Chlorosulfonated polyethylene voltage-resistance and high-performance special anticorrosive paint and production method thereof

Abstract

The invention discloses chlorosulfonated polyethylene voltage-resistance and high-performance special anticorrosive paint. The paint comprises chlorosulfonated polyethylene, acrylic polyurethane, high chlorinated potyethlene, dimethylbenzene, titanium white chloridization, phthalo blue, phthalo green, ironoxidered, ultramarine, o-xylene, mica sheet, zinc powder and the like. The production method comprises the following steps: ingredients are stirred, rolled and mixed; produced copolymerized grease adhesive tapes are prepared to copolymerized grease adhesive sheets by a slicer; and after being totally added in a reaction kettle to react for a certain time, all raw materials are filtered and packaged to obtain finished products after the inspection thereof is qualified. The product has the characteristics of easy production method, long anticorrosive protection period, unique performances of resisting ultraviolet rays, water, oil, cold, acid, alkali and salt, resistance to low temperature of -60 DEG C, resistance to voltage of 20,000 V, excellent insulation performance, excellent wear and impact resistance, good flexibility, strong adhesion and long service life. The paint is suitable for protective coating of facilities and equipment in various power industries.

Description

1. Technical field

[0001] The invention relates to an anti-corrosion coating and a production method thereof, in particular to a special anti-corrosion coating of chlorosulfonated polyethylene with high voltage resistance and high performance and a production method thereof. 2. Background technology

[0002] The electric power industry originated in the late 19th century and has achieved rapid development for more than 100 years since its birth. Electricity has become the lifeblood of the development of the national economy, and the development of the electric power industry reflects the development of the national economy. With the development of the power industry, more and more power facilities are used. Most of the power facilities operate outdoors, and they are exposed to wind, sun, and rain for a long time, as well as pollution from emissions such as dust, sulfur dioxide, and nitrogen oxides in the atmosphere, as well as pollution and corrosion such as acid rain, light...

Examples

Embodiment Construction

[0013] The present invention is a chlorosulfonated polyethylene anti-voltage high-performance special anti-corrosion coating. The components of the anti-corrosion coating are: 50 kg of chlorosulfonated polyethylene, 20 kg of acrylic polyurethane, 50 kg of high-chlorinated polyethylene, 500 kg of xylene, and chlorination method Titanium dioxide 49.8kg, phthalocyanine blue 5kg, phthalocyanine green 5kg, iron red powder 30kg, ultramarine 5.2kg, o-xylene 200kg, mica flakes 25kg, zinc powder 30kg, n-butanol 15kg, turpentine 15kg.

[0014] Implement the production method of product of the present invention to be:

[0015] 1. First, add chlorosulfonated polyethylene, acrylic polyurethane, and high-chlorinated polyethylene to 40kg of xylene to dissolve to make a liquid material. Pour each liquid material into the preparation kettle and mix for 20 minutes to make it react.

[0016] 2. Pour the prepared liquid material into the hot mixer for rolling and mixing. At the same time, add chl...

1. Technical field

[0001] The invention relates to an anti-corrosion coating and a production method thereof, in particular to a special anti-corrosion coating of chlorosulfonated polyethylene with high voltage resistance and high performance and a production method thereof. 2. Background technology

[0002] The electric power industry originated in the late 19th century and has achieved rapid development for more than 100 years since its birth. Electricity has become the lifeblood of the development of the national economy, and the development of the electric power industry reflects the development of the national economy. With the development of the power industry, more and more power facilities are used. Most of the power facilities operate outdoors, and they are exposed to wind, sun, and rain for a long time, as well as pollution from emissions such as dust, sulfur dioxide, and nitrogen oxides in the atmosphere, as well as pollution and corrosion such as acid rain, light...

Examples

Embodiment Construction

[0013] The present invention is a chlorosulfonated polyethylene anti-voltage high-performance special anti-corrosion coating. The components of the anti-corrosion coating are: 50 kg of chlorosulfonated polyethylene, 20 kg of acrylic polyurethane, 50 kg of high-chlorinated polyethylene, 500 kg of xylene, and chlorination method Titanium dioxide 49.8kg, phthalocyanine blue 5kg, phthalocyanine green 5kg, iron red powder 30kg, ultramarine 5.2kg, o-xylene 200kg, mica flakes 25kg, zinc powder 30kg, n-butanol 15kg, turpentine 15kg.

[0014] Implement the production method of product of the present invention to be:

[0015] 1. First, add chlorosulfonated polyethylene, acrylic polyurethane, and high-chlorinated polyethylene to 40kg of xylene to dissolve to make a liquid material. Pour each liquid material into the preparation kettle and mix for 20 minutes to make it react.

[0016] 2. Pour the prepared liquid material into the hot mixer for rolling and mixing. At the same time, add chl...