A kind of method for preparing coral structure porous boric acid

A technology of boric acid and coral, which is applied in the field of preparation of coral-structured porous boric acid, can solve the problems that it is difficult to meet the requirements of boric acid surface reactivity, high specific surface area and porosity, and achieve the effect of low cost and high yield

Active Publication Date: 2022-01-14
DALIAN UNIV OF TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the currently produced boric acid is lamellar crystal, which is difficult to meet the requirements of boric acid surface reactivity, high specific surface area and porosity. Therefore, it is necessary to develop and propose a preparation technology for porous boric acid

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method for preparing coral structure porous boric acid
  • A kind of method for preparing coral structure porous boric acid
  • A kind of method for preparing coral structure porous boric acid

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Add 80g of analytically pure boric acid into a pressure vessel equipped with 100g of mixed liquid solvent, wherein the mixed liquid solvent is prepared by ethanol, glycerol and water according to the above formula ratio; heat the pressure vessel to make the temperature reach 150°C to obtain a clear solution; then control the cooling rate 3-5°C / min, let the temperature drop to 20°C, let it stand for 1 hour, then raise it to 30-40°C at a heating rate of 2°C / min, let it stand for 30 minutes, then cool down to room temperature naturally, a large amount of white crystal liquid can be obtained, the Suction filter the feed liquid, and dry at 60°C to obtain coral-like porous boric acid powder, whose appearance is as follows: figure 1 shown; the X-ray diffraction pattern of the obtained powder is shown in figure 2 , according to the analysis of the standard card JCPDS No.30-0199; the corresponding adsorption equilibrium curve is as follows Figure 4 It is shown that it has a r...

Embodiment 2

[0027] Add 30g of analytically pure boric acid into a pressure vessel containing 10g of a mixed solution solvent, wherein the mixed solution solvent is prepared from methanol, isopropanol and water according to the above formula ratio; heat the pressure vessel until the temperature reaches 80°C to obtain a clear solution; then control the cooling rate 2-3°C / min, let the temperature drop to 20°C, let it stand for 1 hour, then raise it to 40°C at a rate of 2-4°C / min, let it stand for 30 minutes, then cool down to room temperature naturally, a large amount of white crystal liquid can be obtained, the The feed liquid is suction filtered and dried at 60°C to obtain rich tubular porous coral structure boric acid, whose appearance is as follows: image 3 shown.

Embodiment 3

[0029] Add 45g of analytically pure boric acid into a pressure vessel with 100g of mixed solution solvent, wherein the mixed solution solvent is prepared by ethanol, n-butanol and water according to the above formula ratio; heat the pressure vessel to make the temperature reach 110°C to obtain a clear solution; then control the cooling rate 3-5°C / min, let the temperature drop to 5°C, stand for 1h, then increase the temperature at a rate of 3-5°C / min to 40°C for 1h, then cool naturally to room temperature, a large amount of white crystal solution can be obtained, the solution After suction filtration and drying at 60°C, the loose coral porous boric acid powder can be obtained, and its appearance is as follows: Figure 5 shown.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the technical field of preparation of inorganic functional materials and provides a method for preparing coral-structured porous boric acid. This method is based on the formation mechanism of coral reef structures in the ocean. Some cheap and easy-to-remove hydroxyl-containing organic molecules are selected as inducers. Under the action of organic inducers, the coral structure is obtained by changing the temperature gradient in the process of dissolution-crystallization-redissolution, etc. porous boric acid. The method can realize the particle size of the boric acid product is uniform, the operation is safe and simple, and the porous structure can improve the surface reactivity and use efficiency. This method provides optional material support for broadening the application field of boric acid and improving the application performance of boric acid in battery materials, biomaterial design and catalysis.

Description

technical field [0001] The invention belongs to the technical field of preparation of inorganic functional materials, and relates to a preparation method of coral-structured porous boric acid. Background technique [0002] Inorganic porous materials have the advantages of small relative density, large specific surface area, and fast mass transfer rate. Coral-structured porous materials are a class of functional materials that have received special attention in recent years. They have shown great promise in new catalytic materials, biological materials, and battery materials. Huge and potential application prospects. [0003] Boron-containing chemicals such as boric acid exhibit properties such as stimuli-responsive luminescence, sterilization, heat conduction, and ion capture due to the electron-deficiency of boron and other electronic and structural characteristics. They are used in many fields such as battery materials, catalysis, biological materials, and medical diagnosi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C01B35/10
CPCC01B35/1045C01P2002/72C01P2004/03
Inventor 宁桂玲毕胜南朱培函叶俊伟田朋林源
Owner DALIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap