High strength thick steel plate for high heat input welding with excellent brittle crack arrestability and manufacturing method therefor

A technology for high-intensity welding and brittle crack propagation, applied in the field of high-strength thick steel plates, can solve the problems of difficult control of production scale, and achieve the effect of high-intensity welded joints with excellent toughness and improved safety.

Active Publication Date: 2015-11-25
JFE STEEL CORP
View PDF14 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] However, the steel materials described in Patent Documents 1 and 2 with excellent brittle crack propagation stopping characteristics are steel materials with a specific structure obtained by cooling only the surface layer of the steel material once and then reheating and performing processing during the reheating. Difficult to control at production scale

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High strength thick steel plate for high heat input welding with excellent brittle crack arrestability and manufacturing method therefor
  • High strength thick steel plate for high heat input welding with excellent brittle crack arrestability and manufacturing method therefor
  • High strength thick steel plate for high heat input welding with excellent brittle crack arrestability and manufacturing method therefor

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0136] Melt molten steel (steel codes A to Q) of each composition shown in Table 1 using a converter, and make steel raw materials (slab thickness of 250mm or 300mm) by continuous casting, hot rolling to a plate thickness of 55 to 100mm, and then carry out Cool to obtain No.1-27 test steels. For some, tempering was also performed after cooling. Table 2 shows hot rolling conditions and cooling conditions.

[0137] From the obtained thick steel plate, a φ14mm JIS14A test piece was cut from 1 / 4 of the plate thickness so that the longitudinal direction of the test piece was at right angles to the rolling direction, and a tensile test was performed to measure the yield strength (YS) and tensile strength (TS).

[0138] In addition, in order to evaluate the toughness value, JIS 4 is cut out from the thickness surface layer part and the thickness center part (hereinafter, the thickness center part may be referred to as 1 / 2t part) so that the longitudinal direction of the test piece ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

Provided are a high strength thick steel plate for high heat input welding, the plate of a preferred plate thickness of at least 50 mm being used for ships and having excellent brittle crack arrestability, and a manufacturing method therefor. A thick steel plate having a specific component composition, the main constituent of the metal structure being bainite, the thick steel plate having a texture in which the density in the RD / / (110) plane at the plate thickness center is 1.5-4.0, and the Charpy fracture appearance transition temperature (vTrs) at the surface layer and the plate thickness center being no more than -40°C; and a manufacturing method therefor.

Description

technical field [0001] The present invention relates to a high-strength thick steel plate for high heat input welding with excellent brittle crack arrestability (brittle crack arrestability) and a manufacturing method thereof, and particularly relates to a high-strength thick steel plate suitable for ships with a thickness of 50 mm or more. Strong thick steel plate. Background technique [0002] For large structures such as ships, accidents associated with brittle fractures have a large impact on the economy and the environment. Therefore, improvement of safety is generally required, and toughness at service temperature and brittle crack propagation stop characteristic are required for the steel material to be used. [0003] Vessels such as container ships and bulk carriers use high-strength thick-walled materials as outer plate of ship'shull in their structures. Recently, with the enlargement of ship hulls, high-strength and thick-walled materials have been further develo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/00C21D1/26C21D8/02C22C38/14C22C38/58
CPCC21D1/26C21D8/02C21D8/0226C21D2201/05C21D2211/002C22C38/00C22C38/14C22C38/58C22C38/001C22C38/002C22C38/005C22C38/02C22C38/04C22C38/06C22C38/08C22C38/12C22C38/16C22C38/20C22C38/26C22C38/28C22C38/38C22C38/42C22C38/48C22C38/50C22C38/54
Inventor 长谷和邦竹内佳子三田尾真司
Owner JFE STEEL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap