Glaze material for ceramic tea set

A tea set and glaze technology, which is applied in the field of daily-use ceramic glazes, can solve the problems of low hardness and poor wear resistance, and achieve the effect of high hardness, good wear resistance and beautiful glaze surface

CN105967520AInactive Publication Date: 2016-09-28安徽省德邦瓷业有限公司
3 Cites 2 Cited by

Patent Information

Authority / Receiving Office
CN · China
Current Assignee / Owner
Publication Date
2016-09-28
Estimated Expiration
Not applicable · inactive patent
Patent Text Reader

Abstract

The invention discloses a ceramic tea set glaze, which is composed of the following raw materials in parts by weight: 45-72 parts of silicon dioxide, 12-28 parts of aluminum oxide, 5-15 parts of calcium oxide, and 1-4 parts of iron oxide , titanium oxide 1~3.8 parts, sodium oxide 0.2~1.3 parts, zinc oxide 1~2.3 parts, cobalt oxide 0.1~0.3 parts, bentonite 5~12 parts, diatomite 5~10 parts, methyl cellulose sodium 3~ 8 parts, 0.1~0.3 parts of boron nitride, 20~35 parts of fluororesin, 1~4 parts of solid lubricant and 6~12 parts of thickener. This kind of ceramic tea set glaze has good wear resistance, high hardness, safety, environmental protection, non-toxicity, and has a certain effect of purifying and mineralizing water quality. The finished porcelain glaze is beautiful, light and delicate, and can be widely used in Living porcelain.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to a daily-use ceramic glaze, in particular to a ceramic tea set glaze. Background technique

[0002] Ceramic products are widely used all over the world. With the promotion of tea culture, ceramic tea sets are loved by more and more people. Ceramic tea sets are beautiful, durable, and colorfully decorated. However, the existing glaze generally adopts common frit glaze, which has poor wear resistance and low hardness, and has potential safety hazards. Contents of the invention

[0003] The purpose of the present invention is to solve the above problems, and provides a ceramic tea set glaze.

[0004] In order to achieve the above object, the present invention provides a ceramic tea set glaze, which is composed of the following raw materials in parts by weight: 45-72 parts of silicon dioxide, 12-28 parts of aluminum oxide, 5-15 parts of calcium oxide, 1~4 parts of iron, 1~3.8 parts of titanium oxide, 0.2~1.3 parts of sodium oxid...

Examples

Embodiment Construction

[0008] The present invention adopts the following technical solutions to achieve: the ceramic tea set glaze is composed of the following raw materials in parts by weight: 45-72 parts of silicon dioxide, 12-28 parts of aluminum oxide, 5-15 parts of calcium oxide, 1~4 parts of iron, 1~3.8 parts of titanium oxide, 0.2~1.3 parts of sodium oxide, 1~2.3 parts of zinc oxide, 0.1~0.3 parts of cobalt oxide, 5~12 parts of bentonite, 5~10 parts of diatomaceous earth, methyl 3~8 parts of sodium cellulose, 0.1~0.3 parts of boron nitride, 20~35 parts of fluororesin, 1~4 parts of solid lubricant and 6~12 parts of thickener.

[0009] As a preferred version of the present invention, the ceramic tea set glaze is composed of the following raw materials in parts by weight: 55-62 parts of silicon dioxide, 16-25 parts of aluminum oxide, 7-13 parts of calcium oxide, and 1.3-3.7 parts of iron oxide , titanium oxide 2~3.5 parts, sodium oxide 0.4~0.9 parts, zinc oxide 1.4~2.1 parts, cobalt oxide 0.2~0....