The time temperature is 17°C;

[0025] (3) After soaking in soaking solution A, bake the wicker in an ov...

Embodiment 3

[0029] A processing method of willow wicker as raw material, comprising the following steps:

[0030] (1) Dry the freshly cut wicker in the sun for 3 days, bundle them into small bundles and put them in a water tank. Stir to dissolve, heat at 100°C, heat for 2 hours, cool down naturally after heating, take out the wicker, use tweezers to remove the bark of the wicker, and put the peeled wicker in an environment of minus 10°C for 10 hours. ;

[0031] (2) Take out the refrigerated wicker and put it into the soaking solution A for 3 hours. The soaking solution A is made of the following ingredients in terms of mass percentage: polyethyleneimine 1.2%, melamine formaldehyde resin 1.0%, epoxy resin 0.8% polyamide resin, 0.6% polyvinyl alcohol, 0.3% succinic acid chisulphonate, 0.2% lignosulfonate, and the rest is water. The temperature is controlled at 10°C for 1.5 hours before soaking, and the rest is soaked The time temperature is 20°C;

[0032] (3) After soaking in soaking sol...

technical field

[0001] The invention belongs to the technical field of willow weaving handicrafts, and in particular relates to a processing method for willow weaving raw material wicker. Background technique

[0002] Willow is one of the traditional Chinese folk handicrafts. In ancient times, it was only used as an ordinary daily utility, and it did not rise until the last few decades of the 20th century, and it gradually became an item for export in some parts of China. There are three willow weaving production bases in China: Shandong, Henan and Anhui. Willow weaving is a traditional national handicraft, which has established a perfect image of natural, pollution-free, high-quality and low-cost in many countries, and has increasingly shown economic value and social benefits. Willow craft products have been developed in our district for nearly 20 years. It once participated in the "Canton Fair" and obtained a final product number that has been used until now. With the ...

Examples

Embodiment 1

[0015] A processing method of willow wicker as raw material, comprising the following steps:

[0016] (1) Dry the freshly cut wicker in the sun for 2 days, bundle them into small bundles and put them in a water tank. Stir to dissolve, heat at 90°C, heat for 1 hour, cool down naturally after heating, take out the wicker, use tweezers to remove the bark of the wicker, and put the peeled wicker in an environment of minus 15°C for 8 hours ;

[0017] (2) Take out the refrigerated wicker, put it into the soaking solution A for 2 hours, the soaking solution A is made of the following ingredients in terms of mass percentage: 1.1% polyethyleneimine, 0.8% melamine formaldehyde resin, epoxy 0.6% for polyamide resin, 0.3% for polyvinyl alcohol, 0.2% for succinic acid chisulphonate, 0.1% for lignosulfonate, and the rest is water. The temperature is controlled at 5 ° C for 1 hour before soaking, and the rest is soaked The time temperature is 15°C;

[0018] (3) After soaking in soaking so...

Embodiment 2

[0022] A processing method of willow wicker as raw material, comprising the following steps:

[0023] (1) Dry the freshly cut wicker in the sun for 2 days, bundle them into small bundles and put them in a water tank. Stir to dissolve, the heating temperature is 95°C, and the heating time is 1.5 hours. After heating, cool down naturally, take out the wicker, use tweezers to remove the bark of the wicker, and put the peeled wicker in the environment of minus 12°C for 9 hours. ;

[0024] (2) Take out the refrigerated wicker, put it into the soaking solution A and soak for 2.5 hours. The soaking solution A is made of the following ingredients in terms of mass percentage: 1.15% polyethyleneimine, 0.9% melamine formaldehyde resin, epoxy 0.7% for polyamide resin, 0.4% for polyvinyl alcohol, 0.25% for succinic acid chitosulfonate, 0.15% for lignosulfonate, and the rest is water. The time temperature is 17°C;

[0025] (3) After soaking in soaking solution A, bake the wicker in an ov...

Embodiment 3

[0029] A processing method of willow wicker as raw material, comprising the following steps:

[0030] (1) Dry the freshly cut wicker in the sun for 3 days, bundle them into small bundles and put them in a water tank. Stir to dissolve, heat at 100°C, heat for 2 hours, cool down naturally after heating, take out the wicker, use tweezers to remove the bark of the wicker, and put the peeled wicker in an environment of minus 10°C for 10 hours. ;

[0031] (2) Take out the refrigerated wicker and put it into the soaking solution A for 3 hours. The soaking solution A is made of the following ingredients in terms of mass percentage: polyethyleneimine 1.2%, melamine formaldehyde resin 1.0%, epoxy resin 0.8% polyamide resin, 0.6% polyvinyl alcohol, 0.3% succinic acid chisulphonate, 0.2% lignosulfonate, and the rest is water. The temperature is controlled at 10°C for 1.5 hours before soaking, and the rest is soaked The time temperature is 20°C;

[0032] (3) After soaking in soaking sol...