Phosphatized cold-rolled strip steel and manufacturing method thereof

Abstract

The invention provides a phosphatized cold-rolled strip steel and a manufacturing method thereof. The phosphatized cold-rolled strip steel is composed of, by mass: 0.01-0.10% of C, 0.1-0.6% of Mn, less than or equal to 0.10% of Si, less than or equal to 0.10% of Al, less than or equal to 0.02% of P, less than or equal to 0.015% of S, and the balance Fe and impurity elements. Phosphating treatmentequipment is additionally arranged between a leveling straightening machine and an oiling machine of a continuous annealing unit; the phosphating treatment equipment consists of a phosphating section,a rinsing section and a drying box; after the strip steel is uncoiled, the strip steel enters a phosphating treatment area after being subjected to conventional treatment such as welding, cleaning, annealing, flattening and tension straightening; and the strip steel after the phosphating treatment is directly coiled into a coil without oiling. According to production of the cold-rolled phosphatized coil, the production process of the client side is simplified, the efficiency is improved, the phosphating quality is improved, and the problem that the phosphating effect is influenced due to unthorough degreasing and cleaning of the client terminal is solved.

Description

technical field

[0001] The invention belongs to the technical field of iron and steel production, in particular to a phosphating cold-rolled steel strip and a manufacturing method. Background technique

[0002] Cold-rolled strip steel has the advantages of good surface finish, good flatness, high dimensional accuracy, and good mechanical properties. It can be used to make oil barrels and containers, and can also be used to manufacture building panels, office supply cabinets, and electronic machinery. However, after processing and forming and before coating, the cold-rolled strip steel needs to be phosphating. Surface phosphating treatment is an extremely important process in the manufacturing process of steel drums, such as steel coil uncoiling and blanking, stamping and forming of drum bottom cover, welding and forming assembly of drum body, surface phosphating, internal and external coating, etc. Phosphating is the process in which metal reacts with dilute phosphoric acid...

Examples

Embodiment 1

[0036] The chemical composition of steel for oil barrels is: C 0.030%, Mn 0.40%, Si 0.01%, Al 0.05%, P 0.018%, S 0.0035%, and the balance is Fe and impurity elements.

[0037] The strip steel whose chemical composition meets the above requirements is subjected to conventional treatments such as decoiling, welding, degreasing cleaning, annealing, leveling and tension leveling on the continuous annealing line. was 1.4%. After the treatment, enter the phosphating treatment area, first enter the phosphating section for phosphating treatment, the phosphating section adopts a spray process, the pH value of the phosphating solution is 2.2, the phosphating time is 41s, and the temperature of the phosphating solution is 42°C. The phosphating solution is composed of the following components: zinc dihydrogen phosphate 80g / L, zinc nitrate 69g / L, phosphoric acid 15g / L, sodium chlorate 1.9g / L, tartaric acid 5.8g / L, sodium fluoride 1.5g / L, sulfuric acid Hydroxylamine 2.2g / L, phytic acid 1.7...

Embodiment 2

[0041] The chemical composition of steel for oil barrels is: C 0.040%, Mn 0.20%, Si 0.018%, Al 0.027%, P 0.005%, S 0.011%, and the balance is Fe and impurity elements.

[0042]The strip steel whose chemical composition meets the above requirements is subjected to conventional treatments such as decoiling, welding, degreasing cleaning, annealing, leveling and tension leveling on the continuous annealing line. was 1.1%. After the treatment, enter the phosphating treatment area, first enter the phosphating section for phosphating treatment, the phosphating section adopts a spray process, the pH value of the phosphating solution is 2.8, the phosphating time is 49s, and the temperature of the phosphating solution is 45°C. The phosphating solution is composed of the following components: zinc dihydrogen phosphate 65g / L, zinc nitrate 78g / L, phosphoric acid 11g / L, sodium chlorate 1.3g / L, tartaric acid 6.8g / L, sodium fluoride 1.9g / L, sulfuric acid Hydroxylamine 1.1g / L, phytic acid 1.2...

Embodiment 3

[0046] The chemical composition of steel for oil barrels is: C 0.035%, Mn 0.30%, Si 0.04%, Al 0.01%, P 0.012%, S 0.0047%, and the balance is Fe and impurity elements.

