Lightweight anti-radiation nano thermal insulation material and preparation method thereof

Abstract

The invention relates to a lightweight anti-radiation nanometer heat insulation material and a preparation method thereof. The method comprises the following steps: preparing a nanometer oxide dispersion liquid; uniformly mixing the oxide dispersion liquid and an adsorbent through high-speed shear stirring and ultrasonic treatment to obtain a mixed solution; placing the solution in a closed container for high-temperature hydrothermal reaction to obtain a semi-solid gel block; fully mixing the semi-solid gel block, the hydrophobic silicon carbide nano powder, the chopped fibers and the glass powder, and mechanically stirring to form mixed slurry; then extrusion forming is conducted through a mold, the steps of aftertreatment, aging and drying are conducted, and finally the graded heat treatment process is conducted to prepare the light anti-radiation nanometer heat insulation material. According to the preparation method, the light anti-radiation nano thermal insulation material with good temperature resistance and low density can be obtained.

Description

Technical Field

[0001] The invention relates to the technical field of aerogel preparation, and in particular to a lightweight radiation-resistant nano thermal insulation material and a preparation method thereof. Background Art

[0002] Nanoporous aerogel (abbreviated as aerogel) is a gel material whose dispersion medium is gas. It is a nanoporous solid material with a network structure composed of colloidal particles or polymer molecules. The size of the pores in the material is in the nanometer order of magnitude. At present, the most widely used field of aerogel is still the field of thermal insulation, because the unique nanostructure of aerogel can effectively reduce convection conduction, solid phase conduction and thermal radiation.

[0003] Most traditional aerogel materials are pearl necklace-like structures formed by the accumulation of nanoparticles. Aerogel materials with this structure are brittle and require fiber reinforcement to achieve structural strengthening in practical applications. However, the fiber reinforcement process will increase the density, increase the solid-phase thermal conductivity and increase the complexity of the process. In addition, there are some skeleton strengthening methods to prepare pure phase aerogel materials with good structural strength. However, this method often requires a high-temperature sintering process to increase the skeleton size to improve the strength of the material, which will bring new problems such as high thermal conductivity and high brittleness. Nanocellulose can be used to prepare nanocellulose aerogels with certain structural strength and toughness to a certain extent. However, the organic component determines that its temperature resistance is poor and is not suitable for thermal insulation applications. Therefore, it is of great significance to develop a nano aerogel material with good structural strength and toughness. The patent applied for by the inventor is " Alumina nanowire aerogel thermal insulation material and preparation method thereof (CN202010669268.X)" uses a hydrothermal method to prepare an alumina nanowire precursor solution containing acidic silica sol and boric acid, and achieves the preparation of alumina nanowire aerogel through freeze drying and heat treatment processes. The aerogel prepared by freeze drying in this preparation method has larger pores and no secondary structure is constructed, so its gas phase heat conduction is larger.

[0004] With the development of science and technology, various fields have put forward higher requirements on the strength, temperature resistance, lightness and thermal insulation performance of thermal insulation materials. Especially in high temperature environments, radiation heat transfer dominates. Therefore, it is very necessary to develop an effective method to prepare a lightweight, high-strength, radiation-resistant nano thermal insulation material. Inspired by the microstructure of shells, the present invention constructs a brick-sand structure, with alumina nanowires as bricks and silicon carbide nanopowder as sand. This special microstructure determines that its macroscopic structure can show high strength and infrared radiation resistance. Summary of the invention

[0005] In order to solve the technical problems existing in the prior art, the present invention provides a nano thermal insulation material with simple preparation process, good high temperature resistance, light weight and radiation resistance, and a preparation method thereof.

[0006] In a first aspect, the present invention provides a method for preparing a lightweight radiation-resistant nano thermal insulation material, the method comprising the following steps:

[0007] (1) mixing aluminum oxide nanopowder and an acidic solution in deionized water, and obtaining a uniform mixed solution by high-speed shear stirring and ultrasonic treatment;

[0008] The specific steps are as follows: dissolving aluminum oxide nanopowder with a diameter distribution of 10 to 100 nm in water, adding sulfuric acid solution of 1% of the total solution mass, the concentration range of the sulfuric acid solution is 0.1 to 30 mol / L, and the mass fraction of the aluminum oxide nanopowder in the mixed solution is 5% to 20%;

[0009] (2) placing the mixed solution in a sealed container and performing a hydrothermal reaction at 150 to 300° C. for 1 to 48 hours to obtain a semi-solid gel block;

[0010] The specific steps are as follows: the reaction must be carried out under fully closed conditions, and the container material must be a polymer material that does not react with the system;

[0011] (3) adding hydrophobic nano-silicon carbide, chopped fibers and glass powder to the gel block, mixing them thoroughly, and forming a mixed slurry by mechanical stirring;

[0012] The specific steps are: the gel block obtained in step 2, chopped fibers (5% to 50% of the mass of the gel block) and glass powder (1% to 20% of the mass of the gel block) are first fully mixed for 0.1 to 4 hours, and then the hydrophobic nano-silicon carbide is added, and the mixing is continued for 0.1 to 4 hours to obtain a mixed slurry;

[0013] (4) shaping the mixed slurry obtained in step (3) using a mold as required;

[0014] The specific steps are as follows: adding the mixed slurry into a metal mold coated with a release agent, flattening and filling the material body with a tool, then closing the mold, applying a certain pressure to achieve shaping, and the pressure is controlled at 0.1-5MPa;

[0015] (5) subjecting the shaped block to a solvent replacement process and a supercritical drying step to obtain a preform;

[0016] The specific steps are: using ethanol as a solvent for solvent replacement, the amount of solvent used is 8 to 10 times the volume of the gel block after shaping, the replacement times are 3 to 5 times, and after the solvent replacement process is completed, a carbon dioxide supercritical drying process is performed, the supercritical drying temperature is 20 to 60°C, and the pressure is 10 to 16Mpa;

[0017] (6) performing graded heat treatment on the prefabricated parts to obtain a lightweight radiation-resistant nano thermal insulation material;

[0018] The specific steps are: heat treating the prefabricated parts under an inert atmosphere at a temperature of 600° C. for a time of 0.5 to 2 hours, and then continuing to heat the prefabricated parts to 1000 to 1200° C. for a time of 0.5 to 2 hours.

[0019] The above steps realize the preparation of a lightweight radiation-resistant nano thermal insulation material.

[0020] In a second aspect, the present invention provides a lightweight radiation-resistant nano thermal insulation material prepared by the preparation method described in the first aspect of the present invention.

[0021] Compared with the prior art, the present invention has at least the following beneficial effects:

[0022] (1) Compared with traditional pearl necklace-shaped aerogel materials, the present invention has better mechanical strength. Inspired by the microstructure of shells, the "brick-sand" structure constructed by the present invention is composed of nanowires entangled with each other, and glass powder is used as an adhesive to form bonding nodes at the overlap of nanofibers, greatly improving the structural strength of the material.

[0023] (2) The present invention adopts a multi-level structure assembled from three structures of micron fiber, nanofiber and nanoparticle as basic units. The hydrophobic nanoparticles form clusters similar to emulsions during the mixing process. The nanoparticles increase the solid phase heat conduction path and reduce the gas phase heat conduction. The nanofiber skeleton acts as a good support and can achieve a high-efficiency heat insulation effect under the condition of radiation resistance.

[0024] (3) The density of the aerogel material prepared by the present invention can be as low as 0.12 g / cm 3 , compared with other low-density aerogel materials of the same strength, it has the characteristics of ultra-low density.

[0025] (4) The gelation process in the aerogel preparation method of the present invention is a hydrothermal process. Different from the traditional RTM pressure injection process, it is not limited by the shape and size of the reinforcement and can prepare aerogel materials of any shape and thickness.

[0026] (5) The aerogel material obtained in the preparation process of the present invention from gelation, post-treatment process to supercritical drying does not have any dimensional shrinkage, and the net size molding of the product can be achieved, avoiding the cost and cycle increase caused by the mechanical processing process.

[0027] (6) In the present invention, the alumina nanowire solution, glass powder and ceramic fiber are first dispersed into an aqueous solution, and hydrophobic nano-silicon carbide is used as a hydrophobic dispersed phase to achieve two controllable components, realize the selective bonding of the glass powder, and ensure the efficient thermal insulation of the nanoparticles on the material.

[0028] (7) The aerogel material prepared by the method of the present invention adopts a segmented heat treatment process, which slows down the crystal transformation process of the material, avoids the structural collapse of the porous structure during rapid shrinkage, and achieves the strengthening of the microstructure of the aerogel material, which is conducive to the formation of the silicon-aluminum composite phase and the stabilization of the nano-skeleton.

[0029] (8) The doped silicon carbide nanoparticles of the present invention exist in the form of hydrophobic particle clusters, which can effectively resist the effects of infrared radiation and greatly improve the high-temperature thermal insulation performance of the thermal insulation material.

[0030] (9) The aerogel material prepared by the method of the present invention has excellent high temperature resistance while maintaining a low thermal conductivity of less than 0.026 W / mK, and can be used for long-term thermal insulation at 1100°C.

[0031] (10) The porosity of the nanowire aerogel material prepared by the method of the present invention is above 98%, the pore size is 5 to 500 nm, the diameter of the nanowire of the aerogel is 30 to 200 nm, and the specific surface area at high temperature is 100 to 600 m 2 / g, the heat resistance temperature is above 1100℃, and the high temperature thermal conductivity is as low as 0.055W / mK. BRIEF DESCRIPTION OF THE DRAWINGS

[0032] Figure 1 It is a preparation flow chart of the present invention.

[0033] Figure 2 This is a schematic diagram of the structure of the shell-like "brick sand" prepared by the present invention

[0034] Figure 3 This is a SEM image of the nanowire portion prepared in Example 1. DETAILED DESCRIPTION

[0035] In order to make the purpose, technical solution and advantages of the present invention clearer, the technical solution of the present invention will be clearly and completely described below in combination with the embodiments of the present invention. Obviously, the described embodiments are part of the embodiments of the present invention, not all of the embodiments. Based on the embodiments of the present invention, all other embodiments obtained by ordinary technicians in this field without making creative work are within the scope of protection of the present invention.

[0036] The present invention will be further described below by way of examples, but the protection scope of the present invention is not limited to these embodiments.

[0037] Example 1

[0038] (1) mixing aluminum oxide nanopowder and an acidic solution in deionized water, and obtaining a uniform mixed solution by high-speed shear stirring and ultrasonic treatment;

[0039] The specific steps are as follows: dissolving aluminum oxide nanopowder with a diameter distribution of 10 to 15 nm in water, adding sulfuric acid solution of 1% of the total solution mass, the concentration of the sulfuric acid solution is 10 mol / L, and the mass fraction of aluminum oxide nanopowder in the mixed solution is 8%;

[0040] (2) placing the mixed solution in a sealed container and performing a hydrothermal reaction at 230° C. for 5 h to obtain a semi-solid gel block;

[0041] The specific steps are as follows: the reaction must be carried out under fully closed conditions, and the container material must be a polymer material that does not react with the system;

[0042] (3) adding hydrophobic nano-silicon carbide, chopped fibers and glass powder to the gel block, mixing them thoroughly, and forming a mixed slurry by mechanical stirring;

[0043] The specific steps are as follows: the gel block, chopped fibers (10% of the mass of the gel block) and glass powder (10% of the mass of the gel block) obtained in step 2 are first fully mixed for 0.1 to 4 hours, and then hydrophobic nano silicon carbide (3% of the mass of the gel block, chopped fibers and glass powder) is added, and the mixing is continued for 0.1 to 4 hours to obtain a mixed slurry;

[0044] (4) shaping the mixed slurry obtained in step (3) using a mold as required;

[0045] The specific steps are as follows: adding the mixed slurry into a metal mold coated with a release agent, flattening and filling the material body with a tool, then closing the mold, applying a certain pressure to achieve shaping, and the pressure is controlled at 0.9-1.1MPa;

[0046] (5) subjecting the shaped block to a solvent replacement process and a supercritical drying step to obtain a preform;

[0047] The specific steps are as follows: using ethanol as solvent for solvent replacement, the amount of solvent used is 10 times the volume of the gel block after shaping, the replacement times are 3 times, and after the solvent replacement process is completed, a carbon dioxide supercritical drying process is performed, the supercritical drying temperature is 40°C, and the pressure is 15Mpa;

[0048] (6) performing graded heat treatment on the prefabricated parts to obtain a lightweight radiation-resistant nano thermal insulation material;

[0049] The specific steps are: heat treating the prefabricated parts under an inert atmosphere at a temperature of 600° C. for 2 h, and then continuing to heat the prefabricated parts to 1100° C. for 2 h.

[0050] The lightweight anti-radiation nano thermal insulation material prepared in Example 1 has good structural strength. The thermal insulation performance of the lightweight anti-radiation nano thermal insulation material in Example 1 was tested and found to have no Loss of Light ,none Discoloration , no falling off, other performance indicators are shown in Table 1.

[0051] Example 2

[0052] Example 2 is substantially the same as Example 1, except that: during the preparation of the dispersion in step 1, no glass powder is added.

[0053] The strength of the nano thermal insulation material prepared in Example 2 is slightly weaker than that in Example 1, but it can also form a complete block. Other performance indicators are shown in Table 1.

[0054] Example 3

[0055] Example 3 is basically the same as Example 1, except that: during the preparation of the dispersion in step 1, 10 mol / L acetic acid solution is added to account for 1% of the total solution mass.

[0056] The strength of the nano thermal insulation material prepared in Example 3 is relatively weak and no relatively complete block is formed. Other performance indicators are shown in Table 1.

[0057] Example 4

[0058] Example 4 is substantially the same as Example 1, except that during the preparation of the nano-dispersion solution in step 1, 0.5% of the total solution mass of a 10 mol / L sulfuric acid solution is added.

[0059] The nano thermal insulation material in Example 4 has weak strength and powdering phenomenon. Other performance indicators are shown in Table 1.

[0060] Example 5

[0061] Example 5 is basically the same as Example 1, except that no chopped fibers are added during the mixing process with the gel block to obtain an aerogel-based thermal insulation material.

[0062] The aerogel-based thermal insulation material in Example 5 is relatively strong but brittle. Other performance indicators are shown in Table 1.

[0063] Example 6

[0064] Example 6 is basically the same as Example 1, except that no nano-silicon carbide is added during the mixing process with the gel block to obtain an aerogel-based thermal insulation material.

[0065] The aerogel-based thermal insulation material in Example 6 has relatively strong strength, and other performance indicators are shown in Table 1.

[0066] Example 7

[0067] Example 7 is basically the same as Example 1, except that hydrophilic nano-silicon carbide is added during the mixing process with the gel block instead of hydrophobic nano-silicon carbide to obtain an aerogel-based thermal insulation material.

[0068] The aerogel-based thermal insulation material in Example 7 has a relatively strong strength, and a thermal insulation performance test was conducted, and it was found that its thermal conductivity was relatively high. Other performance indicators are shown in Table 1.

[0069] Example 8

[0070] Example 8 is substantially the same as Example 1, except that no graded heat treatment is performed to obtain an aerogel-based thermal insulation material.

[0071] The aerogel-based thermal insulation material in Example 8 can maintain structural integrity, but does not have high strength characteristics. Other performance indicators are shown in Table 1.

[0072] Example 9

[0073] Example 9 is substantially the same as Example 1, except that the solvent replacement process in step 4 is not performed to obtain an aerogel-based thermal insulation material.

[0074] The thermal insulation performance of the nano-aerogel material in Example 9 was tested, and it was found that the aerogel was powdered and difficult to shape. Other performance indicators are shown in Table 1.

[0075] Example 10

[0076] Example 10 is basically the same as Example 1, except that the supercritical drying process in step 4 is not performed, and normal pressure drying is performed instead to obtain the nanowire aerogel material.

[0077] The nano aerogel material in Example 10 has a larger shrinkage and a higher density. Other performance indicators are shown in Table 1.

[0078] Comparative Example 1: "A high temperature resistant and high toughness nanowire aerogel material and its preparation method ( CN202210563030.8 )”

[0079] ① Aluminum oxide nanopowder with a particle size range of 10-15 nm, boron nitride nanosheets with a particle size range of 1-2 μm and a thickness range of 60-120 nm, and a sulfuric acid solution with a concentration of 10 mol / L are mixed in deionized water, and mixed evenly by stirring and ultrasonication to obtain a mixed solution; in the mixed solution, the mass percentage of the aluminum oxide nanopowder is 8%, the mass percentage of the boron nitride nanosheets is 2%, and the amount of the sulfuric acid solution accounts for 1% of the total weight of the mixed solution.

[0080] ② Place the above mixed solution in a sealed container and perform hydrothermal reaction at 230°C for 15 hours to obtain a semi-solid gel.

[0081] ③ The gel was immersed in a silica sol solution for 24 hours, and then the block was placed in a sealed container and aged in a 90°C oven for 24 hours; during the immersion, the liquid surface of the silica sol solution was made to cover the gel; the silica sol solution was prepared as follows: the mass ratio of acidic silica sol to ammonium fluoride solution was 100:4, and the ammonium fluoride solution was added to the acidic silica sol and mixed for 2 hours to obtain a silica sol solution with a solid content of 10%, and the concentration of the ammonium fluoride solution was 1.5 mol / L.

[0082] ④ The treated gel block obtained in step ③ is subjected to a solvent replacement process and a supercritical drying step to obtain a boron nitride-doped nanowire aerogel material; the specific steps are: ethanol is used as the solvent for solvent replacement, and the replacement is performed 3 times according to 10 times the volume of the gel block, and then a supercritical carbon dioxide drying process is performed, and the supercritical drying temperature is 50°C and the pressure is 14MPa.

[0083] ⑤ The boron nitride-doped nanowire aerogel material is heat-treated in an inert atmosphere at a temperature of 1150° C. for 0.5 h to obtain a high-temperature resistant and high-strength nanowire aerogel material.

[0084] Table 1: Performance indicators of a lightweight radiation-resistant nano thermal insulation material prepared in Examples 1 to 10 and the thermal insulation material of the comparative example.

[0085]

[0086] Finally, it should be noted that the above embodiments are only used to illustrate the technical solutions of the present invention, rather than to limit it. Although the present invention has been described in detail with reference to the aforementioned embodiments, those skilled in the art should understand that they can still modify the technical solutions described in the aforementioned embodiments, or make equivalent replacements for some of the technical features therein. However, these modifications or replacements do not deviate the essence of the corresponding technical solutions from the spirit and scope of the technical solutions of the embodiments of the present invention.

Claims

1. A method for preparing a lightweight radiation-resistant nano thermal insulation material, characterized in that The method comprises the following steps: (1) mixing aluminum oxide nanopowder and an acidic solution in deionized water, and obtaining a uniform mixed solution by high-speed shear stirring and ultrasonic treatment; (2) placing the mixed solution in a sealed container and performing a hydrothermal reaction at 150 to 300° C. for 1 to 48 hours to obtain a semi-solid gel block; (3) adding hydrophobic nano-silicon carbide, chopped fibers and glass powder to the gel block, mixing them thoroughly, and forming a mixed slurry by mechanical stirring; (4) shaping the mixed slurry obtained in step (3) using a mold as required; (5) performing a solvent replacement process and a supercritical drying process on the shaped block to obtain a preform; (6) The prefabricated parts are subjected to a graded heat treatment process to obtain a lightweight radiation-resistant nano thermal insulation material.

2. The preparation method according to claim 1, wherein in step (1), aluminum oxide nanopowder having a diameter distribution in the range of 10 to 100 nm is dissolved in water, and a sulfuric acid solution accounting for 1% of the total solution mass is added, the concentration range of the sulfuric acid solution is 0.1 to 30 mol / L, and the mass fraction of the aluminum oxide nanopowder in the obtained mixed solution is 5% to 20%.

3. According to the preparation method of claim 1, in step (2), the reaction must be carried out under fully closed conditions, and the container material is a polymer material that does not react with the system.

4. The preparation method according to claim 1, in step (3), the gel block obtained in step (2) is first fully mixed with the chopped fibers and glass powder for 0.1 to 4 hours, and then the hydrophobic nano-silicon carbide is added and the mixing is continued for 0.1 to 4 hours to obtain a mixed slurry.

5. The preparation method according to claim 1, in the corresponding step (4), the mixed slurry obtained in step (3) is added to a metal mold coated with a release agent, the material body is flattened and filled with a tool, and then the mold is closed and a certain pressure is applied to achieve shaping, and the pressure is controlled at 0.1 to 5 MPa.

6. The preparation method according to claim 1, wherein in step (5), ethanol is used as the solvent for solvent replacement, the amount of the solvent used is 8 to 10 times the volume of the block after shaping, the number of replacements is 3 to 5 times, and after the solvent replacement process is completed, a carbon dioxide supercritical drying process is performed, the supercritical drying temperature is 20 to 60° C., and the pressure is 10 to 16 MPa.

7. The preparation method according to claim 1, wherein in step (6), a graded heat treatment process is performed, wherein the treatment system is in an inert atmosphere, the treatment temperature is 600°C, the treatment time is 0.5 to 2 hours, and then the temperature is continued to rise to 1000 to 1200°C, and the treatment time is 0.5 to 2 hours.

8. A lightweight radiation-resistant nano thermal insulation material, which is obtained by the preparation method according to any one of claims 1 to 7, wherein the minimum density of the prepared thermal insulation material can reach 0.12 g / cm 3 The porosity is above 98%, the pore size is 5-500nm, and the nanowire diameter is 30-200nm. When the low thermal conductivity is maintained at less than 0.026W / mK, it can achieve long-term 1100℃ thermal insulation application. The specific surface area at high temperature is 100-600m 2 / g, the heat resistance temperature is above 1100℃, and the high temperature thermal conductivity is as low as 0.055W / mK.