6101B aluminum alloy casting production process

Abstract

The invention relates to a 6101B aluminum alloy casting production process, and belongs to the field of aluminum alloy casting production. The 6101B aluminum alloy casting production process comprisesthe steps of burdening, furnace charging, smelting, stirring, refining, slagging-off, component adjusting, online refining, online degassing, filtering and casting. Through connection of all processsteps in the production process and control over all process parameters, the 6101B aluminum alloy casting production process is optimized, products meet the mechanical property requirement, the product yield is increased, and the corrosion resistance and oxidation resistance of the products are improved.

Description

technical field

[0001] The invention belongs to the field of aluminum alloy casting production, and relates to a 6101B aluminum alloy casting production process. Background technique

[0002] Aluminum alloy is a kind of non-ferrous metal material widely used in industry. It is widely used in aviation, automobile, machinery manufacturing, shipbuilding and chemical industry. As one of them, 6101B aluminum alloy has many applications. However, the current casting production process of 6101B aluminum alloy is still incomplete, and there is a lack of mature experience guidance for the control of process parameters, so it is difficult to effectively guarantee the performance requirements of 6101B aluminum alloy. SUMMARY OF THE INVENTION

[0003] In view of this, the purpose of the present invention is to provide a 6101B aluminum alloy casting production process to solve the shortcomings of the existing casting production process.

[0004] To achieve the above object, the presen...

Examples

Embodiment Construction

[0024] The embodiments of the present invention are described below through specific specific examples, and those skilled in the art can easily understand other advantages and effects of the present invention from the contents disclosed in this specification. The present invention can also be implemented or applied through other different specific embodiments, and various details in this specification can also be modified or changed based on different viewpoints and applications without departing from the spirit of the present invention. It should be noted that, the following embodiments and features in the embodiments may be combined with each other under the condition of no conflict.

[0025] The present embodiment provides a 6101B aluminum alloy casting production process, comprising the following steps:

[0026] S1. Ingredients: prepare aluminum alloy raw materials according to the following ratios by weight, Si: 0.40-0.45%, Fe: 0.13-0.25%, Cu: ≤ 0.03%, Mn: ≤ 0.03%, Mg: 0....

technical field

[0001] The invention belongs to the field of aluminum alloy casting production, and relates to a 6101B aluminum alloy casting production process. Background technique

[0002] Aluminum alloy is a kind of non-ferrous metal material widely used in industry. It is widely used in aviation, automobile, machinery manufacturing, shipbuilding and chemical industry. As one of them, 6101B aluminum alloy has many applications. However, the current casting production process of 6101B aluminum alloy is still incomplete, and there is a lack of mature experience guidance for the control of process parameters, so it is difficult to effectively guarantee the performance requirements of 6101B aluminum alloy. SUMMARY OF THE INVENTION

[0003] In view of this, the purpose of the present invention is to provide a 6101B aluminum alloy casting production process to solve the shortcomings of the existing casting production process.

[0004] To achieve the above object, the presen...

Examples

Embodiment Construction

[0024] The embodiments of the present invention are described below through specific specific examples, and those skilled in the art can easily understand other advantages and effects of the present invention from the contents disclosed in this specification. The present invention can also be implemented or applied through other different specific embodiments, and various details in this specification can also be modified or changed based on different viewpoints and applications without departing from the spirit of the present invention. It should be noted that, the following embodiments and features in the embodiments may be combined with each other under the condition of no conflict.

[0025] The present embodiment provides a 6101B aluminum alloy casting production process, comprising the following steps:

[0026] S1. Ingredients: prepare aluminum alloy raw materials according to the following ratios by weight, Si: 0.40-0.45%, Fe: 0.13-0.25%, Cu: ≤ 0.03%, Mn: ≤ 0.03%, Mg: 0....