Rubber rain shoes with matting effect based on rubber decal cold transfer process and manufacturing method

Abstract

The invention belongs to the technical field of rain shoes, and particularly relates to a rubber rain shoe with a matting effect based on a rubber decal cold transfer process and a manufacturing method. The invention provides rubber rain shoes with a mattingeffect based on a rubber decal cold transfer process and a manufacturing method, and aims to solve the problem that in the prior art, the printing transfer completeness degree is not ideal enough when decal cold transfer is carried out on rubber rain shoes. The manufacturing method comprises the steps: adding chloroprene rubber resin and an auxiliary agent into a plasticator, and carrying out plastication; obtaining a raw rubber sheet after plastication is completed; printing a required pattern on a printing film; transferring the pattern on the printing film to the raw rubber sheet, and making the rain shoes from the raw rubber sheet; and spraying a matting agent to the surface of the rubber rain shoe to obtain a finished matting rain shoe product. According to the invention, the problem that in the prior art, the printing transfer completeness degree of chloroprene rubber rain shoes is not ideal is solved by adding the auxiliaries, and the decal cold transfer process can be better applied to the rubber rain shoes.

Description

technical field

[0001] The invention belongs to the technical field of rain boots, and in particular relates to rubber rain boots with a matting effect based on a rubber decal cold transfer process and a manufacturing method. Background technique

[0002] Rain boots are a kind of polymer overshoes up to the ankle to protect the feet from external pollutants when it rains, agricultural activities, and muddy ground. It is an excellent equipment for traveling in rainy days. The decal cold transfer process is a printing transfer technology that does not require heating during the transfer process. However, the rubber rain boots in the prior art often have the problem that the integrity of the printing transfer is not ideal when the decals are cold transferred.

[0003] For example, a Chinese invention patent application discloses a rubber rain boot [application number: 201510190104.8], which is made of the following raw materials in parts by weight: 15-35 parts of 26-type nitri...

Examples

Embodiment 1

[0027] This embodiment provides a method for making rubber rain boots with matting effect based on the cold transfer process of rubber appliques, comprising the following steps:

[0028] Step 1: adding neoprene resin and additives to a masticating machine for masticating, and obtaining raw rubber sheets after masticating is completed;

[0029] Step 2: Print the required pattern on the printing film;

[0030] Step 3: transfer the pattern on the printing film to the raw rubber sheet prepared in step 1, and use the raw rubber sheet to make rain boots;

[0031] Step 4: Spray the matting agent on the surface of the rubber rain boots prepared in step 3 to obtain the finished matting rain boots. The amount of matting agent sprayed is 4% of the total mass of neoprene resin and additives.

[0032] Wherein, the mass fraction that neoprene resin adds is 40 parts, and described auxiliary agent comprises the nitrile rubber that mass fraction is respectively 30 parts, the polyvinyl chlorid...

Embodiment 2

[0035] This embodiment provides a method for making rubber rain boots with matting effect based on the cold transfer process of rubber appliques, comprising the following steps:

[0036] Step 1: adding neoprene resin and additives to a masticating machine for masticating, and obtaining raw rubber sheets after masticating is completed;

[0037] Step 2: Print the required pattern on the printing film;

[0038] Step 3: transfer the pattern on the printing film to the raw rubber sheet prepared in step 1, and use the raw rubber sheet to make rain boots;

[0039] Step 4: Spray a matting agent on the surface of the rubber rain boots prepared in Step 3 to obtain a finished matting rain boot. The amount of the matting agent sprayed is 0.1% of the total mass of the neoprene resin and additives.

[0040] Wherein, the mass fraction that neoprene resin adds is 50 parts, and described auxiliary agent comprises the nitrile rubber that mass fraction is respectively 20 parts, the polyvinyl ch...

Embodiment 3

[0043] This embodiment provides a method for making rubber rain boots with matting effect based on the cold transfer process of rubber appliques, comprising the following steps:

[0044] Step 1: adding neoprene resin and additives to a masticating machine for masticating, and obtaining raw rubber sheets after masticating is completed;

[0045] Step 2: Print the required pattern on the printing film;

[0046] Step 3: transfer the pattern on the printing film to the raw rubber sheet prepared in step 1, and use the raw rubber sheet to make rain boots;

[0047] Step 4: Spray the matting agent on the surface of the rubber rain boots prepared in step 3 to obtain the finished matting rain boots. The amount of matting agent sprayed is 2% of the total mass of neoprene resin and additives.

[0048] Wherein, the mass fraction that neoprene resin adds is 44 parts, and described auxiliary agent comprises the nitrile rubber that mass fraction is respectively 26 parts, the polyvinyl chlorid...

technical field

[0001] The invention belongs to the technical field of rain boots, and in particular relates to rubber rain boots with a matting effect based on a rubber decal cold transfer process and a manufacturing method. Background technique

[0002] Rain boots are a kind of polymer overshoes up to the ankle to protect the feet from external pollutants when it rains, agricultural activities, and muddy ground. It is an excellent equipment for traveling in rainy days. The decal cold transfer process is a printing transfer technology that does not require heating during the transfer process. However, the rubber rain boots in the prior art often have the problem that the integrity of the printing transfer is not ideal when the decals are cold transferred.

[0003] For example, a Chinese invention patent application discloses a rubber rain boot [application number: 201510190104.8], which is made of the following raw materials in parts by weight: 15-35 parts of 26-type nitri...

Examples

Embodiment 1

[0027] This embodiment provides a method for making rubber rain boots with matting effect based on the cold transfer process of rubber appliques, comprising the following steps:

[0028] Step 1: adding neoprene resin and additives to a masticating machine for masticating, and obtaining raw rubber sheets after masticating is completed;

[0029] Step 2: Print the required pattern on the printing film;

[0030] Step 3: transfer the pattern on the printing film to the raw rubber sheet prepared in step 1, and use the raw rubber sheet to make rain boots;

[0031] Step 4: Spray the matting agent on the surface of the rubber rain boots prepared in step 3 to obtain the finished matting rain boots. The amount of matting agent sprayed is 4% of the total mass of neoprene resin and additives.

[0032] Wherein, the mass fraction that neoprene resin adds is 40 parts, and described auxiliary agent comprises the nitrile rubber that mass fraction is respectively 30 parts, the polyvinyl chlorid...

Embodiment 2

[0035] This embodiment provides a method for making rubber rain boots with matting effect based on the cold transfer process of rubber appliques, comprising the following steps:

[0036] Step 1: adding neoprene resin and additives to a masticating machine for masticating, and obtaining raw rubber sheets after masticating is completed;

[0037] Step 2: Print the required pattern on the printing film;

[0038] Step 3: transfer the pattern on the printing film to the raw rubber sheet prepared in step 1, and use the raw rubber sheet to make rain boots;

[0039] Step 4: Spray a matting agent on the surface of the rubber rain boots prepared in Step 3 to obtain a finished matting rain boot. The amount of the matting agent sprayed is 0.1% of the total mass of the neoprene resin and additives.

[0040] Wherein, the mass fraction that neoprene resin adds is 50 parts, and described auxiliary agent comprises the nitrile rubber that mass fraction is respectively 20 parts, the polyvinyl ch...

Embodiment 3

[0043] This embodiment provides a method for making rubber rain boots with matting effect based on the cold transfer process of rubber appliques, comprising the following steps:

[0044] Step 1: adding neoprene resin and additives to a masticating machine for masticating, and obtaining raw rubber sheets after masticating is completed;

[0045] Step 2: Print the required pattern on the printing film;

[0046] Step 3: transfer the pattern on the printing film to the raw rubber sheet prepared in step 1, and use the raw rubber sheet to make rain boots;

[0047] Step 4: Spray the matting agent on the surface of the rubber rain boots prepared in step 3 to obtain the finished matting rain boots. The amount of matting agent sprayed is 2% of the total mass of neoprene resin and additives.

[0048] Wherein, the mass fraction that neoprene resin adds is 44 parts, and described auxiliary agent comprises the nitrile rubber that mass fraction is respectively 26 parts, the polyvinyl chlorid...