[0047] The steel strip whose chemical composition meets the above requirements is subjected to conventional treatments such as uncoiling, welding, degreasing cleaning, annealing, leveling and tension leveling on the continuous annealing line. was 1.2%. After the treatment, enter the phosphating treatment area, first enter the phosphating section for phosphating treatment, the phosphating section adopts a spraying process, the pH value of the phosphating solution is 2.5, the phosphating time is 49s, and the temperature of the phosphating solution is 48°C. The phosphating solution is composed of the following components: zinc dihydrogen phosphate 97g / L, zinc nitrate 52g / L, phosphoric acid 18g / L, sodium chlorate 3.0g / L, tartaric acid 5.4g / L, sodium fluoride 1.2g / L, sulfuric acid Hydroxylamine 1.7g / L, phytic acid ...

technical field

[0001] The invention belongs to the technical field of iron and steel production, in particular to a phosphating cold-rolled steel strip and a manufacturing method. Background technique

[0002] Cold-rolled strip steel has the advantages of good surface finish, good flatness, high dimensional accuracy, and good mechanical properties. It can be used to make oil barrels and containers, and can also be used to manufacture building panels, office supply cabinets, and electronic machinery. However, after processing and forming and before coating, the cold-rolled strip steel needs to be phosphating. Surface phosphating treatment is an extremely important process in the manufacturing process of steel drums, such as steel coil uncoiling and blanking, stamping and forming of drum bottom cover, welding and forming assembly of drum body, surface phosphating, internal and external coating, etc. Phosphating is the process in which metal reacts with dilute phosphoric acid...

Examples

Embodiment 1

[0036] The chemical composition of steel for oil barrels is: C 0.030%, Mn 0.40%, Si 0.01%, Al 0.05%, P 0.018%, S 0.0035%, and the balance is Fe and impurity elements.

[0037] The strip steel whose chemical composition meets the above requirements is subjected to conventional treatments such as decoiling, welding, degreasing cleaning, annealing, leveling and tension leveling on the continuous annealing line. was 1.4%. After the treatment, enter the phosphating treatment area, first enter the phosphating section for phosphating treatment, the phosphating section adopts a spray process, the pH value of the phosphating solution is 2.2, the phosphating time is 41s, and the temperature of the phosphating solution is 42°C. The phosphating solution is composed of the following components: zinc dihydrogen phosphate 80g / L, zinc nitrate 69g / L, phosphoric acid 15g / L, sodium chlorate 1.9g / L, tartaric acid 5.8g / L, sodium fluoride 1.5g / L, sulfuric acid Hydroxylamine 2.2g / L, phytic acid 1.7...

Embodiment 2

[0041] The chemical composition of steel for oil barrels is: C 0.040%, Mn 0.20%, Si 0.018%, Al 0.027%, P 0.005%, S 0.011%, and the balance is Fe and impurity elements.

[0042]The strip steel whose chemical composition meets the above requirements is subjected to conventional treatments such as decoiling, welding, degreasing cleaning, annealing, leveling and tension leveling on the continuous annealing line. was 1.1%. After the treatment, enter the phosphating treatment area, first enter the phosphating section for phosphating treatment, the phosphating section adopts a spray process, the pH value of the phosphating solution is 2.8, the phosphating time is 49s, and the temperature of the phosphating solution is 45°C. The phosphating solution is composed of the following components: zinc dihydrogen phosphate 65g / L, zinc nitrate 78g / L, phosphoric acid 11g / L, sodium chlorate 1.3g / L, tartaric acid 6.8g / L, sodium fluoride 1.9g / L, sulfuric acid Hydroxylamine 1.1g / L, phytic acid 1.2...

Embodiment 3

[0046] The chemical composition of steel for oil barrels is: C 0.035%, Mn 0.30%, Si 0.04%, Al 0.01%, P 0.012%, S 0.0047%, and the balance is Fe and impurity elements.

[0047] The steel strip whose chemical composition meets the above requirements is subjected to conventional treatments such as uncoiling, welding, degreasing cleaning, annealing, leveling and tension leveling on the continuous annealing line. was 1.2%. After the treatment, enter the phosphating treatment area, first enter the phosphating section for phosphating treatment, the phosphating section adopts a spraying process, the pH value of the phosphating solution is 2.5, the phosphating time is 49s, and the temperature of the phosphating solution is 48°C. The phosphating solution is composed of the following components: zinc dihydrogen phosphate 97g / L, zinc nitrate 52g / L, phosphoric acid 18g / L, sodium chlorate 3.0g / L, tartaric acid 5.4g / L, sodium fluoride 1.2g / L, sulfuric acid Hydroxylamine 1.7g / L, phytic acid ...