Shock absorbing member for automobile door, automobile door, blank, and method for manufacturing shock absorbing member for automobile door

Abstract

The invention relates to a shock absorbing member for an automobile door, the automobile door, a blank, and a method for manufacturing the shock absorbing member for the automobile door. A shock absorbing member for an automobile door, which is molded from a blank that is a single blank or a split blank, is provided with: a coupling band part that extends in a first direction; and at least three parts to be connected, one end of which is connected to the connecting belt part, the parts to be connected having an impact absorbing portion having a closed cross-sectional structure in a second direction intersecting the first direction.

Description

Technical Field

[0001] The invention relates to an impact absorbing component for an automobile door, an automobile door, a blank and a method for manufacturing the impact absorbing component for an automobile door.

[0002] This application claims priority based on Japanese Patent Application No. 2022-107800 filed in Japan on July 4, 2022, the contents of which are incorporated herein by reference. Background Art

[0003] In recent years, the application of high-strength steel sheets to automobile exterior panels has been studied. By using high-strength steel sheets, the thickness of the steel sheets can be reduced, thereby achieving a reduction in the weight of automobile exterior parts.

[0004] However, since the tensile rigidity of the exterior member depends on the plate thickness, if the plate thickness is reduced, the tensile rigidity will be insufficient. In other words, if the plate thickness is reduced, the exterior member is easily deformed when the exterior member is pressed by hand.

[0005] Patent Document 1 discloses a technique in which shock absorbing members are disposed vertically and horizontally inside an exterior panel, thereby making it possible to reduce the weight of the exterior member without reducing the tensile rigidity and shock resistance even if the thickness of the exterior member is reduced.

[0006] Prior art literature

[0007] Patent Literature

[0008] Patent Document 1: International Publication No. 2018 / 021422 Summary of the invention

[0009] Problems to be solved by the invention

[0010] In the technology disclosed in Patent Document 1, since a plurality of impact absorbing members are individually press-formed, the number of components is large. In addition, a press die having a different shape must be prepared for each inner surface shape of the attachment portion of the exterior panel.

[0011] Furthermore, when welding the individual impact absorbing members to the exterior panel one by one, the welding is performed after positioning each one, which results in a large number of working man-hours and an increase in manufacturing cost.

[0012] The present invention has been made in view of the above problems, and an object of the present invention is to provide an impact absorbing member for an automobile door, an automobile door, a blank, and a method for manufacturing the impact absorbing member for an automobile door, which can exhibit excellent tensile rigidity and impact resistance at low cost.

[0013] Means for solving problems

[0014] The specific embodiments of the present invention are as follows.

[0015] (1) A first embodiment of the present invention is an impact absorbing component for an automobile door, which is formed from a blank that is a single-piece blank or a spliced ​​blank, and the impact absorbing component for an automobile door comprises: a connecting strip portion extending along a first direction; and at least three connected portions, one end of which is connected to the connecting strip portion and extends along a second direction intersecting the first direction, and the connected portions have an impact absorbing portion with a closed cross-section structure.

[0016] (2) In the impact absorbing member for an automobile door described in (1) above, the blank may be the split blank, and the connecting belt portion and the connected portion may be integrally connected via a joining portion.

[0017] (3) In the impact absorbing component for a vehicle door described in (2) above, the connected portion may have an overlapping surface overlapping a portion of the connecting belt portion, and the joining portion may be formed on the overlapping surface, whereby the connecting belt portion and the connected portion are integrally connected.

[0018] (4) In the impact absorbing member for an automobile door described in (2) or (3) above, the joining portion may be a welded portion, and the welded portion may not have a HAZ softened portion.

[0019] (5) In the impact absorbing member for an automobile door according to any one of (1) to (4) above, the tensile strength of the connected portion may be 1100 MPa or more.

[0020] (6) In the impact absorbing member for an automobile door according to any one of (1) to (5) above, the Vickers hardness of the connected portion may be 350 HV or more.

[0021] (7) A second aspect of the present invention is a vehicle door comprising: the impact absorbing component for a vehicle door as described in any one of (1) to (6) above; and an exterior panel on which the impact absorbing component for a vehicle door is mounted.

[0022] (8) In the automobile door described in (7) above, the automobile door impact absorbing member may be attached to a reinforcing member.

[0023] (9) In the automobile door described in (8) above, the cross section of the reinforcing member perpendicular to its extension direction may have an open cross section, and a closed cross section structure may be formed by installing the connecting belt portion of the impact absorbing member for the automobile door on the reinforcing member.

[0024] (10) The third mode of the present invention is a blank for molding an impact absorbing component for an automobile door, the impact absorbing component for an automobile door having: a connecting belt portion extending along a first direction; and at least three connected portions, one end of which is connected to the connecting belt portion and extends along a second direction intersecting the first direction, the connected portion having an impact absorbing portion with a closed cross-sectional structure. The blank has: a connecting belt portion forming region extending along the first direction and molded into the connecting belt portion; and at least three connected portion forming regions, one end of which is connected to the connecting belt portion forming region and extends along the second direction and molded into the at least three connected portions, the blank being a single-piece blank or a spliced ​​blank.

[0025] (11) In the blank described in (10), the blank may be the split blank, and the connecting belt forming region and the connected portion forming region may be integrally connected via a joining portion.

[0026] (12) In the blank described in (11) above, the connected portion forming region may have an overlapping surface forming region overlapping with a portion of the connecting belt portion forming region, and the joining portion may be formed on the overlapping surface, thereby the connecting belt portion forming region and the connected portion forming region are integrally connected via the joining portion.

[0027] (13) In the blank described in any one of (10) to (12) above, a notch may be formed near a portion where the connecting belt forming region and the connected portion forming region are connected.

[0028] (14) A fourth aspect of the present invention is a method for manufacturing an impact absorbing component for an automobile door, wherein the impact absorbing component for an automobile door comprises: a connecting strip portion extending along a first direction; and at least three connected portions, one end of which is connected to the connecting strip portion and extends along a second direction intersecting the first direction, wherein the connected portion has an impact absorbing portion with a closed cross-section structure. The method for manufacturing the impact absorbing component for an automobile door comprises: a first step of stamping a blank which is a single-piece blank or a spliced ​​blank in a cold state to obtain an intermediate stamped product, wherein the blank has: a connecting strip portion forming area extending along the first direction, a forming area The connecting belt portion; and at least three connected portion forming areas, one end of which is connected to the connecting belt portion forming area, extending along the second direction, and formed into the at least three connected portions; and a second process, using the intermediate stamping molded product to perform stamping to obtain an impact absorbing component for a car door, in which, when the blank is the single-piece blank, the intermediate stamping molded product is stamped in a state heated to a temperature above the Ac3 point, and when the blank is the spliced ​​blank, the intermediate stamping molded product is stamped in a cold state or in a state heated to a temperature above the Ac3 point.

[0029] (15) In the method for manufacturing an impact absorbing component for an automobile door described in (14), the blank may be the split blank, and the connecting belt forming region and the connected portion forming region may be integrally connected via a joining portion.

[0030] (16) In the manufacturing method of the impact absorbing component for the automobile door described in (15) above, the above-mentioned connected portion forming area may have an overlapping surface forming area overlapping with a part of the above-mentioned connecting strip portion forming area, and the above-mentioned joining portion is formed on the above-mentioned overlapping surface, thereby the above-mentioned connecting strip portion forming area and the above-mentioned connected portion forming area are integrally connected through the above-mentioned joining portion.

[0031] (17) In the manufacturing method of the impact absorbing component for automobile door described in (15) or (16) above, in the second step, the intermediate stamped product may be stamped while being heated to a temperature above the Ac3 point.

[0032] Effects of the Invention

[0033] According to the present invention, it is possible to provide an impact absorbing member for an automobile door that can exhibit excellent tensile rigidity and impact resistance at low cost, an automobile door, a blank, and a method for producing the impact absorbing member for an automobile door. BRIEF DESCRIPTION OF THE DRAWINGS

[0034] Figure 1It is a perspective view showing the structure of a vehicle door to which the impact absorbing member according to the first embodiment of the present invention is mounted.

[0035] Figure 2 It means along Figure 1 Schematic diagram of the cross section along the dot-dash line II'.

[0036] Figure 3 This is a schematic diagram of the shock absorbing member according to the first embodiment as viewed from the vehicle cabin side.

[0037] Figure 4 It is a schematic diagram showing the dimensions of the test piece.

[0038] Figure 5 It means along Figure 3 Schematic diagram of the cross section along the dot-dash line II-II'.

[0039] Figure 6 yes Figure 3 An enlarged view of section A1 is shown.

[0040] Figure 7 It is a diagram for explaining the process for manufacturing the impact absorbing member of the first embodiment.

[0041] Figure 8 This is a schematic diagram showing a single blank for producing the shock absorbing member according to the first embodiment.

[0042] Fig. 9 It means that it will follow Figure 8 The cross section along the dashed line III-III' is a schematic diagram showing a state in which the single-piece blank is set in the first mold.

[0043] Fig.10 It means along Fig. 9 Schematic diagram of the cross section along the dashed line IV-IV'.

[0044] Fig.11 It means in Fig.10 The schematic diagram of the state in which the upper mold is lowered to the bottom dead point in the first mold shown.

[0045] Fig.12 This is a schematic diagram showing a state where a component molded by a first mold is set in a second mold.

[0046] Fig.13 It means along Fig.12 Schematic diagram of the cross section along the dot-dash line V-V'.

[0047] Fig.14 It means in Fig.13 The schematic diagram of the state in which the upper mold is lowered to the bottom dead point in the second mold shown.

[0048] Fig.15 It is a schematic diagram showing a state where the intermediate press-molded product is set in the third die.

[0049] Fig.16 It means along Fig.15 Schematic diagram of the cross section along the dashed line VI-VI'.

[0050] Fig.17 It means in Fig.16 The schematic diagram of the third mold is shown in the state where the upper mold is lowered to the bottom dead point.

[0051] Fig.18 It is a schematic diagram showing a shock absorbing member according to a second embodiment of the present invention.

[0052] Fig.19 yes Fig.18 An enlarged view of section A2 is shown.

[0053] Fig. 20 It is a diagram for explaining the process for manufacturing the impact absorbing member of the second embodiment.

[0054] Fig.21 It is a schematic diagram showing a split blank for producing the impact absorbing member according to the second embodiment.

[0055] Fig. 22 It is a schematic diagram showing a shock absorbing member according to a third embodiment of the present invention.

[0056] Fig.23 yes Fig. 22 An enlarged view of section A3 is shown.

[0057] Fig.24 It is a schematic diagram showing a blank for producing a shock absorbing member according to a third embodiment.

[0058] Fig.25 It is a schematic diagram showing a modified example of the blank.

[0059] Fig.26 It means from Fig.25 An enlarged view of a portion of the impact absorbing component formed from a blank is shown.

[0060] Fig. 27 The present invention is a perspective view showing the structure of a vehicle door to which a reinforcement member extending in the horizontal direction is further installed. DETAILED DESCRIPTION

[0061] Hereinafter, the present invention will be described in detail based on the embodiments. In addition, in this specification and the drawings, components having substantially the same functional configuration are denoted by the same reference numerals, and repeated descriptions are omitted.

[0062] In the following description, "integrally connected" refers to a method of connecting separate parts to each other by welding or the like. For example, when two blank steel plates are joined to each other by overlapping welding (spot welding, laser welding, etc.), it is expressed as "two blank steel plates are integrally connected". In addition, a blank formed by integrally connecting a plurality of blank steel plates having at least one of different plate thickness and strength or having the same plate thickness and strength is sometimes referred to as a spliced ​​blank. The spliced ​​blank is regarded as one blank.

[0063] "Connected in series" refers to a method in which different parts of a single component are continuously connected. For example, a T-shaped blank obtained by punching a single plate is "connected in series at two straight line parts". In addition, a blank connected in series in this way is sometimes called a single-piece blank.

[0064] (First Embodiment)

[0065] Hereinafter, a shock absorbing member 10 for an automobile door (hereinafter referred to as the shock absorbing member 10 ) according to a first embodiment of the present invention will be described.

[0066] The impact absorbing member 10 of the present embodiment is manufactured by press forming from a single sheet blank 100 made of steel as a raw material, and is mounted on a vehicle door 1 .

[0067] The automobile door 1 is a front door disposed on a side portion of the automobile.

[0068] Figure 1 FIG. 1 is a perspective view showing the structure of a vehicle door 1 equipped with a shock absorbing member 10, and shows a state where the vehicle door 1 is viewed from the outside of the vehicle. Figure 1 An exterior panel 1a described later is omitted in the figure.

[0069] also, Figure 2 It means along Figure 1 Schematic diagram of the cross section along the dot-dash line II'.

[0070] like Figure 1 as well as Figure 2 As shown, the automobile door 1 includes an outer panel 1 a , a reinforcement member 1 b , and an inner panel 1 c .

[0071] For the purpose of weight reduction, a high-strength steel sheet having a tensile strength of 340 MPa or more is preferably used for the exterior panel 1 a of the automobile door 1 .

[0072] Furthermore, from the viewpoint of weight reduction, the thickness of the exterior panel 1a is preferably 0.6 mm or less.

[0073] In addition, from the perspective of weight reduction, the thinner the thickness of the exterior panel 1a, the better. However, on the other hand, the tensile rigidity decreases. When the thickness of the exterior panel 1a is 0.3 mm or less, in order to ensure the tensile rigidity, the impact absorbing member 10 needs to be provided in a larger area, resulting in an increase in weight. Therefore, the thickness of the exterior panel 1a is preferably 0.3 mm or more.

[0074] like Figure 1 as well as Figure 2 As shown, the reinforcing member 1b extends in the horizontal direction (in the case of this embodiment, the vehicle front-rear direction) between the exterior panel 1a and the interior panel 1c of the automobile door 1. The reinforcing member 1b requires high bending rigidity in order to absorb the impact during a side collision and to reinforce the vicinity of the opening for raising and lowering the window glass.

[0075] like Figure 2 As shown, the reinforcing member 1b has a hat-shaped open cross section. That is, the reinforcing member 1b has a top plate portion 1b1, a pair of side wall portions 1b2 bent and connected from the ends of the top plate portion 1b1, and a pair of flange portions 1b3 bent and connected from the ends of the side wall portions 1b2.

[0076] The reinforcement member 1 b is attached to the automobile door 1 so that the top plate portion 1 b 1 faces the interior panel 1 c .

[0077] In addition, the reinforcing member 1b may include a joint member welded to connect the pair of flange portions 1b3 to each other. In this case, the reinforcing member 1b has a closed cross-sectional structure having an axis in the horizontal direction, thereby further improving the bending rigidity.

[0078] As a material of the reinforcing member 1 b , various materials such as steel, stainless steel, aluminum, aluminum alloy, and CFRP (carbon fiber reinforced plastic) can be used.

