A kind of method of producing methyl acetate

A technology of methyl acetate and dimethyl ether, which is applied in the field of preparing methyl acetate through carbonylation of dimethyl ether, can solve the problems of short life, poor catalyst stability, and restricted application, and achieve the effect of prolonging life and improving stability

Active Publication Date: 2015-12-09
DALIAN INST OF CHEM PHYSICS CHINESE ACAD OF SCI
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, under the reaction conditions, the pyridine adsorbed in the mordenite will slowly desorb, and the carbon deposition of the zeolite molecular sieve will also slowly increase, resulting in a gradual decline in catalyst activity, poor catalyst stability and short life, which seriously restricts its use in large-scale applications. Application in large-scale industrial production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method of producing methyl acetate
  • A kind of method of producing methyl acetate
  • A kind of method of producing methyl acetate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] 50 g of hydrogen-type mordenite with a silicon-aluminum ratio of 4:1 was calcined at 550° C. for 5 hours in an air atmosphere in a muffle furnace, and a part of the powder samples were pressed into tablets and crushed into 20-40 meshes for activity testing. Weigh 10 g of the hydrogen-type mordenite sample, put it into a stainless steel reaction tube with an inner diameter of 8.5 mm, activate it with nitrogen gas at normal pressure and 300 °C for 1 hour, and then bubble it with nitrogen gas liquid, will Blow into hydrogen-type mordenite, treat for 2 hours, and then blow with nitrogen for 1 hour, then drop to 250 ° C, pass through carbon monoxide: dimethyl ether: Slowly increase the pressure to the reaction pressure of 2MPa, control the reaction space velocity GHSV=1000h -1 , using gas chromatography to detect and analyze the tail gas online, and calculate the conversion rate of dimethyl ether and the selectivity of methyl acetate. The reaction results are shown in Ta...

Embodiment 2

[0042] The experimental procedure is the same as in Example 1, the silicon-alumina ratio of the hydrogen-type mordenite is changed to 6: 1, and the pre-absorbed alicyclic organic amine on the catalyst is changed to The alicyclic organic amine in the feed gas is replaced by The rest of the experimental steps are consistent with Example 1, and the reaction results are shown in Table 1.

Embodiment 3

[0044] The experimental procedure is the same as in Example 1, the silicon-aluminum ratio of the hydrogen-type mordenite is changed to 60: 1, and the pre-absorbed alicyclic organic amine on the catalyst is changed to The alicyclic organic amine in the feed gas is replaced by the molar ratio of 1:1 The rest of the experimental steps are consistent with Example 1, and the reaction results are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a method used for producing methyl acetate. According to the method, raw material gas containing alicyclic organic amine, dimethyl ether, carbonic oxide, and optionally selected hydrogen passes through a reaction reactor filled with a hydrogen-type mordenite molecular sieve catalyst so as to prepare methyl acetate, wherein the hydrogen-type mordenite molecular sieve catalyst is alicyclic organic amine absorbed hydrogen-type mordenite molecular sieve catalyst. According to the method, alicyclic organic amine absorbed hydrogen-type mordenite molecular sieve is taken as the catalyst, and alicyclic organic amine is added into the raw material gas, so that desorption of alicyclic organic amine in reaction processes can be made up stably, stability of the catalyst is increased, and service life of the catalyst is prolonged.

Description

technical field [0001] The present invention relates to a kind of method of producing methyl acetate, especially the method for preparing methyl acetate by carbonylation of dimethyl ether. Background technique [0002] Methyl acetate is an important organic chemical raw material and solvent. Methyl acetate can be used to synthesize acetic acid and its derivatives such as acetic anhydride and vinyl acetate. At present, acetic acid is mainly industrially produced through the homogeneous methanol carbonylation method of Monsanto and BP. During the reaction process, noble metal catalysts containing Rh or Ir and corrosive CH are used. 3 I and other co-catalysts [J.Catal.245 (2007) 110-123]. Methyl acetate can also be synthesized into ethanol by hydrogenation reduction [ChemSusChem3 (2010) 1192-1199]. Ethanol has a higher octane number than gasoline, can be completely burned in internal combustion engines, and can be used alone or mixed with gasoline as a fuel for automobiles. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C07C69/14C07C67/37
CPCC07C67/37C07C69/14
Inventor 倪友明朱文良刘红超刘勇刘中民孟霜鹤李利娜刘世平周慧
Owner DALIAN INST OF CHEM PHYSICS CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap