Colored high-titanium heavy slag self-cleaning water permeable brick and manufacturing method thereof

Abstract

The invention discloses a colored high-titanium heavy slag self-cleaning water permeable brick. After carbonization treatment, carbonized pea stalk is ground at room temperature; the pore surface adsorbs a photocatalytic material nanometer titania; and light irradiation is conducted to generate hydroxyl radical, super-oxygen ion free radical and H2O free radical which have strong capacity of oxidization and decomposition to directly oxidize various organic matter into inorganic micomolecules such as CO2 and H2O, etc. By applying the above product into a water permeable brick, the obtained water permeable brick can degrade automobile exhaust and the like in the atmosphere. In addition, the water permeable brick has strong adsorbability and excellent sound-absorption and noise-reduction effects. According to the invention, modified sugar filter mud is used as a pore-forming agent, and high-titanium heavy slag, slag from a power plant and hemihydrate gypsum are used as aggregates. The water permeable brick prepared after high-temperature sintering of the materials has large porosity, excellent self-cleaning effect, good water permeability and high compressive strength. In addition, cost of raw materials is low, and environmental pollution caused by blast furnace slag is also avoided. The water permeable brick can be paved on plazas or sidewalk.

Description

technical field

[0001] The invention relates to the technical field of building materials, in particular to a colored high-titanium heavy slag self-cleaning permeable brick and a manufacturing method thereof. Background technique

[0002] With the continuous shortage of urban water resources and the pursuit of humanization of the urban environment, the research and development of permeable bricks has attracted extensive attention from experts in materials, environment and municipal engineering. Permeable bricks have good water permeability and moisture retention, which can well alleviate the "urban desertification" and "heat island effect" caused by the city being covered by non-permeable ground pavement. It can also alleviate urban waterlogging to a certain extent and replenish urban groundwater. , regulate the urban environment, and help maintain the urban water balance. Existing permeable bricks are developing towards high density and high strength, and their compressive...

Examples

Embodiment Construction

[0012] A colored high-titanium heavy slag self-cleaning permeable brick, made of the following raw materials in parts by weight: high-titanium heavy slag sand 30, power plant waste 25, sugar filter mud 18, hemihydrate gypsum 13, expanded vitrified beads 6, colored Cement 10, Magnesium Oxide 1, Linseed Oil 3, Ferrocene 1.2, Brown Sugar Residue 5, Nano Titanium Dioxide 0.6, Pea Straw 7, Appropriate amount of water.

[0013] The manufacturing method of a colored high-titanium heavy slag self-cleaning permeable brick includes the following steps:

[0014] (1) Dry the pea stalks and place them in a carbonization furnace at a temperature of 450°C, carbonize for 20 minutes without air, cool to room temperature, add nano-titanium dioxide, and brown sugar slag to grind for 40 minutes;

[0015] (2) After washing the sugar filter mud, dry it at 50°C, put it into a high-speed mixer, add linseed oil, ferrocene and an appropriate amount of water, stir it at a high speed of 1400 rpm for 15 m...

technical field

[0001] The invention relates to the technical field of building materials, in particular to a colored high-titanium heavy slag self-cleaning permeable brick and a manufacturing method thereof. Background technique

[0002] With the continuous shortage of urban water resources and the pursuit of humanization of the urban environment, the research and development of permeable bricks has attracted extensive attention from experts in materials, environment and municipal engineering. Permeable bricks have good water permeability and moisture retention, which can well alleviate the "urban desertification" and "heat island effect" caused by the city being covered by non-permeable ground pavement. It can also alleviate urban waterlogging to a certain extent and replenish urban groundwater. , regulate the urban environment, and help maintain the urban water balance. Existing permeable bricks are developing towards high density and high strength, and their compressive...

Examples

Embodiment Construction

[0012] A colored high-titanium heavy slag self-cleaning permeable brick, made of the following raw materials in parts by weight: high-titanium heavy slag sand 30, power plant waste 25, sugar filter mud 18, hemihydrate gypsum 13, expanded vitrified beads 6, colored Cement 10, Magnesium Oxide 1, Linseed Oil 3, Ferrocene 1.2, Brown Sugar Residue 5, Nano Titanium Dioxide 0.6, Pea Straw 7, Appropriate amount of water.

[0013] The manufacturing method of a colored high-titanium heavy slag self-cleaning permeable brick includes the following steps:

[0014] (1) Dry the pea stalks and place them in a carbonization furnace at a temperature of 450°C, carbonize for 20 minutes without air, cool to room temperature, add nano-titanium dioxide, and brown sugar slag to grind for 40 minutes;

[0015] (2) After washing the sugar filter mud, dry it at 50°C, put it into a high-speed mixer, add linseed oil, ferrocene and an appropriate amount of water, stir it at a high speed of 1400 rpm for 15 m...