[0079] Figure 3 Schematic diagram of the impact absorbing member 10 when viewed from the inside of the vehicle toward the outside. Figure 3 As shown, the shock absorbing member 10 of the present embodiment includes a first connecting belt portion 11 , three connected portions 13 , and a second connecting belt portion 15 .

[0080] like Figure 1 As shown, the impact absorbing member 10 is mounted along the inner surface of the exterior panel 1a of the automobile door 1 with the first connecting belt portion 11 extending in a substantially horizontal direction and the connected portion 13 extending in a substantially vertical direction (in the vehicle height direction in this embodiment).

[0081] In the following description, the direction in which the first connecting belt portion 11 extends, that is, the longitudinal direction of the first connecting belt portion 11 is referred to as a first direction α. ​​Also, the direction in which the connected portion 13 extends, that is, the direction intersecting the first direction α is referred to as a second direction β.

[0082] The plate thickness of the impact absorbing member 10 is preferably 0.6 mm or more and 2.0 mm or less.

[0083] When the plate thickness of the shock absorbing member 10 is 2.0 mm or less, the shock absorbing member 10 can be reduced in weight. The plate thickness of the shock absorbing member 10 is more preferably 1.2 mm or less.

[0084] On the other hand, when the thickness of the shock absorbing member 10 is 0.6 mm or more, the shock absorbing performance of the shock absorbing member 10 can be ensured and the bending rigidity of the first connecting belt portion 11 can be sufficiently ensured, so that the mounting operation of the automobile door 1 to the shock absorbing member 10 can be simplified.

[0085] From the viewpoint of weight reduction, the impact absorbing member 10 preferably has a tensile strength of 1100 MPa or more as measured at the connected portion 13 .

[0086] Here, the tensile strength is the tensile strength measured on a test piece collected from a portion of the connected portion 13 excluding a portion where the strength locally changes, such as a bent deformed portion and a welded portion.

[0087] Test piece use Figure 4 The test pieces were of the dimensions shown. The thickness of the test pieces was the same as that of the components. The tensile strength was measured by conducting a tensile test at a tensile speed (crosshead displacement speed) of 10 mm / min in accordance with JIS Z 2241 (2011).

[0088] Furthermore, in the impact absorbing member 10 , from the viewpoint of weight reduction, the Vickers hardness measured at the connected portion 13 is preferably 350 HV or more.

[0089] Here, the Vickers hardness is measured according to the Vickers hardness test method specified in JIS Z 2244-1:2020 at five points at a distance of 10 mm or more from a portion other than a portion where hardness locally changes, such as a bent deformed portion and a welded portion, in the connected portion 13 .

[0090] The Vickers hardness was measured at five points on the cut surface at a distance of 1 / 4 of the plate thickness from the surface in the plate thickness direction, with a load (test force) of 9.8 N and at a distance of 1.0 mm or more.

[0091] The average value of the Vickers hardnesses measured at these five points is defined as the Vickers hardness of the connected portion 13 .

[0092] As will be described later, the method for manufacturing the shock absorbing member 10 includes a second step of hot pressing. Therefore, the shock absorbing member 10 generally has a martensitic structure.

[0093] The first connecting belt portion 11 is a portion that connects and aligns the three connected portions 13. The first connecting belt portion 11 is attached to the automobile door 1 by welding or the like.

[0094] Here, if Figure 1 as well as Figure 2 As shown, the first connecting belt portion 11 is preferably mounted by welding so as to connect a pair of flange portions 1 b 3 of a reinforcing member 1 b having a hat-shaped open cross section to each other.

[0095] As described above, by attaching a joint member welded to the reinforcing member 1b so as to connect the pair of flange portions 1b3 to each other to form a closed cross-section structure, the bending rigidity can be improved. However, in this case, the number of components increases.

[0096] On the other hand, by making the first connecting belt portion 11 welded so as to connect the pair of flange portions 1b3 to each other, a closed cross-section structure can be formed without increasing the number of components, thereby achieving an effect of improving bending rigidity. Therefore, the automobile door 1 can be further reduced in weight and manufactured at a lower cost.

[0097] Alternatively, the first connecting belt portion 11 may be mounted only on a portion of the reinforcing member 1b, for example, only on the lower flange portion 1b3 (if a joining member is mounted, the portion of the joining member mounted on the lower flange portion 1b3).

[0098] The connected portion 13 is a portion extending from an end edge 11 a of the first connecting belt portion 11 in the width direction (direction perpendicular to the first direction α) along the second direction β.

[0099] like Figure 3 As shown, the connected portion 13 has a shock absorbing portion 13 a , a first transition portion 13 b , and a second transition portion 13 c .

[0100] Figure 5 It means along Figure 3 FIG. 2 is a schematic diagram of a cross section taken along a dashed line II-II′, ie, a cross section of the impact absorbing portion 13 a perpendicular to the second direction β.

[0101] like Figure 5 As shown, the impact absorbing portion 13a has a closed cross-sectional structure, that is, the impact absorbing portion 13a has a bottom surface 13a1, a pair of side wall surfaces 13a2 bent and connected from the ends of the bottom surface 13a1, and two top surfaces 13a3 bent and connected from the ends of the side wall surfaces 13a2.

[0102] Furthermore, the ends of the two top surfaces 13a3 are in contact or joined with each other to form a closed cross-sectional structure.

[0103] In the present application, when a gap of 3 mm or less is formed between the edges of the two top surfaces 13 a 3 , it can be regarded as a closed cross-sectional structure.

[0104] This is because when a load is applied to the impact absorbing portion 13a from the outside of the vehicle toward the inside, the impact absorbing portion 13a bends and deforms, and the cross section of the impact absorbing portion 13a deforms in a direction in which the edges of the top surfaces 13a3 contact each other, thereby closing the gap.

[0105] The impact absorbing portion 13 a has a closed cross-sectional structure, thereby providing tensile rigidity to the exterior panel 1 a and increasing the amount of impact absorption when the automobile door 1 is subjected to an impact caused by a collision.

[0106] The cross-sectional shape may be circular, elliptical, trapezoidal, etc., but in order to further increase the impact absorption, a rectangular closed cross-sectional structure is preferably adopted.

[0107] The impact absorbing portion 13a is provided so that the bottom surface 13a1 is at least partially joined along the inner surface of the exterior panel 1a, thereby imparting tensile rigidity to the exterior panel 1a and increasing the amount of impact absorption when the automobile door 1 is subjected to an impact caused by a collision.

[0108] Furthermore, the bottom surface 13a1 and the inner surface of the exterior panel 1a may be joined together using an adhesive such as an adhesive sealant.

[0109] The impact absorbing portion 13 a forms a second transition portion 13 c extending to the connected portion 13 , and the three second transition portions 13 c are continuously connected to the second connecting belt portion 15 .

[0110] like Figure 1 As shown, the second connecting belt portion 15 is in contact with the lower end of the interior panel 1 c of the automobile door 1 and is mounted by welding or the like.

[0111] When the second connecting belt portion 15 is not provided, the front ends (lower ends) of the three connected portions 13 may be brought into contact with the lower ends of the interior panel 1 c of the automobile door 1 and attached by welding or the like.

[0112] Figure 6 yes Figure 3 The enlarged view of the A1 section is shown. Figure 6As shown, the first transition portion 13b extends along the second direction β from the widthwise end edge 11a of the first connecting belt portion 11. The first transition portion 13b is processed so as to gradually approach the cross-sectional shape of the impact absorbing portion 13a as it moves away from the first connecting belt portion 11.

[0113] like Figure 5 as well as Figure 6 As shown, the first transition portion 13b has a bottom surface 13b1 connected to the bottom surface 13a1 of the impact absorbing portion 13a, a side wall surface 13b2 connected to the side wall surface 13a2 of the impact absorbing portion 13a, and a top surface 13b3 connected to the top surface 13a3 of the impact absorbing portion 13a.

[0114] The impact absorbing member 10 of this embodiment is formed from a single blank 100, so the bottom surface 13b1 is continuously connected to the first connecting belt portion 11. That is, there is no physical boundary such as a joining mark between the bottom surface 13b1 and the first connecting belt portion 11.

[0115] In the first transition portion 13 b , since the flat-plate-shaped first connecting band portion 11 and the shock absorbing portion 13 a having a closed cross-section structure are connected by gently changing the cross-section, it is possible to suppress the occurrence of cracks when machining the shock absorbing portion 13 a .

[0116] According to the impact absorbing member 10 of the present embodiment, by forming the impact absorbing portion 13 a having a closed cross-sectional structure, it is possible to exhibit excellent tensile rigidity and impact resistance while being lightweight.

[0117] Furthermore, since the impact absorbing member 10 is press-formed from the single blank 100 , the first connecting belt portion 11 and the three connected portions 13 are continuously connected, and therefore, there is no need to join the first connecting belt portion 11 and the connected portions 13 after press-forming.

[0118] Furthermore, compared with the case where the first connecting belt portion 11 and the three connected portions 13 are processed separately, the number of components and the number of dies can be reduced.

[0119] Furthermore, since it is not necessary to separately process the first connecting band portion 11 and the three connected portions 13 and join them by welding, cracks caused by the HAZ softening portion formed during welding can be avoided.

[0120] Furthermore, when the impact absorbing member 10 is mounted on the automobile door 1 , the impact absorbing member 10 only needs to be mounted on the automobile door 1 as a single component, so the mounting operation is simpler than when each component is transported, positioned, and mounted.

[0121] Therefore, according to the impact absorbing member 10 of the present embodiment, the automobile door 1 capable of exhibiting excellent tensile rigidity and impact resistance can be manufactured at low cost.

[0122] Next, a method for manufacturing the impact absorbing member 10 will be described.

[0123] Figure 7 The diagram is for explaining the process of manufacturing the impact absorbing member 10 .

[0124] The impact absorbing member 10 can be manufactured by performing a first step of press-forming the single blank 100 in a cold state to obtain an intermediate press-formed product 120 and a second step of hot-pressing the intermediate press-formed product 120 , and further performing trimming as needed.

[0125] The single blank 100 can be obtained by punching out one blank steel plate.

[0126] Figure 8 is a schematic diagram of a single sheet blank 100 .

[0127] The single blank 100 has a first connecting belt portion forming region 101 formed into a first connecting belt portion 11 by a stamping process, a three connected portion forming region 103 formed into three connected portions 13 by a stamping process, and a second connecting belt portion forming region 105 formed into a second connecting belt portion 15 by a stamping process.

[0128] In addition, the connected portion forming area 103 includes an impact absorbing portion forming area 103a formed into an impact absorbing portion 13a by a stamping process, a first transition portion forming area 103b formed into a first transition portion 13b by a stamping process, and a second transition portion forming area 103c formed into a second transition portion 13c by a stamping process.

[0129] The single-piece blank 100 is obtained by punching a single blank steel plate, and therefore the first connecting band forming region 101 , the connected portion forming region 103 , and the second connecting band forming region 105 are connected to each other.

[0130] The plate thickness of the single blank 100 is the same as the plate thickness of the impact absorbing member 10 , and is preferably 0.6 mm or more and 2.0 mm or less.

[0131] In order to prevent cracks from being generated in the first step due to cold pressing, the single blank 100 is preferably 800 MPa or less.

[0132] (First process)

[0133] In the first step, the single blank 100 is press-formed in a cold state to obtain an intermediate press-formed product 120. In the example described here, the intermediate press-formed product 120 is manufactured by cold press forming twice.

[0134] Cold stamping refers to stamping at room temperature.

[0135] (Based on the molding of the first mold)

[0136] First, a single sheet of blank 100 is formed into a component 110 using a first mold 1000 .

[0137] Specifically, the connected portion forming region 103 of the single-piece blank 100 is molded into the connected portion forming region 113 of the component 110 .

[0138] Fig. 9 It means that it will follow Figure 8 The cross section along the dashed line III-III′ is a schematic diagram showing a state where the single-piece blank 100 is set in the first mold 1000 .

[0139] Fig.10 It means along Fig. 9 Schematic diagram of the cross section along the dashed line IV-IV'.

[0140] like Fig. 9 as well as Fig.10 As shown, the first mold 1000 is composed of a lower mold 1100 and an upper mold 1200 .

[0141] The lower mold 1100 includes a lower mold body 1110 and a gasket 1120. The gasket 1120 is connected to, for example, a pressurizing device (not shown) disposed below the lower mold body 1110, and is thus independently movable up and down relative to the lower mold body 1110.

[0142] The lower mold body 1110 has a placement surface 1111 on which the individual blank 100 is placed, and a groove portion 1112 formed to be recessed from the placement surface 1111 .

[0143] The gasket 1120 is provided in the groove portion 1112 of the lower mold body 1110 so that the top surface 1120U thereof faces the lower surface of the single-piece blank 100 .

[0144] like Fig. 9 As shown, the pad 1120 has a structure in which a first portion 1121 for placing the first connecting belt portion forming region 101 of the single-piece blank 100 and a second portion 1123 for placing the connected portion forming region 103 of the single-piece blank 100 are integrally formed.

[0145] The upper mold 1200 has an upper mold body 1210 .

[0146] The upper mold body 1210 has a convex shape corresponding to the groove 1112 of the lower mold body 1110. The upper mold body 1210 is provided so that its bottom surface 1210D faces the upper surface of the single blank 100.

[0147] The upper end of the upper mold body 1210 is connected to a driving mechanism (not shown) so that the upper mold body 1210 can move up and down freely.

[0148] like Fig. 9 As shown, the upper mold body 1210 has a structure in which a first portion 1211 facing the first connecting belt forming region 101 of the single-piece blank 100 and a second portion 1213 facing the connected portion forming region 103 of the single-piece blank 100 are integrally formed.

[0149] Fig.11 It means in Fig.10 FIG. 1 is a schematic diagram showing a state in which the upper mold 1200 of the first mold 1000 is lowered to the bottom dead point.

[0150] like Fig.11 As shown, by lowering the upper die body 1210 to the bottom dead center, the single-piece blank 100 can be punched into the component 110 .

[0151] When the upper die body 1210 is lowered, the center portion in the width direction of the impact absorbing portion forming region 103a of the single blank 100 is clamped by the bottom surface 1210D of the upper die body 1210 and the top surface 1120U of the pad 1120. Then, when the upper die body 1210 is further lowered from this state, the pad 1120 also follows and the single blank 100 is pressed and formed into the component 110 in a state where the single blank 100 is clamped by the top surface 1120U and the bottom surface 1210D.

[0152] (Molding based on the second mold)

[0153] Next, the component 110 press-formed by the first die is formed into an intermediate press-formed product 120 using the second die 2000 .

[0154] Fig.12 It is a schematic diagram showing a state where the component 110 is set in the second mold 2000 .

[0155] Fig.13 It means along Fig.12 Schematic diagram of the cross section along the dot-dash line V-V'.

[0156] like Fig.12 as well as Fig.13 As shown, the second mold 2000 is composed of a lower mold 2100 and an upper mold 2200 .

[0157] The lower mold 2100 has a lower mold body 2110. The lower mold body 2110 has a top surface 2110U on which the mounting member 110 is placed.

[0158] like Fig.12 As shown, the lower mold body 2110 has a structure in which a first portion 2111 of the bottom surface of the first connecting belt forming area 111 for placing the component 110 and a second portion 2113 of the bottom surface of the connected portion forming area 113 for placing the component 110 are integrally formed.

[0159] like Fig.12 As shown, the upper mold 2200 includes an upper mold body 2210 and a gasket 2220. The gasket 2220 is connected to, for example, a pressurizing device (not shown) disposed on the upper side of the upper mold body 2210, and is thus independently movable up and down relative to the upper mold body 2210.

[0160] like Fig.13 As shown, the upper mold body 2210 has an inverted U-shaped depression formed by an inclined surface 2211, a vertical wall surface 2212 and a top surface 2213. The upper end of the upper mold body 2210 is connected to a driving mechanism not shown in the figure, thereby being able to move up and down freely. The upper mold body 2210 is arranged above the second portion 2113 of the lower mold body 2110. That is, it is arranged above the position of the connected portion forming area 113 of the component 110.

[0161] The gasket 2220 is disposed above the first portion 2111 of the lower mold body 2110 . That is, it is disposed above the position of the first connecting belt portion forming region 111 of the component 110 .

[0162] Fig.14 It means in Fig.13 The schematic diagram of the second mold 2000 is shown in the state where the upper mold 2200 is lowered to the bottom dead point.

[0163] With the first connecting band forming region 111 of the component 110 clamped by the first portion 2111 of the lower mold body 2110 and the gasket 2220 , the upper mold body 2210 is lowered to the bottom dead center, thereby stamping the component 110 into an intermediate stamped product 120 .

[0164] When the upper mold body 2210 is lowered, the edge of “the portion corresponding to the top surface 13 a 3 ” of the component 110 comes into contact with the inclined surface 2211 of the upper mold body 2210 .

[0165] When the upper mold body 2210 is further lowered, the edge of the “portion corresponding to the top surface 13 a 3 ” is pressed while sliding on the inclined surface 2211 , and is formed into an intermediate pressed product 120 .

[0166] (Second process)

[0167] In the second step, the intermediate press-molded product 120 heated to a temperature equal to or higher than the Ac3 point is molded into the impact absorbing member 10 using the third mold 3000 .

[0168] As a method for heating the intermediate stamping molded product 120, heating by a heating furnace or electric heating can be used. However, since temperature management is easy and even a complex shape can be heated uniformly, it is preferred to heat by a heating furnace. Examples of heating furnaces include gas heating furnaces, electric heating furnaces, infrared heating furnaces, and high-frequency heating furnaces.

[0169] The Ac3 point is a temperature at which a steel material is austenitized, and is represented by the following formula as an example.

[0170] Ac3 point (℃) = 910-203×√C (mass%)-30×Mn (mass%)-11×Cr (mass%)+44.7×Si (mass%)+400×Al (mass%)+700×P (mass%)-15.2×Ni (mass%)-20×Cu (mass%)+400×Ti (mass%)+104×V (mass%)+31.5×Mo (mass%)

[0171] In addition, C, Mn, Cr, Si, Al, P, Ni, Cu, Ti, V, and Mo in the above formula are the contents of chemical components of the steel constituting the connected portion forming region 103.

[0172] Fig.15 1 is a schematic diagram showing a state where the intermediate press-molded product 120 is set in the third die 3000 .

[0173] Fig.16 It means along Fig.15 Schematic diagram of the cross section along the dashed line VI-VI'.

[0174] like Fig.15 as well as Fig.16 As shown, the third mold 3000 is composed of a lower mold 3100 and an upper mold 3200 .

[0175] The lower mold 3100 has a lower mold body 3110. The lower mold body 3110 has a recess having a shape corresponding to the shock absorbing member 10.

[0176] like Fig.15 As shown, the lower mold body 3110 has a structure in which a first portion 3111 is integrally formed with a first connecting belt portion forming area 121 for placing the intermediate stamping molded product 120, and a second portion 3113 is configured with a connected portion forming area 123 of the intermediate stamping molded product 120 above.

[0177] The upper mold 3200 includes an upper mold body 3210 and a gasket 3220 .

[0178] The upper mold body 3210 has a convex portion 3211 having a shape corresponding to the concave portion of the lower mold body 3110 .

[0179] like Fig.15 As shown, the gasket 3220 is provided above the portion corresponding to the first connecting belt portion forming region 121 of the intermediate stamped product 120. The gasket 3220 is connected to a pressurizing device (not shown) disposed on the upper mold body 3210, for example, and is thus independently movable up and down relative to the upper mold body 3210.

[0180] A cooling mechanism using a cooling medium such as water cooling is built into the lower mold 3100 and the upper mold 3200 .

[0181] Fig.17 It means in Fig.16 The schematic diagram of the third mold 3000 is shown in the state where the upper mold 3200 is lowered to the bottom dead point.

[0182] The impact absorbing member 10 can be obtained by placing the intermediate press-molded product 120 , which has been preheated to a temperature equal to or higher than the Ac3 point, on the lower die 3100 and lowering the upper die 3200 to the bottom dead center.

[0183] By incorporating a cooling mechanism into the lower die 3100 and the upper die 3200 , the intermediate press-formed product 120 in a heated state can be held at the bottom dead center of the press forming process, thereby enabling more efficient quenching.

[0184] The molded product held at the bottom dead center can be cooled by cooling the mold after being cooled by a cooling medium, or can be directly cooled by cooling the cooling medium supplied from the molding surface of the mold. By directly cooling with a cooling medium, quenching can be performed more efficiently.

[0185] In addition, it is not necessary to provide a cooling mechanism for the mold.

[0186] Alternatively, after the press forming is completed, a member obtained by trimming as necessary and cutting off unnecessary portions may be used as the shock absorbing member 10 .

[0187] According to the method of manufacturing the impact absorbing member 10 using the single-piece blank 100 as described above, it is not necessary to weld the first connecting belt portion 11 and the connected portion 13 after press forming.

[0188] Furthermore, the plurality of shock absorbing portions 13a can be molded into a single shock absorbing member 10 and assembled to the automobile door 1. Therefore, the shock absorbing member 10 can be manufactured efficiently and at low cost.

[0189] (Second Embodiment)

[0190] Hereinafter, a shock absorbing member 20 for an automobile door (hereinafter referred to as the shock absorbing member 20 ) according to a second embodiment of the present invention will be described.

[0191] The impact absorbing member 10 of the first embodiment is a member manufactured by press forming a single-piece blank 100 made of steel, but the impact absorbing member 20 of the second embodiment is different from the first embodiment in that it is a member manufactured by press forming a split blank 200 made of steel.

[0192] In order to simplify the description, the description overlapping with the first embodiment will be omitted.

[0193] Fig.18 Schematic diagram of the impact absorbing component 20. Fig.18 As shown in FIG. 1 , the shock absorbing member 20 of the present embodiment includes a first connecting belt portion 21 , three connected portions 23 , and a second connecting belt portion 25 .

[0194] The preferred plate thickness, tensile strength, and Vickers hardness of the impact absorbing member 20 are the same as those described for the impact absorbing member 10 of the first embodiment. However, since the impact absorbing member 20 is formed using the split blank 200, the first connecting belt portion 21, the three connected portions 23, and the second connecting belt portion 25 can have different plate thicknesses, tensile strengths, and Vickers hardnesses.

[0195] In addition, the shock absorbing member 20 may have a martensitic structure. More specifically, at least one of the first connecting band portion 21 , the connected portion 23 , and the second connecting band portion 25 in the shock absorbing member 20 may have substantially a martensitic structure.

[0196] The first connecting belt portion 21 is a portion that overlaps with the three connected portions 23 and is integrally connected by the spot welding portions w. The first connecting belt portion 21 is attached to the automobile door 1 by welding or the like.

[0197] The spot welded portion w is an example of a welded portion. From the viewpoint of workability, it is preferable to form the welded portion by spot welding, but the welded portion may be a linear welded portion by laser welding or plasma welding.

[0198] In addition, a joining portion using rivets or the like may be used instead of the welded portion.

[0199] The connected portion 23 is a portion extending from an end edge 21 a of the first connecting belt portion 21 in the width direction (a direction perpendicular to the first direction α) along the second direction β.

[0200] like Fig.18As shown, the connected portion 23 has a shock absorbing portion 23 a , a first transition portion 23 b , and a second transition portion 23 c .

[0201] Fig.19 yes Fig.18 The enlarged view of the A2 section is shown. Fig.19 As shown, the first transition portion 23b extends along the second direction β from the widthwise end edge 21a of the first connecting belt portion 21. The first transition portion 23b is processed into a cross-sectional shape that gradually approaches the impact absorbing portion 23a as it moves away from the first connecting belt portion 21.

[0202] like Fig.19 As shown, the first transition portion 23b has a bottom surface 23b1, a side wall surface 23b2, and a top surface 23b3 which are continuously connected to the impact absorbing portion 23a.

[0203] In the impact absorbing member 20 of the present embodiment, the overlapping surface 23E overlapping the first connecting strip portion 21 is connected to the end of the bottom surface 23b1 so as to be continuous. The overlapping surface 23E is connected to the first connecting strip portion 21 by the spot welding portion w.

[0204] In the first transition portion 23 b , the flat-plate-shaped first connecting band portion 21 and the shock absorbing portion 23 a having a closed cross-sectional structure are connected with a gently changing cross-section, so that cracking during machining of the shock absorbing portion 23 a can be suppressed.

[0205] Furthermore, since the overlapping surface 23E connected to the first transition portion 23 b overlaps with the first connecting belt portion 21 , it is possible to obtain an effect of improving the bending rigidity and strength of the first connecting belt portion 21 .

[0206] According to the impact absorbing member 20 of the present embodiment, by forming the impact absorbing portion 23 a having a closed cross-sectional structure, it is possible to exhibit excellent tensile rigidity and impact resistance while being lightweight.

[0207] Furthermore, the impact absorbing member 20 is press-formed from the split blank 200 , whereby the first connecting belt portion 21 and the three connected portions 23 are integrally connected, and therefore, there is no need to join the first connecting belt portion 21 and the connected portions 23 after press-forming.

[0208] Furthermore, compared with the case where the first connecting belt portion 21 and the three connected portions 23 are processed separately, the number of components and the number of dies can be reduced.

[0209] Furthermore, when hot pressing is selected in the second step described later, the HAZ softened portion formed at the spot welded portion w of the split blank 200 can be reduced or eliminated by the heat input during hot pressing, so cracks caused by the HAZ softened portion can also be suppressed.

[0210] In addition, in the present application, the HAZ softened area refers to a portion in the peripheral area of ​​the weld (weld line) (the area of ​​both welded parts) where the metal structure changes due to the influence of the thermal cycle during welding and the hardness is reduced by 20% or more compared with the base material. Specifically, the change in the metal structure is a change to tempered martensite due to tempering, and a change from a ferrite-austenite two-phase region to a mixed structure containing ferrite due to cooling.

[0211] The absence of a HAZ softened portion can be confirmed by the following procedure.

[0212] First, at 5 points at a distance of 10 mm or more from the center point of the weld (or the center line of the weld line), the Vickers hardness of the base material is measured according to the Vickers hardness test method specified in JIS Z 2244-1: 2020. Specifically, in the cross-section including the weld, at a distance of 1 / 4 of the plate thickness from the surface toward the plate thickness direction, 5 points at a distance of 1.0 mm or more are measured with a load (test force) of 9.8 N. The average value of the Vickers hardness measured at these 5 points is taken as the Vickers hardness of the base material.

[0213] Next, in an area within 10 mm from the center point of the weld (or the center line of the weld line), the Vickers hardness is measured at a position 1 / 4 of the thickness from the surface in the plate thickness direction in the cut surface including the weld, with a load (test force) of 3 N and a measurement interval of 0.5 mm according to the Vickers hardness test method specified in JIS Z 2244-1:2020. In the case of overlap, the Vickers hardness is measured at a position 1 / 4 of the thickness from the surface of the overlapping side in the plate thickness direction. When the minimum value of the Vickers hardness exceeds 80% of the Vickers hardness of the parent material, it is judged that there is no HAZ softening portion.

[0214] When cold pressing is selected in the second step described below, the HAZ softening portion may be reduced or eliminated by local tempering heat treatment after spot welding (for example, high-frequency heating, laser heating, post-energization during spot welding).

[0215] Furthermore, when the impact absorbing member 20 is mounted on the automobile door 1 , the impact absorbing member 20 only needs to be mounted on the automobile door 1 as a single component, so the mounting operation is simpler than when each component is transported, positioned, and mounted.

[0216] Therefore, according to the impact absorbing member 20 of the present embodiment, the automobile door 1 capable of exhibiting excellent tensile rigidity and impact resistance can be manufactured at low cost.

[0217] Next, a method for manufacturing the impact absorbing member 20 will be described.

[0218] Fig. 20 It is a diagram for explaining the process for manufacturing the impact absorbing member 20 .

[0219] The impact absorbing member 20 can be manufactured by performing a first step of press-forming the split blank 200 in a cold state to obtain an intermediate press-formed product and a second step of cold-pressing or hot-pressing the intermediate press-formed product and performing trimming as necessary.

[0220] The connected portion forming region in the split blank 200 has an overlapping surface forming region overlapping a portion of the connecting belt portion forming region, and the joining portion is formed on the overlapping surface, whereby the connecting belt portion forming region and the connected portion forming region are integrally connected via the joining portion.

[0221] The method for manufacturing the shock absorbing member 20 is substantially the same as the method for manufacturing the shock absorbing member 10 of the first embodiment, except that the split blank 200 is used instead of the single blank 100 , and therefore a detailed description thereof will be omitted.

[0222] Furthermore, when the split blank 200 is used, cold pressing is selected in the second step, so that, for example, a high-strength steel sheet can be applied only to the impact absorbing portion 23a. Therefore, the automobile door 1 that can exhibit excellent tensile rigidity and impact resistance can be manufactured at a lower cost.

[0223] On the other hand, when the split blank 200 is used, by selecting hot pressing in the second step, the HAZ softened portion can be eliminated even without performing the tempering heat treatment.

[0224] The combined blank 200 can be obtained by integrally connecting a plurality of blank steel plates by the spot welding portion w.

[0225] Fig.21 2 is a schematic diagram of a spliced ​​blank 200 .

[0226] The split blank 200 has a first connecting belt portion forming region 201 formed into a first connecting belt portion 21 by a stamping process, a three connected portion forming region 203 formed into three connected portions 23 by a stamping process, and a second connecting belt portion forming region 205 formed into a second connecting belt portion 25 by a stamping process.

[0227] In addition, the connected portion forming area 203 has an impact absorbing portion forming area 203a formed into an impact absorbing portion 23a through a stamping process, a first transition portion forming area 203b formed into a first transition portion 23b through a stamping process, and a second transition portion forming area 203c formed into a second transition portion 23c through a stamping process.

[0228] The plate thickness and strength of the split blank 200 may be within the same range as the plate thickness and strength of the single blank 100 described in the first embodiment.

[0229] However, since the combined blank 200 is obtained by overlapping a plurality of blank steel plates, different plate thicknesses, strengths, and component compositions can be used between the first connecting belt portion forming region 201, the three connected portion forming regions 203, and the second connecting belt portion forming region 205. In the case of using the overlapping method, the allowable range of the dimensional error of the outer shape of each region before joining can be expanded compared to the case of using the butt-jointing method. In addition, in the case of using the overlapping method, spot welding can be used, so the impact absorbing component 10 can be manufactured efficiently and at low cost.

[0230] According to the method of manufacturing the impact absorbing member 20 using the split blank 200 as described above, it is not necessary to weld the first connecting belt portion 21 and the connected portion 23 after press forming.

[0231] Furthermore, the plurality of shock absorbing portions 23a can be molded into a single shock absorbing member 20 and mounted on the automobile door 1. Therefore, the shock absorbing member 20 can be manufactured efficiently and at low cost.

[0232] Furthermore, the roughly rectangular blank steel plates corresponding to the first connecting belt portion forming region 201, the connected portion forming region 203, and the second connecting belt portion forming region 205 are punched out and then joined to each other, thereby obtaining the combined blank 200. Therefore, the amount of scrap of the blank steel plates can be reduced. Therefore, the yield rate is improved, and the impact absorbing member 20 can be manufactured at a lower cost.

[0233] In the second embodiment, the split blank 200 joined at the overlapping portion is taken as an example, but a split blank in which the end edges of the blank steel plates are joined by laser welding, plasma welding, or the like may be employed.

[0234] Furthermore, in the above-described split blank 200 , the joining portion (welded portion w) exists at the boundary between the first connecting belt portion 21 and the connected portion 23 , but the present invention is not limited thereto.

[0235] (Third Embodiment)

[0236] Hereinafter, a shock absorbing member 30 for an automobile door (hereinafter referred to as the shock absorbing member 30 ) according to a third embodiment of the present invention will be described.

[0237] The shock absorbing members 10 and 20 of the first and second embodiments are formed using a single blank 100 or a split blank 200 in which the connected portion forming regions 103 and 203 are linear.

[0238] The basic structure of the shock absorbing member 30 of the third embodiment is the same as that of the shock absorbing members 10 and 20 of the first and second embodiments, but is different in that a blank 300 having a shape in which the notch C is formed is used.

[0239] In order to simplify the description, the description overlapping with the first embodiment and the second embodiment will be omitted.

[0240] Fig. 22 Schematic diagram of the impact absorbing component 30. Fig. 22 As shown, the shock absorbing member 30 of the present embodiment includes a first connecting belt portion 31 , three connected portions 33 , and a second connecting belt portion 35 .

[0241] The first connecting belt portion 31 is a portion that integrally connects the three connected portions 33 through the spot welding portions w. The first connecting belt portion 31 is attached to the automobile door 1 by welding or the like.

[0242] The connected portion 33 is a portion extending from an end edge 31 a of the first connecting belt portion 31 in the width direction (a direction perpendicular to the first direction α) along the second direction β.

[0243] like Fig. 22 As shown, the connected portion 33 has a shock absorbing portion 33 a , a first transition portion 33 b , and a second transition portion 33 c .

[0244] Fig.23 yes Fig. 22 The enlarged view of the A3 section is shown. Fig.23 As shown, the first transition portion 33 b extends from the end edge 31 a of the first connecting belt portion 31 in the width direction along the second direction β.

[0245] like Fig.23 As shown, the first transition portion 33 b has a bottom surface 33 b 1 continuously connected to the bottom surface of the impact absorbing portion 33 a .

[0246] That is, the first transition portion 33 b connects the first connecting belt portion 31 and the bottom surface of the impact absorbing portion 33 a in a planar shape.

[0247] In the first transition portion 33b, the flat first connecting band portion 31 is connected to the flat bottom surface of the shock absorbing portion 33a having a closed cross-section structure without significantly changing the cross-sectional shape, so that cracks can be suppressed from being generated when machining the shock absorbing portion 33a.

[0248] Furthermore, since the length of the first transition portion 33 b in the second direction β can be reduced, the length of the shock absorbing portion 33 a in the second direction β can be increased. Therefore, the shock absorption amount of the shock absorbing portion 33 a can be increased.

[0249] Therefore, according to the impact absorbing member 30 of the present embodiment, the automobile door 1 capable of exhibiting excellent tensile rigidity and impact resistance can be manufactured at low cost.

[0250] The method for manufacturing the shock absorbing member 30 is substantially the same as the method for manufacturing the shock absorbing member 10 of the first embodiment, except that the blank 300 is used instead of the single blank 100 , and therefore the description thereof is omitted.

[0251] Next, the blank 300 will be described.

[0252] Fig.24 is a schematic diagram of a blank 300 .

[0253] The blank 300 includes a first connecting belt portion forming region 301 formed into the first connecting belt portion 31 by a stamping process, a three connected portion forming region 303 formed into three connected portions 33 by a stamping process, and a second connecting belt portion forming region 305 formed into the second connecting belt portion 35 by a stamping process.

[0254] In addition, the connected portion forming area 303 includes an impact absorbing portion forming area 303a formed into an impact absorbing portion 33a through a stamping process, a first transition portion forming area 303b formed into a first transition portion 33b through a stamping process, and a second transition portion forming area 303c formed into a second transition portion 33c through a stamping process.

[0255] In the blank 300 , in the first transition portion forming region 303 b , cutouts C are formed at both ends in the width direction.

[0256] By forming such a cutout C, when the blank 300 is pressed to form the shock absorbing member 30, the flat first connecting band portion 31 can be connected to the flat bottom surface of the shock absorbing portion 33a of the closed cross-section structure in the first transition portion 33b. Therefore, it is possible to suppress the generation of cracks when processing the shock absorbing portion 33a.

[0257] Furthermore, since the length of the first transition portion 33 b in the second direction β can be reduced, the length of the shock absorbing portion 33 a in the second direction β can be increased. Therefore, the shock absorption amount of the shock absorbing portion 33 a can be increased.

[0258] In addition, you can also Fig.25 As in the blank 300A of the illustrated modification, the cutout C is formed in the first connecting belt portion.

[0259] In the single-piece blank 100 of the first embodiment or the split blank 200 of the second embodiment, the method of manufacturing the impact absorbing member 30 using the blank 300 having the cutout C as described above does not require welding the first connecting belt portion 31 and the connected portion 33 after press forming.

[0260] Furthermore, a plurality of shock absorbing portions 33 a may be formed into a single shock absorbing member 30 and mounted on the automobile door 1 .

[0261] Furthermore, by forming the notch C, it is possible to suppress the occurrence of cracks when machining the impact absorbing portion 33 a.

[0262] in addition, Fig.26 Is Fig.25 FIG. 3 is a partial enlarged view of the impact absorbing component 30A formed from the blank 300A. Fig.26 As shown, a plane portion Q formed by folding a portion of the first transition portion 33b is formed at the end of the first transition portion 33b of the connected portion 33. When the plane portion Q is overlapped and arranged on the flange portion 1b3 of the reinforcing member 1b, the collision load applied to the impact absorbing member 10 can be efficiently supported by the reinforcing member 1b.

[0263] Therefore, the automobile door 1 capable of exhibiting excellent tensile rigidity and impact resistance can be manufactured at low cost.

[0264] The preferred embodiments of the present invention are described in detail with reference to the accompanying drawings, but the present invention is not limited to the examples described above. Obviously, anyone with common knowledge in the technical field to which the present invention belongs can think of various variations or modifications within the scope of the technical concept of the present invention, and it should be understood that these also belong to the technical scope of the present invention.

[0265] For example, you can also Fig. 27 As shown in the automobile door 2, another shock absorbing member 50 is attached in a posture where the connected portion extends in the horizontal direction. As the shock absorbing member 50, the shock absorbing members 10, 20, and 30 described in the above embodiment may be used.

[0266] Although an example of a structure in which the first connecting belt portion connects three connected parts is cited, the number of connected parts may be four or more. In addition, in the above embodiment, although an example of a structure in which the upper end of the connected part is connected by the first connecting belt portion and the lower end is connected by the second connecting belt portion is cited, it may also be a structure in which only one end (upper end or lower end) is connected by the first connecting belt portion.

[0267] In addition, the automobile door may be not only a front door disposed on the side of the automobile, but also a rear door disposed on the side of the automobile, or a back door (also called a tailgate) disposed on the rear of the automobile.

[0268] In the above-described embodiment, steel is used as the material of the blank and the shock absorbing member, but metal such as stainless steel, aluminum, and aluminum alloy, or CFRP may be used.

[0269] Industrial Applicability

[0270] According to the present invention, there are provided an impact absorbing member for an automobile door capable of exhibiting excellent tensile rigidity and impact resistance at low cost, an automobile door, a blank, and a method for producing the impact absorbing member for an automobile door.

[0271] Explanation of symbols

[0272] 1: automobile door; 1a: exterior panel; 1b: reinforcement component; 1c: interior panel; 10: impact absorbing component; 11: first connecting belt portion; 13: connected portion; 13a: impact absorbing portion; 13b: first transition portion; 13c: second transition portion; 15: second connecting belt portion; 23E: overlapping surface; 100: single-piece blank; 200: spliced ​​blank.

Claims

1. An impact absorbing component for a vehicle door, formed from a blank as a single blank or a spliced ​​blank, characterized in that: have: A connecting belt portion extending along a first direction; and At least three connected parts, one end of which is connected to the connecting belt part and extends along a second direction intersecting the first direction. The connected portion has a shock absorbing portion having a closed cross-sectional structure.

2. The impact absorbing member for an automobile door according to claim 1, characterized in that: The above-mentioned blank is the above-mentioned spliced ​​blank, The connecting belt portion and the connected portion are integrally connected via a joining portion.

3. The impact absorbing member for an automobile door according to claim 2, characterized in that: The connected portion has an overlapping surface overlapping a portion of the connecting belt portion. The joining portion is formed on the overlapping surface, whereby the connecting belt portion and the connected portion are integrally connected.

4. The impact absorbing member for an automobile door according to claim 2, characterized in that: The joining portion is a welded portion, and there is no HAZ softened portion in the welded portion.

5. The impact absorbing member for an automobile door according to claim 1, characterized in that: The tensile strength of the connected portion is 1100 MPa or more.

6. The impact absorbing member for an automobile door according to claim 1, characterized in that: The Vickers hardness of the connected portion is 350 HV or more.

7. A car door, characterized in that: have: The impact absorbing member for an automobile door according to any one of claims 1 to 6; and An exterior panel is provided with the above-mentioned impact absorbing component for automobile door.

8. The automobile door according to claim 7, characterized in that: The above-mentioned impact absorbing member for automobile door is mounted on the reinforcing member.

9. The automobile door according to claim 8, characterized in that: The cross section of the reinforcing member perpendicular to its extension direction has an open cross section. The closed cross-section structure is formed by attaching the connecting belt portion of the impact absorbing member for an automobile door to the reinforcing member.

10. A blank for forming an impact absorbing component for an automobile door, characterized in that: The impact absorbing component for automobile door comprises: a connecting belt portion extending along a first direction; and at least three connected portions, one end of which is connected to the connecting belt portion and extends along a second direction intersecting the first direction, wherein the connected portions have an impact absorbing portion with a closed cross-section structure. The above blank has: A connecting belt portion forming region extending along the first direction and formed into the connecting belt portion; and At least three connected portion forming areas, one end of which is connected to the above-mentioned connecting belt portion forming area, extends along the above-mentioned second direction, and is formed into the above-mentioned at least three connected portions, The above-mentioned blank is a single-piece blank or a spliced ​​blank.

11. The blank according to claim 10, characterized in that The above-mentioned blank is the above-mentioned spliced ​​blank, The connecting belt portion forming region and the connected portion forming region are integrally connected via a joining portion.

12. The blank according to claim 11, characterized in that The connected portion forming region has an overlapping surface forming region overlapping a portion of the connecting belt portion forming region, The joining portion is formed on the overlapping surface, whereby the connecting belt portion forming region and the connected portion forming region are integrally connected via the joining portion.

13. The blank according to any one of claims 10 to 12, characterized in that A notch is formed near a portion where the connecting belt portion forming region and the connected portion forming region are connected.

14. A method for manufacturing an impact absorbing component for an automobile door, characterized in that: The impact absorbing component for automobile door comprises: a connecting belt portion extending along a first direction; and at least three connected portions, one end of which is connected to the connecting belt portion and extends along a second direction intersecting the first direction, wherein the connected portions have an impact absorbing portion with a closed cross-section structure. The manufacturing method of the impact absorbing component for automobile door comprises: In the first step, a blank, which is a single-piece blank or a combined blank, is stamped in a cold state to obtain an intermediate stamped product, wherein the blank has: a connecting belt portion forming region extending along the first direction and formed into the connecting belt portion; and at least three connected portion forming regions, one end of which is connected to the connecting belt portion forming region and extends along the second direction and formed into the at least three connected portions; and In the second step, the intermediate stamped product is used for stamping to obtain a shock absorbing member for an automobile door. In the above second step, When the above-mentioned blank is the above-mentioned single-piece blank, the above-mentioned intermediate stamping product is stamped while being heated to a temperature above the Ac3 point. When the above-mentioned blank is the above-mentioned spliced ​​blank, the above-mentioned intermediate stamping product is stamped while being cold or heated to a temperature above the Ac3 point.

15. The method for manufacturing an impact absorbing member for an automobile door according to claim 14, characterized in that: The above-mentioned blank is the above-mentioned spliced ​​blank, The connecting belt portion forming region and the connected portion forming region are integrally connected via a joining portion.

16. The method for manufacturing an impact absorbing member for an automobile door according to claim 15, characterized in that: The connected portion forming region has an overlapping surface forming region overlapping a portion of the connecting belt portion forming region, The joining portion is formed on the overlapping surface, whereby the connecting belt portion forming region and the connected portion forming region are integrally connected via the joining portion.

17. The method for manufacturing a shock absorbing member for an automobile door according to claim 15 or 16, characterized in that: In the second step, the intermediate press-formed product is press-formed while being heated to a temperature equal to or higher than the Ac3 point.