Water glass old sand-based permeable sintered pavement brick and preparation method thereof

A technology of water glass and pavement bricks, which is applied in the field of water glass old sand-based permeable sintered pavement bricks and its preparation, which can solve the problems of air heat and humidity exchange, urban groundwater level drop, waste of limited resources, etc., and reduce firing temperature, lower eutectic temperature, and lower energy consumption

Active Publication Date: 2015-12-30
浙江路兴环保科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As a result, a series of environmental problems have arisen: the rainwater that can infiltrate the surface has decreased significantly, and the underground water table in the city has dropped sharply; Rainwater cannot seep into the ground in time, which may easily cause social problems such as flooded roads and traffic paralysis
In addition, there is a relative shortage of high-quality quartz sand resources in my country. If the old water glass sand is not comprehensively utilized and discarded in large quantities, it will be a great waste of limited resources and cause serious environmental pollution.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water glass old sand-based permeable sintered pavement brick and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A water-glass old sand-based permeable sintered pavement brick. The raw material composition and proportion of the permeable pavement brick: water glass old sand is primary used sand, and the dominant mineral of clay is kaolinite. The proportion is: water glass old sand 892.5 g, coal gangue 52.5g, clay 31.5g, water glass 21g, glass powder 31.5g, water 21g.

[0031] The preparation method of the above-mentioned water glass old sand-based permeable sintered pavement brick comprises the following steps:

[0032] (1) Pulverization: Put the old water glass sand and coal gangue into a pulverizer to crush them into fine aggregates. The fineness modulus of the old water glass sand after crushing is 2.0, and the particle size of the coal gangue after crushing is 0.15mm~0.6mm;

[0033] (2) Mixing: Fully mix the above-mentioned raw materials except water glass and water according to the ratio, stir evenly, add water glass and water for wet mixing, and age the evenly mixed ingredie...

Embodiment 2

[0038] A water-glass old sand-based permeable sintered pavement brick, the raw material composition and proportion of the water-permeable pavement brick: water glass old sand is quaternary old sand, the dominant mineral of clay is montmorillonite, and the proportion is: water glass old sand 525g, coal gangue 157.5g, clay 157.5g, water glass 31.5g, glass powder 157.5g, water 21g.

[0039] The preparation method of the above-mentioned water glass old sand-based permeable sintered pavement brick comprises the following steps:

[0040] (1) Pulverization: Put the old water glass sand and coal gangue into a pulverizer to crush them into fine aggregates. The fineness modulus of the old water glass sand after crushing is 2.5, and the particle size of the coal gangue after crushing is 0.15mm~0.6mm;

[0041] (2) Mixing: Fully mix the above-mentioned raw materials except water glass and water according to the ratio, stir evenly, add water glass and water for wet mixing, and age the evenl...

Embodiment 3

[0046] A water-glass old sand-based permeable sintered pavement brick. The raw material composition and proportion of the permeable pavement brick: water glass old sand is tertiary old sand, and the dominant mineral of clay is kaolinite. The proportion is: water glass old sand 682.5 g, coal gangue 210g, clay 42g, water glass 52.5g, glass powder 42g, water 21g.

[0047] The preparation method of the above-mentioned water glass old sand-based permeable sintered pavement brick comprises the following steps:

[0048] (1) Pulverization: Put the old water glass sand and coal gangue into a pulverizer to crush them into fine aggregates. The fineness modulus of the old water glass sand after crushing is 2.3, and the particle size of the coal gangue after crushing is 0.15mm~0.6mm;

[0049] (2) Mixing: Fully mix the above-mentioned raw materials except water glass and water according to the ratio, stir evenly, add water glass and water for wet mixing, and age the evenly mixed ingredients...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

A water-glass old sand-based permeable sintered pavement brick and a preparation method thereof, which belong to the technical field of comprehensive utilization of industrial solid waste and road building materials. The water-glass old sand-based water-permeable sintered pavement brick consists of 100 parts of the following Raw materials: 50-85 parts of industrial solid waste water glass old sand produced in the foundry industry, 5-20 parts of coal gangue, 3-15 parts of clay, 2-5 parts of water glass, 3-15 parts of glass powder, and the balance for water. The present invention is characterized by the following aspects: (1) water glass old sand-based permeable sintered pavement bricks are beneficial to solve the problems of a large amount of water glass old sand produced in the foundry industry and pollution to the ecological environment; (2) water glass old sand The firing temperature of water-based permeable sintered pavement bricks can be reduced to 1000°C~1150°C, reducing energy consumption; (3) Water glass old sand-based permeable sintered pavement bricks can save silica sand resources. This invention is in line with the national industry of energy conservation, emission reduction and environmental protection Policies are conducive to the promotion and application.

Description

technical field [0001] The invention belongs to the technical field of comprehensive utilization of industrial solid waste and road building materials, and in particular relates to a water-glass old sand-based water-permeable sintered pavement brick and a preparation method thereof. Background technique [0002] With the development of economy and the process of urbanization, the surface of modern cities is gradually covered by reinforced concrete buildings and impermeable roads. But these impermeable roads have brought many negative impacts to the ecological environment of the city. Concrete pavements lack the ability to absorb heat and infiltrate rainwater compared to natural soil. As a result, a series of environmental problems have arisen: the rainwater that can infiltrate the surface has decreased significantly, and the underground water table in the city has dropped sharply; Rainwater cannot seep into the ground in time, which can easily cause social problems such as...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): C04B38/00
Inventor王继娜徐开东李彦彦汪潇牛季收朱凯
Owner浙江路兴环保科技有限公司