Methyl tert-butyl ether cracking catalyst for isobutylene and preparation method thereof

A technology of methyl tert-butyl ether and catalyst, which is applied in the field of methyl tert-butyl ether cracking to produce isobutylene catalyst and its preparation, can solve the problems of increased side reaction activity, influence on catalyst selectivity, influence on catalyst service life, etc., and achieve Improve the polarity, weaken the adsorption force, and improve the effect of the pore structure

Active Publication Date: 2014-10-15
CHINA PETROLEUM & CHEM CORP +1
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the above two methods, the calcination temperature used is above 700°C to optimize the activity and selectivity of the catalyst, and when the calcination temperature is lower than 700°C, the activity of side reactions such as isobutylene polymerization or methanol dehydration of the obtained catalyst increases. This affects the selectivity of the catalyst, and at the same time affects the service life of the catalyst due to the deposition of polymers in the by-products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Alumina A1 and Silicalite-1 molecular sieves were mixed at a weight ratio of 1:10, rolled into balls, dried at 110°C for 3 hours, and calcined at 500°C for 4 hours to obtain H-1. Catalyst C-1 was obtained by treating H-1 with saturated water vapor at 200°C for 5 hours and drying at 110°C for 3 hours. Table 1 shows its physical and chemical properties.

Embodiment 2

[0034] Alumina A1 and Silicalite-1 molecular sieves were mixed at a weight ratio of 1:25, rolled into balls, dried at 110°C for 3 hours, and calcined at 500°C for 4 hours to obtain H-2. Catalyst C-2 was obtained by treating H-2 with saturated water vapor at 200°C for 5 hours and drying at 110°C for 3 hours, and its physical and chemical properties are listed in Table 1.

Embodiment 3

[0036] Alumina A2 and Silicalite-1 molecular sieves were mixed at a weight ratio of 1:20, rolled into balls, dried at 110°C for 3 hours, and calcined at 500°C for 4 hours to obtain H-3. Catalyst C-3 was obtained by treating H-3 with saturated water vapor at 200°C for 5 hours and drying at 110°C for 3 hours, and its physical and chemical properties are listed in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses a catalyst used in production of isobutene through cracking of methyl tert-butyl ether (MTBE) and a preparation method thereof. The catalyst comprises alumina and a Silicalite-1 molecular sieve; alumina and the Silicalite-1 molecular sieve are mixed and molded and then undergo hydro-thermal treatment, and a resultant is used as the catalyst; preferably, the catalyst is loaded with a proper amount of active metal components; and the catalyst is used for cracking of MTBE for production of isobutene. The catalyst prepared in the invention has good catalysis performance, enables good selectivity on methanol and isobutene and a high conversion rate of MTBE to be obtained and inhibits generation of dimethyl ether, a reaction by-product.

Description

technical field [0001] The invention relates to a catalyst for producing isobutylene by cracking methyl tert-butyl ether and a preparation method thereof. Background technique [0002] Isobutene is an important organic chemical raw material. High-purity isobutene is widely used in the production of butyl rubber, polyisobutene and other products. Methyl tert-butyl ether (MTBE) cracking to produce high-purity isobutene is an advanced and economical method among many production methods. A better method. The by-product of MTBE cracking, dimethyl ether, is the main factor affecting the purity of the product isobutylene. When the product isobutylene is used to produce butyl rubber, the requirements for its dimethyl ether content are particularly strict. Therefore, it is the core of this technology to develop a catalyst with excellent MTBE cracking conversion rate and isobutene selectivity to minimize or not generate dimethyl ether and reduce the burden of subsequent separation of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J29/035C07C11/09C07C1/20
CPCY02P20/52
Inventor 张淑梅翟庆铜陈明乔凯郭长新王春梅
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap