Process for preparing etching cream of glass fibre

A technology of glass filament and frosting, which is applied in the field of preparation of glass silk screen frosting paste, which can solve the problems of affecting the frosting effect, complicated operation, and low efficacy

Inactive Publication Date: 2005-03-30
上海多林玻璃技术有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Glass frosting and frosting were originally operated manually and mechanically. The operation process is relatively primitive, and the frosting pattern obtained is not detailed enough. Some glass parts are frosted with wax protection or screen ink protection, and then the protected glass is placed in the frosting solution. The disadvantages of this process are complex operation, low efficiency and high cost
Chinese patent ZL96122275 introduces a "formulation and frosting method of frosting liquid for glass products". Affects the frosting effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for preparing etching cream of glass fibre
  • Process for preparing etching cream of glass fibre

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0005] Embodiment 1: With reference to accompanying drawing, at first prepare frosting powder, in 100 grams, 55 grams of ammonium bifluoride, 5 grams of ammonium fluoride, 4 grams of calcium fluoride, 6 grams of sodium fluoroborate, 5 grams of potassium fluoroborate, fluoroboric acid 3 grams of magnesium, 4 grams of oxalic acid, 6 grams of starch, 8 grams of barium sulfate, and 4 grams of sodium fluorosilicate; put the above mixture in a rotary stirring tank and stir it for 20 minutes; mix the frosting powder and industrial hydrochloric acid by 1 : 0.5 to carry out the mixed reaction to obtain the frosting liquid, the time of the mixed reaction is 30 hours, the frosting liquid is filtered with 10-100 order ordinary screen or nylon mesh to obtain a uniform milky frosting liquid; a clean glass sheet is placed in the Filtrate for 30 seconds, it can be seen that the glass sheet has been frosted evenly, and the frosting cream is prepared, and its weight ratio is as follows (in 100 g...

Embodiment 2

[0006] Embodiment 2: With reference to accompanying drawing, at first prepare frosting powder, in 100 grams, 35 grams of ammonium bifluoride, 8 grams of ammonium fluoride, 9 grams of calcium fluoride, 10 grams of sodium fluoroborate, 10 grams of potassium fluoroborate, fluoroboric acid 4 grams of magnesium, 4 grams of oxalic acid, 7 grams of starch, 10 grams of barium sulfate, and 3 grams of sodium fluorosilicate; put the above mixture in a rotary stirring tank and stir for 25 minutes; mix the frosting powder and industrial hydrochloric acid by 1 : 1 to carry out mixed reaction to obtain frosting liquid, the time of mixed reaction is 50 hours, the frosting liquid is filtered with 10-100 order ordinary screen or nylon net to obtain uniform milky frosting liquid; a clean glass sheet is placed in the Filtrate for 50 seconds, you can see that the glass sheet is frosted evenly, prepare the frosting paste, its weight ratio is as follows (in 100 grams): 35 grams of milky frosting liqu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

An etching cream for silk screen printing on surface of glass is prepared through preparing etching powder from 10 raw materials including ammonium hydrogen fluoride, ammonium fluoride, starch, barium sulfate, etc. stirring in sealed state, proportionally mixing it with industrial hydrochloric acid, reaction, filtering to obtain etching liquid, mixing it with organic solvent, polyacrylic resin, polyose compound, barium salt and lipomatic compound, and stirring.

Description

1. Technical field [0001] The invention relates to a method for preparing a frosting material, in particular to a method for preparing a frosting paste for glass silk screen printing, in which various silk screen frosting glass products are obtained by coating the glass surface with a nylon screen. 2. Background technology [0002] Glass frosting and frosting were originally operated manually and mechanically. The operation process is relatively primitive, and the frosting pattern obtained is not detailed enough. Some glass parts are frosted with wax protection or screen ink protection, and then the protected glass is placed in the frosting solution. The disadvantages of this process are complicated operation, low efficiency and high cost. Chinese patent ZL96122275 introduces a "formulation and frosting method of frosting liquid for glass products". This patent uses the method of solution etching to obtain frosted glass. Affects the frosting effect. 3. Contents of the inv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C15/00
Inventor 李建辉
Owner 上海多林玻璃技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com