Manufacturing method of toothpaste and toothpaste

Abstract

The invention discloses toothpaste and a manufacturing method thereof. The toothpaste comprises 30-55 parts of calcium carbonate, 2-3 parts of an activity addition agent, 5-6 parts of a stabilizing agent, 0.01-0.1 part of saccharin, 0.5-1 part of sorbitol, 1-1.5 parts of glycerinum, 1-2 parts of propylene glycol, 1000 parts of deionized water, 1000 parts of purified water, 11 parts of an ionized calcium water solubility preparation, and 0.2-0.3 part of spice. The ionized calcium water solubility preparation is added into the toothpaste, is obtained through special technological processing high-temperature treatment, and is not bonded with acid groups; and after the ionized calcium water solubility preparation is dissolved into water, a complex with calcium as the principal and surrounding hydroxy radicals is formed, so that erosion of acid radicals to enamel is reduced so as to clean and strengthen teeth. Due to the fact that the ionized calcium water solubility preparation does not react with fluorochemicals, the ionized calcium water solubility preparation can be used as base materials of the toothpaste containing fluoride, enamel will not be damaged, the brightness of the toothpaste can be improved, and the toothpaste has the good tooth strengthening and cleaning force.

Description

technical field

[0001] The invention relates to a toothpaste and a preparation method of the toothpaste. Background technique

[0002] Calcium carbonate is a commonly used abrasive in toothpaste, and light calcium carbonate powder is often used as a filler or carrier. Calcium oxide is usually obtained by calcining limestone, and calcium oxide is added to toothpaste. Very fine calcium carbonate powder is often used as a filler. Toothpaste is composed of various inorganic and organic substances, including abrasives and detergents. , binders, humectants, sweeteners, fragrances and moisture.

[0003] Abrasives are the main body of toothpaste, commonly used abrasives are calcium carbonate (CaCO 3 ), calcium hydrogen phosphate (CaHPO 4 2H 2 O), the consumption is between 30%~55%. In order to increase the decontamination effect, it is necessary to add detergent foaming agent sodium lauryl sulfate (ROSO 3 Na), the dosage is about 2% to 3%. Toothpaste can whiten teeth mainly b...

Examples

Embodiment 1

[0025] A kind of toothpaste making method described in this embodiment, in at least one step in the toothpaste making process, add ionic calcium water-soluble preparation.

[0026] The specific steps are:

[0027] 1), pass 30 parts of calcium carbonate raw materials through a 400-mesh sieve, and add 2 parts of active additives, 5 parts of stabilizer, and 0.01 part of saccharin into the premixing pot;

[0028] 2) Add 0.5 parts of sorbitol, 1 part of glycerin, 1 part of propylene glycol and 1000 parts of deionized water into the liquid material storage tank, and fully stir for 60 minutes;

[0029] 3) Add 1,000 parts of purified water at a temperature of 3°C treated by a reverse osmosis ion exchange pure water processor and 1 part of ionic calcium water-soluble preparation into a 0.3MPA airtight water injection tank and fully dissolve for 30 minutes;

[0030] 4) Add the ionic calcium water-soluble preparation water in step 3) evenly into the paste making pot at a flow rate great...

Embodiment 2

[0034] A kind of toothpaste making method described in this embodiment, in at least one step in the toothpaste making process, add ionic calcium water-soluble preparation.

[0035] The specific steps are:

[0036] 1), pass 55 parts of calcium carbonate raw materials through a 500-mesh sieve, and add 3 parts of active additives, 6 parts of stabilizer, and 0.1 part of saccharin into the premixing pot;

[0037] 2), add 1 part of sorbitol, 1.5 parts of glycerin, 2 parts of propylene glycol and 1000 parts of deionized water into the liquid material storage tank, and fully stir for 90 minutes;

[0038] 3) Add 1,000 parts of purified water at a temperature of 4°C treated by a reverse osmosis ion exchange pure water processor and 1 part of ionic calcium water-soluble preparation into a 0.3MPA airtight water injection tank and fully dissolve for 60 minutes;

[0039]4) Add the ionic calcium water-soluble preparation water in step 3) evenly into the paste making pot at a flow rate great...

Embodiment 3

[0043] A kind of toothpaste making method described in this embodiment, in at least one step in the toothpaste making process, add ionic calcium water-soluble preparation.

[0044] The specific steps are:

[0045] 1), pass 40 parts of calcium carbonate raw materials through a 450 mesh sieve, and add 2.5 parts of active additives, 5.5 parts of stabilizers, and 0.05 parts of saccharin into the premixing pot;

[0046] 2), add 0.75 parts of sorbitol, 1.2 parts of glycerin, 1.5 parts of propylene glycol and 1000 parts of deionized water into the liquid material storage tank, and fully stir for 80 minutes;

[0047] 3) Add 1,000 parts of purified water at a temperature of 3.5°C treated with a reverse osmosis ion exchange pure water processor and 1 part of ionic calcium water-soluble preparation into a 0.3MPA airtight water injection tank and fully dissolve for 30-60 minutes;

[0048] 4) Add the ionic calcium water-soluble preparation water in step 3) evenly into the paste making pot...

technical field

[0001] The invention relates to a toothpaste and a preparation method of the toothpaste. Background technique

[0002] Calcium carbonate is a commonly used abrasive in toothpaste, and light calcium carbonate powder is often used as a filler or carrier. Calcium oxide is usually obtained by calcining limestone, and calcium oxide is added to toothpaste. Very fine calcium carbonate powder is often used as a filler. Toothpaste is composed of various inorganic and organic substances, including abrasives and detergents. , binders, humectants, sweeteners, fragrances and moisture.

[0003] Abrasives are the main body of toothpaste, commonly used abrasives are calcium carbonate (CaCO 3 ), calcium hydrogen phosphate (CaHPO 4 2H 2 O), the consumption is between 30%~55%. In order to increase the decontamination effect, it is necessary to add detergent foaming agent sodium lauryl sulfate (ROSO 3 Na), the dosage is about 2% to 3%. Toothpaste can whiten teeth mainly b...

Examples

Embodiment 1

[0025] A kind of toothpaste making method described in this embodiment, in at least one step in the toothpaste making process, add ionic calcium water-soluble preparation.

[0026] The specific steps are:

[0027] 1), pass 30 parts of calcium carbonate raw materials through a 400-mesh sieve, and add 2 parts of active additives, 5 parts of stabilizer, and 0.01 part of saccharin into the premixing pot;

[0028] 2) Add 0.5 parts of sorbitol, 1 part of glycerin, 1 part of propylene glycol and 1000 parts of deionized water into the liquid material storage tank, and fully stir for 60 minutes;

[0029] 3) Add 1,000 parts of purified water at a temperature of 3°C treated by a reverse osmosis ion exchange pure water processor and 1 part of ionic calcium water-soluble preparation into a 0.3MPA airtight water injection tank and fully dissolve for 30 minutes;

[0030] 4) Add the ionic calcium water-soluble preparation water in step 3) evenly into the paste making pot at a flow rate great...

Embodiment 2

[0034] A kind of toothpaste making method described in this embodiment, in at least one step in the toothpaste making process, add ionic calcium water-soluble preparation.

[0035] The specific steps are:

[0036] 1), pass 55 parts of calcium carbonate raw materials through a 500-mesh sieve, and add 3 parts of active additives, 6 parts of stabilizer, and 0.1 part of saccharin into the premixing pot;

[0037] 2), add 1 part of sorbitol, 1.5 parts of glycerin, 2 parts of propylene glycol and 1000 parts of deionized water into the liquid material storage tank, and fully stir for 90 minutes;

[0038] 3) Add 1,000 parts of purified water at a temperature of 4°C treated by a reverse osmosis ion exchange pure water processor and 1 part of ionic calcium water-soluble preparation into a 0.3MPA airtight water injection tank and fully dissolve for 60 minutes;

[0039]4) Add the ionic calcium water-soluble preparation water in step 3) evenly into the paste making pot at a flow rate great...

Embodiment 3

[0043] A kind of toothpaste making method described in this embodiment, in at least one step in the toothpaste making process, add ionic calcium water-soluble preparation.

[0044] The specific steps are:

[0045] 1), pass 40 parts of calcium carbonate raw materials through a 450 mesh sieve, and add 2.5 parts of active additives, 5.5 parts of stabilizers, and 0.05 parts of saccharin into the premixing pot;

[0046] 2), add 0.75 parts of sorbitol, 1.2 parts of glycerin, 1.5 parts of propylene glycol and 1000 parts of deionized water into the liquid material storage tank, and fully stir for 80 minutes;

[0047] 3) Add 1,000 parts of purified water at a temperature of 3.5°C treated with a reverse osmosis ion exchange pure water processor and 1 part of ionic calcium water-soluble preparation into a 0.3MPA airtight water injection tank and fully dissolve for 30-60 minutes;

[0048] 4) Add the ionic calcium water-soluble preparation water in step 3) evenly into the paste making pot...